By A. Steiner, K. L. Komarek

Activities of aluminum in solid Ni-A1 alloys have been determined between 20 and 60 at. pet Al and 1200" and 1400°K by an isopiestic method in which nickel specimens, heated in a temperature gradient, are equilibrated with aluminum vabor in a closed all-alumina system. The activity of aluminum shows a strong negative deviation from Raoult's law at low concentrations but increases by three orders of magnitude within the ß(NiAl) phase. The partial molar enthalpy and entropy of mixing are negative. Using Wagner and Schottky's theory of ordered compounds, a degree of disorder of 4 x 10 -4 for NiAl and 1.25 X 10-2 for FeAl has been calculated THE Ni-A1 system has been studied by a great number of investigators, and the results, as far as the phase diagram is concerned, have been compiled by Hansen.1 The phase boundaries from 0 to 50 at. pet Ni are well-established. At higher nickel contents the boundaries are still in dispute and an additional phase, A12Ni3, has been reported.' The phase diagram is dominated by a very stable high-melting compound, NiA1, with a relatively wide range of homogeneity. Heats of formation of solid alloys have been determined calorimetrically by Oelsen and Middel3 from 20 to 95 at. pet Ni and by Kubaschewski4 from 25 to 80 at. pet Ni. According to the most recent compilation5 no other thermodynamic investigations have been reported for the Ni-A1 system. Due to the corrosive nature and the low vapor pressure of aluminum, a method has been employed for determining activities of aluminum which was previously developed for the Fe-A1 system.= Nickel specimens, heated in a closed evacuated alumina system in a temperature gradient, were equilibrated with aluminum vapor from a source within the system kept at constant temperature. After complete equilibration the specimens were analyzed and activities calculated from the known vapor pressure of aluminum. APPARATUS AND EXPERIMENTAL PROCEDURE Materials. The nickel specimens were made from wafers of electrolytic nickel (International Nickel Corp.) of 99.99 pet purity which were rolled to a 0.001-in.-thick foil by Driver-Harris Co. and to a 0.005-in.-thick sheet in our laboratory. The aluminum (Aluminum Corp. of America) had a purity of 99.99+ pct. The alumina tubes and crucibles were made of impervious recrystallized alumina with an alumina content of 99.7 pet (Triangle RR, Mor-ganite Inc.). Experimental Procedure. Annular specimens were punched from the sheet, the punching burrs removed, and the specimens degreased in carbon tetrachloride and acetone and weighed on a micro-balance to within an accuracy of ±0.01 mg. The specimens were positioned with alumina spacers along an alumina tube, and the positions measured. Aluminum metal was machined into cylindrical shape, and placed into an alumina crucible. The tube with the specimens was then inserted into a hole drilled into the aluminum metal. An alumina tube with its closed end at the top was slipped over the specimens so that its lower end fitted snugly into the alumina crucible. The assembled reaction tube was inserted into a mullite tube with a water-cooled brass head which had an opening for a quartz thermocouple protection tube and a metal-to-glass connection to a conventional vacuum system. A Pt-Pt 10 pet Rh thermocouple could be raised and lowered in the quartz tube which was placed along the outside of the alumina reaction tube. The mullite tube was heated by two separately controlled resistance-tube furnaces so that in the experimental temperature range an over-all temperature gradient of approximately 150o to 250°C could be imposed on the reaction tube. The position of the mullite tube was adjusted so that the surface of the aluminum metal was always at the temperature minimum. The reaction tube was thoroughly evacuated before and during slowly heating the assembly up to the melting point of aluminum. A pressure of less than 2 µ (Hg) was maintained during an experiment. Once the aluminum had melted, it isolated the contents of the alumina tube from the surroundings. Several times during an experiment the temperature gradient was carefully measured. An experiment lasted from 3 to 6 weeks and it was terminated by air cooling the evacuated mullite tube. For further details of the experimental procedure the paper on the Fe-A1 system6 should be consulted.

Jan 1, 1964

By J. L. Smith, A. L. Albee

This article presents a series of guidelines by which the geologist can evaluate the likelihood of surface faulting and its probable extent at any given site in Southern California and Nevada. The information is intended primarily for geologists concerned with establishing design criteria for proposed nuclear plants. The geologic problems involved in the location of a nuclear power plant are fundamentally no different from those for other types of installations. They fall into four main categories: foundation stability, landslides and slope stability, shaking due to earthquakes, and surface faulting. For problems in the first three categories the foundation engineer, the geologist, and the seismologist can provide criteria for plant location and design, and these problems can generally be economically handled by appropriate design measures for a project of the magnitude of a nuclear plant. However, problems in the last category — surface faulting — are more difficult to handle and require a unique evaluation. Accordingly, this paper will deal primarily with the problem of establishing design criteria for surface faulting, particularly as it affects nuclear facilities. A nuclear reactor is a power source that for greater safety is contained in a heavy, air-tight structure, just as gas, oil, water, and other power sources must be contained. Surface faulting is significant in that it may reduce the integrity of the containment by affecting critical exterior piping or by breaching of the containment. A similar significance exists relative to dams or tanks for the storage of water, gas, or oil, except that in these latter examples the breaching of the container automatically releases the fluids to do their damage. This is not necessarily the case with the rupture of a reactor containment structure because the function of the containment is totally protective, i.e., it is necessary only in the event that radioactive products are released from the reactor, and there are many other safeguards to pre- vent this release even if the containment is ruptured. At the present time, nuclear power plants must be located near large sources of water for cooling the steam generated. The construction of an industrial facility of any kind on the coast line is esthetically distasteful to most people since, unfortunately, there is not enough coast to fulfill all the needs and all the desires of all the people. In most cases where industrial facilities encroach on the lives of citizens, there is no mechanism other than zoning laws by which a person can effectively protest. But in the case of a nuclear facility, the public hearing required by the Atomic Energy Commission provides a forum for dissent, as in recent case histories, and the question of safety provides objectors with a weapon for fighting the construction of the plant. The nature of a public hearing for a nuclear plant is such that the prospective owner and operator must prove that there is no undue hazard, whereas the objectors need only demonstrate that there is a reasonable doubt. It is in this situation that geology becomes the Achilles Heel of nuclear power plant location. For his investigation, the geologist has natural exposures of rock at the ground surface and a limited number of trenches and drill holes to give him a fairly complete picture of the distribution of the various rock types. From the surficial data, he must infer three more dimensions — depth below the surface, past time, and future time. Unlike many problems faced by engineers, the geologist has only this one set of data from which to reach a conclusion — he is unable to reproduce the natural sequence of events in order to obtain another set of data for comparison. Hence, by the very deductive nature of a geologic conclusion, it is difficult to prove a geologic conclusion beyond a reasonable doubt even to other geologists — and perhaps one should say especially to other geologists because the experience and background of a geologist will strongly influence his conclusion, and no two geologists have exactly the same experience and training. The engineer and the public official would like the geologist to conclude that faulting cannot occur at a given site or to assign a numerical value to the probability of its occurrence — but no responsible geologist can do either of these things. Since government officials and others must make decisions that affect the public safety, it would seem that the geologic profession must attempt to establish criteria and

