Search Documents

By A. H. Kline, E. B. Zimmer, Zay Jeffries

It is well known that many properties of a given metal vary with the size of grain or cell. For most industrial purposes, where high ultimate strength and high elastic limit are desired, the manufacturer tries to produce a fine-grained structure. For some purposes, for example in transformer iron, a coarse-grained structure is desirable. The terms fine-grained and coarse-grained are used only in a relative sense. For example, a fine-grained cast copper might have grains 100 times larger than coarse-grained high-speed steel. Similarly, a finegrained steel rail might have grains or cells 100 times larger than coarsegrained wire, which was made of steel from the same heat. In some metals, the change in grain size is more appreciable khan the changes in any of the properties determined by the tensile test. Furthermore, in metals which have been annealed or subjected to high temperatures, grain size may prove to be a better indication of the life of the metal in use than the tensile test. One of the authors was able to supplant the tensile test with grain-size determinations in the control of metal for a specific use, the latter determination being more indicative of the life of the metal part than the tensile test. A grain-size determination with a tensile stest is, of course, more valuable than either singly. At present there is a decided dearth of data on actual grain-size determinations in metals, and consequently a corresponding lack of ability to interpret the determinations after they are made. It would be desirable to have correlation made between grain size and properties of metals, comparing thousands of determinations. In this way, grain-size determinations might be interpreted in much the same manner that tensile tests are now. Several Methods of Measuring Grain Size One of the chief reasons why more grain-size measurements have not been made is the excessive work involved in making a determination.

Jan 1, 1916

By F. S. Buffington, Morris Cohen

THERE is little quantitative information available concerning the effect of applied stress, in both the elastic and plastic ranges, on diffusion kinetics. Accordingly, a program has been undertaken to determine the rate of self-diffusion in high purity iron, with the specimens subjected to stress during the course of diffusion. Results are reported here for body-centered cubic iron at a diffusion temperature of 890°C. The iron used was 99.97 pct Fe, the principal impurities being 0.002 pct C, 0.008 pct 0, and 0.02 pct Si. The surface-decrease method of self-diffusion analysis was employed, and Fe55 Mn x-radiation, 2.9 years half-life) was the tracer element. Details of specimen preparation and equipment are given elsewhere.' Disks of the high purity iron, % in. diam x 1/4 in. thick, were annealed at 890°C for 18 hr in dry hydrogen to produce large grains of a ferrite. The faces of the disks were then surface ground, and possible grinding stresses were relieved by annealing at 890 °C for 45 min in vacuum. A layer of radioactive iron 0.00186 cm thick was electroplated on one face of each disk. The self-diffusion coefficient was calculated from the ratio of the radiation intensities emanating from each of these faces, as measured before and after diffusion.' The heating was carried out in a vacuum furnace (10-5 mm Hg) controlled to ±1.5°C. The specimens were loaded in compression between two quartz disks during the diffusion runs by means of a lever system operating through a vacuum seal. Thus one quartz disk was pressed directly against the radioactive face of the specimen, minimizing the vapor loss of radioactive iron. Steady-state creep occurred in all instances where permanent deformation could be detected, but the specimens did not exhibit appreciable transverse barreling until natural strains of 0.2 to 0.3 were attained. Essentially, the diffusion took place under uniaxial stress. The plastic strain in each case was obtained at the diffusion zone by measuring the diameter d there before and after the run: e = 2 In — do Let Du equal the self-diffusion coefficient which would have prevailed at the given temperature if no stress had been applied. This was calculated from the temperature-dependence equation which had been previously determined: —59,800 D, = 6.2 exp ( I sq cm per sec* [I]

