By Hsun Hu

Three single crystal strips of a 3 pct Si-Fe alloy with approximately (110) [001], (210) [001], and (100) [001] orientations were rolled at room temperature to 30, 50, and 70 pct reductions in thickness. Their deformation and annealing textures were studied. In most cases, the change in texture upon recrystallization and subsequent growth can be described as rotations around the <I10 > axes. A < WO > rotational relationship was also observed. The temperature dependence of recrystallization textures was discussed. WhILE considerable data have been published on the rolling and annealing textures in silicon-iron crystals, very little study has been made on the texture formation at various stages of rolling deformation, and during the process of recrystallization. Dunn&apos; in some of his early works had studied the orientation of recrystallized grains in crystals cut out from lightly rolled (10 to 20 pct reduction) large grained sheets. He found that in most cases a third-order twin relationship exists between the crystal and the recrystallized grains. This orientation relationship actually corresponds to rotations around the <110> axes. The more recent studies of Dunn &apos; and of Dunn and Koh &apos;5 on the rolling and annealing textures in various silicon-iron crystals were concerned mostly with a cold-rolling reduction of 70 pct and annealing at 980OC for recrystallization. Reductions of similar magnitude were also employed by Walter and Hibbard in rolling columnar crystal aggregates of a silicon-iron ingot. A systematic study of the effect of rolling reduction on the deforma- tion and annealing textures is still lacking. Regarding the effect of annealing temperature on the texture formation, Dunn3 has observed a change in therecrys-tallization texture by annealing a 70 pct rolled (1 10) [001] crystal first at a low temperature then atahigh temperature. But the details of texture formation during the annealing treatments were not thoroughly investigated. The present investigation was undertaken to study the texture developments at various stages of rolling deformation and of the recrystallization process, so that a better understanding on the texture formation in silicon-iron crystals may be obtained. EXPERIMENTAL PROCEDURE The three single crystals used in the present investigation were selected from the group of single crystal strips previously prepared7 from a high grade commercial Si-Fe alloy with 3 pct Si. The thickness of these single crystal strips was 0.040 in. The orientations of the three crystals as determined by the X-ray back-reflection Laue technique are shown in Table I. Each of the three crystals was rolled at room temperature along the strip direction to 30, 50, and 70

Jan 1, 1962

By R. Maddin, C. H. Mathewson, W. R. Hibbard

Recent publicationsl.2 establishing the presence of cross-slip in strained metallic single crystals oriented wholly within the area of single slip as predicted from the generalizations of Taylor and Elam3 described these markings as they appeared during the initial stages of the deformation process. At that time, the plane having a common glide direction with the primary slipping plane was reported as the cross-slip plane although the specific direction was not confirmed. Consequently, in continuation of the research, it seemed advisable to investigate the micro-graphic appearance of cross-slip together with the Laue back-reflection X ray analysis and stress-strain data during the later stages of the deformation process. Accordingly, a single crystal of brass (72.75 pct Cu, 0.01 pct Fe, 0.01 pct Pb, 27.23 pct Zn) was polished mechanically and repolished electrolytically after the manner described in the earlier paper.&apos; Three pairs of flat surfaces, parallel to the specimen axis, and (1) perpendicular to the plane containing the pole of the primary glide plane and the specimen axis, (2) perpendicular to the plane containing the pole of the cross-slip plane and the specimen axis, and (3) perpendicular to the plane containing the slip direction and the specimen axis, were polished mechanically and repolished electrolytically, resulting in a final minimum gauge diameter of 0.4864 in. in a gauge length of 3.36 in. The specimen was elongated in tension and load-extension readings were taken following the method described in the initial investigation.&apos; Observed reorientations were obtained from a series of Laue back-reflection photograms at the center and ends of the gauge length and at various positions around the circumference of the specimen. These were interpreted after the manner of A. B. Greninger.4 Cross-slip (Fig 1 and 2) was found with the first appearance of the primary slip clusters and usually joined members of these clusters. In addition, a third set of entirely different markings (Fig 3) could be noted. The displacement of this third set by the primary slip lines was measured as 8300 at. diam (3.04 microns). Since the specimen was carefully observed at high magnifications before any deformation and no markings of any type could be noted, it would appear that this third set was formed during the deformation process prior to the initiation of classical primary slip. Additional extensions produced no unusual change in the appearance of either cross-slip or the third set of markings. The number of lines increased with increasing elongation and appeared, generally, in areas where earlier markings were present. The continuity of the clusters of cross-slip lines in Fig 4, 5 and 6 illustrates that they are neither noticeably displaced by nor do they displace the primary lines at this stage. In Fig 7, cross-slip appears in a long narrow localized band approximately 45 degrees from the stress axis. This somewhat resembles a twin band except for the lack of a sharp boundary. After a shear of 0.257, suffcient additional glide occurred on the cross-slip plane to displace the primary slip lines (Fig 8). Generally, where a large number of cross-slip lines could be observed in an area on one flat surface, few cross-slip lines appeared on the diametrically opposite position on the parallel flat (Fig 9). These, of course, were not matched observations on the same glide ellipses. It was extremely difficult to make such comparisons. The third set of markings (Fig 10) was extensively displaced by glide on the primary slip planes. A plot of the width of primary slip clusters versus their displacement of the third set of lines is shown in Fig 11. The slope and the linearity of the plot suggest that each primary glide plane slips to a constant maximum value of shear before further slip is transferred to another plane. A shear value of 0.28 was determined in this case. Heidenreich5 has presented a similar schematic representation of glide for aluminum. After the specimen had attained an elongation of 51.8 pct, corresponding to a shear of 0.973, cross-slip appeared very prominently in certain areas as shown in Fig 12, yet at diametrically opposite positions very little cross-slip could be noted, Fig 13. Classical conjugate slip was found at this advanced stage in the deformation, Fig 14, which corresponds to the axial location shown at 12 in Fig 15. It should be noted that cross-slip occurs within the conjugate slip clusters and on the same plane as the cross-slip associated with the closely spaced primary lines which constitute a background in less distinct focus. The third set of markings noted at all stages in the deformation of the

