By Robert L. Dean, Michael Hoch, Samuel M. Wolosin, Chung K. Hwu

The general shape of the 1450°C isotherm of the Ti-TiO-ZrO2-Zr region was evaluated from the surrounding binary phase diagrams and from thermo-dynamic data on the metal-oxygen binaries. The phase boundaries were accurately determined using X-ray and metallographic techniques. At 1450°C the system shows a large bcc ß field, which extends from the two metal-oxygen binary systems as a Gaussian error function, and is stable up to 30 at. pct 0 when Ti and Zr are present in equal amounts. At higher O Concentrations, the ß field is in equilibrium with t-ZrO . The following four regions, with three solid phases, are present: two a ß t-ZrO,, a TW t-ZrO,, and TiO t-ZrO2 c-ZrO2. On cooling the ß phase transforms into the a phase, going through the w transition phase. The isotherm at 1500°C for the region TiO-TiO,-ZrO, was obtained by using X-ray diffraction. At 1500°C a large c-ZrOz region is present as well as a large two-phase field, Ti0 c-ZrO,. The following regions, with three solid phases in equilibrium, were found These regions are relatively small. The solidus and liquidus relationships were determined by observing samples suspended in a tungsten crucible by means of a fine tungsten wire and heated in vacuum. Eleven univariant points were found. C-ZrO, decomposes through a peritectic reaction into liquid t-ZrO2. The activities of Ti and TiO in the TiO t-ZrOz and in the two a ß t-ZrO regions were measured using the Knudsen effusion method. In the a TiO t-ZrO, region the activities of Ti and Ti are the same, as in the a — Ti TiO binary. In the two a t-ZrO, regions, the Ti activity is high and the Ti0 activity very low, although all phases present contain at least 30 at. pct 0. This indicates a short-range order in the solid phases, Zr atoms being preferentially surrounded by 0. 1 HE system Ti-Zr-0 is of interest because of the wide ranges of solid solubility exhibited by the boundary systems; as titanium and zirconium both belong to the same group of the periodic table, large single-phase regions should occur within the system, with a great variation of properties (as the composition changes within the single-phase region). Furthermore, the possibility of modifying ZrO, to make it a more usable refractory by the addition of other metals makes this system also of interest. Because of the high affinity of titanium and zirconium for oxygen, the oxygen partial pressure is very low at all compositions; thus, there exists a ternary metal-metal-oxygen system in which the oxygen pressure is not an important variable, so long as it is low enough. When a sample is heated in vacuum to a temperature high enough for vaporization to occur, the vapor phase will consist of metal and metal-oxide gas, the oxygen concentration being very low. The phase relationships in the surrounding binary systems have already been reported in the literature; therefore, the study of the ternary diagram

Jan 1, 1962

By Frederick Laist

The ores received at the Washoe Smelter come almost entirely from the mines in Butte and contain the following minerals : Chalcocite, Cu2S; covellite, CuS; chalcopyrite, CuFeS2, (trace); bornite, Cu3FeS3; enargite, Cu3AsS4; malachite, Cu2CO4 + H2O (trace); pyrite, FeS2; sphalerite, ZnS; rhodo-chrosite, MnCO3, (less than 1 per cent.); rhodonite, MnSiO3, (less than I per cent.). The country-rock of Butte is of the granite family and is a quartz-monzonite containing a little less silica than typical granite. It is made up of the following rock-minerals in approximately the proportions indicated: Minerals. Composition. Per Cent. Quartz SiO2 20 Andesine 1/2 NaAlSi3O8; 4 CaAI2Si2O8 42 Orthoclase KA1Si308 23 Hornblende 1/2 Ca(MgFe)3Si4O12; & (MgFe)2(AlFe)4Si2O12 6 Biotite (HK)2(MgFe)2A12Si3O12 9 Titanite CaTiSiO5 0.1 Apatite (CaF)Ca4(PO4)3 0.05 Magnetite (FeO)(Fe2O3 0.15 Pyrite FeS2 0.02 99.32 The main country-rock (quartz-monzonite) is cut by dikes of aplite, a granite having the following composition: Quartz, 30; andesine, 20; orthoclase, 45; ferro-rnagnesian minerals, 3; pyrite, 0.1; total, 98.1 per cent. Closely associated with the copper-deposits are dikes and bodies of " Modoe" porphyry, technically known as quartz-

