Search Documents

By Kenneth C. Vincent, A. M. Gaudin

In a study1 of the action of amyl xan-thate on chalcocite in water suspension, it was found that if the xanthate is added in relatively large quantity the xanthate group can be accounted for in three forms: (1) as xanthate ion remaining in water, (2) as benzene-soluble cuprous xanthate on the chalcocite, (3) as a benzene-insoluble coating on the chalcocite. Reduction in the amount of xanthate added leads to disappearance of form I then of form 2. With minute quantities of added xanthate, substantially all the reagent is of the "unleachable" kind. Yet this unleach-able xanthate can be dissolved by pyridine to form a soluble cuprous xanthate complex, and it is sufficient in effectiveness to make chalcocite flotable even if insufficient in quantity to form a complete mono-molecular film on the mineral. In that study it was also found that chalcocite abstracts cuprous xanthate from benzene so1ution, in what may (or may not) be a case of molecular adsorption. It seemed desirable, therefore, to study further the "unleachable" xanthate on the chalcocite, and particularly to ascertain whether it is formed as a result of the benzene leach or is actually formed during the conditioning of chalcocite in aqueous xanthate solution. A 'splendid tool to make such studies has recently been perfected; that is, the use of radioactive spies or tracer atoms. With this tool, it was thought possible to answer the problem stated above, but, unfortunately, this did not prove to be true. Answer to the flotation question was clouded by the existence of rapid and selective diffusion of copper atoms in the solid mineral—a phenomenon that was totally unexpected yet remains interesting and perhaps important. Method of Radioactive Spies The method of radioactive spies is discussed in many places. Two convenient references are the article by Evans2 and the book by pollard and Davidson.3 The method was first developed by van Hevesy and paneth in 1013, when only natural radioactive isotopes were available. These isotopes are few in number, and so the method remained limited in scope. Recently the synthesis of over 350 active isotopes of all the known stable chemical elements4 has opened widely expanded possibilities for the method, A fundamental tenet of the method is that a radioactive atom and a nonradio-active atom are exactly alike until disintegration of the radioactive atom. Then, by its sudden death, the spy reveals its location. The relative abundance of spies at various locations makes it possible to ascertain the relative abundance of the corresponding nonradioactive atoms at the same times and locations. A second fundamental tenet of the method of radioactive tracers is that the radioactivity lies in the nucleus of the atom: transfer of radioactivity from one

Jan 1, 1947

By Earl W. Palmer, Cyril Stanley Smith

StKip of any of the metals used for deep drawing operations occasionally yields cups that are defective because of a rim that varies in height around the cup in a wave-like manner. Some such defects are traceable to tools or other press factors, but when the protuberances formed (usually four in number on brass and other copper alloys) are symmetrically disposed with respect to the rolling direction of the strip, they are invariably attributable to the metal. The effect is known as "earing" and the protuberances are called "ears." Other terms frequently heard are "tips," "scallops," and "corners." It is recognized that the effect is most commonly a result of a directional crystal structure produced by rolling and annealing operations in the manufacture of the metal strip. Numerous papers dealing with various aspects of the earing effect have appeared in the literature, those listed in the references1 being especially interesting and valuable. An investigation of the factors influencing earing of brass cups has been in progress in the laboratories of the American Brass Co. for several years, and it was thought desirable to make some of the results generally available in summarized form. The present paper discusses many factors that do and do not contribute to ear formation. In addition, a section is devoted to methods of minimizing the earing tendency of brass sheet by proper selection of the cold-rolling and annealing schedule by which it is produced. In the space available, it is impossible to quote detailed experimental procedures and numerical results. However, the authors make no statement that they do not believe to be properly substantiated, either by experimental evidence obtained under laboratory conditions or by experience in the actual production of deep-drawing brass in the brass mill. Mechanism of Ear Formation It must be clearly understood that the formation on cups of symmetrical ears, four or more in number, is attributable solely to the strip metal, and results from the strip having different deformation characteristics in different directions. The tools used in the drawing process, or the type and completeness of lubrication of the strip, have nothing to do with the problem of ears, although they do, of course, greatly affect the "drawing quality" of the strip and the general appearance of the cup. A single tip may be drawn up on the rim of a cup because of misalignment of the tools, or because the gauge of metal varies from side to side of the strip. The two-ear form that sometimes appears is also traceable to gauge variations. However, the four-ear and six-ear symmetrical forms that we are concerned with here are caused by factors inherent in the structure of the metal itself.

