By D. C. Hilty, W. Crafts

Determination of the solubility of oxygen in iron containing silicon, or manganese, or both, has confirmed the earlier work on silicon, shown that manganese is more effective than expected, and has demonstrated that the combination of silicon and manganese is a much stronger deoxidizer than might have been inferred from their individual effects. SILICON and manganese are of primary impor-tance in the deoxidation of steel, and a study has been made at the Union Carbide and Carbon Research Laboratories, Inc. of the solubility of oxygen in iron in the presence of silicon and manganese, singly and in combination, as a basis for more effective control of inclusion formation. The investigation was carried out with the same equipment and experimental procedure that were used in the determination of the oxygen solubility of iron containing aluminum'. The heats were melted in a rotating crucible furnace under an argon atmosphere. Bath temperatures were controlled by platinum/platinum +10 pct rhodium thermocouples to attain equilibrium at 1550°, 1600°, and 1650°C, so that oxygen solubility isotherms were determined directly without requiring calculation from a temperature coefficient. A detailed description of the furnace and procedure is given in the paper on aluminum deoxidation1. Oxygen solubility in the presence of more than 0.10 pct silicon was found to approximate earlier determinations closely, but some deviation was observed at lower silicon contents. Manganese appeared to be more effective than had been anticipated. The combination of silicon and manganese lowered the solubility for oxygen markedy as compared with either silicon or manganese alone. Although the solubility for oxygen in the presence of both silicon and manganese represents only a part of the information needed to control inclusion formation, it suggests a partial explanation of the benefits of this combination that have been observed in practice. Manganese and Oxygen in Liquid Iron: The study of oxygen in iron in the presence of manganese was carried out in magnesia crucibles of the type furnished commercially for laboratory induction furnaces. Alumina crucibles were unsatisfactory, because the work on the aluminum-oxygen equilibria in iron' had shown that merely melting iron in an alumina crucible limited the solubility of oxygen to a level considerably below that anticipated for moderate concentrations of manganese. Silica crucibles appeared unsuitable because of the dangers of excessive fluxing by the melt. Moreover, as will be shown later, melting iron in a silica crucible also limits the oxygen content below that in equilibrium with

Jan 1, 1951

By John D. Sullivan, Edwin J. Rogers, Chester R. Austin

THE problem of making a building unit combining the necessary physical and mechanical properties and good thermal insulation has been foremost in the minds of architects and ceramic and construction engineers for many years. This paper presents the results of studies on thermally expanding shales or clays to produce light-weight cellular products suitable for making building units. An expanded clay block suitable for building purposes should be large enough so that substantial savings may be effected in labor costs in laying the wall. The permeability should be low and it should have sufficiently good "dry-wall" characteristics to permit exposing the exterior surface to the elements, and to permit plastering directly the inside wall surface. The thermal conductivity should be low and the mechanical properties should be adequate. Obviously, a unit possessing satisfactory qualities for constructing an outside wall would be satisfactory for interior walls and for back-up purposes. The results of studies on bloating various shales or clays† and the properties of the expanded products are reported. In another paper1 basic factors involved in bloating of clays are discussed. Manufacturers of ceramic products, particularly structural clay, may encounter bloating of the ware during burning, and precautions must be followed to avoid this phenomenon. About 1927 the C. F. Burgess Laboratories, Madison, Wis., while carrying on an investigation for the American Face Brick Research Corporation, conceived the idea of intentionally bloating clay while holding it in a restrained condition, with the hope of producing a unitary cellular mass. Work was carried on until about 1931, when studies were terminated because of business conditions. These studies were continued later by The Western Brick Co., Danville, Ill., which developed a process of "inwardly expansive bloating." The major purpose of the latter investigation was to produce back-up tile to compete with concrete blocks made from Haydite or cinder aggregate. Haydite is a light-weight aggregate formed by heating certain clays or shales rapidly in a rotary kiln. While the investigations at the C. F. Burgess Laboratories or at Western Brick Co. were not carried far enough to lead to the commercial production of material for the construction of walls, particularly outside walls, they showed that certain clays could be thermally expanded and that it was possible to produce a material of low permeability with a large percentage of the total voids or cells closed. Commencing in 1939, the Ozark Chemical Co. sponsored a research program at Battelle Memorial Institute for the purpose of determining whether it is technically feasible to make thermally expanded building units, and specifically to get answers to the following questions:

Jan 1, 1942

By R. J. Wasilewski

The variation of elastic modulus with terrzperature between -150° and 600°C has been investigated. Compounds close to equiatomic cornposition exhibit very low modulus values and very high damping near room temperature. The modulus rises steeply with both decreasing and increasing temperature. The modulus minimum and the high damping are believed to be connected with a martensitic transformation of TiNi. In bulk material this transition takes place slightly above room temperature quite rapidly and reversibly, with a hysteresis of some 30°C, depending on the Ti:Ni ratio. Oxygen impurity affects the reaction time. THE inter metallic compound TiNi has been reported to exist in an ordered CsCl (B2) structure,l-6 the homogeneity range varying rather markedly with temperature.7 Some investigators reported this compound to decompose peritectoidally to Ti2Ni and TiNi, between 650° and 800°C,3 or below,',g the latter workers also suggesting the decomposition to be strain-sensitive. Purdy and Parr were the first to report a structural transformation to a new, possibly hexagonal, structure at 36°C,7 a temperature indubitably too low to allow the significant amount of diffusion necessary for a peritectoid reaction. Mechanical-property investigations of compositions close to TiNi just above room temperature have qualitatively shown remarkable anomalies, particularly with respect to clamping,' and to a "memory" effect, that is, plastically deformed material returning to its original shape on being heated through the "decomposition" temperature.9 The original explanation of this effect—based on the apparent experimental observation of Ti2Ni or TiNi, formation in the material subjected to tensile or compressive stresses, respectivelp—does not appear plausible. It appeared more probable that the change involved may be a martensitic, diffusionless structural transformation, similar to those observed in other B2 structures such as 0 brass,'' AuCd,ll and AuZn.12 The existence of such transformation has been established recently,', although the symmetry of the low-temperature structure is not yet known. The present paper describes the elastic modulus and damping behavior of polycrystalline TiNi in both structures. EXPERIMENTAL METHOD 1) Specimens. All the specimens to be investigated were prepared from premelted electrolytic nickel and iodide titanium by nonconsumable arc melting and casting in a water-cooled copper mold. The cast billets were canned in mild steel, extruded, and swaged to approximately 0.375 in. diam. The cans were then removed by pickling or machining. Preliminary material balance checks indicated no significant weight losses on melting (less than 5 mg on a 50-g button); hence nominal compositions have been used throughout. In agreement with previously reported observations7 no single-phase material was obtained at—or close to—Ti 1.00 Ni1.00 a small amount of finely divided second phase always being present. It was found that most of the oxygen impurity was associated with this minor phase, which was identified as oxygen-bearing Ti2Ni—possibly Ti,Ni,O. The amount of this phase—at any given Ti:Ni composi-

Jan 1, 1965

By H. O. Hofman

In the blast-furnace smelting of lead, copper and other non-ferrous metals, the largest part of the product obtained is slag. Its formation consumes more of the heat-energy of the fuel charged than any other chemical reaction that takes place. It is therefore of importance to know at what temperatures the different slags will form, so as to be able to choose in a given case the slag that will form at the right point in the operation, will keep the products thoroughly fluid, so as to insure a satisfactory separation, and will permit the consumption of fuel to be reduced to the lowest practicable point. While practical experience has brought out in a general way the leading differences as to the formation-temperatures of Rome silica—iron —lime slags, accurate details are still wanting. The object of the investigation here described was to supply some of these.* Prominent among the men who have worked on the fusibility of silicates are Lampadius, † Sefström,‡ Berthier,§

Jan 1, 1900

By George J. Young

DURing the spring of 1910 1 visited a number of open-pit brown-coal mines and underground workings in the vicinity of Halle, Halberstadt, Leipsic, Cologne and Bonn. The notes which I took and the observations which I made at the time have been condensed and make up the principal part of this paper. Certain supplementary information has been taken from several sources which are given in the paper. The mining of brown coal is one of the important industries of Germany. The coal varies in color from dark brown to almost black and is soft like loam. Pieces of wood and strips of bark and even parts of tree trunks are frequently encountered in the excavation although the coal for the most part consists of a pulverulent, more or less matted mass of small particles of vegetal matter. It is a product between peat and lignitic coal. An analysis, taken from Coal Resources of the World shows the approximate composition of the material: Moisture, 53.73 per cent.; ash, 4.98; fixed carbon, 18.08; volatile carbon, 23.31 per cent. Thc principal characteristic is the amount of moisture. This seldom runs less than 48 per cent. The ash is usually low and ranges from 5 to 10 per cent. The sulphur content is usually less than 0.5 per cent. The heating effect of the fuel ranges from 2,000 to 2,500 calories. The commercial deposits are confined to the Tertiary period although

Jan 1, 1916

By W. Rostoker, S. Spachner

A N alloy of 50 pct Ni-50 pct Fe is currently manu- factured in tape thickness down to 1/8 mil. In the annealed form, this alloy produces an almost square hysteresis loop. This has generally been related to the fact that by proper rolling and annealing practice a sharp cube, (100) [OOl], texture can be developed. As part of a program directed toward an understanding of the relationships between magnetic properties and structure of tape core materials, analyses were made of preferred orientations in tapes of various thicknesses. Annealed tapes of this alloy in 2, 1, 1/2, ¼, and Y' mil gages were acquired from commercial sources. Pole figures constructed for the 2 and 1 mil tapes showed the expected sharp cube texture. However, the ½, ¼, and ? mil annealed tapes showed no evidence of any preferred orientations. A comparison of two transmission patterns is shown in Fig. 1. The origin of the absence of texture in the tapes of less than 1 mil thickness was explored in some detail. The basic questions were whether the heat treatment for the thinner tapes was wrongly selected, whether the initial cold worked textures were different, or whether the actual thickness of the tape exercised some influence on its annealing characteristics. Quantities of the five gages of tape were acquired in the as-rolled condition just prior to the final anneal. Pole figures of the cold worked textures were constructed for each of the tapes. Eye estimates of in-

