The Effect of Scandium on the Microstructure of Al Alloys

"A small amount(0.2mass%) of Scandium(Sc) was added to the 7.NOl and 5083 Al alloys as a refiner and stabilizer of microstructure, and the resulting microstructures were discussed in comparison with the effects of the conventional additives. The followings are summarized: 1) in the as-solidified structure, a ·decreased tendency of constitutional supercooling and increased solubility of Mg were recognized for the Sc-added 5083 alloy. Sc is a -better microstructure refiner for the 7N01 alloy than Zr, in a sense that it does not suppress the favorable effect of· coexisting Ti. 2) Sc effectively suppresses recrystallization both in the 5083 and 7N01 alloys. 3) The rod like primary Al3Sc crystals formed during solidification, as well as the fine dispersion of Al3Sc precipitates formed by subsequent heat treatment, can act as a strong recrystallization suppresser. IntroductionThe 7N01 and 5083 alloys are the most popular industrial Al alloys and they are widely' used for various structures because of their superior properties. Fine macro and micro structures of the materials are required for obtaining acceptable sec resistance,consistent appearance of anodized surface and good weldability, as well as good mechanical properties. In order to produce fine grain structures, transition metals, such as Cr, Zr, and Mn, have been conventionally added.It has been reported that Sc is an efficient refiner [l, 2] and can be an alternative for the conventional and also suppresses recrystallization in Al alloys [3,4]. Scandium is the lightest transition element and forms an equilibrium intermetallic phase. The equilibrium phase, Ll2-Al3Sc, is coherent with the matrix, and of _spherical shape. A fine dispersion of the spherical precipitates is obtained by quenching and aging after solutionizing annealing. The authors have already reported a part of the experimental results on the effect of Sc on the as homogenized microstructure of the 5083 alloy [5]. In the present study, the effects of Sc on the macro and micro structures of the industrial high strength Al alloys(7N01 and 5083) for extrusion are investigated, and the superior role of Sc as a grain refiner is shown"