By O. N. Carlson, K. E. Solie

The brittle-ductile transition temperatures of single and poly crystalline chromium metal were studied as a function of nitrogen concentration and chromium nitride distribution. It was observed that In recent years there has been an increasing interest in chromium-base alloys for high-temperature applications. The principal disadvantages, however, have been the difficulties of fabrication and the design problems associated with a material of such limited ductility. Various studies have been the effects noted in the poly crystalline material are essentially reversed in the single crystals. These observations are discussed in terms of existing theories for the brittleness of chromium. conducted recently directed toward a determination of the cause of this brittleness and to find ways for minimizing its effects. Allen et al.,' Wain Abrahamson and rant,' and weaver4 have carried out studies on the effects of interstitial impurities on the brittle-ductile transition of chromium metal of various degrees of purity. These investigations have shown that oxygen has little or no effect on the transition temperature of chromium in all conditions studied but that carbon increases the transition temperature under all conditions tested. Nitrogen was found to increase the transition temperature in the wrought condition and in the quenched or cast conditionS but reportedly has no effect in the furnace-cooled condition.

Jan 1, 1964

By V. V. Strishkov, Zane E. Murphy, George Markon

Soviet industrial expansion depends on coal as a source of power and raw materials for the USSR's metallurgical and chemical industries. Knowledge of the Soviet Union's coal resources and production outlook is essential for a critical evaluation of the Soviet industrial potential. Although there is considerable literature on the Soviet coal industry, no single source provides an authoritative study of how the coal industry functions and how well it per- formed its job. Soviet reports are singularly lacking in the precise data in terms that are comprehensible to a westerner. It is essential, therefore, to clarify the terms in Soviet parlance. These terms are not comparable to those in common use in the West and are the cause of most inaccurate results. Official Soviet data on labor productivity refer to a limited group of "production workers" while in the West all wage earners are counted. Statistics are based on unprepared or run-of-mine coal, whereas it is customary elsewhere to measure productivity in terms of marketable coal. Thus, many western publications, while diligently and accurately reporting published Soviet data, overstate the case, presenting an exaggerated picture of Soviet progress in coal production and technology. (In terms of Western criteria, there is a three-fold exaggeration of labor productivity.)

Jan 5, 1973

By C. H. Jr. Herty

IT Is well known that manganese will desulfurize molten iron through the formation of manganese sulfide, which, being only slightly soluble in the metal, rises to and enters the slag where it remains as such (mixer slag) or is converted partly or wholly to calcium sulfide (basic open¬hearth slag). The reaction by which manganese sulfide is formed is Mn + FeS = MnS + Fe. This reaction is generally considered to be reversible, although McCance1 states- that such is not the case. The experimental work was carried out to confirm the results of Rohl2 as to the reversibility of the reaction. Six trials are herein considered. In each 200 grams of electrolytic iron free from manganese and sulfur were melted in a pure zirconia crucible in a carbon resistance electric furnace. To the melted iron in runs 2, 3 and 4 metallic manganese and manganese sulfide were added to give 1, 2 and 4 per cent. manganese respectively, with 0.50 per cent. of sulfur in each. In runs 5, 6 and 7, metallic manganese andiron sulfide to give the same proportions of manganese and sulphur as in runs 2, 3 and 4, were added. The melts were held molten in the furnace for an hour and then cast into small ingots.

Jan 2, 1925

By Arthur L. Walker

In June, 1893, while I was with the Old Dominion Copper Co. at Globe, Ariz., I received an offer to take charge, as manager, of the Baltimore Electric? Refining Co. which had recently built a plant at Baltimore, Md., having a capacity of about 1200 tons of electrolytic copper per month, using the Hayden series system. This was a very large output, for in those days the plants were small and the art was in its infancy. At the beginning of 1893 there were 11 electrolytic refineries in the United States, most of them using the multiple system. The Hayden series system was used at Baltimore and Bridgeport and the Smith series system was in operation at the Electrolytic Copper Co. at Ansonia, COM., and at the Pennsylvania Salt Co. at Philadelphia. In the latter system the plates were placed in a horizontal position, but the operating difficulties were so numerous it was soon discarded. The total production of these 11 plants in 1892 was very small; I have not been able to discover reliable figures of production. There were about thirty electrolytic copper refineries in the world that year, according to Titus Ulke, and the entire production of these

Jan 1, 1932

By J. C. Coughlin, M. C. Flemings, T. Z. Kattamis

Experiments on Al-4.5 pct Cu alloy shou the dendrite arnz spacing increases with time during isothermal holding in the liquid-solid region. This coarsening of the dendrite structure is then shown to occur at roughly the same rate during solidification as during isothermal holding. Final dendrite arm spacing in both types of experiments depends primarily on coarsening kinetics. It is concluded that driving force for the coarsening is reduction of liquid-solid sur/ace area. Calculations based on two simple models show qualitative apreement with experinzent. 1 HERE has been considerable interest in recent years in determining effects of solidification variables on dendrite arm spacing in cast alloys. The interest has resulted primarily from the clear evidence that 1) the degree of homogeneity which can be obtained in a cast alloy with commercially practical homogeni- zation treatments depends on dendrite arm spacing, and 2) mechanical properties of the heat-treated casting depend on the homogeneity obtained.'-' In wrought alloys, microsegregation from the original ingot is carried to some extent into the final wrought product, and affects mechanical properties in similar fashion Experimental evidence available indicates that dendrite arm spacing in cast aluminum alloys is influenced only by cooling rate (or "local solidification timev*) and alloy content.Fig. 1, for example,

Jan 1, 1968

By H. Hansen, A. U. Seybolt, P. Yurcisin, B. W. Roberts

The Bi-Mn phase diagram in the region near BiMn was investigated, using principally thermal analysis and changes in magnetization with temperature. Of chief interest are the findings related to the magnetic transformation in Bi-Mn. THE Bi-Mn system is of both theoretical and practical interest because of the occurrence of the compound BiMn which exhibits unusual ferromagnetic properties. Because the Bi-Mn phase diagram reviewed by Hansen' (see Fig. 1) in 1936 is based on work done by BekierY in 1914 and by Siebe" in 1919, which left considerable doubt about the nature of the diagram. it appeared desirable as an aid in understanding the alloying characteristics and magnetic behavior to examine the pertinent regions of the phase diagram. The most interesting reaction is the peritectic at 445°C which forms BiMn by the reaction: Liquid + Mn(sulfield) ? BiMn(sol field) There is also a eutectic at 262° C between pure bismuth and BiMn. Hansen draws in BiMn dotted, since in 1936 evidence for its existence was uncertain. Experimental Materials—Preparation of Alloys Electrolytic manganese of about 99.97 pet purity and bismuth of 99.99 + pet purity were used as starting materials.

