By L. A. Geoffrion, R. H. Perkins, J. C. Biery

Densities of cerium metal and several lour-melting binary cerium alloys were measured over the range 25° to 800°C. A rolumeter, using NaK as working fluid, was used to obtain the data. The cerium, Ce-Co, Ce-Ni, and Ce-Cu alloys all exhibited an increase in density on melting, while a Ce-Mn alloy expanded on melting. FOR the proper design of a nuclear reactor, the change in density of the fuel with temperature must be known. This is especially important in a system utilizing molten fuel, such as LAMPRE (Los Alamos Molten Plutonium Reactor Experiment), since a relatively large change in density usually occurs during the solid-liquid transition. The fuel for LAMPRE is a Pu-2.5 wt pct Fe alloy with a melting temperature of 410°C. However, limitations in reactor design with this fuel have led to consideration of other plutonium-containing alloys for use in future generations of this type of reactor. Several ternary alloys containing plutonium and cerium as two components have satisfactorily low melting points. The system that at the present time appears to be most acceptable is Pu-Ce-Co; it exhibits little change in melting temperature with wide variation in plutonium concentration. Other alloys that have received some consideration contain nickel, copper, and manganese as the third constituent. The proposed fuel alloys are difficult to handle experimentally in the 25" to 800°C temperature range since they oxidize readily, react with many solvents, and contain a poisonous fissionable material. In addition, in this temperature range the alloys pass through the solid-liquid transition. Several techniques are available for measuring the densities and volume coefficients of expansion of solids or liquids. However, the only apparatus that appears suitable for measuring expansion coefficients over this temperature range and through the phase transition is a volumeter. In a volumeter, the indicating medium must be essentially inert to and insoluble in the material being studied. It must also possess a low vapor pressure over the operating temperature range, and its coefficient of expansion must be accurately known. One material that is satisfactory in nearly all of these respects is the alloy Na-78 wt pct K, which melts at -10°C and has a vapor pressure of 860 mm Hg at 800°C. This relatively high vapor pressure at 800°C requires an overpressure of an inert gas to prevent boiling. While a volumeter is capable of determining accurately the volume coefficients of expansion of materials, it cannot be used for absolute density measurements. Therefore, a density determination at a known temperature must be coupled with the volumeter measurements to give all the desired data. The weight-loss technique using immersion in bromobenzene at room temperature proved to be satisfactory. The preliminary work that was done on this experimental program involved developing and calibrating the equipment, and measuring the densities and volume coefficients of expansion of cerium and some low-melting binary cerium alloys. The complications that are caused with the introduction of plutonium into the system were avoided until the equipment was proved to be satisfactory and until experience was gained in its operation. It is this first phase of the experimental work that is described in this report. DESCRIPTION OF EQUIPMENT AND OPERATING PROCEDURE The NaK volumeter is shown schematically in Fig. 1. Basically, the equipment consists of two weld-sealed stainless-steel containers of nearly identical volume. One container holds a tantalum crucible and the specimen being measured; the other contains a tantalum crucible and a tantalum specimen used as a control reference material. To avoid temperature gradients, the bombs are located in a copper block inside the furnace. Stainless-steel capillaries of equal length and volume connect each stainless-steel container to a glass viewing capillary. The stainless-steel containers, stainless-steel capillaries, and a portion of the glass capillaries are filled with NaK (22 wt pct Na-78 wt pct K). The NaK/gas interface in the glass capillary is viewed with a cathetometer which is accurate to *0.5 mm. The cathetometer readings are used to calculate the volume changes of the samples during a run. This volumeter is basically the same as that described by F. Knight in Plutonium 1960. 2 However, changes in equipment design and operating procedure were made to eliminate some major operating difficulties. These changes are summarized below. 1) In filling the manometer with NaK, gas was frequently entrained in the system. Evacuation of the system before filling failed to eliminate the en-

Jan 1, 1965

By J. E. Hanafee, G. J. London

MANY studies of the deformation behavior of materials under a superimposed hydrostatic pressure have shown that materials brittle at ambient pressure behave in a ductile manner under pressure. Thus, with a metal such as beryllium which possesses relatively low ductility, but otherwise exhibits quite useful physical and mechanical properties, hydrostatic pressure may be particularly useful for both forming beryllium shapes and studying its deformation behavior. In fact, it has been found1"4 that polycrystal-line beryllium in both ingot and powder form appears to behave in a more ductile manner on a macroscopic level in a hydrostatic pressure environment, and it has been suggested2 that this is due to activating a new slip mode. Furthermore, Andrews and Radcliffe5 have found pressure induced nonbasal dislocation activity in hot pressed beryllium. Recently6 it has been shown in "c-axis" compression tests under hydro-static pressures up to 28 kbars that the shear stress needed to cause slip with a Burgers vector out of the basal plane (pyramidal slip) does not change with increasing pressure in beryllium with a purity of some 99.5 pct. This material is equivalent or more pure than the beryllium used in the previous pressure studies. Thus, it appears, as suggested by Inoue et al.,3 that the hydrostatic pressure affects the fracture stress rather than the stress necessary to activate pyramidal slip in beryllium. However, in "c-axis" pressure tests on high purity 12 zone pass beryllium (˜50 ppm total impurities) the macroscopic compression stress needed to cause pyramidal slip was considerably lower than that at ambient pressure.6 It has further been shown that alloying beryllium with nickel and copper in the range 2-5 wt pct also favors the occurrence of pyramidal slip in "c-axis" compression tests,7'8 while lower amounts of nickel and copper do not have significant effects. In the present study the combined effect of hydrostatic pressure and alloying high purity beryllium on the shear stress needed to cause pyramidal slip has been ascertained. A 2.5 wt pct Cu alloy was selected as the first alloy to study as this level of copper did favor pyramidal slip at room pressure. A high purity (12 zone pass) single crystal of beryllium 0.3 by 0.1 by 0.1 in. was cut and polished by an orientation and lapping technique8 so that the top and bottom compression surfaces were parallel and within 3 min of arc to the (0001) plane and the sides parallel to the {l010} and {ll20} planes. In these compression specimens, therefore, the resolved shear stress was nearly zero on both the basal and prism planes, and slip was restricted to pyramidal systems. Analysis of slip traces on the two lateral surfaces served to accurately identify the active slip planes.6'9 The pressure unit was a modified piston-cylinder device fitted with a manganin transducer coil arrangement which continuously monitored and recorded the hydro-static pressure. The load on the specimen was measured by a strain gage load cell which operated entirely within the pressure chamber. This load cell was calibrated before and after each pressure cycle at room pressure in situ and the calibration did not vary more than ±1 pet. These techniques and devices have been previously described in more detail.6 Successively higher compressive stresses were applied to the single crystal under a superimposed hydrostatic pressure until fracture occurred. The strain rate was (4.5 ± 2.0) x 10-6 sec-1 and the average rate of pressure application and release was approximately 0.3 kbars per min. As the load on the specimen was applied by the piston which was used to increase the hydrostatic pressure, the pressure increased during the compression test. This increase ranged from 0.0 to 0.8 kbars, and the maximum hydrostatic pressures are quoted in Fig. 1. The lateral surfaces of the specimen were examined in a light microscope after each pressurization/stress cycle so that the stress at the onset of {1122} pyramidal slip could be ascertained. Post compression height measurements allowed the plastic strain in the specimen to be evaluated to within 0.03 pct. The resulting compression stress-plastic strain curve is shown in Fig. 1 with results of a "c-axis" test on a similar Be-2.5 wt pct Cu single

