By G. F. Comstock

A serious disagreement as to the effect of titanium on the hardenability of steel exists in published references to this subject. Kramer, Hafner and Toleman reported1 that acid-soluble titanium decreased the hardenability, with multiplying factors less than unity according to Grossmann's system for calculating hardenability from the composition. Crafts and Lamont, on the other hand, showed2 how titanium increased the hardenability, with multiplying fdctors up to nearly I.; for about 0.1 per cent titanium, though reducing the hardenability with higher titanium. Their data, however, were obtained almost exclusively from steels containing more than 1.4 per cent manganese, and thus should be considered as applying mainly to manganese steels. Likewise, the results of Kramer, Hafner and Toleman regarding titanium are subject to the limitation that although they eliminated the effect of the insoluble titanium compounds from their calculations, they did not make a similar correc- tion for the carbon that was combined with titanium and therefore occurred in a similarly ineffective form. It is suggested by the literature referred to that titanium may have different effects on hardenability, depending on the mode of its occurrence in the steel. The different effects on strength, ductility, etc., have already been discussed by the author.3 In the present discussion some comparisons, on the basis of hardenability as revealed by the Jominy end-quench test, are given between three titanium and two non-titanium steels heat-treated in the same ways, and between other titanium steels heat-treated in several different ways. Comparison of Plain-carbon, Vanadium and Titanium Steels The five steels used for these experiments were cominercially melted and rolled products received in the form of 1.5-in. rounds from three different mills. Their analyses are given in Table I. Steels 2, 3, and 4 are from the same basic electric heat1 containing 0.009 per cent of phosphorus and the same amount of sulphur. They were made by adding aluminum and low-carbon ferrotitanium to different ingots. No. I is a plain carbon

Jan 1, 1947

By J. Russ, C. L. Clark

For many years attempts have been made to develop a laboratory test that would serve to indicate the proper temperatures to be used in the various hot-working applications to which metals may be subjected as they are being processed from the cast ingot to the desired finished products. That these attempts have not been very successful is indicated by the fact that most of the temperatures in use today in these operations have been developed over a period of years by trial and error. In other words, the selection of the proper temperatures for the hot-working of metals is generally an art rather than a science. Our knowledge with respect to the behavior of metals at elevated temperatures has been greatly extended during the past several years. While most of the work in this field has been done at proposed operating temperatures of equipment, rather than at processing or fabricating temperatures, one outstanding fact has been developed, which is applicable to the entire high-temperature range; that is, that the rate of deformation to which the metal is subjected is of the same order of importance as the temperature. The failure to properly recognize this fact has greatly retarded the development of a suitable laboratory test for determining hot-working temperatures. Influence of Rate of Deformation on High-temperature Properties It is not the intent of this paper to survey all the work that has been done On the effect of deformation rate On the properties of metals. The importance of this factor, however, was shown by Zay Jeffries' as early as 1919, when he called attention to the existence of the so-called equicohesive temperature and to the effect of certain factors on the location of this temperature' Fig. I is a diagrammatic sketch showing the effect of temperature On the relative strength of the crystals and grain boundaries and the type of fracture that will res depnding On the location of the test, or Or temperature with respect to the equicOhesive temperature. Since the type fracture varies, it also follows that at temperatures below the equicohesive temperature the major deformation occurs in the grains: while at temperatures above, the deformation results either from the movement of the grains with respect to each other or recrystallization of the strained material occurs almost instantaneously, producing new crystals at the fracture. As previously indicated, it is an established fact that the position of this equicohesive temperature for any given metal is dependent On the deformation rate' For example, in 0.15 per cent plain carbon steel the location of this temperature under

