Search Documents

By K. R. Evans

The deformation mechanisms occurring in polycrys-talline, commercially pure titanium and a Ti-8 pct A1 alloy have been investigated and compared to earlier results by Levine on high-purity titanium single crystals and by Conrad on commercially pure titanium. In accord with Levine, two consecutive deformation mechanisms are observed to exist below 500°K with the transition temperature between mechanisms, Tc, strongly dependent upon interstitial composition. T, is found to be 210°. 375° -430°, and 450°K for alloys A large number of investigations have been conducted to determine the rate-controlling mechanisms of plastic deformation occurring in fcc and bcc metals. Very few investigations of a similar nature have been conducted for hexagonal metals. In fact, until very recently, magnesium is the only hexagonal metal which has been systematically investigated for determination of the rate-controlling deformation mechanisms.1"3 From these investigations, it was concluded that basal slip below 420°K occurs by the intersection of forest dislocations,1'3 while for prismatic slip the Peierls mechanism is rate-controlling at low temperatures with interstitial compositions of 0.024, 0.42, 0.61, and 1.13 at. pct expressed in terns of oxygen equivalents. The low-temperature mechanism is found to be an impurity obstacle mechanism in contrast to Levine's earlier conclusion of the Peierls barrier. Measurement of the activation parameters for deformation and estimation of the force-distance profile of the obstacles show their retarding force to be effective over longer distances from the obstacle as the interstitial composition increases. and thermally activated cross slip at higher temperatures. 2 The potential technological importance of titanium alloys has prompted recent studies of the deformation and fracture characteristics of titanium and its alloys. 4-8 Levine' systematically investigated the low-temperature deformation behavior of high purity titanium single crystals oriented for either basal or prismatic slip. It was concluded that the Peierls mechanism was rate-controlling at temperatures below 210°K, while above this temperature an undefined mechanism was rate-controlling. Conrad 7,8 concluded from an analysis of the composition dependence of the critical shear stress at 0°K and measurement of the activation parameters that the low-temperature deformation of titanium is controlled by an impurity

Jan 1, 1969

By W. A. Wood, H. L. Wain, R. I. Garrod

The mechanical behavior of recrystallized chromil~m of high purity has been studied, principally in torsion and to a lesser extent in tension, at temperatures between —196oand 350oC. Depending upon the conditions of test, the material may show brittle or ductile behavior or an intermediate or subduc-tile state having some of the characteristics of each. This latter state existed at temperatures between approximately ±50°C and was characterized by a) extensive creep at stresses well below the normal fracture stress, b) nonelastic loading/unloading effects during creep, c) strain softening under cyclic loading, and d) final failure of a brittle type. Suggestions are made on the dislocation processes and interactions which give rise to subductile behavior The ductile-brittle transition in bee metals has been studied mainly by tension and bend tests. These methods, however, favor crack propagation which may follow too closely on initiation for detailed study of the transition itself. For work of this nature, therefore, other modes of deformation less favorable to crack propagation may be preferable. This paper describes a study of the ductile-brittle transition in chromium which is based mainly on torsional testing although a few subsidiary experiments were made in tension. It appears to reveal at the transition an intermediate state that cannot properly be described as either brittle or ductile. Torsional tests on chromium have been made by other workers1 but not, as here, primarily for study of this intermediate state. EXPERIMENTAL The chromium, in the form of swaged rod, was prepared by techniques already described.' The particular material used was one in which the main impurities were 0.03 wt pet 0 and 0.006 wt pet N and one in which transition from ductile to brittle states in torsion conveniently fell at about room temperature. For torsion, test specimens were from 5/16-in.-diam rod to provide test portions 1-1/4 in. long by 7/32 in. diam, a twist of 1 deg thereby corresponding throughout this paper to 0.0015 surface shear. The specimens before test were annealed for 2 hr at 1200°C in vacuo, which left them with a re-crystallized grain size of about 0.01 mm, and then electropolished. They were tested under dead-weight loading in an apparatus in which they could be surrounded by a furnace or cooling chamber, tests in practice being made at various temperatures between -196" and +350°C. For tension tests, cylindrical specimens were prepared in a similar manner and tested at room temperature under dead-weight loading. RESULTS (TORSION) Subductile State. The state described above as intermediate between brittle and ductile may be perhaps best defined by reference to torque/twist curves at various temperatures. These are grouped in Fig. 1. Below about -50°C the material was brittle, in the sense that it exhibited little plastic deformation under stress and fractured by cleavage along planes of maximum resolved tension, which in torsion produces the well-known helical type of fracture. The deformation is typified by the curves for -196" and -150°C in Fig. 1; it shows a slight but progressive deviation from linearity above a certain torque, here about 50 lb-in., until fracture occurs at about 95 lb-in. A feature to which it is desired specially to call attention is that under none of the loads did the specimens show significant creep.

