By C. G. Bieber, R. F. Decker

The effects of minor constituents on the malleability of nickel alloys are described. These effects are related to the atomic diameter, valence, and position on the Periodic Table. The basic methods for removal or neutralization of deleterious elements are then reviewed. Finally, practical methods for melting nickel alloys are described in detail and related to minor constituent control. L HE first malleable nickel was produced by Fleit-man in about 1870 by the addition of manganese and magnesium to the molten metal to counteract the harmful effects of sulfur. Merica and Waltenbergl explained the mechanism by which these elements accomplished the desired result. They showed that sulfur in concentrations in excess of about 0.005 pct produced films of a brittle low melting eutectic of nickel-nickel sulfide which completely surrounded the grains. When manganese was added to molten nickel it reacted with the sulfur to form manganese sulfide which precipitated as widely scattered globules in the grain boundaries. The further addition of small amounts of magnesium converted the sulfur to a very stable sulfide of magnesium which was relatively insoluble in both the liauid and solid states and therefore occurred as finely divided particles within the grains where it had relatively little detrimental effect upon the malleability of nickel or its alloys. The practice of treating nickel with manganese and magnesium came to be called "deoxidation" and was employed without appreciable modification for the commercial production of wrought nickel and high nickel alloys (in this paper—50 pct or more nickel) until about 1930 even though the results were never entirely satisfactory. At that time a more extensive study was made of the effects of minor constituents on malleability and metallurgical quality. The results, small portions of which have been published,2-4 are presented here with other pertinent data. EFFECTS OF MINOR CONSTITUENTS UPON NICKEL Systematic additions were made of 0.5 pct or less of each of most of the elements of the periodic ta- ble. It was established in this study that some minor constituents other than manganese and magnesium were extremely influential. The malleability, as evaluated by the reduction of area in tension tests, depended roughly on temperature as shown in Fig. 1. Four temperature zones are of interest; the cold malleable zone (up to about 1000° F), the red short zone from roughly 1000° to 1500' F, the hot malleable zone around 2000° F and the incipient melting zone. Most of the malleability problems are associated with the red short zone and the discussion will concern this mainly. The reduction of area in normal tensile tests on high-purity nickel (see curve A of Fig. 1) appeared to have no

Jan 1, 1962

By S. S. Cole, H. Sigurdson

The melting points of mixtures of titanium dioxide and other titanates have been reported to a limited extent as binary systems and some results have been reported in conjunction with silicon dioxide. The limited data indicated that a low melting zone might exist in a ternary or quarternary system of CaO-MgO-TiO2-Al2O3, since the eutectics reported in the binary systems of MgO.TiO2-TiO2, Al2O3TiO2-TiO2 and CaO.TiO2-TiO2 were of about equivalent composition of TiO2. The importance of a low melting region with a high titanium oxide value in the developing of high titanium slags is fully appreciated by metallurgists. A comprehensive study was undertaken to establish basic information on low melting titanate mixtures. Compounds in the System CaO-MgO-TiO2 -Al2O3 Preparation of the titanates of CaO, MgO and Al2O3 confirmed reported data that the following compounds could be formed under oxidizing conditions in solid state reactions: CaO.TiO2, 2MgO.TiO2, MgO.TiO2, MgO-2TiO2 and Al2O3.TiO2. Under oxidizing conditions it was not possible to react MgO with TiO2 in mol ratios higher than 1:2 without having unreacted TiO2 in the product, nor was it possible to form calcium or aluminum titanates with a higher mol ratio of CaO and A12O3 to TiO2 than 1:1. By fusing mixtures of Al2O3-TiO2 and MgO-2TiO2 together a series of solid solution products were obtained, which showed an MgO-2TiO2 X ray diffraction pattern shifted to smaller inter-planar spacings. Range of Investigation Data in the literature1 indicated that these titanates had melting points which ranged from 1645 to 1860°C. Since the purpose of the study was primarily to provide useful data for smelting titaniferous ores, the work was restricted to the zone of the system which would include the crystalline phases present in the slags. The explored limits were bounded by CaO.-TiO2-MgO.TiO2-TiO2in the base plane. The system was extended to a fourth component Al2O3-TiO2 since many titaniferous ores contain appreciable amounts of A12O3. In the quarternary system CaO-TiO2-MgOTiO2-TiO2-Al2O3TiO2, a tetrahedron was used to represent graphically the components, with one component at each point of the tetrahedron. In the base plane, mixtures were pre- pared to represent fairly uniform changes of composition over the desired range expressed on a mol percent basis. Al2O3-TiO2 was brought into the system in increments of 10 mol pct up to 40 pct. Mixtures were then made up for each of the Al2O3-TiO2 planes. The ranges employed were then represented by five planes cutting the tetrahedron at 10 mol pct Al2O3-TiO2 intervals. Choice of Equipment Although it was necessary for all smelting work to be done in a strongly reducing atmosphere, it was decided that all melting point determinations should be done under oxidizing conditions. This decision was prompted by the fact that TiO2 reduced to lower oxides in a reducing atmosphere with consequent changes in melting points. The use of a micropyrometer and a platinum strip furnace for work of this type is adequately described in the literature.2 With modifications, equipment was selected which provided a fairly rapid method of determining melting points of refractory oxides. The final assembly, which was used, consisted of a platinum strip furnace and a Leeds and Northrup disappearing filament optical pyrometer attached to a special telescope which magnified the sample about 20 diam. The furnace assembly consisted of a platinum strip 0.005 X 0.3 X 2.2 in. mounted on brass posts on a refractory base. This was enclosed in a black steel shell which had a 2-in. opening at the top for purposes of sighting the telescope. The platinum strip was in series with two 0.04 ohm nichrome resistors connected to the secondary of a 2 kw transformer which supplied 17 volts. The current to the primary was varied

