Search Documents

By W. Lawrence Austin

It has been suggested to me that some data, bearing on the treatment of silver ores in Southern Arizona, would be in accord with the objects of the present meeting. I have, therefore, made a few notes, gathered from practical experience at some of the best known works of that district. Presuming the general arrangement of a silver mill to be familiar to members, the subject having been repeatedly brought to the notice of the Institute, it is my aim in the following description of the modus operandi at the different mills to which I would invite your attention, to give simply such salient points of the apparatus as have a direct bearing upon results, together with the cost of materials, labor, etc. I have gone somewhat deeply into detail in my descriptions of machinery, thinking that possibly some of our members engaged in this branch of the profession might find something of interest among them. In an industry such as silver milling, where the various works are scattered over a vast extent of territory, and the conditions under which results are obtained are subject to the greatest variations, it is essential to go into rather minute details in describing plants, processes, etc., in order to afford a clear idea of the operations. Not only should results be given, but also the means by which such are attained. The milleralogical and chemical constituents of the ore, and its physical properties, throw a flood of light upon the success or failure of a process Figures representing totals I have subdivided as much as possible, so that the cost per ton for labor, castings, chemicals, etc., are apparent. Unless all these Factors are known, no accurate comparison can be drawn, since in this branch of metallurgy, more perhaps than in others, the weakness of any one link in the chain of operations demoralizes the remainder. That it costs $10 to mill in one

Jan 1, 1883

By Sam Harlan

At intervals during the past several years the oil industry has been confronted with the problem of forestalling crises in its affairs. These crises have been reduced to periods of depression which, fortunately, the industry has been able to survive. Under the existing competitive practices which control the producing division of the industry it apparently has been proved that the best efforts logically to curtail development and producing operations are inadequate for effecting a true production balance and the consequent stabilization of prices. The industry is awakening to the fact that the situation warrants revolutionary thought and at this time it is looking for a permanent solution of its problem in a general plan for unit development and operation such as the one first proposed by Henry L. Doherty. Mr. Doherty's proposal was designed not only as a means for stabilizing the industry as a whole, but its principles involve very definite potential benefits for the average individual operator and royalty owner as participants in pooled projects. The benefits to these individuals would be derived from maximum recovery, the maximum utilization of natural energies, the minimization of development and operating costs, enhanced values of leases and royalties through improved efficiencies and ultimate yields, improved earnings through stabilized crude oil prices, etc. This plan was revolutionary to the industry's practices and at the time was rejected, but it now appears that the development and operating policies for new properties are continually approaching the ideal of the original plan. Oil companies are constantly extending their efforts to improve all factors that have a bearing on the costs and efficiencies of their operations. These efforts may, in some degree, be a normal outgrowth of the industry's progress, but the forced consideration of market conditions, the growing appreciation of the importance of regulating operations for maximum ultimate economies and the depreciation of the old principle of maximum flush at any cost, come from a new school of thought which has been stimulated by the immediate pressure of overproduction and

Jan 1, 1930

By P. E. Busby, C. Wells, M. E. Warga

Fundamental data on the rate of diffusion of boron in austenite and solubility of boron in the a and y phases of iron and steel have been obtained from deboronizing experiments and provide partial explanations for some of the phenomena observed in boron steels. The rate of diffusion of boron is about the same as carbon in austenite. The solubility of boron in austenite at normal heat-treating temperatures is less than 0.001 pct. A partial tentative Fe-B phase diagram in the important low boron concentration ranges and an equation representing the diffusion of boron in austenite are presented. A LTHOUGH a search of the literature revealed ALTHOUGHthat boron diffusion had not been studied quantitatively and systematically prior to 1948, a few qualitative observations which were made by following the diffusion of boron into iron packed in ferro-boron1-3 suggest that boron obeys normal diffusion laws and that the rate of diffusion increases with increasing temperature. The claim of Cornelius and Bollenrath1 that boron does not appear to influence the rate of carbon diffusion has recently been substantiated by Wells, Batz, and Mehl.4 Calculations based on data from the paper by Campbell and Fayv indicated that the diffusion coefficient (D) for boron in iron at 900°C is approximately 3x10 sq cm per sec; a value of 2x10-7 sq cm per sec at 1038°C has been reported by Digges et al in connection with decarburizing experiments on a commercial boron steel containing 0.43 pct C. During the period 1948 to 1950 several diffusivity constant (D) values for the diffusion of boron in the y phase of iron and steel and a number of solubility values for boron in both a and y phases were reported. It was concluded tentatively as a result of Metals Research Laboratory studies that D values for boron in y and a phases are about the same as for carbon in the comparable phasesa and that carbon up to 0.4 pct did not affect the rate of diffusion of boron in y iron above 1000°C within the limits of experimental error. Whether saturation of the y or a phases with carbon would significantly affect rates of diffusion of boron through them was then and still remains in doubt. The best estimate of Q (activation energy) was reported to be about 25,000 cal, somewhat lower than that for carbon in y iron. The solubility of boron in y iron at 1000°C was thought to be higher than 0.004 pct B but not as high as a more recent analysis of available data shows it to be. The solubility of boron in a iron at 700°C was reported to be 0.0004 pct B, but it would not have surprised the authors if the true solubility value is actually lower than this. Breaks in diffusion curves which were not understood when first obtained prior to 1950 have now been recognized as indicating solubility limits, and these are included in the present paper. Experimental Procedure Two methods were employed in an effort to determine diffusion coefficients (D) for boron in austenite. Early experiments involved the use of welded couples prepared in accordance with the procedure of Wells and Mehl,' but when the results of these experiments proved to be unsatisfactory for calculating D values, studies were continued by means of deboronizing experiments. In both cases, boron analyses following the diffusion anneal were carried out spectrographically and all D values were computed using the Grube solution of Fick's law. The precision of the spectrographic method used proved to be about equal to that reported by Corliss and Scribner" —average deviation from the mean about 5 pct of the amount present when the boron content is 0.003 pct. Concentration-penetration curves obtained from spectrographic analyses of welded couples generally indicated that practically no boron was transported across the weld interface during the diffusion anneal. Furthermore the concentration-penetration

