Surface Magnetization And Block Structure Of Ferrite

THE magnetic powder method, long used for roughly mapping magnetic fields, has recently been refined 1,2 for investigating the microscopic variations in the surface magnetization of ferromagnetic crystals. Bitter' first discovered regular powder patterns connected with the crystal structure of such specimens. Several other investigators3 have used Bitter's original technique, with slight modifications, to study the variation of the patterns with variations in the magnetizing field applied parallel to the surface, and their dependence upon the state of strain, of polish and of crystal cut. All of the explanations of these patterns on metallic ferromagnetics have been couched in general terms. In a preliminary report we have described an improvement in the powder technique which led us to the discovery of a new effect throwing considerable light on the magnetic secondary structure of alpha iron4 and of nickel' single crystals. We now report additional evidence confirming the existence and stability of a magnetic block secondary structure. SPECIMENS The following list describes the specimens used in the present investigation. DESIGNATION DESCRIPTION A1 Silicon ferrite furnished to us by Dr. W. E. Ruder, of the General Electric Co., for which he gave the following typical analysis: C, 0.05; P, 0.038; 5, 0.026; Mn, 0.15; Si, 3.24. Disk, 0.60 cm. diameter, about 0.05 cm. thick.