Jan 1, 1956

By D. K. Crampton, H. l. Burghoff, J. T. Stacy

THE effect of cold-working upon electrical conductivity of copper and of copper alloys appears not to be generally known in detail Although several papers on the subject have been presented, showing variable effects according to alloy composition, it is often assumed that the 2 to 3 per cent lowering of the conductivity of ordinary tough-pitch copper by severe cold-working is typical for copper alloys Because of this situation it was decided to carry out the present work upon several types of copper, copper-zinc alloys over the commercial range of brasses, other binary alloys, and numerous age-hardening alloys in the quenched, and quenched and aged conditions The large number of alloys investigated made it impossible to study every one in the detail it may have merited Inasmuch as several interesting points that could not be satisfactorily explained came to light, further work is contemplated by the authors It is usually considered that the normal effect of cold-work on ductile metals and unordered alloys is to decrease conductivity slightly In alloys that are in the ordered state, as annealed or otherwise heat-treated, cold-working tends to disorder the structure, resulting in very marked lowering of conductivity The random state of atomic arrangement produces lower conductivity than the ordered state for the same composition 1 PREVIOUS WORK previous work in the authors' laboratory has shown the electrical conductivity of several copper alloys to be decreased by greater amounts than might have been expected, in view of the general knowledge on the subject, when cold-worked Guillet and Ballay2 investigated the influence of cold-work upon the resistivity of several metals and alloys, including copper and some copper alloys The increase of resistivity due to severe working was less than 4 per cent for all pure metals tested, while the increases for the alloys were generally higher In the copper-zinc alloys, they found that the increase of resistance due to drawing increased with zinc content, and reported a 21 7 per cent increase of resistance for an alloy containing 67 9 per cent Cu as severely worked Masima and Sachs3 studied the change in electrical resistance of three brass crystals when stretched in the tensile test, obtaining increases in resistance of the order of 3 per cent for 30 to 40 per cent reduction of area of the specimens The resistance decreased again when the cold-worked crystals were subsequently annealed Bardenheuer and Schmidt4 found that the conductivity of copper was decreased by 3 to 4 per cent when reduced 50 per cent by working The conductivity of 72-28

Jan 1, 1941

By F. Keeler, C. M. Craighead

Aluminum alloys containing magnesium and silicon are susceptible to strengthening and hardening by suitable heat-treatments, and they constitute a class of alloys of considerable commercial importance. Generally, they contain these two elements in the proportions required for the formation of the intermetallic compound Mg2Si, or an excess of silicon; no commercial wrought alloys are made with an appreciable excess of magnesium. The reason for not having excess magnesium is obvious from the results given in this paper, since it is shown that excess magnesium results in a proportional decrease in the solubility of Mg2Si. This is the eighteenthl of a series of papers from the Aluminum Research Laboratories dealing with the equilibrium relations in aluminum-alloy systems; most of the previous publications concerned binary aluminum-alloy systems; this is the fourth of a group pertaining to ternary aluminum-alloy systems. The work on this system was completed in 1930, but the results were not published because of the pressure of other work. Hanson and Gaylor2, in 1921, presented the results of an extensive investigation of the aluminum-magnesium-silicon system. Their results indicated that an excess of magnesium over the amount required to form the compound MgzSi caused a noticeable decrease in the solid solubility of MgzSi in aluminum. A more recent investigation3 in these laboratories showed that the solid solubility of MgzSi in aluminum was 1.85 per cent at 595' C. and decreased to 0.30 per cent at 300' C. The results of the latter investigation were used as the basis for the present work. The Present Investigation In the present investigation, a study was made of the effect of various amounts of excess magnesium upon the solid solubility of MgzSi in

Jan 1, 1936

By A. Steiner, E. Miller, K. L. Komarek

Equations have been derived to calculate the chemical potentials of the components of liquid binary alloys from liquidus and enthalpy data. The equations are applicable to systems with intermetal-lic compounds of limited solid solubility. The liquidus curve of the Mg-Sn system was accurately redetermined, and the melting point of the compound Mg2Sn was found to be 770.5° * 0.3°C. The thermo-dynamic properties of the liquid alloys were calcu -lated from the liquidus data. The activity of tin shows both positive and negative deviations from Raoult&apos;s law and the relative integral entropy is positive. THE phase boundaries in an equilibrium phase diagram are functions of the thermodynamic properties of the coexisting phases. Specifically, the shape of the liquidus curve near an intermediate compound is determined by the properties of the compound and the liquid phase. Hauffe and wagnerl have derived an equation for the chemical potential differences (ui) of the liquid alloys near the congruent melting point when the heat of fusion of the compound and the liquidus curve are known. In their derivation the temperature dependence of the ui value was neglected, and liquid of stoichio-metric composition was chosen as the reference state. To obtain chemical potentials over the ntire composition range of the phase diagram with the pure components as the reference state, equations have been derived which incorporate the temperature dependence of the chemical potentials. Such a thermodynamic analysis can be carried out when the liquidus curve and the enthalpy values are known. The equations have been applied to the redetermined liquidus curve of the Mg-Sn system to obtain the thermodynamic properties of liquid Mg-Sn alloys. The Mg-Sn phase diagram has been studied by various investigators and the results have been compiled and critically assessed by Hansen.2 Preliminary thermal analyses showed that the basic features of the diagram were correct. The system has one congruent melting compound, Mg2Sn, two eutectics, and some solid solubility of tin in magnesium. However, the published liquidus temperatures show considerable scatter. In order to perform an accurate thermodynamic analysis, the liquidus curve between the magnesium-rich and tin-rich eutectic compositions was therefore redetermined by careful thermal analysis using highest-purity starting materials. EXPERIMENTAL PROCEDURE The magnesium metal (Dominion Magnesium Ltd, Toronto, Canada) had a purity of 99.99+ pct with the following impurities (in ppm): 20 Al, 30 Zn, 10 Si, <1 Ni, <1 Cu, <10 Fe; tin (Cominco Products, Spokane, Wash.) contained 99.999+ pct Sn. The graphite crucibles were machined from graphite rods (United Carbon Products Corp., Bay City, Mich.) which had an average total ash content of less than 30 ppm. All the graphite parts were baked out in vacuum at 950" to 1000°C for a minimum of 24 hr to remove volatile organic materials. The graphite crucibles (3 in. long, 1-5/8 in. OD, 1-3/8 in. ID) were tightly closed with a threaded cover (1/2 in. thick) which had a central thermocouple well (2-1/4 in. long, 5/16 in. OD, 3/16 in. ID). Cover and thermocouple well were machined from one piece of graphite. A thin sheath of quartz was inserted in the well to protect the thermocouple