Jan 1, 1942

By Cyril Stanley Smith, Earl W. Palmer

StKip of any of the metals used for deep drawing operations occasionally yields cups that are defective because of a rim that varies in height around the cup in a wave-like manner. Some such defects are traceable to tools or other press factors, but when the protuberances formed (usually four in number on brass and other copper alloys) are symmetrically disposed with respect to the rolling direction of the strip, they are invariably attributable to the metal. The effect is known as "earing" and the protuberances are called "ears." Other terms frequently heard are "tips," "scallops," and "corners." It is recognized that the effect is most commonly a result of a directional crystal structure produced by rolling and annealing operations in the manufacture of the metal strip. Numerous papers dealing with various aspects of the earing effect have appeared in the literature, those listed in the references1 being especially interesting and valuable. An investigation of the factors influencing earing of brass cups has been in progress in the laboratories of the American Brass Co. for several years, and it was thought desirable to make some of the results generally available in summarized form. The present paper discusses many factors that do and do not contribute to ear formation. In addition, a section is devoted to methods of minimizing the earing tendency of brass sheet by proper selection of the cold-rolling and annealing schedule by which it is produced. In the space available, it is impossible to quote detailed experimental procedures and numerical results. However, the authors make no statement that they do not believe to be properly substantiated, either by experimental evidence obtained under laboratory conditions or by experience in the actual production of deep-drawing brass in the brass mill. Mechanism of Ear Formation It must be clearly understood that the formation on cups of symmetrical ears, four or more in number, is attributable solely to the strip metal, and results from the strip having different deformation characteristics in different directions. The tools used in the drawing process, or the type and completeness of lubrication of the strip, have nothing to do with the problem of ears, although they do, of course, greatly affect the "drawing quality" of the strip and the general appearance of the cup. A single tip may be drawn up on the rim of a cup because of misalignment of the tools, or because the gauge of metal varies from side to side of the strip. The two-ear form that sometimes appears is also traceable to gauge variations. However, the four-ear and six-ear symmetrical forms that we are concerned with here are caused by factors inherent in the structure of the metal itself.

Jan 1, 1942

By D. W. Philips

The problem of strata control has of necessity been prominent in mining, and accounts of individual experience and research abound in the literature of most mining countries. Organized rescarch began in Britain by the formation of a committee, upon the recommendation of the Safety in Mines Research Board in 1923, to investigate methods of reducing accidents from falls of roof in coal mines. This committee examined current practice in supporting underground workings in the principal coal fields, and its findings have been published in the Board's publications.' - Toward the end of these investigations it was suggested by the Chief Inspector of Mines that committees of the several mining institutes be formed to examine the problem in their respective districts. The formation of these committees marked a new phase in research on strata control. The work, though being done in the separate coal fields, followed a scheme outlined by the chief Mining Engineer of the Research Board, and was coordinated by his office. FACTORS INVOLVED The subject is being considered in Britain from two aspects: 1. To provide. by supports, means to prevent falls of fractured ground. 2. TO develop methods whereby the strata can be maintained in the least broken condition and thus make falls less likely. The first aspect is the one that will most likely lead to immediate results from the accident standpoint. It depends largely upon the assimilation of already acquired knowledge regarding the properties of supports and their correct application. The second aspect is perhaps more fundamental, and involves also the properties of the strata and their behavior under the influence of the forces induced by mining. The problem involves many natural factors that cannot be controlled, such as depth, inclination and thickness of seam and nature of the rocks. Other factors, which may be considered to a certain extent controllable, cannot be varied readily and with sufficient frequency to facilitate easy investigation; some of these are: rate of advance of the working face, length of face, direction of the face with regard to cleat and inclination, system and arrangements of rock packing behind longwall faces. In any given case the very many factors present have a mutual influence upon the effects produced in the mine. For example, a study of the effects of rate of advance cannot be done without considering the effects of other factors such as nature of strata, direction of face and quality and arrangement of supports. Conversely, the length and direction of a working face

Jan 1, 1947

By D. W. Philips

The problem of strata control has of necessity been prominent in mining, and accounts of individual experience and research abound in the literature of most mining countries. Organized rescarch began in Britain by the formation of a committee, upon the recommendation of the Safety in Mines Research Board in 1923, to investigate methods of reducing accidents from falls of roof in coal mines. This committee examined current practice in supporting underground workings in the principal coal fields, and its findings have been published in the Board's publications.' - Toward the end of these investigations it was suggested by the Chief Inspector of Mines that committees of the several mining institutes be formed to examine the problem in their respective districts. The formation of these committees marked a new phase in research on strata control. The work, though being done in the separate coal fields, followed a scheme outlined by the chief Mining Engineer of the Research Board, and was coordinated by his office. FACTORS INVOLVED The subject is being considered in Britain from two aspects: 1. To provide. by supports, means to prevent falls of fractured ground. 2. TO develop methods whereby the strata can be maintained in the least broken condition and thus make falls less likely. The first aspect is the one that will most likely lead to immediate results from the accident standpoint. It depends largely upon the assimilation of already acquired knowledge regarding the properties of supports and their correct application. The second aspect is perhaps more fundamental, and involves also the properties of the strata and their behavior under the influence of the forces induced by mining. The problem involves many natural factors that cannot be controlled, such as depth, inclination and thickness of seam and nature of the rocks. Other factors, which may be considered to a certain extent controllable, cannot be varied readily and with sufficient frequency to facilitate easy investigation; some of these are: rate of advance of the working face, length of face, direction of the face with regard to cleat and inclination, system and arrangements of rock packing behind longwall faces. In any given case the very many factors present have a mutual influence upon the effects produced in the mine. For example, a study of the effects of rate of advance cannot be done without considering the effects of other factors such as nature of strata, direction of face and quality and arrangement of supports. Conversely, the length and direction of a working face