Jan 1, 1957

By J. M. Camp

In conforniity with the design of the oficials of the United States Steel Corporation for the standardization of the methods employed in the sampling and analysis of all materials encountered in their various lines of manufacture, the Chemists' Committee presents this compilatioti of standard methods for the sampling and subsequent analysis of molten pig-iron. In selecting the methods, the Committee employed the same line of procedure as in former cases, viz., the careful consideration of all the methods employed in each laboratory of the Corporation, evolving therefrom the several methods herein described, the immediate adoption of which is desired. The services of Messrs. W. B. N. Hawk, William Brady, and C. H. Rich, a sub-committee appointed for the preparation of the present paper, are gratefully acknowledged. II. Introduction. A quite obvious cause of nonconformity of results of comparative analyses in the various laboratories of the Corporation has been an apparent lack of uniformity of method in the sampling and analysis of molten iron. This condition is particularly apparent with regard to the determination of the sulphur, numerous discrepancies in which would appear t.o indicate the absence of, and the necessity for, some uniform method of procedure. The estimation of the

Jan 1, 1913

By M. H. Forester, John D. Cooner

ALTHOUGH the unmined anthracite will last for approximately 150 years, most of the thicker and cleaner coal beds have been almost entirely first-mined and pretty well robbed, leaving much of the present and future production to come from thin and dirtier beds. Herewith is a section of one of the dirty beds being mined in the Wyoming region [ ] This section shows that 45.8 per cent of the bed is made up of impurities and that the 45 in. of coal in the bed is in five benches, the thickest of which is 19 in. In some localities of the anthracite region there are 14 beds of minable coal. Orderly and proper mining of the coal makes it necessary to rob or second-mine--almost all beds have already been first-mined-in sequence from the top downward. Therefore the robbing of the few remaining portions of the thicker and cleaner beds is in many instances being held up by the mining of the overlying thin and dirtier coal beds. Impurities Impurities consist of fire clay, slate, rock, and bone. The latter, which is black, contains 40 to 60 per cent carbon and often resembles good coal. In some beds there are also bands of "blue" coal, which, as the name implies,

Jan 1, 1950

By John Burns

THE object of this chapter is to present data concerning the effect of the introduction of relatively slight amounts of carbon and nitrogen into supersaturated solution in iron. The study is confined to the alpha temperature range of both the Fe-C and Fe-N systems. The age-harden-ing characteristics of these two systems are considered. These data are compared to those of other age-hardening alloy systems and a "classifica-tion" is essayed. A.-RELATION OF LATTICE PARAMETER AND ELECTRICAL CONDUCTIVITY TO CHANGES IN PHYSICAL PROPERTIES DUE TO AGING OF FE-C ALLOYS Since Whiteley1 in 1927 showed that some of the iron carbide that is normally present in slowly cooled low carbon-iron alloys disappears on rapid cooling from just below the A1 point, interest has been manifested in the possibilities of age-hardening in these alloys. Masing and Koch,2 and at the same time and independently, W. Koster,3 proved these alloys to be age-hardenable. A. A. Bates4 a little later also published an interesting paper on changes in physical properties due to the aging of low-carbon steels. Many other papers have appeared showing changes in physical properties in specific instances due to this same phenomenon.

Jan 1, 1934

By C. H. Chou, Albert Sauveur

The following experiments were conducted in order to study the influence of the rate of cooling through and below solidification on the dendritic structure (macrostructure) and microstructure of some hypo-eutectoid steel. The steel selected was of commercial grade and had the following composition: C, 0.40 per cent.; Mn, 0.85; Si, 0.70; P, 0.099; S, 0.043. After melting in vacuum in an Arsem furnace, the various samples were allowed to solidify and to cool to room temperature as indicated in Fig. I. Samples were thus obtained representing all possible combinations of slow and fast cooling through the various ranges of temperatures indicated, namely: (I) zone of solidification or primary crystallization, (2) zone of granulation, and (3) zone of secondary crystallization. The location of the different temperature zones in the iron-carbon equilibrium diagram is shown in Fig. 2. The authors adopted Belaiew's notations. The designations of the various samples readily indicate their treatment, as will be apparent from Table 1. Sample SSS.—This sample was slowly solidified and cooled to room temperature in the crucible in which it was melted. The dendritic (macro) structure is shown in Fig. 3. The dendrites an: sharp and dis-

