Search Documents

By E. S. Anolick, Joseph Singer

The magnetic after-effect, in the form of time decay of permeability (l/µ), has been used to obtain independent data on the solubility of' carbon in pure iron. The results differ slightly from the solubilities obtained through internal -friction experiments. The mechanism of the time decay being the magnetic analogue of internal friction, it appears necessary to explain the observed discrepancies, and some suggestions are made. THE purpose of this work was to establish the reliability of the time decay of permeability as a measure of dissolved interstitial in the body-centered-cubic lattice, and further, to establish techniques suitable for such measurements with samples of a form convenient for various other measurements. This particular sample form was the "epstein" strip, i.e., 25 cm by 3 cm by 0.035 cms. While the general conclusions are not limited by this geometry, there are two aspects of the samples that may be relevant: a) texture, and b) grain size, which ranged generally from 1 to 10 mm. Effects due to these two possible parameters were thought to be small and were not investigated. Calibrating the time decay technique and the other experimental procedures by measuring the solubility of carbon in pure iron suggested itself because of the accumulation of data on this subject through the related technique of the internal friction'; The essentials of this report have been published in a somewhat condensed form.5 Since then some additional data have been taken. It is the purpose of this paper to add these data and to provide more complete description of the experimental techniques than was possible then. The time decay of permeability is a form of the magnetic after-effect.6,7 Permeability is measured immediately after demagnetization (µº) and also long after (µ8). The time decay, ?(l/µ), is the difference 1/µ8 - 1/µ0 and has been considered to be proportional to the concentration of a dissolved interstitial6,8,9,12 The relaxation time! 7, is characteristic of a particular diffusion, and affects the permeability as follows: where he being the activation energy for diffusion of the interstitial. Reference is made to the works of snoek6 and Neel7 for a complete discussion. A brief exposition of the principal ideas may be in order here, as follows. On the basis of the simplest model, resistance against domain wall motion increases with time after demagnetization due to the diffusion of interstitials to preferred sites created by the magnetostrictive tetragonolization under the strong magnetic field. Thus permeability, measured with a small field after the abrupt removal of the large field, will continuously fall with the process of diffusion of the interstitials, and the total "time decay" (or "time decrease") should be proportional to the amount of interstitial in solid solution. In the present report, use is made only of the total time decay rather than of the nature of the progress of the decay; the only problem involved in this approach is the need for assurance that only one interstitial is contributing to the effect as used. It is felt that the special use made here of the total time decay warrants the conclusions. Other work has been going on elsewhere on the detailed study of the nature of the time decay.8'9 EXPERIMENTAL A) Materials—12-lb ingots were made in a vacuum furnace from high-purity iron and by a series of hot and warm reductions were brought down to 14-mil strip. This was cut into 25-cm epsteins. The pure iron was decarburized at 750 °C by hydrogen. The time decay measurement for the decarburized iron (see below) indicated a satisfactorily low starting level of interstitials. Grain growth to grain sizes of 1 to 10 mm was produced in the pure iron by a 700" anneal in hydrogen after a critical reduction of about 7 pct as suggested by previous trials. No measurement of texture in the pure iron was made. The grain size was taken to be large enough to be beyond any sharply critical size regarding solubility. B) Infusion of Carbon—Since the permeability measurement required about two dozen epsteins, a special method of carbon infusion had to be developed to ensure homogeneity of infused carbon. This was accomplished by setting the samples edgewise in a

Jan 1, 1961

By Robert E. Green, T. Hinton

The velocities of the three possible modes of elastic-wave Propagation have been calculated for single-crystal aluminum at 1-deg intervals throughout the standard steveographic triangle. The results are presented as isospeed contours. The deviations between the direction of maximum energy propagation and specirzen axes are presented as arrows drawn within the standard triangle. The orientation factors associated with dislocation nzotion on the primary slip system only and also on all twelve slip systenzs have been calculated for all three elastic waves. The orientation factors associated with a longitudinal standing--7aue resonant specivnen hazle also been calculated. The relevance of these results to ultrasonic attenuation measurements is discussed. DUE to the widespread use of ultrasonics in the investigation of the properties of solids a number of authors15 have discussed in detail the theory of elastic-wave propagation in solids. In this paper the modes of wave propagation are evaluated according to the procedure suggested by reeen' for the case of single-crystal aluminum at 1-deg intervals throughout the standard stereographic triangle. The wave speeds are presented in the form of contour diagrams within the standard triangle. The deviations between the direction of maximum energy propagation and the normals to the wave fronts are presented as arrows drawn within the standard triangle. The orientation-de pendent factors (orientation factors) associated with dislocation damping as derived in the preceding paper6 have been calculated for the case of aluminum at 1-deg intervals throughout the standard triangle. The orientation factors for dislocation motion on the primary slip system only and on all twelve slip systems are presented in the form of contour diagrams, for both the traveling- and the standing-wave conditions. The relevance of these results to ultrasonic attenuation measurements is discussed. ELASTIC-WAVE PROPAGATION Three waves can be propagated in a linear elastic homogeneous anisotropic medium. The velocity of propagation v of each of these waves in a medium of density p can be obtained from the determination of the eigenvalues and eigenvectors of the matrix equa- The A's are a series of moduli which are functions of the elastic constants cij and the direction cosines 1, m, and n of the specimen axis. In the case of cubic single crystals where there are only three nonzero elastic constants cll, c12, and C, the A's are, The solution of Eq. [I] will give the wave speeds (eigenvalues) and the direction cosines a, 0, and y of the particle displacements (eigenvectors). To obtain the direction of maximum energy flux requires the calculation of the energy-flux vector ET with com- w is the angular frequency, A, the amplitude, and v the velocity of the wave. The direction cosines a, b, and c of the energy flux vector are then given by

