By J. B. Wagstaff

The raceway in front of the tuyere of the blast furnace has been studied quantitatively and a correlation obtained for the penetrastudiedtion of the blast. Some evidence is presented for the height and width of the raceway which suggests that all the raceways of a ffurnace overlap. The size of the coke in this zone has been measfurnaceoverlap.ured photographically during normal operation and results are given for the various areas. IN an earlier paper,' it was shown that a raceway exists opposite each tuyere of a blast furnace. This raceway is formed by the jet effect of the air emerging from the tuyere and consists essentially of a turbulence in which coke particles are recir-culated at high speed. Its presence was deduced originally from observations on movies taken with a high-speed camera through the tuyeres of various furnaces and was confirmed by experiments made on a model. In the model described,' this raceway was shown as operating in a vertical plane only, although there was a suggestion in the motion-picture film exhibited at that time that the raceway was three dimensional, unless artificially restricted. There was also some doubt then about the factors influencing its size. This paper describes the next steps in the investigation. Since the size of the raceway is obviously of importance in the operation of the furnace, it seemed worth while to study the subject more carefully. It is probably in this region that about half the coke in the furnace is consumed, so that the movement of the stock column may well be controlled by raceway behavior. Furthermore, there is some evidence to suggest that the coke is packed densely in the center of the furnace to form the "dead man" and more loosely above the raceway. It is therefore probable that the bulk of the gases passing up the stack flow from the top surface of this raceway. Clearly then, a knowledge of this critical zone is of interest to the blast furnace operator, and the first half of this report is devoted to a quantitative discussion of the subject. A further topic of interest among operators is the degree of breakdown of coke in the furnace, with which is inseparably linked the importance of a strong coke. Indeed, the whole question of the optimum size and type of coke may be as dependent on the condition of the coke in the bottom of the blast furnace as at the top. Attempts have been made from time to time to obtain samples of coke from the tuyeres and other furnace openings but they all suffer from the fact that the coke is filled to a varying degree with metal and slag and is probably broken up by the very act of taking the sample. It has proved difficult to make any reliable studies of coke size by these methods. However, it did seem possible to use the highspeed movies mentioned earlier1 to estimate the size of the coke. These movies provide an accurate record of individual coke particles so that, in theory at least, it should be possible to measure the size of the particles one by one and to obtain, for the first time, information on the coke being blown around the raceway under actual operating conditions while the furnace is performing normally. Such a study has been made and is discussed in the second half of this paper. The results obtained enabled the blast furnace data to be correlated with the model results given in the first half. Raceway Size In order to make a quantitative study of the size of the raceway it was necessary to devise some apparatus of laboratory scale, which could be handled quickly and easily. This focused attention on models, which in turn means that the laws of similarity governing this particular process must be ascertained. Method of Procedure: Since the work was to be carried out on a smaller scale than the blast furnace, the linear dimensions of the model became unimportant provided that the scale was known; it is only important to insure that the container does not affect the raceway being observed. The studies therefore were carried out in a glass-sided box, 11 in. high x 7 in. wide x 3 in. deep, using air jets ranging

Jan 1, 1954

By C. S. Smith

The solubility of tantalum at 1100°C is 0.025 pct in pure copper, 1.2 pct with 20 pct Ni, and 2.7 pct with -30 pct Ni. The solubility decreases with temperature, and the alloys are precipitation hardenable. A 79/20/1 Cu-Ni-Ta alloy reaches maximum hardness after aging at about 750°C and, if cold worked, does not recrystal-lize below that temperature. The alloys have good tensile properties at moderately elevated temperatures and, since they can be hot and cold worked nearly as easily as cupronickel, they are suggested for service at temperatures above the usual limits for copper alloys. MASSIVE tantalum dissolves extremely slowly in copper-rich alloys, and tantalum powder forms refractory surface layers which prevent its solution unless special precautions are taken. After many trials, an 80 pit recovery was consistently obtained by using a mixture of a finely divided tantalum powder with two or three times its volume of potassium tantalum fluoride (K2TaF1,-melting point about 750°C) poured in a slow stream directly on to the surface of the molten copper alloy, so that each particle would remain coated with flux and be immediately and individually wetted by the molten metal. A 50-50 nickel-tantalum alloy has a melting point of about 1400°C and small lumps of it slowly but satisfactorily dissolve in molten copper-nickel alloys as does commerical "ferro-tantalum." The high affinity of tantalum for carbon makes it necessary to avoid carbonaceous crucibles. COPPER-TANTALUM ALLOYS Castings with good shrinkage resulted when 0.1 pct Ta or more was added to copper melted under charcoal and cast in air. Copper in two-pound melts to which 0.1, 0.15, and 0.2 pct Ta had been added retained residual amounts, by analysis, of 0.025, 0.023 and 0.026 pct, respectively. The solubility of tantalum in molten copper at about 1200 °C is therefore about 0.025 pct. The electrical conductivity of these three samples was 100.48, 100.00 and 100.20 pct IACS in the annealed condition, and 98.24, 97.98 and 98.08 in the cold-drawn condition. Wires 0.080 in. in diam withstood from thirteen to nineteen reversed bends after annealing for 30 min in hydrogen at 850°C and the metal was therefore completely deoxidized. The annealing temperature corresponding to 50 pct loss of work hardness in 1 hr in a strip cold rolled 77 pct reduction was 175C, compared to 230°C for equivalent undeoxidized material. It is unusual for a decrease of recrystallization temperature to result from an alloying addition, and the tantalum probably combines with and removes some minor impurity in the original copper that restrained its recrystalliza- tion. No difficulty whatever was encountered in hot or cold rolling or drawing these ingots, and were tantalum not so expensive it would make an excellent deoxidizer for copper. COPPER-NIcKEL-TANTALUM ALLOYS Studies were made of the solubility of tantalum in a large number of copper-rich alloys, but of these significant solubilities were found only in the case of an iron alloy (which, however, separated into two immiscible liquid layers) and alloys of copper and nickel, in which tantalum is freely soluble and which were found to have interesting properties. The latter alloys are the subject of U. S. Patent No. 2,430,306 (1947). They are not at present available commercially. The Ternary Constitution Diagram—The copper-rich corner of the constitution diagram was constructed on the basis of microscopic examination of samples of various composition and treatments. The alloys were hot rolled to 0.25 in. from castings 0.625 in. thick, then annealed for 1 hr at 1000°C, quenched, cold rolled to 0.10 in. and finally annealed for various periods of time at temperatures between 800" and 1100°C in a nonoxidizing atmosphere and quenched. When the solid-solubility limit had been transgressed, particles of a compound believed to be Ni2Ta*were

