By J. Grosso, D. J. Nagel

In many metallurgical studies, it is necessary to reveal the composition and structural properties of materials. Usually this is done by etching, but some substances do not etch well or easily. Anodizing is known to provide an alternate treatment in many cases. In general, this technique is simple, often more sensitive to composition differences than etching, has excellent resolution, and provides variable contrast in those elements and alloys which anodize. Here we report the use of anodizing in diffusion studies in the TiCb system. Fig. 1 shows a cross section of the diffusion zone in a TiCb couple. The anodizing has clearly revealed both composition and crystallographic features. The maximum bulk penetration of the titanium into the columbium is marked by a sharp line because of the steep concentration gradient. The titanium grain size and orientation differences are also evident. Variation in the grain size reflects the gradually decreasing columbium concentration.

Jan 1, 1967

By Arthur C. Simmons

In common with all other producing areas of the United States, Pennsylvania enjoyed increased activity and prosperity during 1937 (Table I). Prices of crude oil were better than for any year since 1930, and the Bradford average was $2.599, compared with an average price of $2.60 in 1930. Production and drilling activities were increased over 1936, although drilling for oil represented almost entirely a program of secondary development in both the water-flood areas and the air-gas repressuring areas. Bradford Oil Field The Bradford oil field continued to produce the major portion of Pennsylvania oil; however, no changes occurred in oil-production methods during 1937. Practically all of the production in the Bradford field is by water-flooding and the total number of oil and water wells completed within the area increased from 3205 in 1936 to 4112 in 1937; an increase of approximately one-third over 1936 completions. The percentage of water wells is approximately one-half of the total completions, although any specific five-spot development will have a proportion of 55 to 60 per cent water wells and 40 to 45 per cent oil wells. Offsetti~ig and boundary oil wells probably will result in a division or percentage of 50 per cent oil and 50 per cent water wells. The quoted figures for well completions include the entire Bradford field, approximately 12 per cent of which is in Cattaraugus County, New York. It is possible to make a segregation of production, but it is not possible to segregate well completions. Production in the Pennsylvania end of the Bradford field in 1937 totaled 15,076,000 bbl., or a daily average of 41,300 bbl. compared with a daily average of 37,000 hbl. in 1936.

Jan 1, 1938

By R. A. Flinn, John T. Norton

A CONSIDERABLE number of experiments in recent years have definitely established the fact that the internal friction or mechanical hysteresis of a metal under cyclic stress is a property that is highly "structure sensitive." Because of this fact, it has been suggested that an observation of this property, which often is referred to as "damping. capacity," might be a useful indicator of structural. changes taking place when a metal or alloy is subjected to any of a number of metallurgical treatments. Damping capacity is of interest to both engineer and metallurgist, but from a rather different point of view, and the information that each desires from such observations is of a different nature. The metallurgist is in search of various external indications of changes taking place in the interior of a metal; changes which are in themselves not directly observable. Even if the observed phenomenon cannot be explained in fundamental terms, it may be empirically related to certain characteristics of the material and prove of real value in research. Internal friction os mechanical hysteresis occupies such a position, and, although it is nor well understood in terms of basic metallic theory, an observation of itt changes can serve in a very useful capacity. Of course, there is nothing new in the measurement of damping, but the use of this property in metallurgical research constitutes a vast field, which has received all too little attention: The present work is essentially of an exploratory nature in this field and is an attempt to evaluate the process as a research tool. The phenomenon of age-hardening was chosen as a typical example of a structural change and one method of measuring damping was examined in considerable detail.

Jan 1, 1938

By J. W. Spretnak, G. W. King

THE crystallography and morphology of 0-Al,Fe precipitates in an A1 + 0.5 wt pct Fe alloy have been studied by transmission electron microscopy. The alloy was cast in cylindrical ingots, 15 cm in diameter and 60 cm in length, and cooled slowly. The measured composition was 0.527 wt pct Fe, 0.001 wt pct Mg, and 0.003 wt pct Cu. Spectrographic analysis revealed no additional trace impurities. Thin slices were cut from the ingot and reduced by more than 95 pct by rolling to a thickness of 0.1 mm with no intermediate annealing treatments. These thin sheets were then vacuum-annealed for 1 hr at 612°C and air-cooled in their capsules. Thin foils for examination in the electron microscope were prepared by electropolishing. The precipitate is found in the form of oval platelets on the (110) planes of the matrix. The major axes of the platelets are parallel to the (110) directions of the matrix, and vary in length from 1/2 to 2 p. The thickness is about 1/10 p. Examples of platelets, both in the plane of the foil and normal to the foil, are shown in Figs. l(a) and l(b), respectively. lack' found that ?-A13Fe (more correctly All13Fe4) belongs to the monoclinic system. Using Black's structural data and simultaneous electron-diffraction patterns from the matrix and precipitates, the habit planes and directions were determined to be: (00l)? || (110)Al [100]? || [001]Al The orthogonal crystallographic axes of the precipitates are accurately in the habit plane, while the measured coincidences of the directions are only within 10 deg. The major axis of the platelet is parallel to [010] in the 0. This orientation corresponds to the direction of nearest registry of the lattices.

Jan 1, 1964

By C. T. Eddy

The refining of native copper in the reverberatory furnace, as practiced in the Lake Superior district of Michigan, is very similar to the reverberatory melting and refining of cathodes, but the presence of arsenic in some of the copper concentrates renders the operation somewhat more difficult. Though the copper occurs as the native metal, which is often excep tionally pure—purer, in fact, than after it has undergone refining—its intimate association with the gangue minerals necessitates the cumbersome reverberatory treatment. The gangue consists chiefly of complex silicates of calcium, magnesium, iron, aluminum and sodium, but in certain ore deposits other minerals are often found, among them the native copper arsenides—mohawkite, whitneyite, algodonite and the like. These latter minerals, when present, because of their relatively high specific gravity (7.5 to 8.5), find their way into the concentrates through the gravity concentration processes employed in the recovery of the copper. When such concentrates are melted, the silicates are removed as slag, but, because of the great affinity of molten copper for arsenic, the arsenides dissolve more or less completely in the copper bath. Because of the stability of the resulting melt, the arsenic is tenaciously held in solution. The influence of arsenic on the properties of copper, especially on its electrical conductivity, is generally recognized. For certain uses it is beneficial, and in many instances its presence in limited amounts is not objectionable, but if the metal is to be used for electrical purposes, the almost complete removal of the arsenic is of prime importance. Considerable research has been done on the subject of the influence of arsenic on the electrical conductivity of copperll but the conclusions presented in the literature dealing with the problem show some disagreement. The methods now in use for the removal of arsenic have not

