Study of Lattice Distortion in Plastically Deformed Alpha Iron

IT is generally agreed that cold-working mechanically refines the grains into smaller fragments and with continued working these are oriented with certain crystallographic directions bearing a relation to the direction in which the metal is worked. Some of the energy expended on the metal during plastic deformation appears in the form of heat, but a very small portion remains in the metal as stored energy. The entropy, specific heat capacity, temperature at which recrystallization will just begin, density, ductility, elasticity, tensile strength, and resistance to corrosion are affected. These properties have been studied extensively and some of the changes in the physical properties due to cold-working were attributed to lattice distortion.1-8 The broadening of the K. lines on the X-ray diffraction diagrams of plastically deformed metals is believed to indicate lattice distortion, and consequently the existence of internal stresses. The evidence supporting this theory rests solely upon the observed experimental fact that the dif-fraction lines are broadened and the K a doublets are completely diffused. Elam9 has reviewed the matter of lattice distortion in relationship to the hardening of metals by plastic deformation. The X-ray diagrams of plastically deformed metals differ in general from annealed metals. The hardening of a metal was believed due to lattice distortion.9 The resolu-tion of the doublet is lost when a metal is cold-worked and the Lane spots are elongated. At one time this elongation was thought to indicate the elastic bending of the crystal planes. However, more careful work showed that the asterism was due to new orientations developed within the fragmented grains during plastic deformation. Some theories attrib-uted the hardening to fragmentation of the grains into smaller units.