Some Effects Of Zirconium On Extrusion Properties Of Magnesium-Base Alloys Containing Zinc

THE important literature concerning zirconium in magnesium-base alloys is predominantly contained in patent references. Sauerwald, Eisenreich, and Holub1-4 discovered the profound grain-refining influence of small amounts of zirconium on cast magnesium and the attendant increases in strength, and ductility. They extended their work to reveal that limited amounts of certain other elements, including zinc, could be added for further improvement in strength and hardness. British. Patent 5111376 relates to the parent discoveries of Sauerwald, Eisen¬reich, and Holub. All of these references deal primarily with casting characteristics and properties in the cast state. Minor mention is made of desirable tensile strength, ductility, and toughness of wrought Mg-Zr alloys* modified by one or more additional elements. No extensive reference in the literature" has been found to the particular characteristics of wrought Mg-Zn-Zr alloys, with which the present paper is concerned. - The work to be discussed represents essentially an extrusion study of the Mg-Zn-Zr alloys and indicates that this system is highly interesting in the wrought state both academically and commercially. Accordingly, an important aim of this paper is to describe the hot-workability, tension and compression properties, metal¬lography, and toughness of these alloys. Compositional variations are limited to the ranges o to 7 per cent Zn and o to I per cent Zr. EXPERIMENTAL PROCEDURE Alloying and Casting Alloying ingredients were cell mag¬nesium, commercial zinc (intermediate grade), and a chloride salt containing approximately 50 per cent ZrCl2 and 50 per cent alkali chlorides. This salt is produced by Titanium Alloy Manu¬facturing Company. Melting, alloying, and pouring procedure essentially followed the crucible process as described by Nelson.6 The magnesium was melted using Dow No. 310 flux, and the temperature raised to 1350° to 1400°F for the alloying operations. After alloying of the zinc, the zirconium containing salt was added in small portions with vigorous stirring. This is an adaptation of the method described in British Patent 533264.7 The alloying efficiency of zir¬conium was approximately 30 per cent. During the alloying of zirconium, fluorspar was added in amount required as a flux¬inspissating agent. Next the melt was refined with Dow No. 310 flux and held quietly for 15 min. Finally billets were cast in a book-type permanent mold