In a previous publication from this laboratory1 the conclusion was drawn that the embrittling effect of occluded hydrogen on iron and steel must result from the precipitation of the gas within small openings through the crystal structure. A review of the literature then published indicated the real existence of crystal substructures of the mosaic type and gave presumptive evidence that the "rift openings" associated with hydrogen occlusion are the same as the L'disjunctions" of the mosaic theory. Inasmuch as no clear conception of the actual nature of the crystal fragments and openings inherent in these theories has been established, it was considered desirable to obtain direct micrographic evidence of their true configuration. In this direction the standard methods of metallographic attack have proved useless. Recourse was had, therefore, to the direct examination of the surfaces upon which failure by cleavage had resulted from the presence of hydrogen. It was expected that such a surface, unaffected by chemical attack and undis-torted by polishing, would reveal the fine openings penetrated by the gas and thus indicate the real nature of the substructures. Materials Studied In commercial steels, defects caused by hydrogen take various external forms according to such factors as structure and purity, and to the extent to which hydrogen either occludes or produces chemical changes. The present work relates only to the well-known transcrystalline hydrogen embrittlement—-"pickling brittleness "—in which elemental hydrogen occluded within the grain develops cleavage characteristics. For example, hydrogen embrittlement resulting from hydrogen reaction products is excluded from detailed study. It was also desirable, as far as possible, to have the study uncomplicated by other elements which themselves cause brittleness. Three types of iron were used. These included ingot iron, decarburized free-machining steel, and a specially prepared, aluminum-killed, electrolytic iron. This choice allowed a comprehensive selection of unavoidable minor impurities and inclusions, which could subsequently be shown to have no specific effects on the structures within the grains. Carbon, and any other impurities free to react with hydrogen, were first removed by a preliminary annealing treatment in hydrogen. Subsequent treatment in vacuo extracted much of this hydrogen and its gaseous reaction products. The resultant ductile iron was then embrittled either by a second anneal in hydrogen, followed by rapid cooling, or by cathodic electrolysis. Group 1: Prepared from Armco Ingot Iron As shown in Table 1, the principal impurity in this iron was oxygen, which survived the purifying treatment to a large extent. Two series were prepared. The first (Nos. SIO-24) was purified only one day in hydrogen and dehydrogenized one day in nitrogen. Containing both hydrogen and its

Jan 1, 1943

By Carl A. Zapffe, George A. Moore

In a previous publication from this laboratory1 the conclusion was drawn that the embrittling effect of occluded hydrogen on iron and steel must result from the precipitation of the gas within small openings through the crystal structure. A review of the literature then published indicated the real existence of crystal substructures of the mosaic type and gave presumptive evidence that the "rift openings" associated with hydrogen occlusion are the same as the L'disjunctions" of the mosaic theory. Inasmuch as no clear conception of the actual nature of the crystal fragments and openings inherent in these theories has been established, it was considered desirable to obtain direct micrographic evidence of their true configuration. In this direction the standard methods of metallographic attack have proved useless. Recourse was had, therefore, to the direct examination of the surfaces upon which failure by cleavage had resulted from the presence of hydrogen. It was expected that such a surface, unaffected by chemical attack and undis-torted by polishing, would reveal the fine openings penetrated by the gas and thus indicate the real nature of the substructures. Materials Studied In commercial steels, defects caused by hydrogen take various external forms according to such factors as structure and purity, and to the extent to which hydrogen either occludes or produces chemical changes. The present work relates only to the well-known transcrystalline hydrogen embrittlement—-"pickling brittleness "—in which elemental hydrogen occluded within the grain develops cleavage characteristics. For example, hydrogen embrittlement resulting from hydrogen reaction products is excluded from detailed study. It was also desirable, as far as possible, to have the study uncomplicated by other elements which themselves cause brittleness. Three types of iron were used. These included ingot iron, decarburized free-machining steel, and a specially prepared, aluminum-killed, electrolytic iron. This choice allowed a comprehensive selection of unavoidable minor impurities and inclusions, which could subsequently be shown to have no specific effects on the structures within the grains. Carbon, and any other impurities free to react with hydrogen, were first removed by a preliminary annealing treatment in hydrogen. Subsequent treatment in vacuo extracted much of this hydrogen and its gaseous reaction products. The resultant ductile iron was then embrittled either by a second anneal in hydrogen, followed by rapid cooling, or by cathodic electrolysis. Group 1: Prepared from Armco Ingot Iron As shown in Table 1, the principal impurity in this iron was oxygen, which survived the purifying treatment to a large extent. Two series were prepared. The first (Nos. SIO-24) was purified only one day in hydrogen and dehydrogenized one day in nitrogen. Containing both hydrogen and its

Jan 1, 1943

By H. B. Pulsifer

One of the most common basic open-hearth furnace products is a simple carbon steel with a carbon range from 0.05 to 0.15 per cent. The material is widely used for sheets, tubes, bars, wire and the innumerable special objects of secondary fabrication. The properties of the material vary over wide ranges, depending on the more exact composition and details of manufacture or treatment that affect its structure. The present paper is a review of those properties and structures that have been found by studying this steel as used in the cap screw industry. At first glance this might be thought a narrow application of the steel, but, since the industry uses the material in the cold-worked, annealed and heat-treated conditions, the title of the paper may be excused for its comprehensiveness. Yet, in studying the wide ranges of properties and structures that preclude a more specific title, there can be no suggestion of completeness or finality. Even a summary of a few years' work is no more than a preliminary survey of a field that will be fertile in scientific data and industrial products for many years to come. An outline of the structures will be given first, then a list of the previous contributions that are at hand and finally some details of the work and related problems, especially concerning this low-carbon steel in the surface-hardened condition. Wire Used in Manufacture of Cap Screws The wire that is used for making cold-upset and roll-threaded cap screws has been cold-drawn from hot-rolled rods that were pickled and limed. The common sizes used in the industry range from 0.185 to 0.750 in. dia., the exact diameters depending on the plant practice and having the usual tolerances of 0.002 in. for the smaller sizes and 0.003 in. for the larger sizes. The carbon range, by pit analysis, is usually between 0.07 and 0.12 per cent. Manganese should be within the usual 0.30 to 0.50 per cent. range. Sulfur rarely exceeds 0.045 per cent. and phosphorus seldom exceeds 0.030 per cent. Silicon is usually below 0.03 per cent. but in the silicon-killed steels may be in the customary 0.10 to 0.25 per cent. range. Rimmed steel is not considered most suitable for cap screws that are cold-headed or for parts that are to be surface-hardened.

