Research on Sintering Properties of Vanadium-Titanum Magnetite Concentrates

"The sintering properties of vanadium-titanium magnetite concentrate(VTC) was studied in this paper. Through the optimizing the sintering process of VTC, the suitable granulation moisture and coke proportion were determined. The sintering velocity decreased from 23.05 mm/min to 18.22 mm/min. With the increase of VTC proportion from 0 to 46%, the specific productivity and tumbler index were respectively decreased from 1.55 t/(m2·h) to 1.21 t/(m2·h), and 62.93% to 57.73%. The temperature of liquid phase formations of mixtures increased, the amount of liquid lowered, and the content and sharp of sintering mineral gradually changed with the increase of VTC ,these lead that sinter quality became worse.IntroductionIn recent years, the steel industry of China is developing rapidly. And the steel production was 627 million tons in 2010. At present, the resources of vanadium-titanium magnetite concentrate(VTC) was about 14.4% of the total national iron reserves of China[1]. VTC has been used as sintering material by Magang, Chenggang and Pangang. The amount of VTC in Pangang is maximum. However, there exist many problems in VTC sintering, which involve in high specific productivity, bad sintering tumbler strength and high energy consumption[2~5]. That’s why the proportion of VTC is limited in sintering.The high quality of iron ore resources is worse in China. Therefore, it’s necessary to study the properties of VTC sintering, and to find out the reason how the VTC ratio affect the sinter performance. Purpose and significance of the research is to get high-quality sinter with the proportion of VTC greatly raised."