Jan 1, 1953

By S. Kado, G. Derge, L. Yang

Self-diffusion coefficients of silver in molten silver have been measured by means of the capillary-reservoir method in the temperature range 1002" to 1105°C. The results can be .represented by the equation D = (7.10 i 0.06) X 10-4 exp [(—8150 ± 1130)/RT]. The heat of activation agrees within the limit of experimental uncertainty with that for the viscous flow. The validity of the Eyring and the Stokes-Einstein equations are examined on the basis of the self-diffusion coefficients obtained and the known viscosity data of molten silver. MEASUREMENT of the self-diffusion coefficient of silver in molten silver was made in the temperature range 1275° to 1378°K, using the capillary-reservoir method and &"' as the radioactive tracer. The experimental arrangement is shown in Fig. 1. Silver of 99.99 pct purity (fine silver), was melted and degassed in vacuum in a graphite crucible situated inside a McDanel vacuum jacket. The crucible (4 in. tall and 1 in. ID) was protected both at the top and at the bottom with graphite shields and contained about 220 g of silver. The sample holder was a piece of graphite rod (1 in. long and 1/2 in. diam) with 4 capillaries drilled longitudinally into it. The holder was screwed onto a long graphite rod (12 in. long and 74 in. diam) which was connected to a steel disk hanging on a nylon string through a glass pulley. The steel disk kept the sample holder at the center of the McDanel tube and was heavy enough to overcome the buoyancy when the holder was lowered into the molten silver. By turning a handle connected to the pulley through a tapered glass joint, it was possible to raise or lower the sample holder without breaking the vacuum. Two such arrangements were constructed, sitting side by side in 2 Kanthal furnaces. One with non-radioactive silver in its crucible was used for the diffusion run and the other with radioactive silver in its crucible was used for filling the capillaries. To fill the capillaries with radioactive silver, the sample holder was degassed first and then lowered into the radioactive molten silver in vacuum. Purified argon gas was then admitted into the system to push the liquid silver into the capillaries. After cooling in argon, the filled capillaries were polished on emery paper to expose the top of the rod and used immediately as samples for the diffusion run which was carried out at the same temperature as that used for filling the capillaries. During the diffusion run, the samples were degassed in vacuum and lowered slowly into the nonradioactive molten silver before purified argon was admitted into the system. After a predetermined period of time, the samples were raised out of the melt and cooled in argon. The temperature of the melt was measured before and after the run with a chromel-alumel thermocouple inside a McDanel protection tube. Another chromel-alumel thermocouple attached to the outside wall of the McDanel vacuum jacket was used to indicate any fluctuation in the temperature of the furnace during the run, which was found to be less than ± 2°C for the longest run made (93 min). The temperature gradient inside the molten silver was found to be negligible. No significant difference was observed in the results obtained whether the melt was stagnant during the run or was stirred by raising and lowering the sample holder slowly a few times a minute for a distance of about 1/4 in. inside the melt.

Jan 1, 1959

By H. E. Wheeler

The work described was carried out during 1917 and 1918 at the testing laboratory of Watertown Arsenal at the instigation of the Nitrate Division and later with the concurrence of the Cannon Section of the Ordnance Department, U. 8. A. The experiments follow three principal lines of work: First, the effect of nitrogen under pressure on steel containers of various compositions at a red heat; second, the effect of decomposing ammonia on various alloy steels, iron, and non-ferrous alloys; third, a new theory of the erosion of guns in respect to the effect of nitrogen in steel. Part I In the Haber process for the manufacture of ammonia from its elcnlents, it is necessary to have nitrogen and hydrogen of 1500 lb. per sq. in. (105.5 kg. per sq. cm.) at a temperature of 500 to 600' C. The steel containers for these gases gave trouble by failing without apparent cause. When the General Chemical Co. began to develop its method for the production of ammonia, it experienced the same difficulty and, knowing that the Haber process had solved the difficulty by the use of alloy steels, it made several small steel bottles of different compositions and kept them filled with these gases at this pressure and temperature until they failed. The time of service varied from a few days, for the plain steel casting, to two years for a chrome-vanadium forging. Four of these steel bottles were sent to this laboratory for investigation; they were a plain carbon-steel forging, a nickel-stee1 forging, a chrome-vanadium steel forging, and a chrome-steel forging. The time of service was as follows: plain carbon steel, 4 mo.; nickel steel, 6 mo.; chrome-vanadium steel, over 2 yr.; chrome steel, 4 mo. When these containers were cut open and the cross-section surface polished, they showed an inside zone with a different luster from the rest of the metal. Upon etching, this zone was almost unaffected while the rest of the steel etched normally.