Jan 1, 1913

By J. E. Neal, C. T. Naber, O&apos

Silicon thin films were deposited by electron beam evaporation in an ultrahigh vacuum onto (0001) and (1102) sapphire substrates. Attempts were made to correlate the structural properties of the deposited silicon films with the following: 1) substrate orientation, 2) substrate surface condition, 3) substrate temperature, and 4) deposition rate. The substrate temperatures were varied between 500° and 1000°C and the deposition rates were varied between approximately 50 and 700A per min. The following sapphire surface treatments were investigated: 1) annealing in the ultrahigh vacuum at 1200° C; 2) heating in a hydrogen atmosphere at about 1350°C; and 3) etching with silicon by evaporating silicon onto sapphire substrates heated to 1200° or 1300°C. Twinned silicon films were occasionally formed at substrate temperatures between the 800° and 1000°C on unprocessed mechanically polished substrates; however, the reproducibility and crystallinity of these films were generally poor. Single-crystal and twinned silicon films were formed at substrate temperatures between 700° and 1000°C on substrates which were silicon-etched at 1300°C prior to deposition. Fiber texture films were formed at substrate temperatures between 500° and 700°C. The (111) lattice plane of the silicon single-crystal films was parallel to the (0001) sapphire plane and the (100) silicon plane was parallel to the (1102) sapphire plane. TECHNIQUES are well-established for growing single-crystal silicon thin films on sapphire by chemical methods.'-* Vacuum epitaxial techniques have a number of advantages over chemical epitaxial techniques in the fabrication of thin film microcircuits.5 One of the most significant is that vacuum techniques are compatible with well-established procedures for forming vacuum-deposited thin-film resistors, capacitors, and interconnections. Salatna, Tucker, and young6 recently reported the formation of relatively poor crystalline-quality silicon films on sapphire by electron beam evaporation in a vacuum of about 7 x 10-7 Torr. The purpose of the investigation described here is to determine the relationships between the structural properties of silicon thin films deposited on sapphire substrates by electron beam evaporation in an ultra-high vacuum and the following: 1) substrate orientation; 2) substrate surface condition; 3) substrate temperature; and 4) deposition rate. The substrate temperatures were varied between 500° and 1000° C and the deposition rates were varied between approximately 50 and 700A per min. Two orientations of sapphire were used: (0001) and (1102). The thick-nesses of the films were between 8000 and 16,000A. The morphology and crystallinity of the deposited films and substrate surfaces were investigated by optical microscopy, electron microscopy, and electron diffraction. APPARATUS AND PROCEDURE A cross section of the ultrahigh-vacuum thin-film evaporator is shown in Fig. 1. The bell jar is stainless steel and copper gaskets are utilized at all seals. High vacuum is attained by a 6001iter per sec ion pump and a titanium sublimation pump. Sorption pumps are used to rough the system to a pressure of about 10 µ prior to starting the ion pump. Vacuums in the 10- 10 Torr range were attained after baking the system at about 250°C for 8 hr. Vacuums in the 10-8 to 10-9 Torr range were maintained during silicon evaporation. The silicon charges, which were cut from p-type single-crystal boules which had resistivities between 2000 and 4500 ohm-cm, were placed in the water-cooled copper crucible of a 180 deg bent-beam 5-kw electron beam evaporator. During evaporation, a molten zone was formed in the top center of the silicon charge, and the portion of the silicon charge in contact with the water-cooled crucible remained solid. The substrate heater, which has been described

Jan 1, 1969

By Frank C. Appleyard

Gypsum, the dihydrate form of calcium sulfate, has a history of usefulness to man dating back several thousand years, and a worldwide industry has been built on the mining and processing of this versatile industrial mineral. However, anhydrite, the other principal calcium sulfate mineral has very limited use, so much so that separate statistics for it are not always kept, but are usually included with those for gypsum. Although often found in close association, the two minerals have important chemical differences in that anhydrite is the anhydrous form of calcium sulfate (CaSO,) whereas gypsum is the dihydrate (CAS0;2H20). These two molecules of combined water result in significant differences in hardness, density, and solubility of the two minerals. However, of most importance is the difference in thermal properties wherein gypsum, upon the application of a modest amount of heat, can be converted to the hemihydrate of calcium sulfate (CaS0;Vi H,O) or plaster of paris, an intermediate product upon which is based over 90% of the value of all calcium sulfate end products. Anhydrite, on the other hand, is inert at these temperatures and its uses have been limited to only those few cases where calcium sulfate in the anhydrous form may have an advantage. The earliest known use of gypsum plaster dates back some 5000 years to the time of the Pharaohs of Egypt who had discovered that gypsum rock, when exposed to fire, broke down into a powder which when mixed with water would form a putty that could be "plastered" on a rough mud brick or stone wall to make a smooth finish. It was used down through the centuries in a limited way for ornamental purposes, but did not achieve wide acceptance because of its quick (25 to 30 min) setting or hardening time which made it difficult to use. The first real understanding of gypsum chemistry was developed in France about 1755, and the gradual growth of its present utilization dates from that time. In the United States, the first utilization of gypsum was to grind it to a fine material for use as a soil conditioner at about the time of the Revolutionary War, and the term "land plaster" for ground gypsum has remained in use. Another cementituous material-lime or calcium oxide-had become the usual plastering material, but by about 1870 a method for retarding the set of gypsum plaster was discovered and it has today almost completely replaced lime as a plastering material. In recent years, gypsum products sold in the United States have reached a total valuation of approximately $500 million per year as illustrated in [Table 1].

Jan 1, 1975

By E. M. Wise

THE properties required of gold alloys for jewelry are not well standardized, due in part to problems peculiar to certain branches of the jewelry industry, in part to the individual preference of the fabricator and to his willingness to cope with certain difficulties in manufacture, which arise with the use of certain alloys. GENERAL REQUIREMENTS In general, the properties desired may be classed as follows: 1. Color should conform to the dictates of good taste and smart style. 2. Corrosion resistance and tarnish resistance should be good. This is to a considerable extent determined by the carat. Resistance to such corrosive agents as mercuric chloride as well as certain depilatories is unreasonable to expect and difficult to meet. 3. Strength and hardness must be adequate to maintain the delicate contours of finely modeled jewelry. 4. Wear resistance must be great enough to resist abnormal wear, such as is encountered by a wedding ring in a lifetime of wear. 5. Ductility must be sufficient to permit the fabrication of drawn shells, tubes and difficult shapes. Material having a yield point of not less than 60,000 lb. per sq. in., an ultimate strength of 100,000 lb. per sq. in., and an elongation of 40 per cent. is desirable. 6. Melting point should be between 800° and 1200° C.