Jan 1, 1931

By J. L. Brimhall

Slip-line formation during bending has been studied on neutron-irradiated molybdenum single crystals. For equivalent strains, the slip lines are coarse and distinct in the irradiated molybdenum and not resolvable in the unirradiated molybdenum. The slip lines have been directly correlated with dislocation channels present in the irradiated and deformed thin foils. The heterogeneous distribution of the dislocations during deformation in the irradiated material results from dislocation interaction with the dejects produced during irradiation. Impurities , in the form of' carbides, affected the dislocation channeling Principally by acting as dislocation sources. ALTHOUGH the mechanical behavior of irradiated materials has been studied extensively, the precise mechanism of irradiation hardening has not been established. Some information on the microstructural species responsible for hardening of irradiated materials has been derived from direct and indirect observations. The direct observation of the structure of deformed irradiated metals, particularly by transmission electron microscopy, is a relatively new and unexplored area. Slip-line studies in fcc metals have been restricted primarily to copper.1-3 Very coarse slip lines, representing slip on many closely spaced planes, have been observed in deformed, irradiated copper. Coarse slip lines have also been observed in irradiated aluminum.4 Clear channels in irradiated copper caused by dislocation motion through the defect structure have been seen by transmission electron microscopy and correlated with slip lines.5-6 To date, little work has been reported on the irradiated bcc metals. Eyre described the slip lines around hardness indentations on irradiated iron and found them to be more distinct than lines in unirradiated material.' Mastel et al.' have observed channels in deformed irradiated molybdenum similar to those reported in copper. As part of a program concerned with the effect of neutron irradiation on metals, the slip-line

Jan 1, 1965

By J. M. Davey

Lead-zinc sulphide ores at Mount Isa are currently treated at the rate of 180,000 long tons per 28 day period in the No. 2 Concentrator of Mount Isa Mines Limited. Prior to June 1966 lead-zinc ore was treated in part of the No. 1 Concentrator up to a rate of 70,000 long tons per period. Since 1955, two major changes in ore type being processed have occurred. Because of these changes, problems arising from treatment of the ore have altered and during the period several major changes in practice have been advocated and experimentally tested. Most of these flow sheets were developed with a view to overcoming one major problem in the ore. These were invariably abandoned as the Mount Isa lead-zinc ore contains a number of equally major problems all of which must be overcome in the treatment process. MINERALOGY The orebodies are situated in the Mount Isa Shale Group which is Proterozoic in age (Carpentarian System). The sediments consist dominantly of fine grained dolomitic, quartzo-feldspathic shales and siltstones. Specifically, the Mount Isa orebodies lie in the Urquhart shale formation which is characterised by sediments of high albite and orthoclase content denoting a large volcanic component. The Urquhart shales are approximately 3,500 feet thick and extend at least north and south of Mount Isa for 20 miles in each direction. In the area of the silver-lead-zinc orebodies the Urquhart shales are highly pyritic and have a relatively high carbon content. The

Jan 1, 1970

By R. A. Pasternak, B. Evans

A dynamic technique for the determination of solubilities of gases in metals has been explored, using the N-Nb system as a test case. An initially clean sample, maintained at constant high temperature, is exposed to the gas at low pressure: the rate of sorp-tion and the corresponding change in sample resistance are measured continuously. A pronounced decrease in the slope of the resistance concentration curve is observed at the terminal solubility. The rate of gas uptake by the sample was determined in an ultrahigh-vacuum flow system equipped with a servo-control which maintains constant pressure in the sample chamber; the system and the technique have been described in detail elsewhere. 1,2 The sample was held at constant temperature during sorption by maintaining approximately constant power input into it; this results in constant temperature, since the emissivity of a metal is independent of moderate concentrations of dissolved gas. The simple electrical circuit used both for heating and for resistance measurement is shown in Fig. 1. The power input into the filament is where R is the filament resistance, RL is an adjustable resistance in series with the filament, and VT is the constant dc potential of the power source. If RL is set equal to R at the beginning of an absorption run, the power input becomes insensitive to subsequent resistance changes; for example, an increase of 20 pct in sample resistance is accompanied by a decrease in power input of less than 0.8 pct; i.e., the

Jan 1, 1967

By A. E. Bibb, F. W. Kunz

A platelet form of zirconium hydride was found in zirconium and ZY-1 wt pct U single crystals containing hydvogen in the range of 50 to 100 ppm. The habit planes for the hydride plateletg in the zirconium crystals were found to be {1012}, {1121}, and (1122) while the habit planes in the ZY-1 wt pct U crystals were {1121), {1123}, and (1.231). With the exception of the {1231} plane, these have been identified as the twin planes in zirconium. The different effect of hydridc on the mechanical puoperlies of zirconium at high and low strain rates has been explained in terms of the defornzation mechanism and the habit planes of the hydride. ZIRCONIUM and zirconium-base alloys are considered for many nuclear reactor applications, where the pick-up of hydrogen is a distinct possibility, if not an unavoidable occurrence. An excellent example of this is the absorption of hydrogen by zirconium and its alloys during aqueous corrosion, where as much as 30 pct of the hydrogen produced by the corrosion reaction is picked up by the metal. Under the proper conditions, the absorbed hydrogen would precipitate as zirconium hydride and consequently alter the mechanical and physical properties of the zirconium-base alloys. The knowledge obtained from a study of the crystallographic aspects of the hydride precipitation is necessary for the interpretation of the observed changes in the mechanical and physical properties. The deleterious effect of hydrogen on zirconium-base materials is not always observed in normal slow tensile loadings at or above room temperature, but becomes immediately obvious under impact loading, where the energy absorbed decreases with increasing hydrogen content,' and in notched specimens where triaxial loadings are attained.2 This effect is of serious consequence in the applications of Zr where shock loads or high strain rates are experienced. The purpose of this investigation was to determine the crystallographic planes of the Zr and Zr-1 wt pct U matrices upon which zirconium hydride will precipitate and to correlate these with the observed mechanical property data. PROCEDURE Crystal Growth—Single crystals of Zr and Zr-1 wt pct U alloy were used in this investigation. The Zr crystals were made from sponge that had a typical analysis as shown in Table I. Large grains were grown in this material by rapid cooling an arc-melted charge in a button furnace. This operation undoubtedly lowered the volatile impurity concentration below those listed in Table I. Back-reflection Laue patterns of these large grains showed the presence of considerable substructure and lattice distortion within each grain. It was found that an 18-day anneal in an argon atmosphere at 840°C (a high a heat-treatment) followed by furnace cooling, resulted in the further growth of the large grains and removed the detectable substructure ana lattice distortion. Equiaxed crystals with a cube edge of approximately 1/4 in. were produced in this manner. Large crystals of Zircaloy-2 (1.5 wt pct Sn, 0.15 wt pct Fe, 0.1 wt pct Cr, 0.05 wt pct Ni) also were produced by this technique but the large amount of substructure formed could not be removed by annealing. The Zr-1 wt pct U solid solution crystals were produced from an alloy rod consisting of Westing-house-Foote hafnium-free crystal bar zirconium and depleted uranium. The chemical analysis of the alloy is also given in Table I. Three-inch sections were cut from an 0.120-in.-diameter alloy rod and tapered to a fine point on each end. The samples were sealed in evacuated Vycor tubes, homogenized for 5 hr at 1000°C in the ß-phase field, and slowly lowered in a gradient furnace into the a phase (800°C), annealed for 60 hr at this temperature to produce grain growth and furnace cooled. This technique produced large grains approximately 1/2 to 3/4 in. long over the entire cross section of the rod, which were free of observable substructure. Metallographic examination up to X1000 did not show the existence of any second phase in these grains. Crystal Orientation—All crystals were abraded on fine emery paper to produce two flat surfaces 90 deg to each other. The crystals were analyzed by the standard Back-Reflection Laue technique to obtain the crystal orientation with respect to the abraded surfaces. The Back-Reflection Laue Photograms of all crystals used were clear and sharp indicating that the crystals were free from any substructure that could be detected by these means. Hydriding—Only samples containing four to five grains were used for hydriding. Samples that exhibited fine grained patches were discarded. The samples were hydrided using the following technique. After etching in 48 vol. pct HNO3, 48 vol. pct H2O, and 4 vol. pct HF (48 pct) solution, the specimens