Jan 1, 1947

By C. L. Clark, J. Russ

For many years attempts have been made to develop a laboratory test that would serve to indicate the proper temperatures to be used in the various hot-working applications to which metals may be subjected as they are being processed from the cast ingot to the desired finished products. That these attempts have not been very successful is indicated by the fact that most of the temperatures in use today in these operations have been developed over a period of years by trial and error. In other words, the selection of the proper temperatures for the hot-working of metals is generally an art rather than a science. Our knowledge with respect to the behavior of metals at elevated temperatures has been greatly extended during the past several years. While most of the work in this field has been done at proposed operating temperatures of equipment, rather than at processing or fabricating temperatures, one outstanding fact has been developed, which is applicable to the entire high-temperature range; that is, that the rate of deformation to which the metal is subjected is of the same order of importance as the temperature. The failure to properly recognize this fact has greatly retarded the development of a suitable laboratory test for determining hot-working temperatures. Influence of Rate of Deformation on High-temperature Properties It is not the intent of this paper to survey all the work that has been done On the effect of deformation rate On the properties of metals. The importance of this factor, however, was shown by Zay Jeffries' as early as 1919, when he called attention to the existence of the so-called equicohesive temperature and to the effect of certain factors on the location of this temperature' Fig. I is a diagrammatic sketch showing the effect of temperature On the relative strength of the crystals and grain boundaries and the type of fracture that will res depnding On the location of the test, or Or temperature with respect to the equicOhesive temperature. Since the type fracture varies, it also follows that at temperatures below the equicohesive temperature the major deformation occurs in the grains: while at temperatures above, the deformation results either from the movement of the grains with respect to each other or recrystallization of the strained material occurs almost instantaneously, producing new crystals at the fracture. As previously indicated, it is an established fact that the position of this equicohesive temperature for any given metal is dependent On the deformation rate' For example, in 0.15 per cent plain carbon steel the location of this temperature under

Jan 1, 1947

Jan 1, 1947

Jan 1, 1947

By Harry K. Ihrig

The hot-working of iron and steel is an art dating back to antiquity, but until about 25 years ago, relatively few alloying elements were used, and these were present only in small percentages. With the exception of sulphur, the amounts of other elements in steels did not markedly affect their hot-workability. The references in the literature on the effect of other elements on the hot-workability of steel are usually reports of failure of these steels in forging or rolling.1-8 With the increased use of alloying elements, and their use in larger amounts, it was observed that many of the new steels were red short in certain critical ranges or at all hot-working temperatures. The stainless steels are particularly difficult to hot-work. The determining of the correct conditions for piercing, rolling and forging of these alloys by experimentation in the mill often results in large losses of these expensive metals. It also is found that the hot-workability limits of many types vary from heat to heat, and hence poor results are obtained on changing to a new heat after a previous one has rolled satisfactorily. To determine the effect on hot-workability of iron to which various elements have been added, it was necessary to devise a method that could be used on small quantities of metal. In such a method, the minimum number of variables should be present, and the procedure should be simple, quick and correlatable with large-scale hot-working operations. Sauveur,9 in the first Henry Marion Howe lecture in 1924, described the effect of carbon on the ductility of steels in torsion near their critical points. He found that carbon increases the plasticity of gamma iron. In the 1930 Campbell Memorial lecture,10 he gives the effect of carbon, chromium, and chromium and nickel on the ductility of steels under 2000°F. in torsion. Ellis11 has studied the malleability of steels at various elevated temperatures by means of a single-blow drop-hammer test. In this test the percentage decrease in height of standard cylinders is taken as a measure of their malleability. He has shown that in the low-alloy steels studied, carbon has a greater effect than nickel, chromium and vanadium. In 1938 the first tests were run on a new quantitative hot-workability test in the laboratories of the Globe Steel Tubes CO. Thum12 mentioned it in 1940. An illustration of the apparatus was published in January 1942.'' The effect of a few alloying elements on the hot-workability of metals was shown in a description of the test in 1944.14 Description of Test Method The method adopted after a trial of several others is a rapid twisting of bars to failure in a furnace. The standard-size bar was chosen as 9/16 in. It is prepared from larger pieces by forging and cold-