Jan 1, 1928

By Horace Pops

Martensitic transformation has been studied during cooling and heating in ß-phase Cu-Zn alloys to which small additions have been made of Ni, Ag, Au, Cd, Ga, In, Si, Ge, Sn, and Sb. The start and finish of the martensitic reaction and the variation of transformation temperature with third-element content were determined by electrical-resistivity measurements from alloys which had either constant zinc contents or constant values of electron concentration. All of the third elements, except nickel, lowered the transformation temperature if the results were plotted along the lines of constant zinc contents in each ternary system. A significant difference in the rate of lowering of the transformation temperature per atomic percent of the third element was observed for elements which had the same nominal valence. No systematic variation of transformation temperature with the valence of the third element was observed. It is suggested that the observed increase in transformation temperature for nickel-bearing alloys is due to the transfer of electrons from the conduction band of the alloy to virtual bound states. However, electron concentration is not the most important factor controlling the instability of the 0 phase. The transformation temperatures of the ternary alloys can be predicted from the following approxilnate expression: Ms (°K) = +3280 - 80 Zn + 8 Ni - 30 Ag - 12 Au - 140 Cd -90 Ga- 145 In - 80 Ge -175 Sn - 120 Si - 150 Sb MOST binary ß -phase alloys based upon the noble metals copper, silver, and gold are unstable at low temperatures and transform spontaneously by a martensitic reaction. This transformation has been studied recently in the ordered bcc ß'-phase Cu-Zn binary al1oys1,2 where the transformation temperature is below the room temperature and decreases with an increase in zinc content. It has been reported that the transformation temperatures can be raised above room temperature by small additions of a third element such as silicon3,5 or gallium,4,5 but no quantitative study has been made. The transformation temperature of different binary alloys can be altered by third-element additions. For example, it was shown that nickel and copper may have a large effect on the Ms temperature of CU-Al6 and Au-cd7 alloys. The present investigation was made to determine systematically the influence of various third elements on the martensite-transformation temperature of Cu-Zn ß-phase alloys. Since these alloys have an electronic origin,' alloy compositions were chosen so that the transformation temperatures could be determined at constant zinc contents or at constant values of electron concentration. I) EXPERIMENTAL PROCEDURE Ten ternary alloy systems were obtained by adding nickel, the noble metals silver and gold, and some B-subgroup elements to a Cu-Zn matrix. These are arranged according to their rows and columns in the Period Table as follows: Each ternary alloy was prepared by melting and casting weighed quantities of high-purity metals (99.99+ pct) in sealed quartz tubes under a partial pressure of helium to make a 4-g ingot. The molten alloys were shaken vigorously and then quenched in water. Since the weight loss was negligible, the compositions of the ingots after casting and annealing were assumed to be the same as the nominal compositions. The ingots were homogenized after casting in helium-filled Vycor tubes for 24 hr at temperatures between 750" and 810 C and quenched into brine. Metallographic examination revealed that all alloys were homogeneous, poly crystalline ß-phase alloys, and that the grain size was in the range 1 to 5 mm. Electrical-resistivity measurements were made to determine transformation temperatures of the ternary alloys during continuous cooling or heating. Transformation temperatures of the ternary alloys can be determined by electrical-resistivity measurements since the resistance of the martensitic phase is much higher than that of the 0' phase. The technique has been described previously in connection with a study of Au-Zn alloys.9 The reproducibility of transformation temperature was approximately ±6°C. II)RESULTS A hysteresis was always observed in electrical-resistivity curves and was usually less than about 12°C.

Jan 1, 1967

By A. L. Holley

THE members of the society are doubtless aware that the production of American Bessemer steel works is constantly increasing ; that the same converters and machinery are doing more work every year. This enlarged output is due to various causes, chiefly the following: 1st. Better organization-better knowledge on the part of both managers and men, of the plant and the process ; of the way to economize the more exhausting labor, and of the arrangement of the details of labor and operations so that they shall not conflict; also, more pluck-a greater willingness to take risks, or, more properly, such an intimate knowledge of the nature and capacities of the refractory tory linings in various stages of disrepair, and the probable be- . havior of the fluid metal at various stages of its treatment, that the precise nature of the risk may be better known, so that the works may be crowded to their full capacity. In the early practice, after getting four or five consecutive heats in a day, the men preferred to "let well enough alone," and to devote the remaining time to preparation for another turn. Now, thirty, and sometimes forty heats are regularly made during the twenty-four hours, day after day, without the frequent occurrence and without the fear of breakdowns or "messes," as the spilling of steel charges was graphically named in Sheffield. 2d. Although no new refractory materials have been developed, improved means of preparing such as we have, and of imbedding

Jan 1, 1874

By R. C. Himes, K. Zanio, J. B. Wagner, J. W. Moody, J. F. Miller, W. Johnson

The recent research with which this paper deals has been concerned with the preparation of pure PbTe crystals suitable for control of radiative processes and othe.v electronic applications. The research has been directed toward the developrnent of methods for the preparation of puve, homogeneous, loul-ca,wier-density PbTe crystals suitable for use in the fabrication of optically pumped and electrically pumped diode lasers. Steps in the preparation of the crystals include 1) purification of the starting materials, 2) synthesis and purification of the PbTe, 3) growoth of PbTe crystals, and 4) adjustt~zertt of composition of the crystals This Paper describes the general preparation procedure employed and discusses some investigntiotzs of purification processes. THE as-received lead and tellurium are nominally 99.999 to 99.9999 pct pure. Assays furnished by the suppliers, obtained by emission spectrographic analysis, show only the presence of about 2 ppm Mg in the tellurium. Such analyses are not very informative, however, since they give no information on the concentrations of normally gaseous impurity elements such as oxygen. Both the lead and the tellurium in the as-received state usually contain appreciable concentrations of oxygen—primarily in the form of oxides on the surfaces of the material. To reduce the oxygen content, the lead is held in the molten state in hydrogen at -700°C for several hours. For this treatment, the lead is contained in a graphite boat which is rf-heated, and the hydrogen is passed through a liquid-nitrogen trap prior to use. Tellurium is subjected to multiple distillation in hydrogen to remove oxygen and other foreign impurities. If, in conducting the distillation, approximately the last 10 pct of the charge at each "stage" is left as the discard cut, purification of the tellurium proceeds as indicated in Fig. 1.l Tellurium used in this work has been distilled two or three times to reduce carrier concentration to about 10" per cu cm. The PbTe is prepared from the purified elements by reacting them in the molten state in sealed, evacuated, or hydrogen-filled silica ampoules. The charge is usually held above the melting point of PbTe (923°C) at 1000 C for 24 hr to ensure that it has been homogenized. Two methods have been employed for the growth of the required single crystals of PbTe: growth from the melt, which will be discussed first, and growth from the vapor phase. Large single crystals of p-type PbTe can be grown readily from the melt by the Bridgman method. For this method of crystal growth, the PbTe is synthesized in situ from proper proportions of the purified elements. Growth (dropping) rates in the range 1.3 to 6.5 mm per hr are employed. Material near the maximum melting composition (about 50.012 at. pct Te) is utilized to avoid composition change on freezing, and thus to obtain crystals of nearly uniform composition. Crystals prepared by use of procedures described up to this point were sufficiently pure and perfect that they could be used for the preparation of laser crystals in studies at Lincoln Laboratory.2-5 ADJUSTMENT OF COMPOSITION Good n-type crystals of PbTe cannot readily be grown from the melt. Further, growth from the melt of crystals of any compositions (n or p type) other than those near the maximum melting composition is difficult because of the large composition changes that must occur on freezing.'" However, melt-grown crystals can rapidly be brought to other desired compositions by isothermal equilibration through the vapor phase with a two-phase Pb-Te stock material, essentially as described by Brebrick and Allgaier.1 The work to be discussed has been concerned with the preparation of n-type crystals; thus, the two-phase stock which was employed contained excess lead, and all ensuing discussion is of the preparation and properties of n-type crystals. The equilibration was designed to the shift composition to the lead-rich limit of stability at the selected temperature. Initial treatment of the crystals at high temperature was employed to minimize the total time required for the equilibration. Final adjustments of the composition and state of the crystals were made by use of low-temperature heat treatment at temperatures in the range 200" to