Jan 1, 1961

By L. C. Michels, O. G. Ricketts

The disorientations between s?nall grains, whose growth has been arrested at an early stage of recrys-tallization, and the deformed matrix in cold-rolled aluminum single crystals were determined using transmission Kikuchi line and electron diffraction patterns. The orientations of the recrystallized grains were found to be random, and the disorientations of these grains with the matrix weve found to be intermediate to large. This leads to the conclusion that the observed vecrystallization began in small areas of large disorientation present in the cold-worked structure. heavily cold-worked thin sections of aluminunz single crystals and of polycrystalline aluminum and nickel were produced directly by a mechanical technique. The specinlens thus prepared were heated with the electron beam to bring about vecrystallization during observation in the electron microscope. Motion pictures taken du.ring heating and the electvon, microg.raphs taken both before and aftev heating allowed the recrystallization process to be traced to its ovigin. Re cvystallized grains originated in very s,mall regions of the cold-worked structure and developed through rapid migration of high-angle boundaries. The boundaries either were present as such in the matrix or were formed out of dense dislocation networks. SIGNIFICANT advances have been made in recent years in the study of nucleation of recrystallization using the technique of transmission electron microscopy of thin metal foils. Bollman1 in a study of heavily rolled polycrystalline nickel found support for the Cahn-Cottrell2,3 theory of nucleation. According to this theory nuclei form by the initially slow growth of subgrains formed through polygonization. During this initial period of slow growth (the incubation period) the migrating boundary of the subgrain increases its disorientation with the cold-worked matrix and thereby increases its mobility to become a rapidly migrating high-angle boundary. Bailey4,5 investigated the annealing behavior of several metals deformed both in tension and by rolling and concluded that recrystallization took place through the migration of high-angle boundaries. With low deformations these boundaries were present in the metal before deformation. With high deformation it was not possible to tell whether the boundaries were pieces of the original grain boundaries or were produced either during deformation or by polygonization during ameal- ing. Direct observation during heating of metal foils indicated that subgrains form by polygonization and grow at an uneven rate. The grain size obtained decreased with decreasing foil thickness indicating that the foil surface resists boundary motion. Votava,6 in heating stage experiments on rolled copper, observed nuclei to appear suddenly and grow in jumps of differing magnitude. However, he found no special dislocation configurations where the nuclei appeared. Fujita,7 as a result of a study of subgrain growth in heavily worked aluminum, concluded that the boundary of a recrystallized grain initially forms from the boundary of a group of subgrains. This occurred by a process of deposition of vacancies and dislocations in the group boundary as the boundaries within the group disappear. HU8,9 directly observed a similar process in heating stage experiments on 70 pct rolled Si-Fe single crystals. The growth of subgrains appeared to proceed by a coalescence mechanism. The observed fading away of the boundary between two subgrains was explained by the moving out of dislocations from the disappearing boundary into the connecting or intersecting boundaries around the subgrains. The subgrain size and degree of disorientation with the surrounding structure were thus increased. With the increase in disorientation occurred a corresponding increase in boundary mobility, which eventually allowed the boundary to migrate rapidly. This process was observed to occur within "microbands" consisting of parallel narrow segments disoriented by a few degrees present in the as-rolled structure. The conclusion of Rzepski and Montuelle10 that growth is preceded by the coalescence of blocks through disappearance of their common boundaries supports this view. In contrast to Hu's coalescence model for nucleation were the conclusions of Walter and ~och.""~ Working with the same material as Hu, of the same orientation and rolled to the same reduction, they concluded that nucleation occurred by the Cahn-Cottrell mechanism. They observed, in agreement with Hu, that recrystallization began in the "microband" regions which they referred to as "transition" bands. Bartuska13 studied subgrain growth in heavily rolled nickel using a beam heating method in the electron microscope. He concluded that nuclei for recrystallization form from the largest most perfect subgrains present in the cold-worked structure by rapid intermittent migration of parts of subboundaries. In rare instances he observed subgrain growth by coalescence. EXPERIMENTAL PROCEDURE The materials used in this study were 99.999 pct A1 supplied by A.I.A.G. Metals, Inc., and 99.999 pct Ni supplied by Johnson and Matthey and Co., Ltd. The Hitachi HU-11 electron microscope, with uniaxial