Jan 1, 1968

By David Turnbull

IN isothermal recrystallization processes, new crystals generally grow into the matrix until they impinge upon other new crystals or an external surface, at constant linear rates G. Before impingement the perceptible course of growth can be described by the equation: 1 = G(t-7) C1I where, G = dl/dt, 1 is a crystal dimension measured in a constant direction, t is the time, and 7, the nucleation period, is a positive intercept on the time axis. Fig. 1 is a schematic representation of I as a function of time for a recrystallizing grain. G is dependent upon temperature, driving energy (strain or surface energy), relative grain and boundary orientations, but is generally independent of time. The frequency of nucleation, fi, (time" volume") can be defined by the equation: N = 1/fV [2] where ? is the mean nucleation period and V is the volume of the specimen that has not recrystallized. The kinetics of primary and secondary recrystallization generally can be described satisfactorily in terms of the parameters N and G only.'-" After recrystallization is complete the average grain size 7 increases with time by "normal grain growth;" didt, the average rate of grain growth, is strongly time dependent and has not yet been precisely related to G for the motion of the individual grain boundaries constituting the system. It has been suggested4* " that the elementary act in grain boundary migration is closely related to the elementary act in grain boundary self-diffusion. Although the distance of atom movement in the two processes may be somewhat different, there is reason to expect that the activated states may be very similar, so that the free energy of activation for grain boundary migration should be of the same order of magnitude as for grain boundary self-diffusion. Therefore, it is desirable to develop a satisfactory basis for comparing data on self-diffusion and grain boundary migration and to make such comparisons where possible. Theory The formal theory of grain boundary migration rates is analogous to the theory for the rate of growth of crystals into supercooled liquids reviewed elsewhere 6-8. Boreliuss has shown that the latter theory describes, within the theoretical uncertainty, the growth of selenium crystals into supercooled liquid selenium. Motto and more recently Smolu-chowski" have derived expressions for the rate of boundary migration in recrystallization. The treatment to be presented is similar to Mott's excepting that the formalism of the absolute reaction rate theory will be used. The atomic mobility, M, in grain boundary migration is defined by: G = -M6p/6x where p is the chemical potential per atom and x is the coordinate measured in the direction of grain boundary movement. Let AF be the free energy difference per gram atom on the two sides of the boundary and k the thickness of the boundary. For RT>>AF the potential gradient across the boundary (6p/6x) is essentially linear and it follows that: SF/8x = - aF/N\ [4] where N is Avogadro's number. According to the Nernst-Einstein equation, M is related to a diffusion coefficient, Do, for matter transport in grain boundary migration by the equation: M = Da/kT [5] Substituting eqs 4 and 5 into eq 3 gives the basic relation between Do and G: G = DoaF/\RT [6] Do values may be calculated from experimental values of G from eq 6 and directly compared with the coefficient of self-diffusion within the crystal, DL, or the grain boundary self-diffusion coefficient D,. However, a more convenient, though equivalent, basis for comparing atomic mobility in grain boundary migration and self-diffusion is through the constants of the absolute reaction rate theory. According to this theory diffusion coefficients may be written:" D = k2(kT/h) exp [-AF,/RT] 171 aFa, the free energy of activation, is related to the measured energy of activation, Q, by the equation: AFA = Q - T aSx - RT [8] where aSa is the entropy of activation. Substituting eqs 8 and 7 into eq 6 gives: G = ek(kT/h) (aF/RT) exp [(AS,,)C/R] exp C-Qc/RTI C91 where the subscript G refers to boundary migration. The relationship between the driving free energy and the free energy of activation in boundary migration is indicated schematically in Fig. 2. Experience indicates that the variation of G with temperature can be described by: G= Go exp [- Qc/RT] [10] where Go and Qc are generally temperature independent over wide ranges of temperature. Comparison of eq 9 with eq 10 gives:

Jan 1, 1952

By G. L. Chierici

Starting from Muskat's theory of water and gas coning, maximum permissible oil production rates without water and/or free-gas production have been determined, in a broad range of reservoir and well parameters, using the potentiometric model technique. The main assumptions made are as follows: (1) the reservoir rock is homogeneeous (either isotropic or anisotropic); (2) the volume of the aquifer underlying the oil zone is very small, so that it does not contribute to reservoir energy; and (3) the gas cap expands at a very low rate, so that it can be assumed to be in quasi-static conditions. The results obtained are presented in the form of diagrams which can be used for solving two types of problems: (1) given the reservoir and fluids characteristics, as well as the position and length of the perforated interval, determine the maximum oil production rate without water and/or free-gas production; and (2) given the reservoir and fluids characteristics only, determine the position and length of the perforated interval which optimize the maximum permissible oil production rate, without water and/or free-gas production. INTRODUCTION In oil reservoirs where the oil-bearing formation is underlain by an aquifer which does not participate in the production mechanism, water-coning is a limiting factor to the flow rates of producing wells. Production rates are usually kept to a value that will prevent the water from entering the wells. The entry of water into a well lowers its productivity by increasing the weigbt of the fluid column; moreover, the separation of water from the effluent, at the surface, may constitute a very difficult problem in cases of heavy viscous oils. A similar situation is encountered in oil reservoirs with a gas cap overlying the oil-saturated zone; here a downward gas cone is induced by the flow of oil towards the producing wells. Production rates must be low enough to prevent the gas from being produced; producing gas from the gas cap would be a waste of energy. Of course, water-coning and gas-coning phenomena can occur at the same time in the same reservoir if the oil-producing formation is both overlain by a gas zone and underlain by a water zone. Due to its relevant practical importance, the mechanism of coning was studied by many people.2,3,5-8 Defining the conditions for getting the maximum water-free and/or gas-free oil production rate is a difficult problem, often encountered under one of the following aspects: 1. Predict the maximum flow rate that can be assigned to a completed well without the simultaneous production of water and/or free-gas. 2. Define the optimum length and position of the interval to be perforated in a well, in order to obtain the maximum water and gas-free production rate. A systematic study of these problems was made by means of the electrical analog technique. The results of this study are presented here, under the form of a set of curves providing solutions for the above stated problems. These curves are valid only for homogeneous forrnations, either isotropic or anisotropic. Should the formation be non-homogeneous (by horizontal or vertical variation of permeability, shale diaphragms, fractures, etc.), a specific potentiometric study would be required for each specific case. Especially when shale diaphragms of some radial extension are present, the critical rates observed are much larger than would be expected from the diagrams. STATEMENT OF THE PROBLEM In the present study the aquifer is supposed to be of such limited volume that it does not contribute to the energy of the reservoir. Moreover, the gas cap is supposed to expand at such a low rate that the potential gradient in the gas cap is negligible. Under static conditions water-oil and gas-oil interfaces (T1 and T2) are both horizontal. When the reservoir production starts, below each well these interfaces take a cone-like shape (Fig. 1) having as an axis the axis of the well. This shape results from the equilibrium between potential gradients in the oil zone and gravitational forces due to density differences between oil and water and between oil and gas. Assuming the oil-bearing formation to be homogeneous and the oil to be incompressible, the analysis of the problem (see Appendix) shows that the oil-water and gas-oil interfaces are stable only if the oil production rate of the well is not higher than the following values.