Jan 1, 1950

By F. R. Pyne

The following notes are presented in an endeavor to point out the disadvantages attending the use of chrome brick in reverberatory furnaces in which are conducted the treatment of materials of such a nature that absorption by the brick is of too great value to be wasted, and these values must be recovered, if possible, in order to prevent metal losses that can not be tolerated. Several years ago one of the large Eastern copper refineries decided to utilize basic material in place of siliceous material in the walls of their reverberatory furnaces for the treatment of very foul blister copper, as the latter rapidly corroded the siliceous linings. It was also expected that there would be less slag formation, with a consequent decrease in the cost of treatment and a reduction in the metal losses. Magnesite brick were first used, but while the corrosive action of the foul material was greatly reduced, and the amount of slag formed was very much less, the magnesite proved to be unsatisfactory in certain parts of the furnace, because of its tendency to crack and spall badly when subjected to the alternate heating and cooling that takes place in a reverberatory refining furnace. This made many repairs necessary, and consequent frequent interruption in the operation of the furnace, which, together with the high price of the magnesite brick, ran up the cost of maintenance to an unreasonable amount. It was, therefore, decided to substitute chrome brick for magnesite brick in the parts of the furnace affected. The results, as far as the reverberatory furnace was concerned, were very satisfactory. The corrosion due to the action of the foul blister was small and the amount of slag formed was no greater than when using magnesite, and the tendency to crack and spall shown by the magnesite was eliminated. Gradually the use of chrome brick was extended to all furnaces, those treating blister copper as well as those melting cathodes, and the results were so satisfactory that the siliceous roofs were replaced by roofs of chrome brick except in certain places where experience showed a more satisfactory performance on the part of the silica brick. It was immediately recognized, for both the magnesite and the chrome brick, that the metal absorption was very heavy, but it was felt that the

Jan 1, 1918

By Robert A. Cook

In the increasing struggle to cheapen the cost of our iron and steel products a great deal of attention lias been given to economies in the manufacture of coke; and while but little lias been accomplished in this direction in the United States, the narrow margin between cost and market-price, which has obtained here for the past few years of continuing manufactur ing depression, has brought the coke-maker face to face with the problem, how to save, and benefit by it, the hitherto waste products of distillation. I These may be summed up under three heads, generally rank ing, in value, in the following order: 1. Ammonia salts.. 2. Oil- or tar-products. 3. Gas. There are cases in which the last may assume the position of greatest importance. The greatest obstacle encountered by the American coke maker, on investigating the subject, has been the apparent necessity of discarding his existing plant of bee-hive ovens, and erecting an entirely new and very expensive system of retort ovens, against the product of which Be has probably been prejudiced from his earliest knowledge of the subject. The object of this paper is to bring prominently before our coke-experts a brief history of the development at Sheffield, England, of a most successful system of the utilization of by products in connection with all already existing plant of bee hive ovens. This system has now been in satisfactory operation for about five years, and is applied to a series of blocks of ovens, comprising-about 140- in all At this plant, belonging to the well-known firm of Newton,

Jan 1, 1897

By J. A. B. Forster

W. G. WOOLF*—The paper has a wealth of data that take careful, detailed study. As has been indicated the highlights can be only touched in the paper. The design and the arrangement of the rabble teeth as well as some of the other details of operation show a very careful study and a scientific approach to the problem which in most plants using hearth roasters are matters of trial and error with empirical conclusions and, perhaps too often, just arbitrary supervisory preferences which may be erroneous. Here the problem has been approached from a scientific angle which think well merits careful study. The ability to treat the tonnages they get through these furnaces think is made easier by reason of the high sulphide sulphur in the resulting calcines which the balance of the plant—the leaching and so on—can cope with. As indicated by Mr. Weldon in his dis- cussion earlier this morning, in most zinc plants an attempt is made to have as low a sulphide sulphur content in the roaster calcine as possible. But in the operation of the Risdon plants, they are able to cope with sulphide sulphur content up to 5 pct which is far beyond the amount of sulphide sulphur that can be handled elsewhere. I think the autogenous roasting is made easier because driving out the last percentages of sulphide sulphur brings on the necessity for extraneous heat, and that is further exemplified because even at Risdon the author shows the desirability of using some oil to better the operation, particularly for uniformity of roasting results and to obtain more regularity of furnace operation. A. A. CENTER*—Regarding the hard crusts in the beds of the furnace and autogenous roasting, the paper speaks of the former being due, at least to a considerable extent, to lead sulphide in the crusts. I wonder if the author has considered the hard crusts as being due in large part to zinc sulphate. While I was developing large zinc operations we ran into hard crusts which had to be dug up. I took several lumps which were so hard they showed the marks of the rabble teeth very plainly and kept them in my office for some weeks. A visitor came along one day, and as he was having similar troubles, I told him what we were doing about ours. I started to pick up one of these lumps and to my amazement the thing crumbled in my hands whereas originally it had been so hard it wore the rabbles down very rapidly in the furnace. I sent the sample to the laboratory and found that it analyzed very high in water-soluble zinc and sulphate-sulphur. The crumbling of the lumps was evidently due to the anhydrous zinc sulphate gradually taking on moisture from the air and forming crystalline zinc sulphate seven parts water. The increase in volume would, of course, result in disintegration of the lumps. As to getting a high tonnage in the autogenous roast, that is partly because of finishing at about 5 pct sulphide sulphur. It is a real job to get down to, say, ½ pct sulphide sulphur, which is what is usually desired, and still put through a good tonnage.

