By J. H. Nead

The subject of this paper is one to which there are many references in the literature on the manufacture of steel in the open-hearth furnace, but few actual experimental data have been published. For that reason, the presentation of results obtained from two open-hearth heats where attempts were made to measure the sulfur absorption will be of considerable interest and value. The two heats on which the experiments were made were Armco ingot-iron heats and differ from the usual open-hearth heat of medium- or mild-carbon steel in that the refining is carried further; in this product the carbon and manganese are reduced practically to traces. In most other respects, and especially in respect to the absorption of sulfur from the producer gas, the two heats are typical of usual open-hearth practice. The object of the experiments made on the first Armco iron heat was to determine the fluctuation of the composition of the metal bath and the slag throughout the course of the heat, with especial reference to the variations in sulfur. It was hoped to determine whether there was an increase in sulfur in the bath from the producer gas and if so at what stage in the process the increase occurred. The experimental method consisted of charging analyzed scrap and pig iron, so that the sulfur in the charge could be calculated. Then, throughout the duration of the heat, metal and slag samples were takcn every half hour, beginning as soon as there was enough molten metal to take a sample. These samples were analyzed; the results are given in Table 1. All domestic scrap was used and the charge was made up as follows: Head End Finish Pounds Pound Pig iron........................ 36,300 Pig iron....................... 23,900 Sheet scrap bundles............. 36,200 Sheet bars..................... 23,900 Sheet bm..................... 40;200 The total charge, exclusive of the re-pig added near the end of the heat, was 160,500 Ib. The limestone charged was 21,400 Ib., or 13½ per cent.

Jan 1, 1924

By Zay Jeffries

This paper will include a brief discussion of Prof. Howe's paper on The Supposed Reversal of Inheritance of Ferrite Grain Size from that of Austenite.l The general subject of grain refining in steel and iron will also be treated. The conclusions reached are stated in the following hypotheses which are discussed more in detail below. 1. The ferrite grain size in pure iron, the ferrite and pearlite grain size in hypoeutectoid steel, the pearlite grain size in eutectoid steel and the cementite and pearlite grain size of hypereutectoid steel are not inherited from the grain size of the mother austenite. 2. The only structural feature that is generally inherited from the austenite of hypo- and hypereutectoid steels on cooling through their transformation ranges is the position of the excess ferrite or cementite at the austenite grain boundaries, sometimes causing complete and sometimes incomplete networks which outline the old austenite grain boundaries. Rapid cooling through the transformation range will cause the non-inheritance of this structural (network) feature. 3. The austenite grain boundaries themselves are nearly always effaced in all steels and also in pure iron during the At transformations. 4. The grain-size refining of steel and iron is brought about by the combined effect of non-inheritance of the transformation products on either heating or cooling, i.e., the austenite transformation products do cst inherit their grain size from the austenite on cooling through the transformation range nor does austenite inherit its grain size from the products which form austenite on heating. 5. In general, in both iron and carbon steel the larger the austenite grain size, the larger will be the grain size of the transformation products on cooling. This, of course, assumes all other conditions constant except the austenite grain size. An exception is found to this general rule in very pure iron such as electrolytic iron. In this instance small austenite grains may form very large ferrite grains on cooling through Arg.

Jan 1, 1918

By C. van der Poel

When oil is displaced from a horizontal formation by another fluid of lower density, the latter tends to override the former in the shape of a tongue owing to gravity segregation. This gravity tongue has an adverse influence on the oil recovery. If the fluids are miscible, diffusion (mixing) takes place at the interfacial boundary of the gravity tongue. This mixing should have a favorable effect on oil recovery. The report describes a laboratory study of the magnitude of the mixing zone under various conditions, so as to assess the effect of diffusion on oil recovery both in laboratory experiments and under actual field conditions. The technique used enables visual observation and measurement of the size of the mixing zone in transparent glass-powder packs. The results show that in experiments in small models and cores the width of the mixing zone may well be of the same order of magnitude as the height of the model. In such cases oil recovery is favorably affected by mixing. It can further be concluded that, under conditions prevailing in the field, mixing of the injected fluid with reservoir oil is equal to that caused by molecular diffusion alone, eddy-mixing not taking place to any appreciable extent. A simple calculation, then, shows that molecular diffusion is too small for a beneficial effect to be expected from the injection of miscible fluids in horizontal or nearly horizontal reservoirs unless pay zones are thin. INTRODUCTION This paper gives results of experiments made on the mixing which occurs when a miscible displacement is carried out in a horizontal reservoir. This mixing takes place at the interfacial boundary of the gravity tongue formed when the lighter injected fluid overrides the oil present in the reservoir. The object of the experiments was to simulate the field case where, for example, propane with a viscosity of 0.075 cp under reservoir conditions displaces an oil of viscosity 0.6 cp. In the experiments the lighter fluid had a viscosity of about 1 cp and the heavier one a viscosity of about 8 cp, so as to obtain the same viscosity ratio. In order to enable the results to be compared with those published in the literature, a set of experiments with viscosity ratio equal to one was also performed. EXPERIMENTAL TECHNIQUE The technique developed for the purpose enables the width of the mixing zone to be studied as a function of time and place. A glass-powder pack is saturated with a water-glycerine mixture of suitable viscosity, which represents the reservoir fluid. The pack is then rendered transparent by dissolving sufficient ammonium thiocyanate in the mixture to obtain a solution with a refractive index matching that of the glass powder. Alkaline water to which phenol-phthalein has been added is used as the lighter and less-viscous displacing fluid. In those places where mixing or diffusion of the two liquids occurs, the slightly acidic ammonium-thiocyanate solution neutralizes the alkali in the water, and the glass pack shows up white against the red-colored invading water. If a black cloth is hung over the back of the apparatus, the transparent part of the glass pack appears black. In this way the position of the two phases and the transition zone between them is clearly visible, as shown in Fig. 1 (where the red-colored invading water is the grey-shaded zone lying uppermost). In all experiments the amount of alkali in the water was chosen such that the upper contour corresponded to a concentration of 5 per cent of the dense liquid. The lower contour is determined by the size of the glass grains and the thickness of the pack and, consequently, varies from experiment to experiment. Corresponding concentrations of the dense liquid range from about 97 per cent for packs of small grain size (permeability = 1 darcy) to about 95 per cent for those with large grains

