The Effect Of Graphene On The Microstructure And Mechanical Properties Of Aluminum/Graphene Produced By Hpt

The aluminum matrix composite reinforced by graphene was successfully fabricated using high pressure torsion (HPT). With only 0.5wt% graphene, the grain size was reduced to 100nm while that of pure Al was about 500nm. The hardness of the composite increased from the center (64HV) to the edge (120HV) of the sample. Moreover, the tensile strength of this composite reached 197MPa, while that of pure Al was 157MPa. The enhancement in mechanical properties was induced by grain refinement, load transfer from the matrix to the reinforcement and dislocations piled up at the grain boundaries.