Jan 1, 1964

By T. N. Williamson

6.3-1. Historical Development. Rotary drilling has been used in surface mining for many years. Its principal use is for primary blasthole drilling. In this use, holes in the range from 4 to 15 in. in diameter are drilled in overburden and massive ore bodies for large initial blasting operation. With properly designed shot patterns and loading, secondary blasting is seldom required. The use of rotary drilling with diamond bits for exploration is discussed in Chapter 3.1. Small rotary drillholes of approximately 2-in. diameter are employed as blastholes to shatter uncovered coal seams, but this is a minor part of surface mining drilling operations. Another minor use of rotary drills in surface mining is for placing wire saw poles in dimension stone quarries, usually accomplished with large-diameter calyx or steel shot drills. Primary blasthole drilling by the rotary method was performed with drag bits until 1949 (19). Its use in mining was only in soft formations, so that rotary drills prior to that time were found principally in overburden drilling for the surface mining of coal. In 1949 it was found that air circulation to remove cuttings resulted in increased penetration rate and prolonged life for the rolling-cutter type of bits. Prior to that time, and since their introduction in oil well drilling in 1907, water had been used for circulation with these bits. The dependence on water to clean the hole had delayed the acceptance of bits with rolling cutters in mines because of water haulage and freezing problems as well as the loss of water through cracks in the formation. After rolling cutters were introduced, subsequent improvements in tools made rotary drilling adaptable to harder formations (18). This system is now used in the hardest formations encountered in mining. 6.3-2. Principles of Operation. ENERGY. Rotary drills attack rock with energy supplied to the bit by a rotating drill stem, and infrequently by

Jan 1, 1968

By G. M. Wiles

The increasing number of problems of the modem mine manager has led the author to discuss the art of management. He lists the principles concerning selection of personnel, exploitation and development, new equipment, process improvements, new processes, maintenance, operating cost data and public relations. Application of the principles to problems of mine startup, operation and rehabilitation are described. Since D. C. Jackling was famous for his adeptness at organizing and training teams of operating personnel, the subject of mine management is particularly appropriate for a Jackling Lecture. In fact, it is doubly appropriate because in very basic ways Jackling&apos;s career changed the nature of the tasks and challenges facing a mine manager. Management of mines, of course, is the art of finding and winning minerals economically from the earth&apos;s crust, and it involves the use of all the engineering sciences. But also of prime importance is a skill which is not yet a science - the area of management often referred to as human engineering. Since expenditures on staff and labor may well involve more than 50% of the direct costs of operating a mine, ability at human engineering is just as important as the ability to plan and put into effect the most efficient operating procedures. In addition to his ability to select and train operating personnel, Jackling possessed, to a degree unmatched by many of his contemporaries, broad, analytical powers covering both the economics and operating phases of large scale mineral extraction. His breadth of vision found its greatest expression at the time he analyzed the Utah copper deposit. Fortunately, Messrs. Penrose and Gemmell had enough faith in his analyses to furnish the capital needed to begin operations. The result, as is well known to all of you, was Kennecott&apos;s lucrative Utah copper mine — and the beginning of the open pit porphyry copper era. The Utah copper mine, and Jackling&apos;s subsequent similar successes in Arizona, New Mexico and Nevada, had one thing in common —all of these large porphyry deposits were worthless until open pit, large daily tonnage schemes were developed for their exploitation. The successful development of such schemes made vast new mineral resources available for economic exploitation. But at the same time, the trend away from smaller high grade operations in favor of the far more complicated operations required to handle large deposits of low grade ore have greatly altered a mine manager&apos;s problems. We are all familiar with the saying "mines make managers." There is still some truth in this statement, but far less than there used to be in the days when high grade properties were the rule rather than the exception. When high grade orebodies prevailed, many managers, superficially at least, could not make a mistake because the profits of their mines

Jan 1, 1962

By F. G. Clapp

IT is to be hoped that no casual reader will erroneously refer to the latest publication&apos; of the Division of Public Relations of the American Petroleum Institute, as being "Petroleum Facts and Fancies." The facts are so faithfully derived and the figures are so authentically sponsored by the highest sources that no person can read this valuable volume (287 pages and numerous tables) without being convinced that every- thing therein set forth is "the truth and nothing but the truth." Yet, having read the volume from the perspective of the world&apos;s petroleum industry and with a critical attitude that comes from years of study of the subjects discussed, I find myself tempted to cogitate and to envisage a few of the fancies that come to mind as a fitting sequel.