Jan 1, 1950

By W. Hodge, A. F. Haskins, R. M. Evans

Refractory boron compounds are shown to resist corrosion by molten zinc. Coatings were made from ferroboron and manganese boron by several methods: welding, hard facing, and pack diffusion; and techniques of coatings are very important. Mechanical failure of the diffusion coatings can be partially eliminated by applying them to type 416 chromium steels rather than carbon steels. Welded coatings made with a tungsten arc are better than those made by other welding methods. Sintered compacts of mixtures of iron and chromium borides developed strengths of about 30,000 psi. They resisted corrosion of zinc at 600°C and oxidation at higher temperatures. MOLTEN zinc rapidly attacks common metals of construction. The rate of attack is greatly amplified at temperatures over 500°C. However, there are many applications where it is necessary, or at least advantageous, to use metal construction, such as for galvanizing pots and zinc smelter equipment. Condensers and agitator linings used in continuous zinc smelting processes are eroded and corroded by violently agitated molten zinc. Pumps, tubing, and other parts to permit transfer of molten zinc would be desirable in many zinc handling operations. The development of metallic materials which are resistant to molten zinc also might permit its use as a heat-transfer medium in modern high efficiency power plants. In reviewing previous work on zinc-resistant metals, it was evident that most of the available data refer to corrosion at temperatures just above the melting point. Tungsten and high Mo-Fe alloys containing more than 80 pct Mo resist corrosion by molten zinc.', ' Imhoff states that because chromium is not attacked by zinc, chromium plating improves galvanizing pot life." Nitrided cast iron has been used in die-casting machines' where the molten alloy is 96 pct Zn and 4 pct Al. Other metals that have been suggested as of possible value for zinc resistance are columbium, tantalum, and titanium.V he corrosion of steel by zinc has been discussed by many authors,z, "2 None of these materials resisted corrosion by molten zinc at the temperatures used in this investigation, i.e., 600" to 700°C. I. Exploratory and Resistant-Coating Tests To make a study of zinc-resistant metals, exploratory tests were conducted to sort out roughly those materials which seemed most worthy of further development. This preliminary study included both solid metals and surface coatings. Exploratory Corrosion Tests in Molten Zinc—In initiating a study of this problem, numerous samples of metals and alloys were evaluated by dynamic corrosion tests made at 440 °C. Each metal was tested in its most readily available form, which, because of shape and size, was often unsuited for standard corrosion testing. The equipment used for dynamic corrosion testing of all materials, except in a few initial experiments, is shown in Fig. 1. Samples were tied to tungsten rods with tungsten wire, immersed in the zinc, and revolved at 12 rpm about the circumference of a 4 in. diam circle. Speed of travel was about 12.5 fpm. The molten zinc was protected from oxidation by an atmosphere of carbon monoxide, or, at a later period in the program, by a 9:1 mixture of nitrogen and hydrogen. When the effect of both molten metal and atmosphere was desired, the zinc level was lowered. Special high grade zinc was used in all of the corrosion tests. Corrosion losses for materials tested are shown in Tables I and 11. Whenever the materials were available in suitable form, the losses are reported in mils per year. It was recognized that weight losses on irregularly shaped specimens did not show the corrosion rate but the important consideration—poor resistance to corrosion—could be determined readily.

Jan 1, 1956

By Herbert H. Kellogg

Graphs representing the standard free-energy of formation as a function of temperature for 21 fluorides are presented, along with estimated values for the standard free-energy of formation of 20 atedadditional fluorides. A few of the many possible uses of these data in metallurgical calculations are discussed, including the fluorination of oxides, sulphides, metallurgicaland chlorides, and the reduction of metal fluorides. RECENT papers which have presented free-energy data for oxides, sulphides, chlorides, carbonates, sulphates, and silicates in the form of free energy vs. temperature plots,1-5 have found important uses in teaching and metallurgical development work. This method of presentation of thermo-dynamic data serves to make available in readily usable form thermodynamic constants which are scattered throughout the literature, and to show by graphical means the stability relations which exist between the compounds of a given type. It is certainly desirable to have these free-energy-temperature diagrams for as many types of compounds as are of present or potential use in metallurgical processes. Thus, even though there are but few uses of metallic fluorides in extractive metallurgy today, the potential uses of fluorine processes are of great importance and serve as the principal justification of this paper. Recent developments in the production of fluoro-carbons have resulted in vastly improved methods for the production and handling of fluorine and corrosive fluorides, with consequent reduction in costs.".' The extractive metallurgist should no longer overlook possible fluorine processes when development of a new process for a relatively high unit-price metal is being considered. In a previous paperv he author outlined in some detail the importance and use of free-energy data in metallurgical calculations and also discussed the properties of a standard free-energy vs. temperature diagram. The same method of presentation is adopted in this paper, and the reader is referred to the earlier work for explanations of the use of free-energy data. Thermodynamic Data This paper presents standard free-energy vs. temperature diagrams, Figs. 1 and 2, for those fluorides for which the major thermodynamic constants are known. In the calculations of the standard free-energy of formation (AGO), values of the enthalpy of formation at 298°K (?Ho,) were taken from "Selected Values of Thermodynamic Constants"8 most of the values of standard entropy at 298°K (S°298) were taken from "Selected Values"," but in a few cases the values given by Kelley9 ere preferred; data for the Phase changes came from "selected Values" and several of Kellley's publics- tions;0-12 and most of the specific-heat data were taken from Kelley.l0 The appendix gives a detailed list of the sources of the data. As explained in an earlier paper,6 he accuracy of some of the standard free-energy relationships is not high. An error of +1 kcal at 1000°C is expected in most of the curves of Figs. 1 and 2. The error may be as high as +3 kcal in some of the curves. Rather than attempt to estimate the reliability of each curve, the source of the data used is reported in the appendix, and the reader may compare these data with newer values as they become available. Figs. 1 and 2 fail to show values for the fluorides of many important metals. In most cases this is because the entropy of the metallic fluoride is unknown. For preliminary calculations it is often useful to have available the best estimate of an unknown datum, rather than no information at all. With this in mind, Table I lists estimated standard free-energy values for a number of important metallic fluorides not included in Figs. 1 and 2. The values reported in Table I were, calculated by Brewer et al.13 and are based on estimated entropy values. The estimated uncertainty of the values for each fluoride were calculated from the uncertainty values given by Brewer1' for ?H°, and the entropy function.

Jan 1, 1952

By Herbert H. Kellogg

C. M. Decroly (University of Brussels, Belgium) — The importance of the fluorides in the process metallurgy of special metals has already been accepted and it will probably increase in the future. Free energy diagrams as such established by Professor Kellogg are therefore very useful. It is interesting to note that the absolute value of the standard free energy of formation of HF increases with temperature, whereas for almost all the other fluorides it decreases; consequently it should be theoretically possible to reduce all the fluorides of the metals which, at low temperature, have a greater affinity for fluorine than hydrogen by this last element, provided a sufficiently high temperature is used in order to have a good efficiency. However, with regard to the reduction of UFe by hydrogen, I doubt that it will be possible to obtain directly the metal at comparatively low temperatures. There are other uranium fluorides which are more stable than UF6 and it is very likely that such fluorides will be obtained first. For example, in considering the reaction: UF6gas + H2gas + UF1so1id + 2 HFgas it is found, using the thermodynamic data of Brewer et al, that ?H298 = —66 kcal and ?G°298, = —65.2 kcal. As a result, the reduction of UF6 to UF4solld should proceed spontaneously even at ordinary temperature. On the other hand, the standard free energy of formation of UF4solid at 298°K is AG°298 = -209 kcal per mol of F2. The reduction of UF4 by hydrogen will be practically difficult and, as it is known, the only practical way of reducing this compound is to use alkaline-earth metals such as calcium or magnesium. I should like to point out, further, that the fluorination of many metal oxides can be carried out very easily by using the ammonium difluoride method of preparation, which renders the use of fluoride gas unnecessary. The first compound formed is generally a double fluoride of the metal and ammonium. This compound can be decomposed by heating either in a vacuum or in an inert atmosphere, ammonium fluoride being volatilized leaving the metal fluoride in a very pure state. H. H. Kellogg (author's reply)—Professor Decroly is quite right in pointing out that the formation of lower halides of uranium may complicate the reduction of UF6 by H2. I was unable to find his reference to the free energy of formation of UF4 in the compilation of Brewer.13 however. The value of AG°298, = —209 kcal for formation of ½ UFa seems rather high, and I hope the source of this value may be made clear.