Jan 1, 1970

By S. S. Marsden, S. A. Khan

Externally generated foam was injected continuously into short porous media. Both flow rate and pressure drop were measured. Liquid saturation was determined by electrical conductivity. Foam yuality I, expressed as the ratio of gas volume to total volume, was varied from 0.70 to 0.96. As measured with a modified fann VG Meter, apparent viscosity of this foam µa decreases with increasing shear rate but usually falls within the range of 50 to 500 cp. At a given shear rate, µa increases almost linearly with I-. When measured with a Bendix Ultraviscoson, kinematic pa is independent of V but absolute pa increases with T from about 3 to 8 cp. The effective permeability -apparent viscosity ratio ke/µa decreases almost linearly with V for porous media of high permeability, but the rate of decrease becomes less for tighter ones. The relative permeability-apparent viscosity ratio kr/µa us V data does not fall on a single line. The kr/µa ratio increases with liquid saturation in the porous medium and with surfactant concentration. Estimates of pa for foam in porous media vary from 30 to 100 cp. INTRODUCTION Although research on the development of a foam-drive, oil recovery process has been going on for almost a decade, most of the significant publications have appeared within the last several years. This illustrates well the rate at which interest in this process is accelerating. Bond and Holbrook 1 were the first to describe the use of foam to improve oil recovery in their patent of 1958. They proposed that an aqueous foaming agent slug be injected into the formation and that this be followed by gas to produce a foam in situ. Fried 2 studied the injection of foam into porous media which had already been subjected to conventional gas or water drives and found that gas could be used to drive a foam bank which would, in turn, displace additional oil in the form of an oil bank. He attributed the increased oil recovery to the high effective viscosity of foam flowing in porous media. His microscopic observations showed the importance of foam generation and regeneration within the porous medium. By injecting both air and aqueous surfactant solution, Bernard3 generated foams within the porous medium in which oil displacement was being studied. In a separate empirical test, he also measured the dynamic foaming characteristics of the same surfactants in water and/or oil. With some exceptions and for the seyen surfactants studied, there seems to be a qualitative relationship between the efficiency of liquid rlisplacrment and the dynamic foaming testtsed. This relationship was not consistent enough to eliminate the necessity of actual foam flood tests in porous media for surfactant selection. In a study basic to gas storage in aquifers, Bennett4 described the displacement of brine by foam in consolidated porous media. Among other things, he stated that the ability of a surfactant solution to foam is more important than the stability of its foam. The presence of a foam bank between the displacing air and the displaced brine improved both breakthrough and ultimate recovery. In a continuation of this work Kolb5 attributed the great reduction in surfactant solution production rate as displacement by air progressed to a decrease in relative permeability to gas. These several effects reported by both Bennett and Kolb can all be attributed to the high apparent viscosity of foam which was obviously flowing in the porous media. Bernard and Holm6 observed that gas permeability in the presence of foam was much less than in the absence of foam when both were measured at the same gas saturations. This reduction in permeability was proportionately greater for more permeable sands and sandstones than for the less permeable. Viscosities of the surfactant solution and air were used for their calculations rather than apparent foam viscosities. The foam stability increased with decreasing permeability, which was probably due to the natural regenerative properties of porous media, and the permeability reduction increased

Jan 1, 1967

By C. E. Ells, A. Sawatzky

The effect of neutron irradiation on tensile properties of the Zr-2.5 wt pet Nb-0.5 wt pet Cu alloy has been evaluated for integrated neutron fluxes up to 3 x 1020 n per sq cm (E > 1 Mev). Specimen temperature during irradiation was normally 300°C. The material was studied both in annealed and in quenched and aged conditions. When the alloy (fab-ricatedfrom sponge zirconium) is quenched from a temperature =40°C below the a + ß/ß transformation and aged 6 hr at 535oC, neutron irradiation up to the maximum studied has little effect 071 reduction in area, although there is a drop in uniform elongation and the yield strength is increased by = 25 pct. Conversely, irradiation of the alloy in an annealed condition can result in much greater changes in properties, with yield-strength increases of up to 200 pet. The dose dependence of irradiation hardening obeys the saturation equntion proposed by Makin and Minter to explain hardening in copper and nickel: Act = C[1 - exp(-Døt)/1/2 A rnodel is proposed to explain the effect of niobium content and metallurgical condition on irradiatiotz behavior. THE Zr-Nb alloys form a class of material susceptible to marked strengthening by quench and age heat treatment. With niobium concentrations as low as 2.5 wt pet, strengths can be developed which are double those of annealed zircaloy-2.1 Since the neutron-capture cross section of the Zr-2.5 wt pet Nb alloy is nearly identical to that of Zircaloy-2, significant gains in power-reactor neutron economy could be obtained by replacing stressed in-reactor components of Zircaloy-2 with the heat-treated Zr-Nb alloy. When the solution heat-treatment temperature is in the high (a + ß) phase, then the tensile properties of the quenched (and aged at 500°C) material have been shown to be relatively insensitive to neutron irradiation.1-3 Addition of small quantities of copper to the binary Zr-2.5 wt pet Nb alloy gives a useful reduction to the corrosion rate in air and carbon di- oxide,&apos; and a ternary alloy of composition Zr-2.5 wt pet Nb-0.5 wt pet Cu was chosen for one component in the Douglas Point Reactor. This application utilizes both the corrosion resistance to a moist air-carbon dioxide environment and the strength developed by a quench and age heat treatment. By suitable choice of solution heat treatment and aging temperatures, tensile properties of the ternary alloy can be made nearly identical to those considered as optimum for the binary alloy. One effect of the copper addition, however, is to give marked changes in the aging kinetics of the alloy.&apos; For this reason, it appeared that neutron irradiation might promote overaging in the ternary alloy, particularly at the elevated service temperature (=300°C). This paper describes the effect of neutron irradiation on the tensile behavior of the Zr-2.5 wt pet Nb-0.5 wt pet Cu alloy in several metallurgical conditions pertinent to its use as a reactor material. The metallurgical conditions included those for which aging occurs in the unirradiated material, and fully annealed conditions for which a higher degree of thermal stability could be expected. 1) EXPERIMENTAL Two batches of alloy were used, both made from sponge zirconium. The fabricator&apos;s analysis of principle constituents showed no significant difference between the two batches, Table I. The rod material was rolled to 1.5 in. diam, and then swaged to final sizes of 0.5 to 0.375 in. diam at nominal temperatures of 785" and 625°C for the AM and AS batches, respectively. Subsequent hydrogen analyses at CRNL confirmed that the hydrogen concentration of the as-received rod was indeed <20 ppm. However, it was found that the (a + ß)/ß transus for the AM material was approximately 25°C lower than that of the AS material, indicating rather more difference in oxygen concentration than given in Table I. Except for a small difference in yield-point behavior, the tensile prop-

Jan 1, 1965

By Rudolph G. Wuerker

THE scarcity of values of tensile strength of rocks has been explained by the lack of successful testing procedures. In the case of mine rock a description is given&apos; of the difficulties encountered in testing a cylindrical specimen, such as a core, by conventional methods. Over a period of years the following method has given definite and reproducible results with the weakest as well as with the strongest rocks. It does not completely supersede the use of cores with special fixtures but is a supplement in all cases where cores cannot be obtained, as from soft rocks, or in cases where it is less expensive to prepare test specimens by cutting them out of the rock instead of drilling cores. Principle and equipment are the same as for the test for tensile strength of hydraulic-cement mortar.&apos; The test specimen, Fig. 1, has the shape of a briquet. While in the original cement mortar test the briquet is cast in a special mold, it is prepared from rocks in different ways, depending on how easily they can be cut and shaped. Soft rocks, which cannot be core-drilled with a carboloy or diamond bit, are simply hand-cut. Only two dimensions need be watched. The first is the 1-in. diam at the narrowest cross-section of the briquet. The other critical measure is the radius of curvature of the waistline, as the roller supports in the grips have a fixed distance. This radius is ground out of the solid by means of a carborundum grinding wheel having a 3/4-in. radius. Medium hard rocks can be core-drilled with a carboloy bit. The resulting core can be used for nondestructive sonic testing first, and after that for any destructive test. By using an EX-bit and by carefully placing the coreholes, preferably by using a tenplate such as shown in Fig. 1, it is possible to obtain from the rock a punched sample from which numerous tensile briquets can be made. The outside radius of the EX-bit differs from the radius of curvature of the briquet by 1/8 in., but this still permits placing and aligning the specimen in the grips. In the case of bedded rocks the core might have bedding planes normal to the plane of the briquets, and rocks can be tested in any arrangement of the bedding planes desired. Hard rocks, limestones, igneous, and metamor-whic rocks can only be diamond-drilled or diamond-cut. Here the method of getting the tension briquets by accurate placing of EX-drill holes is especially economical. The tops of the briquets made from hard rocks cannot be rounded; they are straight cuts made with a diamond cut-off saw and rounded off on a polishing wheel. Results: As long as specimens broke over the waistline the results were considered acceptable. Further statistical treatment of the tests&apos; showed a satisfactory percentage of standard deviation. The tensile strength values obtained by this method do not represent true values because of the stress concentration caused by the curvature of the side of the piece and because of the closeness of the grips. The ratio of maximum to average stress at the plane of failure has been determined to be about 1.75." All tensile strength values listed in Table I are corrected accordingly. To avoid this stress-concentration, if there are a sufficient number of cores, tensile strength can be measured by imbedding the cores in mortar in the two outer briquets in the gangmold.4 Strain-Measurements: The applicability of the briquet specimens for strain observations was tested in the case of sandstone and shale. Two element Rosette SR-4 strain gages were used. Young&apos;s modulus and Poisson&apos;s ratio, both in tension, were computed and found to be different from those in compression, determined during the same test series and from the same rock, see Table I. References 1 L. Obert, S. L. Windes. and W. I. Duvall: Standardized Tests for Determining the Physical Properties of Mine Rock. U. S. Bur. Mines R.I. 3891 (1946). 2 Test for Tensile Strength of Hydraulic-Cement Mortar, ASTM Standard C 190-44. S F. O. Auderegg, R. Weller, and B. Fried: Tension Specimen Shape and Apparent Strength. Proc. ASTM 11939) 39, pp. 1261-1269. 4 API Code 32.