Jan 1, 1964

By W. J. Sharwood

In the cyanide process, gold and silver are dissolved from crushed ore as double alkali-metal cyanides, from which they may be precipitated by such positive metals as sodium (amalgam), aluminum, or zinc, or by electrolysis. Two extreme conditions may be noted. Some works, especially slime plants practising decantation, use a relatively large volume of solution—possibly 4 or 5 tons per ton of ore—nearly all of which may require precipitation, so that the solutions handled are of much lower value per ton than the ore. On the other hand, in some leaching plants it is possible to extract with very little solution, and to percolate some of this more than once through the charge before precipitation, so that the solution to be precipitated may be much less than half the weight of ore, and proportionally richer. Solution intended for further use need not have all its precious metal removed, but any that has to be thrown away should be impoverished as far as is economically possible. In spite of certain advantages possessed by other precipitants, zinc in some form has been almost universally used.. In some of the first attempts to utilize cyanides as gold solvents, a "piece or plate of zinc" was suggested as a precipitant, but extension of surface was early recognized as a desideratum. . Macarthur and the Forrests adopted a "metallurgical filter" of zinc shaving, turned from disks or rolled sheets. They had previously experimented on other forms of zinc, ax! Mscarthur records having tried zinc dust, which had of course been long known as a general reducing agent. It had also been known and used as a precipitant of precious metal from plating and photographic solutions, and comminuted zinc had been patented for recovering copper, etc., from ore leaches. Other inventors proposed the virtual making of zinc powder by the attrition of balls of zinc, and by similar means, during the passage of a stream of gold-bearing solution. Sulman claimed the use of zinc dust, or fume, in a special apparatus, effecting a more or less regular feed of dust and solution by means of intermittent siphons; the mixture or "emulsion" (as it is still called) rising with diminishing velocity through an inverted cone in which it

Jan 1, 1918

By J. S. Bowles

DISCUSSION, M. Cohen presiding J. W. Christian (The Inorganic Chemistry Laboratory, oxford, Englandl)—I was very interested in Dr. Bowles' results on the suppression of the transformation by solid films of alcohol or propane. The transformation in cobalt, which is also martensitic, can be explained by a mechanism involving the reflection of "half dislocations" down a series of atomic planes.* This reflection process is similar to that considered by Frank13 for plastic deformation on a single slip plane and, as he pointed out, reflection would be impossible if the metal were immersed in a liquid of higher density. It seems possible that solid films of alcohol have a similar effect on the lithium transformation. Reflection should also be possible at a grain boundary, though a higher kinetic energy of the dislocation, and hence a lower temperature would be required. As Dr. Bowles used coarse grained polycrystalline speci- mens, transformation on cooling should still have occurred in grains which did not form part of the outside (free surface) of the metal. This may account for the X-ray lines of the low temperature phase which were found. There is thus the interesting possibility that in a polycrystalline specimen a liquid, or in some cases a solid, film of material of or or higher density will lower M,, while in a single crystal it should suppress the transformation completely. In the case of cobalt it is necessary to find a dense liquid which will not react with the metal at the transformation temperature. The most promising liquid appears to be pure lead, but it is very difficult to devise a method of investigating whether or not this does suppress the transformation.

Jan 1, 1952

By Robert S. Schecter, Mark P. Walsh, Michael J. Humenick

In recent years in situ leach mining has emerged as a viable technology for the recovery of uranium from strata in South Texas which contain relatively low concentrations of uranium ore. Because the ore bodies lie within ground-water aquifers, a significant determinant in the economics is the requirement that such aquifers be protected from contamination. Since ammonia is one of the constituents of the leach solutions now being field tested, one environmental problem to be resolved is the removal of ammonia at the end of mining. A second related question is the fate of the ammonia which is not removed by the restoration procedure. This paper considers the displacement and migration of ammonium in a flowing electrolyte with concomitant ion exchange. The ion exchange is an important feature since, during the solution mining phase, ammonium saturates the mineral exchange sites and must be removed from these sites. A mathematical model is used to simulate this process and the model is tested against the results of laborator.y experiments. It is found that the simulations are adequate if an appropriate selection of parameters is made. The model is then used to investigate the effect of cation composition and concentration of the restoration medium as well as dispersion on the overall effectiveness of the process. It is concluded that increasing the concentration of monovalent ions in a solution containing a mixture of both monovalent and divalent ions decreases the adsorption selectivity of the divalent ions with respect to all monovalent ions including ammonium. Thus increasing the ionic concentration of a restoration fluid by increasing the concentration of a nonselectively adsorbed (with respect to ammonium) ion may have a very limited benefit.

Jan 1, 1979

By G. C. Wallick, W. R. Foster, J. G. Savins

The theory of the differentiation method for the Couette flow experiment is reviewed. Particular attention is given to the requirements on data analyses in the case of the class of non-Newtonian materials described as viscoplastics, i.e., materials characterized by a yield point or yield stress. Here changes in boundary conditions arise when the shearing stress attains a critical value with the result that the form of the basic integral equation for Couette flow is determined by the flow conditions existing during the measurement. INTRODUCTION In the preceding papers in this series,l,2 the salient features of the differentiation method of rheological analysis in Poiseuille-type flow were discussed. It was shown that a dual differentiation-integration method analysis of the Poiseuille flow of idealized generalized Newtonian and visco-plastic models could be used to develop a spectrum of highly sensitive response patterns in terms of certain characteristic derivative functions. These functions were shown to optimize the selection of the most appropriate functional relationship between f(p) and p from the Poiseuille flow experiment. The present paper reviews the theory of the differentiation method as applied to the equally important Couette flow experiment. We will also discuss the range of variables over which the basic integral equation for Couette flow is applicable when the non-Newtonian material is of the viscoplastic type, i.e., characterized by a yield point or yield stress. THEORY Having described the application of the differentiation method to Poiseuille-type flow in the preceding papers, we now proceed to the case where the test liquid is confined to the annular space between coaxial cylinders of length L, one of which is in motion, i.e., Couette flow, formulating the basic integral equation after the method of Mooney.3 The observed kinematical and dynamical quantities are the angular velocity O and the torque T. Here, the one nonvanishing component of the shear-rate tensor is