Jan 1, 1968

By N. K. Chen, R. Maddin

Single crystals of molybdenum were extended at temperatures from 1300° to 2500°C. It was found that with increasing temperatures, the yield becomes more pronounced and the number of slip bands for equal amounts of elongation decreases. Slip at high temperatures fragments the structure. OTHER than the investigations on sodium and potassium by Andrade and Tsien,&apos; the researches of Steijn and Brick&apos; on a iron single crystals at low temperatures are about the only studies of the influence of temperature on glide of body-centered cubic single crystals. The effect of test temperature on glide has been rather widely investigated with hexagonal crystals" and less widely with face-centered cubic crystals. ~~ a result of these studies it can be said that, in general, the onset of plastic flow as measured by the initial rate of strain hardening becomes more abrupt with increasing temperature, and the value of the yield decreases with increasing temperature. Strain hardening, however, is markedly affected by changes in temperature except at very low and very high temperatures where the strain hardening rate becames constant. In the present investigation it is shown that temperature affects the glide of molybdenum single crystals in much the same manner as crystals of other classes, it., for comparable strains the number of slip bands decreases with increasing temperature; shear along the slip bands increases with increasing temperature; the yield becomes more pronounced with increasing temperature of test; and the strain hardening approaches a constant at very high temperatures. In addition, it is shown that, in agreement with the work of Tsien and Chow, Qlip occurs on (110) planes in <Ill> directions. It is further shown that slip at high temperatures fragments the structure into either irregular sized cells or bent atomic planes which are roughly aligned in crystallographic directions. Experimental Procedure Single crystals 3 mm in diameter by about 25 mm long were prepared using the technique previously described.&apos; The furnace in which the crystals were grown served as the extension apparatus for the tension tests. It consisted of a 4 in. water-cooled brass tube 20 in. long which was continuously evacuated at the bottom. Two water-cooled copper electrodes held the specimen by means of spherical collets secured in place in the electrodes by set screws. These electrodes served also to transmit power and stress to the specimen. The lower electrode was clamped to a stand, while the upper electrode was fastened to one side of a lever arm flexibly supported at the top through a slightly offset pinion. A metal bellows operating elastically was attached to the upper electrode to affect a vacuum seal and allow freedom of motion. The level of the arm was adjusted by rotating a graduated nut. Rotation of the electrode was prevented by a key fitted into a groove. After the specimen was mounted and the vacuum secured, the lever arm was adjusted so that the bellows was at its relaxed position. This insured that the total weight of the specimen, the upper electrode, and the downpull of the vacuum were balanced by the horizontal beam. Since the specimen was heated by its own resistance, expansion of the specimen proceeded freely by this arrangement. During the time of heating the specimen, the beam was maintained in a horizontal position by turning the nut at the top. By graduating the lever arm and using a known dead weight on the lever arm to supply a tensile stress, the graduated nut could be read to 0.0001 in. extension. Since

Jan 1, 1955

By G. E. Klinzing, S. H. Chiang, R. M. Kakwani

Filtration and dewatering results of -500 µm (-32 mesh) Pittsburgh seam coal are discussed with reference to the microscopic structure parameters, i.e., particle segregation in the cake and particle and pore size distributions at different layers. At low solid concentration of 0.33 kg coal/kg water, a non-uniform cake structure is observed where particle and pore sizes increase from the top to bottom layers in the filter cake. An increase in the solid concentration in slurry produces more uniform cake structure and higher filtration and dewatering rates. Air bubble entrapment in the coal filter cakes is also discussed.

Jan 1, 1985

By Herbert Hoover

DURING the year, the&apos; Institute has made the most remarkable growth in its history. Our actual increase in membership was 1816 and therefore was 80 per cent. larger than any previous year. Even without expectation of any abnormal growth, we should pass in the year 1921 the 10;000 mark. The causes of this increased growth are not far to seek.. They lie in the widening vision of the Institute&apos;s work, not only in its relation to&apos; the profession but as an avenue of service to the nation as a whole. The Institute is today in the first rank of influence among public institutions in the country. During this year we have, for the first time in many years, had a ?deficit of some $3000 in our finances. The sum is not important, but it- does indicate the tendency of the times, and that is the high cost of living:&apos; The increase in our expenses lay, to the largest degree, on the publishing side of the Institute&apos;s work. If we compare the year 1918, as a fairly repre¬sentative year, with that of 1920, we find that the costs of issuing the&apos; Institute&apos;s publications, after deducting the income received from these publications, shows a .net increase of about $33,000. for the year. This has been to some degree due to the enlarged membership but to a large degree due to the cost of the paper and printing.