Jan 1, 1956

Edward Dyer Peters, the only child of Henry Hunter Peters and Susan Barker Thaxter, was born in Dorchester, Mass., June 1, 1849. From his father he was a descendant of the Peters family of Ipswich and Andover, Mass., whose earliest ancestor settled in Essex County in 1659; while upon his mother&apos;s side he descended from several old Hingham families, as well as from the Quineys and from Governor Bradford. Between the ages of fourteen and sixteen he was a student at the Episcopal School for boys in Cheshire, Conn. Near the school was an old tin mine, and he used to spend his Saturday afternoons exploring it. When Edward was sixteen, his father sold his property in South-borough, and for the next three years lived in Europe. Sept. 26, 1865, Edward entered the Royal School of Mines at Freiberg, Saxony. In the summer of 1867 he joined his family on Lake Geneva, and spent a part of the season in that vicinity, going to Chamounix and taking other trips. Extract from a letter to his father: Elbingerode, Harz, Aug. 30, 1868: I left Freiberg with my friend Lilienthal, on Wednesday the 19th of August, reached Leipzig in the evening and spent the night in that city: the next morning we took the cars and in the afternoon reached Eisleben, in Prussia, which was to be our first stopping-place; there are immense copper-mines and smelting-works at this place, and the method of working the mines is very peculiar ... The next morning we got up at five and spent the whole day in the smelting-works where I obtained a number of drawings of the furnaces they use here and a good many valuable data. Saturday morning we got up at four o&apos;clock, and descended a mine about three miles from the town; the Director of this mine was one of the most intelligent and agreeable men that I ever met; he accompanied us in the mine and explained everything that was new to us. The system of mining at Eisleben is peculiar to this town, and is not used at any other place in the world; the copper ore comes in narrow, flat veins eighteen inches high, at the utmost, consequently the men work lying flat on their left side and using the pick with both hands: the ore is carried out of the side passages into the main ones, in very low waggons about twelve inches high, and four by two feet; the boys who pull these waggons have a board buckled to their left thigh and their left arm; they pass their bare foot through a strap in the waggon and wriggle along on their side dragging the waggon after them, with their foot, almost as fast as a man can walk above ground. In the afternoon we walked over to Hittstadt, about twelve miles, and remained there Sunday and Monday. Monday night, at ten o&apos;clock we went out to one of the smelting-works, to see the refining of the copper; this is only done at night, so we worked there from ten in the evening till eleven the next morning, and came home all blackened up and with blistered hands, for our skin was not quite so tough as that of the workmen: at noon the same day we took the stage to Ascherls-leben, and then the train to Stassfurt, where there are immense salt-mines, as well as factories for the manufacture of bromium, which latter process is, however, kept a profound secret, so we had very little hope of seeing anything but the salt mines; we were talking with our landlord about our disappointment, that evening, when he told us that the director of the Bromium works was sitting in the next room with no company but his glass of beer, so we went over to him, introduced ourselves as Americans, and actually succeeded in persuading him that it could do his business no earthly hurt if he showed us his works; at last he consented, after making us give our word of honor

Jan 1, 1919

By W. W. Stephen, J. P. Walsted, W. J. Kroll

FOR the production of carbides, various furnace types are available, especially those using arc, resistance, and high-frequency heating. Selection of a specific means of heating depends primarily on the material to be treated and the physical properties of the carbide produced. In the present case, zirconium carbide had to be prepared on an industrial scale as a raw material for the production of anhydrous zirconium chloride. Considering that a rather expensive pure oxide was to be used, the arc-furnace treatment recommended for zircon sands in a previous publication&apos; was ruled out because of the considerable volatilization and dust losses caused by the blast of the arc. For this reason, either high-frequency or resistance heating seemed to offer more promise. Since there was not enough capacity of the former available, resistance heating was chosen. It was first thought that the Acheson silicon carbide furnace would be suitable for the present purpose, but the voltage in such a furnace, in which the current passes through the batch, varies from 220 to 75 v from the start to the end of a run. This variation is so great that a special tap transformer would have been required. Trouble was also expected by local melting of the carbide. Pure zirconium carbide melts at about 3527°C, but the melting point is brought down to 2427°C, according to Agte,2 when an excess of 6 pct C is present in the carbide. This we found confirmed by experiments in a high-frequency furnace. Excess carbon is needed in the batch to obtain a complete reduction. Fusion of the charge would cause great difficulties in an Acheson-type furnace because of the good electrical conductivity of the carbide as compared with that of the loose batch. Also, fused carbide is much more difficult to chlorinate than the spongy product that can be made in the radiation furnace described below. It was apparent that, to obtain a good-qual-ity zirconium carbide, the heat input would have to be well-controlled. The hairpin-resistor principle seemed to offer possibilities in this regard, and a furnace of this type was therefore developed. The advantages of the hairpin-resistor radiation principle have been discussed in previous publications, and a split-tube graphite-resistor furnace," now increasingly used in various laboratories, as well as a centrifugal quartz melting furnace4 of this type, has demonstrated the usefulness of this heating method. The hairpin-heater element has the following definite advantages over a straight resistor of the type used, for instance, by Georges:5 Its resistance is four times greater; it can expand freely; it is sturdier because of the larger diameter, and it has a larger radiation surface; there are no hot contacts that might wear out or overheat; only one clamp is used which permits assembling all electrical leads at one side of the furnace, making the other sides easily accessible to the operator. The shorter element and its larger diameter permit greater concentration of heat. The furnace developed is shown in fig. 1. The box (I), made of 2 1/2-in. graphite plates, has inside dimensions of 23x17x16 in. It contains the briquet-ted batch (2). The box is embedded in lampblack (3) up to the cover plate. The cover plate contains an opening for the gas escape (4) and for the observation hole (5), which permits measuring the temperature with an optical pyrometer. The cover plate is embedded in charcoal (6). The lampblack is contained in the insulating brick lining (7), held in the 1/4-in. sheet steel box (8). The graphite box is set on two rows of triangular graphite bars (9). The hairpin-heater element (10), the dimensions of which are given below the main drawing, extends horizontally in the graphite chamber and radiates freely on the batch. A graphite tube (11) keeps the lampblack from falling into the slot. The split electrode, which in reality is turned 90" against the drawing, is so arranged that the slot is vertical. The water-cooled packing gland (12) is insulated by an airgap from the heater element. A thin pipe (13)