By W. H. Emmons

This paper is the third of a series treating of the relations of ores of the metals to igneous rocks. The first' outlined the general problem; the second2 proposed a classification of lode ores, and showed how the distribution of the deposits is in a certain measure controlled by the contour of the roof of the parent batholith. A number of mining districts were discussed, the examples being selected chiefly from group 2 of the classification. The proposed classification of lode deposits, briefly stated, is as follows: 1. Cryptobatholithic: near hidden batholiths which have not yet been exhumed by erosion. 2. Acrobatholithic: in and near cupolas or domes of batholiths—the high points of larger underlying masses. 3. Epibatholithic: on batholiths, near their rims, but below eroded cupolas, or below the highest points of the roofs. 4. Embatholithic: among closely-spaced outcrops which probably are parts of a single bathohth. The outcrops of invaded rocks predominate. 5. Endobatholithic. in and near roof pendants of large batholiths. The invading rocks predominate. 6. Hypobatholithic: in deeply-eroded batholiths, where even roof pendants have been eroded. Deposits of certain metals on the roofs of the batholiths are much more numerous in some positions than deposits of other metals, and the horizontal zonal arrangements of lodes of different metals are shown characteristically only in certain groups. In a large measure, also, the character of the fracturing and metallization is determined by the position on the roof of the batholith. The disseminated copper ores in porphyry constitute a clearly-defined type. All the deposits of these ores, as far as known, are in group 2. They appear to have been formed only in and around small upward projections of the parent granitic masses, and not low on the walls of the

Jan 1, 1927

By Robert S. Baker

It has been demonstrated in the laboratory by A. J. Phillips1 that a transformation or conversion from beta directly to alpha may take place in a brass of 61 to 62.5 per cent copper content. The completion of the transformiation is dependent on a rapid rate of cooling from the all-beta field through the alpha + beta range to the alpha field. Phillips states that in a slowly cooled alloy containing 62 per cent copper and 38 per cent zinc the copper content of the beta is progressively decreased from 62 to 56 per cent by precipitation of alpha. Rapid cooling tends to prevent the separation of alpha with a copper content of more than 62 per cent by reducing to a minimum the time required for passing through the alpha + beta range. Upon crossing beyond the (alpha + beta) (alpha) boundary to the all-alpha region below, the material is transformed from beta to alpha. It, is essential that there be no change in composition. Phillips obtained his results by quenching a 62:38 copper-zinc alloy from 850" C. in iced brine at -8" C. No reference to the occurrence of this transformation in a manufacturing process has been found in the literature. An investigation of the microstructures of a number of hot forgings made from leaded brass rods yielded one forging in which this striking conversion from beta to alpha had occurred. The purpose of this paper is to describe the transformation and certain conditions under which it may occur during the hot pressing of brass. The conversion was noted in a shape forged from a leaded brass rod, the composition of which was: Cu, 60.26 per cent; Zn, 37.86; Pb, 1.88. In this study the lead content was disregarded and the alloy was considered to be equivalent to an alloy of 61.40 per cent copper and 35.60 per cent zinc (9812 parts = 100 parts). The possibility that the lead might obstruct or accelerate the precipitation of alpha was not studied. The lead appears as black globules in the photomicrographs and has a negligible solubility in the alloy.

Jan 1, 1932

By Paul B. Crawford, Bobby L. Landrum

An electrical model study has been mode to estimate the effect of horizontal fractures in thick reservoirs on pattern conductivity. For the patterns studied, it is shown that fracturing all the wells in the pattern in-creases the conductivity considerably more than frac-turing only single wells. For certain conditions one large fracture is more effective in increasing conductivity than several fractures of half the radius. Particularly in thick reservoirs and with large fractures, the center of the pay is found to be more responsive than other locations. For the seven-spot pattern fracturing the center well is more effective in increasing pattern con-ductivity than fracturing all outer wells with fractures of the same size. INTRODUCTION Although commercial fracturing has been used for some time very little quantitative information is known about the effects of fractures on reservoir behavior. The purpose of this work was to estimate the effect of horizontal fractures in thick reservoirs on the con-ductivity of various flooding and cycling patterns.2 Circular fractures originating at the wellbore and extending symmetrically into the pay were considered. ANALYSIS Electrical models were used in making this study. Horizontal fractures were simulated by copper sheets shaped like the fractures and of a proportional size; the wellbore was simulated by a copper wire. A dilute salt solution served as a conducting medium. A con-ductivity bridge was used to measure the conductivities of the various patterns studied. EFFECT OF HORIZONTAL FRACTURES ON CONDUCTIVITY Fig. 1 shows the effect on square and staggered line drive patterns of horizontal fractures located in the center of the pay. The model is shown schematically in the insert. The upper and lower groups of lines show the effect on conductivity when all wells are fractured, and when only one well is fractured, respectively. In general, pattern conductivities are substantially improved by fracturing all wells. Fig. 2 shows the effect of multiple horizontal frac-tures on the conductivity of a line-drive pattern. At

