Treatment Of A Low Grade Compact Itabirite Iron Ore From Carajás - Brazil

This paper describes, in detail, results obtained from a research study of a complex iron ore aiming to produce a pellet feed concentrate with at least 65% of Fe and less than 3.5% of SiO2 in the final concentrate. The work includes an ore desliming followed by column flotation at laboratory scale. The ore sample was from Carajás province - Brazil and represents a complex low grade compact itabirite ore, analyzing 35.9% Fe, 45.1% SiO2 and 0.57% of Al2O3. Yet, the feed was treated previously by magnetic separation and grounded to 97% < 20 µm; this sample was named MAG 2. The chemical and mineralogical characterization of the MAG 2 sample showed that Fe and SiO2 grades were 50.7% and 24.3% respectively and was composed mainly by hematite, goethite and quartz. The particle size distribution, using a laser diffraction technique, showed that 90% of the particles were < 18 µm; 50% less than 8 µm and 10% minor than 1 µm. When the cationic reverse flotation without desliming was tested the selectivity of the process was very low and did not meet the concentrate metallurgical goals of the pellet feed product. However, when desliming was applied prior to flotation, a concentrate product with chemical characteristics of the pellet feed was obtained. The best results after desliming and column flotation achieved global iron metallurgical recovery of 72% with Fe grade in the concentrate of 66.5% and 2.1% SiO2 using starch as depressant for the iron oxides minerals at 1200 g/t ? 1500 g/t and an amine as the quartz collector at 100 g/t concentration (pH constant, at 10.5). It is believed that the desliming stage was key in the separation of the iron bearing particles and has a high potential for the flotation process of this type of ores.