Jan 1, 1968

By S. L. Lopata, E. B. Kula

A variation of yield and tensile strength with direction has been noted in heat-treated 4340 steel which had been warn-worked by rolling in the austenitic condition prior to quenching. Measurements by X-rays showed a preferred orientation of martensite crystals. Various ideal preferred orientations of martensite were calculated by assuming a preferred orientation for austenite and transforming this to martensite by the Kurdjumov -Sachs and Nishiyama relationships. Comparison with the measured preferred orientation showed that the ideal rolling texture for austenite in 4340 steel could be expressed as a (112) [111] texture with a component of (110) [112]. No evidence was found for any fiber axis in the rolling direction, or fop- a (123) [412] texture. The observed martensite pole figures can be adequately accounted for by these ideal austenite textures and by the Kurdjumou-Sachs or Nishiyama transformation relationships between austenite and martensite. ALTHOUGH preferred orientations are found in cold-rolled steel sheet and in many nonferrous metals, they are not generally encountered in wrought, heat-treated high-strength steels, since such steels are generally not cold worked sufficiently to develop a strong texture, and any texture that is present is removed during heat treatment by the phase transformations taking place. This report gives details on a preferred orientation found in warm-rolled and hardened 4340 steel. In a recent study, a special combination heat-treating and working technique was used in which 4340 steel was deformed in the austenitic condition, and before re crystallization of the austenite could occur, quenched to form martensite.' Since the austenite was unrecrystallized, it was cold worked and hence could have contained a preferred orientation which could be transmitted to the martensite on quenching, and this in turn could be manifested as a directionality of mechanical properties. Such a directionality of properties was found as a result of working, and this prompted an X-ray study of the preferred orientation. Literature Survey— Rolling Texture in Face-Cen-tered-Cubic Austenite—M a preferred orientation is found in a rolled and hardened steel, it is first appropriate to consider what texture existed in the austenite as a result of the rolling but prior to the transformation to martensite. The changes taking place as a result of the austenite-martensite transformation are then considered. In view of the instability of austenite in 4340 steel at low temperatures, no direct determination of the austenite texture was made. However, an estimate of the texture for austenite in 4340 steel may be made by considering the textures found for other face-centered-cubic metals. Barrett' has reviewed the rolling textures for many materials. The most common orientation in face-centered-cubic metals has the (110) planes parallel to the rolling plane and the [112] directions parallel to the rolling direction, or (110) [112]. Other orientations found are (112) [111], as well as (100) [001], (110) [001], and others. Beck and his co-workers, using quantitative pole figures, report that (123) [121],3 later corrected to (123) [412],4 better describes the ideal orientation. smallman5 reported that the ideal preferred orientation for high-purity face-centered-cubic metals is (123) [121], but that there is a transition to (110) [112] as solid solution elements are added. The latter texture tends to occur more readily at lower temperatures. This transition between the two textures was explained by differences in the slip characteristics with concentration or temperature. More recently, Jones and Fell6 concluded that the (123) [412] texture for face-centered-cubic metals could equally well be represented by a mixture of (110) [112] and (112) [111] textures, and hence it had no physical reality. From the above results it can be seen that there is no agreement on the "ideal" texture for fcc metals and, hence, no firm basis for assuming a texture for austenite in 4340 steel. Therefore, the orientations (110) [112], (123) [412], and (112) [111] have been considered in the following.* *The (123) [4121 is identical to the (123) [121] rotated 90 deg. Orientation Relationship between Austenite and Martensite—When martensite forms from austenite, certain crystallographic planes of the martensite are parallel to planes in the austenite. This orientation relationship was first determined by Kurdjumov and

Jan 1, 1960

By I. L. Dillamore

I. L. Dillamore (University of Birmingham)—The different textures developed in various fcc metals have long awaited satisfactory explanation and it has now become clear that these differences are related to parallel differences in the deformation characteristics of the metals. Liu is correct, therefore, in seeking to account for the observed textures in terms of the flow mechanisms but I believe, for the reasons outlined below, that the particular interpretation of flow mechanisms proposed by Liu is open to substantial objections. By considering the forty-eight possible designations of the twelve octahedral slip systems found in fcc metals as distinct and separate deformation modes, Liu has fallen into the error of assuming that only positive glide dislocations associated with each system are present. In fact both positive and negative dislocations will be present and the only difference between for instance the systems B4 and B4' (in Liu's notation) is that under a stress of given sign the direction of motion of a dislocation is reversed on changing from B4 to B4'. For both orientations positive and negative dislocations will be present. In considering possible dislocation interactions it is, therefore, inadmissible to differentiate between R4 and R4' as Liu does. Liu considers those dislocation interactions which give the biggest reduction in energy to be the most favorable and neglects, on the grounds that they will form strong barriers to slip, interactions between dislocations with perpendicular Burgers vectors. Setting aside interactions between positive and negative dislocations of the same slip system, which must occur regardless of the combination of slip systems chosen, the biggest reduction in energy occurs for the Lomer-Cottrell interaction and it is Lomer-Cottrell barriers which are thought to provide the stronger dislocation obstacles. On the other hand the intersection of dislocations with perpendicular Burgers vectors is thought to be a low-energy process which contributes only a fairly small temperature-dependent part of the total work hardening. On this basis it seems doubtful whether the reduction in energy through possible dislocation interactions provides a reasonable criterion for choosing the operative slip systems. From the point of view of texture development it is unsatisfactory to ignore the slip rotations leading to an end position and to neglect to consider the stability of the chosen end point. It is also unsatisfactory to treat the two stress axes as interchangeable since, if the stress system is idealized as biaxial, one stress is compressive and the other is tensile. For the same reason the rotations of the two stress axes are not made compatible simply by assuming that the same slip directions are responsible for the rotations of the two stress axes. It is, in short, essential to treat the two stress axes as acting together on the same slip systems. Turning to the question of the difference between the copper-type and the brass-type texture, there now remains little doubt that the difference is attributable to differences in stacking-fault energy (y), as noted by Liu, but it is doubtful whether the temperature dependence of the texture in copper and in silver is due to increasing stacking-fault energy with increasing temperature. The results of Swann and Nutting42 cited by Liu were obtained in Cu-A1 alloys and the apparent increase in stacking-fault energy on raising the temperature may be influenced by short-range ordering. In pure metals such effects are absent and the only data available on the variation of y with temperature are those of Buhler et a1.43 for silver. They report a minimum at 200°C which does not fit the hypothesis put forward by Liu. It is much more likely that thermal activation of cross slip is important in determining which texture develops, as proposed by Dillamore and tors. These workers have proposed an explanation for the differences in observed texture among the fcc metals and the pole figures predicted consist of an orientation spread which is in better agreement with observation than the limited number of discrete orientations suggested by Liu. The theory of Dillamore and Roberts is also able to account for the differences between aluminum and copper which Liu still leaves unexplained. Y. C. Liu (author's veply)—The writer appreciates the interest of Dr. Dillamore, but must discuss some of his comments in order to avoid cross purposes. The phrase, "forty-eight slip systems," which appeared twice in the text—in the caption of Fig. 1 and the first paragraph in the Discussion—might unfortunately have led Dr. Dillamore to disagree