Jan 1, 1930

By G. H. Bishop

The kinetics of the inter granular penetration and embrittlement of [100] tilt boundaries in 99.998 pct pure nickel upon exposure to bismuth-rich Ni-Bi liquids have been determined in the temperature range from 700° to 900°C. The kinetics of penetration are parabolic in time at constant temperature over most of the temperature range. In a series of 43-deg bicrystals the rate of penetration is anisotropic with respect to the direction of penetration into the grain boundaries. In lower-angle bicrystals the penetration rate is isotropic. The rate of penetration decreases with tilt angle at 700°C. The activation energy for penetration in the 43-deg bicrystals is 42 kcal per g-atom independent of direction. It is concluded that the intergranular penetration and embrittlement in the presence of the liquid proceeds by a grain boundary diffusion process and not by the intrusion of a liquid film. This was confirmed by a determination that the kinetics of penetration and embrittlement were the same in the 43-deg bicrystals upon exposure to bismuth vapor under conditions such that no bulk liquid phase would be thermodynamically stable. WhEN solid metals are exposed to a corrosive liquid-metal environment, the grain boundaries are sites of preferential attack. Depending on the temperature, the composition of the liquid, and the composition, structure, and state of stress of the solid, a number of modes of attack are possible. This paper reports a study of the kinetics of intergranular penetration and embrittlement of high-purity nickel bicrystals upon exposure to bismuth which, together with an earlier study by Cheney, Hochgraf, and Spencer,&apos; demonstrates that there are at least two modes of intergranular attack possible in the Ni-Bi system. In the study by Cheney et al., columnar-grain specimens of 99.5 pct pure nickel were exposed to liquid bismuth presaturated with nickel in the temperature range 670" to 1050°C. They found that the majority of the boundaries, which were predominantely high-angle boundaries, were penetrated by capillary liquid films, the attack proceeding by a process which will be termed grain boundary wetting. This process occurs in a stress-free solid when twice the liquid-solid surface tension is less than the surface tension of the grain boundary,* i.e., when 2yLs < YGB In this case the penetration of the grain boundary by the liquid occurs at a relatively rapid rate, resulting in the severe embrittlement of a polycrystalline solid. Grain boundary wetting is a common mode of intergranular attack in systems in which the lower melting component is relatively insoluble in the solid, but the solid has an appreciable solubility in the liquid, for example, the Ni-Bi system, Fig. 1. In systems of this type at temperatures above the range of stability of any intermetallic phases, once the liquid is saturated with respect to the solid so that no gross solution occurs, chemical gradients are small, and surface tensions become major driving forces for attack, provided the solid is stress-free. The results of Cheney et al. appear to be typical of those encountered when grain boundary wetting occurs.&apos; Capillary films were observed in the boundaries after quenching from the exposure temperature. The mean depth of penetration increased linearly with time, and the activation energy for the process was found to be 22 kcal per g-atom. In a study of the Cu-Bi system Yukawa and sinott4 found that the depth of penetration of bismuth into high-purity copper bicrystals of orientations from 22 to 63 deg of tilt about (100) at 649°C ranged from 0.05 to 0.25 in. after a 12-hr anneal. This corresponds to a linear rate of 6 to 15 X 10~6 cm per sec. At the same reduced temperature of 0.68 the rate for the Ni-Bi system&apos; was 7 x lo-&apos; cm per sec. In another study of the Cu-Bi system, Scheil and schess15 determined the kinetics of grain boundary wetting in hot-worked commercial rod. While there were several complicating factors present in this study, there is general agreement with the above results. The kinetics of penetration were linear, the activation energy was 20 kcal per g-atom, and at 650°C the rate of wetting was 2 to 5 x 10-6 cm per sec. The rate of wetting in the A1-Ga system6 is somewhat

Jan 1, 1969

By T. G. Digges, C. L. Vold, M. R. Achter

A study was made of the effect of the growth conditions on the perfection of single crystals of niobium (columbium). Dislocation densities, determined by means of double-crystal diffractometer measurements , were not greatly affected by the method of crystal preparation but could be reduced by annealing treatments. However, the size, sharpness, and tilt angles of the substructures, observed with X-ray reflection macrograph, were sensitive to variations in growth procedures as well as to subsequent thermal treatments. Although the dislocation density was the same in both types, there were more low-angle bound-aries in crystals grown by zone melting than in those prepared by strain anneal. Mechanisms to account for these observations are discussed in terms of dislocation movements. A planned study of the structure-sensitive properties of refractory metals required the use of single crystals of a high degree of structural perfection and, for ease of handling, of large cross section. It appeared that the strain-anneal technique could satisfy both of these requirements. First, crystals grown in the solid state have been reported to be more perfect than those obtained from the melt.&apos; Second, the diameters of rods which may be produced by zone melting should have a theoretical limit determined by specific gravity, thermal conductivity, and surface tension, while the diameter of strain-annealed rods is limited only by practical considerations. Previously it was shown that niobium (columbium) single crystals of 1 in. diam2 may be grown by strain anneal, compared to the 0.5 in. maximum diameter achieved by zone melting, as reported for molybdenum by Belk.3 The current research was undertaken to investigate and optimize the effect of various process variables on the perfection of 1/4 and 1/2-in.-diam niobium single crystals grown by strain annealing and to compare their perfection to those grown by zone melting. Characterization of these crystals was more conveniently accomplished by means of X-ray than by metallo-graphic techniques. EXPERIMENTAL PROCEDURE Specimen Preparation. Zone-melted crystals of 1/4 in. diam were produced by the standard electron-beam zone-melting technique. The swaged and cleaned rods were outgassed, in the solid state at a temperature near its melting point, at a rate of 12 in. per hr, and single crystals were grown by making two molten passes at 2 in. per hr. By maintaining a zone length of 4 to % in., very uniform single crystals several inches long were obtained. For the strain-annealed crystals, an induction heater was used, in preference to other types of heating, to take advantage of the good penetration of large sections. A five-turn coil, 1 in. long, operating at 10 kc and powered by a motor generator, was contained in a vacuum chamber. The rod, suspended from the upper end, was raised through the coil for both recrystallization and crystal growth. In preliminary work single crystals of the same material were also grown with single and multiturn coils powered by a 450-kc generator. A vacuum of 2 X 10-6 Torr was maintained at temperatures up to 2400°C. Starting with electron-beam-melted ingots of 21/2 in. diam, the analysis for which is given in Table I, the material was cold-swaged to the desired cross section of 1/4 and 1/2 in. diam and then recrystallized. The rods were then strained in a tensile machine and converted to single crystals by passing through the induction coil. As with zone melting, control of orientation is possible by the use of special procedures. Other investigators, see for example Williamson and smallman,4 have reported that orientation control may be achieved by a bending technique. In the present work the strained rod is partially lowered through the coil to start the growth of the crystal. Then it is removed and bent at a point in the poly crystalline portion. Finally, it is returned to the chamber and growth is continued "around the corner". This procedure has certain limitations. If the bending operation exceeds the critical strain, recrystallization may take place. Also, the amount of bending which can be imparted to the rod is limited by coil geometry, and up to now has been 10 deg. However, by repeating the bending and growing operations it should be possible to attain any desired orientation. In preparation for X-ray examination, single crystals were sectioned and planed by means of the spark-erosion technique. To obtain the maximum reflected intensity, the (110) plane was exposed for examination. They were then etched 3 to 5 min in a mixture of con-