By H. P. Greenwald

THE rapidly increasing use in coal mines of portable auxiliary fans, which are generally "blowers" employed in connection with canvas tubing, raises questions concerning the hazards of such equipment, especially where the practices are opposed to established methods of ventilating face workings. Half a dozen or more coal-mine explosions and some fires have been attributed to the use of auxiliary fans; moreover, competent mining engineers have found many dangerous installations and methods of use-for example, intermittent running of the fans in gassy mines with consequent accumulations of firedamp at the faces. These facts have led the U. S. Bureau of Mines to issue this recommendation: "In the interest of safety, the Bureau of Mines, Department of Commerce, recommends that auxiliary fans or blowers should not be used in coal mines as a substitute for methods of regular and continuous coursing of the air to every face in the mine." The comparatively recent introduction of new types of mining machines, mechanical loaders, face conveyors, and slabbing machines has encouraged the trial of new systems of face mining, all of which have for their object the rapid advance of the faces. Although the latter has certain economic advantages, in gassy mines the rate at which gas is given off is generally found to increase in proportion to the speed of advance into new territory, which in turn increases the difficulties of efficient ventilation of the face workings. Some of the systems of advance mining being tried in connection with new mechanizing methods practically compel the use of blower fans and tubing, as single narrow places are now driven, 300 ft. or more without crosscuts. In some instances a series of parallel headings are driven without crosscuts pre-

Jan 1, 1928

By W. J. Uren, Charles R. Kuzell

The industries engaged in winning minerals from the earth, because of their widespread dissemination, are faced with perhaps as wide a variety of labor-management problems as may be found in any other broad sphere of productive activity. Those problems are continually increasing in volume and complexity, and management has become aware of their growing importance. For the past quarter century at least, labor-management problems have largely been union-management problems. During this period tremendous assistance has been given labor unions through legislation and administrative and political action. In the United States, legislation favorable to unions has come about in the form of the now defunct National Industrial Recovery Act; the Wagner Act, most of which has been carried forward in the Taft-Hartley Act and the Landrum-Griffin Act; the Norris-La Guardia Act, the Wage and Hour Law, the Walsh-Healey Act, and others. The result has been to transfer from the hands of management to those who direct the affairs of the unions a large share of control over the industry and to hamper in many ways the remaining control left to management. In the United States there are many examples of the power of unions to injure whole industries seriously without regard to the interests of management, the employes, or the public. During 1958 and 1959 revelations of corruption and coercion in labor unions made before the McClellan Committee of the U. S. Senate generated considerable public sentiment in favor of legislation to protect the interests of employes and the public. However, the resulting legislation, the Labor-Management Reporting and Disclosure Act of 1959 (Landrum-Griffin Act), demonstrated quite clearly that the political power of the labor union leaders was adequate to prevent adoption of effective measures in this field.

Jan 1, 1964

By R. G. Aspden, D. A. Colling

THE {120}(001) texture has been reported in near 50 pct Ni-Fe alloys <0.004 in. thick1,2 and in copper 0.014 in. thick.3 This texture is one of two types of secondary recrystallization textures observed to replace a cube texture matrix and is desirable in Fe-Ni alloys because of its unique magnetic characteristics.1,2 However, the conditions for and mechanism of the {120}(001) formation are not well understood.3 During an investigation of the influence of alloying elements on the magnetic characteristics of 49 pct Ni-Fe alloys with a sheet thickness of 0.014 in., we have observed the growth of {120}(001) secondaries when strong deoxidizers such as aluminum and calcium were present. It is believed that this observation in unique and provides additional insight with regard to the mechanism for {120}(001) texture formation. Three alloys were prepared with electrolytic iron and nickel and contained a nominal 49 wt pct Ni. Alloy A was a straight binary Fe-Ni alloy, whereas intentional additions of 0.013 wt pct Ca to alloy B and of 0.59 wt pct A1 to alloy C were made. Ingots were forged at 1100 C, hot-rolled to 0.150 in. gage, pickled, and cold-rolled to 0.014 in. Standard U-shaped magnetic test specimens were punched, deburred, sprayed with MgO, and annealed in ~50°C dew point hydrogen. Textures were identified with the aid of etch pits, the