Jan 1, 1950

By J. Szekely, J. W. Evans

A formulation is given for radiant heat loss from the surface of molten steel held in a ladle and numerical solutions are presented for the resultant integrodif-ferential equations. The results are shown on plots of the net rate of heat loss against time, with the geometlry, emissivities, thermal properties of the walls, and Preheat as parameters. It was found that the rate of the vadiant heat loss from the exposed metal surface was comparable to the conductive losses from the Portion of the metal in direct contact with the walls. The radiant heat loss was markedly affected by the geometry and by the thermal properties of the walls the net radiant heat loss from the steel could be drastically reduced by providing a top cover and also by the provision of preheat. The results of this work are thought to be relevant to heat loss calculatious concerned with vacuum degassing and with operatzons in which molten metals are held in ladles. WhEN molten steel is held or transferred in ladles heat losses inevitably occur. The accurate assessment of these heat losses is of importance in process design considerations, as the temperature of the metal may have to meet rigid specifications in certain stages of the processing sequence. As shown in Fig. 1, the principal mechanisms responsible for heat loss are: i) Conduction into the walls and ii) Thermal radation from the top metal surface (possibly augmented by natural convection) The conductive heat loss may be readily calculated as much information is available in the literature on both the general theory1&apos;&apos; and on its particular applications to ladle heat loss calculations. Evaluation of the radiant component of the heat loss is less straight-forward. In two recent papers it has been shown that the presence of a slag layer 2 to 3 in. thick would prevent any significant heat loss for periods up to an hour,5&apos;" however, should bare metal be exposed, constituting the radiant surface, substantial heat losses could occur. This latter case is of considerable practical interest in various degassing operations and in the vacuum processing of certain specialty steels, where the top surface of the metal is not covered by a protective slag layer. Under these conditions a substantial radiant flux is emitted by the top metal surface; part of this flux leaves the system, part of it falls in the ladle walls. The radiant flux incident on the ladle walls is in part absorbed and conducted away, and in part reflected and re radiated. The purpose of the paper is to present a general formulation of the problem, the resultant solution of which should enable computation of the net radiant heat loss from the metal surface. The principal variables, the effect of which will be investigated, include initial metal temperature, geometry, thermal and radiative properties of the wall, and various modes of preheat. FORMULATION Consider a cylindrical enclosure, shown in Fig. 2, with a diameter D, height H, and wall thickness W, the cover at the top of the cylinder having a wall thickness L. If the temperature of the base (representing the top surface of the metal) is kept constant, say, Tb, the problem is to calculate the net rate of heat loss from the base as a function of time, geometry, the initial temperature distribution, and the thermal properties of the system. As customary, the formulation will consist of the mathematical statement of the conservation of thermal energy within the system.

Jan 1, 1970

By M. E. Straumanis, S. M. Riad

The lattice parameter of 99.999 pct pure Ag rtlas redetevnzined and found to be az5 = 4.08626 5 0.000041 with the vefnzctiotz correction included); the expatzsion coejjicient between 10° and 65°C was 18.73 X10-6°C-1. The lattice paratneter increased upon solution indium in silver in good agrement with other authors. The solid-solubility limit around room temperature was at 20.4 wt pct of in, which suggests that the high-temperature solubility (at about 689°C) determined by other authors is too low. The expansion coejficient of si1ver increases with the itzcrease of indium content between 10° and 65° C from, 18.73 (In = 0) to 20.9 x 10-6°C-1 (In = 20.4 pct), being only very slightly influenced by small amounts of indium. The expansion coefficents of all solid solutions increarsed strongly with temperature, reaching values > 27 x 10- 6 800°C. ACCORDING to the Ag-In diagram,&apos; the solubility of indium in silver (the a phase) extends to about 18 pct by weight at room temperature. However, there has been only one investigation of the solubility limit by X-ray methods—that of Weibke and Eggers.2 Hume-Rothery, Lewin, and Reynolds measured only the lattice parameters of Ag-In solid solutions3 as did Owen and Roberts4 and Adler and Wagner.&apos; The thermal expansivity of four solid solutions was determined by Owen and Roberts4 in a temperature range between 25" and 300°C. In view of the limited amount of work on Ag-In solid solutions, it seemed appropriate to redeter-mine the lattice parameters and the room-temperature solid-solubility limit, to find the exact expansion coefficients of the solid solutions at about room temperature (between 10° and 60°C) and the expansivity up to 800°C, and finally to derive the thermal-expansion coefficients for any alloy within the solid-solubility region. THE ALLOYS AND THE DETERMINATION OF LATTICE CONSTANTS The metals used were 99.9991 pet pure, supplied by the ASARCO company. Both silver and indium were weighed accurately on an analytical balance in