Jan 1, 1947

By Harry K. Ihrig

The hot-working of iron and steel is an art dating back to antiquity, but until about 25 years ago, relatively few alloying elements were used, and these were present only in small percentages. With the exception of sulphur, the amounts of other elements in steels did not markedly affect their hot-workability. The references in the literature on the effect of other elements on the hot-workability of steel are usually reports of failure of these steels in forging or rolling.1-8 With the increased use of alloying elements, and their use in larger amounts, it was observed that many of the new steels were red short in certain critical ranges or at all hot-working temperatures. The stainless steels are particularly difficult to hot-work. The determining of the correct conditions for piercing, rolling and forging of these alloys by experimentation in the mill often results in large losses of these expensive metals. It also is found that the hot-workability limits of many types vary from heat to heat, and hence poor results are obtained on changing to a new heat after a previous one has rolled satisfactorily. To determine the effect on hot-workability of iron to which various elements have been added, it was necessary to devise a method that could be used on small quantities of metal. In such a method, the minimum number of variables should be present, and the procedure should be simple, quick and correlatable with large-scale hot-working operations. Sauveur,9 in the first Henry Marion Howe lecture in 1924, described the effect of carbon on the ductility of steels in torsion near their critical points. He found that carbon increases the plasticity of gamma iron. In the 1930 Campbell Memorial lecture,10 he gives the effect of carbon, chromium, and chromium and nickel on the ductility of steels under 2000°F. in torsion. Ellis11 has studied the malleability of steels at various elevated temperatures by means of a single-blow drop-hammer test. In this test the percentage decrease in height of standard cylinders is taken as a measure of their malleability. He has shown that in the low-alloy steels studied, carbon has a greater effect than nickel, chromium and vanadium. In 1938 the first tests were run on a new quantitative hot-workability test in the laboratories of the Globe Steel Tubes CO. Thum12 mentioned it in 1940. An illustration of the apparatus was published in January 1942.'' The effect of a few alloying elements on the hot-workability of metals was shown in a description of the test in 1944.14 Description of Test Method The method adopted after a trial of several others is a rapid twisting of bars to failure in a furnace. The standard-size bar was chosen as 9/16 in. It is prepared from larger pieces by forging and cold-

Jan 1, 1947

By Harry K. Ihrig

Jan 1, 1947

By Harry K. Ihrig

Jan 1, 1947

By George Stern

The purpose of this investigation has been to study one method for making ordinary carbon steel by the powder metallurgy technique. This method con- sists of pressing and subsequently sintering an intimate mixture of iron powder and gaphite in a suitable atmosphere to Produce a steel. Two types of iron Powder have been studied, electrolytic and reduced. The sinkring of mixtures of loose Car-bonyf iron and carbon black for several hours at I000 to 1100 C. (1830' to 2010°F.), followed by forging of the resultant ingots to bars, has been studied by Offermann.' TrailZ has reported on the properties of hydrogen-reduced and electrolytic iron powders, both containing 0.5 per cent carbon. Methods for making steel bodies by powder metallurgy have also been sug- gested by Goetzel13 who recommends the addition of steel powder of well-defined carbon content to pure iron powder, and Volterra,~ who suggests compaction and subsequent sintering of a mixture of steel powder, iron oxide and iron powder. Additional methods for making steel bodies by powder metallurgy have been reported in the literature by Kohering Allen,6 Balke,7 Wulff,8 Boegehold,9 and others.,0,11,12 It is felt that the method of pressing iron powder and graphite, as described herein, lends itself best to production be-Cause of the lubricating action of the

Jan 1, 1946

By George Stern

The purpose of this investigation has been to study one method for making ordinary carbon steel by the powder metallurgy technique. This method con- sists of pressing and subsequently sintering an intimate mixture of iron powder and gaphite in a suitable atmosphere to Produce a steel. Two types of iron Powder have been studied, electrolytic and reduced. The sinkring of mixtures of loose Car-bonyf iron and carbon black for several hours at I000 to 1100 C. (1830' to 2010°F.), followed by forging of the resultant ingots to bars, has been studied by Offermann.' TrailZ has reported on the properties of hydrogen-reduced and electrolytic iron powders, both containing 0.5 per cent carbon. Methods for making steel bodies by powder metallurgy have also been sug- gested by Goetzel13 who recommends the addition of steel powder of well-defined carbon content to pure iron powder, and Volterra,~ who suggests compaction and subsequent sintering of a mixture of steel powder, iron oxide and iron powder. Additional methods for making steel bodies by powder metallurgy have been reported in the literature by Kohering Allen,6 Balke,7 Wulff,8 Boegehold,9 and others.,0,11,12 It is felt that the method of pressing iron powder and graphite, as described herein, lends itself best to production be-Cause of the lubricating action of the