Jan 1, 1931

From the historical account of the coal industry set forth in the preceding pages the reader will have learned that coal is extremely widely spread throughout the United States, and in most places it has been easily found, that it has been remarkably easy to develop, and, where the deposits were available to streams on which it could be transported to markets, it was opened almost as soon as the country was settled. Such were the mines along the James, Susquehanna, Monongahela, Ohio, Kentucky, Cumberland and Big Muddy Rivers. In other localities where such easy means of transport were not convenient, the early production was confined to local use, or to places to which it could be hauled by wagons, but everywhere small mines were established almost as soon as the country was settled, and these increased both in number and size as the available markets grew. These early mines were nearly always opened by local people, and the industry was so far-flung that its growth attracted little or no attention excepting when a labor disturbance or a breakdown in transportation occurred. Had it been concentrated in a few places as most metal industries were, or as the petroleum industry was for many years after it started, it is probable that much better records of its progress would have been kept. When the canal era began, in the eighteen twenties, coal was at first not considered as a valuable source of freight revenue, and much surprise was expressed that the receipts of the Schuylkill Canal were very largely from coal after the first few years, as was the case of the Union Canal though not to such an extent. Even the early railroads to the coal fields did not realize the extent to which the products of mines would figure in their revenues, and it was many years before railroads were built practically solely for prospective coal traffic; indeed this did not happen until some years after the Civil War. Map 12 shows the extent of the canal system in the United States in its relation to the coal fields at the time of its maximum development. It will be seen that only the coal areas in Pennsylvania, Ohio, and to a very small extent in Indiana were able to ship by canal at all, and that only a very small portion of such fields could do so. Looking backward, it is hard to understand the great hopes entertained of canals by their pro-

Jan 1, 1942

By F. H. Wilson, E. W. Palmer

Brass mills are familiar with a recurring problem which reveals itself during deformation of annealed metal as an opening up of cracks which are suggestive of a grain boundary pattern. A typical example is seen in Fig 1, which shows part of the convex surface of a cartridge brass disc which was slightly dished by the punching operation. Another illustration of the same type of defect was found in the surface of a finished cartridge case which split open on firing. These cracks, shown in Fig 2, were away from the split but indicate the presence of the type of weakness which permitted the splitting. Usually the weakness consists of separate cracks, the lengths of which are of the same order of magnitude as the grain size prior to the final anneal. Their typical appearance in a polished section is shown in Fig 3. This structure was found below the surface of a fractured tensile-specimen that had been cut from a large cartridge blank showing the defects on its convex surface. While the pattern formed by these cracks suggests a grain boundary origin, the cracks bear no relation to the currently existing grain structure. Thus Fig 3 shows that the grains have grown up to cracks already present. Since it is doubtful that the cracks were present in the metal before the anneal, they must have formed during the anneal but prior to recrystallization. The term "fire-cracking" has been generally applied to cracking that occurs during an anneal under the influence of internal stress, but refers more specifically to obvious macroscopic cracking attributable to the presence of a low melting phase, usually lead. Since the type of cracking described above may occur when the lead content is very low, we have considered it a somewhat different phenomenon, and have called it "inter-granular parting." While most examples involve cartridge brass, intergranular parting has also been observed in the fabrication of large seamless tubes from discs of both 85/15 red brass and 70/30 cupro-nickel. Similar cracking in nickel silver was investigated by Jones and Whitehead,1 who showed that it could occur during healing or cooling. That which occurred on heating they called "fire cracking," and they suggested that, a transformation at about 320°C might account for its occurrence. It was felt in this laboratory that the observed parting was probably one aspect of the general observation, first made by Rosenhain and Archbutt,2 that a tendency toward intergranular fracture under tensile stress increases with increasing temperature and decreasing rate of strain. In this case the stress involved would be internal. The rate of strain would be exceedingly slow, a localized internal creep. Reference to the literature uncovered no efforts to extend the observations of Rosenhain to conditions involving only internal stress. Accordingly, an exploratory research, sufficient in detail to satisfy us as to the probable truth of this explanation of the observed intergranular parting, was undertaken. The internal stresses present during the early stages of an anneal (prior to recrystallization) would be from two sources: residual stresses developed during deformation, and thermal stresses caused by uneven heating and expansion. Thermal stresses would vary widely according to shape, size and manner of heating, and can be considered as supplementary to residual stresses. It seemed necessary to determine the stress and temperature conditions under which parting would occur in a relatively short time, and then to establish whether or not in- ternal stresses may persist to an extent adequate to cause parting at such temperatures. (Jones and Whitehead1 and Moore and Beckinsale3 made tests which indicated that stress relief required an appreciable time.) During the course of the research the desirability of studying the effect of grain size became apparent, and this factor is one of the major variables of our investigation. Intergranular Parting under Tension at Elevated Temperatures In early experiments, hard 70/30 brass tensile specimens, with unknown residual stresses, held for 10 min. at applied stresses from 30,000 to 40,000 psi at temperatures from 300 to 350°C, showed no macroscopically visible cracks when unloaded and cooled, but cracks very similar in appearance to those observed in commercial practice were revealed in these specimens by pulling them to fracture. Annealed specimens, on the other hand, showed no cracks in such experiments, apparently because they deformed plastically at stresses below those necessary to cause parting in a reasonable time. Hence, the specimens used for this study were first strengthened by cold tensile elongation, giving them an unavoidable residual stress pattern (determined largely by grain size and orientation) which would, however, correspond in direction, at least, to the stress pattern obtained under stress at temperature. A variation in these residual stresses might be expected with variations in grain size, but following any given anneal the reproducibility of stress pattern should be as good as that of the grain size measurement. With no information as to the effect of the amount of prior deformation, tests were conducted on specimens given the same cold elongation, using a stress applied at temperature which was a constant proportion of the stress required to produce this elongation. In

