By J. A. Finch, S. T. Hall

An oxidative alkaline pressure leach is shown to increase the magnetic susceptibility of coal-pyrite particles. The leach was successfully exploited as a pretreatment in the magnetic desulfurization of an eastern Canadian coal. Greater than 50% total sulfur (65% pyritic sulfur) rejection at 85% clean coal yield was achieved using a high-gradient magnetic separator (HGMS) at 1.3 T and 53 mm/s (2 in. per sec) flow rate, after pretreatment at 0.5 mot NaOH, 85ºC (185ºF), 930 kPa (135 psi) air pressure, 15 minutes retention time, and 20% solids by weight (w/w). Without pretreatment, sulfur rejection at these HGMS settings was less than 5%.

Jan 1, 1985

By S. P. Goplen, M. Henriksen, T. F. Barron

In the past decade, numerous large scale drilling projects have made use of reverse circulation air lift methods. Reverse air lift pumping can be established by injecting gas into a column of liquid; the subsequently decreased density of the gas-liquid mixture allows atmospheric pressure outside the lift conduit to establish flow. The rate of flow can be controlled by varying the gas to liquid ratio. A typical reverse circulation air lift system is depicted in [Fig. 1]. Allen 1 has described a number of reverse air lift drilling projects. Although cited examples are generally related to large diameter holes, the method has seen use in other applications such as sand dredging, chemical pumping, water well pumping. and continuous coring. One particular benefit obtained with enclosed reverse circulation drilling is elimination of lost circulation. The required air/water ratio for pumping at a given submergence and lift has been established experimentally by Gibbs.2 His data, however, do not reflect sensitivity of flow rate to air/water ratio. Further, in Gibbs' work, air apparently is injec-

Jan 1, 1980

By W. V. Green

Creep of tantalum was measured at temperatures from 0.6 to 0.89 of the absolute melting temperature. The creep curves include first, second, and third stages. Steady-state creep rate depends on the fourth power of stress. The activation energy for creep throughout this temperature range is approximately 114 kcal per mole, measured by the aT technique. Subgrain formation occurs as a result of creep strain, and pile-up dislocation arrays are observed in etch-pit patterns. BECAUSE of its high melting point-which is exceeded only by those of rhenium and tungsten—and its high room-temperature ductility compared to most of the other high-melting-point metals, tantalum will undoubtedly be utilized in an increasing number of high-temperature applications. Alloying studies directed toward increased high-temperature strength must use data on tantalum itself as a base line in order to evaluate the effectiveness of the alloying additions. However, to date, no systematic study of creep of tantalum at temperatures above one-half of its melting point has been reported in the literature. Conway, Salyards, McCullough, and Flagella1 have measured linear creep rate of tantalum sheet as a function of stress, but at only one temperature, 2600°C. This paper describes a relatively thorough study of the high-temperature creep of tantalum. METHOD Material Tested. The commercially supplied, l/2-innch-diameter tantalum rod used for this work was electron-beam-melted, cold-forged, rolled, swaged, cleaned chemically, and vacuum-annealed for 1 hr at 1000°C, all by its manufacturer. The vendor's analysis included 60 to 170 ppm C, 3.4 to 4.2 ppm H, 60 to 80 ppm 0, 15 ppm N, and a hardness ranging from 66 to 81 Bhn and averaging 76 Bhn. Creep eimens Used. Two creep-tested specimens are shown in Fig. 1. The 1/4 in.-diameter gage section was 3/4 to 1 in. long, and terminated either at shoulders 5 mils high or at 20-mil-diameter tantalum wires spot-welded to the circumference of the gage section. Both kinds of shoulders served equally well as fiducial marks for optical strain measurements. The spot welding did not alter the creep behavior in any detectable way; the 5-mil- high sharp shoulders did not result in any detectable localized effect on the strain. Before testing, each tensile bar was first mechanically polished -id then electrochemically polished according to the method referred to by Forgeng2 as the "Thompson Ramo Woolridge" method, which was suitable for tantalum after small adjustments of technique were made. Two tensile bars tested at low stresses had 1/8-in.-diameter gage sections and utilized only the weight of the bottom grip for the applied load. Although these diameters were smaller than were desired for other reasons, applied loads were known with high precision in the tests in which they were used. Testing Procedure. Two different constant-load creep-testing machines were employed, one of which has been described by Smith, Olson, and Brown.3 In both, the tensile bar is held vertically on the axis of a cylindrical tungsten tube or screen heater by threaded tungsten grips. The tensile bars and associated grips are heated by radiation from the incandescent heaters, which are heated by their own electrical resistance. Both testing machines use pins to hold the bottom grips in place. The load is applied to a tensile bar through hanging weights, a constant force-multiplication lever, a pull rod sealed to the chamber lid, and a top grip threaded to the pull rod at one end and to the tensile bar at the other. In one machine, the vacuum seal is a bellows with a low spring constant; in the other, the seal involves a rotating "0 ring". With the latter, rotation is converted to translation with a crank shaft, so that elongation of the tensile bar is accommodated with no change of tensile load. The incandescent tensile bar is viewed by an external optical system through slots in the radiation shields and heater, and an enlarged image is projected on a ground-glass screen. Gage-length measurements are made on this image with cathetometers on traveling microscopes. With regard to creep-test results, the two machines were identical. Thorium oxide coatings were applied to the threaded ends of the tensile bars, to prevent diffusion welding of the tensile bars to the grips during testing. Specimen temperatures were measured with an L. & N. optical pyrometer which had been calibrated against a standard carbon arc, and were corrected fir window absorption by calculation from the measured spectral transmittance of the quartz observation windows. Longitudinal temperature gradients in the tensile-bar gage length and temperature drifts during testing were detectable but small, and were estimated to be 10°C or less. Accuracy of temperature measurement was confirmed by comparing the temperature measured on the surface of a special