Jan 1, 1946

By Otto H. Henry, J. J. Cordiano

Though powder metallurgy is one of the oldest of metallurgical processes, it is in its infancy as a branch of the modern field of metallurgy. As early as 3000 B.C., the ancients produced implements and weapons of iron by reducing iron ore in a charcoal fire and forging the resultant sponge while still hot into the desired shape. Melting and casting soon superseded the powder metallurgy practice, and it was not until the turn of the twentieth century that powder metallurgy was applied to the commercial manufacture of tungsten lamp filaments. From this beginning, the use of the powder metallurgy process spread" to the manufacture of porous oil-impregnated bearings, cemented carbide tools, contact points, diamond grinding wheels, clutch facings, starter brushes, resin-bonded radio cores, magnets, metallic filters, and other parts. More recently, and particularly during the present war, there has been a definite trend toward the manufacture of machine parts by this process in competition with the more conventional fabricating methods. Notwithstanding these many developments, scientific progress has been slow. While many articles on powder metallurgy have appeared in the press and various publications, there have been too few contributions to our technical societies, with the result that there is a dearth of the type of information necessary for the full development of this science. It is of primary importance that the results of research and development be freely disseminated if powder metallurgy is to realize its fullest potentialities. Purpose of Investigation Excluding the refractory metal field, all commercial powder metallurgical products made by a cold compressing and sintering operation contain voids. These voids can be substantially eliminated by subsequent severe working and heat-treatment, but ' such practice has not proved economical in most applications. By applying heat during the compressing operation, plastic deformation of the powder particles is substantially increased, and the resultant compact or briquette is practically free of voids. However, hot-pressing has many attendant problems, which at present preclude its use in the manufacture of precision parts. The more important of these are to devise: 1. A die steel capable of withstanding high pressures at elevated temperatures. 2. A high-temperature lubricant capable of preventing excessive die wear and welding of the compact to the die walls. 3. A method of retaining a neutral or reducing atmosphere in the compacting zone of the die assembly. 4. A means of ejecting the hot-pressed specimen into a neutral atmosphere until reasonably cold.

Jan 1, 1946

By Otto H. Henry, J. J. Cordiano

Though powder metallurgy is one of the oldest of metallurgical processes, it is in its infancy as a branch of the modern field of metallurgy. As early as 3000 B.C., the ancients produced implements and weapons of iron by reducing iron ore in a charcoal fire and forging the resultant sponge while still hot into the desired shape. Melting and casting soon superseded the powder metallurgy practice, and it was not until the turn of the twentieth century that powder metallurgy was applied to the commercial manufacture of tungsten lamp filaments. From this beginning, the use of the powder metallurgy process spread" to the manufacture of porous oil-impregnated bearings, cemented carbide tools, contact points, diamond grinding wheels, clutch facings, starter brushes, resin-bonded radio cores, magnets, metallic filters, and other parts. More recently, and particularly during the present war, there has been a definite trend toward the manufacture of machine parts by this process in competition with the more conventional fabricating methods. Notwithstanding these many developments, scientific progress has been slow. While many articles on powder metallurgy have appeared in the press and various publications, there have been too few contributions to our technical societies, with the result that there is a dearth of the type of information necessary for the full development of this science. It is of primary importance that the results of research and development be freely disseminated if powder metallurgy is to realize its fullest potentialities. Purpose of Investigation Excluding the refractory metal field, all commercial powder metallurgical products made by a cold compressing and sintering operation contain voids. These voids can be substantially eliminated by subsequent severe working and heat-treatment, but ' such practice has not proved economical in most applications. By applying heat during the compressing operation, plastic deformation of the powder particles is substantially increased, and the resultant compact or briquette is practically free of voids. However, hot-pressing has many attendant problems, which at present preclude its use in the manufacture of precision parts. The more important of these are to devise: 1. A die steel capable of withstanding high pressures at elevated temperatures. 2. A high-temperature lubricant capable of preventing excessive die wear and welding of the compact to the die walls. 3. A method of retaining a neutral or reducing atmosphere in the compacting zone of the die assembly. 4. A means of ejecting the hot-pressed specimen into a neutral atmosphere until reasonably cold.