Jan 1, 1954

By H. M. Otte, A. L. Esquivel

A new leasl-squares method is Presented for determining lattice parameters of hexagonal or tetragonul structures. The method is adapted for use on electronic computers and involves a reiterative procedure. The correction factor employed raries linearly with the lattice parameter, a (determined from the Brag, angle). In contrast, Cohen's method and recent modifications of it use a correction factor that varies incersely as the squure of the lattice paramneter, a. While the recent modifications attempt to improve the precision of the extrapolated lattice parameter, a, (or-cu). by stressing the importance of the weighting factor. the present approach emphasizes the need for choosing the correct extrapolation function. A comparison between the present method (the Linear method) and Cohen's method indicates that the Linear method may be more appropriale in certain cases. through a priori no critertion appears to he available for making a chorce between the methods. The size of hexagonal and tetragonal crystal lattices is determined by two parameters, a, and c,. Although in principle the two lattice parameters can be determined independently from reflections for which h - k = 0 and 1 = 0, respectively, in practice this may be inconvenient (because of the angular positions at which these reflections may occur) or not easily possible (because of low intensity). Furthermore, if a high precision or accuracy is required, the limited number of reflections of this type available, particularly in the high-angle region, is not sufficient for the necessary corrections (mainly due to absorption) to be determined with accuracy. Several methods1-7,11-13 have been proposed employing all reflections, to obtain the optimum values, a. and co, either by a trial and error procedure or a least-squares fit. Of the latter method, cohen's5 is the best known one since it provides explicit expressions for the optimum a. and c,. However, Cohen's method is only strictly valid if an extrapolation function is used that varies linearly with l/a2 or lie2 (see Section 3), a requirement that does not appear to be generally appreciated. On the other hand, all the better known and more widely used A recent trial and error method was proposed by Massalski and King8,7 who computed extensive auxiliary tables of axial ratios vs the functions A = [(4/3)(h2 + hk +k2) + l2+(a/c)2] and C = A(c/a)2 used in computing a and c values from the observed Bragg angles. These values of a and c were then plotted against a function which permitted linear extrapolation. As a criteria; for the "optimum" values, Massalski and King rely upon a visual fitting of the line through points representing reflections of low 1-index points to compute the extrapolated value of ao and high 1-index reflections to obtain CO. The successive computations and graphical plotting required to reach the "optimum" value are quite lengthy and tedious even on a desk calculator and no quantitative assurance is obtained of having in fact selected the optimum value.* If the method of Massalski and King is used on an electronic computer, then their published tables become redundant and a least-squares fit becomes a natural selection for the choice of optimum values. Such an approach will be called the Linear method. For work now in progress on the effect of certain physical variables on the lattice parameters of hexagonal crystals, it has become essential to determine the confidence limits of small changes in the lattice parameters. Since extrapolation functions that varied linearly with a and c actually also appeared to vary linearly with l/a2 or l/c2 when tested against published as well as our data, a comparison of Cohen's method and the Linear method was considered desirable (Sections 3 and 4). For the latter method an electronic computer was required since a reiterative procedure to obtain the optimum ao and co values had to be employed. The purpose of this paper is to describe the principles of the Linear method, illustrate its application, and compare it with Cohen's method. 1) THE LINEAR METHOD The standard practice in obtaining the lattice parameters in the Debye-Scherrer method is to

Jan 1, 1965

By J. A. Berger, R. J. Towner

The pjPocesses of polygonization and subgrain growth were followed in slightly stretched 99.99 pct A1 single crystals heated for cumulative times at 400°, 500°, and 600°C. Changes in sub-grain size and boundary angle were determined from measurements on X-ray micrographs. CAHN1, 2 studied polygonization in stretched and heated aluminum single crystals of 99.99 pct A1 using various techniques, including etch pits, Laue patterns, and a slight restretching of heated specimens to reveal small changes in lattice orientation by the direction of new slip lines. He found that kink bands, which had well-defined boundaries lying in a plane perpendicular to the slip direction (at least in the early stages of deformation), formed during stretching. Also, he noted that bending occurred about the <211> axis lying in the (111) slip plane perpendicular to the <110> slip direction. His studies of polygonization were largely confined to the kink bands rather than to the weakly bent matrix regions between bands. The minimum temperature required to bring about polygonization was established at about 450 "C. Guinier and Tenevin used a focusing Laue X-ray diffraction technique to study polygonization in aluminum single-crystal specimens of 99.99 pct purity. Stretching the crystals 5 pct in tension caused a widening of the focused Laue spots. After heating for 4 hr at 450°C, their method revealed no change in the specimen. Above 450°C polygonization was detected and further annealing near 600°C led to subgrain growth. They concluded that the orientation of the crystal relative to the axis of deformation had no marked effect on polygonization. Gay and Honey-combe4 using an X-ray microbeam technique found that polygonization did not occur in a stretched aluminum crystal heated at 250oC, although some decrease in the yield strength occurred. When the temperature was raised to 475oC, the asterism became broken up as a result of polygonization. Honeycombe5 noted that reflections on X-ray mi-