Jan 1, 1958

By R. D. Nelson, J. C. Shyne

The ß and a ß transformations in plutonium were studied with particular emphasis on the transformation kinetics and microstructure. Significant observations are: 1) The kinetic data show conclusively that the ß — a transformation in high-purity plutonium can proceed isothermally with no athermal component. 2) Plastic deformation of the stable (3 phase retards the subsequent (3 — a transformation. 3) Plastic deformation of the stable a phase accelerates the a — ß transformation; the acceleration is attributed only to residual stresses. 4) The a and a?a volume changes occur anisotroPically in textured plutonium. 5) An apparent crystallogvaphic relationship exists between the parent and the product phases of the and (3 — a transformations. 6) Both applied uniaxial compressive stresses and uniaxial tensile stresses raise the starting temperature for the ß — a transformation. 7) A given uniaxial tensile stress favors the a — ß transformation more than an equivalent applied uniaxial compressive stress opposes the transformation. These observations of the (ß —a and a — ß phase changes in plutonium are consistent with known mar-tensitic transformations. ThIS paper elucidates some of the characteristics of the a— ß and ß —a transformations in plutonium. Because considerable conjecture exists about the mechanisms by which the phase transformations occur in plutonium, experiments have been performed to provide indirect information concerning the mechanisms responsible for the a —ß and ß -a transformations. Indirect information is of particular value in the study of plutonium because of the experimental difficulties presented by the metal. Single crystals have not been produced in any of the allotropes. The large density results in high X-ray and electron-absorption factors and consequently complicating X-ray and electron diffraction. The kinetics of ß — a and a — ß transformations of plutonium and the behavior of the transformations under a variety of conditions have been investigated in detail. Information about the mechanisms of the allo-tropic transformations of plutonium was obtained indirectly from three sources: 1) the effect of plastic deformation of the stable parent phase upon the transformation kinetics; 2) the behavior of the metal transforming under applied stresses; and 3) the microstruc-tural and crystallographic features between parent and product phases. PHASE-TRANSFORMATION CHARACTERISTICS In characterizing solid-state phase transformations in metals and alloys, it is useful to define several types of transformations. An aim of the present work was to identify the low-temperature transformations in plutonium by type, i.e., as martensitic or nonmar-tensitic. Practical definitions for these terms follow. The terms commonly used to categorize phase transformations lack universally accepted definitions. This confusion arises doubtlessly because some terms specify crystallographic or morphological character while other words have a kinetic or a thermodynamic connotation. For example, martensitic specifies certain definite crystallographic restrictions. Unfortunately, martensitic is sometimes used in an ill-defined way to imply kinetic characteristics. Further confusion attends the use of such expressions as nucleation and growth, diffusional, and massive. From time to time new systems of phase-transformation nomenclature are suggested; unfortunately none of these has gained general acceptance.1,2 The authors of the present paper have no intention of entering the controversy. We recognize that some readers may object to the nomencliture used here. For exampie, the terms military and civilian have recently been used in much the same way as martensitic and non-martensitic are used in this paper. This paper is intended to describe several specific details of the low-temperature phase transformations in plutonium. The authors have found it useful to identify these transformations as martensitic; the term was chosen as the best available to describe the experimentally observed features of the transformations studied. A martensitic transformation is one that occurs by the cooperative movement of many atoms; the rearrangement of atoms from parent to product crystal structure occurs by the passage of a mobile semico-herent growth interface. The geometric features characteristic of a martensitic transformation are a specific orientation relationship between the product and parent phase lattices, a specific habit-plane orientation for the growth interface, and a shape change with a specifically oriented shear component. There is no alloy partition between the parent and product phases in a martensitic transformation. Martensitic transformations may display either athermal kinetic behavior or thermally activated isothermal kinetic behavior. Some martensitic transformations occur isothermally, although more commonly martensitic transformations are athermal. Isothermal martensitic transformations are suppressible by rapid cooling. In athermal martensitic transformations, nucleation and growth are not thermally activated and the transformations are essentially time-independent. Nucleation, growth, or both can be thermally activated in isothermal martensitic reactions. Transformation of the parent phase into a marten-