Jan 1, 1951

By A. H. Daane, R. L. Myklebust

The yttrium-manganese system has been investigated by thermal, metallographic, and X-ray diffraction methods. There are three intermetallic compounds present: YMn2 which melts congruently, YMn4, which undergoes syntectic decomposition, and YMn,, which undergoes peritectic decomposition. The compound YMn4 is ferromagnetic at room temperature with a Curie temperature of 214°C. There are eutectics at 25.2, 60.9, and 82.0 wt pct Mn which melt at 878°, 1100°, and 1075°C, respectively. Crys-tallographic data are given for YMn4, and YMn12 . The terminal solid solubilities are low. In a general program of study of yttrium metal in this laboratory some alloy systems of this metal with elements of the first transition period have been examined. This work was originally instigated by experiences in cladding yttrium with jackets of some protective metals such as Inconel for high-temperature service in air.&apos; In some cases a low-melting phase was observed to form between the Inconel and the yttrium resulting in failure of the samples. In characterizing this reaction, a survey was made of the systems of yttrium with chromium, manganese, iron and nickel,, and it was found that a eutectic was formed between these metals and yttrium on the yttrium-rich side of the system. This present study of the Y-Mn system was carried out to examine in more detail the alloying nature of yttrium, and to correlate trends that have been observed in previous related studies. It was observed by Voge13 that in the systems of lanthanum, cerium, and praseodymium with each of the metals in the first transition series, the tendency to form compounds diminished in the order nickel, cobalt, and iron while no compounds were formed with manganese, chromium, or titanium. Beaudry and Daane4 observed a similar behavior in the systems of yttrium with some members of the first transition series except that the tendency for compound formation was greater. Both the Y-Ti5 and Y-Cra systems consist of simple eutectics, while in the Y-Fe,7 Y-CO, and Y-Ni4 systems, there are four, eight, and nine compounds, respectively. In addition to the above trends, the similar atomic radii and electronegativities of yttrium and thorium invite a comparison between their alloying behaviors with a common element such as manganese. In crys- tallographic studies, Florio et al.&apos; have identified three intermediate phases in this system which are ThMn2, Th6Mn23, and ThMn,,. Gschneidner and Waber10 have examined published information on alloy systems of the rare-earth metals and have correlated this information with current alloying theory. From their study, they predicted that the Y-Mn system would contain one intermetallic compound. On the basis of this prediction, the trend in the alloying behavior of yttrium with the elements of the first transition series and the alloying behavior of thorium with manganese, one might expect from one to three intermetallic compounds to form in the Y-Mn system. A consideration of Hume-Rothery&apos;s rules of alloying based on size-factor, electronegativity, and valency suggested a small terminal solubility and possible compound formation. The present study was undertaken to confirm these predictions of low terminal solid solubility and compound formation and to establish the general alloying behavior of yttrium with manganese. EXPERIMENTAL Materials. The manganese used in this investigation was obtained from the Foote Mineral Co. as electrolytic plates of 99.9 pct stated purity; the yttrium metal was prepared in this laboratory. Table I gives the analyses of these materials. For the solubility studies at the yttrium-rich end of the alloy system, distilled yttrium, whose major impurity was 200 ppm Ti, was used. Preparation of Alloys. The alloys were formed by comelting the two metals in an are-melting furnace under an atmosphere of argon. The buttons thus formed were inverted and remelted three to five times to promote homogeneity. Due to the high vapor pressure of manganese, it was assumed that the weight lost during are-melting was all manganese. This assumption was based on the very good agreement observed between calculated compositions and chemical analyses of several alloys. The compositions of the dilute alloys used for solid solu-

Jan 1, 1962

By J. R. Hauber, N. R. Borch

A study uras made on the creep behavior of cast and extruded SR grade beryllium. It is shown that, for stresses below about 1000 psi in the temperature range 760" to 85o° c, the creep behatior is nearly exactly described by the Nabarro-Herring mechanism. The activation energy is apparently that for self-diffusion, 42 2 kcal per mole, below 1000 psi, but it rises to 88.6&apos; kcal per mole at higher stresses. The slress exponent is 4.5 at the higher stresses. Tertiary creep in this material is clearly related to void formation apparently caused by grain boundary sliding. BERYLLIUM is becoming an increasingly important technological material. A search of the literature has revealed a lack of fundamental studies on the creep of beryllium. This investigation was therefore undertaken to gain insight into the creep behavior of this material. EXPERIMENTAL PROCEDURE Tensile creep samples were prepared from cast and extruded SR grade beryllium. The vendor&apos;s chemical analysis of the beryllium tested is shown in Table I. The test specimens were machined as shown in Fig. 1 from i -in.-diam rods. The machined creep specimens were annealed to remove surface damage and to establish a variation in grain size. The heat treatments and their resulting grain diameters are shown in Table 11. The average grain diameters were determined by the intercept method. True average grain diameters were estimated by multiplying the measured average grain diameters by 1.5.&apos; The creep tests were performed at temperatures from 700" to 850°C in a vacuum of 105 Torr or better in a tantalum-element resistance furnace. Loads were applied by an Instron testing machine such that the stress was held constant to within 20 psi. The test temperature was measured by thermocouples on the sample. With one exception the deviation from the desired test temperature was 2"C, and in that case the deviation was 4"C. Elongations were measured by an extensometer within the vacuum chamber which was fastened to the creep specimens at the grooves in the grip ends, as shown in Fig. 1. The precision of measurement of elongation was 1 X loe4 in. The creep tests were begun only after thermal equilibrium had been established in the sample and the extensometer to insure that there was no strain rate component due to transient thermal effects. Two kinds of creep experiments were performed. First, at constant grain size, the effects of varying stress and temperature were studied. In the second set of experiments, the temperature was held constant and the grain size was varied. The activation energy for creep was determined by varying the temperature at constant stress, as described by orn, during the first set of experiments. The variable grain size experiments revealed that creep at low stress apparently occurred by the abarro-errin&apos; mechanism. In all of the creep tests, the stress was held constant only until sufficient strain had occurred to accurately determine the creep rate. The stress was then raised to a new value and the new creep rate determined. This process was reported until tertiary creep occurred. In this manner several data points were obtained from each specimen. The assumption was made that the structure was not changing appreciably between the incremental stress levels. This was verified by reducing stresses to previously tested levels and comparing the creep rates with the creep rates obtained at the lower strains. The re-producibility was within experimental error over strains on the order of 1 pct. EXPERIMENTAL RESULTS A typical series of creep tests is shown in Fig. 2. Primary creep was not observed in any test. Transient creep, which we define as creep rates that are nonlinear with time, was not observed for any change in stress except where tertiary creep occurred. The absence of both primary and transient creep has been previously reported for hot-pressed powder beryllium.= The data for the creep behavior at constant grain size are summarized in Fig. 3. The data show two distinctly different stress dependencies. At stresses below about 1000 psi, in the equation:

Jan 1, 1969

By W. A. Hockings, M. E. Volin, A. L. Mular

Batch grinding tests at short times were made in a laboratory rod mill with 10 x 14 mesh quartzite in corn syrup-water mixtures of varying viscosity. The weight fraction broken and size modulus were found to be independent of viscosity up to 20 cp, but at higher viscosities breakage of the feed decreased while the size modulus increased. The mechanisms of the effect of viscosity are discussed on the basis of particle dynamics. The effect of viscosity of the suspending medium on grinding has not been accorded much attention, although both wet and dry grinding are used in bene-ficiation processes and the viscosities of water and air differ greatly. schweyerl investigated the rates of grinding of quartzite in a pebble mill with air, water and glycerol as the suspending media and found the rate in terms of new surface developed per thousand revolutions of the mill to be constant and dependent on viscosity up to 20,000 rev, but to decrease and become independent of viscosity for longer grinding times. Based on considerations of the drag forces exerted on suspended particles and on the grinding media under turbulent and laminar flow conditions, viscosity can be expected to inhibit the rate of grinding in a given system as it changes the flow conditions from turbulent to laminar. The objective of this study was to determine the effect of viscosity of the suspending fluid in the batch grinding of a homogeneous feed of uniform size for short residence times, a region of more practical interest than the long times investigated by Schweyer. In actual grinding operations, the viscosity of the fluid does not change, but the consistency (apparent viscosity) of the pulp increases with additions of fines. In this study the consistency of the pulp was not measured because it was thought that the grinding times were too short to alter the apparent viscosity appreciably.* *Minus 200 mesh quartz at 65% solids has an apparent viscosity of about 25 cp as measured by a simple consistometer. Personal communication from D. F. Kelsall to A. L. Mular. For the purposes of this study, the effect of viscosity on grinding can be shown sufficiently well on the basis of the cumulative weight fraction finer than the feed size at any time, and the size modulus, ku, of the finer than feed sizes. The parameter, ku, is obtained from a form of the Gaudin-Schuhmann equation. METHOD AND MATERIAL The grinding tests were accomplished in a laboratory rod mill 10-1/2 in. long and 8 in. bore with a 20-lb rod charge consisting of two 1-in., eight 3/4-in., eight 1/2-in., and eight 1/4-in. diam rods. The mill speed was 43.2 rpm. Charges of 400 g 10 x 14 mesh Wisconsin quartzite** were ground for times of 60, **Courtesy of Minnesota Mining and Mfg. Co. 120, 180 and 240 sec in 500 cc of fluid made up of corn syrup and water in measured proportions. The temperature of the pulp was measured immediately upon completion of grinding, and the size distribution of the quartzite was determined by a wash-wet-dry screening technique. Corn syrup was chosen because of its high viscosity and ideal viscous behavior, and also because its density is not greatly different from that of water. The viscosity of each fluid mixture was measured with an Ostwald viscometer at 25 C. and a correction was made for the temperature of the pulp according to tabulated values for sucrose solutions. The density differences were so small that they probably did not significantly affect breakage. RESULTS AND DISCUSSION The conditions of the grinding tests, computed viscosities, weight fractions finer than the feed size and values of a and ku are listed in Table I. The values of a and ku were taken from the linear portions of the log-log plots of cumulative weight fraction finer vs size for the various grinding times. The plots for tests in fluids of average viscosity 8.6 cp are shown in Fig. 1. In general all of the sets of curves were linear throughout most of the size