Jan 1, 1965

By J. L. Lytton

The flow-stress recovery of high-purity aluminurn following a 10 pct tensile prestrain was studied in terms of a fractional flow-stress recovery parameter fr. The flow-stress recovery behavior was related to the dislocation arrangements using transmissiort electron rnicvoscopy. During recovery at 120° and 160°C, nearly stable strength levels were attained, the strength level for 120°C recovery being greater than that for 160°C. This stabilization of flow stress was related to the formation of meta-stable dislocation networks bounding nearly perfect cells. Both network formation and the annealing of dislocation loops were found to be recovery mechanisms, and the stronger metastable strength level joy 120°C recovery was related to a smaller average cell size. Analysis of the networks was consistent with the reaction of sets of dislocations with a/2 (110) Burgers vector to give product Burgers DURING isothermal annealing of cold-worked metals, a degree of softening occurs without re-crystallization, and the processes responsible for this change are termed recovery processes. During recovery annealing, the dislocations generated during cold work become rearranged into low-energy configurations, and as much as 50 pct of the stored energy is released."' The relationship between this rearrangement of dislocations and mechanical behavior is of considerable importance, since the dislocation substructures formed during recovery provide a significant degree of low-temperature strength3j4 and can favorably alter the course of primary creep at high temperatures.4 The purpose of the present study was to relate the flow-stress recovery behavior of high-purity aluminum to the substructural modifications that occur. Electron transmission microscopy was therefore employed for direct observation of dislocation substructures at various stages of recovery following 10 pct prestrain. Several investigators5-' have proposed that dislocations can become rearranged or lost during the preparation of thin foils. It was found early in the present study that the dislocation structures in the thicker regions of the foils changed in a systematic way during the course of recovery. Therefore, it is unlikely that substantial losses or rearrangements occurred during thinning. This point will be discussed in more detail later. The results of various investigators indicate that recovery processes in fcc metals can result in release of 50 pct or more of the total energy stored in the as-prestrained metal, this percentage decreasing with increasing prestrain.' Alloying elements or impurities tend to increase this percentage. The release of stored energy of fcc metals during recovery appears to occur by 1) annealing of point defects if the deformation occurred at sufficiently low temperaturesg and 2) rearrangement of dislocations into low-energy Configurations.1,2In bcc metals, the annealing of dislocation loops has also been observed during recovery after prestrain,10-12 and it has been proposed that this is a recovery mechanism for unidirectionally strained fcc metals.' The density of dislocations in bcc metals has not been observed to decrease appreciably during recovery,10 although the formation of regular dislocation networks has been observed. has shown that the formation of such networks can result in elimination of long-range stresses and can lead to significant release of stored energy without dislocation annihilation. It might thus be expected that network formation is a significant recovery mechanism in fcc metals, although extensive network formation has apparently not been reported in controlled recovery experiments. The formation of sub-boundaries in aluminum has been observed by various investigators13'17 during recovery studies of aluminum, but the structure of these boundaries was not resolved. In this regard, it is significant to note that Bailey and Hirsch,' using transmission electron microscopy, detected no network or sub-boundary formation during recovery of 99.99 pct Ag. Furthermore, Clarebrough et al.2 found no such rearrangements during recovery of copper. EXPERIMENTAL PROCEDURE The high-purity aluminum used in this investigation was obtained in the form of 0.125-in.-thick sheet. Spectrographic analysis revealed that the sheet was 99.995 pct A1 with the following weight-percent impurities: 0.001 Cu, 0.002 Fe, 0.001 Si, and 0.0004 Mg. The as-received sheet was in the heavily cold-rolled condition. The as-received sheet was cold-rolled at room temperature to 0.040-in.-thick sheet in the longitudinal direction, which was the original rolling

