The influence of Fe3+/Fe2+ratio on the viscosity of silicate slags

Viscosity measurement was carried out over a narrow range of silica content around the fayalite composition. A wide range of temperature and oxygen potential was covered where the slag was completely liquid. In order to keep the slag composition and the Fe3+/Fe2+ratio constant, theCO2/CO ratio was kept constant as the temperature was varied. Increasing the Fe3+content has little effect on viscosity for slags with a silica mole fraction of 0.31. At higher silica contents, increasing the Fe3+content brings about a small decrease in the viscosity.