Some Challenges In The Nitride Metallurgy: Synthesis Of Complex Nitrides, Phase Equilibria And Chemical Potential Measurements (Invited)

As part of a systematic study on the thermodynamic properties of complex nitrides, phase equilibria of the system Li-M-N (M Mg, AI, Ga) at 900 K were investigated. An attempt to determine the thermodynamic properties of complex nitrides was made by using the galvanic cell method, which utilizes LiMgN as an electrolyte under nitrogen atmosphere. The electromotive force (Emf) of ilie cell at temperatures between 800 and 1100 K was measured. Whilc the Emf of the cell at 900 K was measured to be 0.137 V, data discrepancies of ±0.03V were found. It was difficult to determine temperature dependence of ilie Emf. The Gibbs energy change for the reaction, 113 LbN (s) + 1/3 Mg3N2 (s) = LiMgN (s), at 900 K was determined to be tJ.Gor (LiMgN) -13.2 (±2.9) kJ/mol. Using thermodynamic information on ilie binary nitride from literature, the standard Gibbs energy of LiMgN was derived to be AGO f (LiMgN)= - 121 kJ at 900 K. The thermodynamic stability range of nitride was discussed by constructing isothermal chemical potential diagrams that provide a better understanding of ilie stability region of the LiMgN phase. The diagram was found to be in good agreement with the isoiliermal phase diagram determined by ilie alloy equilibration meiliod. Although the obtained data includes large uncertainties, the results provide a better understanding of the iliermodynamic stability of nitrides. The potential application of this complex nitride to nitrogen chemical sensors or a medium for controlling nitrogen potential is also shown.