Jan 1, 1961

By Frederick Laist

THE object of the construction and operation of the 80-ton leaching plant was to test out the leaching of sand tailings on a large scale and, if possible, determine a definite method of operation, and the best construction for the larger unit which is now being built. It was also of importance to obtain some practical data as regards cost items. The 80-ton plant was not expected to be a commercial success. A leaching process on such low-grade material necessitates the treatment of a very large tonnage.. Such a cost item as labor, for instance, is entirely out of proportion in such a small plant. The amounts of acid, salt, scrap iron, and fuel for roasting, however, are the same per ton in an 80-ton plant as in a 2,000-ton plant. These costs were definitely established. Also the percentages of extraction and grade of tailings were definitely determined for a large-sized unit. Following will be found the description of the plant, the method of operation and the results obtained. A -general view of the plant is given in Fig. 1. The bins consisted of one coal bin with a capacity of 30 tons, one salt bin with a capacity of 20 tons, and a "mill tailings" or feed bin which held 70 tons. The coal and salt bins were placed with their floor level even with the firing floor of the roasting furnace. The feed bin, to give it greater capacity, discharged about 12 ft. below this point, to a 12-in. conveyor belt, which, in turn discharged into a pug mill. This fed another conveyor belt, which discharged into the top hearth of the furnace. The furnace was an ordinary six-hearth MacDougall roaster, .20-ft. in diameter. It was equipped with two fire boxes, on opposite sides, the flames entering on the third hearth. An induced draft was obtained with a Buffalo blower, worked as an exhaust fan. Just above the top hearth was an annular flue around the whole circumference of the furnace. Slots at intervals of about 18 in. led from this flue down into the top hearth. The slots were 2 in. wide by 6 in. long. This annular flue proved rather unsatisfactory, as it tended to fill up with flue dust and choke the slots, thus cutting down the draft. The volume of gas through

Jan 8, 1914

By Frederick Laist, Howard Aldrich

The object of the construction and operation of the 80-ton leaching plant was to test out the leaching of sand tailings on a large scale and, if possible, determine a definite method of operation, and the best construction for the larger unit which is now being built. It was also of importance to obtain some practical data as regards cost items. The 80-ton plant was not expected to be a commercial success. A leaching process on such low-grade material necessitates the treatment of a very large tonnage. Such a cost item as labor, for instance, is entirely out of proportion in such a small plant. The amounts of acid, salt, scrap iron, and fuel for roasting, however, are the same per ton in an 80-ton plant as in a 2,000-ton plant. These costs were definitely established. Also the percentages of extraction and grade of tailings were definitely determined for a large-sized unit. Following will be found the description of the plant, the method of operation and the- results obtained. A general view of the plant is given in Fig. 1. The bins consisted of one coal bin with a capacity of 30 tons, one salt bin with a capacity of 20 tons, and a "mill tailings" or feed bin which held 70 tons. The coal and salt bins were placed with their floor level even with the firing floor of the roasting furnace. The feed bin, to give it greater capacity, discharged about 12 ft. below this point, to a 12-in. conveyor belt, which in turn discharged into a pug mill. This fed another conveyor belt, which discharged into the top hearth of the furnace. The furnace was an ordinary six-hearth MacDougall roaster, 20 ft. in diameter. It was equipped with two fire boxes, on opposite sides, the flames entering on the third hearth. An induced draft was obtained with a Buffalo blower, worked as an exhaust fan. Just above the top hearth was an annular flue around the whole circumference of the furnace. Slots at intervals of about 18 in. led from this flue down into the top hearth. The slots were 2 in. wide by 6 in. long. This annular flue proved rather unsatisfactory, as it tended to fill up with flue dust and choke the dots, thus cutting down the draft. The volume of gas through