Jan 1, 1965

By Jei Y. Choi, P. G. Shewmon

The surfrrce-diffusion coefficients (DJ for Aulg8 on (100) and (111) surfaces of copper have been determined between 1050" and 780°C using a new avuzlysis imd experimental procedure. The results are: D, has also been determined fm cua4 at 870°C, and the values found are 4.5 times larger than those measured by the grain boundary grooving technique for the same surface orientations. This difference is felt to result from the approximate nature of the mathematical solution used in the present work. Attempts to measure D, for silver on copper and silver surfaces indicated a means of matter transport different from surface diffision was dominant in moving tracer from the source out over the surface. Cnlculations and experiment both indicate that this is the flow of silver through the vapor phase which completely masks the much smaller flow due to surface diffusion. The previous self-difhsion studies of D, for silver and copper are discussed in terms of our own analysis and found to yield values of D, factors of lo5 or more greater than those found by the grain boundary grooving tech -nique. UNTIL about 5 years ago it was widely believed that the activation energy for surface diffusion, AH, , was less than that for grain boundary diffusion, AHb,, which in turn was less than that for diffusion through the lattice, AHz.' This was concluded from various evidence that D,> Db>Dl, and one tracer study of D, for silver on silver from which AH, was inferred.2 In 1959 Mullins and Shewmon demonstrated that D, could be determined from the kinetics of the growth of grain-boundary grooves.3 Using this procedure, Gjostein measured D, on copper between 800" and 1050°C and found that the activation energy was roughly equal to AHl .4 Subsequent work on copper,5" silver,',' and goldg between the melting temperature T, and 0.87 T, confirmed that AH, as determined using the grain boundary grooving or scratch-relaxation technique was equal to or greater than AHz. During the same period, Drew and Pye again determined AH, for silver on silver using a tracer techniquelo and a mathematical solution similar to that of Nicker son and arker.' Though the values of D, Drew and Pye measured at any given temperature were about 200 times smaller than those reported by Nickerson and Parker, they again found a low activation energy of about 10 kcal, or about one fifth that found at the higher temperatures with the mass transport technique. A distinguishing characteristic of these two previous tracer studies is that they have worked at low temperatures (-1/2 T,) where they felt volume diffusion was negligible and then analyzed these data as if all tracer atoms leaving the source flowed out into and remained in a homogeneous high-diffusivity surface layer of undefined thickness. This is totally different from the model used in the mass-transport studies or the studies of grain boundary diffusion, which assume the high-diffusivity surface layer to be only a few angstroms thick. If this latter model is applied to the earlier tracer studies, it is shown that the tracer has really pe!etrated into the lattice a mean distance of 1000A. Thus the tracer distribution observed after an anneal is thought to be due to the combined effects of surface and volume diffusion. Independent of the relative validity of the two models, it seems evident to us that any comparison of the values of D, as determined in these two ways is meaningless and misleading, since the values of D, and AH, obtained in these two ways would be totally different for the same physical distributions of tracer. Once the fundamental difference in the approaches of the two techniques is established, we are faced with the question of which model better approximates physical reality. Here all the evidence seems to be on the side of the ''thin surface layer" analysis. In fact, the authors of Refs. 2 and 9 do not argue for the "thick-layer model" we have described; they simply invoke it through the equation they use to calculate D, . The primary evidence for the thin-film approach is: a) grain boundary grooves and scratches widen in proportion to tU4 and Mullins' rigorous analysis shows that this is only valid for a surface layer which is quite thin relative to the width of the groove;11 b) all accepted or seriously discussed models of solid-vapor interfaces and high-angle grain boundaries assume that the disturbed region of the interface is at most a few a0 thick. With the above in mind, it was desirable to determine D, using a radioactive tracer and a "thin-

Jan 1, 1964

By D. V. Edmonds, C. J. Beevers

Tensile tests were carried out on a! titanium containing 850, 1250, and 2700 ppm 0, and up to -500 ppm H. The tests were performed at -196", -78", 20°, 150°, and 300°C at a strain rate of -1.0 x 10??3 sec-1. Increasing oxygen content, increasing grain size, and decreasing test temperature resulted in enhanced embrittlement of the a titanium by the hydrogen additions. Metallographic observations showed that this can be correlated with the influence of these parameters on the introduction of cracks into the a! titanium by fracture of titanium hydride precipitates. CRAIGHEAD et al.1 reported that the hydrogen content normally found in commercial-purity a! titanium (60 to 100 ppm) was sufficient to cause a substantial lowering of the impact strength, and they attributed this embrittling effect of hydrogen to the precipitation of titanium hydride. Lenning et al.&apos; found that in commercial-purity a titanium there is an almost complete loss of impact strength at about 200 pprn H, which is approximately half the value needed to eliminate the impact strength of high-purity a titanium. They also showed that the presence of 3000 ppm hydrogen reduces the room-temperature tensile ductility of commercial-purity material to a value of the order of 10 pct; the corresponding hydrogen concentration for high-purity titanium is over 9000 ppm. It thus appears that the detrimental effect of hydrogen on the mechanical properties of commercial-purity titanium becomes evident at much lower hydrogen contents than for high-purity titanium. The main difference between the two types of a titanium might be expected to be the higher level of interstitial impurity in the commercial-purity grade. Jaffee et a1.3 studied the influence of temperature and strain rate on the hydrogen embrittlement of high-purity and commercial-purity ! titanium. In general, the behavior was the same for both materials; embrittlement was enhanced by decreasing temperature and increasing strain rate. Recent results from tests on commercial-purity a titanium containing 850 ppm O and varying amounts of hydrogen up to -500 ppm showed that the degree of embrittlement by hydrogen is intimately related to the fracture characteristics of titanium hydride precipitates.4 The present paper considers the interrelationship between the mechanical properties and micro-structural features of commercial-purity a! titanium containing 850, 1250, and 2700 ppm 0 and varying amounts of hydrogen up to -500 ppm. 1. EXPERIMENTAL PROCEDURE Three types of commercial-purity titanium supplied by IMI* were used in the investigation, and for the *Address: Witton, Birmingham 6, United Kingdom. purpose of this paper are designated Ti 115, Ti 130, and Ti 160. The principal impurity elements are given in Table I. The material was received in the form of 12.7 mm diam bars having a fully recrystallized structure. Tensile specimens with a round cross-section of 4.5 mm diam and a gage length of 15.2 mm were machined from the bars. In order to develop the same grain size (mean linear intercept of grain boundaries) in each of the three types the specimens were annealed under a dynamic vacuum of <10?5 mm Hg, Table 11. Specimen hydriding was carried out in a modified Sieverts apparatus;&apos; hydrogen was taken into solution at 450°C and after holding the specimens at this temperature for 24 hr they were furnace-cooled to room temperature at an average rate of -100 C deg per hr. By this method nominal hydrogen contents of 0, 50, 100, 250, and 500 ppm were introduced into specimens of Ti 115, Ti 130, and Ti 160 (100 ppm (wt) -0.5 at. pct). The actual hydrogen contents were calculated from the weight differences obtained by weighing the specimens before and after the hydriding treatment. Tensile tests were carried out at temperatures of -196", -78", 20°, 150°, and 300°C on a 10,000 kg In-stron machine at a nominal strain rate of -1.0 x 10-3 sec-1. Fractured specimens were sectioned in planes parallel to the tensile axis, mechanically polished to 0.25 µm grade of diamond paste, and then attack polished using a solution containing by volume 99 parts H2O, 1 part HF, and 1 part HNO3. Although the latter treatment unavoidably opened out cracks and voids visible after mechanical polishing, it did reveal the grain structure, titanium hydride morphology, and deformation twinning structure.