Jan 1, 1950

By L. T. Larson

The spectral reflectivity of zirconium in light of 441 to 668 nanometers (nm) wavelengths and air immersion has been determined. Bireflectance and apparent-angle -of-rotation measurements show zirconium to be optically isotropic when examined in light of approximately 484 nm wavelength. There is a direct relationship between bireflectance and the tilt of the basal pole of zirconium from the surface normal. This relationship allows the determination of the spatial orientation of the basal pole of an individual single crystal within a coarse-grained poly crystalline section to within± 2 to 3 deg for angles of basal pole tilt from 0 to 90 deg. In recent years considerable attention has been given to the quantitative determination of optical properties of opaque minerals by use of vertically incident, plane-polarized light. In particular, Cameron' and Cameron et a1.2 have developed criteria for the identification of a large number of anisotropic ore minerals based upon measurement of the apparent angle of rotation and the ellipticity or phase difference of the reflected light. It was shown by Larson and Pickle-simer3 that apparent-angle-of-rotation measurements may also be used to determine crystallographic orientations of grains of noncubic metals. In particular, it was shown that the basa.1 pole orientation in space of zirconium grains can be determined to ±3 deg for those grains with basal pole tilts of 10 to 90 deg from the plane of the section. Another, even more widely studied, optical property is reflectivity. cameron4 has commented upon measurement of the reflectance of plane-polarized, vertically incident light and Bowie and Taylor5 have made such measurements an integral part of their system of ore-mineral identification. Leow6 has reported on the spectral reflectivity of molybdenite and has used reflectivity values to calculate refractive indices and absorption coefficients. Cameron7 has made use of reflectivity values to ascertain aniso-tropic ore mineral symmetry and Piller and v. Gehlen8 have evaluated sources and importance of errors in reflectivity measurements as applied to calculation of optical constants. cambon9 has shown that reflectivity measurements using vertically incident, plane-polarized light are useful in the investigation of metals and in the identification of phases present in alloys. Bronson10 has made preliminary measurements on the optical anisotropy of beryIlium and Mott and Haines11 have published qualitative data on the intensity of light reflected from sections of bismuth, tin, and aluminum when these metals are microscopically examined under crossed polarizing plates. Koritnig12 has correlated the reflectivity of homogeneous solid solutions with their chemical compositions. From the above work and investigations in progress by this author, it is apparent that accurately determined values for the reflectance of vertically incident, plane-polarized monochromatic light from carefully polished surfaces of noncubic metals can prove useful in identification, composition determinations, and crystallographic orientation applications. Finally, reflectivity values, when measured in two media of differing refraction index and related to standards whose spectral reflectivities in these media are known, can be used to calculate optical constants such as refractive index and absorption coefficient. These constants may prove of use to those concerned with problems of electron band configuration. This paper reports the spectral reflectivity of zirconium measured in light of 441 to 668 nanometers (nm) wavelengths and air immersion. It also gives maximum bireflectance values for a prism section of zirconium in these wavelengths and shows how bire-flectance may be used to determine the crystallographic orientation of zirconium single crystals. Because of the lack of information on the reflectivities of the standards in oil immersion, no attempt is made to calculate the refractive indices or absorption coefficients although it is recognized that such values may be of fundamental importance. METHOD Single crystals of zirconium were cut by electro-discharge machining from a single-crystal rod grown from iodide bar by an electron-beam zone-melting process.13 The crystal sections were mounted in cold-setting epoxy resin and mechanically polished to a plane, uniform, bright surface. Each crystal was then chemically polished in a 26/26/43/5 mixture (by vol) of water, nitric, lactic, and hydrofluoric acids to remove the mechanically damaged and smeared surface layer. Final polish was obtained by electropolishing at 30 v in a bath of methyl alcohol and perchloric acid (98/2 by vol) at -70oc.14 Reflectivity measurements were made using a photometer system designed and developed at Oak Ridge National Laboratory and described in detail by Larson.15 Briefly, the reflectivity measuring system consists of a reflecting microscope; a double-beam, null-balancing photometer array; a mechanically driven microscope stage; and a direct X-Y readout of the reflectivity of the specimen relative to its orientation on the microscope stage. The measuring photometer receives its signal from the specimen through a slotted Wright occular placed on top of the photovisual head of the microscope. The reference photometer receives light through a flexible glass "light pipe" from a mirror in the reflecting system of the microscope. Monochromatic light is attained through use of interference filters (15-nm half-peak width pass bands) placed in front of a stabilized Vickers 12 v, 100 w, tungsten-filament, quartz-iodide lamp.

