By Louis A. Carapella, William E. Shaw

MAGNESIUM and its alloys have long been characterized as possessing limited capacity for mechanical forming at atmospheric temperatures prior to rupturing despite their outstanding performances in this respect at elevated temperatures. Responsible for this behavior are the fundamental facts that these hexagonal-type metals have comparatively few slip elements at low temperatures for any extensive deformation and that, at high temperatures, additional slip elements become operative, thus enhancing greater plasticity under strain. The transitional point has been set at 225°C by Schmid1 for single crystals, and at 250°°C by Morell and Hanawalt2 for extruded magnesium metal. In a recent X-ray investigation on polycrystalline magnesium-alloy sheets, Barrett and Haller3 have revealed that, below the transitional temperature, the initial plastic deformation proceeds mostly by a twinning action; that, above such a temperature, the action is mostly by slip. The deep-drawing performance of the magnesium + 1.5 pct alloy sheett over a wide range of temperatures has been investigated by Weber and Vanden Berg,' and their results are presented in Fig r. It should be noted from this work that a maximum drawability of about 25 pct at room temperature has been obtained on this alloy under the conventional deep-drawing operations. For the same alloy, it is now possible to augment the cold drawability to about 40 pct by a process to be disclosed. Hitherto, this value has been obtained only by deep-drawing the alloy at around 230°C. That greater plastic flow is attainable at atmospheric temperatures on magnesium under certain deformational techniques was discovered by the authors6 in their analyses of plastic-deformational behaviors of pure magnesium. This fact is best illustrated in Fig 2 from the Hargreaves analysis6 performed by the authors under two different modes of loading. For direct test, a separate unstrained specimen was used for each load duration, whereas for the integrated test the same specimen was employed for all the five intermittent loadings so that the load duration was made additive throughout the investigation. The higher plastic flow-rate at room temperature, as designated by the Hargreaves constant S, was obtained by the integrated or intermittent loading procedure. The authors5 in further tests showed that, under such a procedure greater plastic flow was also realized with a progressive increase in deformational loads. These findings have been applied

Jan 1, 1947

By Harold B. Janzen, M. A. Nobles

Campbell and Martin1 described a new exploratory logging tool which was developed as the result of a new concept of the phenomenon that takes place when a porous formation containing mobile hydrocarbons and irreducible interstitial water is invaded by mud filtrate. They postulate that invasion will create a bank of interstitial water between the flushed zone and the undisturbed formation. This postulate was confirmed by Wyllie.' Thus, if R,, is greater than R, and mobile hydrocarbons are present, the resistivity profile with increasing radii from the borehole is high:low:high, as shown in Fig. 1. If mobile hydrocarbons are absent, the bank of interstitial water is indistinguishable from the undisturbed formation and the resistivity profile, when R is greater than R,, is high:low, as shown in Fig. 2. The zone containing the bank of interstitial water and residual oil was named the "low zone". Campbell and Martin conducted extensive electrolytic wedge and resistivity analog model studies to select a logging system that would reflect the presence or absence of the low zone. The system they selected was that of a family of lateral curves. The model studies indicated that the presence of a low zone could be detected in approximately 60 to 70 per cent of the producing sand reservoirs with a family of lateral curves provided that the sonde effectively occupies 90 per cent of the diameter of the hole. These studies were conducted with D, = 5d. The presence or absence of the low zone is best determined by a plot of the apparent resistivity vs spacing as shown in Figs. 3 and 4. A dip or inflection in the profile that repeats at successive depth intervals is considered diagnostic. To reduce the shunting effect of the hole and mud, a sonde of insulating material that is surrounded by a series of flexible rubber bumpers was designed. The bumper efficiency is considered to be the ratio of the bumper diameter to the hole diameter. Field tests conducted by Campbell and Martin on 10 wells with a tool that provided for station readings indicated that dips or inflections could be detected in 19 out of 25 known producing zones. INSTRUMENT DEVELOPMENT Halliburton developed a logging system to simultaneously and continuously record eight lateral curves. The instrumentation is described in the literature.' The original logs made

By D. S. Eppelsheimer, D. N. Williams

The compression texture of iodide titanium is determined and found to consist of a [0001] texture rotated 15° to 30° from the axis of compression. As the amount of reduction increases, the angle of rotation decreases. The 0001 rotation showed a slight preference for a <1010> rotation axis. RECENT investigation of the cold rolled texture of titanium&apos; has shown this metal to exhibit a new type of rolling texture. This texture can best be described as a (0001) [10i0] with the 0001 planes rotated approximately 30" to the transverse direction around a <10i0> rotation axis. Rather good results in explaining the cold rolled texture have been obtained by other workers&apos; by examination of the tension and compression textures. No information was found giving the tension texture of titanium. Generally the tension texture of a hexagonal close-packed metal is identical with its wire texture. The drawn texture of titanium has been investigatedh nd has been found to be predominately [10?0]. Since this is the common tension texture of hexagonal metals of low c/a ratio, the explanation of the difference between the rolling texture of titanium and the rolling texture of other hexagonal metals is not indicated by examination of the tension texture. Therefore, the compression texture of titanium should be particularly important in the explanation of the unusual transverse rotation of the 0001 planes found in the cold rolled texture. The compression texture of titanium was examined by Yen.",&apos; His results showed titanium to exhibit the usual [0001] texture up to 85 pct reduction. At higher reduction a double texture appeared in which the 0001 planes were rotated from 10" to 30" from the plane of compression. This change in the compression texture seemed unusual since the tendency for hexagonal close-packed metals is to approach the [0001] texture as the idea compression texture. Mechanical twinning generally occurs over a considerable range of reductions beginning at a rather low reduction. The samples used by Yen in his investigations were prepared by two methods. Compression in a testing machine was used up to a reduction of 85 pct. Compression by compression rolling was used at higher reductions. Since the change in texture occurred at the same reduction as the change in the method of compression, a connection between the two seemed likely. To check this possibility and to locate the position of the change in texture definitely, if it was found to exist, the compression texture of titanium was re-examined. An iodide titanium crystal bar (99.9 pct Ti) produced by the New Jersey Zinc Co. and donated by the Titanium Alloy Manufacturing Div. of the National Lead Co. was used in this investigation. Procedure The investigation of the compression texture was carried out in three steps; compression, specimen