Jan 1, 1965

By W. R. Foster, J. M. McMillen, A. S. Odeh

The complete equations of average linear momentum balance for a single-phase fluid in an incompreisible, homogeneous, porous medium are derived. The derivation begins with Euler&apos;s equation of motion for a continuum and uses an integral transform recently developed by Slattery. 7 For steady flow of a compressible, Newtonian fluid, the usual equations of motion result. For transient flow, the space-time description of the pressure is determined in the lowest approximation by the telegrapher&apos;s equation. From the analysis a new phenomenological coefficient results which connects the viscous traction to the deriv ative of the linear momentum density. The magnitude of this coefficient determines the velocity of sound through the pore structure in this approximation to the pressure field. INTRODUCTION The modification of Darcy&apos;s law of momentum balance for steady, single-phase flow through porous media has been discussed for many years. The first modification was suggested by Forcheimerl who added terms of higher order in the velocity. These can be expected to appear because the underlying microscopic equations of momentum balance are themselves nonlinear in the point velocity field. The Reynolds tensor pvv, which represents the convective flux of momentum density, appears in the momentum balance equation. Only in rectilinear flow (parallel stream lines) does the divergence of this tensor vanish. Since the steady flow stream lines in most porous media are not parallel, nonlinear dependence of the pressure gradient on the velocity should naturally appear. This nonlinearity has nothing to do with turbulence in the ordinary sense of random fluctuations in the pressure and velocity fields. It arises simply because the stream lines converge and diverge, even for steady flows. Klinkenberg2 demonstrated that the permeability coefficient in Darcy&apos;s law depends on the absolute pressure or, alternatively, on the density field. However, because he neglected inertial terms of the Forcheimer type, his correction coefficient could not be represented by a constant but tended toward a constant as the velocity decreased. Forcheimer&apos;s and Klinkenberg&apos;s modifications can be combined in a rigorous way to account for both inertia and slip during steady flow. This will be shown in a future paper. The transient change of pressure in porous media has been described by the diffusion equation.3 This form results from eliminating the velocity and density fields from a combination of the equations of motion in the form of Darcy&apos;s law, the continuity equation and an equation of state. Fatt4 suggested that the cause of deviations from the prediction of the diffusion equation for pressure transients lies not in the choice of Darcy&apos;s law as the equation of motion but on the existence of dead-end pores which might invalidate the averaged equation of continuity. On the other hand, Oroveanu and Pascal5 noted chat the time derivative of the momentum density must be included in the equations of motion since this measures the local rate of change of momentum density. Their differential equation for pressure is the telegrapher&apos;s equation (neglecting gravity). However, their form of this equation predicts that the speed of pressure propagation through the pore structure is the same as that through the bulk fluid. M. K. Hubbert6 attempted a derivation of Darcy&apos;s law by volume averaging the Navier-Stokes equations. Since these equations represent momentum balance at a point within an open set of points containing the fluid itself, Hubbert&apos;s volume averaging cannot lead to tenns involving transfer of momentum between the fluid and the walls of the pores. Once these viscous tractions are lost by choosing a control volume containing only fluid, they cannot

By J. Chipman, J. C. Fulton

Reduction of silicon from blast-furnace-type slags by carbon-saturated iron is a very slow reaction even under conditions of rapid stirring. Equilibrium under atmospheric pressure of carbon monoxide was approached from both sides, and the silica-silicon relation was established at temperatures of 1425º to 1700°C for slags containing up to 20 pct Al2O3. Silicon carbide is formed by reaction of graphite with high silica slags and the conditions for its formation were determined. Activities of SiO2 and of CaO in their binary solutions at 1600°C were determined. The effects on the activity of SiO2 were established for additions of 10 to 20 pct AI2O3 and of 10 pct MgO. STUDIES of chemical reactions between blast-*>-5 furnace slags and metal have been focussed on the transfer of sulphur from metal to slag. The important role which silica reduction plays in this process&apos; has led to a study of the transfer of silicon from slag to metal and the equilibrium represented by the equation SiO2 (in slag) + 2C (graphite) = Si + 2CO (g). [I.] The authors2 have published an account of the experimental method employed in attacking this problem and of three series of experimental results at 1600°C. This paper contains data on some additional compositions and extends the observations to cover the temperature range 1425° to 1700°C. The data are used to determine the activity of silica in the slags. As in the earlier experiments, the atmosphere was carbon monoxide which flowed through the furnace at 150 ml per min. In certain heats designated in the tables and figures, the gas was bubbled through the melt using a graphite tube. The latter increased in porosity during a run and in some cases bubbling ceased as indicated by cessation of surging. Some results were discarded for this reason. Experimental Results The new data are shown in Tables I through V and both old and new data are plotted in Figs. 1

