By J. R. Long, E. T. Hayes, R. S. Dean, F. S. Wartman

The production of titanium in I5-lb. lots and with a purity sufficient to be consolidated into ductile metal, as described in a previous paper,' has provided adequate material for a study of the physical properties of titanium and a more thorough examination of its working qualities. Data on the physical properties reported in that paper were obtained on metal fabricated by a fixed procedure, standardized for the purpose of control of the reduction, and are representative only of material fabricated under those conditions. There are many possible variables in the working schedule, which will have significant effects on the properties of the finished material; and since the previous working methods were not necessarily the best, an investigation of the fabrication of titanium by other methods was undertaken. In this work the consolidation of the powder by pressing and sintering was conducted essentially as outlined in the report cited' and all efforts were centered on fabrication methods for those powders and the proper- ties produced by them. Hardness, density, microstructure, and tensile properties were determined at various stages in the working and annealing; and resistivity measurements were made on a few bars and drawn wire. Consolidation of the PowdeR The screen analysis of the available titanium powder is given in Table I. No attempt was made to alter the size distribution from that noted because this powder, although coarse by normal powder-metallurgy standards, produced acceptable compacts suitable for the present work. Because of their large specific surface, finer powders are more contaminated by oxygen and produce harder compacts, which are difficult to work. The powder as produced is soft, compresses in a normal fashion, and exhibits very little tendency to adhere to the die surfaces. Unlike aluminum and magnesium powders, it can be readily pressed without the use of die lubricants. When compacted at 50 tons per

Jan 1, 1946

By Bruce W. Gonser, Robert I. Jaffee

Recent work by the authors1 established the constitutional diagram of the gold-germanium system. Of particular interest in the simple euctectiferous system was the eutectic alloy at 12 per cent Ge, which melted at the very low temperature of 356°C and had an unusually fine eutectic structure. It was of interest to investigate the effect of third components on the melting point, microstructure, and strength of this alloy, and in this work the effect of copper is discussed rather completely, with less complete data on the effects of silver, platinum, nickel, and zinc. No reference in the literature has been found on ternary systems with gold-germanium. Materials and Alloying -4s in the work on the binary system, gold-germanium, the germanium used in this investigation was the cyanide-reduced, 99.9 per cent product, produced by the Eagle-Picher Co. Fine gold sheet from Handy and Harmon, pure platinum sheet from the American Platinum Works, copper magnet wire from Anaconda, nickel wire assaying 99.6 per cent Ni. and electrolytic zinc were used for alloying. To make the alloys, charges of the pure metals were put in a graphite crucible and melted in an atmosphere of pure hydrogen. The temperature was brought up to about I050 C, and the metal allowed to freeze in the crucible. Except with alloys containing zinc, melting losses were consistently less than a few milligrams. When zinc was a component, weight losses up to half the weight of the zinc present were incurred, and the alloy compositions were calculated by assuming the entire weight loss to be that of zinc. In all other cases the composition of the alloys could safely be taken as that of the charge. The ingots, as solidified, were segregated, the heavier primary phases being at the bottom and sides of the ingots and the lighter primary phases at the top, but by sectioning the entire ingot vertically for microscopic examination, this factor could be evaluated. Ingots for microscopic examination weighed one gram, and those for thermal analysis weighed three grams. Thermal Analysis In this work, the eutectic line composition and thermal arrests were desired, and, after microscopic exploration had established the position of the eutectic line at a given percentage of the third component, a thermal analysis was run at that composition. The method of thermal analysis used in the work on the binary Au-Ge system,' a method particularly well suited for a small quantity of material, was used in this work. Clearly defined arrests were obtained, although with some alloys containing platinum

Jan 1, 1946

By Robert I. Jaffee, Bruce W. Gonser

Recent work by the authors1 established the constitutional diagram of the gold-germanium system. Of particular interest in the simple euctectiferous system was the eutectic alloy at 12 per cent Ge, which melted at the very low temperature of 356°C and had an unusually fine eutectic structure. It was of interest to investigate the effect of third components on the melting point, microstructure, and strength of this alloy, and in this work the effect of copper is discussed rather completely, with less complete data on the effects of silver, platinum, nickel, and zinc. No reference in the literature has been found on ternary systems with gold-germanium. Materials and Alloying -4s in the work on the binary system, gold-germanium, the germanium used in this investigation was the cyanide-reduced, 99.9 per cent product, produced by the Eagle-Picher Co. Fine gold sheet from Handy and Harmon, pure platinum sheet from the American Platinum Works, copper magnet wire from Anaconda, nickel wire assaying 99.6 per cent Ni. and electrolytic zinc were used for alloying. To make the alloys, charges of the pure metals were put in a graphite crucible and melted in an atmosphere of pure hydrogen. The temperature was brought up to about I050 C, and the metal allowed to freeze in the crucible. Except with alloys containing zinc, melting losses were consistently less than a few milligrams. When zinc was a component, weight losses up to half the weight of the zinc present were incurred, and the alloy compositions were calculated by assuming the entire weight loss to be that of zinc. In all other cases the composition of the alloys could safely be taken as that of the charge. The ingots, as solidified, were segregated, the heavier primary phases being at the bottom and sides of the ingots and the lighter primary phases at the top, but by sectioning the entire ingot vertically for microscopic examination, this factor could be evaluated. Ingots for microscopic examination weighed one gram, and those for thermal analysis weighed three grams. Thermal Analysis In this work, the eutectic line composition and thermal arrests were desired, and, after microscopic exploration had established the position of the eutectic line at a given percentage of the third component, a thermal analysis was run at that composition. The method of thermal analysis used in the work on the binary Au-Ge system,' a method particularly well suited for a small quantity of material, was used in this work. Clearly defined arrests were obtained, although with some alloys containing platinum