Jan 1, 1960

By H. E. Swanson

A description of the field apparatus has been published by D. G. Brubaker. Data from laboratory model studies of the in-line and broadside methods of operation are detailed. The conductor models include a single sheet conductor at several strike and dip angles and a schistose-type conductor. In addition, data on the effects of the strike length and of the depth of the conductor are presented for the broadside method of operation. All of the data show that the inclintion reverses direction over the top edge of dipping single sheet conductors. Differences between anomalies over conductors dipping between 90" and 30" are subtle,but flat-lying sheets can be readily distinguished from steeply dipping sheets. Schistose conductors are easily distinguished from single sheet conductors, and a procedure is given for determing the direction of schistosity. The depth of penetration under ideal conditions is 0.7 of the coil separation. In 1950, The New Jersey Zinc Co. (of Pa.) developed a lightweight apparatus for electromagnetic prospecting. A description of this apparatus has been published by D. G. Brubaker.1 It consists of a small, battery-powered vertical source coil and a direction-finding receiving coil. Source and receiver are kept a fixed distance apart and move as a unit along the survey lines. At each receiver station the inclination of the magnetic field created by the source is measured. Two methods of operation are used, in each of which measurements are taken with a constant source-to-receiver distance and with the plane of the source oriented to pass through the receiver station. In one procedure, called the in-line method, source and receiver travel in tandem along the same line. In the other procedure, called the broadside method, source and receiver move along adjacent lines, with the source-to-receiver direction oriented parallel to the assumed strike direction. The data recorded in either case are the inclinations, measured in degrees from the horizontal, of the magnetic field created by the source. These data are plotted at the receiver stations on a map. Scale-model studies of both methods of operation have been conducted in the laboratory and are reported in this paper. APPARATUS Small source and receiving coils wound with many turns of fine copper wire were used to produce and measure an alternating magnetic field in the same manner as the field apparatus. The model source coil was mounted in a vertical position and oriented so that the receiving coil was in the plane of the source. The receiving coil was mounted in a frame so it could be rotated to obtain the inclination measurements. The source coil was excited by a 100-kc signal generator. A tuned amplifier and a voltmeter were used to detect the null position of the receiving coil. The coils used in the field apparatus are usually spaced about 400 ft. The coils used in the model work were spaced from 4 in. to 4 ft apart. Thus the scale of the model work ranges between 1/1200 to 1/100 natural size. The model conductors were aluminum-coated building paper supported on wooden frames. The conductivity-thickness product was measured using a four-electrode system and was found to be about 300 ohms-'. CONDUCTIVITY CONSIDERATIONS The electromagnetic response from a thin sheet conductor is a function of the product of the conductivity of the sheet times the thickness of the sheet times the frequency of the alternating electromagnetic field times some linear dimension of the system such as the coil separation which indicates scale. The secondary electromagnetic field produced by the conductor increases in amplitude from zero at zero conductivity to a maximum value for infinite conductivity, while the phase of the secondary field with respect to the primary field shifts from 90" at zero conductivity to 0" at infinite conductivity. Several authors2-' have shown that most of both the increase in amplitude and the change in phase of the secondary field takes place over a three-decade range of the conductivity-thickness-frequency product. Only small changes in the amplitude and

Jan 1, 1961

By Persifor Frazer

Comparative columns expressing the series of rocks of the lower half of the Mesozoic age in this country and in Europe are not yet definitely established. The following represents a co-ordination of the beds in England and Germany,* with a list of materials to be worked in from this country .†

By J. C. Bokros

At temperatures above 950°F, zirconium which has been strained a critical amount will experience critical recrystalli-zation. The large grain size thus formed can result in a reduction in the fatigue life by a factor of 2 to a factor of 9 at both high and low temperatures. The critical strains for zirconium vary from 15 pct at 900°F to about 2 pct at 1125°F, while those for zircaloy III vary from 15 pct at 1050°F to 5 pct at 1200°F. Zircaloy II ,experiences no critical recrystallization up to 1200°F. ZIRCONIUM has become increasingly important for nuclear applications and is being employed in reactors at temperatures where recrystallization can occur. Recent work' on the fatigue properties of zirconium has shown that coarse-grained structures developed in zirconium during recrystallization have much lower fatigue lives than fine-grained material. The development of these large grain sizes under such conditions is well known to be the result of critical recrystallization.2-4 Briefly, critical recrystallization occurs when a metal is strained a critical amount and annealed in the recrystallization range. The critical strain is defined as that minimum strain necessary to promote nucleation in the time unit and temperature considered. The maximum grain size occurs at the critical strain, since at this strain the fewest stable nuclei per unit volume grow into new grains. Recrystallization is not evident below this; strain since the nucleation rate is vanishingly lolw, and metal strained more than the critical amount has a higher nucleation rate per unit volume which results in a finer grained structure. This paper describes the critical recrystallization observed in reactor-grade zirconium, zircaloy 11, and zircaloy I11 as a function of annealing temperature and temperature of strain. EXPERIMENTAL The zirconium used was hafnium-free, double arc-melted sponge obtained from the Bureau of Mines. The ingots were forged and hot reduced to 0.08 to 0.10-in. sheet and subsequently cold reduced to 0.035-in. sheet with intermediate and final anneals at 1200 OF for 15 min. The zircaloy II and zircaloy III used were 0.035-in. sheets in the annealed condition. Compositions of these materials as tested are given in Table I. To determine the critical strain at a given temperature, tensile specimens having a0.065-in. taper in a 2-in. gage length were machined from the sheets parallel to the rolling direction. The specimens were polished, etched, and examined metallographically to ensure that all of them were strain-free, initially. Tukon indentations were made every half millimeter along the gage length of each specimen. These served as fiducial marks enabling the plastic strain to be measured with a microscope and micrometer stage. The specimens were pulled to failure at a rate of 0.002 in. per min in an Instron tensile-testing machine. Three temperatures were used for straining: room temperature, 500 ºF, and 900 ºF. The 500º and 900 ºF tests were run in an argon atmosphere. Since the rate of work hardening changes with temperature, a different critical strain was obtained for each temperature of strain. Specimens, prepared in the manner described, were annealed in vacuunl at various temperatures ranging from 900" to 1200 F for up to 1000 hr, after which they were examined metallographically. The critical strain and the recrystallized grain size as a function of strain were determined for each specimen. Results for the same temperature and time indicated that the critical strain measured was reproducible to within 5 pct of each other. RESULTS AND DISCUSSION Since increasing the time of anneal increases the probability of the nucleation of a new grain, the critical strain decreases with time at a decreasing