Jan 1, 1952

By Sanai Nakabe

Japanese wartime economy demanded domestic cobalt production. This paper describes a process operated for two years at the Besshi mine and smelter on extremely low grade (0.1 pct Co) pyrite concentrates obtained from copper ore. 'The steps in the process were roasting, leaching, precipitation, reduction fusion to crude cobalt, and finally refining by electrolysis to 99+ pct. COBALT ore deposits in Japan are all small and of poor grade. In the past, a small amount of cobalt has been produced from the best portions of a few of these deposits, and very little production is expected in the future. In addition to these lean cobalt ores, cobalt is present in the cupriferous pyrite which is fairly abundant although of low grade, as is shown in Table I. Considerable cobalt is expected from these deposits because of their extent. Cobalt cannot be exclusively recovered economically from ore of this type; however, if means could be devised to recover it as a byproduct of copper production, a fairly large production at reasonable cost could be expected from Japanese sources. It was along this line that the research work was done. Selection of Suitable Process The process for extracting cobalt differs from ore to ore according to their composition. The difficulty in cobalt metallurgy arises from the fact that chemically cobalt resembles many such common metals as Mn, Fe, Ni, Cu, and Zn, associated with it in the ores. In the present case the most serious difficulties were: 1—Extremely low grade ore, 0.1 pct Co. 2—The large proportion of iron accompanying cobalt and its close similarity in chemical behavior. 3—The fairly large proportion of zinc and manganese and their chemical similarity to cobalt. The recovery of cobalt oxide as a byproduct of the hydrometallurgy of copper had been attempted in Japan but was stopped after a short period because it proved uneconomical. The literature disclosed no method for the recovery of cobalt from cobaltiferous copper pyrite and it was therefore necessary to devise a new process. The following basic principles were considered in selecting the process: 1—A major alteration in copper production methods should not be necessary. 2—The first step should be the extraction of cobalt leaving the large quantity of iron unaffected. For this purpose wet metallurgy would be preferred.

Jan 1, 1952

By J. E. Powell, F. H. Spedding

WHILE rare earths are reported to be widely distributed in nature and are not really rare," in practice, there are only a few minerals which are sufficiently rich in rare earths to serve as practical sources. Perhaps the best known of these is monazite which is a phosphate mineral containing rare earths and thorium. This mineral occurs as a dense brown sand in gravel beds and is particularly rich in the light rare earths of the cerium subgroup. This mineral is processed commercially for its thorium, cerium, and lanthanum content, and, consequently, furnishes rich concentrates from which neodymium, praseodymium, samarium, europium, and gadolinium may be obtained. Unfortunately, monazite is rather lean in rare earths heavier than gadolinium. A second mineral which is rich in the light rare earths is bastnasite, a fluoro-carbonate. Extensive deposits of this ore have been discovered in the western United States and have received considerable newspaper publicity in recent years. While bastnasite is very rich with respect to cerium, lanthanum, and neodymium, it contains even less heavy rare earths than does monazite. One of the better sources of heavy rare earths of the yttrium subgroup is gadolinite, a black silicate rock from which the rare-earth content can be extracted readily by acid leaching. It is obtained chiefly from Norway at the present time, although there are known deposits in the United States. Other sources of heavy rare earths include fergu-sonite, euxenite, and samarskite which are refractory tantalo-columbate ores. These minerals require caustic fusion or reduction to carbides with carbon before the rare-earth content can be extracted. All of the minerals which are rich in the heavy rare earths contain yttrium as a major constituent. After the rare earths have been extracted as a group from an ore by chemical means, it is generally convenient to precipitate them from acid media with oxalic acid in order to eliminate certain non-rare-earth impurities such as iron, beryllium, etc., which are usually present. The oxalate can then be readily ignited to R2O3. The oxide can be dissolved in acid and is the starting point for subsequent separation into the pure components. Perhaps the principal reason why the rare earths have not been studied as extensively as other elements of the periodic table, whose natural abundances are comparable, is that they are extremely difficult to separate from each other by the usual chemical means. Prior to 1945, the separation of one trivalent rare earth from another was a laborious process. All separations were based on repeated fractionation processes, i.e., fractional precipitation, fractional decomposition, fractional crystallization, etc. These processes were repeated from a few hundred to many thousands of times in order to obtain individual rare-earth salts of reasonable purity. Of course, mention should be made that, in the few cases where a rare earth could be oxidized or reduced to a valence state other than three, more conventional chemical means could be utilized to separate the oxidized or reduced ion from the other normally trivalent rare earths. The ionic states which deserve special mention are CeIV, SmII, Eu11, and Yb11. When it is possible to remove an element of the series efficiently, due to an optional valence state, its immediate neighbors also become easier to isolate. For example, binary mixtures of lanthanum and cerium, and praseodymium and cerium can be obtained by a relatively small number of fractional operations. The tetravalent state of cerium then allows the complete resolution of the binary mixtures by ordinary chemical means. Although the tetravalent state of cerium has been known for a long time, the divalent states of samarium, europium, and ytterbium were not used extensively in separations prior to 1930 because they are relatively unstable in aqueous media.'-" No attempt will be made to give a comprehensive review of the extensive literature dealing with the separation of rare earths. Rather, this paper will be confined to a review of those methods which have been developed at Iowa State College during recent years, and which have proved extraordinarily successful for the isolation of highly pure rare earths in quantity. It was obvious that, if pure rare earths were to become generally available, methods would have to be developed wherein the thousands of fractional operations made necessary by the similarity of rare-earth properties could be performed automatically. The development of chromatographic techniques and ion-exchange resins appeared to offer a mechanism by which this objective could be accomplished. A number of early attempts were made to separate rare earths by these means; for example, Russell and Pearce12 passed a mixture of rare earths through a cation-exchange column and reported