Jan 1, 1967

By K. Tanaka, J. D. Mote, J. E. Dorn

It) an attempt to ulLcoce.lP the operative strain-rate-contl-olliy: dislocation nieclzanistns, specially oviented sizgle clystals of the intel-nzediate 1zexagonal phase containing Ag plus 33 at. pct A1 were tested in tension over a wide range of temperatures. Slip was observed to take place by the {0001} <1120> {l100} mechani fracture took place across the(i100) plane and winning occurred by the (i01Z) ?lechanisn. Basal slip exhibited a strong yield point over the -alzge from 77 to 450°K, the upper ,esolved shear st]-ess having the exceptionally high value of 10,500 psi over this entire ?-a?zge of tenzpei,atuves. The critical 9-esolved shear stress for prismatic slip decreased f7-om 48,000 psi at 4.3"K to 23,000 psi at 170°K (Region 1) follozcirg zt:lzich it decl>eased sloz&ly to 21,500 psi at 475°K (Res&apos;on II); from 475" to 575°K (Regioz III), the c7-itical esolced shear stress dec&apos;-eased precipitously to 2000 psi; and from 575" to 750°K (Region IV) it decreased less afi&apos;dly to a low value of about 500 psi. Pvistintic slip in Region I was pobably controlled by the tliel-nally activated riecharzisui of nucleation and g,-ozcth of kinks in dislocations lying in Peierls potential troughs. In Region II for prismatic slip the critical 1-esolved shear stress was slzocn to be deteemined by sh0l.t-range 01-dering, Overall the forgiorz fo basal slip, 7.c.lre1-e a Strong yield-point phenorlienu ia7as observed, the critical vesolved slzea?-stress was shoztn to be determined by n conibirzation 0-f Szizuki locking and short-range-order Izavderzizg, The precipitous decrease in the critical resolved shear stress with increase in ter,/pe7-atrir-e over Region HI was tentatively ascribed to a decrease in the degree of slort-)ange 07-del;iqq (0)- clusteing) and also the effect of fluctuations the degree of o?der, It is at pgreser2t zrtzce)taitz as to 1t1hethe1- these or other possi1)le effects are also ,esponsible. fo- the data obsel-ved 172 Region IV. 1NTEREST in inter metallic compounds stems not only from their role in dispersion hardening of polyphase alloy ystems but equally from their potentialities for high strength, hardness, and stability not only at atmospheric temperatures but especially at elevated temperatures. As summarized in a re- cent symposium of the Electrochemical Society on "Mechanical Properties of Inter metallic Compound", most of the experimental evidence regarding the mechanical behavior of intermetallic compounds centers about the effect of temperature on the hardness and ductility of polycrystalline specimens. The available data reveal that the plastic behavior of intermetallic compounds might be rationalized in terms of the usual dislocation mechanisms appropriate to a solid solutions providing the additional complexities arising from crystal structure, long-range ordering, short-range ordering, and defect lattices are taken into consideration. It is apparent, however, in terms of the history on a solid solutions, that a complete detailed mechanistic rationalization of dislocation processes may not be possible until the deformation processes are studied in single crystals of intermetallic compounds. The present paper contains a preliminary report on the plastic behavior of single crystals of the hexagonal Ag-A1 intermetallic phase over a wide range of temperatures. The results confirm the thesis that single crystal data provide a most effective method of identifying operative dislocation mechanisms in intermetallic compounds. EXPERIMENTAL TECHNIQUES Several factors prompted the selection of the hexagonal Ag-A1 intermetallic phase for this preliminar investigation on the plastic properties of single crystals of intermetallic compounds: 1) This phase has a wide solubility range5 which would permit future investigations on the effect of composition and axial ratios on slip mechanisms. 2) Although it undoubtedly exhibits short-range ordering (or clustering) this intermetallic phase is free from complexities arising from long-range ordering.6 3) Since the atomic radii of aluminum and silver are practically identical, the possible complications due to Cottrell locking are minimized. 4)Whereas the dislocations on the basal planes are expected to dissociate into Shockley partials and are thus susceptible to Suzuki locking, those on the prismatic planes probably remain complete. 5) The axial ratio, being 1.61, is almost ideal, suggesting that short-range ordering may be almost spherically symmetrical. The present investigation was conducted exclusively with the hexagonal Ag-A1 alloy containing 33 at. pct Al. Preliminary investigations revealed that this alloy undergoes basal slip by the (0001)