Jan 1, 1915

By Colin Baker, G. C. Smith

Investigation of the initiation and propagation of ductile failure in OFHC copper was undertaken to determine the role of nonmetallic inclusions. The effect of inclusion initiated voids on the formation of the internal cavity and the final shear separation was studied by metallographic eranzination of strained test pieces. A strain anneal technique was used to enlarge the voids under uniaxial stress conditions to elinzinate triaxial stress effects. Measurements of void size us stress and strain were made to show the point at which void im&apos;tiation begins and becomes an important factor in the deformation process. The work of separation of copper-cuprous oxide was determined to attempt to correlate the breakdown of the matrix inclusion interface with void initiation and propagation. The zloid shape and position relative to the tensile axis suggested an interface breakdown mechanisnz of initiation. Evidence is presented that shows a basic similarity between the central cavity propagation and the 45-deg shear portions of the failure. DUCTILE fracture has been studied by a number of workers1-lo and attention drawn to the importance of hard second phase particles in the initiation of the failure. Holes formed at the matrix-particle interface can elongate by plastic deformation and then subsequently expand sideways to link up and produce a major crack. This is usually observed first in the center of the macroscopically necked region of a test-piece where the hydrostatic stresses are at a maximum. As the crack spreads sideways towards the free surface of the specimen, well defined shear zones develop from the crack tip and the final separation is along a direction at approximately 45 deg to the stress axis. This shear failure may also be associated with voids formed adjacent to second phase particles. In this way a cup and cone type fracture is produced. The stage at which separation takes place between particles and the surrounding matrix has not been clearly identified. In addition, although researchers have dealt with anisotropy of tensile behavior" as a result of material fabrication variables, not much is known about the microstructural features of aniso-tropic behavior. In the present work evidence on these points is presented in relation to the behavior of copper containing second phase particles of cuprous oxide. I. MATERIALS AND PROCEDURES EMPLOYED The material used was +-in. diam or 2-in. sq cold-drawn OFHC copper bar which contained 0.6 pct by volume of cuprous oxide inclusions. These ranged in COLIN BAKER, Junior Member AIME, formerly at -mnF of Metallurgy, University of Cambridge, Cambridge, England, is presently Research Scientist Reynolds Metals Co., Richrnand, Va. G. C. SMITH, Member AIME, is Senior Lecturer, Department of Metallurgy, University of Cambridge. Manuscript submitted June 20, 1967. IMD size from approximately 1 to 6 p in length and 1 to 4 p in width. The shape was generally slightly ovoid. Tensile tests were made on specimens having a gage length of 2.5 cm and diameter of 0.643 cm. Metallographic examination was carried out by sectioning deformed and fractured specimens; in addition fracture surfaces were examined optically and with a scanning electron microscope. Some measurements of the work of separation between copper and cuprous oxide were made, using a sessile drop technique which was a modification of that used by Kingery and umenick." The best metallographic results were obtained by using a vibratory polisher, which minimized smearing of the surface. 11. RESULTS A) Initial Experiments. Specimens from the +-in. diam rod were annealed for 2 hr at 650°C in uacuo, at which temperature complete recrystallization occurred without any change in the form of the inclusion. They were then fractured at temperatures from -190" to 600°C. Cup and cone fractures were obtained at all temperatures from -196" to 400°C. With increase in temperature there was, however, a continuous increase in the extent of the central transverse area and a corresponding decrease in the shear portion of the fracture. Above 400°C, the fractures became intergranular. Sections of specimens tested below 400°C revealed extensive small voids which were always associated with inclusions. However, the voids only reached dimensions greater than the inclusion size in the region of the macroscopic neck, where they were many times longer. Lateral expansion was found only near the fracture surface of the test pieces. As observed by Puttick, the voids were either (a) triangular holes initiated in the direction of the tensile axis and elon-

Jan 1, 1969

Carlisle: Jim Knapp, has been the good friend of hundreds-maybe thousands-of mining men in these western states in the last 40 or 50 years. Jim is going to talk about many of the mining camps of Nevada, where he has done plenty in the mining field during the last 50 years. Jim, for a starter, how did you happen to go to Nevada? Knapp: In the summer of 1902, two years after the discovery at Tonopah, the professor of mining at Stanford sent out myself and another student by the name of Joe Miller to make a report on the camp. We left San Francisco at 8 p.m., got to Reno the next morning, then took the train to Sodaville, arriving about 4:30 in the afternoon. The first man I met when I arrived at the Tonopah station was Tasker Oddie, a gentleman who later became the Govenor of the State and then a United States Senator. Before we got away from the stage station I also met S. H. Brady, the first mining engineer to put out his shingle in Tonopah. He afterwards became general manager of the West End Mining Co.

Jan 3, 1965

By E. R. Parker, E. A. Smith

Metallurgists and engineers have always been interested in the mechanism of high-speed deformation because metals are rapidly deformed in various applica-tions and manufacturing processes. The deformation of metals by impact loads has recently engaged the attention of a number of investigators. Many of their results have not been disclosed but some of the published investigations1-8 have shown that the tensile strength, yield strength and elongation generally increase with increasing strain rate. The investigation reported herein is an attempt to determine the reason for this increase in strength and elongation. found to depend upon the strain rate. In the bars broken at high speeds, the slip bands appear to be more numerous. This might account for the higher strength as well as the greater elongation. Experimental Procedure Single crystals of copper (approximately 99.98 per cent) were made in graphite molds by the conventional method of lowering the mold out of the hot zone of a hydrogen furnace at a rate of one inch per hour. Solidification progressed from the bottom upward, forming a single crystal. The crystals were about 0.30 in. in diameter and 4 in. long. They were