Jan 1, 1970

By A. Raman, P. P. Singh

The constitution of the La-Rh system was studied by powder X-ray diffraction, metallopaphic, and differential thermal analysis techniques and an equilibrium diagram is presented. Eleven intermediate phases occur in the system and the crystal structural data for nine of them were determined. La3Rh crystallizes in an orthorhombic structure of undetermined type, whose unit cell is obtained by doubling the 'a; and 'c,,' edges of an FesC type unit cell. The other intermediate phases of the system are LarRh-3( undetermined structures also occur in the system. LaRh, undergoes a polymorphic phase transformation at 1240°C. LaRh3 and La2Rh7 also exhibit polymorphisnz. The phases Laah and LazRh7 melt congruently. The latter undergoes a eutectoid transformation into LaRh, and Rh at 1205°C. Laah3 is formed by a peritectoid reaction between Laah and La,Rh,,. The other Phases result from peritectic reactions between the liquid and the adjacent rhodium-rich phases. The intermediate Phases of the La-Rh system are compared with those of the La-Co and La-Ni systems. DURING the course of a detailed investigation to study the occurrence of CrB, FeB, A1B2, and related structures in the rare earth alloys it was found that much information is lacking for the rare earth noble metal systems. Although the structures of several rare earth alloys containing the noble metals at the AB and AB2 stoichiometries have been reported, the occurrence of related structures at other stoichiometries has not been studied. We have initiated a project to study the crystal structural features of selected rare earth-rhodium alloys and to map the equilibrium diagrams of representative systems with conventional methods. The results of our investigation in the La-Rh system are presented in this paper. Two phases were known in the La-Rh system. LaRh has the CrB-type structure.' LaRhz is a MgCu2-type Laves phase.z EXPERIMENTAL PROCEDURE Alloys weighing less than 1 g were prepared from commercially pure lanthanum (99.9 pct +), supplied by Lunex Company, Pleasant Valley, Iowa, and rhodium (99.92 pct +), supplied by Engelhardt Industries, Newark, N.J., in a conventional arc melting furnace under argon atmosphere. The buttons were turned upside down and remelted three times to insure homogeneity in the samples. Since negligible loss of material was encountered during melting, a chemical analysis of the alloy buttons was not undertaken. Powder specimens for X-ray diffraction studies in the as cast state were then prepared. The buttons were wrapped in thin molybdenum foils and homogenized by heating in vacuum at suitable high temperatures for more than 1 week. They were then broken into three or four pieces for annealing experiments. The pieces were wrapped in molybdenum foils and annealed at various temperatures in evacuated quartz capsules. The annealing was carried out for 2 hr at or above 1200°C, 1 day at temperatures close to llOO°C, 2 days at 1000°C, and for 1 week at temperatures below 1000°C. After annealing the alloy pieces were again broken and powder specimens for X-ray diffraction were prepared. The powders of the lanthanum rich alloys with more than 80 at. pct La were prepared by filing. The filings were sealed in molybdenum tubings and stress-relieved at 600°C in vacuum. It was not deemed necessary to stress-relieve the powders of the other alloys, since the alloys were very brittle and were ground easily. POWDER X-RAY DIFFRACTION X-ray diffraction photographs of powders (-325 mesh size) of the alloys in the as cast and annealed states were prepared in a Guinier-de Wolff focussing camera with copper K, X radiations. These patterns were studied to identify the stoichiometries and the crystal structures of the intermediate phases. The lattice parameters of the phases were calculated after minimizing the differences between the observed sin2 6 values, calculated from the diffraction angles 8, and the sin2 8 values, calculated using approximate lattice constants obtained from a few lines. These differences were minimized manually to less than 0.0005. The latLice constants are judged to be accurate to *0.005A for values less thp about 10A and to k0.01~ for values greater than 10A. The relative intensities of the lines were calculated using a computer program written by Jeitschko and Parthk.~ No attempt was made to refine the atomic positional parameters in the phases. METALLOGRAPHY The phase equilibria in the investigated alloys in the as cast and annealed states were also studied by metallographic examination. The polished specimen surfaces were etched with 10 pct picric acid in alcohol (alloys up to 25 pct Rh), concentrated picric acid (from 25 to 37.5 pct Rh), 2 pct nital (40 to 50 pct Rh), 10 pct nital (from 50 to 66.7 pct Rh) and with concentrated 48 pct HF for the other rhodium-rich alloys. Selected microstruture~ were then photographed using a Po-laroid Land camera. THERMAL ANALYSIS Differential thermal analysis of the alloys was carried out in DTA-668 Stone differential thermal ana-

Jan 1, 1970

By L. Leibowitz, M. G. Chasanov, L. W. Mishler

A drop calorimeter system is described for use in measuring enthalpies to 3600°K. Data are presented for tungsten between 2800" and 3600°K. The enthalpy of tungsten in cal per mole between 2000° and 3600°K can be represented by the equation HºT- Hº298 = - 1.7622 X 103 + 5.7772T + 8.9861 where T is in degrees Kelvin. A tabulation of com -puted values is presented for heat capacity, entropy, and free energy function. A drop calorimeter has been constructed to carry out enthalpy measurements at temperatures to 3600°K. Samples are heated by induction1 and dropped into a commercial adiabatic calorimeter, modified for this purpose. The experimental temperature is limited by the melting point of container materials and compatibility of the container and its contents. Several high-temperature drop calorimeters have been described in the literature1-5 but none has been used at temperatures as high as those in the present work; our measurements of the enthalpy of tungsten range from 2800" to 3600°K. DESCRIPTION OF EQUIPMENT An overall schematic view of the equipment is shown in Fig. 1. Power for the induction coil is supplied by a 25-kw 250 kHz Ther-Monic generator coupled to an iron core RF transformer. The Sample capsule is suspended in the work coil by 10-mil diam tungsten wires which are wrapped around a horizontal 5-mil diam tungsten wire. The horizontal suspension wire is clamped between two massive copper electrodes which are fixed in an x-y motion device that allows adjustment of the position of the heated capsule from outside the vacuum chamber. The copper electrodes are connected by flexible copper straps to a 1250-joule (5 kv, 100 pfarad) condenser bank. When it is desired to release the capsule, the condensers are discharged through the horizontal suspension wire causing it to vaporize rapidly. Very reliable and precise release of the capsule is achieved in this manner. Experiments have shown that no heat correction is required for this discharge energy. As part of the temperature measuring system, two prism holders have been incorporated in the apparatus. The upper prism holder is in the main vacuum chamber itself, whereas the lower one is in a side arm attached to the drop tube below the gate valve. The upper prism is mounted on a rotary vacuum feed-through, and may be moved under a protective shield when not in use. This prevents deposition of vapors on the prism surfaces when temperature measurements are not being made. Similarly, the lower prism is mounted on a push-pull vacuum feed-through, and when not in use may be pulled into its side tube. The prism mountings are fitted with guides and stops so that they may be moved precisely into the desired position. The aim throughout is to minimize the time the prisms are exposed to vapors from the hot samples. At the high temperatures reported in this paper, only the lower prism was used. The upper prism holder in these cases was fitted with an additional radiation shield. By using a prism and viewport, the lower surface of the samples can be observed by an optical pyrometer. The measurements discussed in this paper were obtained with a Leeds and Northrup 8622-C-S series manual pyrometer which is estimated to be accurate to 0.5 pct. Pyrometer calibrations and prism and window corrections were carried out in the conventional manner6 using tungsten strip lamps calibrated by the National Physical Laboratory, Teddington, England. Prism corrections were rechecked after each use. All work to date has been done in vacuum, and no measurable change has been observed in the prism correction below -2300°K for the upper prism and below -2800°K for the lower one. The total time of exposure of the prisms is about 50 sec per run. At high temperature, the final temperature reading is corrected by using the final A value for the prism; see Ref. 6 for details of this procedure. The calorimeter is a modified Parr Instrument Co. (Moline, lll.), Series 1230 adiabatic calorimeter with automatic jacket control. Other authors5 have used a similar calorimeter with good results. The calorimeter jacket cover and calorimeter cover are attached to the drop tube which contains a radiation shield. This shield is a gold-plated copper disc which can be operated manually from outside the calorimeter. The receiver is attached below the radiation shield and is lined with tungsten. In a typical experiment, the calorimeter and its jacket water temperatures were adjusted to 0.000°K temperature difference. The sample was allowed to equilibrate in the furnace at the desired temperature for about 20 min. The initial calorimeter temperature was then recorded, the sample dropped, and appropriate shutters closed. After about 3 min, the drop tube and receiver were filled with helium to 60 torr. The final calorimeter temperature was recorded after it had remained constant over a 5-min period. The equilibration time in the calorimeter was about 25 min. Thermistor probes are used to operate a hot and cold water supply system to maintain the jacket temperature equal to the calorimeter temperature. For actual measurements of the calorimeter temperatures, a quartz thermometer was used (Hewlett Packard Dymec Thermometer, Model #2801A). This thermome-