Jan 1, 1962

By R. S. Hooper

In attempting to describe recent mining developments at the Bunker Hill mine, it may be well to recall first the old days of hand mining when holes were laboriously drilled by hand to a maximum depth of three feet, and were shot one or two at a time, in order that the miner could take advantage of every slip, crack or bedding plane, and so save as much drilling as possible. Broken muck, of course, was loaded by hand shoveling into wheelbarrows or small cars, and heading advances or stope tonnages were governed by the number of men that could find room to work in any given place. The first big improvement over these old methods was the introduction of the reciprocating type of air-powered rock drill. This innovation, crude as it was, enabled the miners to set up a machine and drill a complete round of holes in one shift; but broken muck was still loaded by hand, and the size and rate of advance in headings were limited by time required to remove the broken rock. The next improvement of consequence was the appearance of the hammer-type rock drill, which greatly increased drilling speed over the reciprocating type, and made possible the completion of a full cycle in one shift, by the use of crossbars in headings, and permitted drilling and mucking to be carried on at the same time. Rock drills continued to improve as time passed, and finally the smaller and more efficient mucking machines appeared on the scene, and it became possible to muck out a round of broken rock and have a clean setup for one or more drill columns and machines. A complete cycle of mucking, drilling, and blasting was completed in one shift with an average advance of five feet. These conditions prevailed for several years, but as the mine grew deeper, the distances to transport the workers grew longer, and this fact together with the shortening of the working day, soon presented the problem of attempting to complete a cycle of operations in a shift of only six hours at the working faces. Anticipating this condition, the operating heads at the Bunker Hill had started an intensive study of more and better mechanization, and over a period of comparatively few years have adopted and placed in service methods and machines that make it possible for a three-man crew to consistently advance headings seven by nine feet in cross section, at the rate of eight feet, and more, per shift, doing all the mucking, switching, drilling and loading. These improvements consist of the following major items: I. The development of a light, flexible, easily transported jumbo equipped with pneumatic columns (Fig I), that has decreased the "setting up" and "tearing down" time an average of 11/2 hr per shift, Or 25 PCt of the available working time. These jumbos were developed at the Bunker Hill mine by members of the staff and consist of two pneumatic columns attached to a suitable carriage. They fold

Jan 1, 1949

By G. W. Powell

G. W. Powell (Ohio State University)—Appleton and Bever measured the quantity Es which, for a solid torsion specimen, is basically an average quantity. Es is the amount of energy stored in a solid torsion specimen strained to a surface shear strain of divided by the total number of gram-atoms of alloy in the specimen. It would seem more meaningful and rigorous to deal instead with the quantity which is the energy stored per gram-atom of an alloy uniformly strained to the shear strain . The purpose of this discussion is to demonstrate that as a function of y is readily obtained from the torsion data. radius of the torsion specimen, shear strain at the surface of the torsion specimen density of the alloy, atomic weight of the alloy, and total energy stored in unit length of the torsion specimen. The energy stored in unit length of an elemental tubular section of the torsion specimen is, as given by Appleton and Bever, where E is expressed as calories per gram-atom. The energy stored in unit length of the torsion specimen is

Jan 1, 1963

By Max Barber

PRESENT equipment and practices in open-pit mines of the Lake Superior iron ranges have been described recently in some detail by A. H. Hubbell.1 It is anticipated that any further improvements will be the result of gradual evolution of present methods and equipment, just as those now used have been gradually evolved from earlier methods. An exception to the process of gradual evolution during the last decade has been the adoption of electric power for operating shovels and trains in open-pit mines, but it is not expected that any such revolutionary changes will be made in the future. The use of Diesel, engine equipment will gain considerable headway, no doubt, and will find favor in certain lines of operation as improvements and adaptations are evolved to meet particular requirements. The question of installing belt conveyors for handling material from deep mines of restricted area, where haulage grades become a serious consideration, or even for transferring earth, rock, or ore material for distances of several miles, is now being studied and some very interesting data are being obtained.

Jan 1, 1932

By Thomas Wilson

IN a single-crystal cube of iron the arrangement of the atoms is that characteristic of iron at room temperature: the body-centered cubic lattice. X-ray investigation has shown this structure to be characteristic of iron, as it has shown the atomic arrangement of other metals to be characteristic of those metals also. Rarely do substances have more than one characteristic atomic arrangement. Many physical properties of metals are directly connected with their atomic arrangements, so that changes of arrangements produce changes of properties. Only chemical change influences atomic arrangement. If a difference in the physical properties of a metal is caused by a process which involves no chemical change, the cause of the difference in properties must be sought elsewhere than in the atomic arrangement. Frequently this cause can be traced to alteration of crystal orientation. The orientation of a crystal may be defined as the relationship which the crystallographic axes bear to some quantity of reference. A cube of iron appears cubic whether it is regarded from a face, an edge, or a corner. Yet these three positions represent three different orientations of the cube with respect to the observer. It is evident that the orientation of this cube of iron, unlike the atomic arrangement, is not characteristic of iron but is entirely dependent on the previous history of the cube. Most of the processes of metal working, such as wire-drawing, rolling, and bending, change the orientation of the crystals present in the worked metals. These processes usually tend to produce rotation of the crystals into positions approaching a mean. Specimens of metals show-ing this characteristic are said to possess a preferred, orientation. Tensile strength, ductility, and many other properties are influenced by orientation changes; therefore two specimens of the same metal may show different values of these quantities. In metal specimens possessing a narrowly limited preferred orientation, these quantities will vary in magnitude in different directions throughout the specimens. The investigation of the influence of manufacturing operations upon crystal orientation, and hence upon physical properties of metals, is an important