Jan 1, 1965

By J. N. Maycock, P. W. M. Jacobs

Previous measurements of the thermoelectric power of ionic crystals are reviewed briefly. It is concluded that, while extensive measurerements are available on systems in which the electrode M has a cation in cornon with the sall MX, there is as yet little modern work on systems in which the metal electrode M' does not haue a calion in common with the salt. We haue now measured the thermoelectric power of- single cryslals of KC1 and of KC1 + SrCl2 between plati.nu?n electrodes over a much wider range of temperature than before. individual ionic heats of transport, which, while probably not very accurate, are of a reasonable order of magnitude, are obtained from this data on the basis of an assumption that charge carriers do not cross the electrode/salt interface. RELATIVELY little work has been done on thermal diffusion in ionic crystals. Reinhold and coworkers1-I measured the thermoelectric power and Soret effect in silver and cuprous salts and their mixed crystals. One electrode was kept at constant temperature and electromotive force was measured as a function of the temperature gradient. This is not a satisfactory technique if the results are to be compared with theory; rather should the electromotive force be measured for small temperature differences as a function of the mean temperature of the two electrodes. They used electrodes having the same cation as the salt. Patrick and Lawsons measured the thermoelectric power of AgBr and of AgBr containing 0.25 mole pct CdBr2 using silver electrodes and temperature gradients of 10°C in the temperature range 100° to 400°C. The results were analyzed using the Teltow9 values of the ratio of the mobility of the two types of charge carrier (cation vacancies and interstitials) found from conductance measurements and the wagnerlo estimate of the heterogeneous contribution to the thermopower, Ohet They obtained values of qi = 0.017 ev and q$ = -0.385 ev for the heats of transport of interstitial Ag ions and cation vacancies, respectively. Their data has been reanalyzed by Haga using the corrections to the Wagner formula for ehet given by Howard andLidiard; Haga found ev. Christy et a1.14 have measured the thermopower of AgBr containing 0.01 to 1.0 mole pct CdBr,. They analyzed their results in terms of the theory of Howard and Lidiard and found that excellent agreement with the theory was obtained if q5 + : + hF was set equal to 0.70 ev at 175°C and equal to 0.58 ev at 250°C. Since Teltow's value for hF, the enthalpy of formation of a Frenkel defect pair, is 1.27 ev, this means that qt + q: increases in magnitude from -0.57 ev at 175°C to -0.69 ev at 250°C. This result is in poor agreement with Patrick and Lawson's value of -0.37 ev for pure AgBr (for which the corrections to the Wagner estimate for ehet are very small). christy1' has also reported thermopower measurements for pure silver halides and for the systems he finds that qr + qt for AgBr increases in magnitude from about -0.55 ev at 150°C to about -1.1 ev at 400°C. The temperature dependence of the sum of the heats of transport in AgCl is very similar in magnitude. The sum qi + q cannot be decomposed into the individual interstitial and vacancy heats of transport without a knowledge of the entropy contribution from the change in the lattice vibrational frequencies around the interstitial and vacancy. Despite this it seems an inescapable conclusion from Christy's analysis that and -6 = Q Ag are quite strongly temperature-de pendent and that -q: is much greater in magnitude than the corresponding activation energy for vacancy migration, +0.37 ev. It remains a mystery as to why the data for pure AgBr are fitted so well by the assumption of temperature-independent heats of transport if association of impurity ions and vacancies is neglected.l The values for q$ and q: so obtained are also much more in line with those expected from a simple kinetic interpretation of the heats of transport due to wirtz.17 Christy and Hsueh have also measured the thermopower of CuCl between copper electrodes; 0 for pure CuCl is comparable with that for the silver halides but, owing to the limited solubility of divalent cation impurities it was not found possible to deduce values for the heats of transport. In contrast to these extensive measurements on cells of the type M MX 1 M, there have been relatively few attempts to measure the thermoelectric power of cells of the form M' 1 MX I M'. (We specifically exclude from discussion cells of this type in which the metal electrodes M' are in contact with gas containing a controlled partial pressure of either M or X,, since in these cells the electrochemical reactions are analogous to those of the first type.) The thermoelectric power of Pb12, PbC12, TlC1, TlBr, TlI, NaNO3, and KNO 3 between platinum electrodes was measured by Thie1e.l3 In discussing these measurements Holtan20 asserts that the thermopotential initially fluctuated wildly and even changed sign before approaching a steady value. A high degree of irreproducibility is also evident in the work of Nikitinskaya and Murin21 who first studied the thermopower of NaCl and KC1 between platinum electrodes. Much better reproduci-bility was achieved in our earlier measurements on KC1;22 these were, however, confined to a relatively narrow temperature range and one of the objects of the work reported in this paper was to extend the temperature range of the measurements of the thermoelectric power 8 of KC1. The only other published

Jan 1, 1967

By W. D. Forgeng, R. L. Folkman, D. C. Hilty

The solubility of oxygen in molten Fe-Cr alloys has been determined at 1550° , 1600°, and 1650°C for alloys containing up to alloyshasbeenabout 50 pct Cr and found to decrease as chromium increases to 6 pet and then to increase gradually. Phase relations in the Fe-Cr-0 system at steelmaking temperatures have been evaluated and two previously unreported oxides have been identified. OPERATIONS in the melting and refining of chromium steels are dependent to a major degree on the reactions of chromium and iron with oxygen and are primarily directed toward controlling and modifying these reactions to secure maximum advantage in the utilization of chromium. Although fairly effective practices have been developed empirically, understanding of the specific reactions is limited. Moreover, the ability of molten steel to dissolve oxygen that subsequently precipitates as oxide inclusions during solidification is well known, so that clarification of the effect of chromium on the nature and mechanism of formation of these inclusions is desirable. Study of the problem indicated that increased knowledge of the fundamental Fe-Cr-0 system is essential to further technical and economic improvement. Consequently, an investigation of the influence of chromium on the solubility of oxygen in molten iron and of phases and phase relations in the Fe-Cr-0 system was undertaken at the Metals Research Laboratories of the Electro Metallurgical Co. as part of a general program on the effective utilization of chromium in chromium steel production. Experimental Procedure All of the experimental runs made during this investigation were carried out in the rotating crucible induction furnace which has been described in detail in a previous publication.' In review, the principle underlying this furnace is that rotational forces in the crucible cause the molten metal to assume a concave shape in such a manner that the slag is contained in the molten metal cup, thereby minimizing slag/crucible contact and subsequent reaction. Practically all of the heats were melted in commercial-quality magnesia crucibles of the type usually furnished for laboratory induction furnaces. All of the runs were made under an argon atmosphere after the furnace chamber had been degassed. Bath temperatures were controlled by Pt—Pt-10 pct Rh thermocouples. The basic furnace charge consisted of a premelted 12 to 15 lb electrolytic iron slug which had been cast to a shape convenient for fitting into the rotating furnace crucible. A typical analysis of the electrolytic iron slugs is given in Table I. For certain runs, it was desirable to melt down charges containing high initial chromium contents. In these cases the chromium was added to the electrolytic iron during the premelting operations. Chromium was added to the rotating furnace bath in the form of electrolytic chromium of the analysis given in Table 11. In all of the constant temperature runs, the standard procedure was to melt down the electrolytic iron or alloy slug under vacuum, admit argon to slightly greater than atmospheric pressure, and adjust rotational speed to develop a well formed "cup" on the bath surface. The melt was then saturated with oxygen by an addition of ferric oxide and the temperature of the bath adjusted to within +5°C of the desired level. At this point the heat was permitted to come to equilibrium prior to sampling or further addition. This time interval was varied from 15 min to 2 hr but generally was about 20 min. After sampling, the desired chromium addition was made and the bath again equilibrated prior to subsequent sampling. This cycle of addition and sampling continued for the duration of the run which lasted from 4 to 8 hr. At the end of this period, power was shut off and the bath allowed to solidify in the furnace. Quenched metal samples were taken from the equilibrated melts by means of the "Taylor sampler" which has been described by Taylor and Chipman.' Before being submitted to chemical analysis, all samples were carefully examined for surface slag occlusions and cold shuts. Later in the study, each sample was radiographed and examined metal-lographically in cross-section to determine the presence of internal defects. On the basis of these examinations, sound and apparently clean specimens were selected from the Taylor samples for chemical analysis.