Jan 1, 1946

By E. L. Anderson, J. R. Long, R. S. Dean, F. S. Wartman

Titanium has been estimated to comprise about 0.65 per cent of the earth's crust and ranks fourth in abundance among the metallic elements suitable for engineering uses. In spite of this, applications of titanium for structural purposes have not as yet been developed. Its commercial exploitation has been largely confined to the chemical industries and the production of paints and pigments; no doubt because of the difficulties that lie in the way of preparing the pure ductile metal. Published reports, however, indicate that ductile titanium can be prepared and possesses some unique properties. This, together with the occurrence in this country of several important titaniferous deposits, has led the Bureau of Mines to investigate processes for the production of metallic titanium, methods required for its fabrication, and the properties that may be produced in this interesting metal. Methods of Preparing Metallic Titanium Many early investigators claimed to have isolated metallic titanium; but in the light of present knowledge, it seems that they really had produced various mixtures of carbides and nitrides that have a metallic appearance but are brittle, hard, and unworkable. The first metallic titanium pure enough to be malleable when cold was produced by Hunter1 in the early part of the twentieth century. Kroll,~ van Arkel,~ and Fast,4 subsequently confirmed the facts that pure titanium is a. ductile metal and that small amounts of impurities were responsible for previous reports of brittleness. When heated, titanium reacts chemically with various gases, such as hydrogen, oxygen and nitrogen; if the volume of gas thus absorbed is too great, the metal becomes brittle and unworkable. The principal difficulty in making ductile titanium is prevention of such contamination, and the success of a given process may be judged by the completeness with which it solves this difficulty in a practical manner. Of the gases mentioned, hydrogen is the least objectionable, since its absorption by the metal is completely reversible and, although dimensional changes occur and absorption of hydrogen embrittles the metal, the gas may be removed readily by heating in a high vacuum for a short time. On the other hand, the absorption of oxygen or nitrogen results in the formation of permanent solid solutions of the oxide and nitride, which cannot be decomposed by the strongest reducing agentsz with sufticient completeness to restore the inherent ductility of the metal. Because of

Jan 1, 1946

By J. R. Long, E. L. Anderson, R. S. Dean, F. S. Wartman

Titanium has been estimated to comprise about 0.65 per cent of the earth's crust and ranks fourth in abundance among the metallic elements suitable for engineering uses. In spite of this, applications of titanium for structural purposes have not as yet been developed. Its commercial exploitation has been largely confined to the chemical industries and the production of paints and pigments; no doubt because of the difficulties that lie in the way of preparing the pure ductile metal. Published reports, however, indicate that ductile titanium can be prepared and possesses some unique properties. This, together with the occurrence in this country of several important titaniferous deposits, has led the Bureau of Mines to investigate processes for the production of metallic titanium, methods required for its fabrication, and the properties that may be produced in this interesting metal. Methods of Preparing Metallic Titanium Many early investigators claimed to have isolated metallic titanium; but in the light of present knowledge, it seems that they really had produced various mixtures of carbides and nitrides that have a metallic appearance but are brittle, hard, and unworkable. The first metallic titanium pure enough to be malleable when cold was produced by Hunter1 in the early part of the twentieth century. Kroll,~ van Arkel,~ and Fast,4 subsequently confirmed the facts that pure titanium is a. ductile metal and that small amounts of impurities were responsible for previous reports of brittleness. When heated, titanium reacts chemically with various gases, such as hydrogen, oxygen and nitrogen; if the volume of gas thus absorbed is too great, the metal becomes brittle and unworkable. The principal difficulty in making ductile titanium is prevention of such contamination, and the success of a given process may be judged by the completeness with which it solves this difficulty in a practical manner. Of the gases mentioned, hydrogen is the least objectionable, since its absorption by the metal is completely reversible and, although dimensional changes occur and absorption of hydrogen embrittles the metal, the gas may be removed readily by heating in a high vacuum for a short time. On the other hand, the absorption of oxygen or nitrogen results in the formation of permanent solid solutions of the oxide and nitride, which cannot be decomposed by the strongest reducing agentsz with sufticient completeness to restore the inherent ductility of the metal. Because of