Jan 1, 1929

By G. P. Conard, E. H. Rennhack

The creep behavior of hot-rolled, hypoeutectic Zn-Ti alloys was investigated in the temperature range from 0.43 to 0.53 TM. Secondary flow was found to originate primarily from strain-induced gvain growth where grain boundary )nigvation served to relieve the strain energy of distortion introduced by slip, grain boundary sliding, and subgvain formation. The extent to which this recovery mechanism operated was determined by the ratio of grain width to the spacing between planar fibers of TiZn,, compound particles generated in these alloys during rolling. When this ratio was unity, creep resistance demonstrated a marked improvement. In this condition, which was fulfilled by annealing following rolling, structural stability was enhanced with decreasing grain size below the equicohesive temperature (-0.5Tm), while the reverse was true above this temperature. TITANIUM concentrations approaching the eutectic composition of 0.23 wt pctl have been shown to promote a significant increase in the creep resistance of rolled zinc,2 The alloying effect created with titanium is somewhat unique; a structure closely resembling that of a fiber-reinforced metal composite can be developed which selectively modifies creep strength in preference to other mechanical properties. In an earlier investigation,~ the present authors found that, while the fiber network, composed of individual TiZn,, compound particles, had a distinct influence on rolled texture, the crystallographic variations produced were of minor importance with respect to creep. Rather, creep resistance seemingly increased when the grain size appeared to coincide with the in-terfiber spacing. The work described here was undertaken to explore this effect in greater detail. EXPERIMENTAL PROCEDURE Three zinc-base alloys containing 0.05, 0.12, and 0.16 wt pct Ti were prepared from CP zinc and iodide titanium in the form of 4 by 2 by f in. chill-cast ingots. The melting and casting procedures for these alloys have been detailed el~ewhere.~ Individual ingots of each alloy were hot-rolled at 200°C (392°F) to total reductions of 10, 25, 50, 75, and 90 pct in from one to five passes, respectively, employing a 10-min reheat prior to each rolling pass. With grain, tensile-type creep specimens with a 1-in.-long, -in.-wide gage section were machined from the rolled strips for test purposes. Annealing studies to explore the influence of grain size on secondary creep flow were carried out at 400°C (752°F) in argon for times extending up to 60 min. The grain-size effect was evaluated in terms of average grain width and length values statistically derived from lineal intersection measurements.4 A similar method was applied in establishing the average interfiber spacing, i.e., average perpendicular distance between adjacent planar fibers. The creep characteristics of the alloys were investigated by means of constant-load and constant-stress creep tests. The former tests were conducted at 25°C (77°F) under an initial stress of 10,000 psi, while the latter were performed in the range from 25°C (77°F) to 90°C (194°F) at stress levels varying from 8000 to 22,000 psi. Total specimen strain, as determined with Budd HE-1161-B strain gages, was in excess of 0.10. Maintenance of constant stress was achieved through periodic load reductions made at 0.01 strain intervals to compensate for the attendant incremental reduction in specimen cross-sectional area. The maximum indicated error in the applied stress at these strain intervals was less than 3.0 pct. RESULTS AND DISCUSSION Constant-Load Creep. In an effort to clarify the in-terrelation between interfiber spacing and grain size with respect to the creep resistance of the Zn-Ti alloys, their separate effects on secondary creep rate were determined as a function of titanium content and rolling reduction. These results are set forth in Figs. 1 and 2, respectively. The average grain diameter plotted in Fig. 2 was resolved from average grain width and length values. No data are presented for reductions of less than 50 pct because of the inability to obtain consistent measurements on these strips. The curves of Fig. 1 indicated that, for a given titanium content, a decrease in interfiber spacing, as produced with increasing reduction, promoted a decrease in creep rate. Depending on titanium content, however, wide variations in creep rate occurred at the same interfiber spacing suggesting that interfiber spacing, by itself, has little or no influence on creep resistance. Grain size, on the other hand, decreased progressively with both increasing rolling reduction and titanium content, the effect of which led to a pronounced decrease in creep rate, particularly when the average grain diameter became smaller than 3.0 x 10"4 in., Fig. 2. The continuity of this relationship tended to support the view that grain size rather than interfiber spacing was predominant in controlling secondary creep. Annealing Effect. The observed dependence of creep flow on grain size suggested that a further contribution to creep resistance would result when the alloys were annealed to effect a coincidence between grain width and interfiber spacing, see Fig. 3(b). ~eiides creating an immediate barrier to grain boundary movement, annealing offered the possibility of providing increased structural stability by eliminating many high-energy, mobile grain boundaries.= To test this hypothesis, specimens from the Zn-0.16 Ti strips reduced 75 and