Jan 1, 1970

By H. N. Kalia, J. B. Gresham

Several attempts have been made in the past 60 years to commercialize the vast oil shale deposits of the US. However, the industry has yet to become economically viable. To date, it has not been possible to produce oil from oil shales at a competitive price compared with oil produced by conventional methods. The development work, nevertheless, has been fruitful in furthering the art of thick bed mining and technology of in situ retorting. The in situ method has the potential of recovering oil from thick beds, and the resource recovery potential is much greater than that from underground mining and surface retorting. In situ methods require that the shales/marlstones be fragmented in place to induce adequate porosity and permeability to allow in situ heating of the fragmented shales. This can be accomplished by using explosives. However, it has been found that the existing blasting systems, though very efficient, have some drawbacks. The explosives become insensitive when shot in multiplevertical decks. They can also become insensitive when spaced horizontally at close proximity to other charges. Also, since the blasting is done in a very limited free face, the delay time that can be allowed between charges is also quite limited. Consequently, it is not always possible to routinely predict the performance of the blasting system. Furthermore, since it is not possible to undertake secondary blasting, it is imperative that the blast design function properly. Recent successful retorting by Occidental Petroleum Co. Of Retorts 7 and 8 suggests that some of these problems may have been overcome. This paper addresses some aspects of in situ retorting and problems that have impeded the development of a viable oil shale industry in the US.

Jan 1, 1986

By C. G. McLachlan

THIS paper outlines a series of tests carried out during the first six months of 1927, in the laboratory and mill of the Moctezuma Copper Co. The object of the tests was to determine whether the soluble salts present in the mill circuit water were having a detrimental effect on the recovery made by flotation. To accomplish this object a series of water analyses were made, followed by flotation experiments in which definite quantities of the salts found were added as addition agents. Before proceeding to describe the results obtained in the course of the investigation, reference will be made to five articles that have appeared during the last two years in which the action of such salts is discussed. Two of these are by A. T. Tye1,2 and describe flotation practice at Cananea and the way in which water high in ferrous and ferric salts is conditioned for differential flotation. Two, one by A. C. Munro and H. A. Pearse3 and the other by H. A. Pearse,4 outline Britannia milling methods, and the advantages that have been derived from ore washing; while in the fifth, A. W. Hahn5 summarizes the results of laboratory experiments in which ferrous, ferric and aluminum sulfates have been added in varying amounts. The mill of the Moctezuma Copper Co. has a daily capacity of 3000 tons, and is situated about 75 miles south of Douglas, Arizona, on the Rio de Nacozari, in the Mexican state of Sonora. The ore treated is mined from the company&apos;s mine at Pilares, about 5 miles southeast of the Concentrator. This ore contains about 2.5 per. cent. copper -- present almost entirely as chalcopyrite-and 10 per cent. iron, of which

Jan 1, 1928

By C. H. Li, J. Washburn, E. R. Parker

Yield stress in single crystals of zinc was shown to be dependent on prior annealing temperature and rate of cooling after annealing. Rate of strain hardening beyond the yield was not sensitive to annealing procedure. A tentative mechanism for the effect was discussed. COMPARATIVE mechanical tests of metal single crystals generally show a large scatter of results. Many factors may contribute to this variation. The present investigation was undertaken to evaluate the influence of two factors not ordinarily considered of major importance—annealing temperature and cooling rate after annealing. Since plastic properties of crystals are thought to depend on the presence of lattice imperfections, it follows that a variation in properties should result from differences in the distribution and density of these imperfections. Furthermore, in the light of current theories of interaction between edge dislocations and lattice vacancies,&apos; it seems possible that annealing temperature and subsequent rate of cooling might play a part in this distribution. Analysis of the effect of these variables on plastic properties may lead to a better understanding of the annealed state. Single crystals of zinc which have been strained in simple shear undergo complete recovery of mechanical properties upon subsequent annealing. This behavior is useful because a single specimen can be used repeatedly, thus eliminating the uncontrollable variables introduced by the use of many crystals. The test section of the crystals used for these experiments was a cylinder 1/8 in. thick with a cross-sectional area of about 1/3 sq in. The specimens were acid-machined from spherical single crystals 1 in. in diameter in such a way that the slip plane (0001) was at right angles to the axis of the cylinder. In testing, a shear stress was applied along one of the slip directions, [2110] in the (0001) plane.&apos; All crystals, unless otherwise noted, were grown in a helium atmosphere from molten 99.99 pct pure Horse Head Special Zinc. Fig. 1 is a family of curves obtained from one crystal. Each curve was obtained by deforming the crystal to 10 pct strain at a rate of 3 pct per min, following an anneal of 1 hr at 260°C. The strain direction was reversed every other time so that no progressive change in shape of the specimen took place during the series of tests. Since the stress-strain curve was reproducible within a fairly narrow range under the same conditions of annealing, it was then possible to determine the effect of changes in annealing conditions. A crystal was tested repeatedly as previously described but the annealing temperature and rate of cooling preceding each test were varied (Fig. 2). Two cooling rates were used, approximately 30°C per min and 3°C per min. Annealing was conducted at three temperatures, 200°, 300°, and 400°C. For a given annealing time and rate of cooling the room temperature flow stress was higher the higher the annealing temperature. The increase in flow stress was small as the annealing temperature was increased from 200° to 300°C but rose rapidly when the annealing temperature was raised from 300" to 400°C. Faster cooling from the high temperature produced an even greater strengthening of the crystal. The curves were obtained in the order indicated by the numbers. The stress level associated with a certain annealing treatment was, within the limits of scatter, always the same regardless of the