Jan 1, 1967

By Nathaniel Arbiter, Norman L. Weiss

Factors now accelerating the trend to larger concentrators and larger equipment units are reviewed. After almost 40 years of stability with unit sizes less than 100 cu ft, 200 and 300-cu-ft flotation-cell units are now operating and a 500-cu-ft machine is being built. The design of these cells is considered, as is the design and operation of flotation circuits against the background of the need to achieve greater process efficiency while holding down operating and investment costs. Particular attention is paid to the scale-up problem. With the newer cells having five to ten times higher unit capacities, the advantages resulting from this in sampling, mill operation nnd control, testing and plant layout are indicated, as well as the broad direction for changes in the overall design of 50,000 to 100,000-tpd concentrators. A comparison is given of the available larger cells of U.S. manufacture with analysis of differences and similarities. After almost 60 years of application in this country, froth flotation is still by far the most important process for concentrating metallic ores as well as a number of nonmetallic ores including fluorspar, phosphate rock, and potash. Its use on iron ores and coal is increasing. In the metals groups, the largest plants and the greatest progress are found in copper and molybdenum mills, and the section of this paper that deals with applications will be found most pertinent to that field. During its long reign, the flotation process has passed through several phases of evolution and has achieved progress in economy, efficiency. and simplicity of operation. Much of today&apos;s success in the flotation of low-grade ores can be attributed to that progress. Even more important to us than our ability to cope with today&apos;s conditions are tomorrow&apos;s problems, which we can contemplate with some prescience and confidence. Our annual production of copper, lead, zinc, and molybdenum—to mention only the most important metals occurring in the U.S. as sulfides- must be held at a high level in the face of a declining grade of ore. It is probable that the tonnage of such ores mined and processed will double in this country before the turn of the century. Not only will many of the existing flotation mills be enlarged again and again, but larger mills will be built here and abroad to meet our needs. At this moment, in fact, there are at least three proposed new foreign mills or expansions that envision 100,000-tpd milling rate on copper ores. Table 1&apos; shows the trend in copper ore grades in U.S. in recent years. Table 2&apos; shows the projected annual growth rate of consumption 1966-1985. A study by one of the authors 25 years ago showed that of 32 copper mills in North America with more than 100-tpd capacity, only eight had capacities exceeding 10,000 tpd. The average for these eight was 25,000 tpd. These included the three giants of that day, Magna, Arthur, and Morenci; the other five averaged a little over 10,000 tpd. Today instead of the eight mills with capacities exceeding 10,000-tpd capacity we have 25, and the mill with less than 1000-tpd capacity is fast becoming extinct. Much less range is found in lead and zinc mills, which are still generally small except for the few with over 1000-tpd capacity in Missouri, Utah, and Idaho, and a few zinc ore mills in the same size category. Molybdenum and potash operations are the fastest growers in North America today, but when one considers the projected increase in consumption of copper together with the projected decrease in grade of ore (3% annually), he can foresee that copper ore milling will soon lead the list. Technological improvements to meet the challenge of lower-grade ores have taken the wholly predictable path toward bigger equipment. In mining, shovels, draglines, scrapers, and trucks have led the way; in ore processing, we have seen a rapid increase in size of grinding mills, flotation cells, and pumps. Twenty-five years ago, for example, the 10-ft-diam ball mills treating 2000 tpd at Morenci were considered the giants, but today some grinding mills in similar service have five times that capacity. The specific matters to be dealt with in this paper are 1) the underlying principles that affect flotation-machine design, and the conditions required to produce

Jan 1, 1971

By C. W. Thompson

Paul D. Suloff (Goodyear Tire and Rubber Co., Inc., Akron, Ohio)—I would like first to comment on problems of the conveyor belt discussed in Mr. Thompson&apos;s excellent paper, since that is what we hope we know most about. Twists in relatively wide conveyor belt unavoidably produce a lateral maldistribution of tension, raising tension at belt edges and reducing it at the center. They also produce a lateral collapsing force on the belt at the center of the twist owing to the inherent tendency of all the longitudinal elements of the belt to try to pass through a point at the twist center. Calculation of the twist geometry by the methods shown in Mr. Thompson&apos;s paper keeps these extraordinary forces within limits which the belt designer can tolerate. No reduction in belt life due to twisting need be contemplated when this geometry is maintained. There is a minor exception that belts of extreme lateral flexibility will tend to curl laterally at the center of the twist. However, any ordinary fabric construction will perform satisfactorily in this respect. These twists are always made in regions of low tension in the conveyor so that even in the edges of the twist, belt tension does not exceed the average tension found in highly stressed regions of the conveyor. Offsetting these out-of-ordinary belt stresses is the advantage that Mr. Thompson has brought out of getting the return run up out of the dirt where it can be seen. This not only makes it easier to train, but also, in the event that it is not properly trained, frees it of the normal return run edge wear hazard. It is well known that return run edge wear is a prominent cause of belt mortality underground. An interesting aspect of this two-way conveyor is that the belt may be made what is known as a Mobius Strip. A Mobius Strip is obtained by splicing a belt after turning one end of it 180" about its longitudinal axis. In other words, one end is turned upside down before splicing. A belt spliced in this fashion turns itself upside down every time it comes around, but the twist which has been put in the splicing, of course, stays at one location on the conveyor, in this case one of the twist sections at the end. Turning the belt over every revolution might have advantages in some cases. Belts could be made with equal covers and the two sides worn equally and simultaneously. In this case there would be no problem of getting belts on upside down by mistake. However, the two-way conveyor does not have to be a Mobius Strip. It can be twisted in such fashion that the same side is up on both runs. It is simply a question of which way the final 90" twist is made before joining the ends. Another interesting aspect of the two-way conveyor is the problem of operating two-way conveyors in series. Here the sequencing of starting brings up some new problems. It will be recognized, although not always at first glance, that if the starting sequence is planned for one run of the conveyor the reverse will result on the other run. With the two runs carrying bulk material in both directions a reverse sequence on one run would be intolerable. In this situation the only solution appears to be a simultaneous starting of all conveyors in the series. However, with the coal in one direction and intermittent supplies in the other it would be entirely practical to sequence the conveyors for the coal run and accept a reverse sequence on the supply run. The two-way conveyor also lends itself to new driving possibilities. First, it is quite possible to drive at the head end of each run, which of course, means a drive at each end of the two-way conveyor. Driving in this way a given belt can be extended to substantially greater lengths than a conventional conveyor with drive at one end only. In addition to this, under certain conditions the conveyor can be extended to extreme length by driving at one end and at some intermediate point on the most heavily loaded run. As a particular case, a belt carrying coal downgrade and supplies back upgrade could be extended to extreme lengths by driving at the head of the coal run and at an intermediate point of the supply run. Mr. Thompson has been a pioneer in belt conveyor transportation underground and his accomplishment here with the first two-way conveyor of any consequence is another notable addition to the art.