Jan 1, 1970

By J. R. Cahoon, H. W. Paxton

The mechanical properties of unidirectionally solidified A1(rich)-Mg and A1(rich)-Cu castings containing up to 15 wt pct solute have been determined with re -spect to the volume fraction of interdendritic eutectic. Pioperties were determined in the directions pumllel and Perpendicular to that of solidification; the volume fraction of eutectic was varied between the "as-cast" and equilibrizcm amounts by approperiate heat treatment following solidification. The principles of fiber strengthened composites and dispersion strengthened materials are adapted to explain the mechanical properties of these castings. It is generally accepted that castings often have inferior mechanical properties when con~pared to wrought products. However, there is little quantitative data available concerning the factors which make apparently sound castings weak and/or brittle. The relative ease and inexpensiveness of the casting process have always been attractive and, therefore, an understanding of the factors which contribute to the mechanical properties of castings would seem desirable. Such an understanding may lead to an improvement in the mechanical properties to an extent where castings would become competitive in applications where presently only wrought products are considered to have the requisite properties. Such an understanding could also improve the reliability of present cast products. Much of the recent research on castings has centered about determining the extent of segregation in cast alloys. Macrosegregation, particularly inverse segregation, has been studied in some detail 1-8 and a considerable understanding of microsegregation has been obtained.9&apos;10 The effect of solidification rate on dendrite spacing and on the amount of interdendritic eutectic in binary alloys has been established, particularly for Al(rich)-Cu alloys.""0 However, the extension of these ideas to relate the amount of interdendritic eutectic, concentration gradients, micro-segregation, dendrite spacings, and so forth, to the rnechanical properties has been limited. Dean and spear" have related the mechanical properties of an Al-Si-Mg alloy, A356-T62, to the dendrite spacing and have shown that the mechanical properties improve with decreasing dendrite spacing. Passmore et al.12 have shown that annealing at high temperature improves the mechanical properties of Al(rich)-Cu al- loys and Archer and Kempf 13 have shown that an Al-1 pct Mg-1.75 pct Si alloy behaves in a similar manner. Ahearn and Quigley 14 have shown that high temperature homogenization also enhances the mechanical properties of an SAE 4330 steel. However, in the above investigations, no underlying reasons were suggested for the improvement in mechanical properties. The purpose of the present investigation is to relate the mechanical properties of castings to some of the solichfication variables and to derive some equations by which calculations of the mechanical properties may be attempted. In particular, the effect of the amount of interdendritic eutectic and the effect of stress direction with respect to that of solidification on the mechanical properties will be considered. The Al(rich)-Mg and Al(rich)-Cu binary alloy systems were chosen for study. The A1-Mg system was chosen because its constitutional relationships are such that large volunles of eutectic (up to 24 vol pct) may be obtained in the as-cast condition and then be completely dissolved by subsequent heat treatment at about 440°C. This allows a comprehensive study relating the mechanical properties of castings to the amount of interdendritic eutectic. Also the Al(rich)-Mg eutectic is almost a single phase 15 which should make the experimental results more amenable to theoretical interpretation and calculation. The A1-Cu system was chosen for study because of the large amount of related information available concerning segregation, dendrite spacing, and so forth. Unidirectionally solidified castings were used throughout the investigation so that the effect of solidification direction with respect to the direction of applied stress could be determined. THEORETICAL It is well known that upon solidification of binary alloy castings, the nonequilibrium amount of eutectic which forms is given by 10 where fe o is the weight fraction of eutectic, Cs is the solid solubility of solute at the eutectic temperature, k is the equilibrium partition coefficient, and C, is the average composition of the alloy. In the development of Eq. [I], it is assumed that the effects of inverse segregation and diffusion in the solid are negligible, and that no porosity is present. If the casting is homogenized at a high temperature for a long period of time, some (or all) of the eutectic is dissolved and the amount of eutectic for this "equilibrium" condition may be calculated directly from the constitutional diagram. By appropriate intermediate annealing, the