Jan 1, 1954

By P. Shahinian, R. L. Stegman, M. R. Achter

Creep strength has been determined as a function of oxygen pressure for nickel at 510" and 600°C. Creep-rupture life drops from its highest value at the ultimate vacuum of 10-7 torr to a high pressure plateau of nearly constant life which, at 600°C, commences at torr. This behavior is described in terms of a model that relates surface gas adsorption and the generation of fresh crack surfaces. In a calculation based a this model the predicted pressure beyond which the creep strength should not decrease further has been found to agree well with the observed value. The introduction of oxygen during creep in vacuum was found to cause a prompt rise of the creep rate. The magnitude of the environmental effect was much less than generally observed in fatigue and this is attributed to the diffarent crack morphologies in creep and fatigue. GASEOUS environments are known to affect creep resistance adversely1-5 but the effects have received less attention than the much larger ones in fatigue. At low temperatures it has been shown for nickel that the creep rates are faster and the rupture lives are shorter in air than in vacuum and that these environmental effects can be correlated with faster crack growth rates in the reactive environment.&apos; In support of a mechanism of gas adsorption at the crack tip to explain the above effects, a calculation based on kinetic gas theory showed that surface coverage by gas was not as rapid as the exposure of fresh metal at the crack tip in the ultimate vacuum but was in air.7 In fatigue a number of investigations have demonstrated that the reduction of life with gas pressure usually follows a step curve with most of the reduction occurring in a transition range at intermediate pressures and little or no change at high and low pressure.8 There have been no studies, however, in which creep strength has been determined as a function of reactive gas pressure to see whether similar effects would be found. This investigation was undertaken to study the kinetics of the environmental effect in the creep of nickel. EXPERIMENTAL PROCEDURES The environmental creep apparatus was constructed to minimize many of the experimental conditions which can cause scatter in data. Dead weight loading is employed and weights are contained within the environmental chamber to eliminate bellows and the necessity for compensation for gas pressure changes. Elongation over the specimen gage length is recorded from a Riehle Model DV Controlled Environment Extensometer which provides readout to 2.5 x 10- in. Temperature is monitored and controlled from a thermocouple at- tached to the specimen gage length to +0.5oC or better. The freon trapped oil diffusion pump vacuum system included an auxiliary liquid nitrogen trap and, with a wide range variable conductance leak valve, pressures from the ultimate vacuum of 10"7 to l03 torr of any desired gas are obtainable. Pressure is measured by means of a hot filament ionization gage below 10"3 torr and a NRC Model 530 Alphatron Vacuum Gauge above 10-3 torr. The oxygen, which was leaked into the environmental chamber, was an Aviator&apos;s Grade of 99.5 pct purity with a dew point of -80°F. Analysis of the nominal 99.8 pct Ni showed the following percentages of major impurities: 0.02 C, 4.01 Mn, 0.005 Si, 0.01 Cu, 0.02 Fe, and 0.034 Mg. Cylindrical specimens were machined with a 0.180

Jan 1, 1970

By Erwin Pink

It has been pointed out in a previous publication&apos; that, for a given strain rate, serrated yielding can be observed only at certain test temperatures. Fig. 1 shows the results obtained for polycrystalline and re-crystallized tantalum, Va group in the periodic table of elements, where serrations in the course of deformation match the decrease of total elongation. However, there was no evidence of repeated yielding when testing molybdenum or tungsten, VIa group, at similar conditions, i.e., annealed and air-cooled samples (serrations have been found in quenched tungsten2). The reason for the observed serrations in the stress-strain curve are dissolved impurities on interstitial sites of the lattice. Of importance is the concentration of oxygen, carbon, and nitrogen, which are in random solution. Two methods to calculate the limiting concentrations for serrated yielding have been evaluated and applied with more or less success in estimating the role of carbon and nitrogen in mild steel.3 J. Friedel4 has given two equations, which determine the upper and lower strain rates i for the appearance of serrations at a certain test temperature: W denotes the binding energy of the interstitial atom, -1 ev for refractory metals;5 e&apos; the portion of continuous strain in the discontinuous stress-strain curve, measured as -3x10-3; b the Burgers vector, c the concentration, see Table 11, in atom fractions; p the dislocation density, -2 X l09 per cm2 at an average stress ?, -15 kp per mm2 at medium strain. k stands for the Boltzmann constant, T for the absolute temperature, and D for the diffusion coefficient. Table I. Eq. [1], for a given strain rate, determines the minimum temperature, and [2] the maximum temperature, below or above which no "dynamic strain-aging" can occur. According to the calculation, which uses the given quantities, serrations should only be observed within the cross-hatched temperature regions in Fig. 1, and this is in good agreement with the experiment. The effect of varying impurity concentrations is indicated schematically in Fig. 2: only Eq. [I] is affected. Setting Eq. [I] equal to [2], one can calculate the limiting concentration cmin which first causes serrations. The second method uses the aging condition by Cottrell and Bilby6,7 \£i/ \ n. a / where n(t) is the number of impurity atoms, which segregate at a dislocation line of 1 cm length after the time t (t in our case is the time between "repeated yield drops" in the serrated curve, or, the time until the above mentioned strain E&apos; is obtained, i.e., -1 sec for medium intensity or serrations). no is the number of impurity atoms in 1 cm3 and A = Qb4ep[(1 + v)/(l - v)], derived from equations given in Ref. 7. p is the shear modulus, 18,800 kp per mm2 for tantalum, 12,200 for molybdenum, AE the tetragonal distortion caused by interstitial impurities in a bcc lattice (approximately 0.4 for both tantalum and molybdenum) and v Poisson&apos;s ratio (0.35 for tantalum, 0.30 for molybdenum). From Eq. [3], combined with the condition for a pronounced yield drop as formulated by cottrel16 (at least one impurity atom segregated at the unit length of a dislocation), again a no min, and hence the concentration Cmin can be calculated.