Jan 1, 1946

Jan 1, 1946

Jan 1, 1946

By Laurence Delisle, Arron Finger

The alloys formed by the addition of nickel to iron by conventional metallurgical procedures show physical properties that differ widely from those of the individual metals. The effect of alloying on the mechanical properties is most pronounced in alloys containing between 15 and 25 per cent nickel. The tensile strength of an alloy containing, for example, 20 per cent nickel and 80 per cent iron (with 0.06 per cent carbon), in an annealed condition, is above 150,000 lb. per sq. in.$ owing to a martensitic type of transformation, as compared with about 50,000 lb. per sq. in. for pure iron in the same condition. The object of this work was to determine whether the same beneficial alloying effect coulcl be obtained in alloys of iron and nickel prepared by powder metallurgy technique. Procedure Bars and pellets for tension and compression tests, respectively, were made. Two groups of specimens were prepared: (I) by cold-pressing the powders and sintering; (2) by cold-pressing the powders, sintering, repressing and resintering. Raw Materials Nickel powder supplied by Metals Disintegrating Co., marked MD-151, was used. A typical analysis of this powder was as follows: sulphur, 0.040 per cent; copper, 0.18; iron, 0.23; manganese, 0.002; magnesium, o.oo15; lead, 0.035; tin> 0.025; silicon, 0.08; chromium, 0.008. Electrolytic iron powder supplied by Plastic Metals Inc. was used. A repre-sentative chemical analysis for impurities other than gases, supplied by the vendor, gave the following results: carbon, 0.005 per cent; manganese, 0.002; silicon, 0.003; phosphorus, 0.001; sulphur, 0.004; nickel, 0.008. The fractions from these powders passing a 325-mesh sieve were reduced in hydrogen at 600°C. for one hour, to clean the sur-faces of the particles. The reduced pow-ders, slightly caked, were ground in a mortar and screened again through a 325-mesh sieve. Mixing The proper proportions of the powders were mixed overnight on rolls, in glass jars fitted with iron-wire baffles to break aggregates of particles that might form. Pressing All specimens were compacted on hy-draulic presses. The pellets were com-pacted in a cylindrical die, 34-in. diameter. The ratio of thickness to the diameter of the pellets was maintained as nearly as possible at 0.9, as specified for standard short compression pieces. The tensile bars were made by compacting 30 grams of powder. Their shape is shown in Fig. I. The compacting pressures for the pellets and the tensile bars were:

Jan 1, 1946

By Arron Finger, Laurence Delisle

The alloys formed by the addition of nickel to iron by conventional metallurgical procedures show physical properties that differ widely from those of the individual metals. The effect of alloying on the mechanical properties is most pronounced in alloys containing between 15 and 25 per cent nickel. The tensile strength of an alloy containing, for example, 20 per cent nickel and 80 per cent iron (with 0.06 per cent carbon), in an annealed condition, is above 150,000 lb. per sq. in.$ owing to a martensitic type of transformation, as compared with about 50,000 lb. per sq. in. for pure iron in the same condition. The object of this work was to determine whether the same beneficial alloying effect coulcl be obtained in alloys of iron and nickel prepared by powder metallurgy technique. Procedure Bars and pellets for tension and compression tests, respectively, were made. Two groups of specimens were prepared: (I) by cold-pressing the powders and sintering; (2) by cold-pressing the powders, sintering, repressing and resintering. Raw Materials Nickel powder supplied by Metals Disintegrating Co., marked MD-151, was used. A typical analysis of this powder was as follows: sulphur, 0.040 per cent; copper, 0.18; iron, 0.23; manganese, 0.002; magnesium, o.oo15; lead, 0.035; tin> 0.025; silicon, 0.08; chromium, 0.008. Electrolytic iron powder supplied by Plastic Metals Inc. was used. A repre-sentative chemical analysis for impurities other than gases, supplied by the vendor, gave the following results: carbon, 0.005 per cent; manganese, 0.002; silicon, 0.003; phosphorus, 0.001; sulphur, 0.004; nickel, 0.008. The fractions from these powders passing a 325-mesh sieve were reduced in hydrogen at 600°C. for one hour, to clean the sur-faces of the particles. The reduced pow-ders, slightly caked, were ground in a mortar and screened again through a 325-mesh sieve. Mixing The proper proportions of the powders were mixed overnight on rolls, in glass jars fitted with iron-wire baffles to break aggregates of particles that might form. Pressing All specimens were compacted on hy-draulic presses. The pellets were com-pacted in a cylindrical die, 34-in. diameter. The ratio of thickness to the diameter of the pellets was maintained as nearly as possible at 0.9, as specified for standard short compression pieces. The tensile bars were made by compacting 30 grams of powder. Their shape is shown in Fig. I. The compacting pressures for the pellets and the tensile bars were:

Jan 1, 1946

By E. I. Larsen, E. F. Swazy, F. R. Hensel

High strength, high-conductivity copper-base alloys have found considerable use in the resistance welding and electrical industry in the form of castings, forgings, or wrought products. There are a number of parts utilized by these industries which would lend themselves to manufacture by powder metallurgical methods provided the required physical and electrical properties are obtainable with such methods. The present paper describes the results of a study of certain copper-base powder metallurgical products susceptible to precipitation hardening. Copper Powders The general types of commercially available copper powders are flake, spherical and electrolytic. Micrographs of these three types are shown in Figs. I, 2 and 3. The difference in particle shape is pronounced and obvious. The type of powder used is determined, or at least indicated, by the final properties desired in the finished article. The type of powder employed during the present investigation was electrolytic powder shown in Fig. 3, and was chosen because of its particular adaptability to the work described in this Paper. The screen and chemical analyses of this powder are shown in Table I. In the preparation of compacts of high electrical conductivity, the purity of the copper powder is of importance in addition to other factors, such as density and the state of internal stresses. These variables were studied briefly by pressing a number of compacts to various pressed densities, sintering them for one hour in hydrogen at 975OC and repressing. The size of the finished compacts was 1/4, by % by 8 in. The time interval from the application to the termination of pressure was approximately 20 sec. Some of the compacts were annealed before testing. The results are listed in Figs. 4 to 8, inclusive. In Fig. 4 the curves of pressed density vs. compacting pressure, and sintered density versus compacting pressure show the typical direct relationship of pressure and density. Compacting pressures exceeding about 30 tons per sq. in. result fiequently in expansion during sintering for the type of powder used. Fig. 5 indicates that variations in the initial pressed density within the range of about 5 to 6 grams per c, c., affect only slightly the pressure required to obtain a

Jan 1, 1946

By E. I. Larsen, E. F. Swazy, F. R. Hensel

High strength, high-conductivity copper-base alloys have found considerable use in the resistance welding and electrical industry in the form of castings, forgings, or wrought products. There are a number of parts utilized by these industries which would lend themselves to manufacture by powder metallurgical methods provided the required physical and electrical properties are obtainable with such methods. The present paper describes the results of a study of certain copper-base powder metallurgical products susceptible to precipitation hardening. Copper Powders The general types of commercially available copper powders are flake, spherical and electrolytic. Micrographs of these three types are shown in Figs. I, 2 and 3. The difference in particle shape is pronounced and obvious. The type of powder used is determined, or at least indicated, by the final properties desired in the finished article. The type of powder employed during the present investigation was electrolytic powder shown in Fig. 3, and was chosen because of its particular adaptability to the work described in this Paper. The screen and chemical analyses of this powder are shown in Table I. In the preparation of compacts of high electrical conductivity, the purity of the copper powder is of importance in addition to other factors, such as density and the state of internal stresses. These variables were studied briefly by pressing a number of compacts to various pressed densities, sintering them for one hour in hydrogen at 975OC and repressing. The size of the finished compacts was 1/4, by % by 8 in. The time interval from the application to the termination of pressure was approximately 20 sec. Some of the compacts were annealed before testing. The results are listed in Figs. 4 to 8, inclusive. In Fig. 4 the curves of pressed density vs. compacting pressure, and sintered density versus compacting pressure show the typical direct relationship of pressure and density. Compacting pressures exceeding about 30 tons per sq. in. result fiequently in expansion during sintering for the type of powder used. Fig. 5 indicates that variations in the initial pressed density within the range of about 5 to 6 grams per c, c., affect only slightly the pressure required to obtain a

Jan 1, 1946

By Claus G. Goetzel

Pressing of powdered metal parts is best done in the direction of the shortest extension of the piece, to avoid too great a loss of pressing force through internal iriction. As long as curved surfaces, re-cessej, or offsets occur only parallel to this shortest axis of pressure, no special difficulties arise: the cross sections, perpendicular to the pressure, do not vary, nor does the shape of the parts change during compression except for a gradually reduced thickness (Fig. IA). The problem becomes more dificult, however, when the curved surfaces or recesses are perpendicular to the shortest axis of the part (Fig. IB) Two processes for molding uniformly dense parts with complicated shapes from powdered metals are described in detail in this paper. Both can be employed successfully by those trained in the art. The first refers to curved parts; the second is especially adapted to parts having one or more recesses or steps. Both methods, as set forth here, are applied under the condition that presents the more difficult problem. For clarity, before description of the two practical methods, the variable factors in molding powdered metal parts will be reviewed, then an idealized procedure will be considered briefly. Variable Factors in Molding Powdered Metal Parts Compression Ratio Compression ratio is defined as the proportion of the final relative density of the compact to the apparent density of the powder. For iron powder of an apparent density of 3.0, for example, a compression ratio of 2 1/2:1 would be required to produce a compressed compact of 7.5 density; whereas for another iron powder having an apparent density of only 1.5, a compression ratio of 5:1 would be required to produce the same density. The lower the powder's apparent density, the greater must be the compression ratio for pressing compacts of high density.

Jan 1, 1946