Jan 1, 1970

By B. E. Eakin, R. T. Ellington

An apparatus and a procedure for determining the viscosity behavior of hydrocarbons at pressures up to 10,000 psia and temperatures between 77 and 400° F are described. The equipment is suitable for measuring viscosity of either the liquid or vapor phases or the fluid above the two-phase envelope for systems exhihiting retrograde phenomena, according no the phase state of the system within these ranges of temperature and pressure. Equations are developed for calculation of viscosity from the experimental measurements, and new data for the viscosities of ethane and propane at 77° F are reported. INTRODUCTION With the advent of higher pressures and temperatures in industrial processes and deep petroleum and natural gas reservoirs, demand has increased for accurate values of physical properties of hydrocarbons under these conditions. Proportionately, more frequent occurrence of natural gas and condensate-type fluids is encountered as fluid hydrocarbons are discovered at greater depths. This increases the importance, to the reservoir engineer, of being able to predict accurately the physical properties of light hydrocarbon systems in the dense-gas and light-liquid phase states. Reliable gas viscosity data are limited primarily to measurements made on pure components near ambient temperature and at low pressures. Few investigations have been reported for high pressures, and except for methane, data on light hydrocarbons are subject to question. This is demonstrated by the large discrepancy between sets of data on the same component reported by different investigators. For mixtures in the dense gas and light liquid regions and for fluids exhibiting retrograde behavior there are very few published experimental data. Viscosity data for methane have been reported by Bicher and Katz,1 Sage and Lacey,12 Comings, et al,3 Golubev,3 and Carr,3 with good agreement among the last three sets of data. Comings, Golubev and Carr utilized capillary tube instruments for which the theory of fluid flow is well established. The theory permits calculation of the viscosity directly from the experi- mental data and dimensions of the instrument alone. Sage and Lacey, and Bicher and Katz used rolling-ball viscometers. The theory of the rolling-ball viscometer has not been completely established, and these instruments presently require calibration by use of fluids of known viscosity behavior before viscosities of test fluids can be measured. To obtain accurate data it is necessary that the rolling-ball viscometers be calibrated by use of fluids of density and viscosity similar to the test fluids, a difficult selection for the gas phase. From the methane data and experimental tests on various natural gases, Carr developed a correlation for predicting the PVT behavior of light natural gases.2,3,4 This correlation was based on data for a very limited composition range; its application to rich gases and condensate fluids is questionable. The object of this investigation is to develop an instrument which can be used to obtain viscosity data at reservoir temperatures and pressures, for rich gases, condensate-type systems above the two-phase envelope and light liquid mixtures. These data will be used in an effort to develop correlations to represent the viscosity behavior of these fluids. APPARATUS In a previous viscosity study Carr2 utilized a modified Rankine capillary viscometer configuration," Fig. 1. In this instrument the gas to be tested is forced through the capillary tube in laminar flow by motion of a mercury pellet in the fall tube, the measured displacement time being that required for the mercury slug to move between the brass timer rings. The viscometer is constructed of glass and mounted in a steel pressure vessel. The test gas pressure in the viscometer is balanced by an inert gas (usually nitrogen) in the vessel. Excellent results have been obtained with instruments of this type, with Carr2 and Comings5 reporting repro-ducibilities of 99.5 to 99.3 per cent and an estimated absolute accuracy of 99 per cent. However, these instruments have limitations which have precluded their use for liquids. The need for maintaining a balance between pressures of the test fluid and inert gas in the viscometer vessel presents operating problems, and requires charging the test fluid to the viscometer very slowly. The principle drawback to the Rankine unit is behavior of the mercury slug which provides the pressure differential across the capillary. When even trace quantities of propane or heavier hydrocarbons are present in the test gas, the mercury tends to subdivide

By Neils Hansen

The microstructure of dispersion-strengthened aluminum aluminum-oxide products containing from 0.2 to 4.7 wt pct of aluminum oxide has been examined by optical and transmission electron microscopy, and the flow stress has been determined at room temperature and at 400C by tensile testing. Products were examined as recrystallized and as high-temperature extruded, and the microstructures consisted of a fine dispersion of oxide particles in a matrix divided by respectively recrystallized grain boundaries and subgrain boundaries. The flow stress (0.2 pct offset) at room temperature of recrystallized dispersion strengthened aluminum aluminum-oxide products is the superposition of dispersion strengthening and grain boundary strengthening. This superposition has been found to be linear. The flow stress (a) can be related to the grain size (t) by the Petch equation: ing content of oxide and k is a constant independent of the oxide content. For extruded products a similar relation has been found by replacing the grain size by the subgrain size. The k-value is of the same order for the two types of structure, which shows that the subgrain boundaries are as effective slip barriers as grain boundaries. Tensile testing at 400C of re-crystallized and extruded products shows that oxide dispersion strengthening is very effective, whereas the strengthening effect of grain boundaries and subgrain boundaries is small. THE microstructure of dispersion-strengthened products consists of hard particles finely distributed in a metal matrix. The strengthening effect of the dispersed phase has been fairly well established,1 and it has been found that the size and volume fractions of the dispersed particles are important structural parameters. However, in many dispersion-strengthened products which have been worked and heat-treated during manufacture the matrix is divided into well-defined grains or sub-grains, which may also have a strengthening effect. A model of the matrix strengthening in dispersed products worked during manufacture has been proposed,2 introducing the energy of the structure as a strengthening factor, especially at low temperatures. A difficulty in this model is, however, to relate this (stored) energy to the structural parameters directly observable as for instance grain size. The strengthening effect of the matrix grain size after recrystallization has been in- vestigated for nickel-thoria (TD-Nickel) products3 and for copper aluminum-oxide products. Conclusive results were, however, not obtained as the grain size of TD-nickel was constant. 5 to II , after recrystallization at temperatures from 700 to 1200°C and as the copper products containing 5 to 1 wt pct of aluminum oxide could not be recrystallized even after severe cold reduction and heat treatment at 1050C. For aluminum aluminum-oxide products containing from 1 to 5 wt pct of aluminum oxide it has been shown that the tensile strength at room temperature decreases when an extruded product is cold-worked and recrystallized. The matrix in the extruded products is divided into well-defined subgrains of micron size, and as the grain size of the recrystallized products is about two orders of magnitude higher, it is obvious that grain boundary strengthening occurs. Preliminary results8 have indicated that the flow stress containing no grain boundaries, A is a constant and t is the subgrain size. At elevated temperatures the effect of boundaries is more complex; it has been shown11 that recrystallized products having an oxide content of about 3 wt pct are more creep resistant than extruded material in the temperature range 400° to 600°C, whereas on application of a higher strain rate the tensile flow stress (0.2 pct offset) is higher in extruded than in recrystallized aluminum—5 wt pct aluminum oxide products at temperatures from room temperature to 427°C (800), Finally it has been shown12 that the Brinell hardness at 350°C of extruded products having about the same content of aluminum oxide increases with decreasing grain size, determined by X-ray line-width measurements. The present study was undertaken to obtain a quantitative relationship between the tensile strength and the grain size of aluminum aluminum-oxide products in the recrystallized as well as in the extruded state. The tensile testing was performed at room temperature and at 400uC. The grain size of the recrystallized products was varied by changing the degree of cold-work preceding the recrystallization heat treatment. In extruded products grain (or subgrain) size variations were obtained by high-temperature heat treatment after extrusion. EXPERIMENTAL a) Materials. Aluminum aluminum-oxide products have been manufactured by consolidation of aluminum powder covered with a layer of aluminum oxide formed during powder manufacturing. The products examined were manufactured from atomized powder containing

Jan 1, 1970

By E. H. Sellards

ON Oct. 9, 1929, a sink formed in the Sour Lake salt dome oil field in Texas, and on Oct. 12 a second smaller sink formed at the north margin of the first. The purpose of this paper is to give such observations as it has been possible to make on the earth movement incident to this subsidence. Sour Lake salt dome is typical of the salt domes of the Gulf Coastal Plain of Texas. Structurally the dome is a plug of salt which rises to within 900 ft. or less of the surface. Above the salt is a cap rock consisting of anhydrite with more or less calcium carbonate. The salt plug, as contoured on the cap rock, is circular in outline with, however, some appreciable irregularities. Overlying the cap rock are relatively uncompacted sediments consisting of sand, clay and gumbo.. At the crest of the dome these deposits are no more than 700 or 800 ft. thick. However, the sides of the dome are steep, and the sediments thicken rapidly away from the crest. The sink formed about 1500 ft. northeast of the crest of the dome where the sediments overlying the cap rock are from 1000 to 1200 ft. thick. The cavity permitting the subsidence was quite certainly either in the cap rock or in the salt below the cap rock, so that the sink was formed by the caving of as much as 1000 or 1200 ft. of earth.