Jan 1, 1921

By H. F. Bishop, F. A. Brandt, W. S. Pellini

M. S. Fisher and D. R. F. West (Imperial College of Science and Technology, London, England)—It may be of value to compare certain features of the results recorded in this very interesting paper with those of an investigation11 involving determinations of temperature gradients and rates of solidification of steel blocks of 3 in. sq section, cast horizontally in sand molds, some of which contained chills. Castings in plain carbon steels containing up to 0.8 pct C were made and, throughout this range of compositions, both inverse-rate and direct cooling curves, obtained from thermocouples placed within the mold cavity, showed a major arrest, the temperature of which was taken as the "effective liquidus" for the particular steel in question, solidifying under the conditions of the investigation. At the completion of the arrest, the curves showed a comparatively rapid de- crease in temperature. Some of the steels investigated lay within the peritectic region, and a second arrest at 1485°C was detected. In Fig. 15, which shows the effective liquidus temperatures, the limit of the 8 + liquid field has been placed at approximately 0.5 pct C. In inverse-rate curves corresponding to the thermal center of each casting, there was always a discontinuity, viz: an abrupt change of slope, at a temperature about 10 to 20°C below the "liquidus arrest," after which there seemed to be no significant irregularity in the rate of cooling. Curves corresponding to other positions in the casting generally showed some irregularities below the main arrest, probably as a result of heat flow from the solidifying interior. Even the reproducible discontinuity in the curves for the central positions appeared to have no theoretical or practical significance, though it probably corresponded to a stage in the solidification process at which only a relatively small amount of interdendritic liquid remained. Its temperature, rela-

Jan 1, 1953

By D. Weinstein

Yieldilzg in annealed arc-cast molybdenunz in torsion was studied as a function of strain rate and tem-perature. The temperature dependence of the yield point for different strain rates was used to calculate a heat of activation for the yield point. The heat of activation was not a constant but was approximately a linear function of the stress at yield. It is proposed that the rate effect in yielding is determined in part by a site place-change of C (or other interstitial atom) in the metal. THE low-temperature embrittlement phenomenon in metals and alloys has been known to exist for a long time. Although a transition from ductile to brit-tle behavior has been observed in some close-packed hexagonal metals1 and a face-centered cubic alloy, the most common class of metals exhibiting this be-havior has a body-centered cubic lattice structure. For example, a ductile to brittle transition has been observed in iron,3 molybdenum,4 chromium,5 colum-bium,6 and tungsten.7 In the present investigation, molybdenum specimens were tested in torsion over a wide range of temperatures at three widely separated strain rates, and the temperature for onset of embrittlement was determined. Characteristic of body-centered cubic metals and closely associated with plastic deformation is the appearance of a sharp upper and lower yield point. Theoretical explanation of the yield point in iron and low-carbon steel is due to Cottrell,8 who attributes the phenomenon to the pinning of dislocations by the formation of impurity atmospheres around the dislocations. These atmospheres tend to lock the dislocations and make them more difficult to move. The stress required to move a dislocation and thereby cause plastic deformation is greatly increased, and thus an upper yield point is observed. In addition, theoretical analysis,9 as well as experimental observations, show that the upper yield point is strongly a function of temperature. The upper yield point is observed to decrease with an increase in testing temperature, and above a certain temperature (-700° K in iron) it no longer appears. This is consistent with the concept that thermal vibrations will help free a dislocation from its atmosphere, so that the external stress required to free a dislocation from its pinning atmosphere decreases with increasing temperature. Furthermore, with increasing temperature the equilibrium concentration of impurity atoms around a dislocation decreases exponentially with the result that the dislocation is less firmly pinned. In Cottrell&apos;s theory of yield point a static model is visualized in which the pinning atmospheres, particularly interstitial atoms, are immobile, and the dislocations are anchored to stationary positions in the lattice. However, experiments1,7 show the upper yield point to be time-dependent or a function of the rate of straining, a high strain rate causing a high upper yield point. Present theory does not adequately account for the rate dependence of the yield point, and the exact function of the interstitial atom is not under stood. Nevertheless, observation of the temperature dependence and rate dependence strongly suggests that the upper yield point phenomenon is due to the interaction between dislocations and pinning atoms, and that a diffusion mechanism is important in determining the yield point.