Jan 1, 1929

By David L. Holt

The contribution of grain boundary shear to total elongation, CS/E&apos;, has been measured in an Al-Zn eu-tectoid alloy that was quenched from above the invariant temperature, then annealed at 250° C to a grain size of&apos; 1.8 p. At 250°C, ks/E&apos; is low at both high and low strain rates, but reaches a maximum, estimated as 60 pct at an intermediate rate of 5 X 10 per rnin. Rate sensitivity, as measured by the index m = a log a/a log E&apos;, follows the same trend, and furthermore the maximum values of m and -cur at approximately the same strain rate. This result, combined with the metallographic observation that boundary migration enhances boundary shearing, is interpreted as supporting a previous suggestion that the high rate sensitivity characterizing super-plasticity is the result of combined boundary shearing and migration. It is suggested that the latter event relieves stress concentrations at triple points, and smoothes boundaries so that stress is governed largely by a viscous boundary shear. GrAIN boundary shear has been considered in relation to superplasticity in several recent papers.&apos; The problem has been to explain the high strain rate sensitivity of flow stress, and the variation of rate sensitivity with strain rate (E&apos;) and grain size (L). The requirements for superplasticity, small L and high T, suggest the reasonableness of an approach to high rate sensitivity involving grain boundary shear. Further support came from experiments on the A1-Cu eutectic alloy,&apos; where it was found that strain rate sensitivity of cast material annealed to produce an equiaxed, micron-size grain is always low; taking as an index of rate sensitivity m = a log a/a log <, m < 0.3. However, m in hot-worked alloy of comparable grain size can be as high as 0.7. In the cast and annealed material, each phase is a single crystal, the only boundaries are interphase boundaries, and it is, consequently, geometrically impossible for boundary shear to contribute to deformation in any major way. Other observations (for hot-worked material) were a-L at constant (low) strain rates and indications that the rate of recrystallization was enhanced as strain rate increased. As a result of this work, it was proposed that high rate sensitivity arises from a deformation mode of boundary shear associated with boundary migration. Migration serves to relieve stress concentrations at triple points, and smoothes boundaries so that they assume properties of fluid films. On the other hand, the low rate sensitivity observed at high and low strain rates reflects deformation of bulk material. Measurement of the variation of grain boundary shear with strain rate and m have not yet been made. Such measurements are important, especially in view of a proposal, differing in detail from the above, that high m arises merely from a transition between a grain boundary shear mode of deformation at low rates to a transgranular mode at high rates.2&apos;4 In the present work, the contribution of boundary shear to total deformation is measured and in addition metallographic observations are made on surfaces of deformed specimens to look at the interaction between boundary shear and migration. The Al-Zn eutectoid alloy was chosen for its homogeneous, fine-grained structure, which is obtained readily without hot-working. It has also been the subject of a previous phenom-enologically directed study. EXPERIMENTAL Material. Compression specimens, cross section 4 by + in., length \ in., were machined from a sand-cast ingot of composition 77.5 wt pct Zn, 22.5 wt pct Al. (The melt was prepared from 99.9 pct Zn and 99.99 pct Al.) After homogenization at 375°C for 50 hr, the specimens were quenched in brine and removed before the heat evolution that accompanies de -composition of the high-temperature phase.5&apos;6 The resulting microstructure, see Fig. l(a), was too fine for grain boundary sliding to be easily studied; coarser structures were obtained by annealing for various times at 2 50°C. Annealing was terminated by a brine quench. Final average intercept lengths between all grain boundaries (both interphase and those lying in a phase), L, were: 0.5 p [annealed for 15 min, Fig. (a)], 0.8, 1.1, and 1.8 p [Fig. l(b)l. Testing Procedure. An Instron machine was used for most of the compressive deformation. Tests were of two types: those in which crosshead velocity was changed in steps to measure m as a function of strain rate15 and tests at constant velocity to a fixed (engineering) strain of -0.2 (20 pct). Stress reached a steady-state value (a) which was plotted, on a logarithmic scale, against log strain rate (E&apos;). An alternate and equivalent evaluation of m was to take the slope of the log o vs log 6 curve. Time at temperature before testing was 15 min. Strain rates covered by the Instron (4 x lo-&apos; to 4 x 10&apos; per min) were insufficient; at a higher rate of 5 x lo2 per min a gas-operated testing machine was used, the gas driving a piston to compress the specimen at a controlled velocity.&apos; To obtain points on the log a vs log E&apos; curve at low rates, specimens were compressed by a dead weight. strain rate was an average value computed by dividing strain at the end of test by loading time. In some tests strain was measured at fractions of the loading time; creep rate was found to be reasonably constant.

Jan 1, 1969

By D. W. Smith, C. H. Mathewson

In a series of papers published recently,&apos; R. F. Mehl and associates have studied the characteristics of form and orientation of many segregate structures and have found diversified conditions which can be explained only by postulating some specific kind of cooperative mechanism permitting the matrix lattice in some favorable region to transform into the segregate lattice in an adaptable region presenting a geometrically similar arrangement of atoms. We have collected the published data on crystallographic relationships of this sort, chiefly derived from Mehl&apos;s work, in Table 1. It is evident at once that the crystal structure of the matrix does not uniquely determine the location of the plate structures or other forms assumed by the segregate. Thus, the first seven items in the table represent precipitation of platelike forms from a matrix of face-centered cubic structure, but these plates are found stratified along planes of form {1111, {loo), {110) or another unidentified form, depending upon specific conditions involving the nature and concentration of the segregating substance. Again, in a matrix of body-centered cubic structure, plates, needles or stars have been found and the favored inner surface of segregation may be a plane of form (110), (112), {210), or indeed a surface without crystallographic indices defining a bundle of close-packed lattice lines (strings of atoms) taken more or less at random. Such a surface might be formed ideally by revolving one of these parallel strings of atoms around another as an axis. Hanemann and Schroder2 recently discussed these questions, principally with relation to original conceptions concerning the process of

