Tekcrete Fast®: Fiber-Reinforced, Rapid-Setting Sprayed Concrete for Rib and Surface Control

"Fiber-reinforced spayed concrete has been used for several years in civil and tunneling operations. Research conducted to reduce cure times and increase compressive and flexural strengths resulted in the development of Tekcrete Fast®, a cementitious product capable of obtaining 41 MPa (6,000 psi) compressive strength and 8 MPa (1,200 psi) flexural strength in only 3 hours and reaching 7 day strengths of 62 MPa and 11.7 MPa (9,000 and 1,700 psi), respectively. A single bag product that uses conventional shotcrete and gunite application systems make it a natural crossover product for mining applications. The discovery of incredible adhesion properties and high resistance to chloride permeability helps ensure long-term stability and increases the ease of application. Project results from Disaster City® in Texas and the application for rehabilitating a coal mine belt entry are presented. The case study illustrates the effectiveness of the product in stabilizing a coal mine beltway and adjacent cross-cuts that were subjected to progressive sloughage due to humidity and cyclical loading. INTRODUCTION Original research produced a shotcrete formulation that extends beyond stabilization and can be used to restore the structural integrity of damaged infrastructure. The primary challenge was to develop a shotcrete or gunite that had structural strength within a few minutes to prevent parasitic loading, allowing ingress into damaged structures minutes after applying the mix formulation. This also applies to mining conditions where rapid support of progressive failures can minimize failure. An additional benefit was discovering that the product had extremely high adhesion properties in addition to high flexural strengths. The approach to product design was the development of “single bag” dry mixes that are entirely self-contained, can be rapidly transported anywhere in the field or underground, and can be deployed using simple equipment. Dry mix eliminates issues relevant to high shear water mixing because water is added in the form of a mist at the point of delivery; thus a low water-to-cement ratio can be achieved. However, since there is no onsite powder mixing, the product must have a high degree of inherent homogeneity. Minova offers a commercial version of this material, Tekcrete Fast®, a product that has been successfully deployed in the mining industry and is currently being used in civil, construction, and tunneling operations. The material can rapidly stabilize lose ground in metal, nonmetal, and coal mines. This paper described the technology development, product testing results, and applications and describes a case study to stabilize a coal mine beltway."