Jan 1, 1944

By E. A. Smith, E. R. Parker

Metallurgists and engineers have always been interested in the mechanism of high-speed deformation because metals are rapidly deformed in various applica-tions and manufacturing processes. The deformation of metals by impact loads has recently engaged the attention of a number of investigators. Many of their results have not been disclosed but some of the published investigations1-8 have shown that the tensile strength, yield strength and elongation generally increase with increasing strain rate. The investigation reported herein is an attempt to determine the reason for this increase in strength and elongation. found to depend upon the strain rate. In the bars broken at high speeds, the slip bands appear to be more numerous. This might account for the higher strength as well as the greater elongation. Experimental Procedure Single crystals of copper (approximately 99.98 per cent) were made in graphite molds by the conventional method of lowering the mold out of the hot zone of a hydrogen furnace at a rate of one inch per hour. Solidification progressed from the bottom upward, forming a single crystal. The crystals were about 0.30 in. in diameter and 4 in. long. They were

Jan 1, 1944

By Wilson T. Lundy

The history of the production of sulfur from salt domes in Louisiana and Texas originated with the operations of the Union Sulphur CO. at Sulphur, La., followed by the Freeport Sulphur Co. at Bryanmound, Tex. Including the present development of Grande Ecaille by the Free-port Sulphur Co., which constitutes the tenth dome to be equipped for the production of sulfur in the Gulf Coast, less than 10 per cent of all the known domes have proved to contain sulfur in commercial quantities. The Grande Ecaille salt dome is in the tidal marsh of the Mississippi River delta in Plaquemines Parish, Louisiana. It is 10 miles southwest of the right descending bank of the river approximately 45 miles below the city of New Orleans and is within 4 miles of the shore line of the Gulf of Mexico. Terrain Characteristic of the delta region, the terrain consists of a low, flat, uninhabited area of marsh land intersected by many shallow lakes and bayous. With the exception of salt grasses, the region is devoid of vegetation and presents, in all directions, an unobstructed path to the vagaries of the winds. The general character of this area can be best visualized from the mechanism of its formation.&apos; Offshore bars formed enclosing long narrow lagoons between the bar and the inner shore line, the lagoons communicating with the sea by means of tidal inlets. The water in the lagoons, being comparatively quiet, favored the deposition of fine debris composed of sand carried into the lagoons by action of the waves, tides and river-borne sediments from the land surface. As this material accumulated the bottoms of the lagoons were built up and eventually salt grasses obtained a foothold. The successions of growth and decay of these grasses formed a brown fibrous mat varying in depth from a few inches to several feet. This mat of vegetation virtually floats on an ooze that is several feet thick and is composed of alluvial sediments and very fine sand, and the whole is underlain by an unctuous clay. The decayed vegetation from the upper layer when dried has a peaty appearance.

Jan 1, 1934

By D. E. Thomas, C. E. Birchenall

ALTHOUGH Eoltzmann gave a mathematical solution for the diffusion equation (for planar diffusion in infinite 01. semi-infinite systems only) in 1894 allowing for variation of the diffusion coefficient with a change in concentration, it was not until 1933 that this solution was applied to an experimentally investigated metallic system. The calculation was carried out by Matano&apos; on the data obtained by Grube and Jedele3 for the Cu-Ni system. Since that time concentration dependence of the diffusion coefficient has been demonstrated for many pairs of metals. However, the nature of this dependence has never been fully elucidated. Many investigators have suspected that these variations could be related to the thermodynamic properties of the solutions, one of the earliest explicit statements being contained in a discussion of irreversible transport processes by Onsager&apos; in 1931. Development along these lines has been greatly retarded by the lack of reliable data on the variation of tliffusivity with concentration, the paucity of the thermodynamic data for the same systems at the same temperatures and compositions, and an incomplete understanding of the relation of the thermodynamic properties of the activated state for diffusion to the bulk thermodynamic properties. The last factor has been discussed by Fisher, Hollomon, and Turnbull.5 In many instances where data exist, it is difficult to know which are acceptable. This problem probably applies more strongly to diffusion data than to activity measurements. For instance, four sets of observers"-" have reported self-diffusion coefficients for copper. The average spread between extreme results is a factor of about four, though the individual sets of data are self-consistent to about 20 pct. Thus one or more factors are out of control, at least in these experiments, making estimates of internal error unreliable. The most reliable diffusion data in most systems have resulted from the use of welded couples with a plane interface from which layers for analysis are machined parallel to the interface after diffusion. The layers are analyzed, and the result is a graphical relation between distance and concentration, usually called the penetration curve. Given the same set of analytical data and distances and following the same procedure in computation, different observers will generally produce diffusion coefficients which vary appreciably, especially at the extremes of the concentration range. Experiments must be carefully designed so that the precision is good enough to answer a particular question unequivocally. In the first calculation of the dependence of the diffusion coefficient on concentration in the metallic solid solution Cu-Ni, Matano found that the coefficient was insensitive to concentration from 0 to 70 pct Cu, after which it rose more and more steeply to some undetermined value as pure copper was approached.&apos; The same behavior was reported for Au-Ni, Au-Pd, and Au-Pt.* The data used were those of Grube and Jedele which were very good at the time, but are not considered particularly good by present standards. Furthermore, the method of calculation makes the ends of the diffusion coefficient-concentration curve unreliable. For better reliability, the high copper end of the curve has been checked by incremental couples, where the concentration spread is 67.7 to 100 atomic pct Cu. The implication of the curves calculated by Matano was that diffusion is very concentration sensitive in one dilute range of this completely isomorphous system and hardly at all in the other. Matano&apos;s result is confirmed. Later Wells and Mehll0 published data on diffusion in Fe-Ni at 1300°C, which represent a thorough test of the shape of the concentration dependence curve. They ran couples with the following ranges of nickel concentration: 0-25 pct, 1.9-20.1 pct, 0-20.1 pct, 20.1-41.8 pct, 0-99.4 pct, and 79.3-99.4 pct. Although the trend of the data indicates an S-shaped concentration dependence, their curve was drawn to the pattern set by Matano. Their original data have been recalculated for the 0-99.4 and 79.3-99.4 pct couples. Wells and Mehl&apos;s points and two independent recalculations from the raw data are plotted in Fig. 1. What appears to be the best curve is drawn through them. This curve shows little sensitivity to composition in both dilute ranges with a strong dependence at intermediate composi-tions.? Similar experiments on the Cu-Pd system are reported here at temperatures where solubility is unlimited. These lead to the same type of concentration dependence for the diffusion coefficients as was found upon recalculation of the data for the Fe-Ni system. Experimental Procedure Cu-Pd: The concentration dependence of the diffusion coefficient may be determined by the use of

