By Carl E. Swartz

Although a number of articles appeared during the war advocating the use of cadmium in lead-tin solders, very little information of value can be found in the literature regarding the properties of solders containing cadmium. In most of the published articles the cadmium seems to have been considered merely as a partial substitute for tin in a tin-lead alloy rather than as an essential constituent of a ternary alloy. The primary object of the substitution of cadmium for tin was to lessen the amount of tin required, at a time when the latter was scarce and high-priced, and thus to produce a cheaper solder. While this object was accomplished, the new properties resulting from a change from a binary lead-tin alloy to a ternary lead-tin-cadmium alloy were not given proper consideration in many cases. For the past few years, the American Smelting & Refining Co. has been marketing a very considerable amount of cadmium in the form of lead-tin-cadmium alloys for use as solders for certain special purposes, and the successful use of these solders suggested that if more extensive knowledge were available concerning the properties of lead-tin-cadmium alloys of various compositions their field of usefulness might be materially extended. The investigation described in the present paper was undertaken to obtain this information and, by means of tests under conditions approaching those of practical use, to determine the suitability of cadmium solders for various purposes. Characteristics and Requirements of Solders in General General Physical Properties.—When cast into bars, solder should present a smooth and bright appearance free from oxide inclusions and bubbles. Ductility should be as great as possible without sacrificing tensile strength, and vice versa. Hardness and specific gravity are not of any great importance. Melting Characteristics.—The melting or solidification range is important. This statement applies both to the extent of the range and to the actual temperature at which complete solidification occurs. A rather narrow solidification range is desirable in soft solders in order that solidification may take place quickly. The solder should have high fluidity at temperatures only slightly above its melting range. For a

By W. B. McCarter

Broadly speaking, the year 1934, one of the most active in the history of the Coast, has been both disappointing and revealing. Of the 18 new oil-producing areas, only two have shown the qualities of a first class oil field. Many of the new areas are discouraging for the horizons exploited, because of close association of gas and salt water, and the absence of any appreciable oil zone. In spite of amply fulfilling the expectations of drilling and geophysical development, the year has fallen far short of the results that normally should be expected from such a campaign. In 1934, the Cockfield zone has been disappointing because its exploration down the dip from the Conroe and Tom Ball fields revealed only such distillate fields as Splendora, Eureka, and the great gas-sand thickness at Katy. The zone proved good at Raccoon Bend. Newer Oligocene and Frio fields in Texas, with the exception of Hastings, were also disappointing, as Van Vleck arid Old Ocean attest. The discovery at Dickinson is not startling. The development of Hastings, Tom Ball, Dickinson and the deep zone at Raccoon Bend will be slow. A new strip of prospective territory of minor importance lying inland from the Conroe trend was opened by the Kittrell discovery. During the year 206 unproductive wildcats were drilled on the Texas Coast, compared with 207 during 1933 and 141 during 1932. During 1934, there were 835 oil and gas wells and 229 dry holes drilled in proved fields, in contrast with 1100 in 1933 and 512 in 1932. The past year's production was actually 60,868,260 bbl., or 2,020,764 bbl. less than in 1933. The present annual rate of Texas Gulf Coast production is about 61 million barrels per year. The daily Texas Coast production decreased 5537 bbl., or 3.2 per cent, during the year. The total daily production at the end of the year was 173,598 bbl. Eighteen wildcats opened up new oil and gas pools during 1934, so that there are now 78 active pools and 3753 producing oil wells. The production of the average well is 45 bbl. per day. The price of crude oil was almost uniform in 1934,

Jan 1, 1935

By W. A. Wood, W. H. Reimann, Maria Ronay

The basic mechanism of fatigue is studied in annealed a brass subjectecl to alternating torsion at room temperature, 100°, 200°, 300°, and 400°C, and in air. It is shown that the slip-zone micro-cracking which characterizes fatigue damage produced by small amplitudes at room temperature is progressively replaced by grain boundary cracking at elevated temperatures, replacement being complete at 400°C. Replacement occurs not because slip activity decreases hut because slip movements at elevated temperatures cease to concentrate in narrow zones and instead disperse. Decrease of amplitude at 400°C through permitting longer lives of specimens before fracture actually causes in- MOST studies of fatigue at elevated temperature have been concerned with data for design. Observations on the basic mechanism of fatigue have been largely incidental, though they have led to the interesting inference that this mechanism has features in common with that of creep.' This paper is concerned primarily with the mechanism itself. Advantage has been taken of mater- crease in pain boundary damage, an anomaly attributed to the greater difficulty at elevated tempwature of starting and propagating a crack. Surface corrosion was most pronounced along slip bands but since at elevated temperatures the slip hands showed no cracking the surface corrosion did not appear to influence onset and early spread of fatigue damage. Similarly the type of fatigue damage produced at room temperature by cyclic strain at large amplitudes, characterized by irregular mi-crocracks at zones between disoriented regions in a grain, was also replaced by mainly grain boundary cracking at elevated temperature, though not so completely. ials and procedures known to show readily how fatigue affects the microstructure of a metal at room temperature, so that direct comparison might be made with what the same procedures show when the material is subjected to fatigue deformation at higher temperatures. 1) MATERIAL This was 70/30 a brass, used extensively in previous studies at room temperature.' Specimens were turned from extruded rod to have parallel test portions 1-1/4 in. long and 7/32 in. diameter, annealed to a grain size -1/10 mm, and electro-

