Syntheses of Zeolite-A and Zeolite-X from Kaollnite Activated by Mechanochemical Treatment

"A novel mechanochemical processing technique for the preparation of zeolites from kaolinite in NaOH solution was investigated. Dry and wet mechanochemical treatments combined by subsequent moderate heat treatment could accelerate the synthetic reaction for zeolites from kaolinite. This stimulating process produced zeolite-A and zeolite-X from activated kaolinite at extremely lower reaction temperature than conventionally applied for zeolites production. Conversion to zeolite-A and zeolite-X was strongly dependent on the activated state of kaolinite. Wet mechanochemical treatment modified the chemical composition of activated solids. Rapid dissolution of AIO species rather than SiO ones in the reactant solution was accelerated by wet milling together with NaOH that promoted the formation of zeolite-X of high specific surface area.IntroductionZeolites are a family of hydrated alumina-silicate minerals contains alkali and alkaline earth metals. They have a framework structure that encloses inter-connected cavities occupied by large metal cations and water molecules. Zeolites are characterized for their ability toward ion exchange and reversible dehydration. Properties of them are exploited through commercial productions of particular structural and chemical features. Zeolites are used as commercial uses for catalysis for FCC (fluidized catalytic cracking) of petroleum refining, drying reagents of gases and liquids, and selective adsorbent for pollution control [1-3]. In such purposes, artificially synthesized zeolites are employed, although natural ones are associated with hydrothermal and hot spring alteration of volcanic materials. Commercially, a hydrothermal process has been used for the preparation of zeolite synthesis. This preparation method gives zeolites of high chemical homogeneity and purity, however, this wet-chemistry-based processing is significantly influenced by reaction temperature, pH, concentration, and composition of starting substances [4]."