Jan 1, 1932

By Howard R. Pratt, Jimmie L. Bratton

The Air Force Weapons Laboratory (AFWL) has been carrying out a series of experiments whose principal purpose is to measure the dynamic response of rock media to large pressure pulses. Coupled with the field experiments have been theoretical calculations simulating this response. These two approaches allow an appraisal of the current ability to measure in-situ rock response under extreme conditions and also give a fair estimate of the current state-of-the-art in the area of computer calculation of the response of "real" geologic media to a large load. The area chosen for the test series is composed of a sequence of sedimentary units (shale, sandstone, and limestone) located in the Estancia Valley 45 miles east of Albuquerque, N.M. (Fig. 1). The units, which dip gently off the uplifted Manzano Mountains to the west, are essentially horizontal at the test site. An extensive geologic and geophysical investigation of the area was carried out in the form of surface mapping and seismic exploration. Numerous holes were cored and material properties were determined from tests of the cores. In-situ geophysical measure¬ments were also carried out. The experiment consisted of loading a 60X40 ft test area with a 4000-psi transient exponentially decaying pressure pulse. The pulse was initiated at one end and traveled the 60-ft length of the test bed. The test area was instrumented with acceleration, velocity, and strain measuring devices placed in drill holes to depths of 30 ft. Theoretical computer calculations of the response of the layered geologic media have been carried out on the AFWL CDC 6600 using one and

Jan 1, 1972

By G. H. Anderson

During an investigation of the copper-rich portion of the copper-silicon-iron system as part of an extensive research program on P.M.G. alloys, which was begun in 1937 in the research laboratory of the Phelps Dodge Corporation, it became apparent that the binary copper-silicon system below 7 per cent Si needed revision, therefore an investigation was undertaken. Both X-ray methods and microscopic technique were employed. Despite the many investigations that have the clarification of this system as their object, no two successive reports on the system have agreed in placement of the alpha-phase solubility limit, and uncertainty about the secondary phase first to appear has been voiced several times.3,4,5 It was therefore not surprising, when T. Isawa&apos;s6 and M. Okamoto&apos;s7 works were reported at the time we were finishing up our experimental work, to find essential disagreement between their results and ours. But when C. 5. Smith&apos;s latest work on the copper-silicon systema was published just as we were finishing our laboratory report, it was indeed gratifying to find that the latter&apos;s diagram and ours checked in all essential features, except the temperature of the peritectoid line above 830" C. Many attempts were made to retain the beta phase during the present investigation, but none was successful. Isawa,6 however, reports that he has been able to obtain X-ray photograms of the beta phase. The structure, he states, is body-centcrcd cubic with a lattiee constant of 2.848 ,&. at 7.2 per cent Si. Okamoto7 and Smith8 both use the designation Kappa for the hexagonal phase, and to avoid confusion this designation will he adhered to in the present paper. Preparation of Samples The alloys were melted in vacuum in a high-frequency furnace. from copper cathodes containing 99.98 per cent Cu, and specially refined silicon supplied by The Electro Metallurgical Co. This silicon is stated

Jan 1, 1940

By G. H. Anderson

During an investigation of the copper-rich portion of the copper-silicon-iron system as part of an extensive research program on P.M.G. alloys, which was begun in 1937 in the research laboratory of the Phelps Dodge Corporation, it became apparent that the binary copper-silicon system below 7 per cent Si needed revision, therefore an investigation was undertaken. Both X-ray methods and microscopic technique were employed. Despite the many investigations that have the clarification of this system as their object, no two successive reports on the system have agreed in placement of the alpha-phase solubility limit, and uncertainty about the secondary phase first to appear has been voiced several times.3,4,5 It was therefore not surprising, when T. Isawa&apos;s6 and M. Okamoto&apos;s7 works were reported at the time we were finishing up our experimental work, to find essential disagreement between their results and ours. But when C. 5. Smith&apos;s latest work on the copper-silicon systema was published just as we were finishing our laboratory report, it was indeed gratifying to find that the latter&apos;s diagram and ours checked in all essential features, except the temperature of the peritectoid line above 830" C. Many attempts were made to retain the beta phase during the present investigation, but none was successful. Isawa,6 however, reports that he has been able to obtain X-ray photograms of the beta phase. The structure, he states, is body-centcrcd cubic with a lattiee constant of 2.848 ,&. at 7.2 per cent Si. Okamoto7 and Smith8 both use the designation Kappa for the hexagonal phase, and to avoid confusion this designation will he adhered to in the present paper. Preparation of Samples The alloys were melted in vacuum in a high-frequency furnace. from copper cathodes containing 99.98 per cent Cu, and specially refined silicon supplied by The Electro Metallurgical Co. This silicon is stated

Jan 1, 1940

By Edward E. Hicke, Charles A. Stickels

The dihedral angle of liquid-lead inclusions in solid nickel has been measured as a function of temperature from 371 to 816 C at zero pressure. and as a function of pressure up to 50,000 psi at 317 and 593 C. Thermodynamic expressions are derived for the temperature and pressure coefficients of interfacial tensions in this system. A method is presented for obtaining relative tempmature and pressure coefficients from dihedral-angle data, and the resulting values are used in conjunction with the thermodynamic relations to calculate excess properties of the solid-liquid interface. Defining the position of the solid-liquid interface by the condition that the excess concentration of lead is zero, the excess concentration of nickel and the excess entropy at the solid-liquid interface are: where y(593) is the interfacial tension of the nickel grain boundary saturated with lead at 593C and zero pressure. These values are considered reliable to within a factor of two. While similar calculations are not possible for the nickel grain boundary, it is shown that the expwimental results imply that the excess concentration of nickel at the boundary and the excess entropy of the boundary are negative. THE temperature and composition dependencies of interfacial tensions in metal systems have been reported by several authors in the last 15 years.&apos;-&apos; No measurements of the effect of pressure on inter- facial tensions in metals have been reported, although measurements made on nonmetallic gas/liquid and liquid/liquid systems suggest that a measurable effect should exist.6-l2 The purpose of these experiments was to determine the influence of temperature and hydrostatic pressure on dihedral angles in the Pb-Ni system. The equilibrium dihedral angle is expressed as a ratio of interfacial tensions by2: where 8 is the dihedral angle, yGB is the Ni-Ni grain boundary tension, and SL is the solid Ni-liquid Pb interfacial tension. Three sets of ex- periments were run to determine: a) the effect of temperature from 371" to 816°C on the dihedral angle at zero pressure; b) the effect of pressure up to 50,000 psi on the dihedral angle at 371° and 593°C. THERMODYNAMICS The properties of interfaces of most direct concern are the interfacial tension, excess concentrations of various components at the interface and the excess entropy of the interface, S°. These quantities are defined following Gibbs. Consider an interface separating phases a and 0. Construct two surfaces C, and C such that all properties of phase a remain uniform up to C, and all properties of phase 0 remain uniform up to C. The region between C, and Cp is the interfacial region. Let a "dividing surface", D, be constructed in the interfacial region such that it passes through all points "similarly situated with respect to the condition of the adjacent matter."l3 Surface D divides the interfacial region into a portion a&apos; adjacent to phase adjacent to phase . Let a closed curve, C, enclose an area A in D. Erect normal lines to D along C; these lines and the surfaces C,, Cp, and D then enclose volumes V and V&apos; in the two halves of the portion of the