Jan 1, 1955

By W. Rostoker, S. Spachner

A N alloy of 50 pct Ni-50 pct Fe is currently manu- factured in tape thickness down to 1/8 mil. In the annealed form, this alloy produces an almost square hysteresis loop. This has generally been related to the fact that by proper rolling and annealing practice a sharp cube, (100) [OOl], texture can be developed. As part of a program directed toward an understanding of the relationships between magnetic properties and structure of tape core materials, analyses were made of preferred orientations in tapes of various thicknesses. Annealed tapes of this alloy in 2, 1, 1/2, ¼, and Y&apos; mil gages were acquired from commercial sources. Pole figures constructed for the 2 and 1 mil tapes showed the expected sharp cube texture. However, the ½, ¼, and ? mil annealed tapes showed no evidence of any preferred orientations. A comparison of two transmission patterns is shown in Fig. 1. The origin of the absence of texture in the tapes of less than 1 mil thickness was explored in some detail. The basic questions were whether the heat treatment for the thinner tapes was wrongly selected, whether the initial cold worked textures were different, or whether the actual thickness of the tape exercised some influence on its annealing characteristics. Quantities of the five gages of tape were acquired in the as-rolled condition just prior to the final anneal. Pole figures of the cold worked textures were constructed for each of the tapes. Eye estimates of in-

Jan 1, 1956

By W. D. Forgeng, P. F. Wieser

MnSi alloys containing from 2 to 24 at. pct Si have been investigated by metallographic and X-ray methods. Contrary to published data, the temperature of the ß-manganese to a-manganese transformation is lowered by the addition of silicon. The existence of two additional intermediate phases E and ( is demonstrated. E, ranging in composition from 12 to 15.5 at. pct Si, forms by a peritectoid reaction between ß manganese and the second new phase, (. The latter phase is homogeneous at silicon contents from 16.2 to 18 at. pct and forms peritectically from the 0 phase and liquid. The eutectic reaction occurs between the ( phase and MnsSi rather than the ß phase and Mn3Si. As a result of this investigation, a modification of the manganese-rich section of the MnSi equilihrium diagram is proposed. The binary diagram of Mn-Si, according to Hansen,&apos; Fig. 1, exhibits in the low-silicon region (below 24 at. pct Si) a peritectic transformation at 900°C of 0 manganese + Mn3Si to a manganese as determined by R. Vogel and H. Bedarff2 as well as a thermal effect at 980°C between 16.2 and 22.6 at. pct Si reported by the same authors. The nature of the latter transformation was unknown. K. Amark, B. Boren, and A. westgren3 reported indications that possibly four more phases existed in the range of 10 to 27 at. pct Si. The present investigation deals with the phase relations in the range of 2.1 to 17.7 at. pct Si. A few spot checks were conducted up to 23.84 at. pct Si. EXPERIMENTAL PROCEDURE Small experimental heats were prepared by induction melting in a vacuum furnace using argon as a protective atmosphere. The crucible was of commercial-quality magnesia. The furnace charge consisted of silicon metal and dehydrogenated electrolytic manganese. The typical analysis for these materials is shown in Table I. The molten alloy was tapped into 2-in.-square, 7-in.-long ingots. After visual inspection, a small quantity of alloy in the middle portion of the ingot was separated for use in this investigation.MnSi alloys containing from 2 to 24 at. pct Si have been investigated by metallographic and X-ray methods. Contrary to published data, the temperature of the ß-manganese to a-manganese transformation is lowered by the addition of silicon. The existence of two additional intermediate phases E and ( is demonstrated. E, ranging in composition from 12 to 15.5 at. pct Si, forms by a peritectoid reaction between ß manganese and the second new phase, (. The latter phase is homogeneous at silicon contents from 16.2 to 18 at. pct and forms peritectically from the 0 phase and liquid. The eutectic reaction occurs between the ( phase and MnsSi rather than the ß phase and Mn3Si. As a result of this investigation, a modification of the manganese-rich section of the MnSi equilihrium diagram is proposed. The binary diagram of Mn-Si, according to Hansen,&apos; Fig. 1, exhibits in the low-silicon region (below 24 at. pct Si) a peritectic transformation at 900°C of 0 manganese + Mn3Si to a manganese as determined by R. Vogel and H. Bedarff2 as well as a thermal effect at 980°C between 16.2 and 22.6 at. pct Si reported by the same authors. The nature of the latter transformation was unknown. K. Amark, B. Boren, and A. westgren3 reported indications that possibly four more phases existed in the range of 10 to 27 at. pct Si. The present investigation deals with the phase relations in the range of 2.1 to 17.7 at. pct Si. A few spot checks were conducted up to 23.84 at. pct Si. EXPERIMENTAL PROCEDURE Small experimental heats were prepared by induction melting in a vacuum furnace using argon as a protective atmosphere. The crucible was of commercial-quality magnesia. The furnace charge consisted of silicon metal and dehydrogenated electrolytic manganese. The typical analysis for these materials is shown in Table I. The molten alloy was tapped into 2-in.-square, 7-in.-long ingots. After visual inspection, a small quantity of alloy in the middle portion of the ingot was separated for use in this investigation.

