Reduction Behaviors Of Chromite And Nio In Liquid Fe-C Alloys

In this study, reduction behaviours of Turkish chromite concentrate (48 % Cr2O3, 13.30 % FeO, 18.33 % MgO, 12.37 % Al2O3, 5.76 % SiO2) and nickel oxide by Fe-C alloy in graphite crucible were investigated. In the first stage of experiments, steel scraps were melted in graphite crucibles and were saturated with carbon at 1600 °C and 30 min. In the second stage, mixtures of different amount of chromite concentrate, nickel oxide and flux additives (CaO,SiO2 and CaF2) were charged into the graphite crucible containing the Fe-C alloy and heated to 1600 °C for different reduction times (0-180 min) under argon gas. The highest Cr and Ni con-tents in alloys were found as 11.41 and 14.37 % and the highest Cr and Ni recoveries were found as 88 and94 %, respectively at 180 min.