Jan 1, 1955

By A. L. Labbe, J. J. Donoso

Hard-won experience in the operation of smelting plants has pointed the way to the most efficient design and economical operation of a baghouse system for recovery of metallurgical fumes. This paper treats of the principles governing bag filtration and the factors most directly affecting bag life. Methods for temperature conditioning of smoke previous to filtering are described and the evolution of bag shaking mechanisms is brought up to date. THE history of the bag filter process, as applied to the recovery of metallurgical fumes, goes back to 1876, when the Lone Elms Works of Joplin, Missouri, erected a two-section baghouse for filtering fumes from Scotch Hearth lead smelting furnaces. By modern standards this installation was crude, but the basic operating principles remain essentially the same today. Great progress, however, has been made in the mechanization of the process by the use of devices for mechanically and automatically cleaning bags of adhering fumes, in the use of instruments for recording and controlling the variables affecting baghouse operation, and in the conditioning of the smoke previous to filtering. The principles governing bag filtration of fumes were investigated in 1929 by A. J. Seitz of American Smelting and Refining Co., and he arrived at the following conclusions: 1. Pressure on Bags at Constant Volume: The rate at which the pressure builds up in a bag with constant volume is directly proportional to the time, with the same kind of smoke and dust burden (fig. 1). 2. Pressure on Bags for Change in Volume: With equivalent smoke and dust burden, the bag pressure increases with the square of the increase in volume. The rapid increase in pressure is due to (1) increase in volume, (2) increase in amount of dust on the bag, and (3) more intense packing of the dust at higher velocity (fig. 2). 3. Effect of Intensive Filtering on Pressure: Since the pressure builds up directly as the square of the volume, with the same smoke and dust burden, it is necessary to shake the bags in that increased ratio, and vigorously, to keep the pores of the bag open and pressure down. This increases the wear on the bags and the dust losses. 4. Effect of Shaking on Dust Losses: The losses are in direct proportion to the frequency of shaking because the loss takes place immediately after shaking, before the bag seals itself. Tests show that with hand shaking the last 20 pct of the removable dust requires seven times more shaking per unit weight of dust than the first 80 pct. 5. Effect of Fineness of Dust on Losses: The fineness of the dust particle increases the loss in two ways: (1) When the bag is clean a greater percentage of it will pass through before the bag seals itself; (2) fine material penetrates farther into the bag pores, building up pressure faster and necessitating more shaking, thereby increasing the loss. The physical principle of operation of the bag filter is simply the separation of solids from a gaseous carrier through a porous medium, and is analogous to the filtration of solids from liquid carriers. Basically, the mechanics of the process are as follows: Fume-laden gases drawn from the operating fur-

Jan 1, 1951

By Donald Ingvoldstad, Harold E. Lee

AT Bunker Hill the original charge storage and preparation system was installed in 1917 to accommodate lead-silver gravity mill products. Only minor tonnages of wet fines such as vanner and flotation concentrates were received. Charge flux and diluent requirements were .provided by an ample supply of siderite middlings and coarse lime-rock. While oversize material was crushed through ¼in., the use of roll crushers in series resulted in a more or less granular, free-running charge of adequate porosity. Under such conditions, receipts could be proportioned directly from receiving bins, and suitable blending was obtained by passing the resultant layered composite through a small Stedman disintegrator. This elementary system served well for production and smelting of an extremely lead-rich sinter, in the low column blast furnace. Here sinter physical quality is less critical, and appreciable quantities of raw flux and oxidized ore may be charged directly to the blast furnace without seriously impairing furnace capacity. Prior to 1938 the relative proportions of zinc receipts were low and extraneous flux requirements at a minimum. However, subsequent war-inflated zinc demands brought marked increase in fine concentrate and slimy zinc leach residue receipts and an abrupt introduction to smelting a more refractory zinciferous charge. The higher temperature demands of the more refractory zinciferous charge required a higher smelting column and the higher column, in turn, rendered the blast furnace less receptive to improperly prepared feed. Inadequate presinter processing facilities prevented the production of acceptable sinter, and blast furnace production declined to 50 pct of former capacity. In view of a prevailing contention among lead metallurgists as to the deleterious action of high zinc slag on blast furnace capacity, it was natural to overstress this factor and to concentrate on possible changes in furnace design. Another interpretation was that primary correction should be sought through expanded sintering facilities. This divergence of opinion, together with the extreme material shortages of the 1940's, delayed corrective

Jan 1, 1957

By D. V. Doane, G. A. Timmons, W. G. Scholz

Molybdenum of high purity can be produced by direct dissociatiott of commercial molyhdenm disulfide in vacuo at 1600° to 1700°C (2910° to 3090°F). The Product is lower in oxygen than commercially available molybdenzdm powder. Analyses of ingots arc-cast from commercial molybdenum powder, hydrogen-re-cluced from animonium molybdate, and from thermally dissociated molybdenum disulfide indicate that the levels of chemical impurities in these ingots are similar. Equipment now in operation will produce 100-lb hatches of powder product. The paper describes development of processing equipment, control of processing varzahles, handling of the product, and evaluatiotl of the melal produced. MOLYBDENITE (molybdenum disulfide) can be decomposed by heat in the absence of oxygen to produce elemental molybdenum and sulfur, which is evolved as a gas. The temperatures required for the dissociation are above 1370°C (2500°F); the sulfur must be continuously withdrawn to permit the reaction to proceed to completion. This is accomplished by continuous evacuation of the thermal dissociation chamber and condensation of the gaseous sulfur in another part of the system. Cognizance of the fact that the dissociation takes place in two steps is important in controlling the process. Basically, the molybdenite dissociation process has two potential advantages as a method of produc- ing pure molybdenum: 1) The materials entering into the process contain little or no oxygen. Since the process is carried out in vacuum at high temperature, the quantities of interstitial oxygen, nitrogen, and hydrogen in the product should be very low. 2) The process is more direct than the commercia1 method of producing high-purity molybdenum. In the conventional process, molybdenite is roasted to molybdic oxide, the oxide is purified first by sublimation, then by conversion to ammonium molybdate, and finally, the molybdate is reduced in a hydrogen atmosphere (usually in two steps) to the metal lic molybdenum powder. This paper presents a description of the stages in scaling-up of the dissociation equipment and an account of attempts to evaluate the molybdenum produced by thermal dissociation, rather than a report of a fundamental study of the dissociation reaction. Since little has been written on the subject, it is appropriate, before detailing the development of the process, to review briefly the research that has been conducted over quite a period of years. LITERATURE SURVEY The first accounts of the possibility of thermal dissociation of the mineral molybdenite were re-