Jan 1, 1947

By I. Lowthian Bell

THERE has been probably no improvement introduced into the manufacture of iron which created more surprise in the minds of practical smelters and of scientific men than Neilson's discovery of the hot blast. In 1829, Messrs. Dunlop & Co. consumed at the Clyde Works, near Glasgow, nearly 7 3/4 tons of coal to make a ton of pig iron, of which about 20 cwts. was employed under the boilers of the blowing engines, leaving nearly 7 tons for the consumption of the furnace itself. In the year 1833, by heating the air to 612° F. (322° C.), they reduced the 7 3/4 tons to 3 tons by the mere burning of 8 cwts. of coal in the apparatus for raising the blast to this temperature. The statement just given is strictly true in a commercial sense, but when we come to consider the question as one of physical science, it is necessary to eliminate some of the conditions which conduced to so extraordinary a result. Anterior to Neilson's time the fuel employed in smelting iron was coke, and it was supposed at that period, erroneously, however, that coal in its raw state, when burned with cold air, was totally unfit for the purpose in question. This mineral, as it was obtained from the Lanarkshire coal-field, contained about 35 per cent. of volatile matter, but the process of charring it was performed in so unskilful a manner that instead of receiving 88 cwts. of coke from 135 cwts. of coal, 60 cwts. only was the product of the operation. Again, the reduced consumption of carbon in the furnace itself was accompanied by a corresponding diminution of blast, and this was followed by an economy of half a ton in engine coal. After making a proper allowance, however, for all these collateral circumstances, we are within the mark when we admit that in actual coke, which is really the form the fuel has to assume before it is burnt in the blast-furnace, not less than 30 cwts. was saved by heating the blast to 615° F. (322° C.). This unexpected economy, be it remembered, was obtained by the combustion of the 8 cwts. of coal, somewhat wastefully applied in the hot-air apparatus. Numerous have been the opinions advanced by different authorities in the scientific world to account for the apparent anomaly, but none,

Jan 1, 1877

By Anson Hayes, John Chipman

The quality of sheet and strip products made of rimming steel is closely related to the structure and chemistry of the ingots. The variation in composition throughout the ingot, as affected by segregation, is of great importance, as are also the form and distribution of the voids that result from the gases evolved. It is because of this importance that the considerable literature in this field has accumulated. No attempt is made in the present paper to compile a bibliography of the excellent work that has already been done, as this has been adequately covered in the many excellent reports on the heterogeneity of steel ingots prepared by a joint committee and published by the Iron and Steel Institute.' From time to time, in any field of investigation new tools and new technique are developed, which make further progress possible. In the field with which this paper is concerned, this is true. The development of the vacuum-fusion method as a means of following oxygen segregation, and a technique for obtaining the volume and composition of the gases evolved during solidification, have opened the way to obtaining data by means of which some considerable progress has been realized in developing more of the detailed mechanisms of solidification and segregation in rimming-steel ingots. General Theory of Segregation The basic cause of segregation lies in the fact that the impurities are less soluble in solid than in liquid iron. The solid that forms from the impure liquid is more nearly pure than the liquid itself. If solidification proceeds slowly enough, or if the liquid and solid phases are maintained in contact with one another for a sufficient time, a condition of equilibrium is set up, which may be represented by a phase diagram. Portions of the

Jan 1, 1939

By Anson Hayes, John Chipman

The quality of sheet and strip products made of rimming steel is closely related to the structure and chemistry of the ingots. The variation in composition throughout the ingot, as affected by segregation, is of great importance, as are also the form and distribution of the voids that result from the gases evolved. It is because of this importance that the considerable literature in this field has accumulated. No attempt is made in the present paper to compile a bibliography of the excellent work that has already been done, as this has been adequately covered in the many excellent reports on the heterogeneity of steel ingots prepared by a joint committee and published by the Iron and Steel Institute.' From time to time, in any field of investigation new tools and new technique are developed, which make further progress possible. In the field with which this paper is concerned, this is true. The development of the vacuum-fusion method as a means of following oxygen segregation, and a technique for obtaining the volume and composition of the gases evolved during solidification, have opened the way to obtaining data by means of which some considerable progress has been realized in developing more of the detailed mechanisms of solidification and segregation in rimming-steel ingots. General Theory of Segregation The basic cause of segregation lies in the fact that the impurities are less soluble in solid than in liquid iron. The solid that forms from the impure liquid is more nearly pure than the liquid itself. If solidification proceeds slowly enough, or if the liquid and solid phases are maintained in contact with one another for a sufficient time, a condition of equilibrium is set up, which may be represented by a phase diagram. Portions of the