Jan 1, 1967

By J. L. Lamon, W. Crafts

Study with the electron microscope of the carbides in vanadium-chromium-molybdenum steels after tempering up to 1000 hr at 600 teelsto 1400°F confirmed that alloy carbides are formed at the secondary hardening temperature by decomposition of the plate-like iron carbides. It was also demonstrated that vanadium carbide persists as much smaller particles than do chromium- or molybdenum-bearing carbides. Conditions conducive to the formation of fine vanadium carbides are indicated to be favorable for high temperature strength. IN order to determine the effects of long exposure at high temperatures on vanadium-bearing steels, a survey has been made of their hardness and carbide structure. The behavior of carbides in the tempering of martensite was studied by X ray diffraction and electron microscope examination of electrolytically extracted residues in greater detail than in an earlier investigation.&apos; A group of steels with about 0.25 pct carbon and containing chromium up to 5 pct, molybdenum up to 1 pct, and vanadium up to 1 pct was either quenched or annealed and then tempered for peri- ods of up to 1000 hr at 600° to 1400°F. Their hardness after tempering agreed with the Hollomon and Jaffe2 relation of equivalency of time and temperature, and with the degree of secondary hardening predicted from composition. Further, the appearance of the carbides indicated that the time and temperature equivalency relation was also applicable to the degree of carbide development. The mechanism of the tempering of martensite was demonstrated more clearly than in the earlier study. It was confirmed that carbides develop from martensite as poorly defined plates of the Fe2C type carbide followed by thickening of the plates with a transition to Fe,C. Finally the plate structure deteriorates into a lacy mass from which alloy carbides emerge as chunky particles that grow slowly with further increase of tempering temperature. Vanadium carbide derived from tempered martensite was found in characteristically small particles that tended to grow very slowly. The addition of chromium or molybdenum to a steel with predominant vanadium carbide tended to introduce carbides of a chromium- or molybdenum-bearing type having a somewhat larger particle size. The Cr,C, type carbide particles were larger than those of the V,C, type and somewhat smaller than the carbides in steel containing both Cr,C and M,C. Similar observations were made of the carbides in the pear lite of annealed steels. It appeared that high temperature properties would be benefited by the retention of the fine carbide particles that result from a balance of composition and heat-treatment designed to produce a maximum amount of vanadium carbide. Procedure: The steels used in the investigation were made with a base of Armco iron in a high-frequency furnace at the Union Carbide and Carbon Research Labs., Inc. The steels were deoxidized

Jan 1, 1951

By Laurence C. Hicks

Consideration of the past work on the subject of the diffusion of chromium into iron suggested that additional information might be given by the use of X-ray spectroscopy in following the concentration changes through the diffusion zone. Grube and Fleischbeinl packed rods of electrolytic iron in a mixture of alumina and chromium. These specimens were heated in an atmosphere of purified hydrogen for varying lengths of time. After treatment the specimens were examined metallographically and showed the usual structure, consisting of a border of radially oriented columnar grains ending in a sharp boundary line. Reference is made to the fact that etching with certain reagents will attack only the material inside the border of columnar growth and also to the fact that polishing seems to develop a ridge at the position of the boundary between the etched and unetched areas. By chemical analysis of thin layers turned off on a precision lathe, the authors were able to obtain depth-concentration curves. These curves, reproduced in Fig. 1, show that in most cases a pronounced change of slope occurs, corresponding to the position of the boundary of the columnar grains. In a laler paper Grube extends his work to other systems which show the same characteristics.~ He concludes that the reason for the break in the curve is that a hindrance of diffusion occurs at the place where the regularly oriented grains of the diffusion zone meet the random grains of the interior portion, on the assumption that the diffusion velocity in one direction in a grain may be greater than in another direction, and that the grains in the diffusion zone orient themselves so as to give the maximum diffusion rate. Kel1ey" points out that Grube has failed to note that the boundary line does not consistently cross all grains and

Jan 1, 1934

By Marie L. V. Gayler

WITHOUT diffusion taking place in liquid metals and alloys, no castings could be made; it is therefore the most important factor affecting the structure of metals. Diffusion involves the interchange of atoms, a process which takes place during the life history of an ingot. In the liquid, atoms are in a state of high thermal agitation, but this thermal vibration is reduced in amplitude with falling temperature. When solidification sets in, the atoms arrange themselves on an ordered space lattice and the changes in structure which take place in the solid are due to the interchange of atoms on this space lattice. The rate of atomic interchange-e.g., of diffusion-is most rapid at temperatures close to the melting point and decelerates as the temperature is lowered. At room temperature, the rate of diffusion is practically negligible in most alloys, and any change in structure can only be brought about by using methods which will accelerate the rate of diffusion. The rate of diffusion depends on three factors (I) temperature; (2) concentration gradient and (3) activation energy. The growth of grains and particles in the solid alloy also depend on these factors and are therefore intimately associated with diffusion. The rate of homogenization in a cast alloy depends on several factors, such as: (I) rate of solidification, which involves grain and particle size which, in their turn, depend on diffusion: (2) the nature of the constituents; (3) the temperature interval between the melting point of the metal or alloy and the temperature at which it is being heat-treated. It is well known that coarse, cast structures are extremely difficult-if possible to homogenize, and the finer the grain size and particle size, the more readily solid solution will take place. The rate of diffusion depends, also, largely on the nature of the constituents; for instance, copper and magnesium form solid solutions with aluminum quite readily but nickel and iron do not; neither do certain intermetallic compounds, such as alpha and beta FeSi. Furthermore, the actual formation of intermetallic compounds may be a very slow process, particularly when they are formed in the solid state as equilibrium products. For example, ßFeSi is formed in the solid as the result of the reaction aFeSi + Al?ß FeSi. The particles of aFeSi become sur¬rounded with a reaction ring of ßßFeSi. This layer is formed as the result of diffusion of atoms taking place between the aluminum matrix and aFeSi. As the amount of ßFeSi surrounding the core of aFeSi increases the concentration gradient becomes low and so the rate of diffusion of atoms also decreases until it practically ceases. This occurs after a comparatively thin layer of ßFeSi has been formed. It follows that when intermetallic compounds of this type are formed in the solid, as the result of diffusion, it is generally impossible ever to attain equilibrium, since the forma-