Jan 1, 1962

By Alex Boozenny

The results of potential measurements between 1) a titaniurn electrode in NaCl-TiCl, melts and a graphite-cizlorine reference electrode and 2) a titanium electrode in NaC1-Nu "melts and a graphite-chlorine reference electrode show that the following relationship expresses the equilibrium relationship between the TiCl, and the dissolved metallic sodium concentrations, expressed in mole fraction units, in dilute NaCl welts at 850°C. The results of potential measurenments between a graphite electrode in NaCl-TiCl, melts that were saturated with TiCl, and a graphite-chlorine reference electrode, when combined with the standard free energy data given in literature, gave the following expression for the equilibrium relationship between the TiCl, and TiCl, concentrations, expressed in mole fraction units, in dilute NaCl melts at 850°C. These relationships are for melts in equilibrium with pure titanium. In impure systems, less sodiurn and more TiCI, can be copresent with a given concentration of TiCl,. AFTER 10 years of existence, the titanium metal industry still relies on the original Kroll and the sodium reduction processes for the only important means of converting titanium-bearing ores to titanium metal via production of titanium tetrachloride as an intermediate. Through years of modification and development these two processes have evolved to a point where any further major economic advances in the field of titanium metal production must be achieved through implementation of processes which are distinct departures from simple magnesium or sodium reduction of titanium tetrachloride. Concurrently with the refinement of the Kroll and sodium reduction processes, industries and government have sponsored research and development in the field of producing titanium by electrolysis of oxides,' carbides,' and halides3'4 in fused salt media. However, the incomplete understanding of the physical chemistry of fused salt systems has in many cases hindered the development of promising new titanium production processes to the point where they will have a clear advantage over the processes presently employed. Fortunately the volume of information on fused salt physical and electrochemistry is increasing at an accelerating pace. The first approaches tbward investigating the electrochemical behavior of fused salt systems have been the measurements of equilibrium potentials of metals immersed in melts containing their halides.' Some work on the kinetics of fused salt electrochemical processes has been reported.'09" Some descriptions of the structural composition of fused salt systems are also available. The work described herein is a continuation of the study of metal electrode potentials in fused salts. Specifically, this contribution to the growing store of fused salt chemistry information presents a description of the equilibrium relationships between the concentrations of titanium dichloride, titanium trichloride, and metallic sodium in fused sodium chloride. The investigation of the titanium dichloride-titanium trichloride equilibrium relationships is not completely new. Kellog and Krye and Melgren and opie15 have presented the results of chemical analysis of salts containing titanium chlorides. Flengas and lngrahaml' have published the results of an investigation of these equilibrium relationships obtained by measurement of electrode potentials in a fused NaCl-KC1 mixture. The investigation described herein differed from that of Flengas and Ingraham principally in the use of straight NaCl as the solvent in place of the more costly and more difficult to purify mixture. This investigation was conducted in three parts. First, the equilibrium potentials of titanium in sodium chloride containing known concentrations of titanium dichloride were measured. A graphite-chlorine electrode was employed as reference. Second, the equilibrium potentials of titanium immersed in sodium chloride containing known concentrations of elemental sodium were measured. Third, the equilibrium potentials of graphite immersed in titanium tetrachloride-saturated sodium chloride containing known concentrations of titanium trichloride were measured. The results of these three related investigations are presented in the above order. The results are combined with the thermodynamic properties of titanium chlorides and sodium chloride, obtained from literature, to give the titanium dichloride-titanium trichloride-elemental sodium equilibrium concentration relationships. In the test, whenever a melt contains titanium chlorides in predominantly divalent form, the melt

Jan 1, 1962

By J. R. Stone, G. D. Storm

Design features and operating methods of ASARCO's new unit for the continuous melting and casting of tough pitch copper at Perth Amboy are described. Preliminary studies made for determinitzg economic feasibility and design details are also presented. Cathodes are preheated with oil and melted in an electric furnace at 40-ton per hr rate, from whence the molten copper is fed simultaneously to the wire bar casting wheel and the continuous casting of cakes and billets. In the early 1950's the copper refining furnaces at ASARCO's Perth Amboy plant reached a point where major expenditures would have to be made for replacement of the furnaces and the auxiliary equipment. The problem was whether to continue with the standard reverberatory furnaces or to consider continuous melting in electric furnaces. Reverberatory furnaces have been used for years in the copper industry and for some 50 years at the Perth Amboy plant. Reverberatory melting practice, however, imposes certain restrictions. First, labor costs are high, usually requiring three shifts per day. Secondly, they operate on a batch basis, the conventional operation being a 24-hr cycle including

Jan 1, 1961

By O. J. C. Runnalls, L. M. Pidgeon

Some observations on the kinetics of the iodide process are reported. The deposition rate is geometry-sensitive in a system containing a finely divided titanium charge. Further, results indicate that the iodine diffusion rate influences the velocity of the process. The nonvolatile iodide, Til,, forms in the hot filament zone, thus removing iodine from the cycle. TITANIUM metal of 99.9 pct purity may be prepared using a refining technique originated by Van Arkel and de Boer.' The purity of this metal, commonly called iodide titanium, exceeds that produced by any known process. In a recent application, the method was employed by Gonser et al.² to prepare titanium rods up to 2 to 3 cm in diam. In the Van Arkel-de Boer system, the relative influence of the fundamental mechanisms: l—production of titanium iodides, 2—gaseous countercurrent diffusion, and 3—decomposition, on the deposition rate have not been clearly established. Blocher and Campbell" have indicated that the controlling step in the process under practical conditions of operation may be the reaction rate of iodine with the crude metal. Fast' reported that crude titanium metal reacted with iodine rapidly, even at room temperature, in his apparatus. Little has been reported on the effect of gaseous diffusion or decomposition on the deposition rate. It is these aspects of the process about which this investigation is centered. An attempt has been made to separate these latter effects from those due to the formation of the iodides at the crude metal surface by a division of the experimental program. Reaction of Iodine with Titanium Apparatus: In the investigation of gas-metal reactions of this type, the chemical reactivity of the halogen and halide vapors dictates the use of all-glass apparatus. In such a system standard techniques for measuring reaction rates are difficult to employ. Here, a simple apparatus was devised (Fig. 1) so that some indication of the reactivity of titanium powder with iodine vapor could be obtained. A stream of iodine gas was evolved from a bulb of controlled temperature and passed over a sample of titanium powder heated in a horizontal tube furnace. The product of the reaction, TiI4, volatilized and was condensed outside the furnace in a series of four glass bulbs, each cooled to room temperature in turn. Preliminary experiments indicated that distillation was retarded in a sealed evacuated system due to a pressure build-up in the condensing end of the apparatus. Hence, the system was pumped continuously using a mechanical pump and two oil diffusion pumps in series, through a liquid air trap. The iodine bulb was made large and a capillary restriction was inserted between the titanium bulb and the condensers so that the iodine pressure over the metal would approach the equilibrium pressure over solid iodine crystals. The effect of this restriction on the evaporation rate of TiI4, was determined separately. The iodine bulb was heated in an oil bath controlled to ±2°C. The titanium bulb temperature was automatically controlled to ±5°C. Procedure: About 200 mg of —30 mesh titanium powder, weighed to 0.1 mg, was placed in the reaction bulb after part B had been joined to part A. The powder was tapped into a long (5 cm) shallow mass along the bottom of the tube. Two chromel-alumel thermocouples were inserted into the magnesium radiator which was clamped to the reaction

