Research on the Slag Phase Type of Vanadium-Titanium Magnetite in Pre-Reduction -Electric Furnace Smelting

"For the comprehensive recovery ofV, Ti, Fe in vanadium-titanium magnetite in the process of pre-reduction-electric furnace smelting, it is expected that vanadium oxide is reduced into molten iron and titanium oxide is available in the slag. Thus the effect of slag basicity, the content of MgO, MnO and CaF 2 of slag content on the separation of slag and molten iron and the comprehensive recovery of V, Ti, Fe were investigated. The results show that increasing slag basicity, MgO, MnO and CaF2 are all beneficial to the separation of slag and molten iron. Higher slag basicity and the addition of CaF2 strengthen the reduction of vanadium oxide, and inhibite the reduction of titanium oxide, which are in favour of the recovery ofV and Ti. However, the addition ofMgO, MnO was not efficient for the comprehensive recovery ofV, Ti, Fe. For the vanadium-titanium magnetite of Panxi in China, the recovery of Fe was over 98%, the recovery ofV in molten iron was over 85% and the Ti02 content in slag was about 43% under the optimal conditions of slag phase type.IntroductionIt is well known that there are abundant vanadium-titanium magnetite resources which are located in Panzhihua of Sichuan Province[!]. At present the vananium-titanium magnetite concentrates are smelted in the blast furnace, which just make use of iron and vanadium, but lots of titanium is discarded in the slag. At the same time, the process has a large number of disadvantages, such as low recovery of vanadium, long route, pollutions, large investment and expenditure of energy[2-3]. In recent years, in order to efficiently utilize the vanadium-titanium magnetite concentrates, several new non-blast furnace processes have been proposed, such as pre-reduction-electric furnace, pre-reduction-grinding separation and so on[4]. Especially pre-reduction-electric furnace is operating well in South Africa and New Zealand,However,Du to the high slag basicity of the slag, the grade ofTi02 of slag is Corresponding author:Minjun Tang.E-mail:450435123@qq.com. Tel:13627429224."