Jan 1, 1965

By John J. McKetta. Jr., Louis B. Lesem, George H. Fancher

The proration of oil produced in the field frequently is based partially or entirely upon the gas-oil ratio of wells. The measurement of the gas-oil ratio is one of the more important field tests in regulatory and pro-ration work, and the test always should be conducted according to standardized methods and procedure. Obviously, the gas-oil ratio and the volume of gas produced by a well depend upon many factors but should be independent of the method of measurement and of the devices used to measure gas and oil. Consequently, the volume of gas accompanying a barrel of oil produced by a well may be measured by any reliable and accurate device or instrument. Frequently either a critical flow prover or an orifice well tester is used for this purpose, and for a particular well the same rate of flow of gas should be obtained regardless of whether a critical flow prover or an orifice well tester is employed in the test. In Texas, when using either instrument, either Capacity Table 1 or 5&apos; is employed in making the necessary computations. If the tables are used, a discrepancy always is found whenever the two instruments are compared by extrapolation to the same conditions of flow. Clearly, Tables 1 and 5 must be at fault in some respects. The orifice well tester and the Bureau of Mines type of critical flow prover are essentially the same instrument; both devices utilize a square-edged orifice 1/8 in. in di-ameter as the primary element, and both freely discharge gas to the atmosphere. Tables for the orifice well tester&apos; have been published in the ranges of 0 to 15 in, of water and 0 to 40 in. of mercury (Hg) differential in pressure. Coefficients for the critical flow prover have been published for differentials in pressure greater than 75 psia. An extrapolation of either differs from the other set of data as much as 18 per cent at some points. No immediately obvious reasons for the discrepancy was found, and data available from the literature were insufficient to effect reconciliation. Consequently, a series of experiments was performed to check the available data and to determine discharge coefficients for the two devices in an overlapping range of differential pressure. The correlating equation used in preparation of tables such as Tables 1 and 5&apos; is the so-called hydraulic equation, Q = C1 vh .....(1) The tables cover orifice sizes from 1/8 through 1 1/4 in. A second set of tables, for use with greater differentials in pressure, apply only to the 3/4, 1, and 1 1/4-in. orifice plates over a pressure range of 0 to 40 in. of Hg. The correlating equation used in preparation of the tables is Q = C2 vH(29.32 + 0.3H)/G . (2) Each of these equations is valid only for the range to which it has been applied, and neither equation is valid for extrapolation. Theoretical equations for flow through an orifice are based upon assumptions of fractionless flow and an emergent jet the size of the orifice. A multiplier, C,, called the discharge coefficient, is inserted into the theoretical expression to compensate for both frictional losses and the contraction of the jet experienced in the plane of the orifice. Buckingham3 shows that C, should vary with the ratio of upstream to downstream pressure for flow of a compressible fluid at any average linear velocity through the orifice less than the velocity of sound. Work published by the National Advisory Committee for Aeronautics4 indicates that the variation continues into the so-called critical flow region until the vena contracta coincides with the plane of the orifice. The NACA work, however, does not indicate a leveling off of the coefficient. The work of the Bureau of Mines5 for the critical flow prover was based on differential pressures greater than 75 psi and indicates that the discharge coefficient, Cd, is constant in this region at a value of about 0.86.

Jan 1, 1958

By Tong Guangxu

INTRODUCTION Throughout the world, the caving mining methods of ore-draw under the overlying waste rock are sublevel caving in Sweden, block caving in U.S.A. and forced block caving and sublevel caving with sill-pillar in U.S.S.R. These caving methods are of high efficiency, low cost and large production (especially the block caving method) when compared to opencast mining. From the ore production of all under- ground mines, the largest annual production of underground metalliferous mines in the world is caving methods. The sublevel caving in Kiruna Iron Mine of Sweden has reached annual ore production over 20 million tons in 1974. The block caving in Climax Molybdenum Mine and San Manuel Copper Mine of U.S.A. both have produced about 40 thou- sand tons of ore per day in 1971. At the same time, the productivity of Kiruna was 12 thousand tons of ore per man-year, Climax 42.8 tons (48.3 short tons) per man-shift and San Manuel 29.01 tons (32.1 short tons) per man-shift. The main feature of this group of mining methods is the underground extraction of ore from beneath overlying caveable waste rock. Since the loss and dilution of ore are inherent (sometimes to a great extent), the control of ore-draw in these methods as com- pared with other methods is very important. Consequently, concerned Universities and Research Institutes have devoted great amounts of research on ore-draw theory and control management which has provided positive results to mine production, and has apparently promoted the development of the caving methods. During 1979 in China, metalliferous underground mines accounted for 15.22% of the total iron ore produced, while also accounting for 56% of total non-ferrous production. According to the mining methods, sub level caving in the principal underground iron mines counted for about 56.74% of total principal underground iron mine production, but only about 1% of total non-ferrous underground mine production. Relative to forced block caving and sublevel caving with sill pillar, the Chinese non-ferrous under- ground mines estimated about 35% of total non-ferrous underground mine production from these two methods, mainly from the latter. From the trend of development of underground metalliferous mines in China, the percentage of production in caving will be increased in the future, especially in block caving and forced block caving which have already been given great attention in the mining circle. In these types of mining methods the ore is drawn from the stope under a large area of overlying waste rock, which complicates the basic regulation and control of ore-draw, but provides lower loss and dilution than sublevel caving. Because of these reasons, the Kiruna Iron Mine in Sweden is intending to change its sublevel caving by testing a sublevel shrinkage caving method and considering a large area of ore-draw beneath the stope as an advantage. Therefore, the basic regulation and control management of ore-draw under a large area, as practiced in China, will be discussed in this paper. BASIC REGULATION OF ORE- DRAW FROM CAVING STOPE The aim of studying ore-draw under a large area of overlying waste rock is to se- cure a planned draw schedule that guarantees a certain plane of interface between ore and waste rock, and controls the change of its shape in spatial position for reducing ore loss and dilution during the draw process. Presently, the ellipsoid theory is comparatively near the actual attitude of ore-draw from the cave. 1. Ore Drawn Out from Single Drawpoint Laboratory testing and practical experience all show that after a certain amount of ore has been drawn out from a drawpoint, its original shape in the stope before drawing is more or less similar to an ellipsoid, hence the name "draw ellipsoid." This draw ellipsoid is cut at the bottom by a horizontal plane corresponding to the raise of the drawpoint, and its volume can be calculated by the following formula:

Jan 1, 1981

By J. D. Bateman

At Giant Yellowknife, where high grade gold-bearing orebodies are highly irregular in shape, geology has been applied extensively to the mining of ore. The classical functions of the mine geologist in the fields of exploration and mine development have been extended to guide ore extraction, ensuring "clean" mining and effectively reducing waste dilution. THE property of Giant Yellowknife Gold M.ines Ltd. is situated west of Yellowknife Bay on the north shore of Great Slave Lake, a distance of 600 air miles north of Edmonton, Alberta. The Giant claims were staked in 1935, the company was formed in 1937, and the main orebody system was disclosed by diamond drilling in 1944 following a geological study of the property by A. S. Dadson,* Consulting Geologist for the company. Production began in 1948 at the rate of 200 tons per day and, during 1950, reached a daily rate of 425 tons. During the first 3 years of operation a total of 366,000 tons was milled with an average grade of 0.79 oz of gold per ton. Work is in progress with an expansion to 700 tons per day in view. A descriptive account of the geology and gold-bearing shear zone has appeared previously.* The rock formations in the vicinity of Yellowknife Bay have been subjected to protracted pre-Cambrian tectonic deformation culminating in a series of late faults having a cumulative horizontal displacement exceeding 11 miles. The Giant property is underlain by part of an Archean sequence, several miles thick, consisting of basic volcanic flows and minor intercalated tuffs. The volcanic succession forms the west limb of a major syncline, the flows facing east, but overturned on Giant property to dip west at 65" to 75". Orebodies are confined to shear zones up to 200 ft in width, which were formed along early thrust faults. The shear zones assume fold-like attitudes, the larger of which have an amplitude of several hundred feet. The rock formations beyond the limits of the zone of shearing do not reflect the simulated folds, the axes of which are within a few degrees of the strike of the flows. The schistosity and most of the planar elements in both the shear zones and the orebodies dip west • A. S. Dadson and J. D. Bateman: Structural Geology of Camdian Ore Deposits, Can. Inst. Min. Met. Jubilee Volume (1948), PP 273-283. at angles between 65" and 75", generally corresponding to the dip of the flows. The planar elements within the shear zone system thus dip more or less constantly west whether the shear zone is flat, vertical, or expressed as east or west dipping limbs. The shear zones reflect the deformation and alteration of the basic volcanic flows into chlorite schists which, in most places, have undergone metasomatic replacement to form chlorite-sericite-carbonate schists or sericite schists. The boundaries between the shear zones and country rock, although often gradational, usually can be defined within a few feet or even inches as they are expressed by the limits of metasomatic alteration. Orebodies may occupy a small or large proportion of the shear zone and, although they generally conform to the shape of the zone, their morphology is much more complex. Ore boundaries in some instances are sharp and can be delineated with a chalk line; but more generally, a large proportion of the ore boundaries is not visually obvious and can be determined only by the perception acquired by the geological mapping of ore or study of drill cores. Ore shoots in fold-like attitudes may transect the planar elements of the shear zone at any angle; yet the schistosity within the ore shoot may be coincident with that in the enclosing shear zone. Thus it is clear that problems may arise in the delineation of mining boundaries. Ore generally consists of 20 pct or more quartz with ferruginous carbonates in sericite schist deposited in two dominant stages. The earlier stage limits of quartz with carbonate, pyrite, and very fine-grained arsenopyrite in lenses and bands. The later stage consists of quartz-carbonate lodes, in