Jan 1, 1953

By O. J. C. Runnalls, L. M. Pidgeon

J. M. Blocher, Jr. and I. E. Campbell (Battelle Memorial Institute, Columbus, Ohio)—Since the de Boer-Van Arkel process for making titanium metal involves a number of steps in a fairly compact unit, it is difficult to determine simply which of the steps is rate controlling. In any statement as to which step constitutes the rate-controlling process, qualifications appear to be in order. It is possible to design a reaction bulb in which any one of a number of steps is made to be controlling. I—With the filament removed some distance from the crude, as in the case of the authors' experiments, the interdiffusion of iodine and iodide may be controlling. 2—If, as is usually done, the crude metal is placed in a perforated cylindrical basket, or as a briquetted mass, in close proximity to the filament, the rate of deposition is increased (we obtained rates of deposition 5 to 10 times those cited in the authors' paper), and another rate-limiting factor, such as the reactivity of the crude, may take over. In this regard, we have noticed radically different rates of deposition with different crudes, and with crudes in various stages of exhaustion. 3—With a very reactive crude metal and with optimum practical geometry, still another process may be controlling. It is felt that this is a diffusion process in the immediate vicinity of the filament involving the fundamentally adverse situation of a net flow of particles away from the filament. The separate experiments on the reactivity of iodine with titanium are interesting but somewhat inconclusive. Data is still needed on the partial pressure of iodine in an operating decomposition bulb. A knowledge of the gradient of iodine partial pressure from the crude to the filament would be particularly enlightening. Optical absorption may be a useful technique here. Accurate measurements of the total pressure within a decomposition bulb under various conditions would be quite revealing. Preliminary measurements have been made at Battelle in following this line of attack. It is interesting to note that the authors' data on the temperature dependence of deposition rate indicate that the overall rate is not controlled by the kinetics of the decomposition reaction at the filament: TiI1 ? Ti + 4I Any reasonable estimate of the activation energy of this reaction would, if its kinetics were controlling, dictate a much greater temperature dependence than is observed here. The authors apparently attribute the drop in deposition rate (eventually to zero) with increased TiI4 pressure solely to a decrease in diffusion rate. However, there is an equilibrium factor involved here that must not be overlooked. As the partial pressure of TiI4 is increased, a point is reached where, due to the competing reaction of the tetraiodide with titanium to form lower iodides, the equilibrium partial pressure of titanium is reduced to the point that it equals the vapor pressure of titanium at the filament temperature and the deposition rate falls to zero. This effect would

Jan 1, 1953

By B. W. Howlett, M. B. Bever, Somnath Misra

The heats of Formation of the compounds Sb2Se3, Bi2Se3, Sb2Te3, and Bi2Te3 and the heats of solution of tellurium and selenium in liquid bismuth have been measured in a liquid metal solution calorimeter. The heat capacities near the melting point, the heats of fusion, and the melting points of the two tellurides have been measured in a constant temperature gradient calorimeter. The thermo-dynamic quantities are interpreted in relation to the stability of the compounds and the nature of the solid-liquid transition. THE selenides and tellurides of several elements of Group VB of the periodic system are of interest because of their electronic properties. The compounds Sb2Se3, Bi2Se3, Sb2Te3, and Bi2Te3 are semi- conductors; they also have gained prominence in the fields of thermoelectricity and photoconductivity. However, little is known about their thermody-namic properties. As part of a research program on the thermo-dynamic properties of intermetallic compounds, the heats of formation of the compounds Sb2Se3, Bi2Se3, Sb2Te3, and Bi2Te3 were measured in a liquid metal solution calorimeter. The heat capacities near the melting point, the heats of fusion, and the melting points of the two tellurides were measured in a constant temperature gradient calorimeter. The results, in addition to their intrinsic interest as thermodynamic quantities, contribute to an understanding of the stability of the compounds and the nature of the solid-liquid transition. 1) EXPERIMENTAL 1.1) Materials. Samples of the compounds SbzSe3 and Bi2Se3 were prepared by melting the elements in stoichiometric proportions in evacuated Vycor capsules followed by quenchinn in water. They- were then annealed in vacuum for 12 hr at 550°C. A sample of Sb2Te3, consisting mainly of one large grain, supplied by the Lincoln Laboratory,

Jan 1, 1964

By J. W. Byrkit

Design features and operating methods at the new Ajo smelter are described in detail. Successful operation of a novel method of handling and charging wet concentrates to a deep bath type reverberatory furnace contribute to the daily production of 200 tons of anodes with good results from the standpoint of both metallurgy and economy. THE New Cornelia Branch of the Phelps Dodge Corp. is located at Ajo, Ariz. Large scale mining operations were started at Ajo in 1917, when a 5000 ton leaching plant was put in service to treat the copper carbonate ore that overlaid the sulphide ore-body. In 1924 a 5000 ton flotation plant was built to treat the sulphide ore and the leaching operation was abandoned a few years later. Changes in practice and additions to plant facilities have resulted in a gradual increase in the milling rate which now approaches 30,000 tons daily. Prior to the erection of the Ajo smelter, flotation concentrate was shipped by rail to Douglas, Ariz, where it was treated in the Phelps Dodge smelter. Construction of a one reverberatory furnace smelter to produce an average of about 200 tons per day of copper anodes at Ajo was started early in 1949. Initial heating of the reverberatory furnace was begun on June 21, 1950. Charging the furnace was started on july 8, and the first anodes were cast on July 14. Neither the anode furnace nor the reverberatory furnace has cooled since the initial firing. Fig. 1 is a photograph of the new smelter. Built primarily to eliminate the '300 mile haul of concentrate to the Douglas plant, the new smelter was designed to treat the Ajo concentrate, with a minimum of capital investment. A novel, and relatively simple, method of concentrate handling and furnace charging made unnecessary the installation and operation of expensive storage facilities and reclaiming equipment, and obviated the necessity of holding in storage large quantities of copper-bearing materials. (Patents are pending in the United States and abroad on the Ajo process.) In the selection and arrangement of equipment, consideration was given to the full utilization of all smelting facilities, reducing the amount of idle equipment to a minimum. The layout of the smelter is shown in Fig. 2. The important problem of internal transportation was minimized by arranging the reverberatory furnace, converters, and anode furnace in a compact group and providing storage bins inside the smelter building, within reach of overhead cranes, for fluxing materials and other supplies needed in the daily operation. This can be seen in the sectional view of the smelter given in Fig. 3. Incorporated in the design were many innovations in smelting equipment intended to facilitate operations and effect economies in maintenance expense and manpower requirements. Table I gives operating data of the entire plant. Metallurgy The metallurgical practice at Ajo is based essentially upon the use of a single, deep bath reverberatory furnace for smelting wet concentrate, without concentrate storage facilities. The large reservoir of slag and matte maintained in the furnace serves to equalize, to some extent, the day to day variations in the nature and grade of concentrate and permits