Jan 1, 1961

By D. L. Martin

THAT small amounts of impurities have a harm-J- ful effect on the malleability of metals and alloys is well-known. One common type of em-brittlement involves the formation of a small quantity of eutectic at the grain boundaries, and is typified by sulfur embrittlement of nickel. Another example of eutectic embrittlement—sulfur embrittlement of cobalt—is described in this report. In the preparation of specimens for a study of Co-Pt alloys, it was observed that the hot swagabil-ity of the alloys appeared to be influenced by the grade of cobalt used as melting stock. The cause of the hot-shortness was not traced to any particular impurity, although sulfur was suspected.' The damaging action of sulfur on the malleability of cobalt has not been generally recognized,'; in spite of the fact that the Co-S phase diagram8 eveals the same basic conditions—low solubility and eutectic formation—responsible for sulfur embrittlement of iron and nickel.7, 8 Apparently sulfur embrittlement has not been a serious problem in the fabrication of cobalt alloys. One related factor is likely the limited commercial experience with high cobalt alloys, since the predominant use of cobalt has been in alloys containing less than 75 pet Co. A series of Co-S alloys was prepared and studied to establish the effect of sulfur on the hot working characteristics of cobalt. Specimens, 5/8 in. diam by 4 in. long, were prepared by vacuum melting in magnesium oxide crucibles and casting in a copper mold. Two grades of low sulfur electrolytic cobalt were used as the basic material for the study, one from Johnson, Matthey and Co. and the other from the International Nickel Co. Each contained about 99.5 pet Co and had a nominal sulfur content under 0.005 pet. The sulfur was added initially as cobalt sulfide powder. Later, some low sulfur alloys were prepared by diluting the high sulfur alloys with cobalt. Trouble was experienced in controlling the sulfur content. Apparently much of the cobalt sulfide powder was lost during melting, as most of the samples contained a lower sulfur content than was added. The alloys were evaluated for hot brittleness by heating to 1000°C in a hydrogen furnace and swaging in air. The results of these tests are summarized in Table I. All the alloys containing less than 0.008 pet S were successfully hot swaged to 1/4 in. diam. The bars containing more than 0.015 pet S could not be swaged because of the formation of intercrystal-line cracks similar to those illustrated in Fig. 1. Examination of the microstructure of the cast bars revealed cobalt sulfide eutectic at the grain boundaries, Fig. 2. The sulfide was not always continuous at grain boundaries in bars that were hot embrittled but, in general, the particles did form a network that could account for the brittleness above the eutectic temperature, 880°C. There is no question about the brittle nature of a specimen exhibiting a continuous sulfide network such as is shown in Fig. 2b, though a sulfide distribution similar to that in Fig. 2a is marginal. This particular bar cracked when hot-swaged. However, other bars with lower sulfur content but with some sulfide phase at grain boundaries were successfully worked. The reduction of area of a hot tensile test specimen was also found to be a sensitive indicator of sulfur embrittlement. The variation of reduction of area with sulfur content is shown in Fig. 3 for specimens fractured at 900°C in an evacuated capsule. The ductility of cobalt is greatly reduced when the sulfur content exceeds 0.005 pet. Similar results were obtained for alloys tested at 800°C, below the eutectic temperature. The upper sulfur embrittlement limit of 0.015 pet, Table I, agrees with the observation of Kalmus8 hat

Jan 1, 1957

By Elton A. Youngberg

J. H. HEARDING, Jr.*—Extremely hard ferruginous chert (taconite) was encountered in driving a drift at the Fraser underground mine near Chisholm, Minn., on the Mesabi Iron Range. In order to get better results in drilling in this ground, it was decided to try tungsten carbide bits. In the beginning, 1½ in. tungsten carbide bits and 1 1/8 in. round-lugged alloy steel drill rods with "jack-stud" inserts were used. Considerable difficulty was encountered because the jack-stud became loose in the drill rods. Because there was not enough alloy steel drill rod on hand, we began to insert jack-studs in the ordinary high carbon drill rods and found, to our surprise, that there was less trouble with jack-studs working loose in these rods than there had been with the alloy steel rods. As a result, use of the alloy steel rods has been discontinued entirely. Under the heading "Drilling Procedures" the statement is made that all holes are started with detachable bits or conventional steel to prevent undue strain on the tungsten carbide bit inserts when collaring a hole on uneven ground. This practice was followed in our work originally for the same reason. It was soon found, however, that the holes could be started with the tungsten carbide without injuring the inserts if the drill operator was careful and did not give the drill too much air until the bit had a chance to seat itself in the rock. J. C. FRANZ*—In a discussion of other technical papers with reference to percussion drills and the use of carbide tungsten bits, it was my impression that the authors reported one of the first difficulties experienced with the use of standard, conventional percussion drills, was insert bit failures due to crushing of the bit inserts when the bits became dull. During the past few years, some of the rock drill manufacturers, I am told, have adopted an air drill for use with the carbide bits that have a lighter blow and faster rotation than the regular machine. This machine has been tested and the carbide bit failures have been considerably reduced. L. W. DUPUY†—The difficulties Mr. Youngberg mentions that were had with rod and coupling breakage call to mind similar troubles experienced at the Picacho mine in California near Yuma.6 The commercial couplings then available were found to be tempered almost to brittleness. Rod breakage was usually in the threads near the end of the rod. The highly-tempered couplings would break as soon as the rod broke. The solution was to thoroughly anneal the couplings and to put in only a very mild temper. Subsequently the alloy used in making the couplings was changed from the original by the manufacturer, but still only a very mild temper was used. The result was that the softer coupling would give but would not snap and release its hold on the broken rod thread. Fishing jobs were reduced to the few where the rods broke at the rod end of the thread. Thread breakage on the rods was further reduced by thorough annealing prior to tempering. The data Mr. Youngberg presents regarding the use of carbide inserts on long blasthole drilling is most interesting and it would appear that the use in this manner of percussion drills and carbide bits will have many applications. W. M. WOODWARD*—How many feet of hole, on the average, do you get from a tungsten carbide bit, and is there much variation from this average? E. A. YOUNGBERG (author's reply) —In recent months the 2 in. tungsten carbide bit footages in long hole drilling hake varied from 115 .to 140 ft monthly. The footages obtained from individual bits vary from several feet to over 300 ft, however the life of a majority of the bits will be within 25 ft of the average.

Jan 1, 1950

By David V. Ragone, James A. Craig, Richard E. Balzhiser

The Gibbs free energies of formation of UC2 and UC were measured by equilibrating two-phase mixtures of UC2 + C and UC, + UC with liquid bismuth. The measured equilibrium concentrations of uranium in the bismuth combined with available activity coefficient information yielded uranium activities in these two-phase regions. Measurements on UC2 were performed over the range 1015 to 1160 K and on UC over the range 1115° to 1165°K. The values obtained for UC2 are in excellent agveement with values determined using combustton calorimetry and low-temperature heat capacity measurements. The UC values are in fair agreement with the calorimetric values, differing by about 10 pct from the calorimetric determination. MUCH interest has been shown in the uranium carbides in recent years because of their potential as nuclear fuels. As nuclear reactor operating temperatures have been raised to increase thermal efficiency, new fuels have been required. The uranium carbides are of interest because of their high melting points, >2000°C, high thermal conductivity, and resistance to irradiation damage. The manufacture and use of uranium carbides are aided by a knowledge of their stability and reactivity under various conditions. In this regard the thermo-chemical properties of the carbides, i.e., heat capacity, heat of formation, free energy of formation, and so forth, are particularly important. A great amount of work has recently been done on the thermodynamics of the U-C system. Unfortunately, however, there has not been good agreement among the various investigations. This study of the free energies of formation of uranium monocarbide and uranium di-carbide in the temperature region 1100°-1200° K was undertaken to help clarify the situation. It should be noted that in the temperature range of this investigation, 1100°- 1200° K, the thermodynam-ically stable phase in equilibrium with graphite is U2C3, not UC2, Fig. 1. However, U2C3 is reported to be stable only under extremely low oxygen and nitrogen pressure. Although UC2 is metastable below 150O°C, it exists under most experimental conditions. It should also be noted that "UC," never exists as UC2 but with compositions near UC1.9. However, "UC2" will be used to designate the dicarbide phase except when the stoi-chiometry is necessary for clarity. METHOD The approach taken in this study of the free energies of formation of UC and UC2 was to determine the thermo- dynamic activities of uranium in the two-phase regions UC, + C and UC + UC, by equilibrating the two-phase mixtures with the liquid bismuth. When a mixture of solid UC2 + C is brought to equilibrium with liquid bismuth, the reaction that occurs is: Neither carbon nor UC, could be detected as dissolved material in the bismuth. The standard free energy for this reaction may be written: In the two-phase region UC, + C, Fig. 1, the thermo-dynamic activities of UC2 and carbon are unity. The activity of uranium in this region was determined by measuring the concentration of uranium in a liquid bismuth melt in equilibrium with the two-phase mixture. This concentration was then used in conjunction with the activity coefficient data of uranium in bismuth reported by Tien et al.' to determine the activity of uranium in the two-phase region, UC, + C. All of the quantities in Eq. [2] were then known, and the AG; (uc,) was evaluated. UC + UC2. For the studies involving UC + UC,, the reaction taking place when the two-phase mixture is brought to equilibrium with liquid bismuth is: The standard free-energy change for this reaction is given by:

Jan 1, 1969

By R. A. Morse, C. R. Holmgren

The production of oil by water flooding can be substantially increased by the maintenance of free gas saturation in the reservoir during the flooding operation. This effect is accomplished by the alteration of oil relative permeability characteristics and the occupation by gas of pore space that would otherwise be filled with residual oil. The amount of reduction In residual oil can be calculated from appropriate water-oil relative permeability characteristics. This paper presents experimental data in support of the foregoing conclusions and an example of the calculations. The microscopic pore saturation concepts of the mechanism are discussed. A method of practical application to field floods is presented together with discussion of certain limitations. INTRODUCTION The presence of free gas has been reported by a number of investigators to significantly affect the oil recovery which can be obtained from sandstone flow systems by water flooding.1,2,3,4,5 The effect of gas, noted in every instance, has been to cause lower residual oil saturations than could be obtained by water flooding the same systems in the absence of free gas. The degree of improvement in recovery has been observed to vary widely, depending on the systems used and the conditions of the tests. The increased oil recovery obtained because of the presence of gas during a water flood has been variously attributed to changes in physical characteristics of the oil, selective plugging action of the gas, inclusion of oil mist in the free gas phase, and the additional sweeping or driving action of the free gas. All but the first of these suggestions imply changes in the displacement mechanism. The change in viscosity and inter-facial tension of the oil phase, within the pressure range used for all the experimental work, is certainly not sufficient to account for the differences in residual oil saturation noted dess there is a drastic change in the displacement process. One other effect which logically seems capable of causing differences in residual oil saturation of the magnitude noted in the experimental work is that of simple replacement. In a water-wet system containing oil, water, and gas, it is to be expected that the gas will exist inside the oil. This is the position of minimum free surface energy, since the gas-oil interfacial tension will be less than the gas-water interfacial tension. There is no apparent reason to expect that the existence of free gas within the oil phase should alter the saturation at which the non-wetting phase (now oil and gas) should become discontinuous and hence trapped so as to be unrecoverable by direct displacement by water. If this is the situation, then trapping of a certain percentage of gas saturation during water flood should result, at infinite water-oil ratio, in a like reduction of oil saturation below that attainable by flooding in the absence of free gas. It is visualized that the gas will exist as bubbles inside the discontinuous residual oil as illustrated in Fig. 1, with the size of the oil bubbles being substantially unchanged due to the presence of the gas. As a practical matter, it can be anticipated that the presence of a free gas saturation inside the oil phase will reduce the relative permeability to oil which will exist at any particular water saturation. This reduction will be caused by two factors — -the addition of the gas-oil interface, and the reduction of area available for oil flow in the pores containing gas. This reduction in oil permeability at any particular water saturation will result in water breakthrough at a lower water satu-

Jan 1, 1951

By A. Rosen, P. Wynblatt, J. E. Dorn

The temperature, strain rate, and structure dependence of the flow stress in a poly crystalline Fe-2 pct Mn alloy was investigated between 77" and 370°K. It was possible to identify the low-temperature data from 77° to 160°K with Dorn and Rajnak's theory of the Peierls mechanism of plastic deformation. Above 160°K one or more thermally activated mechanisms must he operative; however, these were not identified in this investigation. The mechanistic basis for the rapid decrease in the flow stress of bcc metals with an increase in temperature over the low-temperature range is yet being debated. Various dislocation mechanisms have been suggested in the past but the agreement between the various proposed theories and the experimental results have not been definitive. In the present paper, the authors will demonstrate that the plastic behavior of polycrystalline iron containing 2 wt pct Mn plus interstitials agrees excellently with predictions based on the Peierls mechanism from 77" to 160°K whereas from 160" to about 370°K other as yet unidentified thermally activated mechanisms take over. Undoubtedly, the overlap of these mechanisms with the Peierls mechanism contributed to the difficulties of rationalizing the low-temperature behavior of iron and its alloys. I) EXPERIMENTAL TECHNIQUES AND RESULTS Although extensive data are now available on the effect of temperature and strain rate on the flow stress of various bcc metals and alloys, it was, nevertheless, deemed necessary for the objectives of the present study to obtain highly accurate data of the type most pertinent for checking the theories on a series of well-documented work-hardened states. Iron containing 2 wt pct Mn was used in this investigation in order to obtain a lower ductile to brittle transition temperature than that for iron.' The additional elements present were 0.004 pct C, 0.05 pct 0, 0.004 pct S, 0.003 pct P, 0.006 pct N, and 0.001 pct Si. The as-received 3/8 by 3/4 in. bars were cold-rolled to 0.100-in. thickness, recrystallized under argon for 30 min at 1073"~, further cold-rolled to 0.063-in. thickness, and finally recrystallized under argon for 30 min at 1000°K. This treatment gave a stable reproducible equiaxed grain structure having an average grain diameter of about 90 p. Prior to the final recrystallization treatment, the sheet was machined into tensile specimens 1/4 in. wide having a 1.625-in.-long gage section. All specimens were tested in controlled-temperature baths on an Instron Testing Machine. For convenience in the theoretical analyses the data will be given in terms of the shear stress for flow, 7, the shear strain rate, f, and the shear strain, y. A series of three standard strain-hardened states were obtained by prestraining specimens at 300°K and at a shear strain rate of 7.68 x lo-' per sec to three stress levels of 6.89 X l08, 10.3 X lo8, and 14.5 x 10' dynes per sq cm, respectively. Immediately following this prestrain the temperature bath was changed and each specimen was pulled in tension at either f = 7.68 X lo-' or f = 3.06 X 10"3 per sec. In terms of the accuracy that was achieved, the values obtained did not deviate more than *0.1 X 10' dynes per sq cm and * 1°K from the reported values of stress and temperature and not more than *5 pct in the reported values of the strain rate. The tensile stresses were converted to shear stresses using a factor of 1/2. The shear stress for the initiation of flow at the test temperature was determined by taking a y = 6.16 x 10'3 offset. from the modulus line at which point good accuracy could be achieved in determining y and the associated flow stress 7, with only a negligible increase in the pre-