Jan 1, 1946

By F. R. Hensel

PuRe silver and silver-lead alloys have been studied as to their suitability for bearing~.' A review of the properties of thallium and the silver-thallium constitutional diagram was made by the author to analyze the possibilities of silver-thallium compositions for antifriction materia1s. t The silver-rich end of the diagram as reported in the literatureg-" was found to be sketchy and it was necessary to carry out corisiderable experimental work to arrive at definite conclusions. Some of the results of this work are reported in this paper. Test Materials In the beginning of the work, only fused alloys were investigated. Later, research Table i.—Composition of Fused Silver-thallium Alloys Tested for Antifriction Properties Percentage Alloy No. of Thallium 1533...................... 0.48 1534.................... 1.06 a31 HT................... 2.04 231....................... 2.10 232 HT................... 3.83 Balance 232....................... 4.07 Silver 233 HT................... 5.86 a33....................... 6.38 a34....................... 9.84 a34 HT................... 10.07 was carried out on electroplating methods and diffusion processes. In preparing the fused alloyst care was taken to exhaust the toxic fumes caused by the thaillium content. The compositions of the series of fused alloys are listed in Table I. The silver-thallium alloys were melted in clay-graphite crucibles and cast into preheated steel molds of 3/4-in, diameter. In the cast condition, they showed a cored structure, as indicated by the micrographs of Figs. I to 3. The etching reagent used was a mixture of 2 grams K2Cr207, 8 C.C. H2S04, and IOO C.C. H20. The cored structure is unsatisfactory for the type of corrosion resistance required for bearing applications, and homogenizing experiments were carried out at various temperatures, the results of which are shown in Figs. 4 through 8. The alloys with a lower thallium concentration, which were heated for 2 hr. at 525°C show an almost completely homogenized solid solution type of structure. With higher thallium concentration, the homogenizing temperature was dropped to 475OC. to eliminate the formation of a liquid phase. It is evident that heating for 2 hr. at this temperature did not iesiilt iii complete elimination of the cored structure. As would be expected, cold-working of the cast structure is an expedient in establishing equilibrium conditions. The fine homogeneous grain structure shown in Fig. 7 corresponds to the cold-worked area under the Rockwell ball penetration when the hardness was taken before heat-treatment. A detailed structural study was made on a cast silver-thallium alloy containing 3.67 per cent thallium. Three micrographs (Figs. 9, 10 and 11) show the transition

Jan 1, 1946

By F. R. Hensel

PuRe silver and silver-lead alloys have been studied as to their suitability for bearing~.' A review of the properties of thallium and the silver-thallium constitutional diagram was made by the author to analyze the possibilities of silver-thallium compositions for antifriction materia1s. t The silver-rich end of the diagram as reported in the literatureg-" was found to be sketchy and it was necessary to carry out corisiderable experimental work to arrive at definite conclusions. Some of the results of this work are reported in this paper. Test Materials In the beginning of the work, only fused alloys were investigated. Later, research Table i.—Composition of Fused Silver-thallium Alloys Tested for Antifriction Properties Percentage Alloy No. of Thallium 1533...................... 0.48 1534.................... 1.06 a31 HT................... 2.04 231....................... 2.10 232 HT................... 3.83 Balance 232....................... 4.07 Silver 233 HT................... 5.86 a33....................... 6.38 a34....................... 9.84 a34 HT................... 10.07 was carried out on electroplating methods and diffusion processes. In preparing the fused alloyst care was taken to exhaust the toxic fumes caused by the thaillium content. The compositions of the series of fused alloys are listed in Table I. The silver-thallium alloys were melted in clay-graphite crucibles and cast into preheated steel molds of 3/4-in, diameter. In the cast condition, they showed a cored structure, as indicated by the micrographs of Figs. I to 3. The etching reagent used was a mixture of 2 grams K2Cr207, 8 C.C. H2S04, and IOO C.C. H20. The cored structure is unsatisfactory for the type of corrosion resistance required for bearing applications, and homogenizing experiments were carried out at various temperatures, the results of which are shown in Figs. 4 through 8. The alloys with a lower thallium concentration, which were heated for 2 hr. at 525°C show an almost completely homogenized solid solution type of structure. With higher thallium concentration, the homogenizing temperature was dropped to 475OC. to eliminate the formation of a liquid phase. It is evident that heating for 2 hr. at this temperature did not iesiilt iii complete elimination of the cored structure. As would be expected, cold-working of the cast structure is an expedient in establishing equilibrium conditions. The fine homogeneous grain structure shown in Fig. 7 corresponds to the cold-worked area under the Rockwell ball penetration when the hardness was taken before heat-treatment. A detailed structural study was made on a cast silver-thallium alloy containing 3.67 per cent thallium. Three micrographs (Figs. 9, 10 and 11) show the transition

Jan 1, 1946

By H. C. Lukens, E. V. Potter

The volume of hydrogen released from electrolytic manganese at various temperatures and pressures was determined in a previous investigation1 as part of a study to determine the most practical procedure for removing the hydrogen from electrolytic manganese metal. No attempt was made to determine the absolute volume of gas in the metal at any temperature and pressure; the volume of gas released showed only the variation in solubility with temperature and pressure. The results were very similar to those obtained by Sieverts and Moritz.² Both sets of data show a minimum solubility between 500' and 700°C., but they differ in certain respects; on cooling from 500°C., our results showed an increase in solubility of about 7 C.C. as compared with an increase of 34 C.C. per 100 grams shown by Sieverts. Furthermore, the transition temperatures, as indicated by sharp breaks in the solubility curves, did not agree well with Sieverts' data. This information was of secondary importance in the earlier investigations, and the solubility at low temperatures and the transition temperatures were subject to considerable error. Therefore, a subsequent investigation, reported in this paper, was made to measure the absolute solubility at temperatures from room temperature through the melting point and make more accurate observations of the transition temperatures. Apparatus and Method The apparatus and method were essentially the same as those described in the previous work,' as shown in Fig. I. At high temperatures, the small tube containing the thermocouple in the sample container A frequently broke off, so for some of this work the thermocouple was placed outside the sample container and protected by a quartz tube of about the same wall thickness as the sample container. No significant difference was found in the transition temperatures obtained in the two ways. The automatic temperature controller was used in these tests in the regions where there was little change in solubility with temperature. In the neighborhood of the transition points a continuously variable autotransformer was used instead of the automatic controller, and the power input to the furnace was adjusted so that the temperature increased or decreased at a very slow, uniform rate through the transition range. This procedure was followed because the temperature oscillations produced by the controller were too great compared with the transition range, and the transi- . tion points determined under such conditions were less accurate. Absolute Solubility Procedure ad Results The absolute solubility of hydrogen in manganese could be determined most