Jan 1, 1970

By G. S. Cole, H. Biloni, G. F. Bolling

An experimental investigation of sovlze low .melting point alloys sJtows that a substvucture of isolated depressions can be the first manvestation of constitutional supercooling on solid-liquid interjaces veuealed by decanting. Electron-tni cvop vobe and wletallo gvaplic esanzinations, in tlze bulk belzind the interjace, oj the segregation associated with these isolated areas substantiate tlzei&apos;v depressed nature, since a solute of ko < 1 is enriched, and a solute of ko > 1 depleted. In contrast, the pox structuve, a set of projections often veported in the literature, leaves no trace oj. segvegation. These obserl;atims, accovlrpanied by a brief review of recent literature, point to inconsistencies between experirrental obsevvation and the idea that the fornzation of a projection is a causal step in the development of a cellular substructure. An argument is presented to show instead how it is plausible for substantial depvessiom to form in the pvesence of constitutional supercooling at dislocations threading the solid-liquid interjace. THE development of constitutional supercooling during growth from the melt leads to the formation of the cellular solidification substructure. This well-founded association between structure and instability has been basic in understanding cellular substructure and micro segregation; however, the initial formation of structure seems unclear. Rutter and Chalmers,&apos; in definitive experiments and theory, noted that in the presence of constitutional a planar interface might break down: "resulting in the formation of a small projection on an initially plane or uniformly curved interface." That is, the breakdown from a planar to a cellular interface was implied to be initiated via a projection into the unstable liquid. Later, Walton et (11. found that a structure of isolated projections, termed "pox", appeared at solid-liquid interfaces decanted under growth conditions near the onset of constitutional supercooling; the pox were taken as the indication of the instability promoted by the supercooling. Tiller and Rutter4 in their extensive work studied the shape transitions at decanted interfaces which were generally observed to proceed as— pox, "irregular cells", elongated cells, regular (hexagonal) cells, and so forth. The pox varied in size from lo-&apos; to 1CT4 cm, and tended to disappear as cells increased in number and regularity, but as noted,4 the first real array of cells did not seem to be a development from the pox. In fact these authors implied a lack of connection because they stated that the pox are denser on "irregular cells", and as cell boundaries increase in number (i.e., the cells become smaller) there is less need for the pox which do dis- appear. Thereafter, most authors dealing with either experiment or theory have accepted the reality of pox and have used them as a criterion for the onset of constitutional supercooling. In contrast, Spittle, Hunt, and smiths have now suggested that pox are irrelevant artifacts comprised of such things as entrapped oxide. This proposal invokes the observations of weinberg6 and chadwick7 each of whom have shown that the act of decanting leaves a residual liquid on a decanted interface; the remnant solid layer of the order 10 p may thus contain particles that might have been transported from the external surfaces, or elsewhere, during decanting. With the incentive of this suggestion,= some further experiments and a reexamination of the literature have been conducted, in order to question the validity of pox as evidence of an instability and to examine the initial development of the cellular substructure. 1) EXPERIMENTS Single crystals of zone-refined tin (-99.9999 pct) were grown from the melt in a controlled fashion with various, small concentration additions of lead and antimony, for which ko < 1 and > 1, respectively. The crystals were decanted at conditions near the onset of constitutional supercooling and were thus appropriate for observation of slight perturbations. It was possible to observe two types of small departure from smooth or "planar" interfaces in both cases of lead or antimony additions. Some were projections and others, if in regular array of any type, were depressions. The crystals were etched with suitable reagents progressively dissolving the decanted interface surface; projections left no record, but depressions were continuously associated with spotlike areas contrasting with the rest of the interface. Traverses were made with the beam of an electron microprobe across the regions of contrast; with lead addition the persistent spots were lead-rich, and with antimony addition the persistent spots were antimony-poor. This is consistent only with a dominant role for depressions, because if the projections had left spots but were incorrectly catalogued, a reversed observation should have been made; that is, the Pb(ko < 1) should have been depleted and the Sb(ko > 1) enriched. In the work of Cole and inegard, and elewhere, regular arrays of structure associated with the initial stage of instability have been shown, in photographs and represented as pox or projections. We believe this to be erroneous, by inference, since whenever a regular array was observed, in the present examination, it consisted of depressions, regardless of the nature of the solute, ko 1. Fig. 1 is reproduced8 as an ideal example of the possible optical illusion involved; the observer can satisfy himself from the distribution of illuminated areas that the markings are depressions. Fig. 2 from the present investigation is an interference photograph of an interface similar to that in Fig.