Jan 1, 1965

By M. J. Pool, P. J. Spencer, R. V. Miner

The partial molar heat of solution of rhodiunz in liquid lin and Rh-Sn alloys has been measured as a function of rhodium concentration at 700" , 725" , 750" , and 775°K. The values at infinite dilution are very exo thermic, ranging from -29,950 to -28,260 cal per g-atom Rh at 700" and 775"K, respectively. At the solubility limit the heat of solution becomes sharply nzore exothermic and has permitted the liquidus boundary to be accurately established at each temperature. From the measurements in the two-phase region of liquid Plus RhSn, the heat of formation of RhSn,has been determined. A large increase in the heat of formation between 725" and 750°K suggests the possibility of a phase transformation in this compound. V ERY few measurements have been made of the heats of solution of transition metals in liquid tin; yet those values that are available are of great interest because of their very large exothermic nature. For example, the heat of solution at infinite dilution of palladium in tin has been measured as about -26,000 cal per g-atom (625" to 800°~),' while the heat of solution at infinite dilution of platinum is even more exothermic at -28,591 cal per g-atom (914°K).' These values are of the same order of magnitude as the heat of formation of many intermetallic compounds and as such clearly indicate that very strong bonding must exist between the solute and tin atoms in the liquid solutions. Rhodium might be expected to display similar solution characteristics in tin in view of its close electronic resemblance to palladium and platinum. Since no thermodynamic data are available for Rh-Sn alloys, rhodium was chosen as an appropriate solute for further investigation of transition-metal systems with highly exothermic heats of solution at infinite dilution. EXPERIMENTAL The heat of solution of rhodium in dilute Rh-Sn liquid solutions was measured as a functlon of rhodium concentration at 700°, 725", 750°, and 775°K. The liquid-metal solution calorimeter used in this work has been fully described elsewhere. At the start of each series of measurements, the solvent bath consisted of about 0.5 g-atoms of 99.9+ pct pure tin. To this was made a number of small rhodium additions, about 0.0005 g-atoms each, and the heat of solution was measured for each. Rhodium of 99.9+ pct purity in powder form was used in order to promote rapid dissolution in the liquid tin. The powder specimens were contained in tin foil stated to be purified (lead-free). This foil was found to have no measurable heat of solution in pure tin so the effect of any impurities could be neglected. The energy equivalent of the calorimeter was experi- mentally determined by dropping tungsten and/or tin specimens at intervals during each series of rhodium drops. The tungsten and tin used were 99.95 and 99.999+ pct pure, respectively. The only heat effect due to a tungsten drop, or a tin drop at low rhodium concentrations in the bath, is the sensible heat of the specimen. The heat content of these materials is well-established and is presented in the compilation of Hultgren et al. 4 As the rhodium concentration in the tin bath increases a small heat effect arises from the reaction: Sn (liquid, T) — & (soln, T) where T is the temperature of the tin bath. Where necessary, this heat of solution of tin was determined by Gibbs-Duhem integration, and corrections were made to the heat effect of the tin calibration specimens and the tin foil containing the rhodium specimens. RESULTS AND DISCUSSION The calculated values of the heat of solution of rhodium in dilute Rh-Sn alloys as a function of composition are shown graphically in Fig. 1. The values have been corrected for the sensible heat of the specimens, initially at 273"K, and apply to the reaction:

Jan 1, 1969

By E. T. Hayes, A. H. Roberson, M. H. Davies

ZIRCONIUM has been produced on a pilot-plant scale for only a few years, but the potential uses have led a large number of research establishments to engage in a thorough study of the metal and its alloys. The work described in this paper is part of a cooperative project between the Bureau of Mines and the Air Materiel Command. The Zr-Cr system was one of the first investigated because of the possibilities of improving the properties at elevated temperatures, the chemical corrosion resistance, and the mechanical properties of zirconium in a manner similar to the enhancement of the properties of titanium by additions of chromium. There is no published work on the Zr-Cr system but from the similarity of the metals involved it was expected that it would be similar to the Zr-Fe' and Ti-Cr' systems. The materials used in this investigation were prepared in the Bureau of Mines laboratory at Albany, Ore. Zirconium was produced by magnesium reduction of zirconium tetrachloride, and a typical analysis is as follows: Fe, 0.06 pct; Ox, 0.08; N?, 0.01; C, 0.02; and other impurities such as Al, Pb, Ni, Ti, and Si less than 0.01 pct each. High purity chromium was prepared by treating crushed electrolytic chromium in a stream of dried and purified hydrogen." The resulting powder contained about 0.01 pct 0 and about 0.1 pct total metallic impurities. All alloys were prepared by arc-melting 50 g briquetted compacts of the desired composition in a Kroll-type" arc furnace using an inert atmosphere. The furnace was evacuated twice and backfilled with helium, which was gettered by melting a center zirconium button immediately before the alloys were melted. Alloys were remelted at least once to insure greater uniformity of composition and subsequently were annealed in vacuum at 1250°C for 48 hr. Fairly homogeneous alloys were obtained by this means; a slight loss of chromium from the surface by evaporation during the high temperature homogenization was noted. All alloys were analyzed for chromium and gave results in good agreement with the nominal composition. Spot checks on tungsten and nitrogen showed pick-up of these elements to be negligible. Over 70 alloys were prepared for use in this investigation; only the critical ones are shown in Table I. Alloys containing up to 10 pct Cr were amenable to hot working at 850°C and a number of these were sheath rolled to 1/16 in. thickness. Specimens were cut from the sheet for use as metallographic samples. For the thermal analysis a differential couple was used in conjunction with an X-Y recorder, the temperature of the specimen and the difference in ternperature between it and the standard nickel body were recorded simultaneously. Heating and cooling rates of 5°C per min were used. The sensitivity of the instrument was such that a difference in temperature between the specimen and standard equivalent to 0.1 mv produced a deflection of 1 in. on the recording chart. The chromel-alumel thermocouples were checked against a Bureau of Standards calibrated thermocouple. Melting-point determinations were made in a high vacuum induction furnace using an optical pyrometer. The pyrometer, calibrated against nickel, copper, and zirconium (iodide process) under near black body conditions, was focused on the base of a hole drilled in cylindrical samples. A North American Philips Geiger counter X-ray spectrometer was used for all diffraction studies. This instrument, in addition to supplying precise intensity measurements of planar reflections, has an added advantage in that metallographic specimens mounted in bakelite can be used directly, and this

Jan 1, 1953

By R. A. Morse, C. R. Holmgren

The production of oil by water flooding can be substantially increased by the maintenance of free gas saturation in the reservoir during the flooding operation. This effect is accomplished by the alteration of oil relative permeability characteristics and the occupation by gas of pore space that would otherwise be filled with residual oil. The amount of reduction In residual oil can be calculated from appropriate water-oil relative permeability characteristics. This paper presents experimental data in support of the foregoing conclusions and an example of the calculations. The microscopic pore saturation concepts of the mechanism are discussed. A method of practical application to field floods is presented together with discussion of certain limitations. INTRODUCTION The presence of free gas has been reported by a number of investigators to significantly affect the oil recovery which can be obtained from sandstone flow systems by water flooding.1,2,3,4,5 The effect of gas, noted in every instance, has been to cause lower residual oil saturations than could be obtained by water flooding the same systems in the absence of free gas. The degree of improvement in recovery has been observed to vary widely, depending on the systems used and the conditions of the tests. The increased oil recovery obtained because of the presence of gas during a water flood has been variously attributed to changes in physical characteristics of the oil, selective plugging action of the gas, inclusion of oil mist in the free gas phase, and the additional sweeping or driving action of the free gas. All but the first of these suggestions imply changes in the displacement mechanism. The change in viscosity and inter-facial tension of the oil phase, within the pressure range used for all the experimental work, is certainly not sufficient to account for the differences in residual oil saturation noted dess there is a drastic change in the displacement process. One other effect which logically seems capable of causing differences in residual oil saturation of the magnitude noted in the experimental work is that of simple replacement. In a water-wet system containing oil, water, and gas, it is to be expected that the gas will exist inside the oil. This is the position of minimum free surface energy, since the gas-oil interfacial tension will be less than the gas-water interfacial tension. There is no apparent reason to expect that the existence of free gas within the oil phase should alter the saturation at which the non-wetting phase (now oil and gas) should become discontinuous and hence trapped so as to be unrecoverable by direct displacement by water. If this is the situation, then trapping of a certain percentage of gas saturation during water flood should result, at infinite water-oil ratio, in a like reduction of oil saturation below that attainable by flooding in the absence of free gas. It is visualized that the gas will exist as bubbles inside the discontinuous residual oil as illustrated in Fig. 1, with the size of the oil bubbles being substantially unchanged due to the presence of the gas. As a practical matter, it can be anticipated that the presence of a free gas saturation inside the oil phase will reduce the relative permeability to oil which will exist at any particular water saturation. This reduction will be caused by two factors — -the addition of the gas-oil interface, and the reduction of area available for oil flow in the pores containing gas. This reduction in oil permeability at any particular water saturation will result in water breakthrough at a lower water satu-