Jan 1, 1922

By H. E. Wheeler

The work described was carried out during 1917 and 1918 at the testing laboratory of Watertown Arsenal at the instigation of the Nitrate Division and later with the concurrence of the Cannon Section of the Ordnance Department, U. 8. A. The experiments follow three principal lines of work: First, the effect of nitrogen under pressure on steel containers of various compositions at a red heat; second, the effect of decomposing ammonia on various alloy steels, iron, and non-ferrous alloys; third, a new theory of the erosion of guns in respect to the effect of nitrogen in steel. Part I In the Haber process for the manufacture of ammonia from its elcnlents, it is necessary to have nitrogen and hydrogen of 1500 lb. per sq. in. (105.5 kg. per sq. cm.) at a temperature of 500 to 600' C. The steel containers for these gases gave trouble by failing without apparent cause. When the General Chemical Co. began to develop its method for the production of ammonia, it experienced the same difficulty and, knowing that the Haber process had solved the difficulty by the use of alloy steels, it made several small steel bottles of different compositions and kept them filled with these gases at this pressure and temperature until they failed. The time of service varied from a few days, for the plain steel casting, to two years for a chrome-vanadium forging. Four of these steel bottles were sent to this laboratory for investigation; they were a plain carbon-steel forging, a nickel-stee1 forging, a chrome-vanadium steel forging, and a chrome-steel forging. The time of service was as follows: plain carbon steel, 4 mo.; nickel steel, 6 mo.; chrome-vanadium steel, over 2 yr.; chrome steel, 4 mo. When these containers were cut open and the cross-section surface polished, they showed an inside zone with a different luster from the rest of the metal. Upon etching, this zone was almost unaffected while the rest of the steel etched normally.

Jan 1, 1922

By F. Keller

ALUMINUM alloys containing magnesium and silicon are susceptible to strengthening and hardening by suitable heat-treatments, and they constitute a class of alloys of considerable commercial importance. Generally, they contain these two elements in the proportions required for the formation of the intermetallic compound Mg2Si, or an excess of silicon; no commercial wrought alloys are made with an appreciable excess of magnesium. The reason for not having excess magnesium is obvious from the results given in this paper, since it is shown that excess magnesium results in a proportional decrease in the solubility of Mg2Si. This is the eighteenth1 of a series of papers from the Aluminum Research Laboratories dealing with the equilibrium relations in aluminum-alloy systems; most of the previous publications concerned binary aluminum-alloy systems; this is the fourth of a group pertaining to ternary aluminum-alloy systems. The work on this system was com-pleted in 1930, but the results were not published because of the pressure of other work. Hanson and Gaylor2, in 1921, presented the results of an extensive investigation of the aluminum-magnesium-silicon system. Their results indicated that an excess of magnesium over the amount required to form the compound Mg2Si caused a noticeable decrease in the solid solubility of Mg2Si in aluminum. A more recent investigation3 in these laboratories showed that the solid solubility of Mg2Si in aluminum was 1.85 per cent at 595° C. and decreased to 0.30 per cent at 300° C. The results of the latter investigation were used as the basis for the present work.

Jan 1, 1936

By Sherwin F. Kelly

THAT gold ores occur in Georgia is a fact apparently not widely known outside of that state, yet in the last hundred years nearly $18,000,000 worth of gold has been mined there. The discovery of gold-hearing quartz was made in 1823 on the "Forty Acre Lot" (which now belongs to the Columbia Mining Co.), in McDuffie County, and about seven years later the first stamp mill on record was erected near there. In recent years Georgia's gold production has dwindled to an insignificant figure. However, with the increase in gold price, interest in this district has been revived, so an electrical geophysical survey was undertaken to aid in discovering new quartz veins, on a part of the Forty Acre Lot, the adjoining Hamilton mine, and the nearby Woodall property.