Jan 1, 1964

By R. F. Mehl, J. K. Stanley

THE recrystallization of cold-worked metals is studied ordinarily by determining the temperatures required for complete recrystallization to occur within a given arbitrary time period, usually within 15 min. to 2 hr. The results obtained are conventionally assembled in a three-dimensional diagram relating this temperature to the amount of cold-work (percentage deformation) and the resultant grain size, though sometimes other modes of representation are employed.1 Such three-dimensional diagrams are not complete, for the number of variables exceeds the number represented. The process of recrystallization is characterized by a time-rate, a fact that is not portrayed upon ordinary recrystallization diagrams. It is known that recrystallization consists in the formation of new nuclei and the growth of these nuclei, a process that continues until the matrix is completely consumed and the original set of grains entirely replaced by the new. This knowledge is old.2 Truly heterogeneous reactions invariably proceed by nucleation and growth; the decomposition of eutectoid solid solutions provides an example about which much is known,3 and freezing, originally studied by Tammann, provides the classic example. Although recrystallization is not a heterogeneous reaction .within the orthodox meaning of the term, the mechanism of the process is the same. As in eutectoid inversion and freezing, it should be possible to study the rate of isothermal recrystallization as a function of time, and it should also be possible to analyze the isothermal reaction curve into the component rates of nucleation and growth that determine them.* Other methods, not employing the rates of nucleation and growth, have been used to represent the rates of such reactions, but these in general have been artificial and have not led to progress.4,5? The theory of recrystallization is not in advanced state; if recrystallization data were obtained, in terms of the rate of isothermal recrystallization, and in terms of the rate of nucleation and the rate of growth of recrystallized grains, and in particular if the temperature coefficients of these rates were measured accurately, an adequate theory should be more readily developed.27 Such an effort requires proper experimental technique, but especially requires suitable methods of mathematical analysis to convert measurements made upon a surface of polish into values for the rate of nucleation and the rate of growth and to combine these into a rate of isothermal recrystallization. These methods are now

Jan 1, 1942

By William Klement

THIS note reports the results of some attempts to metastably extend the primary solid solubilities of tin, antimony, and silicon in silver by rapidly quenching these binary alloys from the melt. The procedures employed for alloy preparation, quenching, and Debye-Scherrer X-ray diffraction measurements have been described elsewhere. The lattice parameters obtained for the fcc structures in Ag-Sn and Ag-Sb alloys are presented in Fig. 1, together with the results of Owen and Roberts.4 Alloy compositions are believed to be within ± 0.2 at. pct on the basis of negligible weight losses during preparation and reproducibility of the lattice spacings. Diffraction lines from hcp phases were also detected: the relative visual intensities of the fcc (200) and hcp (10.2) lines were estimated as shown in Table I. The intensities were m for the (200) and w for the (10.2) in a quenched 13.6 at. pct Sn alloy: a lattice spacing for the fcc structure could not be reliably obtained, however. As seen from Fig. 1, the lattice parameters vary linearly with composition up to 8., at. pct Sb and 13." at. pct Sn, respectively, which may be compared with the maximum equilibrium solid solubilities5 of 7.2 at. pct Sb and 11.5 at. pct Sn, respectively. The presence of the hcp phases, which were found together with the fcc phases, is a consequence of the competition1,3 in the nucleation and growth processes during solidification. Both the fcc and hcp phases must be of the same composition for those alloys in the range where lattice parameters increase linearly with solute concentration. Despite much effort with quenched alloys of several silicon concentrations, it has not been possible to obtain lattice spacings of sufficient precision to establish the variation of lattice parameter with composition or the maximum metastable solid solubility: the equilibrium data5 suggest little primary solid solubility of silicon in silver. For alloys containing less than 16 at. pct Si, the Si (111) diffraction line was not observed. For alloys containing 10 to 25 at. pct Si, faint low-angle lines were detected and these could be indexed as the (10.0), (00.2). and (10.1) reflections of an hcp structure with a = 2.87 + 3A. c = 4.52 ± 3A, and c/a = 1.57 ± 2. The 16 at. pct Si alloy was quenched to, and examined at. liquid nitrogen temperatures without any change observed in the proportion of the hcp phase. These experiments were jointly supported by the Atomic Energy Commission and Office of Naval Research under a program directed by Professor P. Duwez. The assistance of H.-L. Luo and A. Abu-Shumays is acknowledged. as is the support afforded