Jan 1, 1930

By J. A. Retty

IN the Labrador iron fields two concessions, totaling nearly 24,000 square miles, have been staked out and commercial-grade deposits delineated. The Newfoundland-Labrador concession, owned by the Labrador Mining and Exploration Co. Ltd., is a 20,000-square-mile tract in the upper basins of the Hamilton and N askaupi Rivers which drain into Lake Melville. The New Quebec licensed area is 3900 square miles, owned by the Hollinger North Shore Exploration Co. Ltd., lying to the northwest of the northwestern part of the Labrador concession. It includes the upper basin of the Swampy Bay River and part of the upper basin of the Whale River, both of which drain into Ungava Bay. Both of the above-named companies are controlled by Hollinger Consolidated Gold Mines Ltd. with The M. A. Hanna Co., of Cleveland, holding a minority interest. When exploration was first undertaken in 1936, the only published map of the area was that prepared by A. P. Low in 1895. It showed only the main watercourses and gave only a rough, general idea of the geology. The numerous lakes of this vast area had to be first sketched and then mapped. Since then, extensive geological and topographical surveys have been conducted by the Labrador company, work which is normally done by Government branches. The object of the work was to examine the area and gradually eliminate unfavorable or less favorable prospecting ground. With this object in view, geological

Jan 1, 1948

By T. E. SCHTVARZ

THE publication of the report by Mr. F. L. Ransome was welcomed by many engineers who had mined in the heart of the Sail Juan country, braved its long and snowy winters, climbed its lofty peaks, run the gauntlet of its snow-slides, and studied its problems of geology, while making dividends for their English or American clients. This report helps one to understand why the bonanzas occurred, and why the inevitable borrasca presents itself where least expected. The Red Mountain district of Ouray county, a very productive section from 1884 to 1893, occupies considerable space in the report mentioned.. The character of the ore-occurrence, being distinctive and presenting many features not existing elsewhere, has been deserving of special study. It is to be regretted that Mr. Ransome was .unable to observe the conditions underground, as all the principal properties, many of which I opened and developed, were closed at the time of his investigation: It has been my privilege to have contributed a few brief papers recording my observations in developing these properties ; and it is the object of the present paper to present certain sections of the Yankee Girl mine, which throw additional light on the geology of the section and make the available data more complete. The main Yankee Girl chimney or " stock" was the most productive for the first 500 ft. in depth of any chimney in the district.

Mar 1, 1905

By D. C. DERINGER

METALLURGISTS and mill operators appreciate, in a general way, .the economic or commercial relationship between recovery and grade of product but few have correlated in detail fluctuating metal prices with the metallurgy. They know that many factors such as metal price, dedusiions for returning charge, transportation, percentage of metal in head ore, etc.; all affect the commercial relationship between recovery and grade of product. In practically every mill some one at some &apos; time has calculated the amount of recovery that can be sacrificed for each percentage increase in grade of concentrate and from this calculated ratio the commercial or ., economic tail has been established. Such a ratio finally becomes a well-entrenched rule by which the progress of the metallurgy is judged.. When once established, these-, ratios are but seldom corrected to changes of metal prices for each possible grade of concentrate that may be produced. The calculation is tedious when often repeated. Other methods have been suggested and used to correlate the commercial with the metallurgical phase. A factor .derived ,by multiplying the grade of concentrate by recovery is often used, but is of little importance because it does not possess a single commercial quantity. The percentage monetary recovery calculated by dividing the gross value of the ore into the net smelter return gives a good economic index and, is to be commended, but it is difficult to correlate exactly and quickly the work of each day on a commercial basis.

Jan 1, 1931

By Cornelius F. Kelley

EVERY man connected with the mining industry should take a significant pride in the fact that he belongs to an industry and to a profession that, from the beginning, has been constructive. The miner digs his ore and he gives the metal to art, to industry, and to commerce. The nature of our business is destructive only in that we deal with a wasting asset. That should be a source of great pride to those who belong to the profession. But unfortunately, the product of our mines, our smelters, and our re- fineries does not always go to constructive purposes. There are times when, in the administration of the affairs of men, our product chiefly goes to purposes which are destructive. When we look upon the panorama of horror that is being enacted throughout the world today, we wonder whether any effort toward the development of civilization and culture and education and well-being has been worthwhile. We are appalled to see the things that have been developed, through the application of science, toward progress and efficiency, now used for the catastrophic destruction of those things which are the most valuable that man has built. We must find hope that this is but an episodic thing; that it must, in the infinite wisdom of the Almighty, usher in a period of peace and progress, of civilization and development that will make man&apos;s existence upon earth worthwhile.

Jan 1, 1941

By D. Jenkins

THE Franklin Laboratory was designed mainly for the analysis of the products from the two concentrating mills situated at Franklin and Sterling Hill, the most important determinations being the zinc, iron, manganese, lime, moisture and silica contents of the ores. Within the last 4 years, however, it has been found advisable to examine most of our supplies, and therefore additional space and equipment was allotted for the examination of such substances as oils, greases, soaps, alloys, fuels, paints, explosives and water. The building as shown in elevation (Fig. 1) and plan (Fig. 2) consists of a main or routine laboratory, an experimental laboratory, a water FIG. 1.-WEST ELEVATION. analysis room and the other accessories such as stock room, library, sampling and drying rooms and office. The main laboratory is further divided into a balance room and zinc analysis room. As the greater part of our determinations are volumetric, good light is a very important factor and with this in view the interior walls of the building were constructed of white enameled brick laid in Keene cement. These also have the additional advantage that they give a clean and attractive appearance to the room. The windows are large, being 76 by 44 in. and even on very dark days the light is good throughout the whole laboratory. Our zinc titration requires a constant light and as, on many days, especially in winter, the light is variable, we installed two Artificial

Jan 8, 1917

By John V. Beall

When the mineral seekers came, they brought romance, excitement and, too often, transitory riches. It has been so for uncounted centuries. While the rich ore lasted, living was high and money flowed-mostly out of town. The whole creation was like a circus. The headframe went up like the center pole of the big top. The reduction works was an ingenious affair; an opportunity for self-expression by the mining engineer on the job. When the high grade gave out or the bottom dropped out of the market, the whole show folded. Machinery was scavenged for the next location. About all that was left were the raw footings, like giantsteps on the hillside; and the headframe above the silent diggings. Mostly, the people went away too. Arizona Territory was like that at the turn of the century. It can still happen. But, in copper, the age-old pattern has been disrupted. From Mineral Park in the northwest to Chino in the east and Cananea in the South, a growing number of companies have emerged-large, stable, productive. Southwest copper is truly a mighty industry, accounting for one fifth of world new copper production. In this period of scientific development, changes are fast, often dramatic. But even mining engineers, or possibly more so because they have an intimate knowledge of the industry, fail to appreciate the evolutionary changes that have shaped Southwest copper into what it is today.

