By D. W. Lillie

Property changes produced by irradiation of Al-0.4 wt pet Li alloys at 270°C to a burnup of 0.155 pct of all atoms are described. Metallographic evidence of the formation of internal pores and the concentration of gases at grain boundaries is shown. Some conclusions are drawn concerning desirable property characteristics for resistance to radiation swelling. RADIATION induced gases are of great practical significance in nuclear engineering since they affect the behavior of fissionable fuels and control rod materials. In fuels the gases xenon and krypton are the major offenders, producing serious em-brittlement at low irradiation temperatures and gross swelling at high irradiation temperatures. In control rod materials containing boron, the production of helium from the B 10 (n, 0) Li7 reaction produces similar reactions. Since the trend in reactor design is for operation at increasingly high temperatures, the phenomenon of high-temperature swelling by these induced gases has been the subject of considerable recent study. The objectives of such work have been to obtain engineering information and quantitative data on the effects in specific fuels and control rods and to obtain further understanding of the mechanism of gas damage so that more intelligent corrective steps can be made. Analogue systems are often useful for the latter objective and in this case alloys containing Li are suitable in view of the reaction Li6 + n - He4 + He 4. Both products are gases and no serious radiation problem is produced to complicate post irradiation handling. Considerable caution is, of course, necessary in any operations in which tritium release is possible. The present program was initiated to provide a detailed study of the effects of He + H3 generated by irradiation in Li-bearing alloys. The results on Mg-Li solid solution alloys have been reported elsewhere.' This paper presents information on irradiation of an A1-0.4 pct Li alloy in which the lithium was present as highly enriched Li6 in order to maximize the radiation burnup. PROCEDURE The original intent in the selection of the alloy content was to have Li in solid solution at all temperatures. It became apparent, however, that the solubility of Li in A1 was substantially lower than that reported in the original reference consulted.' This was substantiated by the work of Nowak3 who reported solubility of less than 0.01 pct Li at 100°C. The alloy used (0.4 pct Li) was therefore two phase at room temperature. The irradiation temperature was estimated to be about 270° C, and at that temperature all or almost all of the Li would be soluble under equilibrium conditions. The precise state of the alloy under irradiation is not known. Aluminum used was 99.996 pct purity (max. impurities Si 0.002 pct, Mg 0.001 pct, Fe 0.0005 pct, and Cu 0.0005 pct). The lithium was obtained from Oak Ridge National Laboratory; 96.1 + 0.1 pct of the lithium was ~i~, but chemical impurities were 0.25 pct Ca, 0.05 pct Fe, 0.02 pct Na, 0.02 pct Cu, 0.01 pct Sr, and 0.01 pct Ba. The two metals were melted in an alumina crucible in a resistance heated furnace in an atmosphere of helium. A l-in. ingot was cast in an iron mold, machined to %-in. round, hot swaged (350°C) to 0.080-in. round, cold swaged to 0.060-in. round, and finally cold drawn to 0.040-in. round. Four-inch wire lengths were then cut and annealed at 250°C for 4 hr in helium. Irradiations were carried out in a VT hole in the Argonne CP-5 reactor. The wires were held in an aluminum jig, sixteen wires per capsule, and were maintained in a helium atmosphere for maximum heat transfer. Eight wires of pure aluminum and eight of Al-Li alloy were placed in each capsule. Argome Laboratory statements were accepted as establishing flux and exposure levels. These were based on previous experience and flux map-

Jan 1, 1961

By P. R. Sperry, A. P. Beck

It has been shown1 that in poly-crystalline strips of high purity aluminum with a fairly random orientation distribution, grain growth progresses gradually until the average grain diameter reaches a value approximately equal to the strip thickness. Recent work at this laboratory led to the realization that grain growth might be impeded to a considerable extent in the presence of a sharply defined texture, where orientation differences between neighboring grains are small. In order to investigate this effect the following experiment was carried out with the same lot of high purity aluminum previously used for grain growth studies in randomly oriented material.' Very large grain size was developed by grain growth at 650°C in specimens of 0.200 in. thickness. These specimens were then rolled to a thickness of 0.050 in. or 1.25 mm—a reduction of 75 pct. In the rolled strip each large grain corresponded to an elongated area easily identified by etching. After annealing for 1 to 25 min at 600°C and re-etching, these elongated areas were again recognizable. Within each area, corresponding to a single large grain before annealing, there formed by recrystallization a multitude of new grains with a fairly well developed preferred orientation. The orientation and the size of the new grains formed in areas corresponding to different large grains, varied widely depending on the orientation of the parent grains with respect to the rolling direction and the plane of rolling. Many areas were found where the average grain size was considerably smaller than the specimen thickness. Such an area occurred in a specimen cut in half before annealing. One half, containing a portion of the area in question, was annealed 1 min at 600°C, the other half, with the remaining portion of this area, for 25 min at the same tempera-Aluminum killed low carbon steel, § which is now used extensively for severe deep drawing or other difficult forming operations, is unusual in that its grain structure, after cold reduction and box annealing in accordance with conventional continuous sheet or strip mill practice, often is elongated, although at times it is equiaxed. Since this unusual structure has been found superior for many, but not all, severe forming operations, recrystallization of the steel, both at constant temperature and on continuous heating, was investigated and compared with that of rimmed steel in the hope that something might be learned about the mechanism of, and the factors controlling, the formation of such elongated grains. In this structure, the grains are elongated both in the lengthwise direction of the strip and transverse to this direction, even though nearly all of the extension in both hot and cold rolling is in the lengthwise direction. The grains are thus roughly pancake-shaped, being longer and wider than they are thick, as observed also by Burns and McCabe,1 and as illustrated by the typical structures shown in Fig 1. Fig la, representing a conventional longitudinal section, shows the length and thickness of the grains, whereas Fig Ib shows their length and width as seen by examining a section parallel to the sheet surface. Both illustrate the very irregular grain boundaries usually associated with the elongated grain shape. A finer equiaxed grain structure in this same grade is shown in Fig Ic. Either the elongated or the equiaxed structure may be present in the annealed product, and in rare instances the two types may coexist in a single specimen, as shown in Fig 1 d. Isothermal Recrystalliza-tion of Rimmed and Alamimum Killed Steel An aluminum killed steel known to have an elongated grain structure after conventional processing (Steel B, Table l), was selected for the initial recrystallization studies; for comparison, a rimmed steel, A in Table 1, was used. Samples of each in the form of hot rolled strip 0.075 and 0.095 in. thick, respectively, were cold rolled on a small laboratory mill in steps of about 0.010 in. per pass to obtain total reductions of 40 and 60 pct. Small pieces of the cold reduced strip were heated in lead at selected constant temperatures for one of several periods of time, then cooled in air. Rate of heating in the lead was, of course, very fast. Hardness of the cooled specimen was measured and a longitudinal section examined metallographically. Isothermal recrystallization curves for these two steels at 1050°F, based on hardness of the air cooled specimens, are shown in Fig 2 in which the amount of recrystallization corresponding to each plotted point is indicated. The marked difference in the behavior of these two types of steel is evident. After a corresponding amount of cold reduction, the rimmed steel recrys-tallizes in a much shorter time than the killed steel and the shape of its recrystallization curve, (plotted on a logarithmic time scale), is very different. The curve for rimmed steel indicates that recrystallization is analogous to isothermal transformation of aus-i.enite in that it proceeds at a progressively faster rate up to some 50 pct recrystallization, then at an increasingly slower rate. For the aluminum killed steel, however, the start of

