The Morphology Control Of Cobalt Compounds And Co3O4 Powder Produced By Homogeneous Precipitation Process

Keywords: Co3O4, Cobalt Compounds, Morphology, Urea, Homogeneous Precipitation Depending on experimental condition, precipitation from cobalt nitrate and chloride solution in the presence of urea yield dispersed cobalt compounds with different chemical compositions and morphologies. The effects of concentration of cobalt solution and urea, agitation, on precipitation morphology were investigated experimentally. Generally in closed systems the particles are identified as cobalt (II) basic carbonate with needle type shape. In open system, spherical and plate-like precipitations of cobalt (II) basic cyanate are formed. The chemical formula of cobalt compounds was confirmed. They are CoII,III(OH)0.83(CO3)0.49 Ay?0.14 H2O (in tightly-capped reactor: A stands for NO3?, Cl?; y[A]molecular weight < 12.9) and CoII,III(OH)0.83(NCO)XAy?0.14 H2O. (in open reactor A stands for: NO3?, Cl?; 42 x + y[A]molecular weight < 44.82). The main reason was that the primary particles had different chemical compositions for the effects of the different kinds of anions and stoichio-chemical compositions of the primary particles. The effect degree of the anions depended on the co-existing anion radius in the reaction solution. According DTA-TG analysis of the cobalt compounds, the latter particles transform to Co3O4 powders on calcining. The shape of the Co3O4 particle with porous character has inheritance with precipitation. In this paper, it concludes that the particle formed by the principle of nucleation-aggregation in aqueous solution. The process of aggregation has played an important role in formation of particles. During calcination, the aggregation would be destroyed partly.