Jan 1, 1939

By W. T. Ober

the hammering effect acts only to a point 3 in. back from the cutting edge, and the hardening heat extends back only 1 in. from the cutting edge. Then, as a steel is taken from the fire, the grain condition is as shown in Fig. I. After the forging operation has been performed the condition shown by Fig. 2 exists. The heating operation to harden the cutting edge produces the effect shown in Fig. 3. The questions that naturally arise are: Will the cost of the extra heat treatment necessary to change this condition (annealing) be more than the saving that may be effected in the drill steel or will the extra heating be an economical as well as a wise thing to do? Is this condition necessarily detrimental to the maximum service of the drill steel? Can this annealing action be obtained in the hardening heat by heating more of the bit, say at least 5 in., to the hardening temperature but quenching only the end of the bit by a shallow immersion? Short Rock-drill Steels Reclaimed by Welding By W. T. Ober, Lynn, Mass. Experimental tests by the Thompson Company have shown that short lengths of rock-drill steels may be reclaimed by electric butt welding. The drills used in the experiments were hollow drills l1/4-in. in diametcr containing 0.95 per cent. to 1.05 per cent. carbon. The ends to be joined must first be ground off fairly square and the greater part of the rust, scale, etc. removed for 3 or 4 in. back in order to insure good electrical contact with the dies of the welder and countersunk, with an 80° countersink, approximately 1/4 in. The steels are then clamped in the copper dies of the welder, so that a length projects from the inside edge of each pair of dies equivalent to from one-half to three-quarters the diameter of the drill. The drills should also be brought into accurate alignment. The first step is to bring the ends into close proximity and then close the primary circuit of the transformer, slowly bringing the steels together until their ends lightly touch, when they will "flash," that is, minute

Jan 1, 1922

By W. T. Ober

the hammering effect acts only to a point 3 in. back from the cutting edge, and the hardening heat extends back only 1 in. from the cutting edge. Then, as a steel is taken from the fire, the grain condition is as shown in Fig. I. After the forging operation has been performed the condition shown by Fig. 2 exists. The heating operation to harden the cutting edge produces the effect shown in Fig. 3. The questions that naturally arise are: Will the cost of the extra heat treatment necessary to change this condition (annealing) be more than the saving that may be effected in the drill steel or will the extra heating be an economical as well as a wise thing to do? Is this condition necessarily detrimental to the maximum service of the drill steel? Can this annealing action be obtained in the hardening heat by heating more of the bit, say at least 5 in., to the hardening temperature but quenching only the end of the bit by a shallow immersion? Short Rock-drill Steels Reclaimed by Welding By W. T. Ober, Lynn, Mass. Experimental tests by the Thompson Company have shown that short lengths of rock-drill steels may be reclaimed by electric butt welding. The drills used in the experiments were hollow drills l1/4-in. in diametcr containing 0.95 per cent. to 1.05 per cent. carbon. The ends to be joined must first be ground off fairly square and the greater part of the rust, scale, etc. removed for 3 or 4 in. back in order to insure good electrical contact with the dies of the welder and countersunk, with an 80° countersink, approximately 1/4 in. The steels are then clamped in the copper dies of the welder, so that a length projects from the inside edge of each pair of dies equivalent to from one-half to three-quarters the diameter of the drill. The drills should also be brought into accurate alignment. The first step is to bring the ends into close proximity and then close the primary circuit of the transformer, slowly bringing the steels together until their ends lightly touch, when they will "flash," that is, minute

Jan 1, 1922

By Thomas L. Wright

Exploration activities were maintained at a high level throughout 1966. Numerous significant discoveries and developments in which geologists played an important part were announced. Although the complete results of exploration activities carried out during the year by private companies have not been announced, the following are among the more important developments that have been made public knowledge. In the western states, exploration for practically all of the metals continued at a high rate. Substantially increased interest in uranium occurred this year, and it is felt by many that a real boom in the demand for uranium may come about in the near future. The reasons have been the more rapid acceptance of atomic power than had been anticipated, and that uranium producers can now sell their product to private interests and even foreign countries. A tremendous demand for uranium is anticipated by many, and this has rekindled exploration activity. On the Colorado Plateau, in Wyoming, and in the area around Grants, N. M., a number of companies have undertaken uranium exploration programs, among which are Kerr-McGee, Homestake, Anaconda and Utah Construction. A new uranium orebody in Texas was brought into production early in 1966 by Susquehanna Western.

Jan 2, 1967

By Minoru Sasabe, Mayurni Sorneno, Kazuhiro Goto

I) The Object of the Present Experiment. When the oxygen chemical potential in the gas phase is changed, the oxygen chemical potential in the liquid metal or in the liquid oxide phase will be subsequently changed. The object of the present experiment is to develop a method of measuring the change in the chemical potential of oxygen in liquid metals and in liquid oxides with respect to time, when the oxygen potential in the gas phase changes. II) The Experimental Method. The following types of the oxygen concentration cells with the solid electrolyte of Zr0z-CaO are used: KAZUHIRO GOTO, MemberAIME.MINORU SASABE,and MAYUMl SOMENO are Associate Professor, Research Associate, and Professor, respectively, Department of Metallurgical Engineering, Tokyo Institute of Technology, Meguro-ku, Tokyo, Japan. Manuscript submitted March 12, 1968, EMD. Igas phase liquid Ag or Pb ZrO2-CaO electrolyte!, The measured reversible electromotive force can be expressed by the next equation, provided that the transference number of the oxygen anion in the electrolyte is unity: E = RT/nF log (at electrode I)/P~ (at electrode 11) where is the electromotive force, R is the gas constant, T is absolute temperature, n is valence of oxygen anion, and Pq is the oxygen pressure at the electrodes. As shown in the previous work1 of the authors, the electromotive force is determined by the difference in the chemical potential of oxygen at the vicinity of the interfaces between the solid electrolyte and the electronic conductors used for the two electrodes. Fig. 1 shows the two kinds of the cell assembly used to measure the change of the chemical potential of oxygen in liquid metals and liquid oxides with respect to time. In both cases, the change of the oxygen pressure in the gas phase is measured by the independent oxygen concentration cell located above the