Jan 1, 1967

By N. O. Gray, John Henderson

Hydrogen-reduction data for naturally occurring single crystals and Prepared polycrystals of dense hematite have been presented. Results cover the temperature range 400o to 1000oC, for particles from ten sources, ranging in size from 0.07 to 10 mm and in shape from spheres to cylinders, cubes, and thin slabs. A consistent pattern of behavior has been demonstrated for single crystals and the reduction mechanism shown to be temperature-dependent. Below 579oC reduction is a simple topochemical process but at higher temperatuves it is complex and occurs in two distinct stages. Prepared particles from these laboratories behave in a similar manner to the single crystals. Data from two investigators showing topochernical reduction of Prepared particles above 575°C are inconsistent with that for other dense hematites. It is concluded that topochenzical reaction should not be used as a model for generalized rate expressions for dense hematites. SINCE 1958, McKewan1-6 has brought to prominence a simple concept of dense hematite reduction. This model is that oxygen is lost from a hematite particle undergoing reduction only from an oxide-iron interface that recedes in such a way that the oxide remaining retains the original shape of the particle, i.e., reduction occurs topochemically. An adjunct to this concept is that any intermediate oxides in the transition from hematite to iron only form thin layers so that oxygen cannot be lost from the particle without movement of the oxide-iron interface. Further, the rate of oxygen loss from the particle is said to be proportional to the area of the receding interface so that the iron layer grows linearly with time and the over-all reduction process can be described by the equation where ro and do are the initial particle radius and density, respectively, R is the fraction of the original oxygen lost, i.e., the fractional reduction, at time t, and K is the rate constant. The idea of an underlying simplicity in hematite reduction is attractive because it gives a tractable basis from which general theories of hematite reduction can be developed and it has received wide support,7-14 based mainly on the large amount of data13 that can be fitted to Eq. [I]. However, despite the fact that this equation has been derived for dense materials, the bulk of the data that have been used to test it13 have been for materials of only about 90 pct of theoretical density (5.26 g cm-3) or less, so that its generality for dense hematites has not been demonstrated. In any case, as will be seen, adherence of reduction data to Eq. [1] does not necessarily imply that reaction occurs topochemically. In this work only data for hematites approaching theoretical density are considered and it will be shown that in only one study besides McKewan&apos;s is topochemical behavior observed over the whole range of temperature investigated. For the majority of materials a linear rate of interface advance is observed to complete reduction only when wustite is not a stable intermediate phase in the transition of hematite to iron, i.e., at temperatures below about 575°C. Above this temperature, reduction is an exceedingly complex series of reactions that takes place in two distinct stages and it is only in the first stage that reaction in any way resembles a topochemical process. This means then that, far from representing general behavior as has commonly been supposed, topochemical reaction for dense hematites is only a particular behavior that may be observed under some circumstances. EXPERIMENTAL Hydrogen-reduction data have been collected and cross-checked in these laboratories by three techniques, weight loss, collection of water evolved in the reduction reactions, and direct metallographic examination. Details of these techniques are discussed elsewhere," where it is shown that results obtained by the three methods are in close agreement. The weight-loss method, by which most of the results were obtained, consisted of hanging the sample in a platinum mesh basket from an Ainsworth Model AV-AU-1 vacuum recording balance inside a vertical l 1/4-in.-ID alumina tube furnace. Dry deoxidized hydrogen was flowed downwards through the tube at 2 to 4 liters min-1 (stp). Single crystals from two sources and artificial oxides from three sources have been examined. The single crystals were from hematite deposits at Yampi Sound, Western Australia, and Brazil, the latter being obtained from Gregory, Bottley and Co., London, U.K. The "Yampi Blue" crystals were hand-picked from washed, magnetically concentrated, sized fractions, -200 mesh BSS (mean diameter ca 0.07 mm) and —36 + 44 mesh BSS (mean diameter ca 0.4 mm) while 10-mm cubes were cut from the Brazilian crystals with a diamond saw. The starting materials for the prepared particles were hematites designated, respectively, "Specpure Iron Oxide", Laboratory No. S639 from Johnson Matthey & Co. Ltd., London, U.K., "Calcined Ferric Oxide" from B.D.H. Laboratory Chemicals Division, Poole, U.K., and "Pigment Grade Oxide", EPR-50, from C. K. Williams & Co., Easton, Pa., U.S.A. Approximately spherical particles were prepared from the artificial oxides by rolling the material, moistened if necessary, in a glass jar, and cylindrical compacts approximately 10 mm in diam and of approximately equal height were pressed in a steel die at 200 psi. These spheres and cylinders were subsequently fired in oxygen for 20 to 100 hr at 1370°C. The