Jan 1, 1964

By Alan D. Smith

Mine roof fall characteristics of 250 falls in 5 different room-and-pillar coal mines, located in Pike, Martin, and Floyd counties, were investigated to determine the relationship of selected parameters associated with roof failure and the assumed condition of the mine roof before failure. The selected parameters used in the study included: presence of cracks and water before the occurrence of fall, sloughing of coal ribs, floor heave condition, type of roof support (resin or mechanical anchor bolts), distance to coal face, and time of occurrence of fall after initial coal extraction. In addition, research hypotheses, utilizing multiple linear regression techniques, were generated to test the relationship among the selected parameters and mine roof condition. The results indicated that the vast majority of falls portrayed some presence of water before the actual fall, occurred in less than 30 weeks after initial coal excavation, located usually greater than 30 meters from nearest coal face, gave evidence of cracks in mine roof before occurrence of fall, generally portrayed a good roof condition before the fall, showed presence of sloughing of coal ribs, and gave no occurrence of floor heave before occurrence of fall. In terms of the characteristics of the original support systems in the mine roof falls studied, most roofs were either supported by mechanical-anchor bolts or resin or full-column bolts; very rarely did the roof appear to fail if supported by posts or cribs. A detail inspection of the hypothesis and model comparison results gave supporting evidence that the condition of the roof is not dependent on the usual indicators of potential failure, such as presence of cracks and moisture. In fact, in most cases of mine roof failure, the immediate roof condition was rated as good or better, which gives little or no indication of pending failure and collapse. Hence, a combination of factors that are not easily accessible to measurement, are the dominant factors in the determination of roof fall-potential areas.

Jan 1, 1984

By O. R. Morris, G. L. Hawkes

A galvanic cell, using as electrolyte a fused salt solution of calcium carbide and as electrodes carbon and a Fe-C alloy of known composition, has been set up to study the thermodynamics of Fe-C alloys in the temperature rmzge 800" to 1000°C. Time independence and reproducibility of the cell electromotive force were taken as evidence of the reversible behavior of the cell. Carbon was believed to be present in the electrolyte as the so-called acetylide ion, C;-. The plots of the cell electromotive force us temperature for a specific alloy composition were straight lines within the limits of experimental error. The average Partial molar enthalpy of carbon in iron relative to pure carbon was found to be +10,610 i 93 cal per g-atom C. Thermodynamic analysis of the data has led to the following equation for the carbon activity, ac, based upon pure carbon as the standard state: In ac = In Zc + 10,560/RT + (10.02 + 77O/T)ZC - 2.350 where ZC is the lattice ratio [nC/(nF, - nc )] and T is the absolute temperature. This equalion gives carbon activity values generally slightly lower than those from gas equilibration studies reported in the literature. METAL LOGRAPHIC examination of a polished cross section of the steel anode used in the electrolysis studies of fused salt solutions of calcium carbide by Morris and Harry revealed extensive carburization of the steel by the electrodeposited carbon. This carburization was reflected in the variability, with time, of the applied potential to the electrolysis cell, necessary to maintain a constant current density at the electrodes. This observation suggested the setting up of a galvanic cell of the "alloy concentration" type to study the thermodynamics of some metal-carbon alloys. Cells of this general type have been widely used for the study of alloy systems.2 In view of the availability of published data in respect of the austenite phase of the Fe-C system, it was decided to carry out measurements upon these alloys before proceeding to studies of less well documented systems. The galvanic cell may be written: where [C] is carbon dissolved in iron. The electrolyte was a fused salt solution of calcium carbide, containing some 5 to 10 mol pct of carbide. The cell reaction is believed to be: C(s)-[CI [I1 Carbon forms an interstitial solid solution in iron, with the atoms located in the octahedral interstices. In the fcc crystal structure of austenite there is one octahedral interstice per iron atom. Thus, the lattice ratio, ZC, shown by Gurney3 to be the fundamental concentration parameter in the context of interstitial solutions, is given by: where nc and nFe are the number of carbon and iron atoms, respectively. chipman4 has recently shown empirically the advantages of using this concentration parameter instead of the more usual atom ratio or atom fraction. The cell electromotive force, E, assuming reversible behavior, is related to the carbon potential or the partial molar free energy of carbon in the solid solution relative to pure carbon at the same temperature and pressure, GP at the composition ZC, by the equation: where z is the carbide ion valency and F is the Faraday constant. An activity of carbon, ac, in the solution relative to the value of unity assigned to pure carbon, and an activity coefficient, qC , are defined such that: where R is the gas constant and T the absolute temperature. GF is further related to the relative partial molar enthalpy Hm, and the temperature coefficient of the cell electromotive force, (aE/aT)Zc, by the equations: Measurement of the cell electromotive force thus enables calculation of the relative partial molar thermodynamic properties of carbon in iron, if z is known. At E = 0, the solid solution is in equilibrium with pure carbon. More convenient for many purposes is the standard state based upon the infinitely dilute solution, Henry&apos;s law. The relationship between the activity coefficient of carbon based upon this standard state, and that based upon the pure carbon standard state, qC , may be obtained by considering the free energy of transfer of carbon from the latter standard state to the former. The relationship is: where +:H is the activity coefficient of carbon in the hypothetical standard state based on a reference of