Jan 1, 1969

By C Macquarie, Maurice Cook

Normally the grain size of cold-rolled and annealed copper sheet is of the order of 0.02 to 0.06 mm., and 0.1 mm., for example, would, for many purposes, be regarded as undesirably large. The occurrence of very large grain sizes in a few isolated cases of copper sheet led the authors to inquire into the causes giving rise to such unusual results. During the course of this work a very large number of experiments have been carried out to determine the effect of varying the conditions of the final and penultimate rolling and annealing operations, as well as of earlier rolling and annealing treatments. A correspondingly large number of observations have been made, but within the space of one paper it is possible only to outline relatively briefly what appear to be the more important of these experiments and observations. The presentation of the results does not follow chronologically the order in which the experiments were carried out and they have been rearranged for the sake of simplicity. In recent years a considerable amount of work has been done in connection with the recrystallization and grain growth in metals arid alloy. that take place on annealing, and a number of generalizations have beell reached. It is known that the crystal size in wrought material in the annealed condition depends on a number of factors, including the time and temperature of the annealing operations and the nature and amount of cold-work to which the material has been subjected. Results. however that are not covered by these generalizations can be obtained, which, in some instances, may even appear to be contradictory to them. Xccortling to these generalizations gradual changes in grain size are effected by progressive variation of the factors involved in annealing or cold-working. The work recorded in the present paper, however, relates to the development of grain sizes which are far beyond those normally encountered in ordinary annealing operations and far in excess of grain sizes which,

Jan 1, 1939

By C Macquarie, Maurice Cook

Normally the grain size of cold-rolled and annealed copper sheet is of the order of 0.02 to 0.06 mm., and 0.1 mm., for example, would, for many purposes, be regarded as undesirably large. The occurrence of very large grain sizes in a few isolated cases of copper sheet led the authors to inquire into the causes giving rise to such unusual results. During the course of this work a very large number of experiments have been carried out to determine the effect of varying the conditions of the final and penultimate rolling and annealing operations, as well as of earlier rolling and annealing treatments. A correspondingly large number of observations have been made, but within the space of one paper it is possible only to outline relatively briefly what appear to be the more important of these experiments and observations. The presentation of the results does not follow chronologically the order in which the experiments were carried out and they have been rearranged for the sake of simplicity. In recent years a considerable amount of work has been done in connection with the recrystallization and grain growth in metals arid alloy. that take place on annealing, and a number of generalizations have beell reached. It is known that the crystal size in wrought material in the annealed condition depends on a number of factors, including the time and temperature of the annealing operations and the nature and amount of cold-work to which the material has been subjected. Results. however that are not covered by these generalizations can be obtained, which, in some instances, may even appear to be contradictory to them. Xccortling to these generalizations gradual changes in grain size are effected by progressive variation of the factors involved in annealing or cold-working. The work recorded in the present paper, however, relates to the development of grain sizes which are far beyond those normally encountered in ordinary annealing operations and far in excess of grain sizes which,

Jan 1, 1939

By Frederick N. Rhines

Pure copper that has been allowed to oxidize at an elevated temperature in the air is found to be covered with two distinguishable layers of oxide scale. The outer of these, which is very thin, is composed of cuprie oxide, while the inner layer, comprising the bulk of the scale, is made up chiefly of cuprous oxide (Fig, la). If a small quantity of an alloying element, such as silicon, is present in the copper, silica particles are found disseminated through the cuprous oxide, deposited most abundantly near the metal surface, and, in addition, silica particles occur to a limited depth within the copper itself (Fig. 1b). It is this inner layer, composetl of oxide particles precipitated in a matrix of metallic copper, that is known as the "subscale" or the zone of internal oxidation. Under a low oxygen pressure it is possible to produce the subscale without the formation of external layers of copper oxides, thus leaving the metal surface bright and apparently clean while oxidation has occurred, in fact, to a considerable depth within the metal (Fig. 2). Although little is yet known in a detailed way of the mechanism of internal oxidation, the general nature of the process is evident. By virtue of the considerable solubility of oxygen in copper,' it is possible to bring the alloying element in contact with oxygen within the metallic solid solution. If the oxide of the alloying element is more stable than cuprous oxide, the foreign oxide may form and, since most oxides are relatively insoluble in copper, it will not long remain in solution, but mill separate as a precipitate. As the metallic solute is exhausted in the zone of precipitation, oxygen that is constantly being supplied at the surface diffuses farther into the alloy and thus produces an ever-thickening shell of subscale. The distribution of the reacting elements in the subscale and adjoining zones must be somewhat as indicated in Fig. 3. The conditions requisite to internal oxidation to be anticipated are thus: (I) a solubility of oxygen in the alloy, (2) the ability of oxygen to diffuse at an appreciable rate into the alloy, (3) the possibility of the