Jan 1, 1970

By W. D. Robertson, A. S. Tetelman

The technique of decorating dislocations was employed to investigate deformation and fracture resulting from Precipitation of hydrogen in Fe-3 pet Si single crystals. It is shown that cracks are produced on (100) planes inside crystals, as a consequence of the precipitation of hydrogen gas, either when crystals are quenched from a hydrogen atmosphere at elevated temperatures or cathodically charged with hydrogen at room temperature. Plastic deformation in the vicinity of cracks, observed as arrays of decorated dislocations, is in conformity with the calculated stress distribution about a crack containing an internal pressure, and the observations provide information permitting a detailed analysis of the mechanics of crack growth. The fracture characteristics of crystals containing internal cracks were evaluated at 25o and -196°C and the results are related to the mechanism of hydrogen embrittlement in terms of the growth of preexisting cracks. HYDROGEN in bee iron or steel produces two characteristic changes in mechanical properties: I), a decrease in ductility (macroscopic strain at fracture) that depends on temperature and strain rate, and 2), spontaneous fracture under static load that depends on time and apparent stress. Resolution of these phenomena into the microscopic processes that combine to produce the macroscopic effects is especially difficult in the Fe-H system in which the active component cannot be directly observed and only maintained in equilibrium with great difficulty in the temperature and pressure range in which embrittlement phenomena appear. As a result of these complications, verification of the numerous hypotheses&apos;-5 that have been proposed to explain the microscopic mechanism of embrittlement depends on self-consistency with measured changes in macroscopic properties that are averaged over the volume of a specimen. It is obviously important to obtain a more direct evaluation of the microscopic processes that combine to produce embrittlement. Accordingly, the present investigation was designed to identify and observe, as directly as possible, the microscopic effects of introducting hydrogen into a bee crystal. It was concluded from a previous investigation6 of X-ray line broadening, produced by introducing hydrogen into pure iron at room temperature, that the only effect that could be associated with the introduction of hydrogen was plastic deformation; in particular, dilation of the lattice was not observed, within ± 0.01 pet, and no evidence was found that could be interpreted to support the idea7&apos;* that hydrogen occupies tetrahedral interstitial sites in the iron lattice. The absence of lattice dilation is consistent with the extremely small solubility of hydrogen in bee iron9,10 (0.015 at. pet at 900oC and 1 atm pressure), and the evidence of plastic deformation is consistent with the fact that hydrogen, introduced by cathodic charging, eliminates the carbon yield point.11-13 Following this investigation, the immediate problem was to devise a method by which plastic deformation could be observed directly. The technique employed by Hibbard and Dunn14 to observe the movement of dislocations during bending and subsequent polygonization of Fe-3 pet Si single crystals was adopted and modified for the present purpose to include the observation of dislocation arrays in the volume of the crystal, and their association with the fracture process. EXPERIMENTAL PROCEDURE Single crystals of a high purity Fe-3 pet Si alloy, containing 0.007 pet C, were grown in vacuum by

Jan 1, 1962

By E. V. Manlapig, David J. Spottiswood

In recent years great advances in the automatic control of flotation plants have been made, mainly due to the development of reliable sensing instruments to monitor process performance and the development of an adequate understanding of system responses to process disturbances. Some of the control strategies used in flotation plants which apply computer control are presented here. These schemes, which involve the control of collector; depressant, frother, and air and pulp level, are analyzed with respect to their control objectives, control variables, and the instrumentation involved. The knowledge gained in understanding these strategies may be applied in the dew and implementation of control system in other concentrators.

