Study of Strengthen Pelletization of Nickel Laterite

"In ferronickel production, nickel oxide and part of the iron oxide are reduced to metal by agglomeration and smelting in blast furnace. Due to the physical and chemical properties of the laterite ores, a large fraction of fines is generated during the pre-treatment stages and the strength of agglomeration is weakened, which results in low productivity and bad quality. In this paper, the process of pelletization of nickel laterite was developed, and some parameters to strengthen the pelletization of nickel laterite have been optimized. The results show that the compressive strength of fired nickel laterite pellet can reach over 2000 Newton per pellet while firing at the temperature of 1220 °C~1250 °C in 12 min. The product pellet can be used as high-quality burden for blast furnace to manufacture ferronickel.IntroductionIn recent years, the global stainless steel market was developed exuberantly, which greatly promoted the needs of the basic raw material of stainless steel smelting - metal nickel. Currently nickel sulfide ores are only 40% of global nickel reserves, but offer 60% of all the nickel production. However, with the deficit of resources, the nickel sulfide ore (high grade ore) is depleting, so there is an increasing focus on the utilization of low-grade nickel laterite. Recent research has focused on the wet treatment process to utilize nickel laterite, and less on the use of other technologies [1-8]. The economical and efficient technology relies on the reduction of nickel oxide and part of the iron oxide metal by agglomeration and smelting in blast furnace in China. Some domestic steel companies have adopted this process [9, 10]. Unfortunately a large fraction of fines is generated during the pre-treatment stages and the strength of agglomeration is weakened, which results in low productivity and bad quality of fired pellets. In this study, the process of pelletization of nickel laterite was developed firstly, and some parameters to strengthen the pelletization of nickel laterite have been optimized, and the product pellet can be used to produce stainless steel and ferronickel alloy by blast furnace."