Jan 1, 1965

By Frank Foote, E. R. Jette

Precision lattice-constant measurements have been widely used in the study of cubic solid solutions but as yet have been rarely applied to noncubic solid solutions. (See, however, references I and 2.) With the high precision at present attainable in the measurement of lattice constants, the X-ray method should be readily applicable to noncubic solid solutions. In the work reported here, hexagonal close-packed magnesium was used as the solvent and either lead, bismuth or gold as the solute. In the magnesium-lead and magnesium-bismuth systems the a and c lattice constants were determined as a function of composition, densities were calculated from these lattice-constant data, these theoretical densities were compared with those directly measured and the solid solubility limit was determined on quenched specimens over a considerable range of temperature. In the magnesium-gold system, the solid solubility is very small but we have obtained an indirect check on the solubility limit previously reported. Materials and Preparation oF the Alloys The magnesium used was obtained from the Aluminum Company of America and was 99.987 per cent pure. Impurities as reported On the label were: Fe, Al, 0&apos;004 per cent; Si, 0.009 per cent; Zn, trace; Cu, Pb, nil. The bismuth was Merck&apos;s analytical grade, minimum purity 99.95 per cent. Maximum impurities as listed on the label were: Fe, 0.008 per cent; Pb, 0.010 per cent; Ag, 0.010 per cent; Cu, 0.005 per cent; Sn, 0.003 per cent; Sb, 0.00; As, 0.000; S, 0.01 per cent. The gold was purified by double precipitation with sulphur dioxide. The lattice constants of these three metals have been previously reported.3 The lead used was test lead, silver free and with a maximum of 0.10 per cent heavy metal impurities. The lattice constant 01 this lead has been measured and found to be 4.94057 ± 0.00016 at 25°C. The alloys were prepared by melting together weighed amounts of the constituent metals in magnesia-lined alundum crucibles under an atmosphere of hydrogen purified by passing over magnesium heated to 500°C. The magnesia lining prevented contamination 01 the alloys with aluminum. Vacuum melting could not be used because of the volatility of magnesium. A high-frequency induction furnace was used for the melting operation and the stirring action of the current resulted in thorough mixing of the constituents. The melts were allowed to freeze in the crucible, the ingots obtained weighed about 10 grams. An extremely thin white film formed on the surface of the melts, sometimes covering only a part of the exposed surface. The ingots were filed clean, placed in small iror crucibles with close-fitting lids and indi. vidually sealed into Pyrex glass tubes Before sealing off, the tubes were alter

Jan 1, 1941

By Frank Foote, E. R. Jette

Precision lattice-constant measurements have been widely used in the study of cubic solid solutions but as yet have been rarely applied to noncubic solid solutions. (See, however, references I and 2.) With the high precision at present attainable in the measurement of lattice constants, the X-ray method should be readily applicable to noncubic solid solutions. In the work reported here, hexagonal close-packed magnesium was used as the solvent and either lead, bismuth or gold as the solute. In the magnesium-lead and magnesium-bismuth systems the a and c lattice constants were determined as a function of composition, densities were calculated from these lattice-constant data, these theoretical densities were compared with those directly measured and the solid solubility limit was determined on quenched specimens over a considerable range of temperature. In the magnesium-gold system, the solid solubility is very small but we have obtained an indirect check on the solubility limit previously reported. Materials and Preparation oF the Alloys The magnesium used was obtained from the Aluminum Company of America and was 99.987 per cent pure. Impurities as reported On the label were: Fe, Al, 0&apos;004 per cent; Si, 0.009 per cent; Zn, trace; Cu, Pb, nil. The bismuth was Merck&apos;s analytical grade, minimum purity 99.95 per cent. Maximum impurities as listed on the label were: Fe, 0.008 per cent; Pb, 0.010 per cent; Ag, 0.010 per cent; Cu, 0.005 per cent; Sn, 0.003 per cent; Sb, 0.00; As, 0.000; S, 0.01 per cent. The gold was purified by double precipitation with sulphur dioxide. The lattice constants of these three metals have been previously reported.3 The lead used was test lead, silver free and with a maximum of 0.10 per cent heavy metal impurities. The lattice constant 01 this lead has been measured and found to be 4.94057 ± 0.00016 at 25°C. The alloys were prepared by melting together weighed amounts of the constituent metals in magnesia-lined alundum crucibles under an atmosphere of hydrogen purified by passing over magnesium heated to 500°C. The magnesia lining prevented contamination 01 the alloys with aluminum. Vacuum melting could not be used because of the volatility of magnesium. A high-frequency induction furnace was used for the melting operation and the stirring action of the current resulted in thorough mixing of the constituents. The melts were allowed to freeze in the crucible, the ingots obtained weighed about 10 grams. An extremely thin white film formed on the surface of the melts, sometimes covering only a part of the exposed surface. The ingots were filed clean, placed in small iror crucibles with close-fitting lids and indi. vidually sealed into Pyrex glass tubes Before sealing off, the tubes were alter

Jan 1, 1941

By Hsun Hu, R. S. Cline

In an earlier publication1 it was shown that a single crystal of Cu-4 wt pct Al cold-rolled in the (110)[112] orientation was stable up to 95 pct reduction, although the orientation spread was considerable larger than in a similarly oriented and cold-rolled copper single crystal. When rolled to 99 pct reduction, the copper crystal retained its initial orientation and a high degree of sharpness of texture, whereas the Cu-4 pct