Jan 1, 1950

By Orville R. Lyons

THE relative performance of coal washing equipment, or the effectiveness with which any type or make of equipment removes impurities from coal, has been most difficult to evaluate in the past. The most widely used yardstick is the Frazer and Yancey efficiency formula developed in 1922,1 but Yancey in a later article states that "washers treating coals of different density composition or operating at different densities of separation cannot be compared directly on the basis of this criterion."' Prior to and since 1922, a variety of other methods has been used for comparison purposes, including the distribution curve, the error area, and the "ecart probable" or probable error. Yancey and Geer in discussing these methods conclude, "Performance can be evaluated in a number of different ways, with the choice of the proper method to use being dictated by the objectives of the investigation and the data available."' It is true that performance can be evaluated in a variety of ways, but if the equipment is to be evaluated on an effectiveness basis, there should be only one universal comparison method. Varying methods have been used because one universal comparison method has not been found or developed. In the article previously quoted, Yancey and Geer state in clear terms the primary concept for a universal comparison method: "One of the simplest, and certainly one of the most obvious evaluations of washery performance is the quantity of sink material in the washed coal and the float material in the refuse. If the washery products are tested at the density at which the washing unit is operated, the sink in the washed coal and the float in the refuse represent material that has been misplaced." The quantity of misplaced material was used as a criterion of washery performance by Lincoln in 1913,8 by the United States Bureau of Mines in 1938,4 by Hancock in 1947,3 and by the national French research agency Cerchar in recent years.2 In 1950 Anderson' proposed the use of this criterion as an efficiency value to replace the Frazer and Yancey formula. However, none of the above-mentioned investigators used the misplaced material concept in a manner that would provide universal coal-cleaning equipment comparisons. The Correlation Theory The ideal coal cleaning process would treat all sizes and would make a perfect separation at any given specific gravity. All material lower in density than the desired value would report in the coal product and all material higher in density would report in the refuse product. Unfortunately, no known cleaning process achieves this goal and there seems little likelihood that any process yet to be invented will do more than approach it. When coal is treated in volume under operating conditions, it is impossible to avoid mechanical entrapment, fluctuations in throughput and effective gravity of separation, and the creation of turbulent currents, even when a true heavy-liquid bath is used and the feed is closely sized and contains little intermediate gravity material. This being so, it is possible to appreciate the difficulties inherent in trying to obtain a perfect separation when treating a wide range of sizes and a feed containing high percentages of intermediate material, using turbulent currents to help create the effective separation gravity, under operating conditions which normally tend to be on the overload side. When coal is separated from refuse in any coal cleaning equipment, some refuse always reports to the coal and some coal to the refuse; the writer therefore assumed that there should be a relationship between the total amount of misplaced material produced by any given piece of equipment and the difficulty of separation as represented by the percentage of near gravity material in the feed. With small amounts of near gravity or ±0.1 material in the feed there should be less misplacement of material than would occur with large amounts of near

Jan 1, 1952

By W. F. Rogers, J. A. Stewart, P. J. Kalish, E. O. Bennett

Detailed descriptions are given of materials, apparatus and the experimental procedure used to study the effect of bacteria on sandstone permeability. The factors affecting permeability during injection of bacterial suspensions which have been investigated are: (I) concentration of bacteria; (2) core permeability and median pore size; (3) species of bacteria, mode of aggregation and relative size; (4) injection rate or pressure differential; (5) mean pressure; and (6) depth of penetration of bacteria. The investigation demonstrated that bacteria cannot reduce core pertneability to zero and that their effect on permeability is subject to definite limitations. Remedial or permeability restoration studies also were made. Acidization in combination with reverse flow war found to be an effective method for restoring permeability In cores partially plugged with bacteria. The relationship between the bacterial quantities in the laboratory tests and those found in field operations is discussed. The linear laboratory flow data have been translated into terms of field radial systems; these data indicate the most practical methods of maintaining injection rates in the presence of bacteria are to increase injection pressures or hydraulically fracture the formation. INTRODUCTION It has long been known that various bacteria flourish in the above-ground components of oil field water-injection systems. The presence of these bacteria has led to the suspicion that they might enter into the causes for reduction of injection well permeability, but only recently has an attempt been made to describe the effects quantitatively.1 Biocides are used in many cases without a firm knowledge as to whether the bacteria are killed, or if they are, whether the dead cells affect formation permeability. This project was undertaken as part of a study to determine the effect of bacteria, residual oil and precipitated solids such as iron sulfide or calcium carbonate on the permeability of sandstones and to learn whether any of these materials adversely affect brine injectivity in secondary recovery or disposal operations. This report deals with that portion relating to the effect of bacteria. MATERIALS CORES Three different permeability ranges of Berea sandstone cores were used in the study. The range of initial, absolute brine permeabilities kj were: high — 278 to 400 md: medium—130 to 162 md; and low—17.7 to 48.3 md. The permeability data for the cores used in the tests are included in Table 1. All cores were cut to a nominal 1 in. diameter. Following air permeability determinations, they were molded with an epoxy resin in 1.5 in. ID aluminum sleeves. The sleeves had drilled and tapped holes for intermediate pressure connections along the length of the cores. After molding, the high- and medium-permeability cores were trimmed to 4 in. in length and the low-permeability cores to 2 in. These lengths resulted in pore volumes of approximately 10.9, 10.4 and 4.4 ml, respectively, for the high-, medium- and low-permeability cores. Pressure-transmitting channels were drilled through the plastic into the core proper, using the sleeve holes as drill guides. Width and depth of channel penetration into the core proper were approximately 0.03 in. and 0.05 in., respectively. Three pressure taps were used with all cores; for the high- and medium-permeability cores the taps were spaced 1 in. apart; for the low-permeability cores the taps were spaced 0.4, 0.8 and 1.2 in. from the inlet end. Pore size distributions were calculated from restored-state capillary pressure curves for representative cores in each of the three permeability ranges. In each case the pore size range with the greatest percentage of the pore space included the very small pores up to 0.5 micron in radius. The median pore radii were in the 5.5 to 6 micron range for the high-permeability cores; in the 4.5 to 5 micron range for the medium-permeability cores; and in the 3.5 to 4 micron range for the low-permeability cores.