Jan 1, 1951

By Michel Elle, John Chipman

The equilibrium of gaseous H20-H2 mixtures with liquid iron-columbium alloys in the range 0.2 to 2.4 pct Cb shows that the activity coefficient of oxygen is strongly diminished by Cb. The oxide in equilibvium with the melt is identified as CbO2. The equi-librium constant at 1600 deg C is [%Cb][fo. % 0]2 = 2.9 x 10-4 where log fo= —0.14 [%Cb]. The deoxidizing power is comparable to that of vanadium, COLUMBIUM (niobium) is finding increasing use as an alloying element in steel. It forms several stable oxides and is removed from the steel bath by oxidizing slags. The specific oxide formed in steel-making is not known although Sazanov snd Shvarts-man,' in their study of its partition between slag and metal, have assumed this to be Cb2O5 It is the purpose of this study to determine its deoxidation equilibrium at 1600°c, the nature of the oxide formed and the interaction between columbium and oxygen in the melt. The investigation was based on the reaction H2 + O=H2O; Kl=ph2o/(pH2[%O]) [1] in which 0 signifies oxygen dissolved in the liquid Fe-Cb alloy. The method and equipment of recent studies2,3 were utilized. In brief, the molten alloy, contained in a small crucible, is held in a controlled mixture of steam, hydrogen, and argon until equilibrium is reached. It is then cooled quickly in a stream of helium and analyzed for columbium and oxygen, the latter by vacuum fusion.4 The solubility of the oxide in liquid iron is determined by visual observation of scum formation on the surface of the melt. Crucibles of MgO proved unsatisfactory because of partial reduction at the metal interface. Pure A12O3 crucibles were heavily blackened by the melt and could not be used at high concentrations of columbium. Silica crucibles were more satisfactory but these introduced some silicon into the melt thus necessitating an uncertain but small correction for its effect on the activities of the other solutes. In silica it was possible to observe the scum formation when the melt became saturated and there was no apparent reaction between scum and crucible. The procedure for saturated melts was as follows. The alloy charge composed of electrolytic iron and columbium grain was melted and held at constant temperature. The gas ratio H2O:H2 was progressively increased by raising the saturator temperature until a point was reached at which a bright film appeared on the surface and covered it completely. This film could be dissolved by raising the temperature of the melt and it reappeared when the temperature was lowered. Under a partial film covering, utilizing bare areas for temperature measurement, the melt was brought to equilibrium with the atmosphere by holding at temperature for about 1 hr as suggested by Dastur.5 INTERACTION IN THE MELT Several experiments were made without columbium to establish a base in silica crucibles. The results are shown in Table I. Except for one run, they agreed well with Floridis1 comparable results in other crucibles. The value of log K1 is taken from Table I as 0.58. This is slightly larger than Floridis' result, probably because of less elaborate safeguards against thermal diffusion. Results obtained in the Fe-Cb-0 series in which no scum formed are shown in Table 11. The equilibrium ratio Kl is defined as ph2o/(ph2[%O]). It is related to the equilibrium constant K1 as follows:

Jan 1, 1962

By J. Chipman, N. J. Grant, E. C. Roberts

An equilibrium study was made of the distribution of chromium and oxygen between liquid iron, containing less than 1 pct Cr, and simple slags of the CaO(MgO)-Si02-FeO-Cr& type in the temperature range 1526' to 1734OC. The effects of slag oxidation, temperature, and basicity were observed. IN spite of the fact that chromium is one of the most important alloying elements in steel, and exists in almost all steels as a significant residual element, little research has been done to determine its behavior in basic steelmaking processes. Considerably more work has been done under silica-saturated acid slag conditions. Korber and Oelsen,' Herasymenko,' and others have generally agreed that in acid steelmaking practice the chromium in the slag behaved as if it were present as the chrom-ous ion (CrO). Work by Hilty- ir, high chromium slags also indicated that chromium may exist as CrO. In basic slag systems no equilibrium data exist. Based on individual studies of basic open hearth and electric furnace practice, Bardenheuer," Rock-rohr,% nd HauckQ oncluded that: 1—chromium recovery increased with decreasing basicity, and 2— chromium recovery increased with increasing temperature, although the effect was small. In similar studies Yavioskii and Dzemyen' concluded that: 1— slag FeO is the most important variable, 2—the basicity of the slag has no effect on chromium recovery, and 3—slag viscosity is not high even when 20 pct Cr,O, is present. Lapitskii\ oncluded that chromium recovery improved as the basicity of the slag decreased and increased with increasing manganese in the metal. Regarding the effectiveness of CrZ08 as a base or acid in basic slags, both Kristofferseno and Trojer" reported that Cr,08 was an acidic component requiring neutralization as 2CaO-Cr,O,. Experimental Procedure The experimental apparatus and procedure used for the present research were similar in most details to those used by Winkler and Chipman" and were described in detail by them. A magnesia crucible was used, holding 60 to 80 lb of Armco iron which was decarburized with hydrogen to about 0.010 pct C. Since all the metal samples solidified without gas evolution, this carbon level was assumed not to be significant. Synthetic slags made by mixing pure oxides were used throughout the study. Temperatures were measured by means of calibrated W-Mo thermocouples and were checked by Pt-Pt-Rh thermocouples. The range of temperatures covered in this study was from 1526" to 1734°C. The chromium content of the iron was in the range 0.032 to 0.82 pct, although the bulk of the tests showed 0.04 to 0.2 pct. The slags were of the CaO(MgO)-SiO,-FeO-Cr,O, type in which the Cr,O, content was from about 2 to 20 pct, although most of the slags showed from about 2 to 10 pct. The FeO range was from about 10 to 65 pct. CaO and SiO, were in the range of about 5 to 45 pct each, yielding a rather wide range of basicity values. The first 12 heats were made without a sulphur addition, and with only 30 min allowed for slag-metal equilibrium to be reached. In previous research it had been shown that less than 30 min was adequate to achieve equilibrium in slags free of Cr2O8.11,14.15 A study of the present data indicated that some of the tests may not have reached equilibrium in this time; accordingly four additional heats were made in which at least 1 hr was permitted for equilibrium to be reached. For reaching