Jan 1, 1953

By H. L. Talbot, A. J. Hall, R. S. Young

A METHOD for the chemical differentiation of oxidized cobalt from sulphide cobalt in complex mine and concentrator products is of considerable interest to a number of mining companies throughout the world. At Rhokana Corporation, in Northern Rhodesia, for instance, cobalt is found chiefly in the sulphide form, as carrollite, but a cobalt oxide mineral also occurs irregularly underground, and relatively small quantities in the mill feed from time to time are difficult to detect it visually at the concentrator. The oxide cobalt is not amenable to the sulphide flotation process used at Rhokana and nearly all of it passes into the tailing. The occasional. period when high tailing losses occur with no appreciable change in the cobalt content of the mill feed has naturally been disturbing to the concentrator staff, who had no means of determining whether an influx of cobalt oxide ore or laxity on the part of the mill flotation operators were responsible for these results. A procedure for determining oxidized copper minerals, based on their solubility in dilute sulphuric acid saturated with SO2, has been used for many years in the copper industry. In the presence of cuprite the procedure fails, but otherwise it gives results quite satisfactory for control purposes. Empirical methods for determining oxidized forms of zinc and lead have been proposed, but they are generally unsatisfactory except in isolated cases of a very simple ore. No published procedure for determining oxidized forms of cobalt or similar elements has come to the authors&apos; notice. EXPERIMENTAL PROCEDURE There are obviously two alternatives in attacking a problem of this nature. One is to employ a solvent for oxide cobalt that will not dissolve cobalt sulphide. The other is, to find a substance capable of oxidizing the cobalt sulphide to sulphate, which of course is water-soluble and can then be leached from the water-insoluble oxide cobalt. A representative sample of Rhokana cobalt oxide ore was secured, ground to minus 200-mesh, and carefully rolled to furnish a standard sample for this work. The analysis of this material gave the following percentages: Co, 0.55; Cu, 1.64; Fe, 2.98; S, 0.08; SiO2, 41.42; A1203, 11.20; CaO, 13.82; MgO, 3.80. As a source of cobalt sulphide a similar large sample of carrollite was prepared, analyzing Co, 23.36 per cent; Cu, 27.32; and S, 31.13. This sample of course was not pure carrollite, but was the best obtainable in quantities sufficient for a standard intended for considerable work. It was a pure sulphide sample, microscopic examination showing only carrollite, a little bornite, and gangue, with no visible sign of oxidized ore present. A wide variety of reagents were used in an effort to selectively dissolve oxide cobalt or to oxidize sulphide cobalt to

Jan 1, 1946

By J. L. Green

Virginia-Carolina Chemical Corp., in its Florida Operations, uses both roller mills and ball mills in dry grinding of phosphate rock. The roller mills have been in operation since 1954 in the Mining Department. The ball mills were installed and put in operation in 1960 in the Harding Concentrate Superphosphate Plant. The roller mills in the Mining Department are used to grind phosphate rock for outside customers. This involves short notice orders of varying grinds, grades and types of rock. The ball mills grind phosphate rock for use in V-C&apos;s own phosphoric acid and concentrated superphosphate plant. These mills grind generally two types of rock for one grind. In 1959, a 10% speed-up was made in the operating speed of the roller mills. This paper deals with the operational gains and resulting cost savings which evolved from this speed-up, and compares the present operations of the roller mills and of the ball mills in grinding phosphate rock. In January 1959 it was decided to determine the feasibility of reducing the grinding cost on the roller mills, per ton of rock ground, by speeding up the mill 10%. At this time, one mill was completely reconditioned so it would be in top condition. Extensive tests were then run both before and after the mill speed-up to determine the resultant cost savings. These tests showed that, due to this 10% speed-up, the mill capacity was increased approximately 20% and grinding power costs per ton were reduced approximately 10%. Table I shows the results of these tests. Each test run actually represents several of the same type rock and grind, averaged together. Each test run lasted approximately three hours. The validity of these runs has been confirmed by subsequent operation in grinding over 1,000,000 tons of phosphate rock. Accurate records have been kept on power consumption and repairs as well as tons produced. Two types of feed rock were used for the tests — pebble phosphate rock and flotation phosphate concentrate rock. The pebble phosphate rock size is approximately 80-90% plus 20 mesh. The flotation concentrate phosphate rock size is approximately 15% plus 20 mesh and 95% plus 100 mesh. The same two types of rock feed were used for all the test runs. Test Nos. 1, 2, and 3 were run at the original mill speed of 85.5 rpm on the vertical shaft. Test No. 1 was run with a feed of high grade flotation concentrates; the desired fineness attempted was 70% passing 200 mesh. Tests No. 2 and No. 3 were run with a feed of low grade pebble. Test No. 2 was run for a desired fineness of 70% passing 200 mesh. Test No. 3 was run for desired fineness of 50% passing 200 mesh.