Jan 1, 1934

The following communication was recently sent President Wilson by J. Parke Channing, Chairman of the Engineering Council: The transportation systems of our country are largely the creations of its professional Engineers. This statement can be made without disparagement to the statesmen, the financiers, the manufacturers, the lawers, the educators, the mechanics, the laborers and many others, who, with the Engineers, have contributed to the development of transportation. Through all stages of preliminary exploration, final survey, construction, upkeep and operation, in financial management, and in adjustment of the relations of transportation to the public, the genius and knowledge of the Engineer are essential. Not only in technical physical matters, but also in determinations of policy, his contributions have supplemented and must ever supplement those of other men. These declarations hold good for all the carriers of commerce, by rail, by highway, by water, by pipe-line, by wire, or by air. Hence, it follows that the body established by Government to regulate the commerce, the carriers and the ways of communication, embracing so many engineering features, should number among its nine members, men of engineering training and experience. Engineering Council, being aware of a vacancy on the Interstate Commerce Commission, begs leave to request the Chief Executive that in filling this vacancy, he give earnest thought to the selection of a man who, to his other qualifications, adds the training and experience of an engineer familiar with transportation problems.

Jan 9, 1919

By W. E. Forsythe

Different forms of optical pyrometers are discussed and the advantages and disadvantages of the different types for measuring high temperatures are pointed out. These advantages and disadvantages lead to the selection of the disappearing-filament type of optical pyrometer for most work. Attention is directed to the necessity for the use of a monochromatic screen with a pyrometer, which leads to a discussion of the meaning and use of the effective wave length of the screen. Methods of calibrating the optical pyrometer are outlined and it is shown that an optical pyrometer can be calibrated just as definitely as any other temperature-measuring device. Accuracy tests are included, in which it is shown that excellent results can be obtained by even untrained or slightly trained observers with this form of optical pyrometer. The various corrections that are necessary in this kind of work are indicated, including corrections for stray light, for absorption of windows, of smoke, and so forth. The troublesome problem of measuring the temperature of bodies that do not radiate like a black body is discussed and the corrections for reducing such readings to the true temperature are given for a number of different materials. Introduction The fundamental idea of temperature depends upon our temperature sense and bodies are said to be hot or cold depending upon the reaction of our hands or some other part of the body to the heat from the source investigated. For measuring the temperature some instrument must be devised, since the temperature of the source studied is apt to be so hot as to greatly injure any part of the body that comes near it, to say nothing about direct contact with it. Definition of Temperature.—The temperature scale is based upon two fixed points, the temperature of freezing water and the temperature of boiling water. This temperature interval, depending upon the scale

Jan 1, 1936

By W. E. Forsythe

Different forms of optical pyrometers are discussed and the advantages and disadvantages of the different types for measuring high temperatures are pointed out. These advantages and disadvantages lead to the selection of the disappearing-filament type of optical pyrometer for most work. Attention is directed to the necessity for the use of a monochromatic screen with a pyrometer, which leads to a discussion of the meaning and use of the effective wave length of the screen. Methods of calibrating the optical pyrometer are outlined and it is shown that an optical pyrometer can be calibrated just as definitely as any other temperature-measuring device. Accuracy tests are included, in which it is shown that excellent results can be obtained by even untrained or slightly trained observers with this form of optical pyrometer. The various corrections that are necessary in this kind of work are indicated, including corrections for stray light, for absorption of windows, of smoke, and so forth. The troublesome problem of measuring the temperature of bodies that do not radiate like a black body is discussed and the corrections for reducing such readings to the true temperature are given for a number of different materials. Introduction The fundamental idea of temperature depends upon our temperature sense and bodies are said to be hot or cold depending upon the reaction of our hands or some other part of the body to the heat from the source investigated. For measuring the temperature some instrument must be devised, since the temperature of the source studied is apt to be so hot as to greatly injure any part of the body that comes near it, to say nothing about direct contact with it. Definition of Temperature.—The temperature scale is based upon two fixed points, the temperature of freezing water and the temperature of boiling water. This temperature interval, depending upon the scale