Jan 1, 1965

By Anton Sawatzky, Erich Vogt

By means of mathematical solutions to the appropriate diffusion equations, we describe the kinetics of the thermal diffusion of hydrogen in Zircaloy-2 for the various temperatures and concentrations encountered in a heavy water moderated reactor. When the hydrogen concentration is below terminal solid solubility only the a Phase is present. Redistributions are then described in terms of the characteristic functions of the difhsion equation. For higher concentrations both the a and 6 phases are present. We assume the two phases to be always in equilibrium. For moderately small hydrogen concentrations exact solutions of the two-phase equation approach the the approximate solutions derived by Sawatzky and for all concentrations the exact solutions exhibit the qualitative features of his result: the two-phase concentration increases with time, everywhere; in the absence of a hydrogen current at the hot end of the sample an a-phase region always exists there; the interface of the a + 6 , a-phase boundary moves toward the cold md of the sample and the hydrogen concentration is discontinuous at the interface. Simultaneous solulions of the a and a + 6 hydrogen distributims and of the concomitant interface motion are obtained and compared to the observations of Sawatzky and Markowitz. The kinetics of the hydrogen diffusion process are shown to lead to m apparent heat of transport of the a phase which is lower than the actual value (even for samples with long anneals) thus resolving at least partially the disparity between experimental measurements of this quantity. A number of recent papers1"4 have reported measurements on the diffusion and redistribution of hydrogen in Zircaloy-2 under temperature and concentration gradients. These studies were instigated by problems arising from increasing use of Zircaloy-2 as a fuel element cladding material in pressurized-water power-reactors. The Zircaloy-2 picks up hydrogen during the operation of the reactor: the consequent precipitation of zirconium hydride in the Zircaloy-2 has pronounced effects on its mechanical properties. The Purpose of the present Paper is to describe the kinetics of the thermal diffusion of hydrogen in Zircaloy-2 for the various hydrogen concentrations and temperatures likely to be encountered in reactors. When the hydrogen in the Zircaloy-2 is entirely in the solid solution phase (a phase), the differential equation for thermal diffusion is well known and the redistribution can be described by standard mathematical methods some of which are given in Section 11 below. The treatment of the a + 6 (hydride) region differs from the earlier treatment of sawatzky3 by taking into account several modifications of the two-phase diffusion equations as suggested to us by Markowitz4 and Kidson.5 Even with the modifications the results obtained in our more complete treatment are substantially the same as those found by Sawatzky. As we show, the difference between the results of sawatzky3 and kIarkowitz4 is largely due to the difference in the geometry of their experiments. In the next section we derive the modified two-phase equation for arbitrary geometry. The exact solution of this equation is given in Section III for linear and cylindrical geometry. It is shown that Sawatzky's approximate solution is quite accurate for almost all the temperatures and hydrogen concentrations which are actually encountered. In Sawatzky's approximate theory the hydrogen concentration everywhere in the two-phase region increases continuously. As his paper pointed out, this result, together with hydrogen conservation, implies that in a sample with no hydrogen current flowing into the hot end a two-phase region is always accompanied by a single-phase region at the hot end of the sample. The net hydrogen gain in the two-phase region is supplied by the decrease of hydrogen in the single-phase region and by the movement of the (a, a + 6) boundary toward the cold end of the sample. Hydrogen conservation at the (a, a + 6) boundary leads to a discontinuity in the concentration and its derivative there. In Section IV it is shown how these qualitative features of the thermal diffusion kinetics arise from the simultaneous solution of the a-phase differential equation and a + 6 phase equation. Methods derived by us previously for the solution of the redistribution in both phases and the accompanying motion of the boundary are used to obtain approximate solutions valid for large times. The solutions account well for the observed redistributions of Sawatzky and Markowitz. It is shown how the continuing motion of the (a, a + 6) boundary leads to measured values of the heat of transport lower than the actual value, even for specimens with relatively long anneals.

Jan 1, 1963

By F. H. Vitovec, D. W. Hoeppner

Pusk-pull fatigue tests were conducted on copper tricrystals of 99.988 pct purity to ascertain the role of grain boundaries in the initiation and propagation of fatigue cracks. Significant differences in behavior were found for specimens which possessed different transverse-boundary misorientation. In speciwens with low boundary angles cracks initiated within the transverse boundary, while higher angles led to transcrystalline fatigue failure. It is suggested that at low angular misorientation moving dislocations may interact with dislocations of the boundary or dislocations present in adjacent pains on favorably oriented glide planes, thus initiating a fatigue crack. MANY fatigue studies have been concerned with fatigue-crack initiation within grains and the mechanism causing initiation and propagation1-3 Although the initiation of fatigue cracks in or near grain boundaries of pure metals has been observed and reported in the literature, the mechanism of this phenomenon has received little attention.4"11 EXPERIMENTAL PROGRAM Testing Procedure. To investigate the role of grain boundaries regarding initiation and propagation of fatigue cracks, copper tricrystals were tested in push-pull. Axial-stress tests were used to avoid the stress gradients introduced by stressing of some other nature. Copper was selected as the most suitable test material since extensive work has been done on the formation of fatigue-induced slip in copper. Tricrystal specimens were used to provide a grain boundary geometry with one boundary transverse to the principal stress axis and one or more boundaries nearly coincident with the direction of maximum resolved shear stress. The boundary energy and the slip characteristics in the vicinity of the transverse boundary depend on the relative orientations of grains across the boundary. Testing was done at room temperature, at a frequency of 700 cpm, in an atmosphere of either air or argon. It is known that the incidence of grain boundary cracking increases with increasing temperature and decreasing frequency.4 The fatigue machine applied a uniaxial tension-compression load to the specimen by a flat spring which was actuated by an adjustable eccentric. Use was made of an adjustable head and a load cell which had strain gages mounted at 120-deg intervals around its periphery, thus providing a means for eliminating any detectable superimposed bending moment. A clip gage was mounted between the gripping heads to record the cyclic strain amplitude applied to the specimen. Each specimen's hysteresis characteristics were recorded by supplying the load and strain signals to an oscilloscope. Microstructural changes were observed and recorded with an optical microscope which was mounted on the fatigue machine. Immediately prior to insertion in the machine, each specimen was chemically polished. Extreme care was exercised while inserting the specimen in the test machine to avoid either bending the specimen or introducing a mean load. Each specimen was stressed in the tensile direction first and subsequently the load was reversed. Specimen Preparation. Tricrystal fatigue specimens of 99.988 pct Cu were grown from the melt using a modified Bridgman technique. Ingots about 1 in. high were grown to the configuration shown in Fig. 1. Upon sectioning the resultant ingot, several specimens were provided with an identical shape and grain boundary orientation. Except for plane sectioning and final polishing, this method eliminated machining the specimens. The apparatus used for growing the tricrystals is shown in Fig. 2. A spectrographically pure graphite mold, Fig. 3, was inserted in a vycor tube which was mounted on a vertical zone-refining table. Prior to insertion in the tube the mold was assembled as follows. The insert and graphite rods were fixed in position in the mold. The copper was then placed in the mold and the entire mold assembly was positioned in the vycor tube, Fig. 2. At this point the tube was sealed, evacuated, purged with helium gas, and finally placed under a slightly positive helium pressure. The heating coil was then adjusted to melt the copper charge, after which it was raised at a speed of 4 in. per hr. It is also possible to use