Jan 1, 1956

By John R. M. Hill, Gerald Zink, Fun-Den Wang

The work described in this paper is sponsored by the Bureau of Mines for the purpose of accelerating the drilling of roof bolt holes and reducing the quantity of materials needed to fill each hole. A high-speed, small-hole drill has been fabricated and tested in the laboratory. High Priority has been given to safety, reliability, and compatibility with underground coal mining practice. The combination of drag bits and erosion jets is designed for high penetration rate, long wear life, and uniform hole size in a variety of sedimentary strata. A reliable high-pressure, high-speed swivel feeds water to the bit at about 4 L/min (1 gpm). The duplex hydraulic intensifier which drives the jets has a 40-kW (30-hp) capacity. Results of recent full-scale laboratory testing (Now. 1977) are presented.

Jan 12, 1979

By C. E. Lundin

The Ce-H system was investigated in the temperature range, 573° to 1023°K, and the pressure range, 10-3 to 630 Torr, as a function of 'composition up to 72 at. pct H. Families of isothermal arid isopleth curves were plotted from the pressure-terr~perature-composition relationships. From these curves the solubility relationships were determined for the system. The isopleths are analytically represented by equilibrium dissociation pressure equations. The relative partial molal enthalpzes and entropies of solution of hydvogen in the systerrz were calculated fronz the dissociation pressure equulions and are tabulated. The integral free energies, enthalpies, and entropies of mixing in the Ce-H system were determined from the relative partial quantities and are also tabulated. The standard free energy, enthelpy, and entvopy of reaction of the dihydride phase at kcal per kcal per mole H2, and ?S° = -34. 1 cal per deg mole H2, respectively. The equilibrium dissociation pressure equation in the two-phase region is: UNTIL recently very little was known of the detailed solubility and thermodynamic relationships of the Ce-H system. Two previous investigations1,2 are noteworthy. However, significant discrepancies and omissions exist on analyzing them. The work of Mulford and Holley1 on cerium did not clearly delineate the boundaries of the two-phase region, Cess - CeH2-x. The plateau partial pressures were not thoroughly defined and were considerably displaced in pressure compared to those from the work of Warf and Korst.2 These latter authors concentrated their studies primarily from 823° to 1023°K in the pressure range of 1 to 760 Torr. No data were determined to outline the regions of primary solid solubility and the hydride phase. Also the establishment of the plateau partial pressures was rather limited in scope. In neither work was a treatment conducted of the relative partial molal enthalpies and entropies of solution of hydrogen in the single-phase regions and the integral thermodynamic quantities of mixing throughout the system. Therefore, it was the objective of this research to determine the complete equilibrium solubility relationships and thermodynamic data for the system by pressure-temperature-composition studies. EXPERIMENTAL PROCEDURE The cerium metal for this study was donated by the Reno Metallurgy Research Center of the Bureau of Mines. Total impurity content was 0.13 pct with only 60 ppm O. The metal was checked metallographically and contained only minor amounts of second phase compared to cerium from other sources. Specimen preparation was done in a dry box flushed with argon gas. The surface of a small rectangular piece of cerium (about 0.2 g) was filed with a clean, mill file. Final weighing was done in a tared enclosed vial containing argon gas. The specimen was then loaded quickly into the reaction chamber which was purged several times with high-purity hydrogen gas and then allowed to pump to about 10-6 Torr. The furnace was heated to the reaction temperature and the run started. The equipment used to conduct the hydriding was a Sievert's-type apparatus. Basically it consisted of a source for pure hydrogen, a precision gas-measuring burette, a heated reaction chamber, a McLeod gage, and a mercury manometer. Pure hydrogen was supplied by the thermal decomposition of uranium hydride. The 100-ml precision gas burette was graduated to 0.1-ml divisions and was used to measure the quantity of gas and admit it to the chamber. The reaction chamber was a quartz tube. Prior to each run, the cerium specimen was wrapped in a tungsten foil capsule to prevent reaction of the cerium with the quartz. Control of the temperature was achieved within ±1°K. Pressures in the manometer range were measured to ±0.5 Torr and in the McLeod range (10-3 to 5 Torr) to ±3 pct. The compositions of hydrogen in cerium were calculated in terms of hydrogen to cerium atomic ratio. These compositions were estimated to be ±0.01 H/Ce ratio. The technique used to study the equilibrium pressure-temperature-composition relationships of the Ce-H system was to develop experimentally a family of isothermal curves of composition vs pressure. The range of pressure through which each isotherm was developed was from 10-9 to about 630 Torr in the temperature interval, 573° to 1023°K. RESULTS AND DISCUSSION The hydriding characteristics of cerium are iso-morphous with those of the elements of the light-rare-earth group (lanthanum, cerium, praseodymium, and neodymium) wherein the region from the dihydride to trihydride is continuously single phase.' The structure of this phase is fcc.3 The heavy rare earths form a trihydride,2 which is hcp, separated by a two-phase region from the fcc dihydride phase. The Ce-H system is represented by the family of experimental isotherms in Fig. 1. Due to the small scale required to draw the curves, the experimental points are omitted; however, a total of 240 experimental data points were taken to prepare these curves. The solubility relationships can be deduced therefrom. Three distinct regions of partial pressure and composition can be seen. The region of cerium solid solution is represented by the rapidly rising isotherms in the dilute composition range. In accordance with Gibbs Phase Rule only one solid phase, the cerium solid so-