Jan 1, 1954

By M. D. Arnold, H. J. Gonzalez, P. B. Crawford

A method is presented for estimating the effective directional permeability ratio and the direction of maximum and minimum permeabilities in anisotropic oil reservoirs. The method is based on the principle that production from a well in an anisotropic reservoir results in elliptical isopo-tentials about the well, rather than circular. Bottom-hole pressure data from three observation wells surrounding a producing well are required to apply the method. The method involves fitting field pressure data to a set of general charts of isopotentials and making a few simple calculations until a solution is found. The method is based on a steady-state equation for homogeneorrs fluid pow. In addition to the method, a brief discussion of the theory underlying it is presented. INTRODUCTION The existence of a different permeability in one direction than another in oil reservoirs has been mentioned in several papers. Hutchinson&apos; reported laboratory tests on 10 limestone cores and pointed out that one-half of them showed significant, preferential, directional permeability ratios, the average being about 16:1. Johnson and Hughesz reported a permeability trend in the Bradford field in the northeast-southwest direction with flow being 25 to 30 per cent greater in that direction. Barfield, Jordan and Moore -eported an effective permeability ratio of 144:1 in the Spraberry. Crawford and Landrum4 showed that sweep efficiencies could often vary by a factor of two to four, and sometimes considerably more, due to variations in flooding direction and patterns in anisotropic media. These findings indicate that the poss&apos;bility of anisotropy may be worthy of consideration in the development of an oil field. In considering this, it should first be determined if anisotropy exists. If it does, the direction of the maximum and minimum permeabilities and the ratio of their magnitudes are quantities which can be of value in planning the most efficient well-spacing patterns. Past methods of determining these quantities have included analysis of oriented cores and analysis of flooding performance of pilot injection patterns. In recent work, Elkins and Skov5 resented an analysis of the pressure behavior in the Spraberry which accounted for anisotropic permeability. This work was based on the transient pres- sure distribution in a porous and permeable medium, with the solution expressed as an exponential integral function involving rock and fluid properties. The purpose of this study is to provide a method, based on steady-state equations, of estimating the direction and relative magnitude of permeabilities in an oil reservoir from field pressure data and well locations only. The method presented is based on work by Muskat6 which shows that Laplace&apos;s equation represents the steady-state pressure distribution for homogeneous fluid flow in homogeneous, anisotropic media if the co-ordinates of the system are shrunk or expanded by replacing x with it is desirable that data be obtained early in the history of a field because knowledge of an anisotropic condition would allow new wells to be spaced in such a manner that reservoir development and subsequent secondary recovery programs could be planned more efficiently. THEORETICAL CONSIDERATIONS A brief discussion of the theoretical basis on which the graphical solution was developed is presented in this section. Muskat&apos;s two-dimensional6 olution for the pressure distribution in an homogeneous, anisotropic medium with an homogeneous fluid flowing can be algebraically manipulated to show that the isobaric lines are perfect ellipses. The ratio of the major axis to the minor axis, a/b, is related to the permeability ratio, k,/k,, as follows. alb = dk,/k,--...........(1) It can also be shown that the pressure varies linearly with the logarithm of the radial distance from the producing well. However, the gradient along any ray is a function of the orientation of that ray, and a ..xiable is present when anisotropy exists which cancels out for a radial (isotropic) system. For a system such as that described, a dimensionless pressure-drop ratio was developed which is completely independent of the actual magnitude of the pressures. This was done by arranging Muskat&apos;s solution in such a way that aIl variables cancelled out except k,/k, and well positions. However, this solution depends on having a co-ordinate system with axes coinciding with the major and minor axes of the elliptical isobars. Thus, it was necessary to introduce a co-ordinate system rotation factor. The two unknown variables are then k,/k. and 0, and the two measured dimensionless pressure-drop ratios are related to the unknown variables as follows.