Jan 1, 1936

By N. E. Truitt, D. G. Russell

The transient pressure behavior of a well which produces a single compressible fluid through a singte-plane wrticat fracture has been investigated mathematically. The fracture is assumed to possess infinite flow capacity, to be of limited mdial extent, and' to penetrate the producing formation completely in the vertical direction. Previous studies of vertically fractured wells have been concerned primarily with production rate performance or semisteady-state pressure behavior. This study was undertaken to ascertain the influence of vertical fractures on transient pressure tests such as pressure build-ups and flow tests. In a vertically fractured system, flow in the region nearest the fracture is practically linear, whereas farther away from the fracture essentially radial flow prevails. Thus, transient pressure analyses based on radial flow theory are somewhat inaccurate. As fracture penetration increases radially, kh values calcutated from pressure build-up and flow test curves become increasingly larger than true values. Failure to consider the effect of fracture penetration also introduces inaccuracies into the catculation of fracture length from the apparent skin factor and into the determination of average reservoir pressure. If the total length of the fracture is 20 per cent, or greater, of the drainage radius of the well, corrections must be made to pressure build-up and flow test results. Methods for correcting such results are discussed in this paper. For wells with prefracturing pressure build-up or flow test data, it is possible to estimate fracture length by comparison with postfracturing build-up or flow test results. In new wells or wells without prefracturing build-up or flow test data, fracture length must be estimated to correct the values obtained from analysis of pressure tests after fracturing. Fracturing efficiency calculations should be made whenever possible to provide an estimate of fracture length. Tables of the dimensionless pressure drop as a function of time and fracture penetration are included in this paper. Using these values should permit analysis of other types of transient pressure behavior in vertically fractured wells. INTRODUCTION Hydraulic fracturing has been used quite successfully for over a decade as a completion and stimulation technique in oil and gas wells completed in low-permeability reservoirs During this period a considerable amount of theory has evolved on the performance of hydraulically fractured reservoirs and on more efficient means of artificial fracturing. Although theory has been developed, no rigorous investigation has been made of pressure build-up and flow test behavior in such wells. Prats et al.1 first discussed the performance of vertically fractured reservoirs for the case of a compressible fluid. Their work was primarily concerned with production performance at constant flowing pressure. These authors also considered large-time (semisteady-state) constant production rate behavior for vertically fractured wells; however, transient pressure behavior at constant rate was not investigated. McGuire and Sikora10 and Dyes, Kemp, and Caudle2 employed an electrical analog to investigate the influence of artificial vertical fractures on well productivity and pressure build-up. They found that fractures which extend beyond 15 per cent of the drainage radius away from the well alter the position and slope of the straight-line portion of the build-up curve. They concluded that these effects must be considered both in the determination of the effective permeability of the formation and in any calculations of final build-up pressure. Although these authors did not undertake an exhaustive study of the influence of vertical fractures on pressure build-up performance, their limited results were quite interesting from the standpoint of the effects they demonstrated. In a more recent paper, Scott- reported the results of an investigation of the effect of vertical fractures on pressure behavior, which was conducted with a heat flow model. Scott's results appear to be consistent with those reported in Refs. 1 and 2. However, the effects of different fracture lengths on performance were not investigated. Pressure build-ups and transient flow tests are among the most diagnostic tools available to the reservoir engineer or production engineer. Since a very high percentage of present-day well completions incorporate the hydraulic fracturing technique, a definite need exists for information on the effect of fractures on transient pressure performance. For these reasons we have undertaken a rigorous study of pressure build-up and flow test behavior in vertically fractured reservoirs. The objectives of this study were (1) to obtain synthetic pressure build-up and flow test

Jan 1, 1965

By AIME AIME

BY the end of 1943, the United States will be able to produce aluminum at a rate of 1,150,000 tons a year. How much aluminum is 1,150,000 tons? It is sufficient to replace every railroad passenger car in this country three times a year. Or, it would put a thirty-piece aluminum cooking utensil set in every one of America's 34,000,000 homes with enough metal left over to make 5,000,000 miles of aluminum transmission cable, such as was used in the electrification of much of rural America. Expansion of aluminum production capacity for the war program has occurred in three steps: (1) expansion by private industry; (2) the letting of contracts by the Defense Plant Corp. for the construction of additional aluminum plants which may remain after the war to compete with existing facilities; and (3) the more recently announced D.P.C. program for the building of emergency plants to make aluminum, using stand-by power available in large metropolitan centers power of relatively higher cost, making it questionable whether such plants, now gravely needed, will be able to compete in a peacetime economy.