Jan 1, 1962

By George R. Cowan

A number of studies hare been reported of the effects produced in metals subjected to deformation by shock waves with maximum pressures ranging from tens to hundreds of kilobars. On the basis of the equations for the flow of mass, momentum, and energy through a stationary shock front, the macroscopic stress-strain curve for the resulting shock deformation can be calculated within narrow limits from the experimentally determined Hugoniol curve. In relatively weak shocks which are preceded by an elastic wave, the stress rises above the clastic limit only as plastic deformation proceeds cold thus the shock has a long toe. In strong shocks that override the elastic wave a high stress is applied without prior plastic deformation. A more important effect of increasing the shock pressure is the generation of shear stresses, called supercrilical shear stresses, that exceed the strength of the perfect lattice. A change in the mechanism of deformation is expected to result from the onset of supercritical shear. The shock disordering of ordered Cu3Au in strong shocks appears to be an example of such a change. It is suggested that the formation of fine twins in copper and nickel and the formation of structures which enable visible twins to be formed in the rarefaction ware, observed in copper and presumably in disordered Cu3 Au, are related to the occurrence of supercritical shear in shock dcformation. In recent years several studies1,2 have been made of the changes in structural and mechanical properties of metals produced by the passage through the metals of strong shock-compression waves ranging from about 50 to 800 kbar pressure. Recent work involving dynamic measurements of the shock compression "Hugoniot" curves 3-8 of many metals has developed techniques and provided data required to obtain the shock pressure and the (transient! plastic deformation produced in the shock-conlpression experirnents.9 Shock deformation has been found to be much more effective than slow deformation in changing the mechanical properties of metals, when the two are compared on the basis of equal plasti strain, Holtzman and Cowan9 made quantitative estimates of the shearing stress occurring in a shock front in a metal by assuming that the shearing stress is similar to that occurring in a shock front in a viscous, heat-conducting fluid, with the addition of a yield stress. Taylor&apos;s solution9 for a weak shock was used to estimate pairs of values of shearing stress and thickness of the shock front obtained by assumed choices of the ratio of effective kinetic viscosity to thermal diffusivity. It was noted from these values that. unless the shock front is extremely thin. heat conduction has slight effect, and the shearing stress is nearly independent of the mechanism of deformation. This mechanism does, however, determine the thickness of the shock front and the rate of strain. Furthermore, since the maximum possible shearing stress occurring in shocks of moderate strength does not greatly exceed the shear stress occurring in conventional slow deformation, the mechanism of deformation is not expected to be qualitatively different. The greater effectiveness of shock deformation in changing the mechanical properties of metals can be attributed partly to the fact that dislocations, when driven by near-conventional stresses, cannot keep up with the shock front, thus necessitating a higher dislocation density than required for an equivalent slow strain. The fast uni-axial strain occurring in the thin shock front would also be expected to cause a larger number of dislocation intersections to occur. In the upper range of shock pressures that have been studied the estimated values of the shearing stress exceeded the estimated shear strength of a perfect crystal. Under these circumstances it is reasonable to expect that the mechanism of deformation might be considerably different from that involved in slow deformation. Except for the observation by smith1 of twins in shocked copper, the effects of shock waves on metals did not show any obvious or large changes in properties that would indicate the onset of a change in the mechanism of deformation. The recent investigation of the effect of shock waves on ordered and disordered specimens of Cu3Au by Beardmore, Holtzman, and ever" showed a spectacular decrease in the amount of long-range order retained by initially ordered Cu3Au when the shock pressure was raised from 290 to 370 kbar. Since Dr. Holtzman and I suspected that this behavior probably was due to the onset of a shearing stress in the shock front in Cu3Au which exceeded the limiting shear strength of the perfect crystal. it was considered appropriate to examine directly the shock-front equations for a solid. and to obtain a sound estimate of the shearing stress occurring in the front using equation of state data obtained from shock studies. In this paper an estimate is made of the

Jan 1, 1965

By Ben-Zion Weiss, Melvin R. Meyerson

Chromium diffusion coatings on commercial Armco iron lead to carbide precipitation at the grain boundaries in and below the coatings. High compressive stresses are introduced into the coating and, as a result, tensile stresses are introduced into the base material below the coating. In coated samples, fatigue cracks form at the grain boundaries below the coating after only a limited portion of the total lifetime (5 to 10 pct). Residual tensile stresses and a stress concentration caused by precipitated carbides seems to be responsible for early crack nucleation. Stage I of Propagation may be divided into two substages: I-a in which the crack Propagates along grain boundaries, and I-b in which the crack propagates along slip boundaries according to a shear mode. In uncoated samples, the cracks form at slip bands after 40 to 50 pct of the total lifetime. In coated samples the Propagation process takes longer than in uncoated samples because of the moderate rate of crack extension until the crack breaks through the coating. The chromium-diffusion coating causes little if any increase in fatigue life. CHROMIUM diffusion is one of the most popular processes used to apply coatings to iron alloys. This popularity stems from the fact that the diffusion treatment is comparatively easy to carry out, and it improves certain surface properties such as corrosion and wear resistance as well as some other properties. Very little effort has been devoted to the investigation of the effect of chromium-diffusion coatings on mechanical properties and particularly on fatigue properties. Since the chromium coating usually represents a small fraction of the total volume of the base material it is generally assumed that the macro properties are dependent principally on the base material rather than the coating. Insofar as fatigue is concerned, there are indications that the fatigue life of the chromium coating is not less than that of the basic material and the fatigue properties are generally not reduced by it.&apos; But chromium diffusion causes drastic structural and chemical changes in the region of the material surface2-4 which introduce additional residual stresses. Such changes must affect fatigue crack nucleation and may sometimes affect the initial stages of propagation. Furthermore, it is conceivable that the secondary stages of the crack propagation could be influenced by some irreversible structural changes in the core of the material, which stem from the long-time heat treatment at high temperatures required to apply the coating. This paper analyses the structural and compositional changes produced in commercial Armco iron by a chromium-diffusion coating and the effect of the coating on fatigue crack initiation and propagation. EXPERIMENTAL PROCEDURES The investigations were carried out with commercial Armco iron. The chemical composition of the iron, the number of specimens tested, the grain size produced during chromizing and heat treating, and the thickness and microhardness of the chromized layers are shown in Table I. Samples were chromized by a gas diffusion process. The temperature and time of the diffusion coating process were chosen according to a previous grain growth study. It had been found that at a temperature of 970°C and a holding time of between 3 and 9 hr there are practically no changes in grain size. To describe the grain size more accurately the ASTM method5 was supplemented by a statistical analysis of the mean volume diameter as outlined by Fullman6 and The The mean volume diameter was deter- mined from D = p/2m where D is the mean volume diameter, and m is the mean reciprocal value of grain diameters as seen on the micrograph. The shape and the size of the asymmetrical sample, see Fig. 1, were chosen so as to facilitate the study of fatigue crack initiation. Before coating, the samples were machined and the surface of the groove was polished. After chromizing, the two side surfaces were machined and polished so as to retain the coating only on the top surface of the groove. Residual stress in the chromized layer was measured on the top of the grooved section of the specimen after the diffusion process. The inclined incident X-ray beam procedure was used.9&apos;10 The computations were performed with the initial assumption of a zero surface normal stress component. An electron microprobe analyzer was used to obtain the relative amounts of chromium and iron con-