Jan 1, 1965

By Frank Foote, Eric J. Jette

The unusual physical, electrical and magnetic properties of the iron-nickel alloys has given rise to a voluminous literature. This work will be reviewed critically in "The Alloys of Iron and Nickel," a monograph of the Alloys of Iron Research Series, soon to be published. In what follows we shall therefore confine ourselves to those of the earlier investigations that involved the use of X-ray crystal-structure methods. The earliest X-ray work on the iron-nickel system was by Miss Andrewsl. Using the powder method of X-ray analysis purely as a means of identifying the phases present, she located a region between 20 and 30 weight per cent nickel in which body-centered and face-centered phases coexisted. No lattice constants nor details of heat-treatment were reported. Bain2 also reported some qualitative observations. McKeehan3 made a systematic investigation over the whole of the system, giving many of his alloys four and some five different heat-treatments. In alloys furnace-cooled from 900' to 950' C. he found two coexisting phases between 0.15 and 30 per cent nickel. The precision of the lattice-constant measurements was low in comparison with what can be obtained today. Even for alloys of the same heat-treatment, differences in the constants were often between two and ten parts per thousand. In regions where no change of lattice constant with heat-treatment should occur, differences of the same order of magnitude were found. Since the maximum change in the lattice constant of nickel with change of composition is only about 2 per cent of the constant for pure nickel, these variations in the constants for a given alloy cause the points to "scatter" badly about any curve that may be drawn to represent them and it is difficult to interpret such results. In spite of this, McKeehan shows that the lattice constant of nickel increased as the iron content increased. His results for the alpha-iron phase are less conclusive. Osawa4 also investigated the entire system. For alloys slowly cooled from 1150' C. and then filed into samples for X-ray analysis, he found

Jan 1, 1936

By H. B. Pulsifer

The unprecedented high price of zinc ore prevailing through the early months of 1915 caused great activity in the Joplin district of Missouri. The Media mill is conspicuous as one of the first of the new "big mills" of the district. The mill was built over a mine previously worked but abandoned in 1912 because of the leanness of the ore and the large quantity of water encountered. The ore prices prevailing—$100 a ton in June, 1915, as against $50 in 1912-—favored the new undertaking. The mill was designed for good recovery so that it might operate in times of depression. In design and equipment, the mill is exclusively local in conception and construction. Former Exploitation The tract of land is a part of the large Guinn holdings; 70 acres are comprised in this particular lot, which is situated just a mile north of the center of Webb City on the Alba line of the Southwest Missouri Electric Railway. The ore lies 242 ft. below the surface at the top of the knoll which is surrounded by the well known properties: Black Cat, Ground Floor, Florence, Hurry-Up, Electrical, and Mercantile. Since the abandonment, in 1913, of the Yellow Dog a bit farther to the north, the Black Cat, Ground Floor, and Florence workings had been flooded. However, as there was no cut through from this side into the area it was proposed to exploit, it was thought that moderate pumping facilities would take care of the water. Three shafts had already been sunk to the ore horizon during the previous operations; the ground was connected by wide drifts and possibly 10 acres mined out, principally about the two southerly shafts which at surface are 8 and 13 ft. lower, respectively, than the collar of the shaft at which the new mill was built. The former mill on the lease was known as the Bohemian Girl. This mill, built in 1910, was removed after some 3 years' work. A head frame and hopper still existed at the middle shaft, sometimes known as the lower Hold Out shaft, but at the most northerly

Jan 1, 1918

By R. G. Knickerbocker, W. H. Yarroll, P. E. Churchward, J. W. Hunter, J. H. Jacobs