Jan 1, 1943

By S. A. Herres, A. R. Elsea

Temper brittleness refers to the loss in the notched-bar impact resistance encountered in most medium- or low-alloy steels when they are tempered within the temperature range of 700 to ll00°F or slowly cooled from a higher tempering temperature. Temper brittleness is important because it impairs the service properties of otherwise suitable steels over the range of hardnesses obtained at medium tempering temperatures and because it is impractical to cool pieces of large section rapidly enough from higher tempering temperatures to prevent temper brittleness. The problem of temper brittleness has always been closely associated with ordnance manufacture because armor plate and gun steels require good shock resistance and are often heat treated in heavy section. However, it is now realized that many brittle failures in structural alloy steel parts are attributable to temper brittleness, and there is little question that it contributes to the low impact resistance of alloy steels used in the hot-rolled or normalized condition which are slowly cooled from the hot-rolling or normalizing temperature. Recently Hollomonl has presented a comprehensive summary of the literature on the subject and an excellent description of the manner in which temper brittleness affects the notched-bar impact resistance and other mechanical properties of steel. Carpenter and Robertson2 have given a good analysis of the probable mechanism of temper brittleness, which is similar in many respects to the precipitation-hardening phenomenon. Fig 1 is their diagram illustrating the response to tempering of a susceptible steel. Three changes are recognized as the temperature of tempering a previously quenched steel is raised: (1) pre- cipitation occurs more rapidly and to a greater extent and the notched-bar impact value falls to a minimum; (2) coalescence of the precipitated particles begins to be effective and the impact values for both rapidly cooled and slowly cooled specimens increase; (3) the precipitate goes back into solution at higher tempering temperatures and the impact values of specimens cooled rapidly enough to retain the solution increase, while reprecipitation occurs in slowly cooled specimens and their impact values decrease again. No change must proceed to completion before the following one begins and there is overlapping in temperature ranges. Although there have been a large number of experimental investigations of temper brittleness, insufficient evidence has been accumulated to permit definite identification of the precipitate wnich causes temper brittleness nor have the specific effects on it of various alloy elements and impurities in steel been definitely established. This lack of evidence is largely a result of the lack of a suitable measure for temper brittleness. Temper brittleness is evidenced by an increase in the temperature of brittle failure of notched-bar impact specimens, but most of the data are in the form of an arbitrary susceptibility ratio of the room-temperature impact value for specimens quenched from a high tempering temper to that of similar specimens furnace cooled from the temper. It is obvious that this numerical ratio is dependent upon the type of specimen used and the specific conditions of testing rather than the characteristics of the steel. In general, manganese, chromium, and nickel alloy steels are most susceptible to temper brittleness and molybdenum has heen used to decrease

Jan 1, 1950

By Lennart Bergstedt, Olov Fägremo

Boliden Metall Aktiebolag, the prime base metal mining company of Sweden, treats some 10-10.9 t/y (11-12 stpy) of sulphide ore in nine concentrators. During the years considerable effort has been devoted to the development of all phases of the technology of ore prospecting, mining, milling, smelting and refining. This has been necessary due to the complex and low grade ores. The autogenous grinding technique was first studied within the company as early as 1945. Basic test work commenced during the early fifties, whereby the merits of pebble grinding could be evaluated. In parallel with the converting of the rod mill/ball mill grinding systems to rod mill/pebble mill systems, the development work concerning the feasibility of autogenous grinding went on resulting in the installation of a 8 6.7 x 2.1 m (8 22 x 7 ft.) cascade mill at the Vassbo lead mine in 1959. Long term tests at the Vassbo plant together with a number of pilot plant test involving low grade silicious ores and pyritic comples base metal ores successive led to a better understanding of the process of autogenous grinding. Before a two stage autogenous grinding system could be chosen for the expansion of the Aitik copper mine, a carefully planned survey concerning grinding characteristics and variances in the ore and flowsheet was undertaken. The expanded plant went on stream in 1972 and in the beginning of 1973 and since then has performed excellently.