Jan 1, 1954

By W. A. Tiller, J. D. Harrison

HOT pressing of powder particles has gained importance recently, since it affords a method in which high densities are rapidly attained. In a recent study on hot pressing of alumina powders, Mangsen, Lam-bertson, and Best1 have shown within the limits of their experiment, the validity the rate equation for densification in hot pressing, originally proposed by Murray, Livey, and Williams.2 i.e., where D = fraction of theoretical density, t = time, P = pressure and 77 is the viscosity, all in appropriate units. This equation was derived from earlier work of Shuttleworth and Mackenzie3 which is based on the closing of spherical pores under the action of surface tension. The integrated form of this equation yields a straight-line relation between log (1 - D) and t. Such conditions were found by Felten4 to be true only after extended periods of pressing. In an endeavor to quantitatively evaluate the exactitude of this equation in the initial sintering stage, i.e., prior to sealing of the pores, spherical anti-

Jan 1, 1962

By A. W. Sommer, H. H. Kellogg

It is shown that SO3-O2 mixtures react with sphalerite at an appreciable rate ill the temperature range of 361° to 527°C to fornz ZnSO4. The rate of reaction follows a parabolle lax. Oxygen, or O2-SO2 mixtures, have a negligible effect on sphalcrite in the same temperatuee range. PRACTICAL roasting of sphalerite is usually performed at 800°C or higher. The calcine is composed of zinc oxide unless the roaster atmosphere contains relatively large amounts of SO2 and the temperature is held to 800oC or lower, in which case zinc sul-fate may also form. Ong, Wadsworth, and assell' have made a careful kinetic study of sphalerite oxidation under these "normal conditions" and have concluded that the rate of the reaction is controlled by the decomposition of an activated complex adsorbed on the sphalerite surface. They found the rate of oxidation to be small at 700°C. Extrapolation of their data to 400°C would indicate an almost negligible rate at this temperature. In our work sphalerite was reacted with air, mixtures of SO2, O2, and N2, and mixtures of SO3, O2, and N2 in the temperature range 361o to 527OC. Negligible rates of oxidation were found, except for the gas mixtures containing SOs. With this latter gas, the oxidation of finely divided sphalerite was fairly rapid and zinc sulfate was the product. Based on the limited evidence available, the rate of sphalerite oxidation by SO3 is postulated to be controlled by gaseous diffusion through pores or cracks in the zinc-sulfate coating. This evidence for the direct reaction of sphalerite and SO, at low temperature may prove of importance to the understanding of zinc-sulfate formation in the dust-collecting equipment usually associated with zinc roasters. The roaster gas carries off fine dust, much of which may be unreacted sphalerite. The temperature in dust-collecting equipment drops from the roaster temperature (about 800°C) through the range of temperature we studied, to ambient temperature. Such dusts are known to contain far larger amounts of zinc sulfate than the primary calcine. It has been assumed in the past that this sulfate is formed by reaction of ZnO dust with SO3 (or SO, plus 0,) in the partly cooled gases. Our work shows that an alternative possibility exists—the direct reaction of SO3 with ZnS dust. EXPERIMENTAL Reaction rates for sphalerite at 350° to 600°C are relatively small so that it was necessary to use finely divided material with a relatively large surface area in order to obtain measureable amounts of reaction. In the preliminary experiments, pure mineral sphalerite, ground to pass a 325-mesh sieve, and chemically precipitated ZnS (in the form of an impalpable powder) were used. In the quantitative rate experiments the ground mineral sphalerite was processed in an Infrasizer to obtain a product with particle size between 9 and 18 µ. The analysis of this material was 66.7 pct Zn, 0.09 pct Fe, and 32.7 pct S (theoretical sphalerite is 67.1 pct Zn, 32.9 pct S). The sized powder was carefully mixed and divided into l-g samples. The apparatus used for the quantitative rate measurements is shown in Fig. 1. For the preliminary experiments the following change was made: The external catalyst furnace (B, C)* was not used. *Letters refer to Fig._______1 .___- Rather, when catalysis of the SO2 + O2 reaction was desired, the glass beads in basket M were replaced by vanadium-oxide pellets. Procedure—A l-g sample of ZnS was placed on a shallow stainless-steel tray, I, and spread evenly to a depth of about 1mm. The tray was placed in the reaction assembly and the assembly inserted in the cold furnace. The furnace tube was flushed with dry argon and then heated to the desired reaction temperature. The temperature was controlled to ±0.5oC. Gas mixtures (O2 + N2 or O2 + SO2) were prepared from tank gases by means of a mixing device identical to that employed by Darken and Gurry.2 The total flow rate of gas was 205 ml per min to point A of Fig. 1. The accuracy of the individual and