Jan 1, 1953

By William R. Chedsey

IN the last two years the E.C.P.D. committees having to do with the inspection of engineering schools for possible accrediting have been concerned with the engineering content of some of the mineral industries courses. Originally the discussion arose with regard to engineering geology, or geological engineering, afterward broadening to metallurgical engineering, ceramic engineering, agricultural engineering, and other branches not pertinent to this discussion. Some members of visiting committees took the attitude that they probably would have to accredit these types of training as included in the engineering group if they met the average standard set by the mining schools, though they questioned -whether they were really engineering.

Jan 1, 1939

By Rollyn P. Jacobson

THE town of Pacific, in Jefferson County, Mo., is 127 miles west of St. Louis. Since the area lies entirely on the flood plain of a cutoff meander of the Meramac River, it was considered a likely environment for accumulation of commercial quantities of sand and gravel. Excellent transportation facilities are afforded by two major railways to St. Louis, and ample water supply for washing and separation is assured by the proximity of the river. As a large washing and separation plant was planned, the property was evaluated in detail to justify the high initial expenditure. An intensive testing program using both geophysical and drilling methods was designed and carried out. The prospect was surveyed topographically and a 200-ft grid staked on which electrical resistivity depth profiles were observed at 130 points. The Wenner 4-electrode configuration and earth resistivity apparatus" were used. In all but a few cases, the electrode spacing, A, was increased in increments of 11/2 ft to a spread of 30 ft and in increments of 3 ft thereafter. Initial drilling was done with a rig designated as the California Earth Boring Machine, which uses a bucket-shaped bit and produces a hole 3 ft in diam. Because of excessive water conditions and lack of consolidation in the gravel there was considerable loss of hole with this type of equipment. A standard churn drill was employed, therefore, to penetrate to bedrock. Eighteen bucket-drill holes and eight churn-drill holes were drilled at widely scattered locations on the grill. The depth to bedrock and the configuration will not be discussed, as this parameter is not the primary concern. Thickness of overburden overlying the gravel beds or lenses became the important economic criterion of the prospect.** The wide variety and gradational character of the geologic conditions prevailing in this area are illustrated by sample sections on Fig. 2. Depth profiles at stations E-3 and J-7 are very similar in shape and numerical range, but as shown by drilling, they are measures of very different geologic sequences. At 5-7 the gravel is overlain by 15 ft of overburden, but at E-3 bedrock is overlain by about 5 ft of soil and mantle. Stations L-8 and H-18 are representative of areas where gravel lies within 10 ft of surface. In most profiles of this type it was very difficult to locate the resistivity breaks denoting the overburden-gravel interface. In a number of cases, as shown by stations M-4 and H-18, the anomaly produced by the water table or the moisture line often obscured the anomaly due to gravel or was mistaken for it. In any case, the precise determination of depth to gravel was prevented by the gradual transition from sand to sandy gravel to gravel. In spite of these difficulties, errors involved in the interpretation were not greatly out of order. However, results indicated that the prospect was very nearly marginal from an economic point of view, and to justify expenditures for plant facilities a more precise evaluation was undertaken. The most favorable sections of the property were tested with hand augers. The original grid was followed. In all, 46 hand auger holes were drilled to gravel or refusal and the results made available to the writer for further analysis and interpretation. When data for this survey was studied, it immediately became apparent that a very definite correlation existed between the numerical value of the apparent resistivity at some constant depth and the thickness of the overburden. Such a correlation is seldom regarded in interpretation in more than a very qualitative way, except in the various theoretical methods developed by Hummel, Tagg (Ref. 1, pp. 136-139), Roman (Ref. 2, pp. 6-12), Rosenzweig (Ref. 3, pp. 408-417), and Wilcox (Ref. 4, pp. 36-46). Various statistical procedures were used to place this relationship on a quantitative basis. The large amount of drilling information available made such an approach feasible. The thickness of overburden was plotted against the apparent resistivity at a constant depth less than the depth of bedrock for the 65 stations where drilling information was available. A curve of best fit was drawn through these points and the equation of the curve determined. For this relationship the curve was found to be of the form p = b D where p is the apparent resistivity, D the thickness of overburden, and b a constant. The equation is of the power type and plots as a straight line on log-log paper. The statistical validity of this equation was analyzed by computation of a parameter called Pearson&apos;s correlation coefficient for several different depths of measurements, see Ref. 5, pp. 196-241. In all but those measurements taken at relatively shallow depths, the correlation as given by this general equation was found to have a high order of validity on the basis of statistical theory.