Jan 1, 1981

By F. Weinberg

WHEN impure Zn (< 99.99 pct)&apos;&apos;Z or Zn-Cd alloys3 are progressively solidified, a cell or "corrugation" substructure4 is produced in the solid, with a high impurity or solute concentration along the cell walls. When these materials are polished and suitably etched, etch pits are often observed along the cell walls. For the Zn-Cd alloys these etch pits have been associated with decorated dislocations, present in the corrugation boundaries to accommodate the lattice strain. In the course of an investigation of Zn-2 pct Au alloy, molten metal of this alloy was poured into cold water and the resultant solid pieces were sectioned, polished and etched with a Cr0 ethant. An extremely regular cell pattern was observed on the etched surface, similar in general to the corrugation structure previously reported for impure zinc and Zn-Cd alloys. At higher magnification, regularly spaced pits were observed along the cell boundaries. An example of the regular cell pattern at the center of a specimen is shown in the center and lower portions of Fig. 1; the top of the figure shows the pattern near the specimen surface. Typical etch pits in the cell walls are shown in Fig. 2. It was surprising that a cell pattern as regular as that shown in the center of Fig. 1 was produced at the very rapid solidification rates used (estimated as > 1 cm per sec). In addition, the distribution coefficient for the Zn-Au system is greater than 1. Accordingly, the center of the cells should be rich in solute and should etch

Jan 1, 1963

By B. Stas, L. Siska, L. Dlouhy, A. Skrabis

The basic research program of the Scientific Coal Research Institute at Ostrava - Radvanice into the problem of geophysics has been influenced by the specific nature of present urgent geo- physical problems in mines and directed to attain higher grade of effectiveness, safety, and overall economy in mining activity. The research has been divided into two basic trends: Seismoaccoustic research deals with questions pertaining to safety in mining especially when work is in coal seams under "heavy roofs", i-e., thick beds of sandstone prone to rock bumps and characterized by caving. Methods have been developed with the definite aim to determine the time and space prognosis of critical states of tension in the rock mass when stability is disturbed as a result of mining activity. Seismic research is directed towards the determination of detailed structural and tectonic elements of the internal geological formation of the Carboniferous rocks, the establishment of continuity or tectonic faulting of coal seams, and the evaluation of magnitude, shape, and time changes in the rock mass surrounding the mine workings. The measurements have been applied either from the surface or in the underground workings according to the specific nature of individual problems. Satisfactory results have been obtained in some branches of this research, other branches being still in the stage of development. Remarkable results have been achieved in the development of seismoaccoustic methods designed to establish the time prognosis of dangerous dynamic phenomena accompanying the process of strata deterioration above the worked longwall face. One of the most

Jan 1, 1971

By E. J. Whittenberger

OVER the past two decades, the Cr-Ni stainless steels, popularly termed 18-8 steels, have been used in ever increasing amounts in the aircraft, automotive, chemical, transportation, and building industries.&apos; The contribution of nickel to these steels is associated with its strong austenite forming tendencies which assure good hot and cold forming characteristics, and with its beneficial influence upon corrosion resistance, especially in oxidizing acids. The adjustment of the chromium and nickel contents has been used advantageously in controlling the rollability and the response of the mechanical properties of these steels to cold reduction. With the advent of the jet age and the government stockpiling of nickel, considerable emphasis has been placed upon the development of satisfactory low nickel or nickel-free substitute austenitic stainless steels, especially for nonmilitary applications.2 Fer-ritic 17 pct Cr (AISI Type 430) stainless steel has been effectively substituted for the austenitic grades in applications with mildly corrosive exposure. However, the limited formability and ferromagnetic behavior of this grade do not permit its satisfactory use for many applications. To achieve better formability in a nenmagnetic steel and conserve nickel, a number of low nickel substitute austenitic grades of stainless steel have been developed in recent years. In most of these steels, manganese and nitrogen have been substituted for a portion of the nickel content, for example, 17 pct Cr-4 pct Ni-6 pct Mn (AISI Type 201), 18 pct Cr-5 pct Ni-8 pct Mn (AISI Type 202), and 16 pct Cr-1 pct Ni-17 pct Mn, all of which contain approximately 0.15 pct N.1 The precipitation of ferrite when large ingots of these Cr-Ni-Mn-N steels are heated to temperatures high enough for conversion to slabs on conventional universal slabbing mills has seriously affected the hot workability of these steels. This has been especially true in the case of the 16 pct Cr-1 pct Ni-17 pct Mn (sometimes referred to as 15 pct Cr-1 pct Ni-15 pct Mn) composition." Because it is possible that little, if any, nickel will be available for nonmilitary stainless steel applications in the event of a national emergency, a need has existed for a nickel-free austenitic stainless steel containing hot and cold forming characteristics similar to 18-8 steels and corrosion resistance at least comparable to the 17 pct Cr ferritic steel. The aforementioned deleterious effect of ferrite upon the hot working characteristics of the 16 pct Cr-1 pct Ni-17 pct Mn, steel indicates the importance of establishing the austenite-austenite plus ferrite phase boundaries as the first step in the development of nickel-free or low nickel substitute steels. This paper presents the data collected in an elevated temperature constitutional study of the Cr-Ni-Mn-N system at the South Works of the United States Steel Corp. Experimental Procedure The 300 compositions used in the investigation were melted in a 26 Ib induction furnace and cast in 3 14 in. diam by 18 in tall hot-tcpped ingot mo1ds.