Jan 1, 1967

By E. D. Gardner

AGAIN in 1945, the fourth year of World War 11, the American mining industry met the necessary demand made upon it for metals. Lack of labor prevented full production in some districts; maximum output, however, was maintained with the man power available. Development work and maintenance of mechanical equipment were neglected in favor of immediate production. Drafting of the younger men continued throughout the year, and the loss of personnel to war industries with higher wage rates continued up to "V-J" Day, Aug. 14. Labor shortages were more critical in 1945 than in 1944 though the man-power situation eased for some districts in the last quarter of the year. The trend in mining for the most part was to increase tons per man-shift by continued increased mechanization and refinements in methods and practices; larger equipment was installed where practicable. Labor shortages, together with the current higher wage rates, have advanced mechanization several years ahead of normal progress. The manpower shortage and the employment of inexperienced men had the effect of decreasing the average efficiency of the individual workman, but this condition was largely balanced by improved organization, greater efforts to improve labor relationship, and increased use of incentive pay systems. Safety instruction was emphasized, personnel contacts were increased, and more frequent foremen meetings were held to clarify contract agreements. Many of the large companies maintained schools to train green workmen.

Jan 1, 1946

By R. J. Robbins, D. L. Anderson

A tunnel boring machine has potential use in al- most any type of mining where the access shaft (or adit) is large enough or can be made large enough for its initial entry and where the orebody is of sufficient size to warrant its use. Some time will inevitably be lost in negotiating curves or making lateral moves and moving from level to level. Nevertheless, if the orebody is sufficiently large, advance scheduling can minimize the lost time encountered in such moves. Ideally, a mine will be planned for the use of these machines, thus eliminating access and transport problems. From the viewpoint of time involved, the rate of advance by boring as compared to conventional means is worthy of review. For instance, the Blanco Tunnel, one section of the Bureau of Reclamation's San Juan-Chama Project in southern Colorado, was bored in competent sedimentary rock with the following performance:

Jan 7, 1967

By Allan E. Martin, Harold M. Feder, Irving Johnson

The cadmium-uranium system was studied by thermal, metallographic, X-7-ay and sampling techniques; special emphasis was placed on the establishment of the liquidus lines, The single inter metallic phase, identified as the compound UCd11 melts peritectically at 473°C to form a-umnium and melt containing 2.5 wt pct uranium. The cadmium-rich eutectic (0.07 wt pct uranium) freezes at 320.6°C. Solid solubilities in uraizium and cadmium appear to be negligible. Between 473°C and 600°C the liquidus line is retograde. NO publication relating to the cadmium-uranium phase diagram was found in the literature. The establishment of this diagram was of considerable interest to us because of a possible application of the system to the pyrometallurgical reprocessing of nuclear fuels. Analysis of liquid samples, metallographic examination, thermal analysis, and X-ray diffraction analysis were used to establish the phase diagram from about 300° to 670°C. Particular emphasis was placed on the establishment of the liquidus lines. The same system was concurrently studied in this laboratory by the galvanic cell method.' Both studies benefited from a continual interchange of information. MATERIALS AND EXPERIMENTAL PROCEDURES Stick cadmium (99.95 pct Cd, American Smelting and Refining Co.) contained 140 ppm lead as the major impurity. Reactor grade uranium (99.9 pct U, National Lead Co.) was most often used in the form of 20-meshspheres. This form was particularly suitable because it does not oxidize as readily as finer powder. The liquidus lines were determined by chemical analysis of filtered samples of the saturated melts. The liquid sampling technique is described elsewhere2 alumina crucibles (Morganite Triangle RR), tantalum stirring rods, tantalum thermocouple protecthecadmiumtion tubes, Vycor or Pyrex sampling tubes, and grades 60 or 80 porous graphite filters were used. Uranium dissolves in liquid cadmium rather slowly. In order to achieve saturation of the melts it was necessary to modify the procedure of Ref. 2 by the use of more vigorous stirring and longer holding periods (at least 3 hr) at each sampling temperature. The samples were analyzed for uranium by spectro-photometry (dibenzoyl methane method) or by polar- ography. The analyses are estimated to be accurate to 2 pct. Thermal analysis was performed on alloys contained in Morganite alumina crucibles in helium atmospheres. Standard techniques were employed; heating and cooling rates were about 1°C per min. For the determination of the peritectic temperature, Cd-10 pct U charges were first held for at least 50 hr at temperatures in the range 435° to 460°C to form substantial amounts of the intermediate phase. For the determination of the effect of cadmium on the a-p transformation temperature of uranium, charges of Cd-25 pct U (-140+100 mesh uranium spheres) were first held near the transformation temperature, with stirring, to promote solution of cadmium in the solid uranium. The holding times and temperatures for these treatments were 18 hr at 680°C for the cooling run and 28 hr at 630°C for the heating run. Alloy specimens for X-ray diffraction and metallographic examination of the intermediate phase were prepared in sealed, helium-filled Vycor or Pyrex tubes. Ingots from solubility runs and thermal analysis experiments also were examined metallographically. Crystals of the intermediate phase were recovered from certain cadmium-rich alloys by selective dissolution of the matrix in 20 pct ammonium nitrate solution at room temperature. Temperatures were measured with calibrated Pt/Pt-10 pct Rh thermocouples to an estimated accuracy of 0.3°C. However, the depression of the freezing point of cadmium at the eutectic is estimated to be accurate to 0.05°C because a special calibration of the thermocouple was made in place in the equipment with pure cadmium just prior to the measurement. EXPERIMENTAL RESULTS The results of this study were used to construct the cadmium-uranium phase diagram shown in Fig. 1. This diagram is relatively simple; it is characterized by a single intermediate phase, 6 (UCd11), which decomposes peritectically, and which forms a eutectic system with cadmium. The solid solubilities in the terminal phases appear to be negligible. An unusual feature of the diagram is the retrograde slope of the liquidus line above the peritectic temperature. The Liquidus Lines. The liquidus lines above and below the peritectic temperature are based on three separate solubility experiments. The data are shown in Fig. 1 and are given in Table I. It is apparent from the figure that the solubility data obtained by the approach to saturation from higher temperatures fall on substantially the same lines as those obtained