Jan 1, 1969

By F. D. Rosi

The plastic properties of extended silver and copper crystals of varying purity were studied as a function of crystal orientation in the early stages of flow. Variations in the gross shape of the shear stress-shear diagram and in the properties of critical Variationsshear stress and shear-hardening coefficient were correlated with changes in slip-band developments. The phenomenon of work hardening is discussed in terms of the existing dislocation theory. IT appears certain from the early studies on the deformation characteristics in metal crystals1-3 that plastic flow takes place in a preferred crystallo-graphic slip system which is determined by the geometry of the crystal (law of maximum shear stress), and that the value of shear stress for this system is independent of crystal orientation (law of critical shear stress). Experimentally, it has been demonstrated further that the law of critical shear stress can be extended to include extensive plastic flow.&apos; Thus, the shear-hardening coefficient, which is defined as the slope of the shear stress-shear curve, also is considered to be independent of orientation. It is noteworthy that deviations from this empirical shear-hardening law have been reported in cubic crystals whose initial orientation favors slip on more than two systems.&apos; Moreover, this law appears to have been derived from stress-strain data relating to relatively high values of shear strain (0.5 to 4), where widespread slip and complex distortions can be expected, regardless of crystal orientation. Since existing data indicate that the strain inhomogeneity in a crystal is manifested particularly in the early stages of flow, it would appear that a more exacting test as to the fundamental nature of the shear-hardening law would be to investigate systematically the shape of the stress-strain curve as a function of crystal orientation in the earlier stages of deformation. With regard to the general form of the shear stress-shear curve for cubic crystals, early studies show a parabolic hardening law, where the shear 1 stress is proportional to the square root of the shear-strain. Since this law was predicted theoretically by Taylor" in his original dislocation model for hard- ening, it has been accepted widely as a fundamental flow characteristic of cubic metals. However, it was recently pointed out by Masing6 hat the parabolic law is not the elementary form of hardening in cubic crystals, but instead is a consequence of complexities in the flow process (e. g., deformation bands and unpredicted secondary slip). Thus, in the very early stages of deformation (< 2 pct extension) where the occurrence of such complexities is unlikely, a different strain-hardening behavior might be anticipated. This view is supported by the recent work of Rosi and Mathewson7 on high purity aluminum where a linear law was obtained for extensions up to 2 pct. A linear hardening over a wider range of deformation also was reported by Rohm and Kochendorfer8 ho deformed aluminum crystals under conditions approximating pure shear. Even more pertinent is the recent evidence of Masing and Raffelsieper9 on high purity aluminum crystals. It was found that for crystals having initial orientations near a <l00> or <1ll> axis, a high hardening was obtained, whereas crystals with a <110> orientation exhibited a low and linear hardening curve followed by a region of more rapid hardening. Since much still remains obscure concerning the details of strain hardening as well as slip-band formation in face-centered-cubic crystals in the early stages of deformation, the present study was undertaken to evaluate the effect of crystal orientation on these two important manifestations of glide. It is important to note here that at the time of this study, Lucke and Lange11 presented information on the orientation-dependence of the shape of the strain-hardening curve in aluminum of various purities. Their work, which essentially represents an extension of that of Masing and Raffelsieper, in many respects is parallel to that of the present study. Experimental Procedure Production of Single Crystals: Single crystals of silver and copper of varying purity were used in

Jan 1, 1955

By H. R. Peiffer, R. Geckle

The silver phase of silver and finely divided alumina composites is shown to grow as single crystabs upon solidification from the melt. These crystals grow without the aid of an externally applied thermal gradient or a mold. The single-crystal growth is more readily disrupted as the alumina content varies from the optimum concentration of 20 wt pct. Pretreatment such as variation of fabrication pressure, and presintering of the specimens appear to play a lesser role in this phenomenon. In actual practice the growth of single crystals of metals from the melt is a tedious, painstaking process.&apos; Care must be taken to insure the proper thermal gradients and rate of growth in a vibration-free environment. Excellent single crystals can be grown when these variables are controlled. When a second insoluble and finely divided phase is present in the melt the growth of single crystals is difficult, if not impossible, even under the most favorable conditions outlined above. During the past few years, a composite of silver and alumina has demonstrated an ability to resist flow even though the major phase, silver, is mo1ten. 2 A more surprising feature of this material is the ease with which single crystals of silver grow upon cooling the composite from temperatures above the melting point of silver to temperatures near room temperature. Observations have been made that demonstrate that single crystals of silver will grow even when conditions most unfavorable for growth of pure silver crystals exist. The crystals grown in this manner are imperfect in that a great deal of subgrain structure exists. It is the purpose of this manuscript to qualitatively describe this process and to attempt to isolate the influencing factors of this behavior. MATERIAL PREPARATION The composite material is prepared by powder-metallurgical techniques. Two items of great importance are the introduction of oxygen into the system and the obvious need for a thorough mixing of the metallic and refractory oxide phases. The oxygen is necessary in order that the silver wets the alumina. Without oxygen the phases separate and the material shows no unusual properties. In order to supply the needed oxygen the silver is added in the form of silver oxide which is readily decomposed to oxygen and silver upon heating. The silver oxide is readily obtained in a finely divided form that allows a uniform mixture of the alumina and silver oxide to be prepared. The correct ratio of alumina to silver oxide is mixed in the presence of alcohol in an ordinary food blender. The mixture has the consistency of a thin slurry and after mixing for approximately 20 min is dried and pressed into billets at various pressures. As is shown in Fig. 1, there is no limit to the shape of the specimens obtainable as single crystals. These billets are heated in air in a predeter-

Jan 1, 1964

By Chingyuan Y. Li, C. Y. Hsieh

Realizing that aluminum will have a great role to play in the coming industrialization of China, Chinese geologists have long been looking about for some aluminum deposits. The possible sources appear to be alunite, the alumina-rich shales, and the bauxite deposits. The locations of deposits are shown in Fig. I. Alunite Our attention was first directed to the alunite deposits along the southeastern coast of China. Table I summarizes the reserves now believed to exist in that region. Other alunite deposits have been found in Kiangpei, Szechuan province; Charming. Liuyang and Hsanshan, Hunnan province Tsingchow and Chowyuan, Shantung province. No reserve figures are available. High-alumina Shale Shale high enough in aluminum to serve as a source of that metal has been found in northeastern China(Tab1e 2). In Manchuria, the Manchuria Light Metals Co., at Antung and Fushun, operating under Japanese control, has been the only active producer of aluminum. It is not known, however, whether the company uses local raw materials or imports ore from elsewhere.* Shantung Bauxite Bauxite was first recognized in China at Paoshan, Shantung province. Although the reserve is reported to be large (estimated at 271 million tons), the high content of insoluble residue (SiO2) and mineral composition (diaspore) are dis-