Jan 1, 1947

By E. V. Potter, H. C. Lukens

The volume of hydrogen released from electrolytic manganese at various temperatures and pressures was determined in a previous investigation1 as part of a study to determine the most practical procedure for removing the hydrogen from electrolytic manganese metal. No attempt was made to determine the absolute volume of gas in the metal at any temperature and pressure; the volume of gas released showed only the variation in solubility with temperature and pressure. The results were very similar to those obtained by Sieverts and Moritz.² Both sets of data show a minimum solubility between 500' and 700°C., but they differ in certain respects; on cooling from 500°C., our results showed an increase in solubility of about 7 C.C. as compared with an increase of 34 C.C. per 100 grams shown by Sieverts. Furthermore, the transition temperatures, as indicated by sharp breaks in the solubility curves, did not agree well with Sieverts' data. This information was of secondary importance in the earlier investigations, and the solubility at low temperatures and the transition temperatures were subject to considerable error. Therefore, a subsequent investigation, reported in this paper, was made to measure the absolute solubility at temperatures from room temperature through the melting point and make more accurate observations of the transition temperatures. Apparatus and Method The apparatus and method were essentially the same as those described in the previous work,' as shown in Fig. I. At high temperatures, the small tube containing the thermocouple in the sample container A frequently broke off, so for some of this work the thermocouple was placed outside the sample container and protected by a quartz tube of about the same wall thickness as the sample container. No significant difference was found in the transition temperatures obtained in the two ways. The automatic temperature controller was used in these tests in the regions where there was little change in solubility with temperature. In the neighborhood of the transition points a continuously variable autotransformer was used instead of the automatic controller, and the power input to the furnace was adjusted so that the temperature increased or decreased at a very slow, uniform rate through the transition range. This procedure was followed because the temperature oscillations produced by the controller were too great compared with the transition range, and the transi- . tion points determined under such conditions were less accurate. Absolute Solubility Procedure ad Results The absolute solubility of hydrogen in manganese could be determined most

Jan 1, 1947

By J. R. Long, E. T. Hayes, D. C. Root, R. S. Dean

The U. S. Bureau of Mines has recently reported on the development of a process for preparing pure ductile titanium in substantial quantities1 and on the physical properties that may be attained in the metal, when consolidated by powder metallurgy methods and fabricated by certain hot and cold-working procedures.2 The high physical properties (Table I), combined with excellent corrosion resistance and light weight, will lead no doubt to appropriatc applications of the metal. In any application, methods of joining will be of considerable importance. The relatively high activity of the metal toward the common gases raises the question of weldability and conditions that might be required for successful welding. Since hydrogen, oxygen, and nitrogen embrittle the metal, it should be protected from these gases at elevated temperatures. This was demonstrated by a few preliminary trials of arc, gas, and resistance welding. In these trials only the resistance method proved to be immediately- applicable. While atomic: hydrogen welding of titanium may be successful in some instances, a considerable amount of development work will be required to prove its worth. In addition, it would be suited only to small assemblies that could be heated subsequently in a high vacuum to remove embrittling hydrogen. Heli-are methods likewise would be limited to small assemblies, which could be completely protected by a helium atmosphere. It was quite apparent that titanium required more protection than was afforded by the normal flow of helium gas used for welding magnesium and aluminum. The hot metal is attacked by oxygen and nitrogen, and the rapid diffusion of the oxide into the metal prevents the formation of a protective coating and requires the helium atmosphere to be maintained until the weld has cooled nearly to room temperature. The preliminary work indicated that titanium could be successfully spot-welded without deterioration of the metal and that the microstructures of the welds were normal, exhibiting good bonding, and no oxidation. The high resistivity of titanium (53 microhms per cu. cm.) suggested that it would behave somewhat like stainless steel and allow considerable latitude in the several welding variables. The results reported here are intended to give a general picture of the effects of varying welding current, welding time, and tip pressure on single spot welds made on several different thicknesses of titanium sheet. The work was undertaken to demonstrate the feasibility of welding titanium rather than as an exhaustive study of spot welding. There are, therefore, a number of factors that will require further investigation to establish the specific controls required for actual applications.