Jan 1, 1940

By Frederick N. Rhines

Pure copper that has been allowed to oxidize at an elevated temperature in the air is found to be covered with two distinguishable layers of oxide scale. The outer of these, which is very thin, is composed of cuprie oxide, while the inner layer, comprising the bulk of the scale, is made up chiefly of cuprous oxide (Fig, la). If a small quantity of an alloying element, such as silicon, is present in the copper, silica particles are found disseminated through the cuprous oxide, deposited most abundantly near the metal surface, and, in addition, silica particles occur to a limited depth within the copper itself (Fig. 1b). It is this inner layer, composetl of oxide particles precipitated in a matrix of metallic copper, that is known as the "subscale" or the zone of internal oxidation. Under a low oxygen pressure it is possible to produce the subscale without the formation of external layers of copper oxides, thus leaving the metal surface bright and apparently clean while oxidation has occurred, in fact, to a considerable depth within the metal (Fig. 2). Although little is yet known in a detailed way of the mechanism of internal oxidation, the general nature of the process is evident. By virtue of the considerable solubility of oxygen in copper,' it is possible to bring the alloying element in contact with oxygen within the metallic solid solution. If the oxide of the alloying element is more stable than cuprous oxide, the foreign oxide may form and, since most oxides are relatively insoluble in copper, it will not long remain in solution, but mill separate as a precipitate. As the metallic solute is exhausted in the zone of precipitation, oxygen that is constantly being supplied at the surface diffuses farther into the alloy and thus produces an ever-thickening shell of subscale. The distribution of the reacting elements in the subscale and adjoining zones must be somewhat as indicated in Fig. 3. The conditions requisite to internal oxidation to be anticipated are thus: (I) a solubility of oxygen in the alloy, (2) the ability of oxygen to diffuse at an appreciable rate into the alloy, (3) the possibility of the

Jan 1, 1940

By C. S. Smith, L. Guttman

It is shown, from a study of geometric probabilities, that the average number of intercepts per unit length of a random line drawn through a three-dimensional structure is exactly half the true ratio of surface to volume. Since the surfaces can be internal or external, the area of grain boundary or of the interface between any two constituents in a micro-structure can be measured. Other metric relations are tabulated that may be of use in studies of the microstructure of polycrystalline, cellular, or particulate matter generally. IN many fields of scientific investigation the structure of cellular aggregates or random arrays of discrete particles imbedded in some matrix is observed on a two-dimensional section and inferences are drawn therefrom as to the real structure in three dimensions. The biologist's microtome slice, the petrologist's thin section, and the metallurgist's plane polished and etched sections are common examples, although the problem is a general one. Scientists have commonly limited their thinking to the same dimensionality as their structures, and the few attempts that have been strictly three-dimensional in character have been laborious and noteworthy. From a metallurgical standpoint it is often of considerable importance to know, in addition to the volume fraction of two or more components in an alloy, the amount of two-dimensional interface between crystals. Such grain boundaries (which may separate either two identical crystals differing only in orientation or two crystals differing in structure, and possibly also in orientation) have a determining factor upon the mechanical behavior. It is at these boundaries that melting commences, that stress-induced corrosion occurs, and that various precipitates (harmful or otherwise) first appear. The boundary is doubtless of equal importance in nonmetallic crystalline aggregates such as rocks, ceramics, and concrete, and the biologist is deeply concerned with the area of cellular membranes. Many synthetic cellular foams involve similar structural problems. The very term structure usually implies the presence of interfaces and a complete understanding of structure involves nothing but an analysis of the geometrical, metrical, and topological relations between the various interfaces (zero, one and two-dimensional) that exist in a three-dimensional structure. Even systems lacking sharp physical interfaces often have interrelated gradients of composition or velocity (as cored crystals or turbulence cells) in which a neutral surface can be treated as a two-dimensional interface. In an earlier paper by one of the authors' the question of cell shape was considered in terms of simple topological principles without regard to physical dimensions. The determination of the actual size of grains in two dimensions is carried out in a routine fashion in innumerable metallurgical laboratories (see, for example, the ASTM standard methods of grain size determination2), though this is done merely to check the uniformity of a product and has no relation to the actual three-dimensional shape or size of the grains. Some authors have discussed the three-dimensional problem but only on the basis of assumptions as to idealized grain shapes.:'-' Quantitative measurements of microstruc-tures to obtain the volumetric relations of various phases have been carried out by petrographers for many years and are of increasing popularity among metallurgists." The present paper will show how, on the basis of no assumptions other than randomness of sectioning (usually realizable in experiment), it is possible to learn a great deal about the three-dimensional structure. The relations to be derived will generally be used on random arrays of cells or other particles, although they are equally applicable to ordered arrays and even to isolated objects of complex shape provided that suitable random sections can be made. Total Area of Interfaces in a Sample Consider a typical microstructure of a single-phase polyerystalline metal, such as that shown pres- in Fig. 1. The plane cross section shown contains a network of lines which subdivides the area into two-dimensional cells. The lines, of course, represent merely the intersection of the two-dimensional plane of sectioning with the two-dimensional interfaces between adjacent three-dimensional cells. The structure also contains points at which two or more lines intersect: in three dimensions the points are, of course, lines. In the more general case there may be in three dimensions isolated particles surrounded by a single interface without contact with others, and both two and one-dimensional features which do not necessarily connect with others. On the two-dimensional section these will appear as areas delineated by a closed line (as at a and b, Fig. 2), as isolated lines