Jan 10, 1965

By J. S., Douglas

IN 1880, the late James Douglas, LL.D., was superintendent of the Chemical Copper Co., operating the Hunt & Douglas process for the treatment of the siliceous copper ores of the Jones mine at Phoenixville, Pa. In conjunction with this a refining furnace was operated. After correspondence with Ben Williams, of Bisbee Ariz., who was commencing the mining and smelting of the Copper Queen ore. Dr. Douglas decided-to make his first journey to Arizona. While making plans for the trip lie visited a friend in Philadelphia, a .Mr. Logan, a prominent lawyer. He, through Professor Treadwell, brother of the discoverer of the great Treadwell gold mine of Douglas Island, Alaska, had an option with his min¬ing partner, Mr. Lenig, on the Eureka and Wade Hampton claims near the headwaters of the Verde River in Yavapai County, Arizona. These two claims, later the source of practically all of the wealth of the Jerome district, were then owned by C. P. Head and Co. Prescott merchants. Hugo Richards, banker, and formerly sutler at Camp Apache; Rod and John McKinnon prospectors and Nova Scotians; and perhaps one or two &apos;other owners of minor interests. Mr. Logan, hearing of Dr. Douglas intended trip to Bisbee, asked him to go first to see the two mining prospects, and this, Douglas, in need of the $500 fee, agreed to do as the time on the option on the claims was running short.

Jan 1, 1935

By A. L. Pranatis, G. M. Pound

Changes in length of copper foils of varying thickness and grain size were measured under such conditions of low stress and high temperature that it is believed that creep was predominately the result of interboundary diffusion of the type recently discussed by Conyers Herring. The surface tension of copper was calculated and results confirmed previous work within the limits of experimental error. Under the assumption of viscous flow, viscosities were calculated as a function of temperature and grain size. Predictions of the Nabarro Herring theory of surface grain boundary flow were borne out fully and the Herring theory of diffusional viscosity is strongly supported. ONLY a relatively few techniques for obtaining the surface tension of solids are presently available. Of these, the simplest and most straight forward is the direct measurement of surface tension by the application of a balancing counterforce. Thin wires or foils are lightly loaded and strain rates (either positive due to the downward force of the applied load or negative if the contracting tendency of surface tension is sufficiently greater than the applied stress) are observed. By plotting strain rates against stress, the load which exactly balances the upward pull is found and a simple calculation yields a value for the surface tension. The technique is of comparative antiquity, and solid surface tension values were reported by Chapman and Porter,&apos; Schottky; and Berggren" in the early part of the century. Later, the filament technique became fairly well established as a method for determining the surface tension of viscous liquids, and Tammann and coworkers,&apos;. " Sawai and co-worker and Mackh howed good agreement between the values of surface tension for glasses and tars obtained by the filament technique and by more conventional methods. With the increased confidence in the technique gained in these experiments, the method was applied to solid metals and the first reliable values of surface tension of solid metals were reported by Sawai and coworkers10&apos; " and by Tammann and Boehme." More recently, Udin and coworkersu-&apos;" have reported the results of experiments with gold, silver, and copper wires. Similar experiments with gold wires were carried out by Alexander, Dawson, and Kling.&apos;" The excellent review articles of Fisher and Dunn" and of Udinl@ should be referred to for detailed criticism of the foregoing work and for discussion of underlying theory. In all the foregoing calculations, it is assumed implicitly that the material contracts or extends uni- formly along the length of the specimen and also that it flows in a viscous fashion, i.e., that strain rates are proportional to stress. For an amorphous material, such as glass, tar, or pitch, the assumptions are quite valid and good agreement is obtained with values of surface tension measured by other techniques. The values reported for metals, however, are occasionally regarded with misgiving, since it can be argued that, because of their crystalline nature, true solids can not deform in a viscous fashion. If this is true, then the results reported for solid metals over a long period of years are of only doubtful value. Thus it is clearly necessary that a mechanism be established that would explain both the viscous flow and the uniform deformation that has been assumed. Such a mechanism has been proposed by Herring."&apos; Briefly, he suggests that, under the conditions of the experiment, deformation takes place by means of a flow of vacancies between grain boundaries and surfaces. This is a direct but independent extension of the theory proposed by Nabarro" in an attempt to explain the microcreep observed by Chalmer~.In a condensed form the Herring viscosity equation is TRL there 7 is the viscosity, T the absolute temperature, R and L grain dimensions, and D the self-diffusion coefficient. In its complete form, all constants are calculable and it includes such factors as grain shape, specimen shape, and degree of grain boundary flow. When applied to existing data, good agreement was obtained between predicted and observed flow rates. The theory received provisional confirmation from the work of Buttner, Funk, and Udin" who observed viscosities in 5 mil Au wire much higher than those in the 1 mil wire used by Alexander, Dawson, and Kling.&apos;" More significant were the completely negligible strain rates found by Greenough" in silver single crystals. Opposed to these observations were those of Udin, Shaler, and Wulff&apos;" who found indications of viscosity decreasing as grain size increased. Thus, complete confirmation of the theory was lacking in that the data to which it could be applied contained only a limited number of grain sizes. Hence, it was proposed that a series of experiments be carried out with thin foils of varying grain size up to and including single crystals, where, according to the Herring theory, deformation would occur only at almost infinitely slow rates.