Jan 1, 1947

By J. R. Long, R. S. Dean, D. C. Root, E. T. Hayes

The U. S. Bureau of Mines has recently reported on the development of a process for preparing pure ductile titanium in substantial quantities1 and on the physical properties that may be attained in the metal, when consolidated by powder metallurgy methods and fabricated by certain hot and cold-working procedures.2 The high physical properties (Table I), combined with excellent corrosion resistance and light weight, will lead no doubt to appropriatc applications of the metal. In any application, methods of joining will be of considerable importance. The relatively high activity of the metal toward the common gases raises the question of weldability and conditions that might be required for successful welding. Since hydrogen, oxygen, and nitrogen embrittle the metal, it should be protected from these gases at elevated temperatures. This was demonstrated by a few preliminary trials of arc, gas, and resistance welding. In these trials only the resistance method proved to be immediately- applicable. While atomic: hydrogen welding of titanium may be successful in some instances, a considerable amount of development work will be required to prove its worth. In addition, it would be suited only to small assemblies that could be heated subsequently in a high vacuum to remove embrittling hydrogen. Heli-are methods likewise would be limited to small assemblies, which could be completely protected by a helium atmosphere. It was quite apparent that titanium required more protection than was afforded by the normal flow of helium gas used for welding magnesium and aluminum. The hot metal is attacked by oxygen and nitrogen, and the rapid diffusion of the oxide into the metal prevents the formation of a protective coating and requires the helium atmosphere to be maintained until the weld has cooled nearly to room temperature. The preliminary work indicated that titanium could be successfully spot-welded without deterioration of the metal and that the microstructures of the welds were normal, exhibiting good bonding, and no oxidation. The high resistivity of titanium (53 microhms per cu. cm.) suggested that it would behave somewhat like stainless steel and allow considerable latitude in the several welding variables. The results reported here are intended to give a general picture of the effects of varying welding current, welding time, and tip pressure on single spot welds made on several different thicknesses of titanium sheet. The work was undertaken to demonstrate the feasibility of welding titanium rather than as an exhaustive study of spot welding. There are, therefore, a number of factors that will require further investigation to establish the specific controls required for actual applications.

Jan 1, 1947

By Otto H. Henry, Edward L. Badwick

Up to the present time, according to Hansenl and Haughton,² the constitution of the bismuth-indium system has not yet been published. The generally accepted value for the melting point of indium, as listed in most scientific journals and textbooks, is 155°C. Recently, however, H. M. Davis3 has determined a new melting point for indium of 157.3²C O.l°C. Since bismuth has been used in preponderance as an alloying element in the majority of low-melting alloys, and indium has been used with considerable success in lowering the melting points of low-melting alloys, 4,6 an interest has been developed in the application of these two metals, making a complete knowledge of the constitution of its alloys desirable. In this investigation, the melting point of indium reported by H. M. Davis has been found to be substantially correct. A value of 157. ²°C ± O.5°C was determined. The two eutectic compositions have been placed at 34 and 50 pct bismuth with their respective eutectic temperatures as 72.4°C ± 0.5°C and 90°C ± 0.5°C. The bismuth-indium phase diagram has been determined by thermal and microscopic analysis and is shown in Fig I. Thermal Analysis Granulated bismuth and indium shot, having a guaranteed purity of 99.99 and 99.95 pct, respectively, were melted in a carbon crucible by means of a laboratory heater. To minimize oxidation of the alloys, a heavy mineral oil (Nujol) having a high- flash point was used. A platinum-platinum rhodium thermocouple of fine wire encased in a thin-walled Pyrex glass tube, about 1/8 in. in diameter, was connected to a type K potentiometer for temperature measurements. The thermocouple was calibrated against the melting points of tin, bismuth, and the silver-copper eutectic and the boiling point of water. Since the temperature readings could be reproduced to 0.²°Cl and the accuracy of the temperature standards in this range is slightly better than 0.5°C, it scems reasonable to assume that the temperature readings are reliable to approximately 0.5°C. The cooling rate could be controlled by varying the amount of insulation surrounding the crucible. Three or four layers of asbestos paper, 1/16 in. thick, sufficed to give a cooling rate of from I° to ²°C per minute. Undercooling was slightly noticeable. This condition was minimized by vigorous stirring, since the advantage of using slower rates was too small to justify the greater expenditure

Jan 1, 1947

By Otto H. Henry, Edward L. Badwick

Up to the present time, according to Hansenl and Haughton,² the constitution of the bismuth-indium system has not yet been published. The generally accepted value for the melting point of indium, as listed in most scientific journals and textbooks, is 155°C. Recently, however, H. M. Davis3 has determined a new melting point for indium of 157.3²C O.l°C. Since bismuth has been used in preponderance as an alloying element in the majority of low-melting alloys, and indium has been used with considerable success in lowering the melting points of low-melting alloys, 4,6 an interest has been developed in the application of these two metals, making a complete knowledge of the constitution of its alloys desirable. In this investigation, the melting point of indium reported by H. M. Davis has been found to be substantially correct. A value of 157. ²°C ± O.5°C was determined. The two eutectic compositions have been placed at 34 and 50 pct bismuth with their respective eutectic temperatures as 72.4°C ± 0.5°C and 90°C ± 0.5°C. The bismuth-indium phase diagram has been determined by thermal and microscopic analysis and is shown in Fig I. Thermal Analysis Granulated bismuth and indium shot, having a guaranteed purity of 99.99 and 99.95 pct, respectively, were melted in a carbon crucible by means of a laboratory heater. To minimize oxidation of the alloys, a heavy mineral oil (Nujol) having a high- flash point was used. A platinum-platinum rhodium thermocouple of fine wire encased in a thin-walled Pyrex glass tube, about 1/8 in. in diameter, was connected to a type K potentiometer for temperature measurements. The thermocouple was calibrated against the melting points of tin, bismuth, and the silver-copper eutectic and the boiling point of water. Since the temperature readings could be reproduced to 0.²°Cl and the accuracy of the temperature standards in this range is slightly better than 0.5°C, it scems reasonable to assume that the temperature readings are reliable to approximately 0.5°C. The cooling rate could be controlled by varying the amount of insulation surrounding the crucible. Three or four layers of asbestos paper, 1/16 in. thick, sufficed to give a cooling rate of from I° to ²°C per minute. Undercooling was slightly noticeable. This condition was minimized by vigorous stirring, since the advantage of using slower rates was too small to justify the greater expenditure