Jan 1, 1963

By William A. Johnson

The fundamental role of diffusion in many reactions occurring in solid metals has long been recognized, and there have been careful measurements of rates of diffusion in numerous alloy systems; but our understanding of the atomic mechanism by which diffusion occurs is scarcely in an advanced state.l-3 It is doubtful that this mechanism can ever be directly ascertained; rather, all imaginable mechanisms must be examined and the one that is in best accord with such data as can be obtained from suitably chosen experiments should be selected. Because of its relative simplicity, diffusion in a system containing only one kind of atomic species—commody called self-diffusion—is of considerable theoretical interest. It may be expected that diffusion theory will not be advanced appreciably until a wide variety of diffusion experiments—of which diffusion in a chemical concentration gradient and self-diffusion are two important types—are carefully performed and inter-compared. Aside from the purely theoretical interest in self-diffusion measurements, such studies will be of considerable engineering importance. The rate of any process in a pure metal requiring the movement of atoms, of which recrystallization and creep are two familiar examples, will be understood more readily with the aid of self-diffusion data.† Self-diffusion implies the diffusion of something into its exact counterpart; the detection of such a process is patently impossible, and it is necessary to substitute for it the diffusion of one isotope (in this case radioactive) into another isotope (in this case stable) of the same chemical element. There is, however, no reason to suppose that a radioactive atom will not diffuse at the same rate as its stable isotope, for all of the isotopes of the same element have exactly the same chemical properties; neither the difference in nuclear energy nor the difference in mass would be expected to exercise an important influence in this phenomenon. In this sense, self-diffusion may be thought of as the diffusion of radioactive atoms down a radioactivity concentration gradient, just as usual diffusion is the diffusion of one kind of atom down its chemical concentration gradient. The first measurements of self-difiusion were made by von Hevesy4-6 using the radioactive lead isotope thorium B in ordinary lead. The recent development of means for producing artificial radioactive elements has made possible similar measurements on gold,7, 8 copper,2, 9 and zinc.10, 11 Many of the data that have been obtained are rather poor, and no adequate reason has been given for their poorness; it appears, however, that the unsatisfactory results are characteristic of the particular experimental procedure employed, and not of self-diffusion measurements in themselves. The experimental technique that has yielded the poorer results is the deposition of a thin layer of radioactive atoms on the surface of a specimen and the determination of the rate of inward diffusion

Jan 1, 1941

By William A. Johnson

The fundamental role of diffusion in many reactions occurring in solid metals has long been recognized, and there have been careful measurements of rates of diffusion in numerous alloy systems; but our understanding of the atomic mechanism by which diffusion occurs is scarcely in an advanced state.l-3 It is doubtful that this mechanism can ever be directly ascertained; rather, all imaginable mechanisms must be examined and the one that is in best accord with such data as can be obtained from suitably chosen experiments should be selected. Because of its relative simplicity, diffusion in a system containing only one kind of atomic species—commody called self-diffusion—is of considerable theoretical interest. It may be expected that diffusion theory will not be advanced appreciably until a wide variety of diffusion experiments—of which diffusion in a chemical concentration gradient and self-diffusion are two important types—are carefully performed and inter-compared. Aside from the purely theoretical interest in self-diffusion measurements, such studies will be of considerable engineering importance. The rate of any process in a pure metal requiring the movement of atoms, of which recrystallization and creep are two familiar examples, will be understood more readily with the aid of self-diffusion data.† Self-diffusion implies the diffusion of something into its exact counterpart; the detection of such a process is patently impossible, and it is necessary to substitute for it the diffusion of one isotope (in this case radioactive) into another isotope (in this case stable) of the same chemical element. There is, however, no reason to suppose that a radioactive atom will not diffuse at the same rate as its stable isotope, for all of the isotopes of the same element have exactly the same chemical properties; neither the difference in nuclear energy nor the difference in mass would be expected to exercise an important influence in this phenomenon. In this sense, self-diffusion may be thought of as the diffusion of radioactive atoms down a radioactivity concentration gradient, just as usual diffusion is the diffusion of one kind of atom down its chemical concentration gradient. The first measurements of self-difiusion were made by von Hevesy4-6 using the radioactive lead isotope thorium B in ordinary lead. The recent development of means for producing artificial radioactive elements has made possible similar measurements on gold,7, 8 copper,2, 9 and zinc.10, 11 Many of the data that have been obtained are rather poor, and no adequate reason has been given for their poorness; it appears, however, that the unsatisfactory results are characteristic of the particular experimental procedure employed, and not of self-diffusion measurements in themselves. The experimental technique that has yielded the poorer results is the deposition of a thin layer of radioactive atoms on the surface of a specimen and the determination of the rate of inward diffusion

Jan 1, 1941

By James Terry Duce

In order to facilitate interpretation of the data in this chapter, we print the following excerpts from circulars to authors, compiled by Mr. Frank A. Herald when he was Vice-chairman for Production of the Petroleum Division, and revised in 1939. Generally in Table 1 the unit for prescntation of data is a field. For our purposes a field is defined as the whole of a surface area wherein productive locations are continuous. Such unit commonly includes and surrounds nonproductive areas. Such unit commonly includes a great variety of geologic conditions—several units of continuous productive reservoirs of distinctly different structure and of distinctly different stratigraphy. Therefore it is hoped that our authors will subdivide "field" so as to enable students to make analyses that may have scientific and /or commercial value. As to each spacc in the tabulation, it is citller (1) not applicable, (2) the proper entry is not determinable, (3) the proper entry is determinable, but not determinable from data available to the author, (4) the proper entry is determinable by the author. In spaces not applicable, the author will please draw horizontal lines; in spaces where the proper entries are not determinable, the author will please insert x; in spaces where the proper entries are detcrminable but not detcrminable from data available to the author, the author will please insert y; in spaces where the proper entries are determinable by the author he will, of course, make such entries. Generally, y implies a hope that in some future year a definite figure will be available. Inability to determine precisely the correct entry for a particular space should not lead the author to insert merely y. Contributions of great value may be made by the author in many cases where entries arc not subject to precise determination. In such rases the author should use his good judgment and make the best entry possible under the circumstances. For many spaces, the correct entries represent the opinion of the author (for example, "Area Proved") and in such cases the entries need not be hedged to such extent as in cases where the quantities are definite yet can be ascertained only approximately by the author. In cases under definite headings but where figures are only approximate, the author may use x. For example, if the total production of a field is known to be between 1,800,000 and 1,850,000, the author may report 1,8xx,xxx; or if the production is between 1,850,000 and 1,900,000, the author may report 1,9xx,xxx. Where a numeral is immediately to the left of x or y, such numeral represents the nearest known number in that position. As to quantity of gas produced from many fields the question will arise as to whether the figures should include merely the gas marketed or should include also estimates of gas used in operations and gas wasted. Although rough approximations

