Stress-corrosion Cracking of Annealed Brasses

SEASON cracking of brass has received wide attention and there is a wealth of technical literature on the subject. Its causes are fairly well understood and means for its prevention are inexpensive and effective, .so that the frequency of failures from this source has diminished of recent years. But its sister phenomenon, the failure of annealed brass by reason of applied tensile stress plus a certain type of corrosion, has received less attention, though it has been responsible for occasional more or less troublesome cases of cracking of brass in service. The work described in the following pages was undertaken about two years ago to determine the relative resistance of various commercial brass mixtures to stress-corrosion cracking, and to learn something of the controlling factors. By stress-corrosion cracking we mean the cracking of brass free- from internal stresses by reason of applied tensile stress and simultaneous attack by certain corrosive agents. Rogers,1 in discussing a paper by Hatfield and Thirkell, says : "He had also applied a solution of mercuric salt to tensile test pieces of brass whilst they were under stress in the testing machine. At very moderate stresses such test pieces cracked, and very readily broke." Moore, Beckinsale and Mallinson2 subjected test pieces to simultane-us corrosion and tensile stress. In order to determine the minimum stress detectable in brass by the mercurous nitrate test, tensile samples were placed under stress and treated with mercurous nitrate solution. They found that brass stressed below a minimum did not crack.