Jan 1, 1965

By J. L. Huitt, S. R. Darin

The use of a partial monolayer of propping agent to obtain a high flow capacity for a hydraulically induced fracture is discussed. From the results of laboratory work it was shown that a modified form of the Kozeny-Carman relation could be used to describe the flow in the partial monolayer propped fracture. With equations presented in the paper, the density pattern of the propping agent (number of particles per unit of fracture surface) that results in the maximum flow capacity for the fracture can be determined. The maxitnum flow capacity obtained with a partial monolayer is often an order of magnitude greater than the flow capacity obtained in greater width fractures containing multilayers of the propping agent. INTRODUCTION One of the predominant factors controlling the success of a hydraulic fracturing operation is the propping of the fracture. The trend in hydraulic fracturing recently has been an increase in the ratio of propping agent-to-fluid. The primary purpose of this increased ratio is to sustain a propped fracture of greater width. It was shown in a recent study' that for some formations low concentrations of propping agent would result in "closing" or "healing" of the fracture. In some cases, in an effort to insure sufficient propping agent concentration, the fracturing operation is designed to obtain a pack of the propping agent in the fracture. The placing of a pack of propping agent in the fracture provides a fracture of maximum width; however, the width alone does not control the flow capacity of the fracture. The flow capacity is dependent on the permeability of the fracture, as well as the fracture width. Thus, increasing the permeability to obtain larger flow capacities is as important as obtaining a greater width fracture. By increasing the concentration and particle diameter of the propping agent, fractures of sufficient flow capacities are obtainable for effective well stimulation in a number of formations. However, in some of the recovery techniques, the fracture capacity obtained by commonly used practices in fracturing is inadequate. One such recovery technique is gravity drainage via a horizontal fracture placed near the base of the productive zone. For this recovery technique, the fracture capacity desired is usually one to two orders of magnitude greater than the fracture capacity normally obtained in fractures propped with the size of sand commonly used (20-40 mesh). By the use of particles of larger diameter, the permeability of a pack2 is increased; however, even a multilayer pack results in a fracture flow capacity lower than that desired for some formations. For example, a fracture of 1/4-in. width, packed with 8-12 mesh sand of about 2,000 darcies permeability, would result in a fracture flow capacity (permeability X fracture width) of only 40,000 md-ft. If the fracture flow capacity needed is an order of magnitude greater than that cited in the example, an approach different from the formation of a pack in the fracture is needed. One approach is a partial monolayer of large-diameter propping agent. In working with this type of fracture system, it was found that the flow problems were unique to the system; therefore, the study discussed in this paper was made. THEORY AND RELATED STUDIES Previous studies, although related to that described in this paper, have not pertained directly to the flow in a fracture propped with a partial monolayer of propping agent. However, studies such as flow between parallel plates,' flow in packed columns,' fracture flow capacity' and flow in simulated fractures reduce the scope of this flow problem considerably. A fracture propped with a partial monolayer of dropping agent may be considered to be between two extremes — between an open fracture and a bed of particles packed In a conduit of fracture geometry. Thus, it seems appropriate to review the extreme cases.

By K. A. Johnson, F. H. Ellinger, C. C. Land

The Pu-In phase diagram has been determined by thevmal, filtvation, micrographic, and X-ray diffraction methods. This alloy system is characterized by 1) limited solubility of indium (-2 at. pet) in 6 and e plutonium, 2) one eutectic, and 3) fizte intermediate phases. Of the latter, PuIn and PuIn3 melt con-gruently, and Pu31n, Pu31n5, and the high-temperatuve 7 solid solution are formed peritectically. The n phase decomposes eutectoidally into Pu3In and PuIn at 865°C. Although the 6 phase can readily be retained to room temperature, it is not thermo-dynamically stable below 300°C. The Pu-In system has been investigated at Los Alamos as part of a study of the alloys of plutonium with the group 111-B elements. Constitutional studies of the Pu-A1 and Pu-Ga systems have been reported earlier.'9' To date, published information on the constitution of Pu-In alloys covers only the identification of the intermediate phases Pu3In and PuIn3.3,4 EXPERIMENTAL The alloys were prepared from five different lots of plutonium and three different lots of indium. The principal impurities in the plutonium differed from lot to lot within the following limits (in ppm): iron, 30 to 80; nickel, 30 to 60; aluminum, 15 to 30; silicon, 20 to 145: thorium, 50 to 300; carbon, 75 to 335; and oxygen, 20 to 135. Spectroanalysis of the indium showed that two of the lots were 99.9 wt pct pure, and the third was 99.98 wt pct pure. The alloys, in the form of about 5-g buttons, were prepared by arc melting in conventional equipment. The components for each alloy were weighed to the nearest 0.1 mg. In most instances the weight losses during melting were negligible; therefore confirmatory chemical analyses were usually not made. A few results are given in Table I. Density measurements of the arc-cast buttons were made by the liquid displacement of bromoben-zene. Heat treating was done in muffle furnaces controlled to +2°C. The alloy buttons were wrapped in tantalum foil before being enclosed in evacuated clear silica capsules. As a precaution against breakage, each capsule was in turn placed in a silica tube closed with a refractory wool plug prior to being charged into the furnace. For a moderately fast quench of the alloys, the outer protection tubes containing the capsules were plunged into cold water. Differential thermal analyses (DTA) in racuo were performed at heating and cooling rates of about 1.5°C per min. Tantalum crucibles having inverted thermocouple wells were used for most of the analyses. It was found micrographically, however, that the liquid alloys containing more than about 35 at. pct In reacted with the tantalum, resulting in contamination of the surface of the alloy. A search for a more satisfactory crucible material was not successful: tungsten and yttria behaved comparably to tantalum; thoria, vitrified magnesia, and vitrified alumina severely contaminated the alloys. So as to minimize the contamination by the crucible mater-

