The New Composite Cast Alloys Copper Based and Technological Peculiarities of Processing

"During the last decades investigators of many countries shows an increased interest to alloys which are characterized by miscibility gap in a liquid state. It is connected with essential possibilities of control of structurization in such alloys because of the melt at certain temperature parameters is · emulsion with disperse phase inclusions. These ensure essential influence ·on structurizations.The certain inclusions can play a role of lubrication ensuring ""wearless"" process. The sizes of inclusions of this phase can be rather large proportional to sizes of strengthening phase (up to 1000 nm). Other inclusions ensure process of strengthening of a main material. In this case requests to a dispersibility character of distribution and structure of such inclusions are much higher.The multicomponent alloys of system of copper - (Fe - Cr - C)- alloy concern to the number of advanced compositions. The copper alloys with structure of a type of a ""frozen emulsion"" in which strengthening phase· is a chromium pig-iron are characterized by high thermal stability in the extreme operating conditions. The mechanism of inclusions forming is emulsifying of a melt in miscibility gap at temperatures close to temperature of binodal under superimposition of external effects.The main complexity of producing of ware from such alloys is .a providing in their structure of necessary dispersible inclusions uniformly distributed all over the volume. Thanks to a selective action of electromagnetic fields on liquid phases with various electroconductivity relative velocity of phases is created and is regulated the ratio of their ""apparent"" specific gravity is changed. Excitation of pulsing force effects with the certain frequency on interphase surface allow actively to influence on process of a dispersion of a liquid metal medium."