Jan 1, 1952

By H. J. Ramey

As fluids move through a wellbore, there is transfer of heat between fluids and the earth due to the diflerence between fluid and geothermal temperatures. This type of heat transmission is involved in drilling and in all producing operations. In certain cases, quantitative knowledge of wellbore heat transmission is very important. This paper presents an approximate solution to the wellbore heat-transmission problem involved in injection of hot or cold fluids. The solution permits estimation of the temperature of fluids, tubing and casing as a function of depth and time. The result is expressed in simple algebraic form suitable for slide-rule calculation. The solution assumes that heat transfer in the wellbore is steady-state, while heat transfer to the earth will be unsteady radial conduction. Allowance is made for heat resistances in the wellbore. The method used may be applied to derivation of other heat problems such as flow through multiple strings in a wellbore. Comparisons of computed and field results are presented to establish the usefulness of the solution. INTRODUCTION During the past few years, considerable interest has been generated in hot-fluid-injection oil-recovery methods. These methods depend upon application of heat to a reservoir by means of a heat-transfer medium heated at the surface. Clearly, heat losses between the surface and the injection interval could be extremely important to this process. Not quite so obvious is the fact that every injection and production operation is accompanied by transmission of heal between wellbore fluids and the earth. Previously, the interpretation of temperature logs&apos;,&apos; has been the main purpose of wellbore heat studies. The only papers dealing specifically with long-time injection operations are those of Moss and White3 and Lesem, et al.&apos; The purpose of the present study is to investigate wellbore heat transmission to provide engineering methods useful in both production and injection operations, and basic techniques useful in all wellbore heat-transmission problems. The approach is similar to that of Moss and White:&apos; DEVELOPMENT The transient heat-transmission problem under consideration is as follows. Let us consider the injection of a fluid down the tubing in a well which is cased to the top of the injection interval. Assuming fluid is injected at known rates and surface temperatures, determine the temperature of the injected fluid as a function of depth anti time. Consideration of the heat transferred from the injected fluid to the formation leads to the following equations. For liquid, Eqs. 1, 1A and 2 are developed in the Appendix. These equations were developed under the assumption that physical and thermal properties of the earth and wellbore fluids do not vary with temperature, that heat will transfer radially in the earth and that heat transmission in the wellbore is rapid compared to heat flow in the formation and. thus, can be represented by steady-state solutions. Special cases of this development have been presented by Nowakl and Moss and White.3 Both references are recommended for excellent background material. Nowak&apos; presents very useful information concerning the effect of a shut-in period on subsequent temperatures. Since one purpose of this paper is to present methods which may be used to derive approximate solutions for heat-transmission problems associated to those specifically considered here, a brief discussion of associated heat problems is also presented in the Appendix. Analysis of the derivation presented in the Appendix will indicate that many terms can be re-defined to modify the solution for application to other problems. Before Eqs. 1, 1A and 2 can be used, it is necessary to consider the significance of the over-all heat-transfer coefficient U and the time function f(t). Thorough discussions of the concept of the over-all heat-transfer coefficient may be found in many references on heat transmission. See McAdams5 or Jakob," for example. Briefly, the over-all coefficient U considers the net- resistance to heat flow offered by fluid inside the tubing, the tubing wall, fluids or solids in the annulus, and the casing wall. The effect of radiant heat transfer from the tubing to the casing and resistance to heat flow caused by scale or wax on the tubing or casing may also be included in the over-all coefficient. According to McAdams, on page 136 of Ref. 5>

By A. R. Troiano, R. F. Hehemann

The influence of partial decomposition to high temperature bainite on reaction kinetics at a lower temperature has been studied in two alloy steels. Reaction at the lower temperature is retarded by the prior treatment, and the extent of decomposition may be reduced. Interpretation of these results is based on a mechanism involving a limitation in the nucleation and growth of bainite plates. OF the major transformations in steel, the characteristics and general behavior of the bainite reaction are probably the least understood and appreciated. Limitations of space preclude a critical evaluation of the present status of the bainite transformation in this presentation; however, such a treatment will shortly appear elsewhere. Only the salient features pertinent to the present investigation will be introduced briefly here. Although the reaction curve for the formation of bainite is similar to that for a nucleation and growth process, other kinetic features are more in keeping with the martensitic mode of transformation. A definite temperature exists above which austenite will not transform to bainite.1-5 his temperature, which has been designated B., is determined by the composition of the austenite. Unlike other nucleation and growth processes, the amount of austenite transformed to .bainite is a function of reaction temperature. The extent of decomposition increases from 0 at H. to 100 pct at some lower temperature.&apos; , This lower temperature will be designated B1 and appears to be relatively insensitive to austenite composition.% 5 The similarity in the effect of reaction temperature on the bainite and martensite transformations serves to emphasize the close connection between these two decomposition processes. Austenite decomposition in the bainite range proceeds without partition of the alloying elements.8-11 Partition of carbon has been proposed" primarily on the basis that partial transformation to bainite lowers M, and increases the amount of austenite retained at room temperature. Carbon enrichment resuslting from such partition has been employed to explain the influence of reaction temperature on the extent of decomposition.&apos;" It should be noted, however, that no enrichment has been detected experimentally in high carbon steels.1,14,15 Lattice-parameter measurements of retained austenite in steels containing 0.3 to 0.4 pct C have indicated carbon enrichment, 3,10-18 although the split indicative of a high carbon martensite has not been reported. Carbon enrichment, if it does occur, must be highly localized around the bainite plates. Therefore, carbon enrichment does not account for the influence of temperature on the progress of the bainite reaction."&apos; Thermal history is known to influence the martensite transformation through stabilization.20,21 No similar phenomenon in the bainite transformation has been reported. Materials and Procedure Two triple-alloy steels were chosen for this investigation. Their compositions were as given in Table I. These steels were chosen because the pearlite reaction did not interfere with the bainite reaction. Steel K was received in the cast condition and forged from 2 in. square bars to 1/2 x1 3/4 in. plates. The 4340 was received as 11/4 in. hot-rolled rounds. Both steels were homogenized in vacuum for one week at 2300°F in order to minimize segregation. A quenching dilatometer similar to that described by Flinn, Cook, and Fellows" was employed for the kinetic measurements. Dimensional changes were detected by a differential transformer coupled with a high speed recorder. The dilatometer was mounted so that it could be transferred to any one of three furnaces: a nitrogen-atmosphere austenitiz-ing furnace and two salt-bath furnaces for isothermal transformation. Dilatometer specimens were 1/32 x 1/4x 1/2 in. with a gage length of 1.4 in. All specimens were nickel plated in order to minimize decarburization during austenitizing. The austenitiz-ing conditions consisted of 10 min at the temperatures given above. Austenitizing temperatures were controlled to 210°F and transformation temperatures to ±3ºF. The precision of the dimensional measurements was estimated to be ± 5 x105 in. per in. Results and Discussion Isothermal Transformation: The characteristics of the isothermal bainite reaction will be described