Jan 1, 1969

By Erwin H. E. Gaertner

The brown-coal opencast mines in Germany&apos;s Rhineland have to cope with several problems. Predominant are densely populated areas with highly productive farmland, many railroads, highways, and rivers, as well as towns and farm settlements which have to be removed before or during the lifetime of a mine. Also the ground- water table has to be lowered to keep the deep opencast mines dry and stable. These problems urged a development towards deep opencast mines with powerful machines; the large material movement and the high coal production are the basis for the economic success in working the Rhenish brown-coal deposits. Up to now, bucket wheel excavators with a daily capacity of 100,000 m3 (130,000 cu yd) are in operation. Machines of twice this capacity are under construction. Corresponding to the excavators development, the stackers&apos; capacity has to be increased too. The new stackers will reach a daily capacity of 240,000 m3 (310,000 cu yd). The haulage in the mine is performed by conveyor belt systems, which are arranged in such a manner that the belt lines meet at a belt switching point. Here the incoming lines may be connected to the outgoing ones so as to direct the material flow to the desired receiving stations. At the moment there are conveyor belts in operation with a width of 2.2 m (7.2 ft); the new belts will have a layout for 37,000 t/h (40,770 stph), the width of which amounts to 3.0 m (9.8 ft). All belts and driving stations on benches are shiftable.

Jan 1, 1976

By C. H. P. Lupis, Henri Gaye

There are m -I conditions for the stability of a solution of m components with respect to infinitesinzal flucturations. However, in most cases, only one of these conditions has to be considered to determine the domain of instability and the existence of this more restrictive condition greatly simplifies the calculations. It may be used advantageously for the prediction of miscibility gaps and the method is illustrated in details for the case of the Ag-Pb-Zn system. THE thermodynamic conditions for the formation of a miscibility gap may be viewed as a necessary consequence of the conditions for spinodal decomposition. A previous article1 has examined in detail the form of these conditions for multicomponent systems. There is only one condition for the stability of a binary system (with respect to infinitesimal fluctuations), but there are two conditions for a ternary system, and m — 1 conditions for an m-component system. The probability of violating a stability condition, and thus forming a miscibility gap, obviously increases with the number of components, a result which is rather intuitive since the atoms of the solution have now many more ways of redistributing themselves and introducing complexities in the form of the free energy hy-persurface. It is of interest to take advantage of this possibility of precipitating new phases and to examine which stability condition is the likeliest to be violated, that is, which stability condition is thermodynamically the most restrictive. The finding of such a condition would greatly simplify the application of the stability criteria since only one condition could then be considered, instead of m - 1. In Ref. 1, coherency strain energy terms were neglected, thus restricting the applications of the treatment to solutions where they are negligible, such as liquid alloys. In the following study the same assumption will be made. To generalize the treatment to systems where the strain energy terms are sizable, the reader is referred to Cahn&apos;s classical article on spinodal decomposition.2 Let us designate by Gij the second derivative of the Gibbs free energy with respect to the number of moles ni and n j. There are several equivalent sets of m — 1 stability conditions.&apos; The one considered here expresses that the successive diagonal determinants of order 1, 2, ... m — 1, associated with the symmetric Gij matrix (for 2 5 i, j 5 m) are positive.&apos; For a binary solution 1-2, the condition for stability is: O(u=G22^0 [1] For a ternary system 1-2-3, the condition [I.] is re- tained (the value of G22 will differ, of course, according to the concentration of 3) and another condition is introduced: £>(21 = G22G33 - Gl3 ^ 0 [2] In a composition diagram, these two conditions define two domains of instability. Starting at a point where the solution is stable (for instance at a point where the solution is very dilute) we gradually change the composition until the condition [I] or [2] is violated. As already noted in the literature, e.g., in the work of Prigogine and Defay,3 it is the boundary of the domain (2) which is first crossed. For if we assume that the boundary of the domain (1) is reached first, at this point G22 = 0 and the second condition is necessarily violated (D(2) = -& 5 0), in contradiction with our original assumption. An exhaustive study of the ternary regular solution case may be found in the work of Meijering.4 Moreover if the boundaries of the two domains have a common point, they also have a common tangent. For if the two lines were to cross each other as is illustrated in Fig. 1(a) any point M in the line QP would be such that £> = 0 and 0"&apos; > 0 which, as shown above, are incompatible results. Thus, the two lines must be tangent at their common point Q as illustrated in the example of Fig. l(b). The reasoning of Fig. l(a) implies that the point Q is not a "singular" point for either boundary line. This singularity may be of two types. First, the lines meet without crossing each other and without being tangent. Second, the tangent at Q for D"&apos; or 0"&apos; is not single-valued. Other types of singularity are unlikely because of the usual analytical forms of D"&apos; and 0"&apos;. The exception to the common tangent requirement due to the first type of singularity was pointed out by John Morral;5 it occurs when the common point, Q&apos; or (3" in Fig. l(b), is located at a boundary of the composition diagram, e.g., at the line X3 = 0. It may also be noted that at the common nonsingular point Q of D(1) and D(2), Fig. 1(b), G23 is necessarily equal to zero, whereas at a point such as Q&apos; or Q", this conclusion is no longer valid because the product G22G33 is now indefinite (of the form 0. a). The exception to the common tangent requirement due to the second type of singularity occurs when two branches of the same boundary line intersect, for example when D(1)or D(2) decomposes into a product of functions, at a point which belongs to the boundary of the other condition. It is possible to show by a simple analytical calculation that, in this case, if Q is a singular point of D(1), then it is necessarily a singular point of D(2), and that the reciprocal is true except if G33 = 0 at Q. For the present article, however, more elaboration on these singularities appears to be unwarranted. To generalize the previous results to an m -component system, we use the mathematical theorem stating that if the diagonal determinant D(r) = 0, then

Jan 1, 1970