Jan 1, 1964

By R. A. Thomas, R. L. Solbod

The importance of transverse diffusion on the finger development in a miscible-phase displacement at an adverse mobility ratio of tbree was studied in a porous plate 1/4-in. thick, 3-in. wide and 18-in. long. Fast displacement rates (29 ft/D) and slow rates (1.6 ft/D) were used to determine the effect of residence time on the geometry of the fingers. The shape of the fingers was observed directly by use of the X-ray technique. At fast rates numerous narrow fingers were observed, but at slow rates a single somewhat bulging finger was produced. The amount of material moved transversely by diffusion across the plate was sufficient to modify the finger geometry in the slow-rate run because of the long residence time. These results are in contradiction to some of the postulates in the literature. The composition of the effluent stream, however, was not affected by the flow rate. This result is not inconsistent with the observed change in the shape of the finger in a short model, but it seems likely that a short model does not offer adequate and proper scaling of the reservoir. The model used was probably a valid one for studying the effect of transverse diffusion on the finger geometry, but a longer model would be needed for proper scaling of the effect of the change in the finger shape on the efficiency of displacement as measured by the composition of the effluent stream. INTRODUCTION Fingering can be defined as the uneven advance of the injected phase as it moves into a porous medium displacing the resident phase from the pore spaces of the rock. The use of this term is usually restticted to the situation in which the displacing phase is less viscous or more mobile than the fluid being displaced. Under these conditions, not only are fingers formed, but the length and width of the fingers grow with distance traveled in the porous medium. This subject has become one of great interest to the oil industry because of the present trend toward the use of various forms of miscible-phase displacement to increase oil recovery. Since in nearly all of the known modifications of the miscible-phase displacements an unfavorable mobility ratio exists (the displacing phase has a lower viscosity than that of the crude oil), the conditions are proper for fingering to develop. An appreciable amount of fingering appears to be a severe handicap to these processes for it increases the volume of agent required for the process to be a success, and such an increase puts a severe strain on the economics of the proposed processes. In some cases, such as for a mobility ratio of 200 unfavorable, it has already been demonstrated that the proposed process would not be economic if the fingering in the field were to be of the same magnitude as that observed in the laboratory. A number of aspects of fingering have been studied and reported in the literature. While the phenomenon of fingering cannot be regarded as a completely understood subject, considerable information exists on the effect of the path length and the mobility ratio on the growth of fingers. Less-complete data are available on the effect of the diameter of the flow path on the character and amount of the fingering, and even less agreement in results exists on the effect of rate of flow on the nature of fingering. This paper deals with one aspect of this latter subject. OBJECTIVE The objective of this study was narrowed down to one rather specific feature of the behavior of fingers in miscible-phase displacement in porous media. The variable studied was the effect of rate of flow on the nature and the development of fingers. It should be made clear at this point that, while rate was the apparent variable, the real variable was residence time; that is, at low rates the fluids are present at a given spot in the porous medium for a longer time interval than at fast rates. The purpose of the study, therefore, was to determine the changes which occur in the fingering and the possible benefits which might accrue from a longer residence time during that period when fingers are

By A. M. Turkalo

IT is a well-known fact that martensitic steels show a greater resistance to brittle fracture than do pearlitic and bainitic steels. It was, therefore, thought worthwhile to investigate the mode of brittle fracture with respect to structure by studying the effect of various austenite decomposition products on the propagation of brittle fracture in steel by means of electron microscopy. Newly developed replication techniques together with the advantages of the electron microscope such as great depth of field, available high magnification and easy adaptation to stereophotography make electron microscopy very suitable for fracture studies. EXPERIMENTAL PROCEDURE An essentially plain carbon steel containing 0.56 pct C, 1.30 pct Mn, 0.02 pct P, 0.03 pct S and 0.22 pct Si was used in this investigation. The following table gives the heat treatments used to obtain the various austenite decomposition products: The resulting austenite grain size from the 870°C austenitization treatment was about an ASTM No. 7 grain size. The specimens which were 2 in. long, 1/4-in. diam bars were austenitized in a tube furnace through which argon gas was blown. The tube was not, however, air-free and the specimens were not completely oxide-free. Isothermal treatments were done in a lead bath. With the exception of the fully hardened specimen and the one as-isothermally transformed at 300°C the heat treated specimens were notched in the following fashion with a jeweler's saw. A cut about 0.08 in. deep was made perpendicular to the length of the bar. The specimen then was rotated about 45 deg and another cut about 0.08 in. deep was made. In the case of the hard martensitic and bainitic specimens, only one cut was made and the depth was not controlled. The design of the two-cut notch caused fracture to initiate at the point of intersection of the two saw cuts. The specimens were broken at -196°C in a Charpy impact testing machine. In order to hold the specimens securely in the impact machine two square pieces of mild steel were made about 5/8 in. long having the same cross section as that of a standard Charpy specimen but containing a hole 1/4 in. diam through the center of the cross-section. These adapters were slipped over the ends of the test specimen which was then secured tightly by means of set screws in the adapters. The specimen with the adapters was cooled to -196°C in liquid N,, then placed in the impact machine and broken within 3 sec. One half of the broken specimen was used for the electron microscope study of the actual fracture surface. The other half was nickel-plated and a cross section through the notch and fracture was polished for electron microscope examination. Carbon replicas of the fracture specimens for the electron microscope study were made essentially according to Bradley's evaporation technique.' Both direct carbon and two-stage carbon replication techniques were used. In the case of the direct carbon technique, a thin layer of carbon was evaporated first at an angle of about 45 deg to the mean fracture surface and then another film of carbon was evaporated normally to the fracture surface. The carbon replica was freed electrolytically.2 The specimen was made an anode in a 10 pct Nital polishing solution. It was etched intermittently by shutting off the power now and then. The freed replica was washed in 40 to 50 pct water solution of nitric acid for 10 min or so, then washed in water and picked up on a screen for examination. The two-stage carbon replication technique involved first making a primary replica of cellulose * acetate from which a carbon replica was then made. One side of a strip of cellulose acetate wet with acetone was pressed lightly against the surface of the specimen, allowed to dry and then stripped. Prior to the deposition of carbon, which was done at 90 deg to the cellulose acetate replica surface, chromium was evaporated at 45 deg. After the carbon evaporation the cellulose acetate was dissolved in acetone according to the Jaffe method3 leaving the carbon replica preshadowed with chromium for examination.