Jan 1, 1970

By A. L. Holley

The members of the society are doubtless aware that the production of American Bessemer steel works is constantly increasing; that the same converters and machinery are doing more work every year. This enlarged output is due to various causes, chiefly the following: 1st. Better organization—better knowledge on the part of both managers and men, of the plant and the process; of the way to economize the more exhausting labor, and of the arrangement of the details of labor and operations so that they shall not conflict; also, more pluck—a greater willingness to take risks, or, more properly, such an intimate knowledge of the nature and capacities of the refractory linings in various stages of disrepair, and the probable be- . havior of the fluid metal at various stages of its treatment, that the precise nature of the risk may be better known, so that the works may be crowded to their full capacity. In the early practice, after getting four or five consecutive heats in a day, the men preferred to " let well enough alone," and to devote the remaining time to preparation for another turn. Now, thirty, and sometimes forty heats are regularly made during the twenty-four hours, day after day, without the frequent occurrence and without the fear of breakdowns or " messes," as the spilling of steel charges was graphically named in Sheffield. 2d. Although no new refractory materials have been developed, improved means of preparing such as we have, and of imbedding

By Frederic L. Kadey

Perlite, as a volcanic glass, has been recognized since the Third Century, B.C. (Langford, 1978). The precise details of discovery often become lost in antiquity, and the variations among the stories pertaining to the more recent discovery of perlite as a material of commerce are no exception. Credit in the United States is given to a dentist who, while experimenting with tooth enamels about 1941, discovered that perlite-the rock-intumesced when subjected to heat. At about the same time it is reported that the chief geologist of Silver and Barytes Ores Mining Co. attempted to put out a picnic bonfire on the shores of Milos Island, Greece by throwing beach sand on it. The ensuing pyrotechnic display immediately conjured up in that man&apos;s mind the possibility of a new use for the volcanic rock that constituted most of the island. Very little was done with this discovery either here or abroad until after World War II. Today the name perlite is applied to both the hydrated volcanic glass, generally of rhyolitic composition, and to the lightweight aggregate that is produced from the expansion of the glass after it has been crushed and sized. Petrologically, it is defined as a glassy rhyolite that has a pearly luster and concentric, onionskin parting. Occurrences of perlite are restricted to several Tertiary to Quaternary age rhyolitic belts that trend in a generally north-south direction around the world. Commercially suitable deposits generally occur as domes of several hundred feet in height, although glassy zones in welded ash-flow tuffs and others associated with dikes and sills also have been reported. Mining is by ripping and blasting from open pits. Because of weight considerations, perlite usually is shipped to the local market area for subsequent expanding. In the United States, New Mexico leads in production with Arizona, California, Nevada, Idaho, and Colorado following in approximately that order. The principal use for expanded perlite is as a lightweight insulating aggregate in cryogenics, in plaster, concrete, and in loose fill insulation. Expanded perlite is also used in horticultural applications, and after subsequent milling and classification, as a filter aid. The United States is the world&apos;s largest producer and consumer of perlite. Table 1 shows the world production of perlite and Table 2 shows the perlite mined, processed, expanded, and sold or used by producers in the United States. Geology Composition and Morphology Any discussion of perlite must take into consideration its dual nomenclature, for it is known by the same name as both the naturally occurring rock and, after processing and expansion, as the lightweight aggregate of commercial significance. In its naturally occurring form, perlite is a rhyolitic glass that contains from 2 to 5% combined water. While perlite also can occur as andesitic or dacitic glass, these latter types are of negligible commercial significance. Table 3 lists the chemical composition of a few typical perlites (Anderson, et al., 1956; Langford, 1979). What sets perlite of commercial significance apart from other volcanic glasses is the fact that under the proper conditions of preparation-crushing and sizing-it will, when rapidly introduced into a flame of sufficient temperature, expand or "pop." All of the elements of composition contribute to the expansibility of the rock. The role of the combined water, however, is the most significant because it is believed not only to produce a fluxing effect in the softening of the highly siliceous glass prior to expansion, but it is also responsible for the explosive force of expansion through volatilization during heating. The current theory of the origin of the water in perlite is now less con-