Jan 1, 1956

By V. Pasupathi, R. E. Hummel, J. W. Koger

Specimens of P1 brass were plastically deformed at room temperature to various degrees of deformation and subsequently cooled in order to transform them to low-temperature martensite. Deformation shifts Ms. A, , and the temperature of minimum resistivity to lower temperatures, and also decreases the temperature coefficient of electrical resistivity. These properties change rapidly up to about 15 pct reduction but vary very little with higher deformation. The possible relationships between martensite formed by deformation and the M, temperature of low-temperature martensite are discussed. Evidence is given that deformation martensite delays the formation of low-temperature martensite. BETA&apos; brass undergoes at least two different types of martensitic transformations. One of these transformations (B1- B2) was first observed by Kaminski and ~urdjumov&apos; and occurs when 81 brass with a zinc content between 38 and 42 wt pct (quenched from the single-phase region) is cooled below room temperature. Jollev and Hull&apos; determined the structure of 0" from X-ray and electron-diffraction data as ortho-rhombic. Kunze came to the conclusion that the super-lattice cell of 0" is one-sided face-centered triclinic (pseudomonoclinic). The second martensitic transformation (B1-A1) occurs when the specimens are deformed at or somewhat above room temperature. This type of martensite will be called deformation martensite. Horn-bogen, Segmuller, and Wassermann4 determined the structure of deformation martensite to be bct. (An intermediate phase, az, occurs before the final phase appears.) At deformations higher than 70 pct, a, transforms into a.4 A critical temperature Md exists above which no transformation occurs during deformation and is estimated to be around 400°C in P1 brass.5 This martensite has elastic properties.6 When the sample is stressed, martensitic plates appear; when the stress is released, the plates disappear. The present paper studies the effect of deformation martensite on the formation of low-temperature martensite. The experiments involved samples of 8, brass which were plastically deformed by various amounts and were subsequently cooled below the transformation temperature. EXPERIMENTAL PROCEDURE The 13 brass investigated was made from 99.999 pct pure copper and 99.9999 pct pure zinc and contained 38.8 wt pct Zn. The specimens, consisting of foils 0.1 mm in thickness, were heat-treated at 8&apos;70°C for 15 min in an argon atmosphere and then quenched into ice water. They were then deformed by cold rolling and subsequently cooled at a rate of 1°C per min. The martensitic transformation that occurred during cooling was followed by electrical resistivity measurements. The resistance measurement technique and its accuracy have been described in a previous paper. Because the transformation 81 —-8" occurs below room temperature, the samples were placed in a cryo-stat which contained isopentane as a cooling medium. The isopentane was cooled by liquid nitrogen pumped under pressure through a 15-ft coil of copper tubing which was immersed in the isopentane. The nitrogen flow was regulated by a temperature controller using two thermistors in the cooling medium. The cryogenic liquid could be heated with an immersion heater. The useful temperature range with this device was from +25° to approximately -155~C. EXPERIMENTAL RESULTS Resistivity Measurements. The following abbreviations are used in this paper to label the characteristic temperatures during the martensitic transformation. M, is the starting point of the martensitic transformation and is defined as that temperature where the resistivity vs temperature curve on cooling first deviates from a straight line. Mf is the temperature at which the martensitic transformation is completed. On reheating, the transformation from martensite to the parent phase starts at a temperature A, and ceases at a temperature Af. Fig. 1 presents five different resistivity vs temperature curves corresponding to the transformation of brass from Dl to 8" after different degrees of reduction in thickness. The following observations can be made from these curves. 1) With increasing degree of deformation the Ms temperature is shifted to lower temperatures. This shift ranges up to 35°C compared to the undeformed state. This is also indicated in Fig. 2, where AM, (the shift of Ms, compared to the undeformed state) is plotted vs the degree of deformation. AM, increases rapidly until a reduction of about 15 pct is reached. With higher deformations, no additional increase in AM, was found. 2) With increasing degree of deformation the temperature of minimum resistivity (M) is also shifted to lower temperatures. The shift, attains a maximum of about 61°C compared to the undeformed state. In Fig. 3, AM is plotted as a function of deformation. It can be seen that, as in 1 above, AM increases rapidly and no further shift of M occurs for deformations greater than 15 pct. 3) The temperature coefficient of resistivity, is given by the slopes (dp/dT) of the linear portions of

Jan 1, 1969

By E. Lifshin, R. E. Hanneman

QUANTITATIVE applications of the electron micro-beam probe frequently involve the evaluation of complex mathematical expressions and/or the analysis of large amounts of experimental data. The purpose of this communication is to describe briefly a versatile and useful computer program system that is applicable to analyze rapidly a wide variety of practical microprobe problems. This system consists of a group of ten FORTRAN programs that can be stored on tape, cards, or in the memory disc of the computer. These programs, or links, can be run individually or in any prespecified sequence without interrupting the operation of the computer or without destroying information which is being transfered from one link to another. For the program system described here a GE-235 computer with disc storage was used, so that the DCHAIN method of program linking was employed. Included in the library are programs to: 1) initiate analysis of a new set of data and transfer control between all other programs in any predetermined manner; 2) generate theoretical calibration curves of composition vs relative intensity; 3) generate empirical deviation parameters from least-square fits of experimental calibration data from standards of known composition; 4) convert raw X-ray data to corrected composition; 5) determine inter diffusion coefficients by Matano analysis of con centrat ion -distance data on a uniaxial diffusion couple; 6) determine activation energies and frequency factors of temperature-activated processes such as diffusion; and 7) generate calibration curves for determination of the thickness of thin films using microanalysis. A detailed description of these computer programs and their underlying principles is available on request from the authors."&apos; The first program to generate theoretical calibration curves of corrected relative intensities vs composition uses the Poole and Thomas atomic number correction&apos; and the Philibert absorption factor&apos; with a voltage-dependent mass absorption coefficient for electrons in the alloy. A modified Castaing fluores- cence correction is also used which includes the effects of both Ka and KO radiation and over voltage.&apos; Once the theoretical curves have been calculated in 1 wt pct intervals, these results are least-squares fit to obtain Ziebold deviation parameters&apos; which are stored in COMMON in the computer memory. The net discrepancies between the original theoretical calibration curve and the regenerated curve using the Ziebold parameter are computed. Although this link is explicitly written for K-K fluorescent interactions, it can be applied to K-L, L-K, and L-L interactions as previously disc~ssed."~ Similar programs have also been written to utilize the Wittry fluorescence correction, Birks combined corrections, and various other corrections.&apos; These modified programs have proved to be quite useful for quantitative comparisons of the results of the various theories. The program for conversion of raw X-ray data to corrected composition includes corrections for drift, backround, and instrumental dead time. The corrected intensities are converted to composition by use of the Ziebold equation"2 and parameter obtained from the program system. The results can be obtained for either atom or weight fractions. In addition to accurately computing interdiffusion coefficients the Matano analysis program calculates least-square smoothed values of concentration, concentration gradient, and curvature for each point on the raw input concentration profile. In order to obtain high accuracies a unique method of performing a least-square polynomial fit to incrementally advancing profile segments which overlap is used.&apos; This program has been successfully modified for use in ternary diffusion problems3 and can readily be modified to handle analysis of diffusion profiles which include phase boundary discontinuities. This link is generally applicable to analysis of interdiffusion data obtained by other techniques as well as by the microprobe. The primary function of the next program is to least-squares fit experimental diffusion data to the normal Arrhenius function: D = Doexp(-Q/RT), to obtain values of Do and Q. In addition the probable error and one, two, and three u statistical confidence limits of DO, Q, and log D are evaluated. This program is also directly useful for analysis of any other simple temperature-activated processes including conductivity, and certain deformation and chemical processes. The program to generate calibration curves for film-thickness determination using the microprobe is based on a numerical integration of the equation derived by Cockett and ~avis.&apos; Values of film thickness obtained by this program for copper on various substrates are in good agreement with measurements made by other techniques. Versions of the above program system have been prepared for use with or without a remote teletype connection to the computer for processing on either a real-time or time-share basis. The instrumentation coupling a microprobe to a teletype for automatic data collection and analysis by the presently described program system has been reported elsewhere by the authors.&apos; If teletype equipment is not used to communicate with the computer, standard methods of card reading and tape reading can be used. In either

Jan 1, 1967