Jan 1, 1961

By A. L. Barnes

Residual oil in watered-out reservoirs is a tremendous reserve which has been unrecoverable by established production methods. A study of the new recovery methods indicated that the forward combustion urocess might- recover oil from such reservoirs; however, no thermal recovery operating experience in a watered-out system was available. The Delaware-Childers pilot thermal test was undertaken to test the feasibility of thermal recovery in this watered-out reservoir. The pilot test consisted of a 2.22-acre, inverted five-spot in the 600-ft deep Bartlesville sand. The reservoir in the pilot area had a porosity of 20.6 per cent, a permeability of 118 md and an average sand thickness of 45 ft. The reservoir contains a 33' API, 6-cp oil. Combustion was started Nov. 22, 1960. The initial air injection capacity was 750 Mscf/D, but it was eventually increased to 2,000 Mscf/D. The test was surrounded by an active water flood; therefore, water production was initially high, but decreased as the heat wave moved toward the producing wells. Oil-bank arrival at an individual well was indicated by a drop in GOR and WOR, and an increase in oil production. Combustion-front arrival was evident at three of the pilot producers, and they were plugged. Cumulative oil production from pilot area wells war over 12,000 bbl. Operational difficulties were negligible and only conventional equipment was necessary. The combustion efficiency of this test averaged over 80 per cent. Results from coring showed that the leading edge of the combustion front tended to be wedge-shaped but a nearly complete sweep of the reservoir was eventually obtained. An isopach map based on evidence from 10 core holes and the existing wells showed that 126 acre-ft had been swept by the heat wave. Using this swept volume, an air requirement of 15.7 MMscf/acre-ft was calculated. It was calculated that 275 ,STB/acre-ft was consumed bv the heat wave. INTRODUCTION There is a large amount of oil remaining in reservoirs that have been water flooded. A study of ways to recover this oil showed that the forward combustion process might be applicable. Results from a number of forward combustion tests have been reported in the literature, but none of these tests were conducted in a watered-out system. The Delaware-Childers pilot thermal test was initiated in 1960 to define the operating characteristics of underground combustion in this watered-out Bartlesville sand reservoir, The purpose of this paper is to present the pilot test results in detail. FORWARD COMBUSTION PROCESS The forward combustion process consists of initiating combustion in the formation surrounding an injection well and driving this heat wave through the formation toward offset producing wells. As the combustion front progresses through the reservoir, oil and formation water are vaporized, driven forward in the gaseous phase, and recon-densed in the cooler part of the formation. These distilled liquids, water of combustion and gaseous combustion products, form a bank or three-phase region ahead of the burning front. This bank pushes mobile reservoir fluids toward the production wells. The rate of movement of the combustion front is controlled by the rate at which the nondistill able residue which serves as process fuel can be completely burned off the sand. The production performance from a heat wave conducted in a watered-out oil reservoir will differ from one conducted in a dissolved gas-depleted reservoir because of the difference in fluid saturations. The primary depleted reservoir contains connate water saturation, relatively high oil saturation and some gas saturation. The watered-out reservoir contains a highly mobile water saturation, residual oil saturation and little gas saturation. As the combustion front moves forward in either type of depleted reservoir, it drives the distillable oil, the water in place and the water of combustion ahead, and burns the nondistillable portion of the oil. The heat-wave process in a watered-out reservoir differs from the process in a

Jan 1, 1966

By Alton B. Cook, G. B. Spencer, F. P. Bobrowski

In estimating production gas/oil ratios and oil recoveries from reservoirs containing highly volatile oils it is highly important to include condensate that may be recovered from the gas produced from the reservoir. The volume of the hydrocarbon liquid condensed from the production of the solution gas that has been liberated. in some reservoirs may equal or even exceed the volume of recoverable stock-tank oil as estimated by present methods. The usual procedure1, 2, 3 in estimating future reservoir performance includes use of relative permeability data of the reservoir rock to gas and oil and includes material-balance calculations utilizing data on the volume of the reservoir fluids, oil and gas production and reservoir pressure decline, and data on the physical properties of the initial reservoir fluids. The inaccuracy in the procedure results from the false assumption that all of the free or liberated gas that enters the well bore of reservoirs containing highly volatile oils remains in the gaseous phase as it is produced. This paper presents a method for estimating future reservoir performance and oil recoveries based on special labora. tory analyses of reservoir-oil samples and recognition of the additional volume of hydrocarbon liquid that will be recovered at various stages of depletion from a solution.gas.drive reservoir. The method also includes calculations of the volume and composition of the hydrocarbon liquids that can be recovered by processing the produced gas in a natural-gasoline plant. The development of the method resulted from a study of laboratory analyses of reservoir samples and of field data obtained from two reservoirs containing oil of the highly velatile type. Relatively high pressures and temperatures prevail in oil reservoirs discovered at the greater depths of present-day drilling. The contained fluids may have high saturation -Dressures and large volumes of gas in solution. The oils and gases under these conditions may be almost identical in compositions and densities.4,5 Also, engineers have noted that, for a number of oil reservoirs and especially the deeper reservoirs, the API gravity of the stock-tank oil increaees as the production gas/oil ratios increase. They attributed this increase in API gravity of the stock-tank oil to the formation of condensate as the liberated gas in the reservoir is being produced. SOURCE OF DATA FOR CALCULATIONS Subsurface oil samples and well-test data were obtained from the E. Constantin-Lambert Well No. 1 in the Elk City Field, Okla., to demonstrate the need for and a method of calculating future reservoir performance when consideration is given to the recoverable hydrocarbon liquid from the production of solution gas that has been or will be liberated in a reservoir. The Lambert well is located in C, SW 1/4, SW 1/4, Set- 18, T-l0-N, R-20-W, Washita County, Okla. At the time of completion it was on the east edge of the development and Was producing from conglomerate through 30 perforations in the 5 1/2-in. casing at a depth of 9,859 to 9,864 ft. The well Was completed on July 9, 1949, and subsurface oil samples were obtained July 29 and August 1, 1949. Production gas/oil ratio data were obtained during the operation in series of two Separators at high and low-pressures of 314 and 44 psia, respectively, and at an average temperature of approximately 60°F. The flowing bottom-hole pressure at the time of sampling was 3,934 psis. The static bottom-hole pressure was not obtained at the time of sampling, as the well could not be shut in long enough for testing because gas produced from the well was used for fuel at an offset drilling well. However, the initial reservoir pressure was calculated to be 4,364 psia from knowledge of pressure gradients in other wells in the field and the depth of the casing perforations in the Lambert NO. 1 well.

