Research on Removal of Potassium and Sodium by Pre-Reduction Sintering

"It is generally known that alkali metals are harmful to blast furnace production resulting in aggravating RDI of sinters, abnormal expansion of pellets, deteriorating blast furnace lining, etc. Sinters regarded as dominating burden of blast furnace are determined as the main source of alkali metals. In this study, the removal behavior of potassium and sodium oxides by pre-reduction sintering during the sintering process was studied. The removal ratio ofK20 and Na20 was greatly influenced by coke powder content, carbon species, coke powder adding ways, additive and so on. Under the conditions of carbon rate 12% and 5% dosage of CO supplied in the sintering process, the corresponding removal ratio ofK20, Na20 was 69.00% and 32.79%, and metallization ratio could reach 4.65%. This technology provided a novel process for reducing the content of alkali metals in sinters and dramatically improving the quality of blast furnace burden.IntroductionSinter is the main iron-bearing charge of blast furnace for iron-making in China, making up about 80% of the total burden; therefore, its quality has a significant influence on the quality of pig iron and blast furnace operation. Research and practice of numerous years prove that potassium and sodium coming from ores are brought into blast furnace and upgraded, which is one of the essential reasons that lead to blast furnace nodulation and influences its strength. Currently, effective flow sheet to remove potassium and sodium is weak magnetic separation-intensive magnetic separation-flotation [l], while iron ore concentrate is still ofhigh levels of potassium and sodium. As sintering process is also not effective to remove potassium and sodium, blast furnace in China is of high alkali burden, e.g. it reaches 5.6-6.2kg/tFe in Baotou iron making plant, which is greater than international tolerated level of2.55kgltFe [l]."