Jan 1, 1956

By J. F. Held

In a study of the influence of cold rolling on mechani cal properties of steel, it was found that the specific rolling procedure influenced crystallographic orientation. Properties developed by several rolling modes were determined and related to crystallographic orientation. Sanzples were cold-rolled various amounts on a laboratory mill. When palm oil was used as a lubricant, the crystallographic orientation was homogeneous throughout the thickness of the samples. Other samples were rolled without lubrication. Variations in intensity of the recrystallization texture components persisted throughout more than 50 pct of the volume of these samples. When the average plastic strain ratio, which is dependent upon crystallogvaphic orientation, was plotted as a function of percent reduction, a maximum was found at 40 pct in the samples which contained the observed texture variation. No maximum was found for the samples with the homogeneous texture distribution. Other mechanical properties, such as tensile strength and yield strength, were not influenced by the variation in crystallopaphic orientation. MECHANICAL properties of steel sheets depend, in general, upon the structural properties of the steel. For example, the Petch equation describes the relationship between yield strength and grain size. Other properties, such as hardness, vary with chemical composition. The plastic strain ratio, or R value, has been found to be dependent upon crystallographic orientation . In the course of investigating the effect of cold rolling on mechanical properties, it was found that a previously reported relationship between percent cold reduction and R value was not always observed. Published data had shown that the optimum cold reduction for best R values is 70 pct for aluminum killed steel.&apos; However, by altering the rolling conditions, the optimum reduction can be shifted to much lower values, or it can be moved to very high values. This paper describes the rolling conditions that lead to shifting of the optimum cold reduction. The effect of rolling conditions on the various structure parameters and the resulting mechanical properties are evaluated. EXPERIMENTAL PROCEDURE Samples of three low-carbon aluminum killed steels were cold-rolled various amounts on a 9-in.-diam 2-high laboratory mill. Hot-mill thermal practice and steel chemistries are listed in Table I. Steel A was rolled with palm oil lubrication and heavy reductions on each pass; i.e., a total reduction of 75 pct was ac- complished with a maximum of five passes. Steel B was rolled without lubrication, and light reductions were given on each pass. After approximately 75 pct reduction, it was necessary to use a small amount of light oil to achieve any additional reduction in thickness. Following cold reduction, the samples were box-annealed at 1300°F for 10 hr. The heating rate between 800" and 1300°F was 50°F per hr, and the cooling rate following the soak period was 50°F per hr. Tensile specimens were machined from the annealed material and these were used to measure yield strength, tensile strength, and the plastic strain ratio (R value). Recrystallization textures were determined by an inverse pole figure technique.*&apos;3 Integrated intensities of the (110), (002), (112), and (222) reflections were recorded for those planes lying parallel to the sheet surface. Examinations were made on both surfaces of each sample, and also at various levels beneath each surface to approximately 0.010 in. depth by etching techniques. RESULTS R Values. The R values obtained in steels A and B are shown as a function of percent cold reduction in Fig. 1. No optimum cold reduction was observed in steel A, rolled with palm oil lubrication. It is likely, however, that an optimum reduction would have occurred had higher reductions than 88 pct been employed. The optimum reduction in steel B occurred at 40 pct. The behavior in both of these steels is quite