Jan 1, 1965

Joseph William Richards, was born in Oldbury, Worcestershire, England, on July 28, 1864, of English-Scotch parents, Joseph and Bridget (Harvey) Richards. In 1871, he came to this country with his parents. He attended the public schools of Philadelphia, Pa., where his father was a manufacturing metallurgist, and in 1882, graduated from the Central High School with the degree of A. B. The same year he entered Lehigh University, from which he received the degree of A. C. (Analytical Chemist) in 1886; M. S. in 1891, and Ph. D. in 1893. His connection with the university was continuous from 1887 until his death, and he therefore adds another to the list of names of men Prominent in the A. I. 11. E. who have helped to develop Lehigh University to the important position which it now occupies in mining and metallurgical education in respect of world-wide fame. It is fitting to recall in this connection that, Eckley B. Coxe, a fonnder of the A. I. M. E., four times its vice-president,, and president in 1878-79, was literally a pillar of the university for several years prior to his death; Thomas M. Drown, founder, vice-presi(lent, secretary for 11 years, honorary member, and president in 1897, was president of Lehigh University from 1895 to 1904; and Henry S. Drinker, founder, manager, vice-president, and honorary member, was president of the university from 1905 to 1920. Doctor Richards was no less active in both institutions. With the exception of the years 1886 to 1887, when he was superintendent of the Delaware Metal Refinery of Philadelphia, his professional life was devoted to the upbuilding of the metallurgical department of the university, in part through his continuous services as a member of the teaching staff, and in part through the international renown won for the department by his achievevements as author, investigator, expert and rerognizcd authority in metallurgy, especially the metallurgy of aluminum, metallurgical-chemical calculations, and electrometallurgy. He was assistant instructor in metallurgy and blowpiping in 1887; instructor, 1888-90; instructor in metallurgy, mineralogy and blowpiping, 1890-97; assistant professor, 1897--1903; professor of metallurgy, 1903-1921. He died at his home in Bethlehem, Pa., on Oct. 12, 1921, of heart failure. To the A. I. M. E., for a continuous period of a dozen years, his services were equally loyal and effective. He was vice-president, 1910-11, and 1916-17; councilor, 1912; dirctor, 1913-15; chairman of the Iron and Steel Clommittee, 191-1-21; he was one of the framers of the Insti-

Jan 1, 1922

Joseph William Richards, was born in Oldbury, Worcestershire, England, on July 28, 1864, of English-Scotch parents, Joseph and Bridget (Harvey) Richards. In 1871, he came to this country with his parents. He attended the public schools of Philadelphia, Pa., where his father was a manufacturing metallurgist, and in 1882, graduated from the Central High School with the degree of A. B. The same year he entered Lehigh University, from which he received the degree of A. C. (Analytical Chemist) in 1886; M. S. in 1891, and Ph. D. in 1893. His connection with the university was continuous from 1887 until his death, and he therefore adds another to the list of names of men Prominent in the A. I. 11. E. who have helped to develop Lehigh University to the important position which it now occupies in mining and metallurgical education in respect of world-wide fame. It is fitting to recall in this connection that, Eckley B. Coxe, a fonnder of the A. I. M. E., four times its vice-president,, and president in 1878-79, was literally a pillar of the university for several years prior to his death; Thomas M. Drown, founder, vice-presi(lent, secretary for 11 years, honorary member, and president in 1897, was president of Lehigh University from 1895 to 1904; and Henry S. Drinker, founder, manager, vice-president, and honorary member, was president of the university from 1905 to 1920. Doctor Richards was no less active in both institutions. With the exception of the years 1886 to 1887, when he was superintendent of the Delaware Metal Refinery of Philadelphia, his professional life was devoted to the upbuilding of the metallurgical department of the university, in part through his continuous services as a member of the teaching staff, and in part through the international renown won for the department by his achievevements as author, investigator, expert and rerognizcd authority in metallurgy, especially the metallurgy of aluminum, metallurgical-chemical calculations, and electrometallurgy. He was assistant instructor in metallurgy and blowpiping in 1887; instructor, 1888-90; instructor in metallurgy, mineralogy and blowpiping, 1890-97; assistant professor, 1897--1903; professor of metallurgy, 1903-1921. He died at his home in Bethlehem, Pa., on Oct. 12, 1921, of heart failure. To the A. I. M. E., for a continuous period of a dozen years, his services were equally loyal and effective. He was vice-president, 1910-11, and 1916-17; councilor, 1912; dirctor, 1913-15; chairman of the Iron and Steel Clommittee, 191-1-21; he was one of the framers of the Insti-

