Study on the Improvements of Reduction Swellability and Low Temperature Reduction Disintegration of Vanadium-Titanium Magnetite Oxidized Pellets

"Reduction swellability index (Rsn and low temperature reduction disintegration index (RDI) of vanadium-titanium magnetite oxidized pellets are harmful to the processing of ironmaking, for example, causing serious gas permeability, decreased yield, higher coke ratio and more furnace dust. Thus, the improvements of RSI and RDI of vanadium-titanium magnetite oxidized pellets were investigated in this paper, including the pretreatment of raw material, additives of dolomite or boric acid, pellets treated in chloride solution and so on. The results showed that damp milling as pretreatment and boric acid added in pelletizing were conducive to the RSI which decreased 5% and 7% respectively, while they were not efficient enough in improving RDI. Dolomite was efficient in improving RSI, but had negative effect on RDI. There was no evidence to show that RSI and RDI would be improved when pellets were treated in chloride solution. Pursuing this further, the mechanism of those improvements were investigated.IntroductionIn the world, vanadium-titanium magnetite utilization is investigated around how to recover iron, titanium, vanadium, and divided into blast-furnace method and non-blast-furnace method according to respective characteristics. Blast furnace method [1, 2] can recover iron and vanadium effectively, but Ti02 cannot be recycled. Non-blast-furnace methods include rotary kiln-electric furnace method, pre-reduction electric furnace method, reduction- grinding method and sodium vanadium-rotary kiln-electric furnace method and so on. [3-7]Comparing to the Non-blast-furnace method, the method of blast furnace smelting has been put into industrial applications. And it has the following advantages: First of all, effective recycling iron and vanadium; Second, technical problems of high titanium slag in blast furnace smelting; Third, it has mature technology in blast furnace smelting."