Study On Thermal Physical Properties Of 304 Stainless Steel

The DIL402C thermal dilatometer and STA449C thermal analyzer were employed to test the linear expansion and contraction coefficient，CP and DSC curve of 304 stainless steel. The result showed that the linear expansion coefficient range was 20.9700×10-6～21.5712×10-6 and the linear contraction coefficient range was 21.2528×10-6～21.9471×10-6.The linear expansion and contraction coefficient were higher than other steel grade，so the 304 stainless steel belonged to the crack sensitive steel. Because of the crystal phase transformation occurred during the 1000~1400 ℃,the curve of CP fluctuated obviously and the defects of casting blank occurred easily. Chosen 1414℃ as the liquidus temperature of 304 stainless steel based on the analysis results of DSC. The curve of DSC was unsmooth during 1450～1100℃，the crystal phase transformation occurs and thermal stability of slab was inferior.When the initial solidified shell formed in this temperature range,the thickness of the shell would be nonuniform and the surface defects occurred more easily.