Jan 1, 1967

By C. S. Sivaramakrishnan, Manjit Singh, Rajendra Kumar

Regarding liquid nzetals structurally as a suspm-sion of clusters , having derivated solid-state coordination, in truly liquid atoms, the recently developed Kuvlar-Samarin technique of centrifuging- in liquid state enabled the determination of the cluster sizes inAl-Cu mid Pb-Sn systems. It is shown that the colutne fraction of the clusters does not exceed 9 pct and the energy of their formation in Al-Cu is about 5.5 kcal per g-atom and in Pb-Sn eutectic alloys about 25 kcal per y-atoni. STRUCTURAL investigations of liquid state have principally followed the following three courses: i) studies with X-ray, electron, or neutron diffraction; these investigations have shown that there is a certain amount of regularity in the structure of liquid metals which can be defined by a coordination number and that the structure is a derived function of that in the solid state; ii) thermodynamical investigations which are based on the concept of ideal behavior; these describe the liquid state in terms of free-energy values and other thermodynamic functions; although these investigations are of help in the study of the general effects of alloying, they do not provide any structural insight into the precise atomic distribution in liquid state; iii) measurements of surface tension and viscosity; although it is natural to expect that the viscosity is related to the structure in liquid state, these investigations have so far only provided information which can be used by the foundry technologists and has been little utilized in formulating models of the structure of liquid state. As it happens, investigators in the three groups have worked almost independently of each other and there is practically no structural correlation between the results of one group with those of another. The purpose of the present paper is to indicate that the experimentally measured parameters of these three groups of research are closely related to the structure in the liquid state. STRUCTURE OF LIQUID METALS Although atomic distribution in solid and gaseous states is rigorously known, that of the liquid state is only appreciated on the fringes. There is no universal model of atomic distribution in liquid state, but two diverse models are at present hotly contested. The first, largely expounded by ~ildebrand,' regards the liquids as condensed gas since many of their properties and much of their behavior can be adequately described by regarding them as fluids. The second mode12j3 considers that some form of near-solid as- sociation of large number of atoms exists in the liquid state. On the other hand, ~ernal' was able to predict rather precisely the radial distribution functions in liquids on the basis of statistical geometric approach which considered that liquids are "homogeneous, coherent, and essentially irregular assemblage of molecules containing no crystalline regions or holes large enough to admit another molecule". He introduced the concept of pseudonuclei in the otherwise random structure as aggregates of closely packed tetrahedra which gradually merge into irregularity and continually replace each other. To what extent the pseudonuclei can be regarded as regions of near-solid association is indefinite but Bernal suggested that the concept of pseudonuclei can be compromised with the latter model if the near-solid associations are regarded as extremely dense and not necessarily crystalline. The difficulty in projecting the structure of liquid metals arises because they exhibit duplicity of character as some of their properties are closer to those of crystalline solids and others to fluids. There is an increasing tendency to discuss the structure of liquid metals in terms of the second concept according to which the structure of liquid metals may be conceived as consisting of i) clusters of atoms where the aggregation is a close derivative of that in the crystalline state, ii) individual atoms which behave like true liquids in respect to degrees of freedom and iii) excess number of vacancies. It is noteworthy that the introduction of only 5 pct vacancies is sufficient to transform crystalline matter into the liquid state. At any instant of time thermodynamic equilibrium exists between i, ii, and iii, but the relative proportion of the clusters and random atoms is not known. That this is so can be appreciated by the fact that, when liquid metal is rapidly cooled, liquid state vacancies may condense in the form of dislocation loops and vacancies in excess of their equilibrium number in solid state. These dislocation loops have been observed in thin foils of aluminum prepared from rapid cooled aluminum. As temperature increases above melting point the number and volume fraction of clusters decrease but those of vacancies and random atoms increase. Clusters are transient in nature. In pure metals the cluster is an aggregation of the metal itself. In alloys, however, the nature of the cluster largely depends on the interaction between solvent and solute atoms. If the interaction between unlike atoms is greater than between like atoms: the clusters are then aggregates of unlike atoms. Examples of this kind of system are A1-Cu, Mg-Pb, and so forth, i.e., systems which exhibit negative departures from the Raoult's law. In systems where the interaction between unlike atoms is smaller than be-

Jan 1, 1968

By W. C. McBee, B. W. Jong, T. A. Sullivan

A sulfur concrete technology has been developed by the US Bureau of Mines, where chemically modified sulfur is used with suitable mineral aggregates to produce construction materials that are resistant to corrosion by acids and salts. This report presents a summary of the basic technology and results of testing the materials under actual operating conditions in 50 corrosive environments in 40 commercial plants. After four years of testing, there was essentially no evidence of material degradation or loss of strength. Regular concrete materials were attacked and, in some cases, completely destroyed under the same conditions. Testing is continuing to establish ultimate longevity and durability of the sulfur concretes. The materials are finding widespread applications in metallurgical, chemical, and fertilizer processing plants.

Jan 1, 1986

By R. B. Newcombe

Despite abnormal economic conditions and the unhealthy state of the petroleum industry, 1930 closed without any marked decline in total production of oil in the Middle Western States. The most accurate figures available would indicate for this district an output of close to 25,000,000 bbl. for 1930 as compared to 26,000,000 bbl. for 1929. This can be accounted for by the settled nature of a great many of the wells producing in this area and the favorable geographical position, which affords adequate refining and marketing facilities. The only new flush production field discovered in the area was the Legrande oil pool in southeastern Hart County in western Kentucky, where wells up to 1000 bbl. initial have been reported from a shallow depth. Important extensions have been found in a number of central Ohio fields, and activity in the central Michigan area resulted in new pools along the northwest trend of the Mt. Pleasant structure. These new districts, known as the Leaton and Vernon pools, have not yet reached the scope of the Mt. Pleasant field proper, and although the structure is similar, sand conditions are not strictly analogous. Wildcatting was retarded somewhat by the scarcity of market for oil and many important wells were shut down for several months. This has not shown such a profound effect on production as the reticence of operators to drill inside proven locations. The major companies have not been able to dispose of their oil and the smaller operating units are having trouble financing their projects. The result is that oil in sight is not being produced and output is suffering accordingly. Another important effect on production was the introduction of proration by the major crude purchasers and a voluntary shut-down by Kentucky operators. This step became necessary because of the glutting of lake port refineries with Mid-Continent oil, and was not fostered by regulating state bodies, as in the case of the southwestern states. Small refining units have sprung up to meet this situation in a number of instances but they have experienced some difficulty in disposing of their product because of "dumping" tactics from other quarters. New refinery outlets on the Great Lakes and new pipe line connections should tend to alleviate this difficulty during the coming year. The

Jan 1, 1931

By W. A. Clark

THE production of sand in an oil well increases operating costs because of abnormal wear in subsurface equipment, the necessity for frequent cleanouts, and the need for a means of disposing of the sand. Moreover, removal of sand from the zone can bring about the creation of cavities from which bodies of formation, sand or shale, may slough into the hole, endangering the shutoff, impeding production or collapsing the liner. The procedure known as gravel packing is attracting attention as a means of controlling these factors and contributing to the productive life of a well. That gravel packing is now substantially beyond the preliminary stage on the Pacific Coast is reflected in the 191,000 bbl, of oil produced monthly by the 66 gravel-packed wells in 11 different producing sectors. REASONS FOR GRAVEL-PACKING Gravel packing, if properly carried out, can be expected to provide the following benefits: 1. Prevent the movement of sand and thus eliminate sand production and sand fills, and prevent the formation of cavities. 2. Provide a practical, relatively inexpensive, large-diameter hole, which will provide well-known theoretical advantages. 3. Support the walls of the hole by completely filling the space between the liner and the formation, regardless of its irregularities, and afford a support for liners. 4. Provide for more efficient pumping operations in wells by: (a) possibly utilizing the gravel as a gas trap in pumping gaseous fluids, (b). allowing deep submergence of the pump into the oil zone.