Jan 1, 1939

By William A. Johnson

THE fundamental role of diffusion in many reactions occurring in solid metals has long been recognized, and there have been careful measurements of rates of diffusion in numerous alloy systems, but our understanding of the atomic mechanism by which diffusion occurs is scarcely in an advanced state 1-3 It is doubtful that this mechanism can ever he directly ascertained, rather, all imaginable mechanisms must be examined and the one that is in best accord with such data as can be obtained from suitably chosen experiments should be selected Because of its relative simplicity, diffusion in a system containing only one kind of atomic species-commonly called self-diffusion-is of considerable theoretical interest It may be expected that diffusion theory will not be advanced appreciably until a wide variety of diffusion experiments-of which diffusion in a chemical concentration gradient and self-diffusion are two important types-are carefully performed and inter-compared Aside from the purely theoretical interest in self-diffusion measurements, such studies will be of considerable engineering importance The rate of any process in a pure metal requiring the movement of atoms, of which recrystallization and creep are two familiar examples, will be understood more readily with the aid of self-diffusion data † Self-diffusion implies the diffusion of something into its exact counterpart, the detection of such a process is patently impossible, and it is-necessary to substitute for it the diffusion of one isotope (in this case radioactive) into another isotope (in this case stable) of the same chemical element There is, however, no reason to suppose that a radioactive atom will not diffuse at the same rate as its stable isotope, for all of the isotopes of the same element have exactly the same chemical properties, neither the difference in nuclear energy nor the difference in mass would be expected to exercise an important influence in this phenomenon In this sense, self-diffusion may be thought of as the diffusion of radioactive atoms down a radioactivity concentration gradient, just as usual diffusion is the diffusion of one kind of atone down its chemical concentration gradient The first measurements of self-diffusion ii ere made by von Hevesy4-6 using the radioactive lead isotope thorium B in ordinary lead The recent development of means for producing artificial radioactive elements has made possible similar measurements on gold,7,8 copper,2,9 and zinc 10 11 Many of the data that have been obtained are rather poor, and no adequate reason has been given for their poorness, it appears, however, that the unsatisfactory results are characteristic of the particular experimental procedure employed, and not of self-diffusion measurements in themselves The experimental technique that has yielded the poorer results is the deposition of a thin layer of radioactive atoms on the surface of a specimen and the determination of the rate of inward diffusion

Jan 1, 1941

By W. C. Coffin

Fire-brick stoves have become a necessary part of the modern coke blast-furnace equipment, and are also superseding the cast-iron pipe stoves in anthracite- and charcoal-furnaces. The brick stoves in general use are of either the Cowper or Whitwell type, or modifications of these bearing the names of those who invented the alterations from the original types rather than any real departure from then]. All these stoves have approximately the same valve-equipment and follow the same line of operation. The waste gas from the furnace enters at one port and burns in a single combustion-chamber, and the heated products are drawn through the various passe; in the brickwork to a stack of proper height to create the necessary draught. The last passes of these stoves receive a very small percentage of the heat from the gas, owing to their extreme distance from the combustion-chamber; and this chamber also suffers great deterioration in the attempt to force the heat into the farthest passes. At best, about 70 per cent. of the heat taken up is held in the combustion-chamher and the first down-pass of the Whitwell stoves. Mr. Hugh Kennedy, Manager of the Isabella Furnaces, Pittsburgh, Pa., who has had a large experience with the fire-brick hotblast stoves, was so strongly impressed with the fact that but about thirty per cent of the brick of the average stove were doing proper duty as heat-agents, that, after careful study and experiment, he had three 20- by 60-feet stoves constructed with a view of more uniformly heating all the brick. In these the general lines of the Whitwell stove are followed, with the blast-connections unaltered, but gas is introduced at the bottom of each pass, and outlets are provided at the top, so that the gases have a direct natural draught in each pass and the highest heats are obtained at the bottom instead of the top. The natural tendency being toward the reverse condition, the brickwork soon acquires an almost uniform temperature.