Jan 1, 1955

By R. S. Rickard, M. C. Fuerstenau

Anodic polarization curves for iron dissolution and cathodic polarization curves for copper deposition and ferric and hydrogen ion reduction were studied. These results were used to predict the relative rates of the reactions: The rates of the first two reactions were found to be first order with respect to the reacting ion, and the rale-controlling step was diffusion of the ions to the callzode surface. The rate of hydrogen ion reduction in an oxygen-free solution is dependent on the reciprocal of the square root of the hydrogen ion activity. In solutions containing oxygen, the rate of hydrogen reduction becomes dependent on the square root of the partial pressure of oxygen. At equal concentrations copper precipitation occurs about twice as fast as ferric ion reduction. In an air-saturated solution containing 0.01 M cupric ion at pH 2, the rate of hydrogen ion reduction zs about 10 times slower than that of copper precipitation. At pH values below 3, the rate of hydrogen reduction in oxygen-free solutions is very slozu. COPPER cementation has been utilized industrially for many years as a means of recovering copper from aqueous solutions. There are many different types of cementation plants, but all simply provide a means of contacting iron with relatively dilute copper solutions. In the past little or no attention has been paid to rates or mechanisms of the reactions involved. As a result, this and other studies'-3 have been undertaken recently to establish the important parameters in this system. The reactions involved in copper cementation by iron are: Since transfer of charge is involved in every case, these reactions should be considered from an electrochemical point of view. In any electrochemical system involving electrolytic conduction, passage of electrons necessitates ion transfer to the respective electrodes according to Faraday's law. The current in the system will be proportional to the rate of ion transfer, and, therefore, when the current in the galvanic cell is known, the rates of the reactions involved can be determined. Galvanostatic electrode measurements5" are applicable for these electrochemical studies, in that with this technique polarization curves (current density vs electrode potential) are established by impressing a constant current through an electrode and measuring the electrode potential. Once the current density, electrode potential, and reacting area are known for each reaction in this cementation system, the rates of the iron-consuming reactions can be determined. EXPERIMENTAL MATERIALS Several metal electrodes were used in this investigation; they are shown in Table I. Solutions were made with reagent-grade salts and conductivity water. Air, nitrogen, and oxygen were employed. All of these gases were saturated with water and degreased prior to use. EXPERIMENTAL PROCEDURE The experimental work was divided into two general areas. The first area involved galvanostatic measurements, which were used to determine the rates of reactions as a function of various parameters. The second area comprised actual cementation experiments to check the rates predicted from the electrode measurements. Galvanostatic Electrode Experiments. Polarization curves were obtained using a standard galvanostatic technique5'= with the apparatus shown in Fig. 1. The various electrode polarization experiments were run the same way except for changes in solution composition, polarity, and type of measured electrode. The general procedure involved the following steps: 1) a solution was made 0.5 M in sulfate ion and to the desired cation concentrations; this solution was placed in a constant-temperature bath and saturated with the desired gas; 2) the electrodes were cleaned and placed in the electrode holder; 3) the previously cleaned apparatus was assembled and immersed in a constant-temperature water bath (temperature controlled to ± 0.05"C); 4) the electrode was then positioned; the solutions were introduced, and the polarization meas-

Jan 1, 1969

By T. L. Joseph

A study is made of the amount of solution loss necessary to maintain the reducing power of the gas stream in the blast furnace. Curves are presented to show the effect of solution loss, moisture in the blast, and carbon dioxide from the flux on the nitrogen in the THE blast furnace process is based upon the counter flow of gases and solids. As CO, N, and H, flow upward from the combustion zones, oxygen is acquired from the descending charge. In the reduction of iron ore, a portion of CO is converted to CO, and similarly a portion of H, is converted to water vapor. The inert N,, from the air used in combustion, passes through the furnace with little change. Its concentration is, however, decreased by reactions such as direct reduction and solution loss which increase the volume of CO in the gas stream; Similarly the evolution of C02 from the limestone also dilutes the nitrogen. he purpose of this paper is to illustrate an idealized and simplified method of studying furnace processes by following changes in the gas phase between the tuyeres and the stock line. A more specific objective is to evaluate the effect of solution loss upon the CO/CO, ratio in that region of the furnace in which FeO is reduced to metallic iron. This last stage of reduction requires relatively high CO/CO, ratios to exceed the equilibrium requirements. Solution loss or the reaction of COZ with C to produce CO has a pronounced effect upon the ratio of the carbon gases and is necessary to maintain the reducing power of the gas stream if the consumption of coke is low. It will be explained later that indirect reduction followed by solution loss is stoichiometri-cally equivalent to direct reduction. Calculations will be made to show how the composition of the gas in the region of the mantle varies with coke consumption and with different amounts of solution loss. Such calculations show the condi- tions under which gasification of C with oxygen in the charge is needed to maintain the reducing power of the gas. Equilibrium conditions for FeO and the carbon gases will be used to establish a minimum CO/CO, ratio below which reduction will not proceed. The manner in which carbon is gasified in the furnace, at the tuyeres with oxygen in the air or above the tuyeres with oxygen from the charge, will be a basic feature of all calculations. It is hoped that greater interest in the use of top gas as a means of following furnace reactions will be aroused by the calculations and generalized curves which are presented. Bosh Gas Equations Subject to some alteration by the amount of moisture in the blast and by direct reduction, the gas leaving the combustion zones of a blast furnace has a definite composition. Because a relatively small amount of oxygen is acquired from the charge in the bosh and in the crucible, the products of combustion undergo little change until they enter the shaft. Bosh gas is, therefore, essentially the products of combustion of carbon in a deep fuel bed with air. The relative weights and volumes of reacting materials are expressed by the equation: 2~ + 0? + 3.76N, = 2C0 $ 3.76NZ [I] Air Bosh Gas -air = 79% N? = 3.76) 21% 02 Starting with a known mass of C consumed largely by air, Eq 1, but partly by water vapor, Eq 2, the volume and C + H2O = CO $ H? [21 composition of the bosh gas can be calculated and subsequent changes followed as reactions take place at various elevations in the furnace. As shown in

Jan 1, 1952

By S. J. Matas, R. F. Hehemann, R. H. Goodenow

The hot-stage metallographic method has been employed to determine radial growth rates of upper and lower bainite. Lower bainite appears to grow as individual plates that increase in both length and thickness while upper bainite grows as sheaves of closely spaced plates or needles. A discontinuity in the temperature dependence of the growth rate appears to be associated with the transition from upper to lower bainite and stepped quenching experiments suggest that lower bainite will not continue to grow when the temperature is raised to the upper range. Thus, a single process does not appear to control the growth of both upper and lower bainite. A tentative model based on the forces acting on a dislocation interface is proposed to account for the slow growth of bainite. It has been recognized since the early studies of Davenport and Bain that a close relationship exists between the martensite and bainite transformations in steels. However, diffusion of carbon during the transformation has lead to considerable controversy concerning the reaction mechanism.1-7 Many studies4,5,7-9 have emphasized the structura and kinetic aspects of the bainite reaction and, in particular, the difference observed between the two forms of bainite—frequently termed upper and lower bainite. A kinetic difference between the two types of bainite has been revealed in the activation energy determined from the overall reaction;4,5 however, many difficulties arise in an interpretation of these activation energies since a number of temperature dependent factors contribute to the kinetics of the overall reaction. The displacive surface relief10 accompanying the bainite reaction permits a separation of the nuclea-tion and growth contributions to the reaction and allows the kinetics of the growth process to be examined. Several investigations of this type have been conducted; however, they have been restricted to the low temperature range.3'6'11 Here, bainite plates are observed to grow slowly in both length and width. The present investigation extends such studies to include the upper bainite range. MATERIALS AND PROCEDURE Materials. The composition of the steels studied in this investigation are presented in Table I. The range of composition permitted a study of the effect of carbon content on the growth rate of upper bainite in the 9 pct Ni steels and consideration of both upper and lower bainite in the higher carbon steels. These steels were received as hot-rolled rounds and were forged to approximately 1/2 in. thick plates for preparation of metallographic specimens. In order to produce an essentially zero carbon steel, Steel A was decarburized in wet hydrogen at 1550°F for 15 days with the result tabulated as Steel AD. Experimental Procedure. In order to study the slow growth of the displacive transformation product, a commercially available Leitz hot stage was modified to permit heating of the specimen by its own resistance in a manner similar to that employed by other investigators.6 The furnace chamber was maintained at a pressure of 2 to 3 X 10-5 mm Hg prior to austenitizing at 2000° ± 12° F for 5 min. Samples could be cooled from the austenitizing to the transformation temperature in approximately 15 sec and the progress of transformation was recorded with a 9 cm by 12 cm single frame camera or a 16 mm movie camera. RESULTS AND DISCUSSION Growth Characteristics. The general growth characteristics observed in this investigation were analogous to those reported previously.3,6,11 Typical growth sequences for the high temperature and low temperature forms are illustrated in Figs. 1 to 5. In both temperature ranges, bainite plates increase in length at slow, temperature dependent rates until interrupted by a grain boundary, another plate, or