Jan 1, 1983

By T. J. Koppenaal, M. E. Fine

A yield point effect attributed to short-range ordevi?g (SRO) occurs in Cu base Al. At at 296°K varies with heat treatment, decreasing as the annealing ternperature is raised .from 433Oto 598°K. Davies aid Cahn&apos; observed a corresponding decrease in SRO. (523 °K anneal, measured at 77°K) is approximateZy proportional to the variations of A7 with strain rate and testing temperature are also Consistent with the idea that is associated with SRO. A preliminary investigation of the tensile properties of a Cu-Al single crystals showed the presence of a rather strong yield-point effect (drop in flow stress after initial yielding). The object of this research was to investigate its origin and behavior. a Cu-Al alloys are particularly interesting because diffuse X-ray scattering measurements by Davies and Cahn,&apos; Houska and Averbach,&apos; and Borie established the presence of short-range order. The degree of local order may be changed with heat treatment.&apos; cottrel14 suggested that the presence of local order might result in a yield-point effect, and thus the possibility exists here for experimentally ascertaining the importance of short-range order with respect to yield points in these alloys. Since a 12 pct difference exists between the atomic sizes, elastic or Cottrell locking5 must also be considered. Further, Howie and swanne have shown that the stacking fault energy of copper is reduced by aluminum additions. The width of extended dislocations should thereby increase. hus the conditions appear attractive for Suzuki locking.&apos; Finally, the possibility of stress-induced order at dislocations, schoeck locking,&apos; must also be examined, EXPERIMENTAL PROCEDURE Alloys up to 14 at. pct Al were prepared by induction melting high-purity (99.999 pct) Cu and (99.996 pct) Al in a graphite boat under a dynamic vacuum of 5 X 10o mm of Hg. After homogenizing the ingots at 900°C for at least 24 hr under vacuum, they were rolled with intermediate anneals to strips 1.55 mm thick. Single crystals 10 in. long were grown by lowering strips, contained in a split graphite mold sealed in fused quartz at 5 X lo-&apos; mm of Hg, through a single coil induction heater at a constant rate of 1/2 in. per hr. Tensile specimens 1.25 in. long were cut from the single crystal strips and reduced cross sections about 0.7 in. long and 3.0 to 3.5 mm2 in area were introduced by filing and abrading.8 To remove the worked portion about 10 pct of the cross-sectional area was removed by etching. Back-reflection Laue photographs of a filed and etched specimen were taken before and after annealing at 900°c for 24 hr. Small, well defined Laue spots were obtained with no visual difference in the two photographs. Further, specimens with and without the reduced sections began yielding at about the same stress. Hence, for our purposes, filing and abrading did not affect the structure of the specimens. Each single crystal specimen was annealed at 900° c in vacuum for at least 24 hr and furnace cooled; while cooling through the range of 250o to 200°c, the rate was about 55°C per hr. Orientations were determined by the usual back-reflection Laue

Jan 1, 1962

By F. C. Bond

Since the Third Theory of Comminution was presented eight years ago (I) it has found increasing use in crushing and grinding problems. The practical utility of its wok index equation is quite generally acknowledged (2). However, its theoretical basis has been questioned in at least three technical articles (3) (4) (&apos;). The purpose of this paper is to present experimental proof that it is scientifically correct. Particles under compressive stress are strained and deformed. They absorb strain energy, and when this locally exceeds the breaking strength, a crack tip forms. The surrounding strain energy flows to the crack tip, which rapidly extends and splits the rock, releasing the strain energy as heat. The initial energy flow causes additional crack tips in highly strained areas. If the compression is rapidly applied by impact, crack tips may form before the strain energy has reached equilibrium in the particle, thus decreasing the total work input required for breakage. The energy necessary to break is essentially the energy necessary to produce crack tips, since the energy necessary to extend the cracks to breakage is already present as strain energy in the deformed particles. After breakage nearly all of this energy appears as heat. The crack length cannot be measured directly. However, in particles of regular and similar shape the crack tip length is considered as equal to the crack depth, or crack extension necessary to break, so that the crack length equals the square root of one-half of the surface area. The Third Theory states that the useful work done in crushing and grinding is directly proportional to the total length of the new cracks formed. It can be confirmed by showing that a constant work input produces a constant length of new cracks when reducing the same material to different product sizes. This is done in the present paper on a wide variety of material. The constant work input was supplied by one revolution of the 12" x 12" laboratory ball mill used in making grindability tests by the Allis-Chalmers method (12) (13) The new crack lengths produced per mill revolution were measured from all available grindability test results at 28, 35, 48, 65, and 100 mesh on fifteen different ores, and were found to remain substantially constant for each ore at all mesh sizes. A new technique is used for the measurement of crack lengths. Size distribution plots of the mill feed and product are made by the Third Theory method (9) and the crack lengths are obtained from these plots by the procedure described in the present paper. The energy input required to produce a unit length is of fundamental importance in the size reduction of brittle solids. The crack length Cr is expressed in centimeters per cubic centimeter of solid material. It bears a definite relationship to the external surface area of the crushed or ground solid. A uniform particle shape must be assumed before the surface area and crack length can be evaluated. In this paper it is assumed that the relationship between the surface area and the particle volume of a particle d microns in diameter is the same as that of cube d microns on a side. The external surface areas of particles with a cubical breakage probably agree approximately with this rule, and correction factors can be applied when physical measurements of the surface areas are available for comparison. However, the assumption of equivalent cubes has been found satisfactory for most calculation purposes. Assuming equivalent cubes, one cubic centimeter of particles d microns in diameter will have a crack length Cr of v30.000/d centimeters, and a surface area of 60,000/d square centimeters. The specific crack length is thus equal to the square root of one-half the specific surface area. Where Sa is the surface area in square centimeters per gram and Sg is the specific gravity of the ground solid, then Cr = vSg . Sa/2 = 173.2/ vd (1)

Jan 1, 1961

By Pedro G. Salom

I HAVE had an opportonity, within the last few months, of making a large number of physical and chemical tests of steel for boiler and ship-plate, which has been, and is now being, used principally for the United States Government cruisers, now building in Mr. John Roach&apos;s yard, at Chester, Pa. Through the courtesy of the Messrs. Houston, of the Chester Rolling Mills, I have the honor to lay before the members of the Institate the results of these tests. These results have developed some points in regard to the nature of steel, which are more or less new, and which, I hope, will prove interesting. The original specifications, as regards the manner of testing, were so inipracticable (when their severity mas taken into consideration), that the keel of the first vessel, which will be launched next month, would, had they been carried out, probably not have been laid until next year. At my suggestion, in order to simplify and expedite the immense amount of testing that had to be done, the Naval Advisory Board was induced, after considerable discussion, to alter the specifications, so as to test each heat, instead of each lot of twenty plates, but reserved the right of making the quenching-test on a piece from each ingot, after it had been rolled. This relieved us from the anxiety of having a lot of plates rejected, after they had beell rolled and sheared, by reason of the presence of one or two plates which might have been injured in heating or rolling, or which might not have been able to stand the tests; while it insured the Government in obtaining a uniform quality of steel, and prevented the temptation to introduce a half-dozen or more had plates in a lot, and run the risk of their being selected as the testplates. I give below a portion of the original specifications, as prescribed

Jan 1, 1884