THE present paper records a chapter in the history of the development of an electrolytic manganese industry in the United States.1 A relatively large pilot plant at Boulder City, Nev., for the production of electrolytic manganese was conceived as part of the national defense program to make this country independent of foreign importation of manganese ore. The first authorization, in November 1940, however, was for a plant of only several hundred pounds capacity. Improvements in process and subsequent additions to some sections authorized by subsequent appropriations have enabled the plant to produce as much as 2000 lb. of manganese a day for substantial periods of time. Since in pilot-plant operation frequent changes are made in the flowsheet, the electrolytic manganese plant was constructed so that equipment could be rearranged with a minimum of expense and time. Several different kinds of the various types of equipment were installed for many of the operations, so that the one most suitable for the process might be chosen. Pilot-plant operations were begun in November 1941 and have been continuous except for brief shutdowns for installation of new equipment. More than one-half million pounds of manganese have been produced. The improvements in process, selection of equipment, and operational procedure developed are recorded here. DEVELOPMENT OF THE PROCESS The work of early investigators on the electrolysis of manganese solutions has been reviewed by Shelton.2 Until the method of continuous production of manganese by electrolysis was perfected by Shelton2-4 and coworkers, no practical procedure had been devised. The method as originally developed by the Bureau of Mines will be described here only briefly. The manganese dioxide ore was reduced in a rotating kiln-type furnace at 650°C. in an atmosphere of "city" gas. The calcine was leached with spent electrolyte and enough sulphuric acid to produce a neutral leach solution containing 25 grams manganese per liter as manganese sulphate and 200 grams per liter of ammonium sulphate. Arsenic was removed from the solution by the addition of 0.05 gram iron per liter as ferrous sulphate followed by oxidation

Jan 1, 1944

By R. B. Sosman, J. C. Hostetter

It is well known that ferric oxide, Fe2O3, is paramagnetic, while magnetite, Fe3o4, is classed among the highly ferromagnetic substances. But magnetic data on oxides intermediate in composition between Fe2o3 and Fe3O4 have been almost completely lacking. Fe2O3 and Fe3O4 form a solid-solution series, according to present evidence.' In this series the properties change continuously from Fe2O3 toward Fe3O4, as the percentage of FeO increases from zero toward 31.03, which is the percentage in magnetite. It is possible that there is a break in the series near Fe3O4, but it has not yet been possible to establish the existence of such a break experimentally. The occurrence of solid solution in this series is shown by the dissociation pressure, or oxygen pressure in equilibrium with the oxides, which falls continuously over the range from Fe2O3 to Fe3O4. The oxygen-pressure curves at 1100" and 1200" are shown in Fig. 1. The existence of solid solution is also demonstrated by the continuous change in optical properties from Fe2O3 over to a composition containing about 18 per cent. FeO, at which point the opacity of the oxide becomes so great that it is impossible to obtain measurements at higher percentages of ferrous iron. Natural oxides of iron intermediate in composition between Fe2O3 and Fe3O4 are much more common than is generally supposed. If a mineral oxide is not strongly attracted by a small hand magnet and if it gives a red streak, it is usually labeled "hematite." If it is strongly attracted by the hand magnet it is usually labeled "magnetite" without further tests. As we shall show later, oxides containing from 1 up to 31 per cent. FeO can be thus erroneously lumped together as "magnetite." It is a fact, nevertheless, that the great bulk of natural oxides of iron lie fairly near either Fe2O3 or Fe3O4 in composition. The reason will be

Jan 1, 1918

By I. C. White, G. H. Ashley, J. A. Bownocker

Among the rich mineral deposits of the great Appalachian field, the Pittsburgh coal bed stands pre-eminent. Other coal beds may cover a wider area, or extend with greater persistence, but none surpasses the Pittsburgh seam in economic importance and value. It was well named by Rogers, and his able assistants of the First Geological Survey of Pennsylvania, in honor of the city to whose industrial growth and supremacy it has contributed so much. Whether or not the prophetic eye of that able geologist ever comprehended fully the part which this coal bed was to play in the future history of the city that gave it a name we do not know; but certain it is that the 7 ft. of fossil fuel, which, in Rogers' time, circled in a long black band around the hills and, overlooking the site of Pittsburgh from an elevation of 400 ft. above the water of the Allegheny and Monongahela, extended up the latter stream in an unbroken sheet for a distance of 200 miles, has been the most potent factor in that wonderful modern growth that has made the Pittsburgh district the manufacturing center of America, and that bids fair to continue until it shall surpass every other district in the world, even if it does not now hold such primacy.' The Pittsburgh coal bed stands today as probably the largest contributor of wealth of any single mineral deposit in the world. If it is not, what other deposit is? It has contributed to Pennsylvania alone more than 2,500,000,000 tons of high-grade coal worth nearly $4,000,000,000; since 1910, it has added more than $2,500,000,000 to the value of Pennsylvania's mineral output. In 1920, this bed2 contributed 127,227,000 tons of coal as follows: Pennsylvania, Pittsburgh district........................ 38,245,000 Connellsville district................................. 34,095,000 Weatmoreland-Ligonier district........................ 16,107,000 88,447,000 West Virginia, Fairmont district........................ 15,571,000 West Virginia-Ohio, Panhandle No. 8 district............. 21,128,000 Maryland-Potomac (Est. one-third of production)......... 2,081,000 38,780,000 Total........................................... 127,227,000