Jan 1, 1963

By T. F. Mueller, P. A. Witherspoon

For the case of an infinite radial system operating at constant terminal rate, the reservoir engineer often uses the "point source" solution of the diffiusivity equation to study pressure interference effects. At early times and at short distances from the inner boundary these solutions are invalid. The amount of error is often not precisely defined because of mathematical difficulties. Work presented here shows that, if dimensionless time is defined appropriately, previous solutions of the pressure equation can be displayed .as a family of curves on one chart. These solutions include the point source solution (referred to in the field of hydrology as the Theis solution) and other solutions obtained with digital computer methods. With these curves, an exact evaluation of the pressure drop within a reservoir or an aquifer can be made by the engineer. Examples of field problem solutions are presented. In most reservoirs the error involved when the Theis solution is employed is often negligible; whereas, in the calculation of interference effects in an aquifer, a substantial error can occur through such an approach. INTRODUCTION Flow equations are used in petroleum engineering to study the behavior of individual wells and reservoirs. In the case of wells, the pressure response at the wellbore face is the major point of interest; whereas, in the case of reservoirs, the pressure response at the interface of the aquifer boundary is sought. To aid in such studies, the flow equations have been solved in terms of the behavior at these two inner boundaries. Only limited work has been published in regard to the pressure conditions away from these points, i.e., within the reservoir or aquifer. Theis and Mortada are among the few who have reported on this problem. The Theis approach employs the exponential integral and is valid for pressure conditions that occur some distance away from the flow disturbance. It is derived from the concept of a point source, as opposed to a flow across some finite area. The Mortada results, on the other hand, are valid at all points within the reservoir or aquifer. They are presented in terms of dimension less ratios of the radius where the pressure is desired to the radius where the flow rate is measured. Their main use, in the past, has been in aquifer studies. The published results are presented in the form of graphs that are limited to a maximum radius ratio of 64. These graphical results are cumbersome to interpolate at non-integral radius ratios, so that one may be forced to utilize a rather involved analytical expression presented by Mortada. BASIC EQUATIONS The solutions of Mortada and Theis are both based on the diffusivity equation as applied to the case of an infinite radial system subject to a constant terminal rate. The equation is obtained by combining the material balance equation with Darcy's flow equation. The assumptions implicit in the use of this equation are as follows: (1) a single fluid is present that occupies the entire pore volume; (2) the reservoir is horizontal, homogeneous, uniform in thickness, and of infinite radial extent; (3) compressibility and viscosity of the fluid remain constant at all pressures; and (4) fluid density obeys the equation Using the diffusivity equation in situations where the above conditions do not hold will result in errors. These errors (not discussed here) but only the errors which arise in the solution of the equation itself. The diffusivity equation for the homogeneous reservoir conditions cited above can be written in cylindrical coordinates, as To obtain a dimensionless equation, so a single solution can be used for applications of different porosity, permeability and fluid properties, the following transformations are usually made: After these transformations are made, Eq. 3 .can be written in dimensionless form, as MORTADA SOLUTION One solution of Eq. 6 has been given by Mortada.

Jan 1, 1966

By W. A. Tiller

The unidirectional freezing of a semiinfinite liquid from one end has been treated by calculating the solute and temperature distributions in the liquid and solid phases with time, when the solid-liquid interface advances at a rate proportional to (time)lt2. The nucleation probability for new grain formation is calculated as a function of the constitutional and thermal properties of the alloy, the pouring conditions and the catalytic efficiency of the nucleating agents. The transition from columnar crystal formation to equiaxed crystal formation is assumed to occur at a critical nucleation frequency for a particular alloy and the quantitative dependence of the ratio (columnar zone length/equiaxed zone length) upon the freezing conditions has been predicted. The effects of (i) fluid flow in the liquid, (ii) heat transfer through a mold wall, and (iii) a finite ingot length, have been explicitly tveated as departures from ideality. These departures from ideality are found to have very important consequences on the ingot stmcture. In Part I&apos; of this series, a qualitative description of the general ingot structure was developed. The factors that determine i) the ratio of the equiaxed zone length to columnar zone length and ii) the grain sizes in these zones, were discussed. In the present paper, topic (i) will be treated quantitatively, and it is intended that topic (ii) will be treated quantitatively in Part 111. The complete treatment has been split in this manner for ease of development and coherency of presentation. The treatments are quite mathematical in nature and, although some of the conclusions to Part 11 depend upon the treatment presented in Part 111, it was felt that the intended audience would find the material more readable and more useful in its present form. To this same end, it seems worthwhile to reiterate some of the qualitative aspects of grain nucleation during ingot solidification before embarking on the mathematical description. QUALITATIVE ANALYSIS In the conventional method of casting, a liquid alloy with a certain degree of superheat is poured into a mold. The outer rim of liquid metal cools rapidly to the liquidus temperature of the alloy and begins to undercool. As the degree of undercooling increases, nuclei of solid begin to form in this chill layer, this nucleation being catalyzed by certain heterogeneous particles in the liquid. The grains in the chill layer which are generally of random orientation, begin to grow inwards because of heat conduction through the mold. The grains usually develop a columnar shape since the frequency of nucleation of new grains in the liquid ahead of the advancing interface is generally insufficient to seriously impede the growth of the original grains. Due to the slow diffusion rate of solute in the liquid, a solute distribution is formed in the liquid adjacent to the interface which is either an excess or a depletion if the partition coefficient, ko, of the solute is < 1 or > 1, respectively. Thus, the liquidus temperature of the liquid adjacent to the interface is a function of position. The actual temperature in the liquid is also a function of position and the temperature gradient at the interface decreases as the interface moves away from the mold wall. Since the rate of advance of the interface decreases with time, the equilibrium temperature distributions and the actual temperature distributions as a function of interface position, X, can be illustrated as in Fig. 1. Thus, a region of liquid may exist in which the actual temperature is below the liquidus temperature. This liquid is contitutionally supercooled and therefore unstable with respect to the nucleation of new grains. Now, since the supercooling in Fig. 1 increases as the interface moves further away from the mold wall, the nucleation rate of new grains will increase. When the nuclea-

Jan 1, 1962