Jan 1, 1939

By H. E. Cline, E. F. Koch, J. L. Walter

It has been postulated and, in a few instances shown, that some kind of dislocation structure will be present at semicoherent interfaces to accommodate small lattice mismatches. In the present study of the NiAl-Cr eutectic, regular arrays of interface dislocations are observed at the boundary between the chromium-rich rods and the NiAl-rich matrix. The networks were examined by transmission electron microscopy and selected area diffraction. The rods and the matrix have a crystallographic relationship in which all directions and planes of the two phases are parallel. The dislocation networks are cmposed of a<100> dislocations lying on the intersections of the cylinders with (100) planes. Dislocations forming hexagonal rather than square arrays are also observed at certain areas of the network. The morphology of the network is consistent with the interpretation of mismatch being accommodated by interface dislocations in the cylindrical geometry. The measured spacing between dislocations was used to calculate an apparent lattice mismatch between the phases (˜0.35 PCt)interface network energy (-140 ergs per sq cm), and network strengthening (-10,000 psi). It has been proposed by Frank and Van der Merwe1 that dislocations should be present at the boundary between two semicoherent crystallographically related phases. The role of the interface dislocations would be to reduce the internal stresses, caused by the mismatch in atomic spacing across the interface. Such dislocations have been observed at the interface between expitaxially grown films and Substrates.2-4 Interfacial dislocations have also been observed at precipitate-matrix interfaces.&apos;-&apos; Directionally solidified eutectics have been shown to have semicoherent phases1&apos; and would, therefore, be expected to have interfacial dislocations as found by Weatherly at a lamellar fault in A1-A12Cu.11 The NiAl-Cr eutectic appeared to be a promising system to examine because both phases are cubic, the lattice mismatch is small, and the phases are crys-tallographically related. Furthermore, the eutectic is easily thinned for transmission microscopy. Indeed, interfacial dislocations were observed and this report describes the nature of the dislocation networks in the boundary between the NiAl-rich ma-trix-phase and the fine chromium-rich rods.21 I) EXPERIMENTAL PROCEDURE Ingots, 3/4 in. in diam and 6 in. long were made by melting in vacuum and casting under argon using 99.9 pct pure material. The composition, in at. pct, was 33 pct Ni, 33 pct Al, and 34 pct Cr. The ingots were then placed in A1203 crucibles on a water-cooled base, melted by means of induction, and withdrawn from the hot zone at the rate of 1 in per hr under argon.* * T his material was first directionally solidified in this laboratory by E. R. Stover Slices were taken perpendicular to the growth direction of the directionally solidified ingot for metallography and for transmission electron microscopy. The electron transmission samples were thinned mechanically, then thinned electrolytically in A-2 electrolyte* *A-2 electrolyte: 62 ml perchloric acid, 700 ml ethanol, 100 ml butylcellosolve, 137 ml distilled H20. until a hole appeared in the foil. 11) EXPERIMENTAL RESULTS A) Optical Microscopy. The microstructure, viewed on a plane perpendicular to the growth direction, is shown in Fig. 1. The structure consists of cells or colonies of parallel chromium-rich rods in the NiAl matrix. The cells occur when there are impurities present12 or, in a ternary eutectic, if the composition is slightly off the eutectic composition. The axis of the chromium-rich rods is parallel to the growth direction except near the cell boundaries. Here the rods may assume angles to the growth direction; however, examination shows that the crystallographic relationship between the rod and the matrix remains the same. Fig. 1 includes cell boundaries where the rods formed at a large angle to the growth direction. The variation of rod position across the cells made it possible to Fig. 1-Structure on plane perpendicular to growth direction. Rods near cell walls are at large angle to growth direction. Magnification 315 times.