Jan 1, 1927

The present paper records a chapter in the history of the development of an electrolytic manganese industry in the United States.l A relatively large pilot plant at Boulder City, Nev., for the production of electrolytic manganese was conceived as part of the national defense program to make this country independent of foreign importation of manganese ore. The first authorization, in November 1940, however, was for a plant of only several hundred pounds capacity. Improvements in process and subsequent additions to some sections authorized by subsequent appropriations have enabled the plant to produce as much as 2000 lb. of manganese a day for substantial periods of time. Since in pilot-plant operation frequent changes are made in the flowsheet, the electrolytic manganese plant was constructed so that equipment could be rearranged with a minimum of expense and time. Several different kinds of the various ¦ types of equipment were installed for many of the operations, so that the one most suitable for the process might be chosen. Pilot-plant operations were begun in November 1941 and have been continuous except for brief shutdowns for installation of new equipment. More than one-half million pounds of manganese have been produced. The improvements in process, selection of equipment, and operational procedure developed are recorded here. Development of the Process The work of early investigators on the electrolysis of manganese solutions has been reviewed by Shelton. Until the method of continuous production of manganese by electrolysis was perfected by SheltonZm4 and coworkers, no practical procedure had been devised. The method as originally developed by the Bureau of Mines will be described here only briefly. The manganese dioxide ore was reduced in a rotating kiln-type furnace at 650°C. in an atmosphere of "city" gas. The calcine was leached with spent electrolyte and enough sulphuric acid to produce a neutral leach solutioil containing 2 5 grams manganese per liter as manganese sulphate and zoo grams per liter of ammonium sulphate. Arsenic was removed from the solution by the addition of 0.0j gram iron per liter as ferrous sulphate followed by oxidation with manganese dioxide, and aeration, which precipitated the iron as ferric hydroxide. The solution, free from iron

Jan 1, 1944

By Donald F. Irwin

Amid the violent economic changes of recent years that have affected Canadian gold-mining operations so deeply, the discovery and early developments of Kirkland Lake might easily be overlooked. There was more than one "false dawn" for the district before developments finally established the fact of a superb mineralized zone extending through the present operating properties. Never far from the railway, Kirkland Lake has had the benefit of direct rail service for many years. The pioneer discovery on which the first mill and cyanide plant was erected was the "Tough-Oakes," this property being on what is now the eastern end of the producing area; some time later, the "Lake Shore" was discovered at the present center of the district, and a small plant was built upon it also. Both of these early treatment plants were of pre-war design. Progress in gold metallurgy has caused a gradual change in cyanide practice since the early days at Kirkland Lake, which may be observed in the various plants now operating there. From the beginning, it was recognized that Kirkland Lake ores were more responsive to cyanidation than to alternative recovery methods, and that their mineralization contained gold in very finely divided form. Although sulfides and tellurides are present, the quantity is small, being in the order of 1 or 2 per cent by weight, so that gravity concentration is undesirable, since gold is not confined to the sulfides. Some complication is offered by the presence of tellurides, which have caused lengthy controversy over their importance in recovery methods, but which are now generally regarded as less harmful in the light of increasingly high recoveries being obtained. Nevertheless, finely divided gold intimately associated with sulfides in the presence of tellurides; and occurring in the hard Kirkland Lake porphyry ore, substantially free from natural slime-forming constituents, indicates fine grinding. This has been the universal practice although the degree of grinding has varied a little among the different mills and is considerably finer now than formerly. The natural condition as outlined caused the establishment of fine grinding at an early stage in the development of Kirkland Lake, during the period of valuation of gold at, $20.67 per ounce. With the arrival