Jan 1, 1958

By D. C. Hilty, W. Crafts

L. S. Darken—Laboratory investigation of deoxidizing and other steelmaking reactions is usually centered, at least first, on the determination of the equilibrium or equilibria involved. This seems a reasonable procedure since equilibrium, if attained, depends only on composition, temperature, and pressure; hence conclusions derived from data on small experimental quantities are applicable to a heat of steel providing eauilibrium is attained in both cases. A knowledge of equilibrium serves as a useful framework even though we may know that practical conditions do not correspond to complete equilibrium. On the other hand, nonequilibrium or rate phenomena depend on a wider variety of conditions and are more difficult to interpret; conclusions applicable to laboratory conditions may or may not apply to larger scale phenomena. Hence the attainment or nonattainment of true equilibrium in the experiments here reported is of critical importance in evaluating their significance. Since some of the statements in this paper and in the closely related preceding one (on aluminum deoxidation) imply some doubt on this matter, I should first like to ask the authors whether their conditions are intended and believed to represent equilibrium. I should like to point out three considerations which seem to cast considerable doubt on the achievement of equilibrium, at least of the particular equilibrium under consideration. 1. In the experiments on manganese deoxidation the authors point out that they could not maintain the manganese-oxide slag on top of the metal in their rotating crucible, and hence they substantially dispensed with this slag. This leads to serious trouble in the interpretation of the results, for any equilibrium is, of course, a particular specific equilibrium—in this case Mn + O = MnO The experimental deletion of the upper layer of manganese oxide means that if equilibrium is attained at all it is attained between the metal and the MnO which has soaked into or adhered to the crucible (under the metal) and has dissolved substantial amounts of the crucible material including impurities. These impurities may constitute a significant portion of the slag by virtue of the small total amount of slag, even though the crucible is relatively pure. Hence there would seem to be a strong presumption that the equilibrium (if attained) involves not a pure MnO (or MnO — FeO) slag but one saturated with alumina and containing perhaps considerable impurities which substantially lower the concentration and activity of MnO, causing the above reaction to proceed to the right further than it would in the absence of alumina and impurities. Hence it is not surprising that manganese here appears as a better deoxidizer than found by other investigators. The present results may represent equilibrium with a slag of unknown composition which seems unlikely to be particularly related to plant experience. 2. The curves representing the observed silicon deoxidation (figs. 3, 4, and 5) are all drawn with a discontinuity in slope at about 0.02 pct oxygen. This point is interpreted as corresponding to the three-phase equilibrium, metal, slag, solid silica. The type of construction shown in these figures (though apparently fitting the data) is contrary to a fundamental principle of heterogeneous equilibrium as pertains to the construction of phase diagrams. According to this principle, the two solubility curves (each of the two portions of the curves in figs. 3, 4, and 5) must intersect in such manner that their (metastable) extensions must lie outside the homogeneous field rather than inside as in these figures. In other words, the "point" in these curves should be aimed in the opposite direction, if it is to be interpreted as corresponding to the three-phase equilibrium. The construction adopted is in violation of the second law of thermodynamics. This matter is discussed in detail in several texts and also by Lipson and Wilson.&apos;" The same criticism applies to the later figures representing conditions for manganese additions. The occurrence of this discontinuity or break at 0.02 pct oxygen casts further doubt on its interpretation. The earlier investigation of this system by Korber and Oelsen is in substantial agreement with the several recent findings of Chipman and coworkers that the oxygen content of iron in equilibrium with silica and silica-saturated iron oxide slag is about one third to one half that (0.24 pct at 1600") of iron saturated with pure iron oxide; thus there seems reliable evidence that iron saturated with silica and iron silicate slag at 1600" contains about 0.1 pct oxygen, or certainly much more than the 0.02 pct proposed in this paper. 3. In the quarternary system iron-silicon-manganese-oxygen one of the equilibria involved may be written 2 Mn + SiO2 (solid) = 2 MnO <slag> + Si The activity of SiO, is constant (if equilibrium is attained) by virtue of its presence as a substantially pure solid. At not too low metallic manganese content, the activity of MnO in the slag is constant by virtue of the fact that the slag is substantially pure manganese silicate saturated with silica and hence of constant composition. Thus the equilibrium constant for the above reaction is asi/a2Mn. Barring unanticipated large changes in the activity coefficients, the equilibrium constant may be adequately approximated for the composition range covered as [% Si]/[% Mn]2. Thus a plot of log [% Mn] against log [% Si] would be expected to be linear with a slope of one half as found by Kijrber and Oelsen. In the present investigation the slope (shown in fig. 15) is found to be one. It is difficult to believe that this finding represents a correct equilibrium determination, since it is at odds both with prior experimental investigation and with. theory. In view of the above points it seems that, although this paper reports many interesting findings, there is room for considerable skepticism as to the attainment of equilibrium and as to the conclusions drawn. N. A. Gokcen—The authors consider that Si% x O2% product is constant. This product is a function of the asi X a0 activity of Si02. The true constant is -------------. If the asio2 slags of this investigation were always saturated with SiO2 then Si% X O2% product would be constant,