Jan 1, 1970

By C. Laird, C. E. Feltner

May different kinds of dislocation structures have been observed in strain-cycled metals and alloys. In order to understand their pattern and causes, an experimental program has been carried out to determine the influence on the dislocation structures of the three variables: 1) slip character of the material, 2) test temperature, and 3) strain amplitude. The results show that at high strain amplitudes cell structures me formed when the slip character is wavy, and that these are progressively replaced by uniform distributions of dislocations as the stacking fault energy is decreased. At lower strains, dislocation debris is formed which consists primarily of dipoles in wavy slip mode materials and multipoles in planar slip mode materials. Temperature merely acts to change the scale of the structure, smaller cells, and clumps of dislocation debris being associated with lower temperatures. It is shown that the results for many metals fit this pattern, which Parallels that occurring in unidirectional deformation. DISLOCATION structures produced by cyclic strain (fatigue) have been examined in a number of metals by transmission electron microscopy. These studies have produced a variety of interesting and often seemingly conflicting results. For example, different investigators have reported such structural features as cells.le4 bands of tangled dislocations,4&apos;5 dense patches or clusters of prismatic dislocation loops, planar arrays,4&apos;10 and various combinations or mixtures of these different structures. Most of these observations have been made on materials which were initially annealed and cyclically strained at low amplitudes resulting in long lives. Recently we have reported observations of the dislocation structures produced in copper and Cu-7.5 pct Al cycled at large amplitudes, resulting in lives of less than 104 cycles.4 These results, examined in combination with those in the literature, have suggested that a common or consistent structural pattern exists. Variations in this pattern appear to be determined chiefly by the three variables, namely, the slip character of the material,4,11 test temperature. and the strain amplitude. To verify this interpretation, we have studied [he influence of the above three variables (in different combinations) on the resultant structures in cyclically strained metals. Copper, fatigued at room temperature, was chosen as a reference state to which all other observations can be compared. The effect of slip character has been investigated by employing fcc metals of different stacking fault energy. Thus aluminum which has a more wavy slip character than copper, and Cu-2.5 pct A1 having a more planar slip char- acter, have been examined. The aluminum samples were fatigued at 210°K thus making their homologous temperature equal to that of copper at room temperature. The influence of temperature has been evaluated by examining the structures in copper at room temperature and 78°K. Finally the effect of strain amplitude was studied by looking at the structures at amplitudes giving lives ranging from 104 to 107 cycles. All of the specimens were examined at the 50 pct life level at which stage the structures have reached a stable configuration.12 I) EXPERIMENTAL PROCEDURE Strip specimens, 0.006 in. in thickness, were prepared from base elements of 99.99 pct purity or greater. Specimens were fatigued by cementing the strips to a lucite substrate which was subjected to reverse plane bending. This method of testing has been described e1sewhere.7 After fatiguing, specimens were thinned and examined in a Philips EM 200 which was equipped with a goniometer stage capable of ±30-deg tilt and 330-deg rotation of the specimen. On the basis of separate calibrations,13 allowances were made for the relative rotation and inversions between the bright-field images and the diffraction patterns. II) RESULTS AND DISCUSSION The life behavior of the materials under different test conditions is shown in Fig. 1 in the form of plots of total strain range vs cycles to failure. Comparisons of structures produced in the different materials were made at amplitudes which produced equal numbers of cycles to failure. The influence of strain amplitude on the structures produced in the reference state material (copper tested at room temperature) is shown in Fig. 2. At the 104 life level the structure produced comprises cells similar to those previously observed.3,4 They are approximately 0.5 p in diam and the cell walls are generally more regular or sharper than those produced by unidirectional deformation.14 At the 10&apos; life level the

Jan 1, 1969

By D. T. Peters, C. R. Cupp

Aging of commercial 18 pct Ni maraging steel and of related binary, ternary, and quaternary alloys has been studied by electrical resistivity, X-ray diffrac-tion, and hardness measurements. The aging process is in three stages: 1) recovery of martensite; 2) two precipitation reactions; 3) formation of nickel- rich austenite. The main objective of this work was to discover the nature of the Co-Mu interaction. Addition of cobalt to the Fe-18 pct Ni-5pct Mo alloy results in acceleration of the pvecipitation reaction by increasing the super-sat~lration 0f molybdenum. The cobalt-containing al- loys show no incubation period for the precipitation reaction, but the alloy without cobalt shows an initial slow reaction. These results are interpreted in terms of precipitation on dislocations. At low aging temperatures, the presence of cobalt leads to the appearance of a second type of precipitate which is a particularly effective hardener. Cobalt was found to retard the formation of austenite. Overaging is a combination of classical overaging and the formation of austenite in the structure. he- activation energy for the precipitation reaction determined from resistivity ,measurements is 42.8 kcal per mole and the growth of the precipitate is found to obey at law at high tenzperatures and a tU3 law at low temperatures. HE mechanism of strengthening of the 18 pct Ni maraging steels has been studied extensively since 1962.&apos;-? The strengthening is due to precipitation hardening of the martensitic matrix. The main precipitate is an inter metallic compound involving molybdenum, but there is disagreement about its identity.

Jan 1, 1967

By A. D. Mutch

IT has long been known that there are wide variations in the thermo-electric potential of pyrite. In the last few years a study of this variation and other properties of pyrite was carried out at the University of Toronto by F. G. Smith on specimens of pyrite from many loyalities. As a result of these studies the pyrite geothermometer was developed by Professor Smith. The calibration of the pyrite geothermometer is based on the assumption that "crystals of any one electronically conducting mineral species deposited at a high temperature have a more positive thermoelectric potential than crystals deposited at a low temperature, and the thermo-electric potential varies continuously between any given limits of the temperature of deposition." The cause of the variation was postulated to be crystal discontinuities, such as lineage boundaries. As yet this postulated relationship has not been established as fact. On theoretical grounds it is indicated that the thermo-electric potential of pyrite or any other partial conductor is dependent upon a number of factors as well as the temperature of formation. For this and other reasons there is ground for doubt as to the validity of the relationship postulated above. To date a large number of readings have been made with the pyrite geothermometer which have been recorded in terms of the calibration of the instrument in degrees centigrade. So far most of the pyrite tested by this technique has been in association with gold ore. The values for the temperature of formation obtained in these tests appear to be reasonable and, in relation to geological problems, to vary in the right sense. Determinations on some specimens not in association with gold ore have given readings that appear to be much too high, taking into account the probable maximum temperature of the host rock. To sum up, although many determinations made with the pyrite geothermometer appear to give reasonable values for the temperature of formation of the pyrite, there are at the same time other readings which seem anomalous. On the basis of an examination of available results of work with the pyrite geothermometer, two problems must be considered: 1—the validity of the calibration of the pyrite geothermometer; and 2— the nature of the distribution of the thermo-electric potentials of pyrite in relation to the specific problems that have been examined. In this paper the academic problem relating to the validity of the calibration of the pyrite geothermometer will not be discussed. Instead, the variations of thermo-electric potential of pyrite in association with gold veins will be discussed with regard to specific examinations. The first of these two examinations deals with the distribution of thermo-electric potentials of pyrite in association with a gold vein and was carried out in the McIntyre Porcupine Mine, Schumacher, Ont., in the summer of 1949 as part of a study with this technique. The second problem deals with variations of thermo-electric potential of pyrite in gold ore specimens from all over the world. The specimens used in this study were part of the private collection of Frank Ebbutt, geologist for Howe Sound Exploration Co. Results of Detailed and Reconnaissance Studies In discussion of the results of determinations made in these two studies the values of thermo-electric potential in millivolts will be used. It will be noted that in some of the diagrams the determinations are recorded in terms of pyrite geothermometer temperatures. Fig. 1 is a calibration chart relating pyrite geothermometer temperatures and thermoelectric potentials. A full discussion of the technique is given in the original paper by F. G. Smith.&apos; Briefly, the determinations are made by placing two stainless steel probes, one hot and the other cold, against the surface of the pyrite crystal being tested. The thermoelectric potential that is developed is read with a null-point potentiometer that is calibrated in what