Jan 1, 1954

By J. F. Martin, J. E. Friedline, L. M. Melnick, G. E. Pellissier

A method has been developed for determining gases in steel in which the gases are extracted by vacuum fusion and analyzed by mass spectrometry. This method is especially applicable for determining small amounts of oxygen and nitrogen. The lower limit of detection for both oxygen and nitrogen is 0.0001 pct with an average deviation of about 0.0001 pct for oxygen and 0.00008 pct for nitrogen. Hydrogen analyses by this method are in good agreement with analyses by vacuum tin-fusion. A complete analysis of all gases extracted from a steel sample can be accomplished in 40 min. It has long been known that certain of the gaseous elements exert particular effects on the physical and mechanical properties of steel. With the recent advent of new experimental steelmaking practices it is now possible to obtain steels with extremely low contents of such elements as oxygen and nitrogen. Present methods for determining these two gases are of insufficient sensitivity as applied to steels made by these newer practices, and therefore a new technique was considered necessary. A review of the literature showed that the conventional vacuum-fusion method1 was the procedure most suitable for modification to obtain a sensitive method for determining the gaseous elements present in steel simultaneously. However, for trace amounts of gases it is impractical to increase the sample size because of the physical limitations of the apparatus and the increased degassing time which would be necessary. Also, when only one of the desired gases is present in trace amounts, quantitative separation by conventional vacuum fusion is almost impossible. Since small analytical mass spectrometers are now commercially available, it was decided to use this instrument in conjunction with conventional vacuum fusion for both qualitative examination and quantitative determinations of the gaseous elements in steel. This technique has already been used with success for the analysis of copper and lanthanum.2"4 APPARATUS A vacuum-fusion unit was first designed and built, Fig. 1. This unit was designed especially for the determination of small amounts of nitrogen and/or oxygen in steel since an acceptable method (vacuum tin-fusion)5 was already in use for the determination of hydrogen in steel. The vacuum system was con- structed of Pyrex glass throughout. Mercury check valves were used in place of stopcocks in the high-vacuum section of the system. Ferromagnetic samples are normally introduced into the vacuum system through a mercury lift. In case of a break in the lift, the mercury is prevented from entering the furnace by a self-locking, mercury safety check valve, Fig. 2. This check valve, developed at our laboratory, is a modified T/S ball-and-socket joint placed in the sample inlet system between the mercury and the furnace. A sudden entry of mercury or air pushes this valve into the closed position, completely blocking the top of the mercury lift. The check valve is held in the closed position by the vacuum of the apparatus. A separate entrance tube also was placed in the system, so that samples which would amalgamate with mercury, or which are nonmagnetic, could be introduced into the furnace. A slightly modified Guldner-Beach furnace is used in this system.8 The optical flat was connected to the system by a ground-glass joint to facilitate cleaning, a quartz delivery tube was substituted for Pyrex, and the crucible was used uncovered. Fusion takes place in a high-purity graphite crucible insulated by — 200-mesh high-purity graphite powder. The crucible set (crucible and funnel) is suspended in a quartz crucible. The furnace envelope and the sample inlet system are exhausted by 2 single-stage, mercury-diffusion pumps in series. The first of these is a high-speed pump, which will work only with a very low backing pressure. This pump is used to exhaust the gases from the furnace as rapidly as possible. The second mercury-diffusion pump is used as a backing pump for the first; the capacity of this pump is much lower. However, it will work efficiently against a back pressure of 3 mm of mercury. To assure positive pumping, a modified Naughton and Uhlig condenser7 is used. With the use of proper valving the second pump is also used as a circulation pump in the catalyst system.