Jan 1, 1951

By J. F. Enrietto

Internal friction measurements were used to determine the effect of manganese on the solubility and precipitation kinetics of nitrogen. Manganese, in concentrations up to 0.75 pct, has little effect on the solubility at temperatures above 250°C. On the other hand, at Concentrations as low as 0.15 pct, manganese inhibits the formation of iron nitrides, especially Fe4N, even though it may not form a precipitnte itself. The precipitation and solubility of carbides and nitrides have been extensively investigated in the pure Fe-C and Fe-N systems.1-3 In recent years, some effort has been ispent in studying the influence of substitutional alloying elements on the behavior of carbon and nitrogen in ferrite.4 -7 In particular Fast, Dijkstra, and Sladek have investigated the effect of 0.5 pct Mn on the internal friction and hardness during the quench aging of Fe-Mn-N alloys.&apos;, &apos; They found that at low temperatures (below 200°C) the presence of 0.5 pct Mn greatly retarded quench aging. For example, after 66 hr at 200°C very little precipitation had taken place in the iron alloyed with manganese, whereas precipitation was complete after a few minutes in a pure Fe-N alloy. The effect of varying the manganese content and the details of the precipitation process were not mentioned in these papers. Fast&apos; postulated that manganese causes a local lowering of the free energy of the lattice with a resulting segregation of nitrogen atoms to these low energy sites. The segregated nitrogen atoms are bound so tightly to the manganese atoms that they cannot form a precipitate. The internal friction measurements of Dijkstra and Sladek tended to confirm the concept of segregation of nitrogen around manganese atoms, and the increase in free energy on transferring a mole of nitrogen atoms from a segregated to a "normal" lattice site was computed to be - 2800 cal. Dijkstra and Sladek9 distinguished between two types of precipitates: ortho, a nitride of appreciably different manganese content than that of the matrix, and para, a nitride with a manganese content essentially that of the matrix. With each type of precipitate a solubility, again designated ortho or para, can be associated. Since the internal friction maximum in alloys which were aged several hours at 600" C dropped almost to zero, Dijkstra and Sladek9 concluded that the ortho solubility must be very low. The effect of temperature on the ortho and para solubilities has no1: been investigated. There are obviously several gaps in our knowledge concerning the influence of manganese on the behavior of nitrogen in a-iron. It was the purpose of the experiments described in this paper to determine the following: 1) The ortho and para solubilities of nitrogen as a function of temperature. 2) The details of the precipitation process at elevated temperatures. 3) The effect of varying the manganese concentration on the above phenomena. EXPERIMENTAL PROCEDURE Internal friction is conveniently employed in studying the precipitation of nitrides and/or carbides from a -iron because it is one of the few parameters, perhaps the only one, which is not affected by the presence of the precipitate itself. For this reason, internal friction techniques were heavily relied upon in the present experiment. A) Preparat of -. All specimens were prepared from electrolytic iron and electrolytic manganese. Alloys containing 0.15, 0.33, 0.65, and 0.75 wt pct Mn were vacuum melted and cast into 25 lb ingots. After being hot rolled to 3/4 in. bars, the ingots were swaged and drawn to 0.030 in. wires. The wires wen? decarburized and denitrided by annealing at 750° C for 17 hr in flowing hydrogen saturated with warer vapor. To obtain a medium grain size, - 0.1 mm, the wires were then heated to 945oC, allowed to soak for 1 hr, furnace cooled to 750°C, and water quenched. Subsequent internal friction measurements showed that this procedure reduced the nitrogen and carbon concentrations of the alloys to less than 0.001 wt pct. The wires were nitrided by sealing them in pyrex capsules containing anhydrous ammonia and annealing them for 24 hr at 580°C, the nitrogen being retained in solid solution by quenching the capsule into water. Immediately after quenching, the wires were stored in liquid nitrogen to prevent any precipitation of nitrides. By varying the pressure of ammonia in the capsule, it was possible to produce any desired nitrogen concentration. B) Internal Friction. The internal Friction measurements were made on a torsional pendulum of the Ke type,&apos;&apos; a frequency OF 1. or 2 cps being used. For

Jan 1, 1962

By K. Reinhardt

The idea of burning blast-furnace gases directly in gas-engines, instead of under steam-boilers, as had previously been done, was first put into practice barely ten years ago, almost simultaneously in Great Britain, Germany and Belgium. The pioneers of this movement made their first experiments with small engines. After these experiments had given satisfactory results, and it had been shown that the thermal value of the poor blast-furnace gases, in spite of defective scrubbing, could with safety be directly transformed into mechanical work in the gas-engine, there very soon arose a considerable demand for gas-engines of large power, similar to the large steam-engines employed in metallurgical works. In face of these sudden requirements, the gas-engine builders were placed in a difficult position; for up to that time the gas-motor was considered as suitable for small engines only, and it was generally believed that the limit of size had been attained with 100 to 150 effective h.p. in a single cylinder. Manufacturers of gas-motors, however, did not underrate the advantages offered by this new field for their manufactures, and it so happened that in Germany the Berlin-Anhaltische Masch-inenbau-Gesellschaft, of Dessau, was the first to undertake the construction of a 600-h.p. two-cycle gas-engine, with two cylinders of the Oechelhauser-Junkers type, for the Hoerder Mining & Smelting Company. The engine was started in 1898, and, with a few improvements and alterations, is still working satisfactorily. This engine worked with astonishingly high effciency, considering the period. The builders were therefore

Jan 1, 1907

By D. B. McGilvra

ANY mining operation in the Altiplano of the Andean range presents problems and imposes obligations on the mining company not usually met with in the United States. The Aguilar mine is in a sparsely populated, semiarid region, 50 km by road from the Argentine State railroad station of Tres Cruces, Jujuy, Argentina. In starting an operation in such a location it becomes necessary for the mining company to prepare first for the needs of the required force of workmen and their families. This program calls for houses, schools, hotels, water, electric power, laundries, post offices, police

Jan 1, 1947