Jan 1, 1953

By A. D. Mutch

IT has long been known that there are wide variations in the thermo-electric potential of pyrite. In the last few years a study of this variation and other properties of pyrite was carried out at the University of Toronto by F. G. Smith on specimens of pyrite from many loyalities. As a result of these studies the pyrite geothermometer was developed by Professor Smith. The calibration of the pyrite geothermometer is based on the assumption that "crystals of any one electronically conducting mineral species deposited at a high temperature have a more positive thermoelectric potential than crystals deposited at a low temperature, and the thermo-electric potential varies continuously between any given limits of the temperature of deposition." The cause of the variation was postulated to be crystal discontinuities, such as lineage boundaries. As yet this postulated relationship has not been established as fact. On theoretical grounds it is indicated that the thermo-electric potential of pyrite or any other partial conductor is dependent upon a number of factors as well as the temperature of formation. For this and other reasons there is ground for doubt as to the validity of the relationship postulated above. To date a large number of readings have been made with the pyrite geothermometer which have been recorded in terms of the calibration of the instrument in degrees centigrade. So far most of the pyrite tested by this technique has been in association with gold ore. The values for the temperature of formation obtained in these tests appear to be reasonable and, in relation to geological problems, to vary in the right sense. Determinations on some specimens not in association with gold ore have given readings that appear to be much too high, taking into account the probable maximum temperature of the host rock. To sum up, although many determinations made with the pyrite geothermometer appear to give reasonable values for the temperature of formation of the pyrite, there are at the same time other readings which seem anomalous. On the basis of an examination of available results of work with the pyrite geothermometer, two problems must be considered: 1—the validity of the calibration of the pyrite geothermometer; and 2— the nature of the distribution of the thermo-electric potentials of pyrite in relation to the specific problems that have been examined. In this paper the academic problem relating to the validity of the calibration of the pyrite geothermometer will not be discussed. Instead, the variations of thermo-electric potential of pyrite in association with gold veins will be discussed with regard to specific examinations. The first of these two examinations deals with the distribution of thermo-electric potentials of pyrite in association with a gold vein and was carried out in the McIntyre Porcupine Mine, Schumacher, Ont., in the summer of 1949 as part of a study with this technique. The second problem deals with variations of thermo-electric potential of pyrite in gold ore specimens from all over the world. The specimens used in this study were part of the private collection of Frank Ebbutt, geologist for Howe Sound Exploration Co. Results of Detailed and Reconnaissance Studies In discussion of the results of determinations made in these two studies the values of thermo-electric potential in millivolts will be used. It will be noted that in some of the diagrams the determinations are recorded in terms of pyrite geothermometer temperatures. Fig. 1 is a calibration chart relating pyrite geothermometer temperatures and thermoelectric potentials. A full discussion of the technique is given in the original paper by F. G. Smith.&apos; Briefly, the determinations are made by placing two stainless steel probes, one hot and the other cold, against the surface of the pyrite crystal being tested. The thermoelectric potential that is developed is read with a null-point potentiometer that is calibrated in what

Jan 1, 1953

By Edward Halse

The occasional occurrence in metalliferous veins of rounded fragments of rock, matrix or ore, lying loose, embedded in clay, or enclosed in some kind of cement, may be attributed to four causes:— I. They have been washed in from the surface, or from an upper portion of the vein.. II. They are of concretionary origin. III. They have been produced by movements in the country-rock or in the walls of the vein. TV. They have been formed in situ, by the upward, downward or lateral flow of water in the vein itself. In this paper the word " conglomerate " is confined to a rock composed of rounded fragments or pebbles cemented together, as distinguished from a " breccia," in which the rock-fragments are angular. * I. Boulders and Pebbles which have been Washed in from the Surface, or from an Upper Portion of the Vein. In this type it is presupposed that the vein at one time communicated by a fissure or open space with the surface, or with the upper portion from whence the fragments have been washed. One well-authenticated occurrence was described long ago by Fournet. Owing, no doubt, to later dislocations in the lode, pebbles from an old alluvium and sands containing titaniferous iron, as well as fragments of wood, were found in a vein at Huelgoet, in France. " Toutes les parties tendres du filon de Pranal ou ces phenome&apos;nes sont les plus prononces ont 6th excaves jusqu&apos;a d&apos;aasez grandes profondeurs par I&apos; impetuosite des torrents, qui out depose la matiere alluviale.&apos;"

Jan 1, 1906