Suppression of Internal Defects in Cold Drawing of Pure Magnesium Wire

"Pure magnesium is a material with high functionality, however, the cold drawing of this material is very difficult, that is why, until this day there are no optimal cold drawing conditions. Furthermore, cold drawing of pure magnesium wire shows a problem with internal defects that occurs under certain conditions. In this research, the aim is the suppression of internal defects, and final target is to create the optimal cold drawing conditions for pure magnesium wires. The first step is the investigation of the drawing limit by using 250°Cannealed wire. As a result, reduction of 10% per pass was chosen for stable wire drawing. However, in this case, it was found that internal defects occurred at total reduction of over 45% during drawing. Investigation of intermediate annealing conditions that can suppress internal defects, and influence on internal defect that the die half angle and reduction per pass. As a result, it was found that the drawing condition capable of suppressing internal defects most efficiently was 13% reduction drawing by using under 6°half angle die. Consequently, it’s possible to manufacture a cold fine drawn pure magnesium wire of 100µm, without defects in the center of the wire and hindering its mechanical properties.INTRODUCTIONMagnesium is a light and high functionality material that has high vibration absorbency, heat dissipation, electromagnetic wave-shielding and recycling efficiency (Conruy, 1989). However, proper cold wire drawing conditions haven’t been established, that is why warm or hot processing is commonly used (Oishi, Mori, &Kawabe, 2005). As a result, strength improvement of the wires is not possible, that is why the production of medical tools is disregarded. If it was possible to cold draw magnesium wires, the applications for material products would expand. Further, in wire drawing such difficult processing material, if appropriate processing conditions are not selected, defects will be generated inside the drawn wire."