Jan 1, 1959

By W. D. Forgeng, R. L. Folkman, D. C. Hilty

The solubility of oxygen in molten Fe-Cr alloys has been determined at 1550° , 1600°, and 1650°C for alloys containing up to alloyshasbeenabout 50 pct Cr and found to decrease as chromium increases to 6 pet and then to increase gradually. Phase relations in the Fe-Cr-0 system at steelmaking temperatures have been evaluated and two previously unreported oxides have been identified. OPERATIONS in the melting and refining of chromium steels are dependent to a major degree on the reactions of chromium and iron with oxygen and are primarily directed toward controlling and modifying these reactions to secure maximum advantage in the utilization of chromium. Although fairly effective practices have been developed empirically, understanding of the specific reactions is limited. Moreover, the ability of molten steel to dissolve oxygen that subsequently precipitates as oxide inclusions during solidification is well known, so that clarification of the effect of chromium on the nature and mechanism of formation of these inclusions is desirable. Study of the problem indicated that increased knowledge of the fundamental Fe-Cr-0 system is essential to further technical and economic improvement. Consequently, an investigation of the influence of chromium on the solubility of oxygen in molten iron and of phases and phase relations in the Fe-Cr-0 system was undertaken at the Metals Research Laboratories of the Electro Metallurgical Co. as part of a general program on the effective utilization of chromium in chromium steel production. Experimental Procedure All of the experimental runs made during this investigation were carried out in the rotating crucible induction furnace which has been described in detail in a previous publication.' In review, the principle underlying this furnace is that rotational forces in the crucible cause the molten metal to assume a concave shape in such a manner that the slag is contained in the molten metal cup, thereby minimizing slag/crucible contact and subsequent reaction. Practically all of the heats were melted in commercial-quality magnesia crucibles of the type usually furnished for laboratory induction furnaces. All of the runs were made under an argon atmosphere after the furnace chamber had been degassed. Bath temperatures were controlled by Pt—Pt-10 pct Rh thermocouples. The basic furnace charge consisted of a premelted 12 to 15 lb electrolytic iron slug which had been cast to a shape convenient for fitting into the rotating furnace crucible. A typical analysis of the electrolytic iron slugs is given in Table I. For certain runs, it was desirable to melt down charges containing high initial chromium contents. In these cases the chromium was added to the electrolytic iron during the premelting operations. Chromium was added to the rotating furnace bath in the form of electrolytic chromium of the analysis given in Table 11. In all of the constant temperature runs, the standard procedure was to melt down the electrolytic iron or alloy slug under vacuum, admit argon to slightly greater than atmospheric pressure, and adjust rotational speed to develop a well formed "cup" on the bath surface. The melt was then saturated with oxygen by an addition of ferric oxide and the temperature of the bath adjusted to within +5°C of the desired level. At this point the heat was permitted to come to equilibrium prior to sampling or further addition. This time interval was varied from 15 min to 2 hr but generally was about 20 min. After sampling, the desired chromium addition was made and the bath again equilibrated prior to subsequent sampling. This cycle of addition and sampling continued for the duration of the run which lasted from 4 to 8 hr. At the end of this period, power was shut off and the bath allowed to solidify in the furnace. Quenched metal samples were taken from the equilibrated melts by means of the "Taylor sampler" which has been described by Taylor and Chipman.' Before being submitted to chemical analysis, all samples were carefully examined for surface slag occlusions and cold shuts. Later in the study, each sample was radiographed and examined metal-lographically in cross-section to determine the presence of internal defects. On the basis of these examinations, sound and apparently clean specimens were selected from the Taylor samples for chemical analysis.

Jan 1, 1956

By E. D. McMurry

INTRODUCTION Before discussing the use of the free piston; it may be well to explain briefly the type of gas lift valves with which the loo] is designed to function. The gas lift valve ii nothing more or less than a small back pressure regulator. It; construction consists of an outer hous ing covering a seamless metallic bellows in such a way as in form a sealed pressure vessel or pressure dome. To the bellow* in attached a stem and to this stem is attached a .rating member. When the valve is run into the hole, a pre-delermined pressure charge is placed in the pressure dome. As shown in Fig. 1. the valve is furnished in four different major assem-blies. to accomplish good results in different types of wells. The valve is mounted on a pup joint (Fig. 2a) : the eoin-plele assembly is entered into the tubing siring at the desired location. Each valve is furnished with a revere flow check valve (Fig. 2-b) to eliminate any back wash through the mechanism. Valve action is as follows: At any time the casing pressure is allowed to exceed the pressure forces within the pressure dome of the valve, the valve simply opens and passes gas from the rasing annulus into the tubing. When the casing pressure forces arc allowed to bleed to a force less than the pressure force within the dome, of the valve. the valve closes. With this type of construction. it is possible to open and close the valve or valves at will from the surface, the medium of the gas pressure in the rasing annnlus. The cycle of operation is governed by a tine cycle motor valve, commonly referred to as a gas lift interutitter or gas life surfacr controller (Fig. 3). In actual practice. after the well is unloaded only one valve is in operation . . . all other valve.: remain in the closed position. On pre-determined time cycles, it is possible to open and close this operating valve at will, and to pass the desired amount of gas through this valve wheneler needed. This method of gas lift is widelv used and has been found In be very efficient. However, it has long been known that even greater efficiency would be obtained if it were possible to place Piston between the injected gas and the fluid head. The free piston which will be discussed here was designed to accomplish this end and has been found to do so with very satisfactory results. DESIGN AND OPERATION OF THE FREE PISTON Basically. the free piston consist- of a telescoping assembly in which are incorporated the various control and operating parts (Fig. A set of sleeve valves which are opened and closed by movement of the telescoping section is contained in the. tool. A cross section of the free piston is shown in Fig. 4-11, 'rile main body cotain- a seamless monel bellows of the same type as that generally used in pressure charged gas lift valves (Fig. 4-c), and a valve core to permit placing a pressure charge in the bellows before the free piston is placed in service. The bellows is the main control unit of the free piston and performs two function: 1. It governs the opening and closing of the sleeve valves. a.: dictated by the producing activities of the well in which the piston is operating. 2. In its normal position, it holds a rubber packer in an elongated position to permit passage of fluid between the packer and the tubing walls. The lower section of the free piston contains a hydraulic shock absorber which cushions the return of the tool to its

Jan 1, 1953