The Effects Of High Al₂O₃ On The Metallurgical Properties Of Sinter

Sintering-pot tests and metallurgical performances of sinter with 4 kind of different Al2O3 contents are experimented in this paper. Results show: when the Al2O3 contents increase from 2.0% to 3.5%, acicular calcium ferrites in mine phase will be gradually replaced by plate-like iron calcium. The increase of Al2O3 contents will lead to the addition of liquid viscosity and the reduction of permeability of sinter bed. Sintering time will be prolonged. The rate of yield is stable basically but production is low; besides, the increase of liquid viscosity will decrease of drum strength. The change of permeability of the material layer will make RDI +3.15 decrease first and then increase when Al2O3 contents changed from 2.0% to 3.5%. RI of sinter shows a contrary trend because many open voids are formed by deterioration of liquidity first and then pores closed.