Jan 1, 1893

By A. J. Mortlock

Cobalt and nickel have been diffused at tracer concentrations in gold at several temperatures in the range from approximately 700° to 950°C. The diffusion penetration profiles were determined by a serial sectioning technique in which the gold is first anodized and then the anodic layer is dissolved in acid. In this ulay sections as thin as 250A could be removed reproduci-bly. In all cases, the region close to the specimen surface was characterized by irregular behavior in the sense that the logarithm of concentration was not linear in the square of the penetration distance. In sotne cases, there zuas an indication of the operation of very slow dijfusion in this region, while in others the apparent diffusion coejj&apos;icient was negative. Possible reasons for this anomalous behavior are briefly discussed. In recent years it has been found that the region close to the surface of a metal can sometimes exhibit anomalously slow diffusion characteristics relative to the interior of the metal. One of the best examples of this fact is the work of Styris and omizuka,&apos; who showed that the apparent diffusion coefficient for zinc in the region withi: about 1 p of the free surface of copper was about ,,,, that at deeper penetrations. This result is particularly interesting, because it is free from the possibly complicating effects of low solubility of the diffusing tracer in the solvent metal. In the case of diffusion under conditions of low solubilitjr, interpretaticn of the results in terms of lattice diffusion is difficult because of the enhanced short-circuiting produced by segregation to dislocations.2&apos;3 Measurements by Duhl et 1. suggest that cobalt diffusing in gold may also show a near-surface effect of this type. Once again the solubility is high, so that this result could be of great interest. However, the technique used for analyzing the diffusion penetration zones by Duhl, viz. the counting of residual gamma activity in the specimen following sectioning, appears to have indicated a near-surface effect in a parallel experiment on the self-diffusion of gold reported at the same time. The latter result is known to be spurious, since Kidson5 has demonstrated that self-diffusion in gold does not show this effect. Duhl et 01. also reported some measurements on the diffusion of nickel in gold, but failed to give any data for the near-surface region. As the solubility of nickel in gold is high, such data would also be of special interest. We, therefore, decided to conduct another set of experiments on the diffusion of nickel and cobalt in gold, using a sectioning technique that allows the individual sections to be assayed for solute content and thus gives direct determinations of penetration profiles. Also, by sectioning with an anodizing/stripping tech- nique, very thin layers can be removed and the region close to the surface studied in detail. MATERIALS The gold specimens were supplied as single crystal disks $ in. in diam by a in. high by Monocrystals Co. of Cleveland, Ohio. The gold itself was of spectro-scopic purity, i.e., better than 99.99 pct pure. METHOD Specimen Preparation. One flat end face of each gold crystal was spark planed with a Servomet spark erosion machine set for minimum spark energy. Following this treatment the crystals were preannealed for 2 to 4 days at temperatures of either 400" or 700°C. The three crystals preannealed at 700°C showed signs of recrystallization. The spark-planed end face of each crystal was then coated with the appropriate amount of 63i or 60 radioactive tracer. This deposit was laid down in a simple plating bath containing the as-supplied solution of the radioactive isotope as well as sufficient ammonium oxalate to saturate the solution. Some ammonium oxalate remained undissolved on the floor of the bath for this purpose. During plating further additions of ammonium oxalate were sometimes required to allow the plating to continue satisfactorily, perhaps due to passivation of the undissolved oxalate already present. The thickness of the deposited layer was determined by comparison of the apparent surface activity of the plated specimen with that of a similar specimen having a weighable deposit of the isotope on its end face. Correction for self-absorption of the radiation was made in this calculation. Annealing. The deposited crystals were annealed in a hydrogen atmosphere in sealed silica tubes. During this heat treatment they were supported, active face down, on optically flat silica plates. The temperature was measured with calibrated Pt vs Pt-10 pct Rh thermocouples, and the tabulated values can be taken to be correct to Z°C. All the crystals showed evidence of recrystallization following these heat treatments, suggesting that initially they may not have been good single crystals or had suffered strain during delivery. Concentration Profile Analysis. After annealing, the crystals were sectioned by the anodizing-stripping technique.6 The anodizing involved suspension of the specimen with its cylindrical axis horiz6ntal by a gold wire in a 200-ml beaker containing 1 M Hg304. A cathode in the form of a strip of gold sheet, 2 in. wide and positioned to be in contact with the curved side of the beaker, completely encircled the specimen. An anodizing current of 30 ma, corresponding to a current density of 5 ma per sq cm on the surface of the specimen, was passed for times ranging from 5 to 150 min depending on the thickness of gold to be removed; the solution was stirred continuously during this process. Following this treatment, the specimen

Jan 1, 1969

By J. T. Berling, J. B. Conway

MANY studies have been devoted to the correlation of low-cycle fatigue behavior. Several of these have also been concerned with the identification of an effective approach to the prediction of low-cycle fatigue behavior from short-term tensile data. Perhaps the first such approach was that reported by coffin1 in the form: where is the plastic strain range, Nf is the number of cycles to failure, and c is a constant characteristic of a material. In this analysis by Coffin it was reasoned that in a short-term tensile test the value of Nf could be considered as equal to a , in which case the value of c is interpreted as the tensile ductility, f, measured in such a test. If, therefore, the Coffin equation is assumed to be applicable to a given material, it is a simple matter to predict the low-cycle fatigue behavior. Once the tensile ductility is known, this point is located at Nf = 1/4 on a log-log plot of vs Nf and a line is drawn through this point with a slope of to yield a prediction for the fatigue life. Actually, while this equation is quite useful it is not generally applicable, for experiment has shown that the value of —$ does not reflect the relationship between and Nf for all materials or even for a given material over all temperature ranges. An equation similar to the Coffin equation was prepared almost simultaneously by Manson.2 This expression had the form: In this case the exponent on Nf was not assigned any particular numerical value in accord with the various values of this exponent which had been observed for different materials and at different test conditions. Because of this characteristic it will be recognized that little use can be made of this expression in predicting low-cycle fatigue results. A fairly effective expression for use in predicting fatigue behavior was proposed by Manson3 based on a study of numerous sets of experimental results. This relation (Method of Universal Slopes) makes use of modulus of elasticity, ultimate strength, and tensile ductility, and assumes an exponent on Nf equal to 0.6 in representing the plastic strain range contribution to total strain range. While this equation of Man-Son does not yield completely accurate results it must be recognized as being the best means available at