Jan 1, 1955

By E. F. Johnson, F. H. Brinkman, H. J. Welge, S. P. Ewing

This paper presents a method for predicting the manrler in which oil will be displaced from a porous body by enriched gas. The calculations apply to a gas rich enough to give a partially, but not a completely, misci-ble displacement. The method — a three-component, two-phase analysis — takes into account condensation of some of the intermediate hydrocarbons from the injected gas into the oil, as well as enhanced volatility of heavier hydrocarbons at elevated pressures and temperatures. The condensation swells the oil and decreases its viscosity, thus aiding in its recovery. The calculations have been extended to apply to actual crude oil-natural gas systems by arranging the components into three groups according to their volatility. As an approximation, each group is then treated as a single component in the analysis. The influence of an angle of dip for an inclined displacement is also taken into account. The recovery predictions are corroborated by experiments which used both consolidated sand cores and un-consolidated glass beads. In some of these tests, actual live crude oil was displaced by a multicomponent gas typical of enriched gases used in oil fields. INTRODUCTION This paper presents a method for predicting the amount of oil that can be displaced from a homogeneous, linear, porous body at various stages during the injection of enriched, or "wet", gas. The porous body can be in either a horizontal or an inclined position. &apos;This type of displacement is sometimes known as condensing gas drive The method is developed especially for the case in which the injected gas is enriched enough to be partially, but not completely, miscible with the reservoir oil. The need for a calcula-tive procedure for this type of operation is emphasized by the number of field projects where completely miscible drives are not practical, but where near-miscible conditions are feasible. The factors taken into account in the predictive calculations include: (1) the condensation of gas components into the oil, with a resulting increase in oil volume; (2) the lowering of oil viscosity by the addition of lighter ends from the gas; (3) the increase in oil volatility at high temperatures and pressures; and (4) the physical displacement of the oil by the gas. The techniques developed in the paper can be extended to other nonequilibrium displacement processes. Other such processes that we have analyzed include a displacement by lean gas which stripped intermediates from the oil, and a water flood in which the water con. tained in solution a substance somewhat soluble in the oil. ANALYSIS OF ENRICHED-GAS DRIVE GENERAL PRINCIPLES Our method for predicting the amount of oil that can be displaced by an enriched gas uses an analogy between a three-component and a multicomponent system.&apos; The predictive method is based on these assumptions: (1) constant, or nearly constant, pressure; (2) complete equilibrium by diffusion perpendicular to the main direction of flow, but no significant mixing along the direction of flow; (3) constant injection velocity; and (4) flow in a linear porous body. The composition of a liquid or a vapor with respect to three components can be plotted on a three-component, or ternary, diagram like that in Fig. 1. Let Point A represent the composition of the oil originally in place. In this case, Oil A is undersaturated with gas. If Point A lay on the equilibrium Curve BF, the oil would be saturated. In the extreme case where the original oil contained no intermediates or dissolved gas, Point A would lie at the lower left-hand corner of the ternary diagram. In a displacement of Oil A by Gas D, there will be a progressive change in the composition of the oil phase as more and more gas is brought into equilibrium with the oil. The end result of this progressive change is an oil having the composition represented by Point F. This oil is richer in intermediate hydrocarbon and methane than the original oil and, therefore, has a greater forma-

By J. E. Burke, A. M. Turkalo

IN 1923 Desch¹ pointed out that the grains in a metal which is anisotropic with respect to its thermal coefficient of expansion would contract differently upon cooling, and that the stresses developed might approximate the plastic strength of the metal. More recently Boas and Honeycombe2-5 studied the behavior of several metals upon thermal cycling and observed that the stresses developed in arlisotropic metals are great enough to produce slip lines in individual grains and a roughening of the specimen surface. This phenomenon they have named "thermal fatigue." The mechanism they propose involves essentially a kneading of the grains, the deformation being alternately in compression and tension in a given grain as the temperature is changed in one direction and then the other. The present work was undertaken to investigate the possibility that an additional mechanism might operate to produce plastic deformation during thermal cycling—a "thermal ratchet" that depends upon a combination of grain boundary flow to relax the stress that develops between differently oriented grains upon raising the temperature and transcrys-talline slip to relax the oppositely directed stress which develops on lowering the temperature. Thus, thermal cycling should produce a nonreversible distortion such that certain grains will change shape differently from their neighbors with a simultaneous displacement being produced at the grain boundary. Temperature Dependence of Grain Boundary and Grain Strength The critical resolved stress for the initiation of slip in metal grains is only mildly affected by temperature." For example, in cadmium it decreases from 0.15 to about 0.05 kg per sq mm when the temperature is increased from 20° to 458°K and further temperature increase causes little further decrease. On the other hand, the work of KG1 indicates that the grain boundaries behave in a viscous fashion that can be described8 by the expression: t = BVexp(Q/RT) [1] t is the shearing stress on the boundary; B, a constant; V, the flow rate at the boundary; Q, the activation energy for grain boundary flow; R, the gas law&apos;s constant; and T, the absolute temperature. Eq 1 indicates that the stress necessary to cause a given grain boundary flow rate, V, decreases rapidly with increasing temperature. The value of the constant B is such that at sufficiently low temperature and ordinary strain rates deformation will occur preferentially by slip rather than by grain boundary flow. There is considerable evidence to indicate Consider the bicrystal shown in Fig. 1. In grain 1 the slip plane lies 45 " to the boundary while in grain 2 the slip plane is 90" to the boundary. The coefficients of expansion of the grains in a direction parallel to the length of the crystal are a1 and a, with a, > a2 for the orientations shown. The sequence of events that can occur upon heating and cooling this specimen is illustrated schematically in Fig. 2. Initially there is assumed to be no stress in the specimen (A). Upon heating, grain 1 attempts to become longer than grain 2, but is constrained by grain 2. Thus grain 1 is loaded in compression and grain 2 is loaded in tension, and a shearing stress is present across the boundary (B). As the temperature is increased, the stress will build up, and finally grain 1 will be plastically deformed by slip, since the greater stress is resolved on its slip planes. Any further heating will result in more slip and the stress will remain constant until some temperature T* is reached where the stress can be relaxed by grain boundary flow.† At this relaxation temperature (C) a step will appear between grain 1 and grain 2. Further heating above T* will cause grain 1 to become relatively longer, but no stress will appear because the grain boundary is too weak to support the stress (D). Upon cooling again, at T* (E), the grain boundary will again be able to support a shearing stress, and upon cooling further, grain 1 will be loaded in tension and grain 2 in compression (F). When the decrease in temperature below T* is sufficient to impose the critical shear stress upon the slip plane of grain 1, it will be stretched by slip.

Jan 1, 1953

By W. S. Cavender

The Round Mountain mining district, Nye County, Ne- vada, was discovered in 1906 on claims owned by Lewis D. Gordon. Initial mining operations uncovered gold veins of spectacular richness, and within a few days of discovery, Gordon sold his controlling interest for some $87,000. From this sale emerged the Round Mountain Mining Co., predecessor of Nevada Porphyry Gold Mines, Inc., the latter destined to become the major property owner in the area. Vein mining in the district continued sporadically into the early 1930s, yielding 9.3 Mg (330,000 oz) of gold plus substantial silver credits from approximately 626 kt (690,000 st) of ore. In addition to the lode deposits, the early miners recognized the placer potential in the alluvial fan material accumulated around the west and north sides of Round Mountain itself. Intermittent placer operations were carried out for a number of years, and in the 1940s and 1950s, Round Mountain Gold Dredging Co. worked the placers under a lease from Nevada Porphyry Gold Mines. The last placer operation terminated in 1959 when it, like some of its predecessors, proved uneconomic. Total placer production for the district is estimated at 3657 km (4 million yd) of gravel containing 59 Mg (210,000 oz) of gold and possibly 2.0 to 2.3 Mg (70,000 to 80,000 oz) of silver. Round Mountain is a small hill situated on the east flank of the Toquima Range in central Nevada. The hill is com- posed of relatively flat-lying Tertiary rhyolitic ash flow tuffs, which overlie Paleozoic metasediments and Cretaceous granites. Throughout the surrounding Round Mountain mining district, most of the known gold ores occur in the tuffs, although the metasediments and granites are also mineralized. Mineralization is structurally controlled, principally by a series of northwest-trending shears and shattered zones. Vein, stockwork, and disseminated ores occur, usually containing simple quartz-pyrite-gold mineral assemblages. The gold itself is electrum, having a silver content of 30% to 40%. In September, 1967, Elwood Dietrich, a prospector and mine promoter, obtained a purchase option on the 4452 ha (1 1,000 acres) of mineral rights held at Round Mountain by Nevada Porphyry Gold Mines. The original option had a buy-out price of $1 million and was established through Dietrich&apos;s friendship with officers of Nevada Porphyry. In April, 1968, Dietrich conveyed his option to Ordrich Gold Reserves Co., a partnership created by a group of west coast investors, mostly employees of the airline industry. There- after, Ordrich invested considerable funds in trying to test and develop the property, but soon recognized the need to seek financial and technical support from the mining industry. In December, 1968, Dietrich contacted Wayne Cavender, then Regional Geologist, Southwest, for Copper Range Exploration Company (CRX) in Tucson, Arizona, and made a data presentation. Shortly thereafter, Cavender was appointed Manager of Exploration and Chief Geologist for Copper Range Co. (parent company of CRX), New York City, and he asked C. Phillips Purdy, CRX Regional Geologist, Northwest, to make an initial property examination. Purdy&apos;s one-week field study took place in March, 1969, and resulted in a recommendation that CRX pursue its investigation of the property. The presence of low-grade gold mineralization in both the alluvial gravels and in the bedrock was verifiable, but the placer was deemed to have the greater immediate economic mining potential. At that time, gold was in the $1.41/g ($40 per oz) price range. Working from Purdy&apos;s information, Cavender decided to attempt acquisition of the property, and the first in a long series of negotiations was initiated with Ordrich. Basically, CRX felt that the placer had a promising potential for several reasons, including (I) past operators had recovered free gold but not the gold contained in the pebble fraction of the gravels; (2) past operations appeared to have been ineffectively designed or managed and not costefficient; and (3) the price of gold appeared to be poised for an upward move. Negotiations with Ordrich were prolonged and difficult, with CRX competing against several ma* mining companies, but finally an agreement was reached, effective June I, 1970. Gold was then back to $35. It is believed that, in