By H. T. Green, R. M. Brick

True stress-strain data on alloys of pure iron with up to 2.4 pct Al were obtained in the temperature range +100° to —185°C. Alumi-num was found to reduce yield and flow stresses of iron at low temperatures but to have little or no effect on ductility. The effects of temperature and composition on strain hardening are discussed. SEVERAL independent studies of the behavior of high purity iron binary alloys at low temperatures are now in progress in attempts to evaluate systematically the variables affecting the low temperature brittleness of ferritic steels. This paper reports the results of one such investigation in which the tensile properties of aluminum and aluminum plus silicon ferrites were measured from 100" to —192°C. True stress-natural strain data have been obtained in order to evaluate as many as possible of the parameters which describe the behavior of the materials involved. In comparable studies at the National Physical Laboratory in England, iron and iron alloys of high purity have been produced&apos; and tested at subat-mospheric temperatures.&apos; True stress-natural strain curves were obtained there also. The purest iron contained 0.0025 pct C and 0.001 pct O and N. Even this, as normalized at 950°C following hot rolling, showed little ductility at -196°C. The grain size was ASTM No. 3, and the room-temperature yield strength was 17,800 psi (which seems too high for pure iron). Some of the NPL irons contained considerably more oxygen and demonstrated intergran-ular fracture at —196°C. The authors2 carefully differentiated between intergranular fractures associated with excessive oxygen content and transcrys-talline cleavage with little ductility encountered at —196°C in the purer material. The cleavage stress was half again as great as that associated with inter-granular fracture. Test Material, Preparation, and Procedures Of a number of Fe-A1 alloys produced, eight were considered to be sufficiently pure for testing. Partial chemical analyses (Table I), low observed yield points, and high ductilities indicate these alloys to be comparatively pure for vacuum-melted irons of sizable ingots, 5 Ib or more. To produce the binary Fe-A1 alloys, electrolytic iron was melted in air, cast into slabs, and rolled to strips 0.010 in. thick. These strips, joined into a continuous ribbon and wound into 2 1/2 in. diameter spools, were subjected for four weeks to a moving atmosphere of purified dry hydrogen in a stainless-steel tube at 1050" to 1150°C. Charges of these spools were melted in beryllia crucibles under good vacuums (1 micron), and aluminum (99.97 pct Al) was added to the melts. Compositions of these alloys are recorded in Table I. The ingots were hot forged and then cold rolled at least 65 pct to 3/8 in. rods which were vacuum annealed to the desired grain size, approximately ASTM No. 4, prior to machining into tensile test bars. All tensile specimens had gage sections 1 in. long, with a fillet of 1.5 in. radius to the shoulder. Gage diameters were 0.250 in, except for a few rods where additional cold work required use of a 0.200 in. gage section. After machining, 0.002 in. was removed from the gage diameter using 240, 400, and 600-grit metallo-graphic papers. The final polish with 600 grit left the fine scratches running in the longitudinal direction. By this means, surface metal strained during machining was removed. A few specimens heat treated after machining were similarly reduced 0.004 in. to remove any material affected chemically by the atmosphere during heat treatments, as is discussed in a later section. Tensile tests of the eight alloys at constant temperatures from +100° to —185°C were performed in apparatus which has been described." The essentials include a double-walled insulated metal vessel which contained the liquid heat-transfer medium surrounding the test specimen. A constant temperature was maintained by means of a pyrometer which regulated the pressure of dry air driving liquid air through a copper coil. Temperature variation was less than ±2°C during a specific test. For axial straining, two lengths of case-hardened chain, terminating in simple shackles, loaded the specimen through threaded grips. The lower grip bar passed through a hole in the bottom of the test vessel to which it was joined by a thin-walled

Jan 1, 1955

By R. E. Zinkham, R. J. Goodwin

A mathematical study has been made of the amount of support a cement sheath could provide to casing cemented into the earth. Several assumptions were required to make the analysis, but only two of them are limiting: (I) the pipe must be completely surrounded with cement, and (2) any mud filter cake between the cement and formation has the same physical properties as either the cement or formation. The calculations showed that little support would be provided to the pipe before an unsupported cement sheath failed in tension; however, when the cement is confined between the pipe and wellbore and is loaded in compression, the pipe could receive a considerable amount of support. In fact, the theoretical results indicate the lower grades and larger sizes of pipe could have their working pressures doubled when reasonable compressive loads were applied to a surrounding cement sheath. These data are shown in six charts. Other down-hole conditions such as setting the cement under pressure, increased temperature and cement confinement all tend to increase the potential usefulness of the sheath. Because of size limitations, a laboratory program to verify the most important results of this mathematical study would be very difficult. However, small-scale field tests would be practicable. This paper shows that, if a solid cement sheath can be obtained in the field by either primary cementing or by repair after detection of flaws by surveys such as the new cement-bond logs, the use of this approach to reducing pipe costs merits further consideration. INTRODUCTION A modification in casing design practices is proposed which may either reduce the amount and grade of steel required to contain a specified internal pressure or permit the working pressure to be increased for a specified weight and grade of pipe. One of the more important considerations in casing design is its resistance to collapse; however, Bowers&apos; and, more recently, O&apos;Brien and Goins&apos; have shown many casing programs are unnecessarily conservative in this respect, and they have indicated how savings can be made by designing for more realistic down-hole conditions. Earlier, Saye and Richardson howed that pipe costs could be reduced by considering the cement sheath as a part of the casing string when collapse resistance was being calculated. More recently, Rogers4 has raised the question as to whether a cement sheath might be considered in the design for burst resistance of the cemented casing. Calculations have been made for the increased burst resistance a cement sheath would provide for casing in a wellbore, and the results show that a sizable amount of support could be obtained in some instances. These data are presented in addition to a discussion of several other factors that are considered to affect the burst strength of pipe supported by cement. Two types of support are treated: Case I for tensile loading of the unconfined cement sheath, and Case for compressive loading of the confined cement sheath. ANALYTICAL TREATMENT AND RESULTS CASE I—TENSILE STRESSES IN AN UNCONFINED CEMENT SHEATH Conditions like this would most likely occur in a greatly enlarged portion of the hole where the cement was not in immediate contact with either the formation or a thin and hard mud cake. The mathematical analysis for this condition, as shown in the Appendix, rests on the following concepts. Pressure inside a unit length of pipe causes: (1) a tensile or tangential stress to be exerted over the longitudinal cross-sectional areas of the pipe and cement; and (2) an equal amount of strain in both the pipe and cement that is uniformly distributed over the wall thickness of each. This analysis was then used to make several calculations for a cement sheath around 51/2-in. OD pipe. The results are illustrated in Fig. 1, which shows that a tensile stress of 500 psi is imposed on a 5-in. thick sheath when the casing contains a pressure of only 1,450 psi. It also shows that a 10-in. thick sheath would be stressed to 500 psi in tension when the pipe contained a pressure of only 2,350 psi. Alternatively, if the stress analysis is made by means of the Lame thick-wall cylinder theory, the inner fibers of the 10-in. thick sheath will be stressed to 500 psi in tension when the pressure in the pipe is only 990 psi. This, of course, reveals that an unconfined sheath is of little support to the pipe in burst; however, an entirely different result is obtained when the cement is confined between the pipe and formation.