Jan 1, 1970

By A. B. Kinzel

THE demands of the petroleum and chemical industries for steels to be used in pressure vessels and similar structures at artificially low tempera-tures are continually increasing, and the writing of proper specifications with suitable tests becomes increasingly important. Likewise, the selec-tion of suitable steels for such applications is of increasing concern to the metallurgist. It is generally recognized that highly alloyed steels of the austenitic stainless type retain their properties even at very low tempera-tures and represent the best technological solution of the low-temperature steel problem. However, in many instances less expensive carbon or low-alloy steels suitable for service within limited temperature ranges are available. The problem thus becomes one of defining the various factors involved in the production and fabrication of these less expensive steels and determining the temperature ranges in which their properties justify engineering application. Most of the applications involve welded structures, and the heat effect of welding as well as the nature of the weld metal are matters of prime concern. The first problem that the metallurgist faces is the determination of the type of test to be used as a criterion of the performance of the steel in low-temperature service. It has been generally recognized that the static properties of steel as determined in the ordinary tensile test undergo a gradual and relatively slight change as the temperature of test is lowered in the range of current interest; i.e., from room temperature to minus 120° C. It is further generally recognized that the behavior of steel under impact involving notch sensitivity is definitely affected at the lower temperatures. While the major subject of this paper is the effect of grain-refining deoxidizers, of low-alloy additions and of welding on the low-temperature notched-bar impact properties, an inquiry into the general behavior of steel under low-temperature impact testing is included. This is a pertinent portion of the investigation and the results thereof are

Jan 1, 1937

By D. G. F. Hedley, D. F. Coates, K. Barron

INTRODUCTION Preceding papers presented in this symposium have considered the influence of various parameters, such as geologic structure, groundwater, etc., on the stability of rock slopes and have given some analyses and guide lines for slope design. To carry out such analyses it is necessary to put numbers to these parameters; where possible, this is best done on the basis of in- situ observation and measurement. Since none of the design analyses can be considered exact and since conditions vary during excavation, it is also desirable to monitor the behaviour of the slopes as the excavation proceeds. In this manner a feedback of information on the actual excavation conditions can allow a continuous reassessment of the design parameters to be made and can give early warning of incipient failures. The purpose of instrumenting rock slopes is thus to provide information which fits into one of two categories: (a) To give basic data to assist on-site assessment and design of the rock excavation. (b) To provide data for the control and assessment of safety during excavation. The purpose of this paper is to review briefly some of the instruments and measuring techniques available for gathering this data and to indicate where such data may prove useful. This is not a comprehensive review of all available instrumentation but, rather, is a survey of some of the instruments and techniques with which the authors have had some experience and which have proven useful. STRUCTURAL ASSESSMENT Whilst most structural assessment of a site is done on the basis of geologic mapping and core examination, there exists some instrumentation which can, in particular circumstances, assist in this assessment. Seismic instruments can be used to determine the geometry of formations and to give an indication of the relative competency of rocks. These instruments operate using seismic reflection or refraction techniques and, although mainly confined to shallow sub-surface exploration, can be useful in distinguishing between soil/ bedrock contacts and, in some cases, the extent of weathered surface rock.

Jan 1, 1971

By G. S. Tint, M. Herman, V. V. Damiano

Dislocation arrays and substructures were studied in cadmium doped zinc crystals using a newly devised etching technique. Cadmium precipitates delineating the dislocations were revealed by etching a surface closely parallel to the (0001) slip plane. Cinephotomicrography of the continuous etching process revealed the three-dimensional aspects of dislocations in the bulk crystal. Dislocation etch patterns were studied in both deformed and annealed crystals after suitable aging at room temperature. The effect of annealing was evidenced by a rearrangement of the dislocations into low-angle boundaries and hexagonal networks. ETCH pit techniques have been used extensively to study dislocations in both deformed and annealed bulk metal crystals. Ideally one hopes to obtain a one-to-one correspondence between the etch pits and the points of emergence of the dislocations at the surface. One then attempts to deduce the way in which dislocations are arranged in the bulk crystal from the arrangement of etch pits on the surface. It is clear that one can obtain only limited information of the dislocation configurations inside the crystal from etch pit studies of single surfaces. Considerably more information is obtained if one is able to follow the course of the dislocations through the crystal using progressive etching technique. Techniques of this sort were used by Gilmanl to study dislocations on the slip planes of NaCl crystals and by Damiano and Tint2 to study dislocation arrangement in zinc crystals grown from the melt. The present paper makes use of a technique first described by Tint and Damiano3 to observe and continuously record the dislocation structures which appear while a crystal surface was being progressively etched. Studies were made on cleaved (0001) surfaces to reveal the dislocations along their length on the surface closely parallel to the slip plane. The technique for revealing segments of dislocations along their length by etching is well known. Wilsdorf and Kuhlmann-wilsdorf4 revealed disloca- tions along their length in aluminum containing a few percent copper, when precipitates segregated along the dislocations. The technique was used by Low and Guard5 to study dislocation configurations on the slip plane in Fe-Si alloys containing carbon. In the present work the technique was applied to zinc containing cadmium since it was shown by Gil-man6 that a cadmium-rich phase could be made to precipitate from supersaturated solutions along dislocations in zinc. Segments of dislocations delineated by the precipitates were revealed by etching a surface prepared by cleaving the crystal. The three-dimensional nature of dislocations and substructures was thus studied from the cinephotomicro-graphic record of the continuous etching process. EXPERIMENTAL Single crystals of zinc containing the order of 0.1 pct Cd were prepared by slowly lowering a graphite crucible containing the melt through a temperature gradient of 15°C per cm at a rate of 1.5 X 10-3 cm per sec. "As grown" crystals were aged for periods of 1 month at room temperature, then cleaved in liquid nitrogen, and etched according to the procedure used by Gilman.&apos; The etchant containing 32 g of CrO3, 6 g of hydrated Na2SO3 in 100 ml of water behaved as a chemical polish for zinc and etch pits were produced at the site of precipitates or inclusions. After the precipitates or inclusions were removed from the surface, the etch pits left behind were eventually polished smooth. This behavior enabled one to continuously observe the surface while the specimen was immersed in the etchant. Best results were obtained when the specimen surface was vertical and the reaction products of polishing were continuously removed by gravitational convection. Some crystals were heavily deformed in excess of 25 pct strain, others were lightly deformed the order of a few pct by compression such that the deformation occurred essentially by basal glide. Some crystals were etched immediately after deformation, others were allowed to age at room temperature for several weeks prior to etching. Heavily deformed crystals were annealed at various temperatures and etched on the cleavage plane immediately after annealing, others were allowed to age at room temperature for several weeks prior to etching. The etched structures of deformed and annealed structures were studied. Similar experiments were conducted on 99.9999 pct pure zone refined Tadanac zinc crystals which