Jan 1, 1985

By B. C. Raynes

IN the early part of 1952, under the auspices of the U. S. Atomic Energy Commission, Horizons Inc. undertook an investigation dealing with the preparation of high purity thorium metal in order to develop an economically competitive production process for this metal based on a recovery of the metal by a fused salt electrolysis, since a survey of the literature of thorium chemistry indicated that electrolytic methods had not received much attention, despite the consideration that electrochemical production methods often offer attractive commercial potentialities. Thorium metal has been prepared by methods which fall into four general categories: 1) reduction of halides or double halides; 2) reduction of the oxide; 3) thermal decomposition of halides; and 4) electrolytic methods. Some of the important results obtained by various investigators since about 1900 in recorded attempts to prepare pure thorium metal are summarized in Table I. A bibliography of pertinent literature is included in this paper. Thorium is strongly electropositive and possesses a great affinity for oxygen and nitrogen. As a result the prospects for the production of high purity thorium from aqueous media or oxygen bearing compounds are remote. The most promising and profitable area of investigation for production of thorium metal lies in fused salt electrolysis. Thorium has been produced previously by this technique from halide salts in fused alkali chloride eutectic mixtures. Until recently, however, the lack of known large uses for thorium has inhibited the investigation of these methods. The basic problem in an investigation into fused salt production methods for thorium is to develop a suitable fused salt system for the economic preparation of thorium. The first portion of the work in these laboratories was a small scale investigation of the electrolysis of potassium thorium fluoride, KThF5, under a variety of conditions. High purity thorium was prepared in this manner, but the process did not appear to offer the simplest and most attractive continuous commercial operation. The work reported here relates to an all-chloride system employing thorium chloride as the cell feed. ThCL4 was produced as an anhydrous material stabilized in molten sodium chloride. This product, further diluted in NaCl, was subjected to electrolysis. The electrolytic process has been studied in cells capable of holding up to 50 lb total salt charge. Ductile, pure thorium metal has been reproducibly obtained in this operation. Considerable experimentation was carried out in the preparation of ThCL as a cell feed free from moisture, oxides, and other impurities. Thorium was cathodically deposited as a coarsely crystalline powder interspersed with residual bath salts. Aqueous procedures for separating and recovering the metal were developed. The thorium metal powder obtained has been evaluated with respect to its hardness, chemical purity, and certain other physical properties. Preparation of ThC1,—Thorium chloride, and the chlorides of some other metals (aluminum, beryllium, tantalum, zirconium, etc.) cannot be obtained from aqueous solution by direct heating and evaporation. Evaporation and heating of a solution of thorium chloride yields a hydrated salt or partially hydrated salt, and finally Tho,. Anhydrous thorium chloride is obtained by forming a hydrated ammonium chloride complex salt in acidified water solution, dehydrating this compound, and finally decomposing the double salt and subliming the ammonium chloride component. Various methods for the preparation of anhydrous thorium chloride, in accordance with this concept, were investigated as indicated in Table I1 from hydrated thorium chloride (ThCl, . 3H2O), and from thorium oxycarbonate (ThOCO,). In the method found most satisfactory for this work, thorium oxycarbonate was dissolved in an excess of concentrated HC1 to give a clear yellow solution. At least 2 mol NH,Cl were added to the solution per mol of contained thorium. Ammonium thorium chloride hydrate was crystallized from solution by cooling and saturation with HC1. The resultant complex, (NH,Cl),ThCl;xH,O, was dehydrated by evaporation at 130° to 150°C and thoroughly dried at about 250°C. The dried ammanium thorium chloride was then mixed with sodium chloride in proportions to form NaThCL or to produce a ThCL4-NaCl mixture with a given thorium content. The ammonium chloride was sublimed off at temperatures above 500°C in an inert atmosphere furnace to give an anhydrous chloride source electrolyte, essentially free of Tho, and of NKC1.

Jan 1, 1958

By G. A. Moore

A brief review is given of methods designed to produce metallic iron of high purity, and typical results are listed. A recent method, utilized at the National Bureau of Standards, consists of the extraction of ferric chloride by ether, reduction of this ferric chloride to ferrous chloride, further purification of this chloride, and the subsequent electrolytic deposition of metallic iron. iron produced by this procedure apparently is softer than, and otherwise different in properties from, any iron previously prepared and contains appreciably smaller amounts of impurities. THE history of attempts to produce "pure" iron reaches to antiquity and it may be presumed that each ancient armorer who succeeded in making a better steel concluded, correctly, that he had done a better job of removing the "base metals," and incorrectly, that he now at last had a "pure" metal. Early metallurgical papers mentioned use of "pure iron" in making alloys—this "pure" iron in most cases being inferior to some commercial stocks of the present time. Improvement has been continuous, and usually at a sufficient rate to convince each succeeding group of workers that they, at last, were using the really pure metal (until the analysts also improved their techniques to again discover the impurities). These adventures were reviewed in some detail by Cleaves and Thompson.&apos; Although the ores of a metal may be abundant, difficulties in extracting it may make the pure metal very rare. When impurities are restricted to a total of a few parts per million, nearly all pure metals become rarities. Lead, copper, gold, mercury, silver, zinc, aluminum, bismuth, and the six platinum metals are claimed to be available with total impurities ranging from 2 to 50 ppm. The present small and scattered world supply of so-called "pure" iron holds an unimpressive place in another group of 16 metals having approximately 100 ppm of foreign material. Of about 20 less rare metals, only the platinum metals are more costly to prepare. While the production of such rare varieties of iron may appear insignificant in the presence of thousand-ton operations with 95 to 99 pct metal, it must be emphasized that all researches on commercially interesting irons and steels are in fact studies of the modifications of the properties of iron by additional materials. Until the properties of high purity iron are directly measured, all ferrous research must operate without known base values. Traces of impurities may affect the properties of a metal in many ways. Infinitesimal traces of solutes, by disturbing the electronic configuration, greatly change the electrical properties of transistors and semiconductors2-3 and slightly larger traces might alter these quantities in iron. Soluble impurities which disturb the perfection of lattice arrangement not only may alter the magnetic constants and electric properties, but by their close association with dislocation phenomena probably control the very existence of the "yield point"; determine the value of yield stress; and perhaps control the selection of slip and cleavage planes. It has been speculated that impurities might even cause the allotropic transformation in iron, but in any case their rearrangement must contribute to the unreliability of heat capacity and other thermodynamic measurements. Impurities which do not remain in solution may cause even greater effects on the properties. Microscopically visible amounts of phases other than ferrite can be found in all high purity irons which have come to my attention. It can be calculated that from 50 to as little as 2 ppm of an insoluble material might be sufficient to completely film all grain boundaries in irons having grain sizes from ASTM Nos. 10 to 1. Should this occur, such films, even though invisible, may be very important in fracture problems, especially at extremes of temperature:&apos; Studies of grain growth and diffusion normally imply consideration of a single-phase system, hence, in the presence of insoluble impurities they can be expected to give ambiguous data." High purity iron is also in demand for use as chemical and spectro-chemical standards; for work in classifying the lines of the iron spectrum; for biological work in nutrition; and for work in nuclear physics. where the presence of some sensitive

Jan 1, 1954