Jan 1, 1947

By B. D. Cullity

Gold and beryllium form an intermediate phase composed of the two metals in equal atomic proportions and having the formula AuBe. According to Winkler,' this phase probably exists in two modifications: beta, stable below about 600°C, and alpha, stable between 600°C and the melting point, about 740°C. Only the low-temperature beta form will be considered in this paper. Experimental Procedure The gold used had a fineness of 999.75 to 999.85, balance mainly silver, and the beryllium purity was better than 99.8 pct. AuBe was prepared by melting the constituents in a beryllia crucible in an evacuated induction furnace. After melting and thorough mixing, the alloy was allowed to solidify in the crucible. No difficulty was encountered in obtaining a homogeneous ingot. Both chemical analysis and microscopic examination of the ingot showed that the alloy was essentially one phase, containing 50 at. pct gold. The alloy was quite brittle and powder samples could easily be prepared by grinding in an agate mortar. The X-ray diffraction patterns were made with CuK-alpha radiation in a Debye-Scherrer powder camera 57.3 mm in diameter. The film was placed unsym-metrically in the camera in order to afford a basis for film-shrinkage corrections. A sample homogenized at 500°C gave the same diffraction pattern as a sample taken from the as-melted ingot. General Results The diffraction pattern of AuBe was readily indexed on the basis of a simple cubic lattice with ao = 4.659 + 0.001kX. If the unit cell is assumed to contain four AuBe "molecules," the calculated X-ray density is 13.46 grams per cc as compared with the measured density of 13.55 gm per cc. The only missing reflections in the diffraction pattern are (100) and (220) (see Table I). Since these missing reflections are not those characteristic of body or face centering, the lattice of AuBe must be simple cubic. To locate the positions of the atoms within the unit cell, two possibilities had to be considered: I. The structure was disordered and there were eight positions to be filled by an LCaverage" gold-beryllium atom. That the structure was disordered seemed unlikely since the lattice parameter did not vary with composition in alloys containing sornewhat more and somewhat less than so at' pet gold, indicating a fixed composition for AuBe.

Jan 1, 1947

By B. D. Cullity

Gold and beryllium form an intermediate phase composed of the two metals in equal atomic proportions and having the formula AuBe. According to Winkler,' this phase probably exists in two modifications: beta, stable below about 600°C, and alpha, stable between 600°C and the melting point, about 740°C. Only the low-temperature beta form will be considered in this paper. Experimental Procedure The gold used had a fineness of 999.75 to 999.85, balance mainly silver, and the beryllium purity was better than 99.8 pct. AuBe was prepared by melting the constituents in a beryllia crucible in an evacuated induction furnace. After melting and thorough mixing, the alloy was allowed to solidify in the crucible. No difficulty was encountered in obtaining a homogeneous ingot. Both chemical analysis and microscopic examination of the ingot showed that the alloy was essentially one phase, containing 50 at. pct gold. The alloy was quite brittle and powder samples could easily be prepared by grinding in an agate mortar. The X-ray diffraction patterns were made with CuK-alpha radiation in a Debye-Scherrer powder camera 57.3 mm in diameter. The film was placed unsym-metrically in the camera in order to afford a basis for film-shrinkage corrections. A sample homogenized at 500°C gave the same diffraction pattern as a sample taken from the as-melted ingot. General Results The diffraction pattern of AuBe was readily indexed on the basis of a simple cubic lattice with ao = 4.659 + 0.001kX. If the unit cell is assumed to contain four AuBe "molecules," the calculated X-ray density is 13.46 grams per cc as compared with the measured density of 13.55 gm per cc. The only missing reflections in the diffraction pattern are (100) and (220) (see Table I). Since these missing reflections are not those characteristic of body or face centering, the lattice of AuBe must be simple cubic. To locate the positions of the atoms within the unit cell, two possibilities had to be considered: I. The structure was disordered and there were eight positions to be filled by an LCaverage" gold-beryllium atom. That the structure was disordered seemed unlikely since the lattice parameter did not vary with composition in alloys containing sornewhat more and somewhat less than so at' pet gold, indicating a fixed composition for AuBe.