Jan 1, 1967

By R. P. Laforce, ZJ. R. Low, A. M. Turkalo, D. F. Stein

The interaction of the crlloying eletnenls, nickel and chromium, with the impurity elements, antimony, pIzosphorus, tin, and arsenic, to producse reversible temper brittleness in a series of high-purity steels containing 0.40 wt pct C has been investigated. The alloyed steels contained approximately 3.5 pcl Ni, 1.7 pct Cr, and 0.05 to 0.08 pct of the particular irnpurity to be investigated. Susceptibility to teirlper embrittlement was measured by comparing the notched-bar transition temperature of each steel after quenching from the final temper and after very slow cooling (step cooling;) following the final temper. A plain carbon steel without alloying elements, bu/ ud/h 0.08 pel Sh, does not embrittle when step-cooled through the emzbrittling range of temperatures. The same embrittling treatment, applied to a steel with about the same antinzony content but with nickel and chvonziunz added, causes a 700°C increase in transition temperature. If chromium or nickel is the only alloying element, the increase in transition temperature is only 50%, again with antimony present. A carbon-free iron containing nickel, chromium, and antimony shou~s a 200°C shift in transition temperature for the same thermal treatment. Specific alloy-impurily interactions are also observed for the other impurity elements, phosphorus, tin, and arsenic. Additional investigations involving electron microscopy, trzicrohard-ness tests of vain boundaries, minor additions of zirconiutn and the rare earth and noble metals, nzainly with negative results, are also described. HE particular type of embrittlement investigated is that which is encountered in alloy steels tempered in the temperature range from about 350" to 525&apos;C or slowly cooled through this range of temperatures when tempered above this range. This type of embrittlement is sometimes called reversible temper brittleness to distinguish it from the embrittlement indicated by a minimum in the room-temperature V -notch Charpy energy vs tempering-temperature curve encountered in the range 28 0" to 350°C. Temper brittle-ness seriously restricts the use of many alloy steels since it precludes tempering or use in the embrittling range of temperatures and may significantly raise the ductile-brittle transition temperature of heavy-section forgings and castings tempered above the embrittling range, since such sections cannot be sufficiently rapidly cooled after tempering to avoid embrittlement. The very voluminous literature of temper brittle-ness up to about 1960 has been reviewed by woodfine&apos; and LOW.&apos; Of particular significance to the present investigation was the demonstration by Balajiva, Cook, and worn3 that high-purity Ni-Cr steel does not exhibit temper brittleness and the subsequent detailed and systematic study by Steven and Balajiva~ of the effect of impurity additions on the susceptibility to embrittlement of Ni-Cr steels. Steven and Balajiva showed that, of the impurities which may be found in commercial steels, Sb, As, P, Sn, Mn, and Si could all produce temper brittleness in a high-purity Ni-Cr steel. The principal purpose of the present investigation was to study the effects of particular alloy-impurity combinations on susceptibility to temper embrittlement. The steels used were high-purity 0.30 to 0.40 wt pct C steels containing 3.5 wt pct Ni and 1.7 wt pct Cr, separately or in combination. The susceptibility of these steels was then determined when approximately 500 ppm by weight of antimony, arsenic, phosphorus, or tin were added as an impurity. The melting, casting, and forging practices used in the preparation of the materials investigated are described in Appendix A. Table A-I in this appendix shows the analysis of all steels to be discussed. The steels were produced as 20- or 2-lb heats. The smaller heats were used after it had been demonstrated (see Appendix B) that a small, round, notched test specimen could be used to measure the shift in the ductile-brittle transition temperature caused by temper brittleness with about the same result as that obtained by Charpy testing. HEAT TREATMENT Unless otherwise noted, all steels were tested for embrittlement in the tempered martensitic condition. A typical heat treatment for a 0.40 C, 3.5 Ni, 1.7 Cr steel was: 1 hr at 870"C, in argon, quench into oil at 100"C, quench into liquid nitrogen, temper 1 hr at 625"C, and water-quench. The warm oil quench was used where quench-cracking was encountered; otherwise the initial quench was into room-temperature oil or water. For other compositions austenitizing temperatures were 50°C above Acs with the remainder of the thermal cycle the same. Steels in this condition, with no further heat treatment, are designated as non-embrittled. The above quenching and tempering cycle for the 0.40 pct C steels resulted in as-quenched hardnesses of 48 to 53 RC and as-tempered hardnesses of 24 to 31 Rc except in the case of the plain nickel or plain carbon steels. In these, the as-tempered hardness was as low as 80 to 90 Rg. No attempt was made to adjust the tempering temperature to obtain the same hardness in ali steels since it was felt that a uniform thermal cycle was more important than exactly equivalent hardness values. Pro- the standard quench and temper described above, the standard embrittling treatment was "step-cooling". For this the thermal cycle was: 593"C, 1 hr; furnace-cool to 538"C, hold 15 hr; cool to 524"C, hold 24 hr; cool to 496"C, hold 48 hr; cool to 468&apos;C, hold 72