Jan 1, 1922

SEC. 1. This Institute is incorporated under the Membership Corporations law of the State of New York; its corporate name is American Institute of Mining and Metallurgical Engineers, Inc.; and its objects are such as are stated in its Certificate of Incorporation. ARTICLE II SEC. 1. The membership of the Institute shall comprise four classes, namely: 1. Members; 2. Honorary Members; 3. Associates; 4. Junior Associates. All members shall be equally entitled to the privileges of membership, excepting that Honorary Members, Junior Associates, and Members and Associates whose residences shall be outside of the United States, Mexico, and Canada shall not be entitled to vote. Members and Associates residing within the United States of America, Mexico, and Canada, and not in arrears for dues, shall be entitled to vote in person at the meetings of the Institute, or, as hereinafter provided for, by letter ballot. SEC. 2. Members shall comprise all those persons who on the third Mon- day of February, 1918, were members of the Institute, and in addition thereto, all those thereafter elected or transferred into the class of Members. A person to be eligible for election or transfer into the class of Members must be at least 27 years of age and must have had at least six years' employment in the practice of engineering, mining, geology, metallurgy or chemistry, during at least three years of which he must have held positions of responsibility in one or more of these fields. Graduation from the scientific course of a college, approved by the Committee on Membership, shall be considered equivalent to two years' employment, as required in the previous sentence. Employment as a teacher of engineering, mining, geology, metallurgy or chemistry, if in direct charge, may be considered a position of responsibility as specified in the second paragraph. Persons employed in research or any scientific literary work or in teaching in the scientific departments of colleges, approved by the Committee on Membership, who at the same time are engaged in consulting or in the active practice of mining, geology, or metallurgy, shall be entitled to consider the time so spent in active practice as equivalent to an equal length of time of employment in positions of responsibility, provided the work done or the positions held seem to the Committee on Membership to warrant the equivalency. The requirement of three years' employment in positions of responsibility may be waived by the Committee on Membership in the case of persons who have done notable original work in mining, or metallurgy, or have won distinction by research or investigations In one or more of these subjects.

Jan 1, 1928

By C. E. Arnold

A brief description of this installation was included in a recent paper by H. Kenyon Burch.l The purpose of the present paper is to amplify Mr. Burch's description, as it is felt by the writer that the subject merits more than passing attention. In making a comparison between the common method of hoisting men in mine shafts, and elevator practice in high buildings, the former shows to great disadvantage both as regards safety measures and smoothness of operation. It is surprising that in view of the inducements offered, the step of applying the building equipment direct to the mine shaft has not been taken before, as in many respects the conditions of service are similar, and the objects to be attained are identical. Even without doing this, it is certain that safety to life and limb in the usual method of hoisting men underground can be greatly enhanced by the application to the mine hoist of some of the features of the building elevator. In the case under consideration, the elevator cage runs in a vertical, concrete-lined shaft compartment 5 ft. 11 in. by 5 ft. 6 in. (1.8 by 1.68 m.) in section and 585 ft. (178 m.) deep, while the counterweight runs in the pipe and ladder compartment of a twin shaft 102 ft. (31 m.) distant. The section of the division of this compartment occupied by the counterweight measures 2 ft. 4 1/4 in. by 3 ft. 101/2 in. (0.72 by 1.18 m.), and the counterweight is made in the form of a small cage which suffices to carry two men for the purpose of making inspections or repairs in the pipe and ladder way. The hoist is designed to carry a load of 7500 lb. (3401.94 kg.), ex-clusive of the cage, which weighs 7500 lb., at a maximum speed of 800 ft. (243 m.) per minute. It is installed in the main hoist and compressor building about 220 ft. away from the elevator shaft and is driven by a 160-hp. direct-current motor which is served by a 190-hp. motor generator set. A small direct-current generator mounted at the end of the motor generator set furnishes the current for the controller magnets, brake and fields of the hoist motor and generator. The drum, which is 72 in. (1.83 m.) in diameter, is driven through the medium of a single reduction herringbone gear. A Francke flexible coupling connects the

Jan 1, 1918

SEC, 1, This Institute is incorporated under the Membership Corporations law of the State of New York; its corporate name is American Institute of Mining and Metallurgical Engineers, Inc,; and its objects are such as are stated in its Certificate of Incorporation. ARTICLE II MEMBERS SEC. 1. The membership of the Institute shall comprise four classes, namely: 1. Members; 2. Honorary Members; 3, Associates; 4, Junior Associates. All members shall be equally- entitled to the privileges of membership, excepting that Honorary Members, Junior Associates, and Members and Associates whose residences shall be outside of the United States, Mexico, and Canada shall not be entitled to vote. Members and Associates residing within the United States of America, Mexico, and Canada, and not in arrears for dues, shall be entitled to vote in person at the meetings of the Institute, or, as hereinafter provided for, by letter ballot, SEC. 2, Members shall comprise all those persons who on the third Monday of February, 1918, were members of the Institute, and in-addition thereto, all those thereafter elected or transferred into the class of Members. A person to be eligible for election or transfer into the class of Members must be at least 27 years of age and must have had at least six years', employment in the practice of engineering, mining, geology, metallurgy or chemistry, during at least three years of which he must have held positions of responsibility in one or more of these fields. Graduation from the scientific course of a college, approved by the Committee on Membership,' shall be considered equivalent to two years' employment, as required in the previous sentence, Employment as -a teacher of engineering, mining, geology, metallurgy or chemistry, if in direct charge, may be considered a position of responsibility as specified in the second paragraph. Persons employed in research or any scientific literary work or in teaching in the scientific departments of colleges, approved by the Committee on Membership, who at the same time are engaged in consulting or in the active practice of mining, geology, or metallurgy, shall be entitled to consider the time so spent in active practice as equivalent to an equal length of time of employment in positions of responsibility, provided the work done or the positions held seem to the Committee on Membership to warrant the equivalency. The requirement of three years' employment in positions of responsibility may be waived by the Committee on Membership in the case of persons who have done notable original work in mining, geology, or metallurgy, or have won distinction by research or investigations, in one or more of these subjects.

