Technology For Processing Of Lead-Bearing Materials From Copper Metallurgy At KGHM Polska Miedz S.A.

During copper production in shaft and flash smelting processes at KGHM Polska Miedz S.A., lead bearing material of sulfide, sulfate, and oxide character is generated in forms such as slime from shaft furnace gas handling systems, converter dusts, and dusts from an electric furnace for copper removal from flash smelting slag. These materials are polymetallic concentrates of Pb, Zn, and Cu, with As, Cl, and Cd as impurities. Shaft furnace slime, containing. about 50% PbS and 15% bituminous substances, is the main lead-bearing material. At the Glogów copper mill, a new plant was commissioned in June 2001 to process 80,000 tonnes per year of lead bearing materials to produce 26,000 tonnes per year of crude lead. The plant consists of a feed conditioning system, three (3) rotary rocking furnaces with a capacity of sixteen (16) tonnes of lead feed fired with natural gas and oxygen-enriched air containing up to 45 vol% O2, and a gas handling system. The gas handling system includes a post-combustion chamber, a gas cooling chamber with Cl neutralization, gas mixing chamber, bag filter, and dry limestone scrubbing system for SO2 removal. The lead-bearing feed is smelted with five (5) wt% Na2CO3 and thirteen (13) wt% iron scrap at a temperature of 950 to 1050°C for three (3) hours. The smelting process consists of four (4) stages; feed drying, firing of gaseous hydrocarbons and solid coal from the feed, lead reduction from slag, and separation of molten products. The flow rates of natural gas and oxygen to the burners are controlled to ensure combustion of the bituminous material in the furnace. The process produces crude lead bullion containing (wt%) 0.1 to 0.5% Cu, 0.02 to 0.5% As, 0.05 to 0.07% Bi, 0.1 to 0.5% Sb, and 0.1 to 0.6%Sn. The process also produces a mixture of sodium silicate slag, Fe-Zn-Pb-Cu-S matte, and Fe-As speiss containing (wt%) 5 to 10% Pb, 2 to 6% Cu, 10 to 15% Zn, 1 to 3% As, 10 to 15% S, 0.5 to 3.0% Cl, 2 to 4% K, 4 to 7% Na, 20 to 30% Fe, and 5 to 10% SiO2. The dust is made up of PbO, ZnO, PbSO4, and PbCI2, KCI, and NaCI with a chemical composition (wt%) of 35 to 50% Pb, 5 to 15% Zn, 3 to 6% As, 4 to 8% Cl, 2 to 5% K, and 2 to 5% Na. The construction of the new lead production plant at the Glogów copper mill will process both current lead-bearing materials as well as lead-bearing material that have been stockpiled over the last fifteen (15) years to give a significant improvement in protection of the natural environment.