By C. L. Magee, H. W. Paxton

The effects of testing temperature, frorn 77" to 420" K, and volume fraction of martensite on the micro-plastic response of unaged Fe-31Ni martensite-austenite aggregates have been determined. The kinetics of the aging phenomena which lead to a decrease in the microplastic response were also characterized. These determinations, supplemented by other experimental results, show that at least two mechanisms of plastic deformation give rise to the apparent softness of the quenched structures. Only one of these mechanisms is fully discussed in this paper The transformation of retained austenite to martensite during the application of stress leads, in specified conditions, to large microplastic strains. This deformation behavior cannot be described by normal transformation plasticity theory but is shown to result from the fact that stress-assisted formation of martensite is a possible deformation mode. The present results and further considerations of previous work lead to the conclusion that it is unnecessary to postulate a special work-hardening mechanism to explain the mechanical properties of unaged martensite. It is now generally accepted that dislocation motion can occur in many solids at stresses very much below the L&apos;macroscpic" yield stress, e.g., 0.1 pct offset. This phenomenon has been investigated by a variety of techniques including measurements of elastic limit,&apos; effective static elastic modulus,~ and irreversible deformation following stressing at low levels.3"5 Of particular interest to the work to be described are exper -iments conducted on the deformation of martensite in attempts to decide whether freshly quenched ferrous martensites are "hard" or "soft".6 Muir, Averbach, and cohenl and McEvily, Ku, and ~ohnston&apos; have shown that as-quenched ferrous rnartensites can be plastically deformed at relatively low stresses. A difference between these two sets of experiments exists in that some diffusion of carbon would take place before testing in the experiments of Muir et a1. because the plain Fe-C alloys which they have tested transform to martensite well above room temperature. McEvily et a1. examined Fe-Ni-C alloys with Ms of about -30"~ and tested the alloys directly after quenching to — 195" ~ —a technique which obviates any appreciable carbon diffusion. Unfortunately, a characteristic of the alloys which transform below room temperature is that they do not transform entirely to martensite. The results discussed below will show that, because the transformation of this retained austenite under stress leads to plastic deformation, one cannot investigate the properties of martensite by such experiments. The existence of a second deformation phenomenon, which is not caused by retained austenite, is also established in the present work. In line with a previous suggestion,&apos; it is believed that the second microdefor-mation mode is principally due to the internal stresses generated by the formation of martensite. To avoid confusion in the present report, the evidence we have found for this interpretation will be discussed separately in a brief note.7 EXPERIMENTAL Materials. The alloys were induction-melted and cast under vacuum; the resulting compositions are given in Table I. The ingots were hot-swaged to 2-in.-diam bar and further cold-swaged and/or cold-rolled prior to specimen preparation. The standard tensile specimens were machined from sheet. The gage section was 0.05 by 0.2 by 5 in.; 0.75-in.-wide ends had 0.2 5-in. centered holes for pinloading. The three-point bend samples were 0.075-in. thick and 0.6 in. bide. The distance between the outer loading points was 5.5 in. In order to establish a standard starting condition, all specimens were quenched to 77°K prior to annealing in vacuo for austenitizing. The temperature of the austenitizing anneal was controlled to + 5"~. The testing and aging temperatures were maintained by various liquid baths (nitrogen, 77"~; freon, 130° to 200°K; acetone, 200 to 300°K; silicone oil, 300&apos; to 450°K) to better than il°K. Strain Measurement. The results herein were derived from both uniaxial tension and three-point bending experiments. For bending tests, the stresses and strains reported are those corresponding to the maximum fiber values. Normally, because of the small strains involved, very sensitive strain measurements are necessary to make microplastic measurements. However, because of the magnitude of the dilatation and shear involved in the martensitic transformation, the requirements in the present experiments proved to be less rigorous. In most experiments the plastic strain was evaluated by measuring stress relaxation and modulus defects. In this method, specimens are loaded rapidly to some predetermined load on an In-

