Technical Notes - Elastic Coefficients of Single Crystals of Alpha Brass

IN ref. 1, on the basis of tension and torsion experiments with single crystals of a brass, the values given in Table I were obtained for elastic coefficients. It was pointed out by Zener that the values for the 71.2 pct Cu were not satisfactory, since they resulted in a negative value for the bulk modulus, namely —4.17X1012 sq cm per dyne. In reevaluating the data of this investigation, it was determined that the reason for this negative bulk modulus lay in the extrapolation of the reciprocal Young's modulus to the zero value of the orientation function shown in Fig. 5 of ref. 1. This extrapolation was reevaluated by the method of least squares (50 pct probability) and a new value of the coefficient S,, was determined as 18.9220.42X 10M sq cm per dyne in lieu of the value originally reported of 18.82x10 sq cm per dyne. This new value of S, leads to a new value of S, of — 9.43 X101" sq cm per dyne. The values of the other coefficients are unchanged. results. This value compares with the value of 12.3X10 sq cm per dyne reported by Schmid and Boas? The new results are summarized in Table 11. These results follow similar qualitative trends, previously published,' relative to the effect of zinc content. However, the derived values of C11, C,, C,, and K are so sensitive to the uncertainty in the first decimal place of the S, values that they are probably not useful. This uncertainty must also apply to the previous results of Masima and Sachs," who obtained S, values from a similar extrapolation drawn wholly above their data points. Acknowledgments Advice and assistance on the statistical methods were obtained from R. W. Guard. The calculations were carried out by Miss E. Saacke.