Jan 1, 1962

By B. H. Caudle, L. G. Davies, I. H. Silberberg

This paper presents a method of predicting the recovery and performance of a five-spot steam injection project, in which a realistic approach to pattern sweepout efficiencies is made. Published methods for radial systems were modified for the five-spot pattern by approximating the stream lines with straight lines radiating from the injection well and then converging to the producing well. In each radial segment, the position of the steam front and the temperature profile ahead of the steam front were determined by heat balance equations, which included an estimation of heat losses to surrounding formations. The location of the saturations behind the cold water front was determined from a Buckley-Leverett solution to the material balance equation. Results from this program show steamflood recovery in a five-spot pattern to be considerably less than that predicted for true linear or radial flow systems. For a specific reservoir containing 900-cp oil, a steamflood in a purely radial flow system was predicted to recover more than 75 percent of the original oil in place when 2 PV of water had been injected as steam. A five-spot steamflood with otherwise identical properties was predicted to recover 10 percent of the original oil in place when 0.15 PV of water had been injected as steam and to recover almost no oil thereafter. A cold water five-spot flood in this system was predicted to recover approximately W percent of the oil in place with I PV of water injected. For a five-spot pattern in an example reservoir with 10-cp oil, steam injection similarly showed lower ultimate recovery than water injection but no improvement in recovery rule. Introduction The thermal recovery method considered in this study is steam injection in a five-spot pattern. Pattern steam injection has been given little attention in the past, possibly because of some rather obvious disadvantages. Unless steam temperature is maintained throughout the entire swept area, the process will revert to simple waterflood with all heat being lost prior to reaching the oil bank. Also, the oil viscosity reduction takes place near the steam front and not around the producing wellbore, so that low producing rates must still be endured. This is the reason for the success of the steam stimulation, or cyclic injection, in which the fluids are produced from the same well used for injection. On the other hand, steamflooding can offer some advantages. Oil displacement is by four methods: (1) mechanical displacement by the condensed water, (2) viscosity reduction of the crude oil, (3) swelling of the crude oil, and (4) distillation of the crude oil in the steam zone. Although dependent upon the crude, laboratory experiments have shown displacements up to 80 percent by steamflooding. In addition, steam is a good heat transport medium, since it is cheap and has a high heat content. Previous Investigations Previous publications have reported methods for predicting recovery in a steamflood for linear and radial systems. Since no pattern sweep efficiency is taken into consideration, the recovery even from a radial system must be greater than from more realistic geometries such as the very common five-spot patterns. Probably the broadest coverage is given by Willman who reported experimental results and offered a method of predicting recovery for a radial flow system. They concluded that both hot water and steam injection recover more oil than an ordinary waterflood, and that steam injection could yield recoveries "as much as 100 percent greater than by water flood." They also concluded that both the heat requirements for a reservoir and the residual oil remaining in the reservoir after steam injection were independent of the amount of oil originally in place, that short exploitation times were desirable, and that a high percentage of net sand in the reservoir with a high initial oil saturation was desirable. The method assumes that the flood occurs in three concentric cylindrical zones: (1) an inner steam zone, (2) a central hot water zone, and (3) an outer cold waterflood zone. Displacement in the steam zone is based on laboratory-determined residual oil saturations while the hot water and cold water zones use the conventional Buckley-Leverett equations. Although the results shown by Willman et al. are for a radial system flowing out from the well to an assumed external circular boundary, their equations did