Jan 1, 1960

By H. Sigurdson, C. H. Moore

Extensive studies have been carried out on electric furnace and blast furnace slags obtained in the winning of iron from its ores. These slags normally consist of elements of the gangue minerals present in the ores, as well as the added flux materials. In consequence, melts of CaO, MgO, Al2O3 and SiO2 can be considered as representing typical slag compositions. When a slag of this composition cools, it usually crystallizes according to predictions possible from an equilibrium diagram of these constituents, providing the melt is not undercooled to form glass. The melt is either viscous or fluid, depending upon the ratio of binary cations to silica, and crystallizes easily or forms a glass for the same reasons. If the melt is not overheated so that carbides of the metal components of the slag are formed and if the composition of the slag is so adjusted that it has a high fluidity, liquid equilibrium is attained and the slag can be held in a liquid state for extended periods of time. Upon tapping, the slag crystallizes into minerals, the type and proportion of which are determined by the melt composition. Since equilibrium is attained, the holding period is not critical. In melts containing a large increment of titanium, however, the normal slag procedures are not applicable. Titanium, as one of the atomic transition elements, is, at elevated temperatures, capable of being reduced to form metalloid compounds much more readily than the refractory oxides present in normal slags. In consequence, an oxide melt containing titanium never reaches equilibrium in a reducing environment, but continues to shift its composition until cooled. If melts of this nature are cooled and samples submitted to metal-lographic and X ray analysis the course of reaction and crystallization in this type of slag can be determined. Preparation of Slag The slags investigated fell into the system CaO-MgO-TiO2-Al2O3-SiO2 and were produced from ilmenite ores reduced by carbon in an electric furnace. Since the equilibrium series1 and the laboratory smelting of ilmenite2 are described in two of the accompanying papers, detailed description of the smelting procedure is not required here. However, certain essentials must be mentioned. Two types of melts were used to produce slags studied in this investigation. The first series of smelts made to determine proper flux addition were produced in a 4 lb Ajax induction furnace. The charge, consisting of ore with the proper flux addition, was heated in a graphite crucible until fluid, held fluid for a sufficient time period to obtain 1-5 pct FeO content, and poured. Because of the small size of the charge only the final sample of these melts could be examined. In the melts made in the 50 lb arc furnace, however, grab samples taken at 10 min. intervals between time of initial melting and final pouring were available for examination. These samples allowed a much clearer picture of the course of reaction and crystallization. amounts of ferrous oxide and reduced titanium compounds is opaque to transmitted light. Therefore, all petro-graphic studies had to be made on polished slag sections. A representative sample of slag was cut or broken, mounted in a thermosetting plastic, ground flat using 400 grit silicon carbide, the coarse scratches removed with 600 grit silicon carbide and polished on billiard cloth using levigated alumina. Rouge was avoided because of the entrainment of the red particles in pores in the slag, causing a possible confusion with some of the mineral phases. In order to prevent sample projection above the plastic surface red bakelite was used to hold the sample, and backed up with clear lucite. In this manner sample labels could be permanently retained in the mounting. The polished samples were examined on a Bausch and Lomb metallograph at magnifications of 250 X, 500 X, 1000 X and 1800 X. The instrument was equipped for examination of specimens under bright field illumination and with crossed nicols. A magenta tint plate to aid in color tone differentiation was also used. Petrology of Slags In order to determine the composition and mineral relatinos of a previously unreported system petrologically, it is essential that the starting composition, reaction temperature and final composition be known. The chemical composition of the ilmenite ore used in these smelts is given in Table 1, and the complete analysis of a typical high titanium, low iron slag is given in Table 2. In the winning of TiO2 from ilmenite by a smelting process it is necessary to produce a slag which will melt at an economically feasible temperature, remain molten as the iron is removed by reduction, be fluid enough to be readily removed from the furnace, contain a high percentage of TiO2 and a low percentage of reduced titanium com-

Jan 1, 1950

By Arnulf Muan, D. P. Masse

PHASE relations in the system CoO-SiO2 have been determined as a basis for further investigations of thermodynamic properties of olivine solid solutions involving Co2SiO4 as a component. Previous data on the system CoO-SiO2 are incomplete or uncertain. Biltz and Lemke1 determined the melting point of cobalt orthosilicate as 1345°C , but Asanti and Kohlmeyer2 have later found a considerably higher temperature, 1420°C. The latter authors also studied melting relations of one mixture on the CO side and two mixtures on the SiO2 side of the orthosilicate composition and sketched a tentative phase diagram for a limited composition range of the system. However, no phase identification was carried out, and the authors left unanswered the question of the possible existence of a stable meta-silicate phase. Greig3 showed that a 90 wt pct SiO2-10 wt pct Co mixture at 1725°C consists of two immiscible liquid phases. The quenching technique was used in the present investigation. Mixtures of high-purity cobalt oxide ("Fisher Certified") and dehydrated silicic acid ("Baker Analyzed") were equilibrated in air atmosphere. The samples were then quenched to room temperature and the phases present were identified by microscopic and X-ray examination. The samples were kept in small envelopes made from thin (0.0004 in.) platinum foil. Thermodynamic data which have become available recently for Pt-Co alloys4 were used to check that the losses of COO from the oxide samples by alloying of cobalt with platinum in the present investigation were too small to change significantly the compositions of the oxide material during the equilibration. A vertical tube furnace with an 80 pct Pt 20 pct Rh resistance winding was used in runs up to 1510°C. Temperatures in these runs were measured with a Pt vs 90 pct Pt 10 pct Rh thermocouple calibrated against the melting point of diopside (CaMgSi2O6, 1391.5?C). The given temperatures as measured by this technique are estimated to be accurate to *5°C. Quench runs at temperatures above 1650°C were made with a modified Roberts and Morey5 strip furnace, using strip resistors composed of a 60 pct Pt-40 pct Rh alloy. Temperatures were measured with an optical pyrometer which was calibrated against the liquidus temperature of a mixture composed of 10 wt pct CaO, 90 wt pct SiO2 (1707°C). The temperatures measured with this technique have an estimated accuracy of +15°C. The results are shown graphically in Fig. 1. Only one intermediate phase, the orthosilicate Co2SiO4 with olivine-type structure, is stable in addition to the end members cobalt oxide and silica. The melting point of the orthosilicate was found to be 1415" ± 5°C. The metastilicate CoSiO3 is not stable at the temperatures of the present investigation. The two eutectic points in the system CoO-SiO2 where COO plus olivine, and olivine plus silica, coexist with liquid were found to be 72 wt pct COO and 1407°C and 63 wt pct COO and 1381°C, respectively. The melting point of cobalt oxide in air was taken as 1745?C, based on the previous data of Aukrust and Muan.6 Within limits of error (+ 5?C), identical eutectic temperatures to those determined in air were found when two representative mixtures were equilibrated at 1 atm O2 pressure and in an atmosphere of 84 vol pct CO2, 16 vol pct H2. This suggests that changes in oxidation state of cobalt in the condensed phases are not significant as far as their effect on the phase relations are concerned. This inference was substantiated by failure to detect7 any "excess oxygen" (i.e., oxygen in excess of that contained in Co2SiO4) in a sample of orthosilicate composition equilibrated in air 10°C above the liquidus temperature and subsequently quenched to room temperature. This work was carried out as part of a research program sponsored by the U.S. Atomic Energy Commission under Contract No. AT(30-1)-2781.

Jan 1, 1965