Jan 1, 1944

By Dwight H. Seely, Louis R. Records

A process for low-temperature dehydration of natural gas utilizing Joule-Thomson effect in expansion through a throttling orifice has been tested in a full-scale field installation. The results of these tests are presented in the form of performance curves from which the process may be easily evaluated. The effect of separation temperature on condensate recovery from the process is also shown. INTRODUCTION The transportation of natural gas from producing well to the consumer has always encountered the problem of hydrate prevention. This problem has become increasingly important in the past ten years due to the rapid increase in produced gas volumes, production pressures, transportation pressures and distance from producing wells to consumer. Natural gas, as normally produced from gas or gas-condensate wells, is saturated with water vapor at well-head conditions of temuerature and pressure. The solution of the hydrate problem require; but one basic process — dehydration of the gas to a water content which will result in a water dew-point below the minimum temperature to be encountered from the producing well to the point of consumption. Much of the recent development of gas and gas-condensate reserves in the Gulf Coast Area has been in locations which are accessible only by water. High well-head pressures, pipeline construction and maintenance costs and the desirability of final central gas-condensate separation facilities have stimulated the development of dehydration equipment which can be installed at each well and which will permit hydrate-free transportation of both gas and condensate in the same line to central facilities. There are four types of natural gas dehydration processes now used: 1. Adsorptive processes. 2. Absorptive processes. 3. Chemical reaction processes. 4. Refrigeration processes. The first three of these processes are indirect in that they require use of adsorbents, absorbents or reactive chemicals. These materials require regeneration and part of the total gas stream is consumed in the regenerative process. Indirect processes have a wide range of flexibility as defined by allowable operating pressure and temperature, but most are not easily adapted to automatic operation. The refrigeration process described in this paper was designed for installation at the producing well-head. It requires no regenerative cycle and with normal well-head temperatures no external source of heat. The flexibility of this process is limited only by the pressure drop which may be allowed between well-head and transportation line. THEORY There are three basic physical concepts involved in the low temperature dehydration process. These are: 1. Formation of hydrocarbon hydrates. 2. Joule-Thompson effect resulting from the expansion of gaseous mixtures through a throttling orifice. 3. The equilibrium composition characteristics of water vapor and gaseous hydrocarbon mixture.. The chemical composition and physical structure of hydrate; have been described by several investigators.3,4,5,10 Specific conditions of temperature, pressure and composition as well as the requirements for turbulence and presence of free water necessary for hydrate formation have been described by Katz.6 Natural gas hydrates, as they are found in plugged gas pipe lines, have the appearance of packed snow. The mass of these hydrates has low continuous porosity and permeability. Joule-Thomson effect. or the reduction in temperature which occurs when natural gas is throttled throusll a restrictive orifice, is the basic phenomenon which permits efficient use of refrigeration for the purpose of dehydrating natural gas. Joule-Thomson coefficients for gafeous mixture; of methane with ethane and with butane have been reported by Buder.-I~olzer, Sage and Lacey.2 Brown1 predicted temperature drops for pressure drops from enthalpy-entropy calculations. Aside from this work there were no fundamental data found which would be applicable to natural gas mixtures of varying spe-