Jan 1, 1948

By Chingyuan Y. Li, C. Y. Hsieh

Realizing that aluminum will have a great role to play in the coming industrialization of China, Chinese geologists have long been looking about for some aluminum deposits. The possible sources appear to be alunite, the alumina-rich shales, and the bauxite deposits. The locations of deposits are shown in Fig. I. Alunite Our attention was first directed to the alunite deposits along the southeastern coast of China. Table I summarizes the reserves now believed to exist in that region. Other alunite deposits have been found in Kiangpei, Szechuan province; Charming. Liuyang and Hsanshan, Hunnan province Tsingchow and Chowyuan, Shantung province. No reserve figures are available. High-alumina Shale Shale high enough in aluminum to serve as a source of that metal has been found in northeastern China(Tab1e 2). In Manchuria, the Manchuria Light Metals Co., at Antung and Fushun, operating under Japanese control, has been the only active producer of aluminum. It is not known, however, whether the company uses local raw materials or imports ore from elsewhere.* Shantung Bauxite Bauxite was first recognized in China at Paoshan, Shantung province. Although the reserve is reported to be large (estimated at 271 million tons), the high content of insoluble residue (SiO2) and mineral composition (diaspore) are dis-

Jan 1, 1948

By D. M. S. Bhatia, Richard D. Hagni

Five sulfide minerals from the Magmont mine, southeast Missouri were sampled for 31 trace elements in over 300 samples by laser microprobe spectrographic analysis of polished sections. The concentration of several trace elements shows a pattern of progressive variation with depth (space) and variation with different paragenetic stages (time) of each mineral. Factor analysis of the geochemical data shows sympathetic correlation both in space and in time of Bi, Cd, Ge, and Sn in galena and sphalerite, and Ni and Co in sphalerite and marcasite.

Jan 1, 1981

By R. D. Pehlke, J. V. Gluck

The effect of small additions of silver on the actiziity of zinc in dilute solution with molten bismuth has been determined ill the range 450° to 650°C. Experimental measurements were made in a multi-electrode galvanic cell. All zinc activities showed large positive deviations from Raoult&apos;s Law. The results are expressed in terms of the interaction parameter EJ, as defined by Wagner. In the binary Zn-Bi system, Henry&apos;s Law was followed at zinc concentrations below 5 mol pct, thus indicating that the binary or self-interaction parameter of zinc in bismuth is essentially zero. The Henry&apos;s Law con- THE determination of thermodynamic interaction parameters requires accurate knowledge of solute activities in the dilute-solution region. Dealy and Pehlke1 have summarized the basis for interaction relations, discussed some theoretical implications, and presented a compilation of interaction parameters calculated for molten nonferrous alloys from stant ranged from 2.43 at 650°C to 3.96 at 450°C. The binary zinc activities were consistent with published data for higher zinc concentrations . The ternary interaction parameter ranged from -1.90 at 650°C to -3.30 at 450° C, varying linearly with the reciprocal of the absolute temperature. The negative value for the parameter reflects the fact that addition of silver decreases the activity of zinc in solution with bismuth. data available in the literature. Most of the data were for two-component systems from which only the self-interactions, Ei, could be calculated. Concentration ranges were often such that a considerable extrapolation was required for calculations at lnfinite dilution. The data for ternary systems were quite limited and often unavailable in suitable systematic fashion—thus few values of the parameter e| could be obtained. Knowledge of both the binary and ternary interaction parameters is necessary for the estimation of the activity coefficient of a given dilute solute in

Jan 1, 1965

By C. H. Herty

The results of a study of the open-hearth process from the physicochemical viewpoint are given. This study includes experimentation in small laboratory furnaces and in standard 100-ton furnaces. The behavior of manganese, carbon and phosphorus are quantitatively explained. The action of "residual" manganese is discussed with reference to its relation to iron oxide dissolved in the metal. The solubility of CO in steel and its relation to dissolved FeO and carbon is given. The equation for phosphorus elimination has been tested out on a 200-ton furnace and the results are given in the text. The effect of temperature and slag composition on the elimination of metalloids in the basic open-hearth process has been qualitatively understood since the early days of steel making. The quantitative effect has, however, only recently been brought to attention. The effect of slag composition has received more attention than that of temperature, primarily because the range of finishing temperatures in the basic open-hearth process is small compared to the large variations found in the composition of the slag at different periods during the process, and to the variations occurring with the use of raw materials of different degrees of impurity. The effect of slag composition on the elimination of metalloids has been studied by Styril from the thermochemical standpoint. This method is open to serious errors, in that thermochemical data at 2900&apos; F. are very inaccurate and in many cases completely lacking. Feild2 has calculated equilibrium constants from the rate at which the metalloids are eliminated. The effect of slag viscosity on rate of elimination will affect the constants calculated by this method. Whitely,a Colcough4 and others have used slag compositions as the basis for calculation of constants by which the extent of elimination may be calculated.

Jan 1, 1926