Selective Laser Melting: Characteristics Of In718 Powder And Microstructures Of Fabricated In718 Sample

Powder characteristics have a significant influence on selective laser melting (SLM) process. In this research, particle size, surface contour and the microstructure of IN718 powder used in SLM were tested, and the physical and chemical changes during heating process of the powder were investigated as well. The shape characteristic and fluid properties of IN718 powder were defined and measured. It is shows that most particles of IN718 powder exhibited nearly spherical shapes, and the particle size is about 22.95μm. On this basis, IN718 sample was fabricated by SLM process using the powder and the microstructure of the fabricated sample was investigated. The results indicated that the sample has a dense microstructure, no macro-defects but a few micropores and porosity. Compared with the powder, there was no new phase formed in the sample and melting point of the sample was little less than that of the powder.