Jan 1, 1928

By M. F. Hawkes, R. F. Mehl

The rate of isothermal transformation of austenite to pearlite depends upon the rate of nucleation, N, and the rate of growth, G, of pearlite in austenite. Values of N are given in terms of the number of nuclei forming in unit time per unit grain boundary area of unreacted austenite; values of C are given in terms of the linear rate of radial growth. Variations in the isothermal rate with temperature result from variation of N and G with temperature. Depth of hardening of a steel depends fundamentally upon values of N and G; changes in carbon and alloy content effect changes in N and G and thus affect depth of hardening. Quantitative studies are available on N and G for the formation of pearlite in plain carbon eutectoid steels.3 Systematic studies in this field are necessary if the phenomena are to be well enough known to furnish a proper basis for full rationalization and for theory. Accordingly, the studies are continuing, both with respect to the effect of alloying elements upon the values of N and G in the formation of pearlite and to the values of N and G for the formation of ferrite in hypoeutectoid steels. The present paper is the first relating to the effect of alloying elements upon the values of N and G for pearlite. It offers special interest since cobalt is known to have an anomalous effect upon the rate of formation of pearlite, accelerating it, whereas all other elements retard it.4 It will be shown that cobalt increases both N and G for pearlite and that this effect is inherent in the Fe-Co-C system and not dependent upon factors relating to austenite heterogeneity nor upon any recognizable adventitious factor. Inasmuch as the rate of diffusion of carbon in austenite and the interlamellar spacing of pearlite are variables related to G and possibly to N (in a manner not yet certain), measurements of the effect of cobalt upon them are also reported here. In the course of the work, measurements were made on the effect of cobalt upon the marten-site temperature and these are given. COBALT AS AN ALLOYING ELEMENT IN STEEL Properties of Cobalt Cobalt resembles iron more closely than does any other chemical element. Its atomic number is 27, hence it is the element immediately following iron in the periodic system. The two differ in atomic structure only in the fact that cobalt contains seven electrons instead of six in the third, or transition, level of .the third shell. The next shell, which is the

Jan 1, 1948

By M. F. Hawkes, R. F. Mehl

The rate of isothermal transformation of austenite to pearlite depends upon the rate of nucleation, N, and the rate of growth, G, of pearlite in austenite. Values of N are given in terms of the number of nuclei forming in unit time per unit grain boundary area of unreacted austenite; values of C are given in terms of the linear rate of radial growth. Variations in the isothermal rate with temperature result from variation of N and G with temperature. Depth of hardening of a steel depends fundamentally upon values of N and G; changes in carbon and alloy content effect changes in N and G and thus affect depth of hardening. Quantitative studies are available on N and G for the formation of pearlite in plain carbon eutectoid steels.3 Systematic studies in this field are necessary if the phenomena are to be well enough known to furnish a proper basis for full rationalization and for theory. Accordingly, the studies are continuing, both with respect to the effect of alloying elements upon the values of N and G in the formation of pearlite and to the values of N and G for the formation of ferrite in hypoeutectoid steels. The present paper is the first relating to the effect of alloying elements upon the values of N and G for pearlite. It offers special interest since cobalt is known to have an anomalous effect upon the rate of formation of pearlite, accelerating it, whereas all other elements retard it.4 It will be shown that cobalt increases both N and G for pearlite and that this effect is inherent in the Fe-Co-C system and not dependent upon factors relating to austenite heterogeneity nor upon any recognizable adventitious factor. Inasmuch as the rate of diffusion of carbon in austenite and the interlamellar spacing of pearlite are variables related to G and possibly to N (in a manner not yet certain), measurements of the effect of cobalt upon them are also reported here. In the course of the work, measurements were made on the effect of cobalt upon the marten-site temperature and these are given. COBALT AS AN ALLOYING ELEMENT IN STEEL Properties of Cobalt Cobalt resembles iron more closely than does any other chemical element. Its atomic number is 27, hence it is the element immediately following iron in the periodic system. The two differ in atomic structure only in the fact that cobalt contains seven electrons instead of six in the third, or transition, level of .the third shell. The next shell, which is the

Jan 1, 1948

The first record of coal anywhere in the Appalachian regions of which we now know is along the north fork of the Potomac River, above the mouth of Savage River, on a map entitled, A Plan of the upper Part of Potomack River call Cohongorooto Survey'd in the Year 1736. Benj. Winslow1 two "Cole-mines" are shown, one just above Green Island and the other just below Hopwood Run. Winslow was in charge of a surveying party to "Lay out the Bounds of the Northern Neck of Virginia," or Lord Fairfax's Grant, his party locating the liver above the mouth of the Shenandoah, while another party located it below that point, and then around Chesapeake Bay and up the Rappahannock River. The results of the two surveys were combined in a map called, The Courses of the Rivers Rappahannock and Potowmack, in Virginia, as surveyed according to Order in the Years 1736 & 1737, made by Wm. Mayo, which does not show the "cole-mines;" this map was used with the report of the boundary commission which was sent to London in the case before the Privy Council. The boundary line decided upon was surveyed on the ground in 1746, just ten years after the original one. The results of this work were shown on A Map of the Northern Neck in Virginia, According to an Actual Survey begun in the Year MDCCXXXVI, and ended in the Year MDCCXLVI, Drawn by Peter Jefferson And Robert Brooke, Surveyors, which is now in the Colonial Office in London. This map shows the "cole-mines" in the same location as on Winslow's map, and taken from his record, of course, as that part of the survey was not retraced. Faulkner, who examined all of these records in his review of the case in 1832, refers to the notes of the original survey as "No. 10. The original field notes of the survey of the Potomac River, and the mouth of the Shenandoah to the head spring of said Poto¬mac River, by Mr. Benjamin Winslow." While the notes of the 1746 survey are in the London records and photographic copies of them are in several libraries in this county, the notes of the 1736 survey cannot be found anywhere. (For Chas. J. Faulkner's report, dated Nov. 6, 1832, see Kercheval's History of the Valley of Virginia, pp. 160-173. Jas. W. Foster's Maps of the First Survey of the Potomac River, 1736-37, in Wm. and Mary College Quarterly History Mag., April, 1938, gives a complete history