Jan 1, 1969

By J. E. Stukel, J. Cocubinsky

A CONSIDERABLE amount of information is available on the equilibrium distribution of manganese between slag and metal under oxidizing conditions. These data have increased our knowledge of the manganese reactions in the open hearth, ladle, and ingot mold. In contrast, there is a paucity of data on the slag-metal distribution of manganese under reducing conditions. The purpose of the present investigation was to study the equilibrium distribution of manganese between blast-furnace type slags and iron saturated with carbon. Experimental Method Furnace: The induction furnace used for the experiments is shown in Fig. 1. A 1 in. pipe, attached to the transite cover, was fitted with a window through which the charge could be observed. Material could be introduced into the furnace through a tee and plug without removing the cover. A graph-it cylinder (3 in. ID and 10'/2 in. long), centered within the induction coil, was used as a heating element. During a test, a zircon plug kept the top of the furnace from becoming too hot from heat radiation. At the bottom, a graphite block on the vertical center line of the furnace and extending 1 1/2 in. into the coil, was used as a support for the graphite crucibles containing the melt. The graphite crucibles, machined from regular carbon electrode stock, had a 2% in. OD with 3/16 in. walls and were 5% in. long. The fumes present in the furnace during the early part of a run made optical readings uncertain. A noble metal thermocouple was, therefore, adopted to measure the temperatures. The arrangement used, shown in Fig. 1, allowed the silmanite protection tube to be replaced with a minimum effort. The thermocouple was calibrated against a standard Pt-Pt-Rh thermocouple in a fused quartz protection tube. The latter was inserted in the molten iron by removing the glass window on the cover. The lower couple was found to be very sensitive to temperature changes. To insure accurate temperature readings, the graphite crucibles were made to fit tightly against the silmanite protection tube. Further, to avoid contamination of the thermocouple by carbon, the silmanite tube was changed and the calibration procedure was repeated at frequent intervals. By using this temperature measuring technique, the furnace was easily held within *1O°C of the desired temperature. Because of the small free space in the furnace, no attempt was made to control the atmosphere. It

Jan 1, 1955

By Roy P. Full, Robert M. Grantham

Regional structural adjustments in early Tertiary time resulted in the development of the Republic graben, a major down-dropped block that is from 6 to 10 miles in width and more than fifty miles in length. The graben became the center of extensive volcanic activity during Eocene and Oligocene time, resulting in a thick sequence of water-laid tuffaceous sediments, volcanic flows, and associated intrusives. A younger series of sediments, pyroclastics, and flows were deposited in structural depressions within the graben following the period of widespread volcanic activity. The Republic mining district is located along one of the major intragraben structural zones, where continuing subsidence during the period of volcanic activity resulted in an increased thickness of flows and associated flow breccias and pyroclastics. Intrusive masses in part healed early graben-forming faults, but later subsidence reopened old faults and created new fracture zones which later became the control for the gold-quartz veins. Considerable block adjustment along the subsidence area is evidenced by the structural pattern in the mines, and telescoped vein structures indicate north-south compressional stresses and east-west graben-forming tensional stresses prior to and during the emplacement of the veins. The veins, varying from a few feet to more than 50 feet in width, are filled primarily by fine-grained quartz, commonly chalcedonic or porcelain-like in appearance. Finely laminated dark-gray to black concentric banding within the veins generally distinguishes the better-grade ore zones, which contain finely disseminated sulfides and ore minerals that include principally electrum, stephanite, naumannite, and native silver.

Jan 1, 1968

By WALTER B. JONES

IN ALABAMA there are three distinct groups of bauxite deposits, as follows: (1) Cambro-Ordovician contact with the principal-deposits located in Talla-dega, Calhoun, DeKalb, and Cherokee Counties, and in adjacent portions of the State of Georgia. (2) Midway-Nanafalia contact, with the principal deposits in Barbour and Henry Counties, and in adjacent portions of Georgia; also in North-eastern Mississippi. (3) Mississippian - Cretaceous contact, with a group of deposits centered around Margerum in Colbert County. For the purpose of more clearly describing bauxite mining in the state, past, present and possible future, these three groups will be described separately.

Jan 1, 1934

By Strathmore R. B. Cooke, Robert E. Brandt

EARLIER work1,2 has shown that the strength developed by fired magnetite pellets containing silica or silicates is due to three separate effects. Two of these are associated with the formation of slag in the interior of each pellet at temperatures above 1000°C, where the atmosphere is substantially though temporarily neutral. The third is independent of the silica content and is responsible for the development of a hard shell around the pellet during the initial stages of firing, a condition which permits the pellet to assume the increasing load of the overlying burden and prevents extrusion of the slagged and semi-liquid interior. Pellets made from hematite concentrates do not show these effects unless specific additives are incorporated, and it is these differences in behavior which in large part account for the difficulty in producing satisfactory pellets from such concentrates. Elsewhere it has been stated that "the most important factor responsible for the development of strength in fired magnetite pellets containing no additive is the oxidation of magnetite to hematite and the subsequent recrystallization and grain growth of this constituent."1 The object of the investigation reported in the present paper was to study in detail the mechanism described above and to evaluate its contribution to the strength of the fired pellet compared with other possible mechanisms, excluding slag bonding. This was effected by placing together polished faces of two cubes prepared from specific minerals and then heating them under constant pressure at different temperatures both in air and in nitrogen.