Jan 1, 1969

By R. I. Garrod, R. A. Coyle

The shapes and positions of X-ray reflections from specimens of copper, steel, and aluminum alloy haue been examined in the elastic and plastic ranges both while the specimen was under stress and in the unloaded condition. For the aluminum alloy the shape was unaltered by the application of stress either within the elastic limit or in the plastic range provided that no additional plastic strain was induced. In copper the broadening accompanying plastic deformation was very slightly reduced when the specimen was unloaded. A similay but more marked elastic component of broadening was also found for steel, but in this case below the yield stress. Line profiles corrected for instrumental and particle-size broadening indicate very large internal stresses in local regions of the plastically deformed metals. The results are discussed in terms of a recent suggestion that the heterogeneous dislocation distribution between the cells and their boundary walls plays a major role in the peak shifts and broadening of the X-ray reflections. STUDIES of the X-ray line profiles from strained polycrystalline aggregates concentrate usually on one or the other of two main parameters: a) the displacement of the peak of the intensity contour from its position for a strain-free aggregate, or b) the shape of the profile. From peak shifts data can be obtained either on the relation in both the elastic and plastic ranges between applied external stress and average lattice strains in a given (hkl) direction, or, alternatively, on the residual lattice strains which are present after a plastically deformed specimen is unloaded.&apos; On the other hand, the shapes of the broadened profiles from cold-worked metals can be analyzed to separate the broadening produced by small particle size and by heterogeneous lattice strains.&apos; In this paper the terms "size broadening" and "strain broadening&apos;&apos; are used in the general sense adopted by warren.&apos; In the past, apart from two early qualitative observation, it has been customary to examine only the movements of the peaks of the profiles while the specimen is actually under load, since the line broadening induced by plastic strain remains after removal of the external stress. Consideration of the implications of existing data of this type suggests, however, that fruitful additional information on a number of fundamental aspects might be gained by careful examination of whether the X-ray line profile is in fact different in the loaded and unloaded states of the specimen. By taking advantage of the sensitivity and convenience of modern diffractometer techniques it is possible to explore with relative ease the magnitude and importance of any elastic effects which may be superimposed upon the well-known permanent changes in profile. The main aim of the work to be described was thus to investigate this point for typical metals and alloys. For this purpose annealed specimens were extended first elastically and then plastically and the positions and shapes of X-ray reflections were recorded. Initially it was anticipated that prime interest would center on observations within the plastic range; it has been found, however, that small changes in profile sometimes occur both before and after the nominal elastic limit of the material is reached. It is shown that the results obtained have important implications in relation to the structural changes and processes associated with deformation. I) EXPERIMENTAL To enable the diffraction lines to be recorded while the specimen was under uniaxial-tensile stress, a small hydraulic testing machine was designed and constructed for direct attachment to the goniometer of a Philips diffractometer. The specimens, which were machined from 1/2-in.-diam rod and had a central rectangular section 3/8 by 1/16 in. over a gage length of 1 in., were held in the machine by split collets mounted in grooves in the cylindrical ends of each specimen. No special precautions were taken to ensure precise axiality of loading. Constant oil pressure was maintained by a lever and weights system and transmitted to the loading rig by flexible pipe. The actual load on the specimen was measured by a load cell in the machine to an accuracy of * 1 pct. To enable smooth X-ray profiles to be obtained the specimen and machine were oscillated continuously during recording through *7-1/2 deg about the normal half-angle position of the goniometer. The three materials chosen for the investigations were high-purity copper as representative of a ductile fcc metal, a low-carbon steel for a bcc metal, and an aluminum alloy as a material in which the proof stress/ultimate strength ratio is high. Details are as follows. a) Copper. 99.999 pct purity. After machining the specimen surface was polished mechanically and

Jan 1, 1964

By A. K. Csazar, L. W. Holm

This paper describes our investigation of a post-water-flood, oil recovery process which consists of injecting a slug of propane followed by water. Also described are the results obtained by applying a modification of the process in which gas was injected ahead of the water. Under the conditions of the latter experiments, misci-bility was not achieved between the propane and gas. Preliminary experiments or) uniform, watered-out sandstone cores showed that an oil bank could be formed and produced by applying this recovery process. However, since reservoirs are not uniform in structure, the process also was applied to porous media containing irregular porosity and to stratified sand systems. As a supplenzerrt to the experinlental work, a mathernatical procedure was developed for calculating the performance of the recovery process in a bounded, layered, porous system with crossflow between layers. As a specific example, the method was applied to predict the perforrnance of the recovery process in a 6-ft long, two-layer, stratified, unconsolidated sand model for comparison with experinlental data. The calculations were programed for the ZBM 704 computer. The equations and calcula-tional procedure presented can be extended to systems containing any number of randomly distributed permeability variations or any number of parallel layers. INTRODUCTION The problem of recovering the oil that remains in a reservoir which has been waterflooded is receiving considerable attention now as an increasing number of water floods reach an economic limit. A large number of the waterflood projects are in shallow reservoirs which are at pressures below 1,000 psi. It has been demonstrated in the laboratory that post-waterflood oil can be recover-ered by miscible displacement, but the LPG-gas, miscible flood and the enriched gas drive cannot be applied effectively at pressures below 1,000 psi. Only a few reports have appeared in the literature2-4 on low pressure, partially miscible recovery methods. However, it is possible to use LPG in a partially miscible displacement process in a reservoir where pressures of 200 to 1,000 psi can be achieved. Under these Pressures and at normal reservoir temperatures, propane is miscible with the oil; but, of course, gas or water used to drive the propane slug would not be miscible with the propane. Because of the lack of complete miscibility, it has generally been concluded that excessive amounts of propane would be required to recover oil and that such a recovery method would not be economical; however, we have found that under conditions present in certain reservoirs, an imrniscible recovery process can be applied effectively. The oil saturation in reservoirs at the economic limit of waterflood projects is usually in the range of 20 to 35 per cent of the pore space." A certain portion of this oil is left trapped by water in various size pores of the rock, but a good part of this so-called "residual" oil can be present in the less permeable lenses or layers of the reservoir rock which were by-passed to some degree by the water. The oil in these permeability traps can be produced only if favorable pressure gradients are formed in the reservoirs between adjacent zones of high and low permeabilities. A low viscosity liquid, miscible with the oil in place, which is driven by water through a stratified or heterogeneous porous system can aid in the development of these favorable pressure gradients. The oil that is released thereby from the permeability traps can be recovered by the subsequent water flood. Studies were made to determine how much oil could be recovered from homogeneous and stratified cores and models, which had been water flooded, by injecting a slug of propane and driving it with water. The effect of injecting a slug of gas ahead of the water was also determined. Most of the work described herein was done with the propane-water combination; unless otherwise specified, no gas was injected. The principal objectives of the investigation were to determine (1) if an oil bank could be formed and (2) what ratio of oil recovered to propane injected would be obtained. A further objective was to develop a method for calculating fluid-flow performance in stratified systems which would account for fluid transfer between zones in hydrodynamic communication but of different permeabilities. THEORETICAL ANALYSIS In a theoretical study of the recovery process, analytical expressions were derived to calculate the pressure distribution, the fluid flux in longitudinal (parallel to layers) and transversal (across the layers) directions, and the fluid distribution at any point in the system. The equations were developed for a two-layer porous system in which it was assumed that the fluids in the system were incompressible and that capillary and gravity effects were