Jan 1, 1942

By C. Altstetter

THE work herein reported is restricted to the carbides which occur in quenched and tempered AISI 43XX steels with carbon contents up to 0.40 pct and silicon additions of up to 3 pct. In view of the instability and extremely small size of the carbides formed at low tempering temperatures, the technique for successfully preparing specimens for X-ray diffraction will be outlined. The alloys listed in Table I were obtained through the courtesy of the United States Steel Corp. in the form of 1/2-in. rounds forged from 100 lb. induction furnace heats (except for 4337 which was a commercial heat). The stock was normalized and then swaged and drawn to 15 mil wire with anneals at 1200F between passes. The wire was austenitized for 45 min in evacuated vycor capsules and quenched into iced brine with simultaneous smashing of the capsule. Tempering was done in air with a water quench after tempering. The carbides were extracted in a simple cell using a solution of 1M KC1 and 0.5 pct citric acid with an initial current density of 0.1 amp per sq cm. One end of a short length of wire was immersed in the solution, and the current at constant voltage was noted as a function of time. After about an hour the current dropped sharply because of the decrease in specimen cross-section. At this point it was found that the dissolution could be stopped and that the very fine wire which then resulted was just large enough to permit handling of the extracted precipitate still clinging to it, yet so small that it diffracted and absorbed only a negligible amount of the X-radiation. This rod of residue with a convenient handle of undissolved wire was rinsed in distilled water. alcohol, and acetone. Then it was dipped in a thin solution of cellulose-acetate cement and dried in vacuum. The resulting specimen was straight, uniform in density, easily handled, but most important, was completely sealed and never exposed to air. Furthermore, the residue had never been subjected to strong acids or rough handling such as in the extraction-replica technique or in the complete extraction to a powdered residue. It was found that improperly coated specimens were pyrophoric, turning to oxide with a dull red glow as they were exposed to air and yielding patterns of Fe2O3 and Fe3O4. The steels containing 3 pct Si were especially difficult to prepare for this reason. The specimens were put in a 57 mm Straumanis camera with double pinholes or slits and irradiated with filtered-chromium radiation. Readable patterns were obtained in less than an hour. A preliminary finding of some note was that for both tempered and as-quenched specimens of steels 4337 and 4337 (1.5 Si). M23C6 patterns were found along with the patterns of other constituents of the residues. This result was somewhat surprising in that previous investigators had reported that this carbide did not appear in a 0.38 pct C, 0.48 pct Mo steel1 or in chromium steels of less than about 10 pct Cr.2 Although the total amount of carbide-forming alloying elements is less than 2 pct, due to their mutual interaction and the action of the plastic deformation in promoting equilibrium, this carbide was able to form even in the steel containing 1.5 pct Si. M23C6 was not detected in the 4337 (3.0 Si) steel and the lower-carbon steels were not investigated in this condition. It is very likely then that the steels studied herein underwent a fourth stage of tempering during the anneals at 1200°F. This result has significance in that even a small amount of undissolved M23C6 in a low-carbon, low-alloy steel would exert a large effect on its hardenability. Its presence would also influence the mechanical properties by decreasing the carbon content of the matrix. Annealing in vacuum for 1 to 4 hr in the austenite field removed all traces of MZ3C+ The results on carbide precipitation during tempering, summarized in Table I, are in agreement with those of Klingler et al.3 for the higher carbon steels. For the AISI 4337 steels it is noteworthy that in the steels with added silicon the E carbide persists to longer times and higher temperatures and that silicon delays the formation of cementite. The results for the lowzr-carbon steels parallel those of the higher-carbon grade. The appearance of E carbide in the AISI 4315 is significant. There is considerable disagreem-nt in the literature as to whether this carbide forms in the tempering of steels containing less than about 0.2 pct C. Following the detection of E carbide in a 0.18 pct C plain-carbon steel,4 its occurrence in a steel containing chromium and molybdenum should be expected. The fact that the low-carbon steels have the same carbide-precipitation sequence as the high-carbon steels has bearing on the larger problem of the exact tempering reactions in all steels. Following the suggestion of Roberts et al.,' the first stage has been generally assumed to result in a metastable equilibrium of c carbide and martensite of about 0.25 pct C. From this it was concluded that a steel having less than 0.25 pct C should then be under-saturated with respect to c carbide and should not precipitate this carbide upon tempering. In view of the experimental findings of c carbide in steels hav-

Jan 1, 1962

By W.M. Peirce

The present work has been done in an endeavor to correlate and complete the data on the constitution of alloys of zinc with other common metals, dealing exclusively, however, with the zinc-rich alloys in which the zinc content is between 90 and 100 per cent. This investigation has included the systems lead-zinc, cadmium-zinc, iron-zinc, copper-zinc, aluminum-zinc, nickel-zinc, manganese-zinc, cobalt-zinc, tin-zinc, and magnesium-zinc. The important ternary system zinc-lead-cadmium and the zinc corners of other ternary systems have been investigated in connection with this work but will not be dealt with here. Zinc does not form a single homogenous zinc-rich solid solution over any considerable range of concentration with any of the metals mentioned. A limited range of solid solubility is said, by previous investigators, to occur in several cases and certain effects on the properties of zinc are attributed (with varying degrees of consistency among different writers) to the presence of certain other metals dissolved in zinc. The increasing use of rolled zinc and the possibilities offered by zinc as a casting alloy in certain fields have made it essential to determine precisely these equilibrium relationships. In carrying out this investigation reliance was placed chiefly on two methods, conductivity measurements and microscopic analysis. The first method proved valuable in determining the existence and extent of solid solubility. The second method stands alone as a means of determining structural characteristics and supplements the first method in the measurement of solid solubility. The scleroscopic hardness of all conductivity specimens was measured partly for its value from the point of view of mechanical properties and partly as a check on the conductivity curves in indicating the limits of solid solubility. No hardness curves are included in this paper, for in no case were they important in arriving at the constitution of any system. Conductivity measurements were in all cases made on cold-rolled strips 0.020 in. thick and 0.5 in. wide, both as cold rolled and after an