Jan 1, 1979

Mr. Tays (communication to the Secretary): Mr. Wynne's criticism of my paper* brings forward a few points which are really important, and might properly have been considered in the original paper. By calling attention to them he has rendered me a service. It is quite true, as Mr. Wynne says, that, in the tests reported by me, the Bryan mill was always working at a relative disadvantage, and my comparison of the work of this mill with that of the stamp-battery should be interpreted, therefore, so much the more favorably to the mill. Of course, wire screens can be used to advantage on the Bryan mill, if they are not of smaller size than 30-mesh; but

Jan 1, 1902

By James A. Barr

Ferrophosphorus, an alloy of phosphorus and iron or perhaps a physical mixture of definite compounds of iron and phosphorus, has become of increasing importance as the use of the basic open hearth has extended. Commercial ferrophosphorus is a porous, brittle metal of crystalline structure and often with a bluish metallic luster. A typical analysis is as follows: Per Cent. Phosphorus......................................... 18.0 to 22.0 Iron............................................... 80.0 76.0 Oxygen............................................ 0.2 Sulfur............................................. 0.3 Silicon............................................. 0.1 Carbon............................................ 0.1 Manganese......................................... 0.2 This alloy was first made in an electric furnace, as it was thought that the high heat of the electric arc together with the reductive effect of carbon was necessary. About 1898, J. J. Gray, Jr., was producing a high-phosphorus pig iron in his furnace at Rockdale, Tenn., by using high-phosphorus, local iron ores. As these high-phosphorus ores were difficult to obtain, he conceived the idea of increasing the phosphorus content of the pig iron by the addition of phosphate rock to the furnace burden. When the phosphorus content of the pig was kept low and only small amounts of phosphate rock were added to the burden, no particular troubles were encountered, but when he increased the amount of phosphate rock to produce an 18 per cent. alloy, his furnace troubles rapidly multiplied. After many failures and freeze-ups, he was partly successful in making short campaigns on 18 to 20 per cent. "ferro." At first, when the furnace got in bad shape on ferro, he would switch to a regular pig-iron burden until the furnace was brought around sufficiently to start on ferro again. About this time, Mr. Gray applied for and obtained his first patent. As he grew more skilled in the furnace operations, he was enabled to extend the furnace campaigns and produce ferrophosphorus continuously for the life of the furnace lining. These improvements were made the subject of another patent issued in 1916.

Jan 1, 1925

By P. H. Mell

AMONG the minerals exhibited at the Atlanta Exhibition of 1881, soapstone, kaolin, and asbestos were well represented. The first two occur in large quantities, of very pure quality, throughout the South. The last is somewhat limited in amount, yet in certain localities it exists in masses sufficiently large to pay for working; in North Carolina, Georgia, and Alabama it has been mined with some profit. I would, in this paper, call special attention to the minerals soapstone and kaolin, because their many valuable qualities seem to have been al most entirely overlooked by our Southern manufacturers. Steatite, particularly, occurs in such large quantities, and generally in such close proximity to the great iron regions of Alabama and Georgia, that it is amazing that the iron companies will persist in sending abroad under. heavy expense for firebrick. It would require a much smaller sum of money to quarry this rock and place it at the various furnaces ; and the results obtained, I am sure, would prove its superiority over the majority of firebrick brought into this region. Soapstone, as well as kaolin, is found throughout the metamorphic regions of Alabama, Georgia, South Carolina, and North Carolina. Below-will be found seven analyses that I have made of this mineral, taken from various points in the four States above mentioned. I have also subjected these same specimens to severe fire-tests, and the results were very satisfactory. The tests were conducted in the following manner: Small portions of the compact variety were carefully weighed and placed in a Fletcher's new crucible furnace for gas, and subjected for half an hour to a heat that will in 12 minutes fuse iron. The only effect upon these specimens was a slight change in color .to a darker shade, a small loss in weight, due evidently to the evaporation of water, and, in one or two specimens, a slight degree of fusion on the sharp edges. The first specimen subjected to investigation was taken from a large outcropping in Tallapoosa County, Alabama. Specific gravity, 2.88 ; hardness, 1.9; color, blue gray. Composition Water, - 2.68 Silica, - 65.46 Iron oxide, - 2.10 Alumina, - 15.02 Magnesia, - 15.35 100.61