Jan 1, 1951

By K. T. Aust

The relative interfacial energies of symmetrical tilt boundaries in silver of greater than 99.999 pct purity were measured as a function of orientation difference 0 between 9° and 36° about <001>. The results are in good agreement with the dislocation model of the grain boundary. The energy vs H curve may be represented by the Shockley and Read equation in the form Eoe (0.55—In 8). READ&apos; has indicated that an ideal experimental method of testing the predictions of the dislocation theory of the grain boundary would be to measure the interfacial energies of symmetrical tilt boundaries between face-centered-cubic grains that have a common <001> axis, as a function of orientation difference 0. The misfit H should be defined by a rotation of each grain through an angle of H/2 away from the boundary. Such boundaries might be expected, from geometrical considerations, to be made up of a series of edge dislocations, at least for small values of 0. Energy vs H relationships for tin&apos; and lead:&apos; were previously obtained for an asymmetrical tilt boundary separating two grains in which generally only one grain was rotated about a <001> specimen axis through an angle of H away from the boundary, the other grain remaining fixed. It is possible, however, that the boundary atoms in tin and lead may have attained a symmetrical position, in relation to the orientations of the grains on either side of the boundary, during equilibrium annealing. The two sets of measurements on silicon ferrite&apos; were somewhat better suited for comparison with theory, since the boundaries were symmetrical tilt boundaries in which the axis of relative rotation was <110> in the first series and <l00> in the second; but this alloy has a body-centered-cubic structure. Although the grain boundaries in silver" were symmetrically tilted, the axis of relative rotation was not a simple crystallographic direction, and it varied from boundary to boundary. Although the above measurements were in good agreement with the Shockley and Read equation,"&apos;: it appeared desirable to carry out experiments under the ideal conditions specified by Read.&apos; Consequently, the relative energies of symmetrical tilt boundaries in silver between grains that have a common <001> axis were measured. The technique of equilibrating grain boundaries in oriented tricrystals was used rather than the less satisfactory thermal groove method previously employed for silver bicrystals." Experimental Details and Observations The solidification and seeding techniques, described previouslyh for growing tricrystals of controlled orientations, were used to prepare tricrystal specimens from silver of greater than 99.999 pct purity. The silver was obtained from American Platinum Works, Newark, N. J., in the form of poly crystalline rods 10 cm long and 7 mm in diam. These rods were then cold worked by rolling or drawing them into suitably shaped blanks. Single crystal seeds and tricrystals were grown in a high purity graphite boat by means of a movable furnace with globar heating elements. The graphite boat was enclosed in a Vycor tube, which was first evacuated to about l00/u Hg and then filled with a static argon atmosphere. The maximum temperature outside the Vycor tube was 1250°C. A typical tricrystal specimen of silver is shown in Fig. 1. Grains B and C were grown from seed crystals with a <001> specimen axis or longitudinal direction parallel to the direction of growth and with another <001> direction perpendicular to the surface. Each of the two seed crystals was rotated 18" about the <001> specimen axis but in opposite directions away from the boundary. A symmetrical tilt boundary, therefore, separated grains B and C with an orientation difference 8 of 36" about <001>. Grain A in Fig. 1 was grown from the middle seed with a <110> direction parallel to the specimen axis and with a <001> direction inclined at 45&apos; to the surface of the specimen. The interfaces sepa-

Jan 1, 1957

By M. T. Simnad, R. F. Mehl, L. Yang

Techniques for studying marker movement in K-Rb interdiffusion have been worked out. The results indicate that Rb diffuses faster than K and that the ring mechanism of diffusion cannot be the dominant one operating in this case or probably in cases involving other alkali metals, despite their low ion core repulsive energies. SEVERAL theoretical attempts have been made in the past decade to elucidate the mechanism of diffusion in body-centered-cubic metals. No general agreement, however, has been reached by different authors. Zener,1 and later LeClaire,2 on the basis of a correlation between the entropy of activation for self-diffusion and the temperature dependence of the elastic constants, predicted that a ring mechanism should operate in the diffusion of body-cen-tered-cubic metals. Paneth3 calculated the activation energies of various ring, vacancy, and interstitial mechanisms for the self-diffusion in alkali metals and concluded that the most likely one was based on the linear motion of "crowdions," which is in fact a different form of interstitial diffusion. Fumi,1 however, showed that the experimental values of the activation energies for self-diffusion in the alkali metals could be better accounted for if the diffusion process in these metals was assumed to follow a vacancy mechanism. The same conclusion was reached by Kojima5 for the self-diffusion in lithium. Experimental evidences published during the past few years seem to exclude the ring mechanism as the predominating one in the diffusion of body-centered-cubic metals. For instance, maker movement has been observed in ß-brass, first in this laboratory" and later by Resnick and Baluffi.5 Shewmon and Bechtoldh also found marker movement in the body-centered-cubic system Ti-Mo and showed that the argument which led Zener and LeClair to favor a ring mechanism was not incompatible with a vacancy mechanism. In spite of this, it seemed to the authors that further experimental tests should be made by studying the Kirkendall effect in body-centered-cubic systems that characteristically have small ion core repulsion, such as the alkali-metal systems. Since the ion core repulsion term constitutes the main part of the activation energy needed for the rotation of a ring, such a test should be the most critical of all. The system K-Rb was chosen for experimental study because these metals form a continuous series of solid solutions. Experimental Investigation Owing to the extremely active nature of these two metals, a brass dry box (18 x 11 x 10 in.) was built for making the diffusion couple. It had a big lucite window on top, two side ports through which neo-prene-rubber gloves were inserted, and another side port covered with an optically flat-glass window for microscopic examination of the sample. Inside the box there were a circulating fan driven with a rotating horse-shoe magnet located outside the box, a heater used to generate potassium vapor for getter-ing the box, and a cold trap for keeping the inside of the box cool. Chemically pure grade K and Rb were triple distilled before they were transferred in vacuum into cylindrical steel molds kept in pyrex-glass ampules, Fig. 1. The latter together with the tools needed for making the diffusion couple were put into the dry box. After the box was flushed with purified argon and gettered with potassium vapor, generated from a heated steel crucible inside the box, the glass ampules were broken and the mound on the top of the alkali-metal ingot was cut off with a razor blade to yield a flat surface. To make the diffusion couple, one K ingot and one Rb ingot were pushed out of the molds together with their steel supports by screwing a metal plunger into the bottom of each mold. They were then laid on a brass cradle inside the assembling carriage (shown separately in Fig. 2) with the flat faces opposite to each

Jan 1, 1959