Jan 1, 1947

By John L. Ham, Robert M. Parke

The melting point of molybdenum is 2625° + 50°C. Heretofore the metal has been considered too refractory to be melted in commercial quantities; hence, it has been formed into rod, wire, and sheet by the methods of powder metallurgy, wherein the temperatures do not exceed 90 per cent of the melting temperature. The manipulation of liquid metals at temperatures of about 2000°C. and above presents some difficult problems in heat transfer, in purification, and in container materials. For metals melting at such high temperatures, it is generally regarded as expedient to circumvent the more common melting and casting process by resorting to powder metallurgy. This circumvention is not accomplished without some penalties, the more notable of which are the relatively high cost of the powder metallurgy method and particularly the size limitations of its product. In an effort to overcome the inherent disadvantages of the powder metallurgy method, especially in respect to the limit of size, a project was begun in 1943 at the Climax Molybdenum Co. laboratory to develop a method of melting and casting molybdenum capable of producing larger bodies of molybdenum than were then obtainable. Later, from Feb. I, 1944, to Aug. 31, 1945, the project was under the supervision of the National Research Committee, Division One. In peacetime, too, there are needs for molybdenurn, which make consideration of another process desirable; for example, large parts for heat engines generally, the omnipresent demand for metal of higher quality and lower cost, and the development of molybdenum-base alloys. This paper describes methods for melting and casting molybdenum, with details of the special process needed to make molybdenum castings ductile, and reports some of the properties of what may be regarded as a new, or at least modified, form of the metal. First Process for Melting and Casting Molybdenum The maintenance of a temperature greater than 2625°C. in a 'pace large enough to melt several pounds of molybdenum may involve the loss of heat at a Very considerable rate. For melting molybdenum, therefore, the source of heat must be of high potential and of fairly high power. Evidently, also, the source of heat must not impair the purity of the product. The electric arc operating in vacuum appeared to meet these requirements and was accordingly the first choice as a source of energy. A number of arc devices for melting molybdenum were examined, and several were tried. In the first experiment, a 20-kw., 60-cycle-per-second alternating-current arc was operated between two horizontal and opposed electrodes of molybdenum- In this arrangement the falling droplets of molybdenum solidified below the arc in an irregular mass. This experiment did not produce a useful casting, but the data obtained indicated that

Jan 1, 1947

By John L. Ham, Robert M. Parke

The melting point of molybdenum is 2625° + 50°C. Heretofore the metal has been considered too refractory to be melted in commercial quantities; hence, it has been formed into rod, wire, and sheet by the methods of powder metallurgy, wherein the temperatures do not exceed 90 per cent of the melting temperature. The manipulation of liquid metals at temperatures of about 2000°C. and above presents some difficult problems in heat transfer, in purification, and in container materials. For metals melting at such high temperatures, it is generally regarded as expedient to circumvent the more common melting and casting process by resorting to powder metallurgy. This circumvention is not accomplished without some penalties, the more notable of which are the relatively high cost of the powder metallurgy method and particularly the size limitations of its product. In an effort to overcome the inherent disadvantages of the powder metallurgy method, especially in respect to the limit of size, a project was begun in 1943 at the Climax Molybdenum Co. laboratory to develop a method of melting and casting molybdenum capable of producing larger bodies of molybdenum than were then obtainable. Later, from Feb. I, 1944, to Aug. 31, 1945, the project was under the supervision of the National Research Committee, Division One. In peacetime, too, there are needs for molybdenurn, which make consideration of another process desirable; for example, large parts for heat engines generally, the omnipresent demand for metal of higher quality and lower cost, and the development of molybdenum-base alloys. This paper describes methods for melting and casting molybdenum, with details of the special process needed to make molybdenum castings ductile, and reports some of the properties of what may be regarded as a new, or at least modified, form of the metal. First Process for Melting and Casting Molybdenum The maintenance of a temperature greater than 2625°C. in a 'pace large enough to melt several pounds of molybdenum may involve the loss of heat at a Very considerable rate. For melting molybdenum, therefore, the source of heat must be of high potential and of fairly high power. Evidently, also, the source of heat must not impair the purity of the product. The electric arc operating in vacuum appeared to meet these requirements and was accordingly the first choice as a source of energy. A number of arc devices for melting molybdenum were examined, and several were tried. In the first experiment, a 20-kw., 60-cycle-per-second alternating-current arc was operated between two horizontal and opposed electrodes of molybdenum- In this arrangement the falling droplets of molybdenum solidified below the arc in an irregular mass. This experiment did not produce a useful casting, but the data obtained indicated that

Jan 1, 1947

By E. A. Nesbitt

The important permanent-magnet alloys 15 years ago contained carbon and depended upon it for their permanent-magnet properties. In recent years great advances have been made in a number of new alloys substantially free of carbon. These include Remalloy,' an alloy of iron, cobalt, and molybdenum, the various iron-nickel-aluminum alloys of the Mishima2 type, and the more recent Alnico V3 in which the best properties are developed by heat-treating in a magnetic field. The Mishima and the Alnico types of alloys are very brittle and after casting must be ground to size. This article describes a permanent-magnet material4 that can be machined as cast, and when handled with some care can be rolled to thin sheet and drawn to fine wire. Optimum magnetic properties are developed by a simple heat-treatment, and at this time the ductility of the alloy disappears. If the cast alloy is heat-treated without cold-working the mag netic energy product is about 1.0 X 106. This material is called Vicalloy I (pronounced vicalloy, V for vanadium, I for iron, and C for cobalt). When the alloy is first hot-worked and then considerably reduced in area by cold-swaging, drawing or grooved rolling, it is found that after heat-treatment the magnetic energy product measured in the direction of previous extension can be increased to 2.0 to 3.5 X 106. These higher values have been obtained only after reductions in area of 75 to 95 per cent, and since the material hardens considerably during working, the reduction ordinarily can be accomplished only in fine wires, although larger sizes can be reduced by the use of powerful machinery. When the material has been cold-worked in such a manner as to improve its energy product substantially, it is called Vicalloy 11. Commercial use of Vicalloy has been made in the recording of speech. Tape 0.002 by 0.050 in. has been found superior in quality to all others tried, and is now used in the Western Electric Mirrorphone 5 In a variety of forms Vicalloy I or I1 is useful in many laboratory instruments, and in experiments in which the sizes and shapes required cannot be obtained with the other more brittle permanent-magnet materials. In 1936, during a study of other age-hardening magnetic systems, it occurred to the author that some of the iron-cobalt-vanadium alloys might be suitable for permanent magnets. The proportions of iron, cobalt, and vanadium were varied and a range of alloys of particular interest was found, as shown by the indicated area in Fig. I. The limits of this range of composition are 30 to 52 per cent iron, 36 to 62 per cent cobalt, and 4 to 16 per cent vanadium. The compositions indicated by points outside this area were also tested. Preparation and Properties OF Vicalloy I The alloys were usually cast in graphite molds into bars 3/4 in. in diameter and

