Tensile Strengths at Elevated Temperatures of Fine Wires of Some Platinum Alloys

THE short-time tensile-strength test, while it has not attained the practical importance of the creep test at elevated temperatures, has the advantage of being rapid and is satisfactory for determining relative strengths. For platinum and its alloys, which frequently are used at high temperatures under ill-defined conditions, the short-time test provides useful data that aid in the selection of the most promising alloy for each use. Measurements have been made upon 13 alloys, using wire 0.0031 in. in diameter, the choice of alloys and of wire size being determined by the requirements of a practical problem. Later the measurements were extended to higher temperatures by the use of heavier wire, 0.010 in, in diameter. APPARATUS The use of fine wire made the necessary equipment very simple, since no effort was made to measure the elongation. A small platinum-wound horizontal furnace was used, ½ in. in internal diameter by 1 ft. long, with the wire threaded through it. The wire, clamped at one end while the other ran over a ball-bearing pulley, of a total length of 29 in., was loaded directly by running sea sand into an attached basket, making the rate of loading and not of elongation constant. The sand flowed from a funnel, under a head of 3 in., into the basket. 3 in. below the orifice, at the rate of 170 grants per minute. Pulley friction and bending resist-ance of the wire as well as the force of impact of the sand could be neg-lected, being 3 grams and 0.5 grams, respectively. Furnace temperature .was uniform within ±5° C. over a length of 3 in., although a drift with time occurred, the largest amount being 20° C. No provision was necessary for a controlled atmosphere.