Jan 4, 1954

By Howard S. Strouth

SINCE the days of the Conquistadores, people have told exaggerated tales of the wealth and possibilities of Mexico and Central and South America, and the mining fraternity has never been known to exaggerate any less than any other professional group known to man or beast. However, during a short stay in Mexico one can probably hear more whoppers than at any other time, when dozens of mining propositions are thrust across the desk, and it is not necessary to remind anyone that a listing of the do's and don't's for Mexico requires special mention of the fact that most mining propositions offered south of the border eventually turn out to be a beautiful fairy tale. The following is not suposed to be either an exact description of Standard Mining Corp.'s operations in Mexico by its mining associate, the Corporacion Minera y Beneficiadora Anahuac, S.A., or the last word as to the most economical way to start such an operation. But rather it is the sum total of the recent experiences of the writer while commencing such an operation in 1951-52 with the help of many qualified gentlemen.

Jan 6, 1953

By Jose A. Ruiz

INTRODUCTION For heterogeneous non-catalytic solid-gas reactions carried out in fluidized bed reactors, nominal bed temperature is an average value between gas and solid. For highly exothermic reactions, actual particle temperature can be up to hundred degrees above termocouple temperature, since heat dissipate at slower rate than heat generation during some steps of transformation. These micro instabilities at particle level can displace thermodynamic equilibrium from the desired phase to others. This effect is important when relatively narrow range of phase stability exists, like in sulphation roasting of sulphides, where bed discharge contains, in addition to the desired sulphate others metastable phases such as basic sulphate and ferrite. For example, for copper-iron sulphide concentration roasted below 680°C, no cupric ferrite is formed, as shown by Jakob et al., therefore the separate Kellogg's stability phase diagrams Cu-S-O represent the roasting (Fig.l). At temperature above this one, like 760°C for example, phase stability changes from CuSO4 to the basic sulphate Cu0•CuSO4. Solid state reaction between Cu0•CuSO4 and Fe203 also occurs to form cupric ferrite, Cu0•Fe2O3, therefore the Cu-Fe-S-O Kellogg's phase diagram of Fig. 1 (continuous line) represents this condition of roasting. Although both Cu0•CuSO4 and Cu0•Fe2O3 are metastable phases under normal operating conditions of sulphation roasting(1-10% SO2, 1-10% 02 and 680°C, points A and B,Fig. 1) sulphation of these species and particularly ferrite are slow and limited due to diffusional control. This explain why reactors discharge contains several phases: CuSO4, Cu0•CuSO4, CuO•Fe203 plus small amounts of CuS and FeS due to the baclonixed conditions of fluidized bed reactors. The presence of cuprous ferrite due to reducing conditions inside individual particles also occurs, but in very limited extent at the reaction interface, as it is demonstrated by the low soluble iron levels of calcines. On the other hand, the presence of cupric ferrites can be explained only due to the higher temperature achieved by particles, since below 680°C cupric ferrite formation does not take place. [ ] This phenomena also occurs for others non-ferrous metal sulphides concentrates roasted under sulphation conditions, such as 7n, Co and Ni. Therefore the prediction of discharge composition of fluidized beds is not possible based only on kinetics and mechanistics models alone or purely thermodynamical considerations, since all factors should be integrated to describe the overall phenomena. SINGLE PARTICLE TRANSFORMATION Assuming a first order reaction with respect to the gas and zero for solid, such as

Jan 1, 1984

US 4,134,944-Production of iron oxide ore pellets of uniform size and excellent strength. Small pieces of ore are rolled into nuclei in a first pellet-rolling circuit in the presence of a binder, the nuclei sized and hardened by sintering or cold-bonding of the binder, the nuclei rolled in additional ore to form product pellets, the pellets sized, the suitable size fraction taken as product, and undersize pellets returned to the rolling operation. P. A. Ilmoni and R. Drugge, assigned to Luossavaara-Kiirunavaara AB Jan 16, 1979. 5 pp. (264-37) Filed- 5-25-77 (800,278) Priority: Sweden, 6-2-76 (76/06,¬241). Same British 1,553,763, dated Oct 10, 1979. US 4,145,210-In the induration of pellets of iron oxide ore or iron works dust or sludge, a charge of dried pellets and 2-20% by weight of coke having a size range of from 5 to 30 mm, a drum index of more than 70, a reactivity index of less than 50, and a tumbler index of more than 50 is charged into a rotary kiln The charge is heated and passed through the rotating kiln to indurate the dried pellets without burning the coke Powder-coated coke is recovered from the kiln for reuse. Ring formation in the kiln is substantially prevented. K. Kato and K Kadota, assigned to Sumitomo Metal Industries, Ltd, and Sumitomo Heavy Industries, Ltd. Mar 20, 1979 10 pp (75-3) Filed- 2-22-77 (770,947) Priority: Japan, 2-24-76 (51/19,754) US 4,145,211-Method of cooling hot metallized iron oxide ore agglomerates from a direct reduction furnace Agglomer¬ates ranging from 3/a in to 41/2 in in cross-section and at a temperature of 1000-2000°F are formed into a moving bed while at rest relative to each other Air at ambient tempera¬ture is passed through the bed at a velocity sufficient to cool the agglomerates rapidly to a temperature no greater than about 500°F without substantial reoxidation of the metal in the agglomerates and by using air as the sole cooling gas. C A Czako, A Berzins, and M J Greaves, assigned to Arthur G McKee & Co Mar. 20, 1979 15 pp. (75-34) Filed: 7-18-77 (816,467)

Jan 1, 1980

(Members are urged to send in for this column any notes of interest concerning themselves or their fellow-members.) The following members have registered recently at the Headquarters of the Institute Seeley W. Mudd, Los Angeles, Cal. Charles Janin, San Francisco, Cal. Edgar Rickard, London, England. Donnel F. Hewett, Washington, D. C. L. Maurice Cockerell, Chihuahua, Mexico.

Jan 4, 1913