Jan 1, 1946

By E. A. Nesbitt

The important permanent-magnet alloys 15 years ago contained carbon and depended upon it for their permanent-magnet properties. In recent years great advances have been made in a number of new alloys substantially free of carbon. These include Remalloy,' an alloy of iron, cobalt, and molybdenum, the various iron-nickel-aluminum alloys of the Mishima2 type, and the more recent Alnico V3 in which the best properties are developed by heat-treating in a magnetic field. The Mishima and the Alnico types of alloys are very brittle and after casting must be ground to size. This article describes a permanent-magnet material4 that can be machined as cast, and when handled with some care can be rolled to thin sheet and drawn to fine wire. Optimum magnetic properties are developed by a simple heat-treatment, and at this time the ductility of the alloy disappears. If the cast alloy is heat-treated without cold-working the mag netic energy product is about 1.0 X 106. This material is called Vicalloy I (pronounced vicalloy, V for vanadium, I for iron, and C for cobalt). When the alloy is first hot-worked and then considerably reduced in area by cold-swaging, drawing or grooved rolling, it is found that after heat-treatment the magnetic energy product measured in the direction of previous extension can be increased to 2.0 to 3.5 X 106. These higher values have been obtained only after reductions in area of 75 to 95 per cent, and since the material hardens considerably during working, the reduction ordinarily can be accomplished only in fine wires, although larger sizes can be reduced by the use of powerful machinery. When the material has been cold-worked in such a manner as to improve its energy product substantially, it is called Vicalloy 11. Commercial use of Vicalloy has been made in the recording of speech. Tape 0.002 by 0.050 in. has been found superior in quality to all others tried, and is now used in the Western Electric Mirrorphone 5 In a variety of forms Vicalloy I or I1 is useful in many laboratory instruments, and in experiments in which the sizes and shapes required cannot be obtained with the other more brittle permanent-magnet materials. In 1936, during a study of other age-hardening magnetic systems, it occurred to the author that some of the iron-cobalt-vanadium alloys might be suitable for permanent magnets. The proportions of iron, cobalt, and vanadium were varied and a range of alloys of particular interest was found, as shown by the indicated area in Fig. I. The limits of this range of composition are 30 to 52 per cent iron, 36 to 62 per cent cobalt, and 4 to 16 per cent vanadium. The compositions indicated by points outside this area were also tested. Preparation and Properties OF Vicalloy I The alloys were usually cast in graphite molds into bars 3/4 in. in diameter and

Jan 1, 1946

By G. Derge, Lo Ching Chang

The chemical and physical propertties of slag systems are of special interest to metallurgists, for nearly all metals are in contact with molten slags during the primary reduction from their ores and then during the subsequent refining and alloying processes that determine their ultimate use. These processes are carried out at high temperatures and involve such complex chemical systems that funda-mental scientific knowledge of the Properties and behavior of these slags is inadequate. Various hypotheses have been Proposed to explain known slag characteristics. The commonest of these regard the molten slag as constituted of compounds that are dissociated in varying degrees into their constituent oxides, as illustrated by Schenckl and the recent Papers of Chipman and co-authors. Another proposal is that these compounds dissociate by com-plete6 or partial ionization, the evidence for which has been reviewed by Martin and Derge.? whatever hypothesis is favored, the exact formulation of these compounds is incomplete. It is based on three principal types of information: 1. Studies of solidified 51% samples by X ray diffraction, petrography, and similar methods that can be used at room temperature. The correlation of this information with the high-temperature properties of the molten slag is uncertain. 2. Studies of slag-metal equilibria, which have the advantage of providing observations on the molten slag at high temperature. However, even these data present problems of interpretation because they require a complete knowledge of the metal phase. 3. Direct measurements of properties of molten slag at the temperature of greatest metallurgical interest. Viscosity, electrical conductivity, specific heats, and similar properties have been measured, but the data of this type are widely scattered and frequently difficult to interpret. Additional direct measurements of properties of molten slag that can be interpreted in terms of chemical behavior are required, and this paper shows that the standard physical-chemical measurement of reversible electrode potentials, which measure the activity of specific constituents, is a fruitful source of such information. The purpose of this investigation, therefore, was to find an electrode combination that would yield reversible electromotive force measurements when dipped into the molten slag to be studied. Slags of the systems cao-sio2 and cao-120,-SiO2 were chosen for study because graphite containers could be used and the data could be correlated with those for viscosity, conductivity, and other proper-

Jan 1, 1948