Jan 1, 1951

By Dwight H. Seely, Louis R. Records

A process for low-temperature dehydration of natural gas utilizing Joule-Thomson effect in expansion through a throttling orifice has been tested in a full-scale field installation. The results of these tests are presented in the form of performance curves from which the process may be easily evaluated. The effect of separation temperature on condensate recovery from the process is also shown. INTRODUCTION The transportation of natural gas from producing well to the consumer has always encountered the problem of hydrate prevention. This problem has become increasingly important in the past ten years due to the rapid increase in produced gas volumes, production pressures, transportation pressures and distance from producing wells to consumer. Natural gas, as normally produced from gas or gas-condensate wells, is saturated with water vapor at well-head conditions of temuerature and pressure. The solution of the hydrate problem require; but one basic process — dehydration of the gas to a water content which will result in a water dew-point below the minimum temperature to be encountered from the producing well to the point of consumption. Much of the recent development of gas and gas-condensate reserves in the Gulf Coast Area has been in locations which are accessible only by water. High well-head pressures, pipeline construction and maintenance costs and the desirability of final central gas-condensate separation facilities have stimulated the development of dehydration equipment which can be installed at each well and which will permit hydrate-free transportation of both gas and condensate in the same line to central facilities. There are four types of natural gas dehydration processes now used: 1. Adsorptive processes. 2. Absorptive processes. 3. Chemical reaction processes. 4. Refrigeration processes. The first three of these processes are indirect in that they require use of adsorbents, absorbents or reactive chemicals. These materials require regeneration and part of the total gas stream is consumed in the regenerative process. Indirect processes have a wide range of flexibility as defined by allowable operating pressure and temperature, but most are not easily adapted to automatic operation. The refrigeration process described in this paper was designed for installation at the producing well-head. It requires no regenerative cycle and with normal well-head temperatures no external source of heat. The flexibility of this process is limited only by the pressure drop which may be allowed between well-head and transportation line. THEORY There are three basic physical concepts involved in the low temperature dehydration process. These are: 1. Formation of hydrocarbon hydrates. 2. Joule-Thompson effect resulting from the expansion of gaseous mixtures through a throttling orifice. 3. The equilibrium composition characteristics of water vapor and gaseous hydrocarbon mixture.. The chemical composition and physical structure of hydrate; have been described by several investigators.3,4,5,10 Specific conditions of temperature, pressure and composition as well as the requirements for turbulence and presence of free water necessary for hydrate formation have been described by Katz.6 Natural gas hydrates, as they are found in plugged gas pipe lines, have the appearance of packed snow. The mass of these hydrates has low continuous porosity and permeability. Joule-Thomson effect. or the reduction in temperature which occurs when natural gas is throttled throusll a restrictive orifice, is the basic phenomenon which permits efficient use of refrigeration for the purpose of dehydrating natural gas. Joule-Thomson coefficients for gafeous mixture; of methane with ethane and with butane have been reported by Buder.-I~olzer, Sage and Lacey.2 Brown1 predicted temperature drops for pressure drops from enthalpy-entropy calculations. Aside from this work there were no fundamental data found which would be applicable to natural gas mixtures of varying spe-

Jan 1, 1951

By Joseph A. Holmes

Iv all new movements unavoidable misapprehensions arise, which should be cleared away, lest they retard the progress of the movement itself. An impression has gone abroad that the movement for conservation of resources is a new movement. No one knows better than the engineer that this is not the case. Men like Douglas and Raymond and John Fritz and Edison and McDonald, and hosts of others, have preached and practiced conservation as applied to mineral resources throughout a long and useful life-time; and, in general, the work of the engineer and the chemist, both in this and in other countries, has been along the line of continually greater efficiency in the use of all available materials. And the results already accomplished through the efforts of these experts are now saving annually many millions of dollars to the people of the United States in materials and labor. It is true, however, that the need for conservation, that is, for a wiser and more efficient use of the natural resources, has taken on a new life, and is being brought home to the people of the United States in a manner which is awakening public interest and even the public conscience. It is, therefore, both appropriate and fortunate that the engineers, the chemists, and the thinking men of all classes are availing themselves of the present impetus to the movement to emphasize anew the lessons which heretofore they have found it more difficult to impress upon the American public or even upon the captains of industry. Still another of these misapprehensions is to the effect that many of the leaders in the present movement hope to bring about conservation of resources through legislation or execu-

May 1, 1909

By Donald B. Hunter

The Ti-Be system up lo 10 wt pct Be with cortlmercialll&apos; pure titanium has been determined using metal-lographic techniques. Beryllium forms the p eutec-toid type of dinqarz with titanium; the eutectoid occurs at 0.5 xt pct Be azd 1500 F, while an eutectic is foritled at 1887°F containing between 5 and 7.5 rt pct Be. The solubility of beryllium in a titanium does not exceed 0.05 zvt pct and the maximum solubility of Beryllim in 0 titanium is 1 wt pet. PREVIOUS work on the Ti-Be phase diagram indicated that additions of beryllium to titanium resulted in a marked lowering of the melting point,&apos;&apos;&apos; and it was also observed that the solubility of beryllium in both a and p titanium was retricted.- With the limited data available, McQuillan and McQuillan constructed a partial hypothetical diagram of the Ti-Be system,= assuming that beryllium formed the 0 eutectoid type of system with titanium. Subsequently Bedford published a tentative diagram of the entire Ti-Be system: although he did not investigate alloys containing less than 10 wt pct Be. This diagram included several compounds described by other authorities.&apos;-l3 The following account describes work directed toward determining the form of the titanium-rich portion of the phase diagram up to 10 wt pct Be. MATERIALS AND METHODS Titanium sponge and a master alloy containing 25 wt pct Be were used in the formulation of the alloys; the chemistry of these materials is detailed in Table I. The alloys were prepared as 250-g compacts which were melted into buttons by arc melting under purified argon on a water-cooled copper hearth. Results of analyses for beryllium are shown in Table I but no determination of other elements was made at this stage. The alloys were hot-rolled at 1650°F to produce 0.1-in.-thick sheet. Alloys containing up to 1.5 pct Be were fabricated without trouble; samples containing 2 pct cracked initially upon hot rolling, but thereafter rolled satisfactorily to sheet. The 5, 7.5, and 10 pct were hot short and could not be rolled. Surface contamination was removed from samples by sandblasting and pickling in a 5 pct HF-35 pct HNOs solution. For metal log raphic examination, heat-treated specimens were mounted transverse to the rolling direction, ground on silicon carbide papers of increasing fineness to 600 grit, and electropolished at 20 v using a solution containing 600 ml of methanol, 60 ml of perchloric acid, 360 ml of butyl cellosolve, and 2 ml of Solvent "X". Difficulty was experienced in obtaining good electropolished surfaces with samples containing more than 1 pct Be, the degree of difficulty in-

Jan 1, 1967