Jan 1, 1968

By R. A. Graham, R. W. Rohde

The effect of hydrostatic pressure upon the austenite start temperature of a commercial Fe-28.4 at. pct Ni-0.5 at. pct C alloy has been determined. For pressures to 20 kbar, the austenite start temperature decreased from its atmospheric pressure value of 380°C at the rate of about 4°C per kbar. These data are analyzed by two different thermodynamic approaches; first, considering the transformation as an isothermal process, and second, considering the transformation as an isentropic process. It was found that both these approaches fit the experimental data equally well. The effect of hydrostatic pressure upon the austenite start temperature is best described by considering the mechanical work done during the transformation as that work obtained by multiplying the applied pressure with the gross volume change of the transformation. It is widely recognized1 that strain has an important effect on the initiation of martensitic transformations.* For example, the martensite start tempera- *In this paper, use of the term martensitic transformation implies the reversal of martensite to austenite as wen as the formation of martensite from austenite. ture, M,, may be increased by plastic deformation. Similarly, plastic deformation is observed to lower the austenite start temperature, A,. The effect of uniaxial stress on the M, of iron-nickel alloys has been studied by Kulin, Cohen, and Averbach.2 They found that the martensite start temperature was significantly changed by stresses well within the elastic region. Moreover, the effect of tensile and compres-sive stresses differed. These effects were explained in terms of the interaction of the applied stress with both the dilational and shear components of the transformation strain. The magnitudes of the influence of uniaxial tension, compression and hydrostatic pressure on Ms were measured in 30 pct Ni 70 pct Fe by Pate1 and Cohen.3 Their thermodynamic calculations and similar calculations by Fisher and Turnbull4 predicted the experimental results when the transformation was assumed to occur isothermally at some fixed driving force. This driving force was assumed to be supplied by a combination of the chemical free energy difference between the austenitic and martensitic phases and the work performed during transformation by the applied stress. More recently, Russell and winchel15 reported the effect of rapidly applied shear stress on the reversal of martensite to austenite in iron-nickel-carbon alloys. They performed a thermodynamic analysis of this transformation based upon the assumption that the re- versal occurred adiabatically. They concluded that the applied shear stress did not significantly interact with the transformation strain and thus did not assist in inducing the reversal. Rather they concluded that the reversal was effected by localized strain heating which resulted from the gross local shear deformation of the experiment. In either the adiabatic or isothermal analysis it is necessary to compute the work performed by the interaction of the applied stress and the transformation strains. In the case of hydrostatic pressure this interaction has been treated by two different methods. In either case the applied pressure is assumed to remain constant during the transformation. In one treatment the applied pressure is assumed to interact directly with the dilatational strain associated with the formation of an individual martensite plate.3&apos;4 This local strain has been measured at atmospheric pressure in iron-nickel alloys by Machlin and Cohen.6 In the above treatment this local strain is assumed invariant with temperature and pressure changes. In the other treatment the applied pressure is assumed to interact with the gross volume change of the transformation.7,8 The usefulness of this latter treatment has been demonstrated by Kaufman, Leyenaar, and Harvey7 who calculated the effects of pressure upon the martensite and austenite start temperatures of Fe-10 at. pct Ni and Fe-25 at. pct Ni alloys. Excellent agreement was obtained between their calculations and their experimental data on an Fe-9.5 at. pct Ni alloy. However, this treatment suffers from the fact that the data required to calculate the volume change of the transformation (i.e., the initial specific volumes, the thermal expansion and compressibility data for both the austenitic and martensitic phases) is, in general, not available for any material except pure iron. Thus the calculations of Kaufman et al.7 were necessarily performed by assuming that the volume change of the martensitic transformation in the iron-nickel alloys was that same volume change occurring during the a-? transformation in pure iron. While this approximation may suffice for very dilute alloys it is likely to be inaccurate in high nickel alloys. We have performed measurements of the effect of hydrostatic pressure to 20 kbar on the A, temperature of an Fe-28.4 at. pct Ni-0.5 at. pct C alloy. The composition is similar to the alloy used by Pate1 and Cohen3 to determine the effect of pressure upon the M, temperature. The present measurements permit calculation of the interaction between the applied pressure and the transformation strain. Additionally, measurements have been made which allow precise determination of the gross volume change of the transformation. The data allow direct comparison between the alternate hypotheses of the interaction between the applied pressure and a dilatational transformation strain characterized by either the formation

Jan 1, 1970

Meeting of Nov. 20, 1914.-Charles F. Rand was unanimously elected as the representative of the Institute on the John Fritz Medal Board of Award. E. Gybbon. Spilsbury was unanimously elected to succeed himself in January, 1915, on the Library Board of the United Engineering Society. . The President appointed Messrs. Walter Douglas, Charles E. Mills, and L. D. Ricketts as delegates to the seventeenth National Convention of the American Mining Congress, Phoenix, Ariz., Dec. 7 to 11, 1914. It was voted that the sum of $857.61, or so much of it as may be necessary, be advanced to the Land Fund from the general funds of the Institute, in anticipation of the collection of unpaid installments of subscriptions to the Land Fund; and that the Treasurer be instructed to pay to Andrew Carnegie at the present. time the sum of $2,500 on account of the Land Fund indebtedness.

Jan 1, 1915

(Members are urged to send in for this column any notes of interest concerning themselves or their fellow-members.) Members and guests who called at Institute headquarters during the period Mar. 10, 1916 to Apr. 10, 1916: R. C. Blanchard, London, England. George H. Packard, Boston, Mass. F. Lynwood Garrison, Philadelphia, Pa. Harvey B. Small, Mangangue, Colombia, S. A. S. A. Horton, Altoona, Pa. H. De Witt Smith, Kennecott, Alaska. J. S. Lane, New York City. Richard Tarantous, Terlingua, Tex. Harry T. Mercer, Painesdale, Mich. S. A. Taylor, Pittsburgh, Pa. A. L. Blomfield, for many years in the employ of Bewick, Moreing & Co. as metallurgist, and for the last eight years mill superintendent of the Golden Cycle mill at Colorado Springs, has become associated with The Dorr. Company as consulting metallurgical engineer, with headquarters at Denver. He retains his connection with the Golden Cycle mill as general superintendent.

Jan 5, 1916

By Edwin A. Sperry

In 1892 I tested an ore, which was peculiarly difficult to treat, on several concentrators then in general use, including t,he Frue-vanner, the Luhrig table and the Cornish buddle. Owing to the character of the ore it had to be crushed- to a very fine state of division, and the results obtained were far from satisfactory; a large proportion of the values was lost in the slimes, which indicated the necessity of a very careful sizing before dressing. Even after reworking some of the slime-tailings, the results, in my opinion, were not as good aa those which might be obtained on a table designed more especially for the handling of slime. Although the subject of slime-concentration has occupied the attention of many engineers who have threshed the field quite thoroughly, the results obtained in my work led to a careful

Jan 1, 1904