Jan 1, 1882

By J. P. Hammond, C. J. Sparks, C. J. McHargue

IN a study of the effects of solid solution alloying on the deformation texture of titanium, an alloy containing 3.8 pct A1 was found to develop a (0001) [1010] texture instead of the texture characteristic of pure titanium.ls2 A short investigation has been made of the change in texture with aluminum content. Alloys containing 0.27, 0.47, 1.05, and 1.43 pct A1 were prepared by vacuum arc melting, using iodide titanium as the base material. Homogenized ingots were reduced 90 pct in thickness by cold rolling. Pole figures were obtained using the usual film techniques. Fig. 1 shows that the change from the tilted to the nontilted (0001) position is gradual. The dashed contour lines in Fig. 1 indicate the extent to which data was collected. The addition of 0.27 pct A1 resulted in a decrease in the transverse spread of basal poles. With increasing aluminum content, the amount of the tilt becomes less and the region of highest intensity takes the shape of a ring about the center of the pole figure. For aluminum contents greater than 1 pct, the (0001) [1010] texture is definitely present—the sharpness increasing as the amount of solute is increased.* It is interesting to note that Williams and Eppel-sheimer9 eported for commercial grade titanium a high intensity region 20" toward the rolling direction from the rolling plane normal in addition to. one 30" toward the transverse direction. Their basal pole figure was similar to Fig. 1, row inree. The observation that the texture changes gradually with solute concentration is similar to the results of similar studies on copper." At the present time these effects are not clearly understood. Acknowledgments This work was sponsored by the Aeronautical Research Laboratory (WCRRL), Wright Air Development Center, under Contract NO. AF' 33(038)-19574. The authors are grateful for the aid received and permission to publish these results.

Jan 1, 1958

By Arthur Philips

THE purpose of this paper is to present certain data and observations resulting from a series of experiments dealing with the heat treatment and microstructure of commercial white cast iron and its derivative, malleable iron. In planning the experimental work, particular pains were taken to secure for the tests white cast iron of "normal" composition; i.e., within the composition limits commonly prescribed by manufacturers of malleable castings. A review of the literature leads us to believe that much data of a fragmentary character treating of the graphitization of white cast iron have been of little value, mainly because of the diversity in chemical composition of the materials employed in the tests. Moreover, when feasible, annealing periods at least comparable to those of current practice have been adopted. We wish to acknowledge our indebtedness to the members of the research department of the Eastern Malleable Iron Co. for the white cast iron used in the tests and, particularly, for their active cooperation during the experimental stage of the work. In this paper the following subjects will be discussed in the order indicated: Data on the thermal critical points of white cast iron and malleable iron. Changes produced in tensile properties and microstructure of white cast iron by annealing at different temperatures within the range, 760 to 1100° C. Relation of thickness of wall section of hard iron to microstructure and tensile properties of malleable iron obtained under normal annealing conditions. Notes on mechanics of graphitization of normal white cast iron as observed in specimens quenched after various periods of anneal at approximately 800° C.

Jan 1, 1922

By Zay Jeffries

THE metallic products of today represent the temporary end point of the efforts and interplay of thousands of years of the human struggle for existence, for pleasure, for conquest, for defense, for improvement in the standard of living, and for the satisfaction of that irrepressible urge to discover and utilize the materials and laws of nature Each metal has gained its place in the sun in severe competition with all other materials, be they metallic or nonmetallic Each serves better than any other for certain purposes. The compromise between cost and properties usually determines the selection of a metallic product for a given use. There are exceptions, as in wartime when the availability at a certain place at a certain time may far outweigh the ordinary economic considerations. In many instances superior properties are vastly more important than cost. If this were not so, the metal industry, for practical purposes, would be the iron industry. The use of 38,000,000 metric tons of newly produced nonferrous metal during, the five-year period from 1940 through 1944 is ample evidence that the special properties of these many metals have great economic value. In fact, our extensive industrial advances would have been quite impossible without the great range and variety of properties and combinations of properties of the nonferrous metals. This observation is not made to detract in the slightest way from the dominant role played by iron and steel. During the past century the production of pig iron has constituted well over 90 per

Jan 1, 1947