Jan 1, 1969

By Lucien F. Trueb

The microstructure of explosion-bonded pairs of similar and dissimilar metals has been investigated by electron microscopy. A review of the specific problems encountered and the methods used for obtaining surface replicas and thin-film transmission specimens of the bond interface is given. The bond area is mainly characterized by continuous and practically diffusionless metallurgical bonding. The very large shear stresses induced along the collision front of the plates being joined causes extreme grain elongation and a symmetrical pattern of subgrains in the bonding direction. The bond zone is also characterized by a very high density of dislocations and pressure-induced twins. Localized heating occurring during the cladding process can result in partial re-crystallization or the formation of thin layers of molten material. The force of precisely controlled explosions causing a high-velocity impact between metal plates has been used for several years to achieve metallurgical bonding between an extremely wide variety of metals. This method essentially consists of accelerating a plate to high velocity toward a stationary plate by a detonating explosive. Since the restrictions to bonding are not those encountered with conventional nethods, it becomes possible to bond pairs of metals having widely different mechanical properties that are immiscible or form brittle intermetallic compounds. Many applications of such composite metals are found in the field of corrosion protection as well as numerous other fields; for example, explosion bonding is being applied for fabricating the materials used by the United States Mint in the new sandwich-type coins. The primary condition for establishing a metallurgical bond is that absolutely clean metal surfaces be brought together. Any metal exposed to the atmosphere is covered with oxides, adsorbed gases, and other contaminants; even a very forceful impact of two such surfaces is not sufficient for bonding. Cowan and Holtz-man,"&apos; who reviewed the dynamics of colliding plates in detail, showed that in order to achieve a good bond the explosion conditions must be chosen in such a way that the plate collision velocity is less than the sonic velocity, in which case no oblique shock waves are attached to the collision front. A pressure wave is then generated ahead of the collision line, and the material forming the colliding surface of each of the plates flows forward and is ejected in the form of a spray, the so-called jet. The dynamic elastic limit of the metals must be exceeded so that there is sufficient plastic deformation. At the point where the jet formed by the junction of the inner surface layers of both plates separates from the combined plates, the material experi- ences a very high shearing strain and the pressure can reach several hundred kilobars. This process strongly influences the microstructure of the bond zone as will be seen later. Behind the collision front, uncontami-nated layers of internal material are brought together under high pressure and are thus metallurgically bonded. I) STRUCTURE OF EXPLOSION BONDS The different types of explosion bonds that can be obtained depend on the explosion conditions, and have been investigated by Cowan and Holtzman,1&apos;2 Holtzman,3 Klein; Bahrani and crossland,&apos; and Buck and Horn-bogen. The preferred kind for practical applications is the so-called wavy bond, typical examples of which are given in Fig. 1 showing light micrographs of various metal-to-metal interfaces. In forming this type-- of bond the collision energy is mainly expended in jetting, the formation of waves, and localized melting. Beyond the crest of the waves, eddy-shaped areas are observed in which the two metals are mixed in a complex pattern of streaks. Cowan and Holtzmanl first proposed that this wavy pattern is analogous to periodic eddy shedding in the flow of a viscous fluid around an obstacle (Von Karman&apos;s eddy street). The mass of metal ahead of the stagnation point, which is associated with the jet and has forward momentum, plays the role of an obstacle and the eddies created in the flow of solid metal around the stagnation point are preserved in the final clad specimen. This idea has been reviewed more recently by Klein4 and the variables involved in the wave formation have been discussed in some detail by Bahrani and crosslands and Buck and Hornbogen.6 Several studies of the structure of explosion bonds by light metallography have already been published.1-6 Aside from the waviness and the eddies which were mentioned above, the most striking characteristic of the area in the vicinity of the bond interface is a very considerable longitudinal grain deformation which appears to be strongest at the metal-to-metal boundary and dies out as one moves away from it. Large twins are often observed within the deformed grains, and molten areas are found in the center of the eddy-shaped structures situated beyond the crest of the waves. The large hydrostatic pressures and shear stresses occurring at the interface modify the mechanical and chemical properties of the bond zone. Increases in hardness in this area have been reported by various authors.396 The defects along the interface can also cause a local increase of the chemical reactivity and thus might be expected to boost the etching rate. However, the effects of this preferential etching cannot be observed by light microscopy due to its inherently limited resolution power. The same limitation precludes the observation of morphological features directly along the bond interface as well as the interface itself. Furthermore, no information can be gained by light-

Jan 1, 1969

By G. D. Van, Arsdale

IT IS particularly appropriate that a paper on this subject should be presented in Spanish, before a Spanish speaking audience, and in a South American country, first because of the facts that these countries today have not only the largest copper leaching plant in existence but also present great opportunities for future extension of hydrometallurgy; and second, because of the fact that the first copper made by any wet method was doubtless produced before existing records at the Rio Tinto deposits in present day Spain.

Jan 1, 1925

By AIME AIME

ROBERT F. MEHL was born in Lancaster, Pa., March 30, 1898 and graduated from Franklin and Marshall College in 1919. He then went to Princeton and was granted his doctor&apos;s degree in physical chemistry in 1924. Two years as head of the department of chemistry at Juniata College, followed by a like period as National Research fellow at Harvard, working with T. W. Richards and Albert Sauveuir, satisfied Bob&apos;s immediate affections for college and university life and prepared him to turn temporarily to other fields.

Jan 1, 1938

Meeting; May 23, 1913.-On the petition of 25 or more members residing in the different localities, the following Local Sections were established: St. Louis Local Section. Southern California Local Section; Denver Local Section. It was voted to publish a statement in regard to tours in connection with the Butte meeting, which-is published on p. i of this Bulletin. Mr. Edward Caldwell was appointed as expert advisor. on printing. The report of the Committee on Printing advising certain changes in methods of printing. was accepted.

Jan 6, 1913

CENTRAL AMERICANIZATION COMMITTEE Chairman, MRS. C. C. BURGER This committee reports progress in drawing up circulars on the. subject of Americanization, to be sent to all the branches of the W. A. A. I. M. E. It is greatly to be desired that all our members should interest themselves personally in work that can be done among the women and children in the mining districts in the way of Americanizing those of foreign birth or extraction; so much can be accomplished by individual interest and sympathy.

Jan 11, 1918

By W. F. Stowasser

A downdraft traveling grate process to agglomerate pelletized iron ore concentrates has been successfully demonstrated in a pilot plant at Carrollville, Wis. Work there followed several years of development in the Allis-Chalmers Mfg. Co. laboratories, and the pilot plant phase was carried out in co-operation with Arthur G. McKee & Co., consultants and engineers to the iron and steel industry. End result of the process is conversion of iron ore concentrates into a form which can easily be transported and smelted in the blast furnace.

Jan 5, 1955

By J. W. Still

CIRCULAR steel sets have proved to be more economical for supporting slusher drifts in the block-caving mining used by the Miami Copper Co., at Miami, Ariz. The first steel sets were installed in July 1950, and up to July 1, 1951, about 474 sets (approximately 1896 ft of drift) were placed; the bulk of this work was done in the latter six months. All of the places selected for the steel were in heavy ground. Based on this experience the following definite conclusions can be drawn:

Jan 11, 1951

By James Gayley

The paper presented to the Institute in 1910, by H. O. Hof-man, on Recent Progress in Blast Roasting,&apos; has called the attention of the iron industry to the adaptability of these processes to the reclamation of by-products such as flue-dust and blue billy, and the better preparation of concentrates and fine ores for use in blast-furnaces. The waste of valuable iron-ore through the production of flue-dust has increased at an enormous rate, and much of it has in

Jan 1, 1912

By R. J. P. Lyon

It is usually assumed1,2 that ore deposition is relatively slow, taking place over tens of thousands of years. Yet many syntheses and phase changes can be completed in the laboratory in a matter of hours, under essentially the same pressure and temperature conditions to be expected in nature. Much has been written about geothermometry, and Ingerson&apos;s recent summary2 can hardly be surpassed. Rather than review the whole field, this article will deal specifically with diffusion rates in solid solutions* of the sulfide minerals.

Jan 11, 1959