Jan 1, 1923

By W. M. Peirce

The present work has been done in an endeavor to correlate and complete the data on the constitution of alloys of zinc with other common metals, dealing exclusively, however, with the zinc-rich alloys in which the zinc content is between 90 and 100 per cent. This investigation has included the systems lead-zinc, cadmium-zinc, iron-zinc, copper-zinc, aluminum-zinc, nickel-zinc, manganese-zinc, cobalt-zinc, tin-zinc, and magnesium-zinc. The important ternary system zinc-lead-cadmium and the zinc corners of other ternary systems have been investigated in connection with this work but will not be dealt with here. Zinc does not form a single homogenous zinc-rich solid solution over any considerable range of concentration with any of the metals mentioned. A limited range of solid solubility is said, by previous investigators, to occur in several cases and certain effects on the properties of zinc are attributed (with varying degrees of consistency among different writers) to the presence of certain other metals dissolved in zinc. The increasing use of rolled zinc and the possibilities offered by zinc as a casting alloy in certain fields have made it essential to determine precisely these equilibrium relationships. In carrying out this investigation reliance was placed chiefly on two methods, conductivity measurements and microscopic analysis. The first method proved valuable in determining the existence and extent of solid solubility. The second method stands alone as a means of determining structural characteristics and supplements the first method in the measurement of solid solubility. The scleroscopic hardness of all conductivity specimens was measured partly for its value from the point of view of mechanical properties and partly as a check on the conductivity curves in indicating the limits of solid solubility. No hardness curves are included in this paper, for in no case were they important in arriving at the constitution of any system. Conductivity measurements were in all cases made on cold-rolled strips 0.020 in. thick and 0.5 in. wide, both as cold rolled and after an

Jan 1, 1923

ZAY JEFFRIES, who has been awarded the Douglas medal, established in 1922 by a group of the friends of the late James Douglas for distin-guished achievement in non-ferrous metallurgy, is one of the most notable graduates of the South Dakota School of Mines where he took his B. S. degree in 1910. The following year he was manager of the Ideal Mining Co., at Custer, and in 1911 he became instructor in metallurgy at the Case School of Applied Science, Cleve-land, where he remained until 1917, and in 1918 he took his D. Sc. degree at Harvard. During all this period he was engaged in experi-mental and consulting work for the Electric Railway Improvement Co., t h e Cleveland Steel Tool Co., the W. S. Tyler Co., the Lincoln Electric Co., the Aluminum Castings Co., and the Cleveland wire di-vision of the General Elec-tric Co. He is now en-gaged in general consulting work, especially for the Aluminum Co. of America, the General Electric Co., and the National Tube Co. He has contributed to the Transactions papers on the determination of grain size in metals (with A. H. Kline and E. B. Zimmer) LIV, 594; grain growth phenomena in metals, LVI, 571; the tungsten-molyb-denum equilibrium diagram and system of crystalliza-tion, LVI, 600; grain size inheritance in iron and carbon steel, LVIII, - 669; effect of temperature, de-formation and grain size on the mechanical properties of metals, LX, 474; metallography of tungsten, LX, 588; physical changes in iron and steel below the thermal critical range, LXIII, and LXVII, 56; and the trend in the science of metals, LXX, 303. In addition to participating freely in the discussion of other papers before the Institute he has found time to contribute notable papers to the Institute of Metals (Great Brit-ain), the principal technical journals, and to write a book on "The Science of Metals" in collaboration with R. S. Archer.

Jan 2, 1927

By William H. Kobbé

THE CHAIRMAN (M. L. REQUA, San Francisco, Cal.).-We have had in California a great deal of trouble from the breaking. off and collapsing of well casings from shifting sand, and it is quite true with us as indicated in the paper, that no casing has been found sufficiently strong to withstand that. I know of wells in which casing that has not been in the hole over 2 or 3 days has collapsed and when that casing has, been pulled out it has been just as flat as your hand. I am also familiar with swelling bed rock in the gold drift mining ground of California. It does swell and keeps on swelling and never seems to stop. Just as long as tunnels are kept open in that kind of material there has to be a gang going through the tunnel constantly cutting out and easing up. They have put in timbers 24 in. in diameter in an effort to hold that kind of ground and it has always filled. The only way to succeed is to keep a gang of men busy all the time cutting out and easing down as it squeezes in. C. NARAMORE, Washington, D. C.-My experience has been very similar to yours in, the same field in the matter of breaking off of casing. I had charge of one well, in which I put in reënforced casing, anchored it in place and got 1 day's production, 150 bbl., out of it. The following morning my lease foreman telephoned that it had broken off. I thought at that time we would have more evidence, so I drove out to the well without ordering a new shoe joint. It had been customary to merely start from town with a new shoe joint, pull the pipe, take off the crooked bottom joint, start the casing back and sometimes never touch any iron (lost casing)- when redrilling the well. Where the flattened joints went

Jan 4, 1917

By Vincent Gianella

Barite deposits are of widespread occurrence in Nevada but there are few pro-ducing properties; most of the latter are in northern Nevada. The production of the state is small at present-in the neighborhood of 15,000 tons annually-but is steadily increasing. The barite occurs in veins and also as replacement deposits in lime-stone. The bulk of the production has come from the replacement deposits. It is thought that the barite was deposited from rising hot waters similar to-and probably contemporaneous with-those responsible for some of the metallic ores of the state. This paper discusses only the deposits in northern Nevada. THE commercial mining of barite did not begin in Nevada until 1916 but although the production has been small there has been a rapid increase in tonnage during the past several years. Barite is widely distributed in the state and production comes from at least nine of the seventeen counties. Apparently this is not generally known, as only two counties are mentioned in a recent publications dealing with barite. The increase in output is due largely to recently discovered barite deposits in northern Nevada. The principal production has come from the northern portions of Lander and Eureka counties; smaller amounts from Elko County. The discussion in this paper is confined largely to the deposits in these counties. Most of the producing area is tributary to the Western Pacific and Southern Pacific Railroads, whose tracks lie along the Humboldt River. Barite is known from other northern counties but so far the production has been small. The output has come entirely from veins and replacement deposits, the latter largely in sedimentary rocks. In general, the barite from veins is white; that from the replacement deposits usually is dark gray to black, although some is light gray or white. Most of the veins contain sulphides and many barite-bearing veins have been worked for their content of base or precious metals.

Jan 1, 1940