Jan 1, 1963

By G. G. Gunther, C. L. Boeke

(Any discussion resulting from presentation at the Los Angeles Extractive Metallurgy Division Meeting will appear in the November 1953 issue.) I. M. Symonds (Cia Minera de Penoles, Monterrey, N. L., Mexico)—This is a most interesting paper describing zinc deleading operations. Mr. Gunther was kind enough to show me his operation last fall. Outside of the excellent results, I was most impressed by the ease of control. I had expected a difficult operation requiring careful control and supervision, but found one requiring little attention. The only disappointing fact of the separation is the poor copper recovery in the concentrate of the deleading float. The final zinc concentrate still has about 3 pct chalcopyrite (assuming the copper is chalcopy-rite) which adversely affects the zinc grade. If the copper mineral is free, the poor recovery is probably due to the high cyanide concentration. Fortunately, about 75 pct of the copper is recovered before the pulp goes to the zinc circuit. Mr. Gunther&apos;s remarks about proper cyanide to zinc sulphate ratios cannot be overemphasized. Although our experience has been mostly confined to the conventional Pb-Zn separation, we have found these ratios most important, and more important in the mill than in the laboratory. The laboratory appears to give optimum results over a wider range of reagent control than the mill, especially in regard to the effect of cyanide. In the mill in handling relatively high grade ores, we usually find that ratios of cyanide to zinc sulphate of 1 to 10 or 20 or higher work best. Where there is a substantial amount of chalcopyrite present, it has been noted that cyanide in the range of 0.02 to 0.10 lb per ton of ore is often beneficial in zinc rejection and possibly in copper recovery in the lead concentrate, while larger amounts, say 0.20 to 0.25 lb per ton, will float more zinc and cause a serious rejection of chalcopyrite. On an ore with 15 to 20 pct Zn content, we have had to use 0.8 to 1.2 lb of zinc sulphate per ton of ore with the above cyanide to obtain optimum results. Sometime ago we made a laboratory study following Parral and Santa Barbara practice on an ore which never had a very satisfactory rejection of zinc in the lead concentrate. The results were not encouraging and a mill test was not run. Since then the study has been reopened using fresh zinc concentrate from the mill in the laboratory instead of one made in the laboratory. A reasonably clean lead float from the zinc concentrate was obtained. It has been checked several times and each time the zinc concentrate made in the mill responds and the one made in the laboratory does not. Although undoubtedly some reasonable explanations can be given, it is presented here only

Jan 1, 1953

By James Terry Duce

In order to facilitate interpretation of the data in this chapter, we print the following excerpts from circulars to authors, compiled by Mr. Frank A. Herald when he was Vice-chairman for Production of the Petroleum Division: Generally in Table 1 the unit for presentation of data is a field. For our purposes a field is defined as the whole of a surface area wherein productive locations are continuous. Such unit commonly includes and surrounds nonproductive areas. Such unit commonly includes a great variety of geologic conditions-—several units of continuous productive reservoirs of distinctly different structure and of distinctly dzerent stratigraphy. Therefore it is hoped that our authors will subdivide "field" so as to enable students to make analyses that may have scientific and/or commercial value. As to each space in the tabulation, it is either (1) not applicable, (2) the proper entry is not determinable, (3) the proper entry is determinable, but not determinable from data available to the author, (4) the proper entry is determinable by the author. In spaces not applicable, the author will please draw horizontal lines; in spaces where the proper entries are not determinable, the author will please insert x; in spaces where the proper entries are determinable but not determinable from data available to the author, the author will please insert y; in spaces where the proper entries are determinable by the author he will, of course, make such entries. Generally, y implies a hope that in some future year a definite figure will be available. Inability to determine precisely the correct entry for a particular space should not lead the author to insert merely y. Contributions of great value may be made by the author in many cases where entries are not subject to precise determination. In such cases the author should use his good judgment and make the best entry possible under the circumstances. For many spaces, the correct entries represent the opinion of the author (for example, "Area Proved") and in such cases the entries need not be hedged to such extent as in cases where the quantities are definite yet can be ascertained only approximately by the author. In cases under definite headings but where figures are only approximate, the author may use 2. For example, if the total production of a field is known to be between 1,800,000 and 1,850,000, the author may report l,8x,xxx; or if the production is between 1,850,000 and 1,900,000, the author may report 1,9xx,xxx. Where a numeral is immediately to the left of x or y, such numeral represents the nearest known number in that position. As to quantity of gas produced from many fields the question will arise as to whether the figures should include merely the gas marketed or should include also estimates of gas used in operations and gas wasted. Although rough approximations

Jan 1, 1937

By H. R. Hendricks

The ore of the Iron King mine, being very hard and having a very fine crystalline structure, presents many problems in milling that are not present in ordinary lead-zinc ores. This very fine crystallization causes much interlocking of minerals and is most prevalent between the gold and pyrite and the sphalerite and pyrite. The recovery of gold is extremely important in the economic value of the ore and therefore constitutes a large part of the metallurgical problem to be solved. All of the gold is free but it has not been observed in any of the mill products except under very high magnification. Some of the gold is tarnished, and this condition also makes recovery difficult. The gold values have been determined to be highest in association with chalcopyrite and arsenopyrite. The silver occurs mostly in association with galena and tennantite. A small amount of native silver has also been observed occasionally. The galena, being softer than the other minerals, frees much better in grinding. Some oxidation of galena is present in the ore, as the non-sulphide lead content amounts to approximately 10 pct of the total lead. Some oxidation of sphalerite is also present in the ore. Microscopic examination of the zinc concentrate shows many grains in the minus 325-mesh to be half pyrite, together with the fact that some of the zinc is marmatite, makes production of a high-grade zinc concentrate very difficult unless recovery is sacrificed. In the grinding, it has been determined that the flotation feed must be maintained at 85 pet minus 200-mesh to free the minerals sufficiently to make the best economic recoveries. Table I illustrates the effect of fine grinding. It shows that the bulk of the recovered minerals is in the minus 325-mesh size and is the part of the minerals that is more readily freed. The pyrite concentrate is not given in the table because it contains practically no minus 325-mesh. Development of Present Flowsheet and Milling Practice The first milling operation started in 1938, with a mill capacity of 140 tons daily, producing a bulk gold-silver-lead concentrate. After several stages of expansion and changes of the mill flowsheet, the mill is currently treating 380 tons of ore daily and three separate concentrates are produced. In order of their importance and value, these are: (I) lead concentrate, (2) zinc concentrate and (3) pyrite concentrate. The present average grade of mill heads is: gold 0.11 oz, silver 4.00 oz, lead 2.50 pet, zinc 7.60 pct, copper 0.22 pct, iron 22 pct and 30 pct insolubles. Specific gravity of the ore is 3.8. During the period when bulk flotation mas practiced, the flowsheet was very simple. The ore was ground fine enough to liberate as much gold, silver and lead as possible. Necessary collectors and frothers were added in sufficient quantity

Jan 1, 1949

By H. R. Hendricks

THE ore of the Iron King Mine, being very hard and having a very fine crystalline structure, presents many problems in milling that are not present in ordinary lead-zinc ores. This very fine crystallization causes much interlocking of minerals and is most prevalent between the gold and pyrite and the sphalerite and pyrite. The recovery of gold is extremely important in the economic value of the ore and therefore constitutes a large part of the metallurgical problem to be solved. All of the gold is free but it has not been observed in any of the mill products except under very high magnification. Some of the gold is tarnished, and this condition also makes recovery difficult. The gold values have been determined to be highest in association with chalchopyrite and arsenopyrite. The silver occurs mostly in association with galena and tennantite. A small amount of native silver has also been observed occasionally. The galena, being softer than the other minerals, frees much better in grinding. Some oxidation of galena is present in the ore, as the nonsulphide lead content amounts to approximately 10 pct of the total lead. Some oxidation of sphalerite is also present in the ore. Microscopic examination of the zinc concentrate shows many grains in the minus 325-mesh to be half pyrite, together with the fact that some of the zinc is marmatite, makes production of a high-grade zinc concentrate very difficult unless recovery is sacrificed. In the grinding, it has been determined that the flotation feed must be maintained at 85 pct minus 200-mesh to free the minerals sufficiently to make the best economic recoveries. Table I illustrates the effect of fine grinding. It shows that the bulk of the recovered minerals is in the minus 325-mesh size and is the part of the minerals that is more readily freed. The pyrite concentrate is not given in the table because it contains practically no minus 325-mesh. DEVELOPMENT OF PRESENT FLOWSHEET AND MILLING PRACTICE The first milling operation started in 1938, with a mill capacity of 140 tons daily, producing a bulk gold-silver-lead concentrate. After several stages of expansion and changes of the mill flowsheet, the mill is currently treating 380 tons of ore daily and three separate concentrates are produced. In order of their importance and value, these are: (1) lead concentrate, (2) zinc concentrate and (3) pyrite concentrate. The present average grade of mill heads is: gold 0.11 oz, silver 4.00 oz, lead 2.50 pct, zinc 7.60 pct, copper 0.22 pct, iron 22 pet and 30 pct insolubles. Specific gravity of the ore is 3.8. During the period when bulk flotation was practiced, the flowsheet was very simple. The ore was ground fine enough to liberate as much gold, silver and lead as possible. Necessary collectors and frothers were added in sufficient quantity

Jan 1, 1947

By J. W. Richards

Plating iron with copper has received great attention from practical and scientific men, but, aside from the deposit secured by immersion of iron in copper salts, by electro-plating, or by welding together thin sheets of iron and copper, these efforts have met with no success. Failure of these efforts, in the production of copper plating, has been due to the fact that the conditions normally and necessarily present in the plating operation are antagonistic to the production of copper-plated iron. In most, if not quite all of them, a bath of molten copper has been used. The temperature of a molten copper bath is so high that the iron becomes oxidized before it can be immersed in the molten copper, and unless a protective flux for the molten copper is used, the surface of the copper will become oxidized, and, in any event, the plated iron will oxidize immediately on its being withdrawn from the molten bath. I recently had the pleasure of visiting the works of The Metals Plating Co. at Elizabeth, N. J., where I witnessed the plating of iron sheets with copper by a new process.l The plating metal is applied to the sheet in the form of a liquid mixture by means of rolls, such as inking rolls. The sheet, after being coated with the mixture, is automatically carried forward and deposited on a link-belt conveyor, which carries it through a furnace maintained at a temperature well above that of molten copper. The basic principle involved in this method lies in the application of the plating metal to the sheet while the sheet is cold and then melting the metal in place on the sheet under conditions which are favorable to the formation of the plating. Plating Mixture The liquid plating mixture is composed of either copper oxide or finely divided copper, or a mixture of both, ground to the consistency of a light varnish in a crude oil having an asphaltic base, of a specific gravity of from 14" to 16&apos; Be. The plating mixture which gives the best results

Jan 1, 1919