Jan 1, 1935

By J. P. Pritchard, J. T. Pierce, O. G. Slay

This paper discusses the results of a technology-evaluation program to ascertain the feasibility of a piotornask-photoresist technology developed for fabrication of multiple-layer thin-film superconductive circuitry. The uehicle selected for this evaluation was a 120-bil associative data processor requiring a set of nine photomasks to define a similar number of patterned material layers of lead, tin, and polymer insulation. A total circuit area of 4 sq in. involved 2500 actitle and 12,000 passive crossings. Several short-free, electrically continuous specimens were satisfactorily completed under this program. Problems encountered in the preparation and use of the requi-ed set of Photomasks are discussed, as also are the problets of providing suitable external connections. A major retarding factor in the development of the superconducting thin-film cryotron technology for many years was the absence of batch fabrication means yielding necessary device density and count per substrate for practical applications. Early workers in the field desired only limited numbers of devices to permit careful study of discrete devices and representative circuitry integrating logic and memory capabilities. For these purposes mask stencils could be formed to selectively control the placement of materials, sequentially vapor-deposited in vacuum, to form the multilayer structure. In general a distinct pattern was required for each material layer; therefore, mechanical provisions were required to change not only the material source, but the patterning mask as well, before each deposition. All deposition steps were preferably performed in a single evacuation of the deposition chamber. Thus the means for storing, transporting, and registering masks and sources with respect to the substrate existed and were operated within the vacuum environment. In the authors' experience, the approach was and remains serviceable for preliminary device study, but was not extensible to an economical manufacturing method by virtue of the difficulties inherent in mask stencil preparation and use, and the capital investment implicit in the mechanization requirements. Since the commercial attraction of the cryotron technology stems principally from its potential for economical batch fabrication, the authors' program has placed major emphasis on fabrication methods. A highly useful method has evolved through adaptation

Jan 1, 1967

By Walter Rosenhain

In selecting solid solutions for the subject of this lecture I have been guided by several considerations. The bodies known under that somewhat paradoxical name play a most important part in all types of alloys; consequently, a deeper knowledge of their constitution must 'be of fundamental importance to both metallurgical science and practice. Further, having been asked to deal with some of the more theoretical aspects of metallurgy, I have been tempted to describe certain considerations, which I believe to be novel, in regard to the nature of solid solutions. These considerations constitute a theory that requires much experimental confirmation, but they have passed the stage of speculations, for experimental evidence has become available and one inference after another, that can be derived from the theory, is found to be in accord with well-known facts. In putting before you these ideas and inferences, it must be understood that detailed quantitative proof of every step cannot be furnished. Our conclusions must therefore be stated with the reservation that their acceptance must depend on the manner in which the discovery of fresh facts may either confirm or confound them. If we wish to understand the structure of solid solutions we nust carefully realize the manner in which these bodies are formed in alloys. The formation of solid solutions is by no means confined to alloys, but it is desirable to confin5 attention, at the outset, to intermetallic solid solutions. It is not easy to formulate a precise definition of the term "solid solution." It may be said that a solid solution is a crystalline body formed from a liquid solution or from an intimate mixture of solids, or of liquid and solid, that retains in the solid state an admixture of the two substances (solvent and solute) as intimate as that which exists in a liquid solution. The term is undoubtedly paradoxical, for one usually associates solution with a liquid, but the difficulty cannot be evaded by using such a term as solidified solution, for this might refer to a solution that has set, or congealed, without undergoing crystallization. The German term mischkry stall avoids the difficulty and appears to

Jan 1, 1923

By John H. Bassarear, A. A. Dor

INTRODUCTION Primary grinding mills as defined in this paper, are autogenous or semi-autogenous rotating, tumbling mills having a coarse feed with a top size usually varying from 150 to 300 mm (6 to 12 inches). Most frequently, the feed to these mills is the product of primary crushing plants but in some cases run of mine ore is used as feed such as at Benguet, McDermitt, L-Bar Sohio, Bear Creek and others. The size of the largest lumps in the mill feed is principally determined by limits set by the mill feed trunnion diameter and by the type and size of conveying equipment used for handling and of bins and stockpiles used for storage. The use of primary mills in mineral processing plants has expanded very significantly in the last twenty years, and they have been successfully applied to the treatment of a wide variety of ores in both wet and dry grinding applications. In the present state of technological development for primary grinding mills, there is a wide choice of acceptable options with respect to type and size, grinding flowsheet and grinding media. The choice of the optimum combination which would result in the most satisfactory condition of operation, from the standpoint of both metallurgical results and costs, depends on the nature of the ore, the required characteristics of the grinding products and on various geographic and economic circumstances. The effects of such factors and considerations on the choice and sizing of primary grinding mills and flowsheets are reviewed and discussed in the following pages. PRIMARY MILLS SELECTION Inherent Characteristics of Primary Grinding Primary grinding is complex because it involves several comminution mechanisms which occur simultaneously and to some degree interfere with one another. These mechanisms of impact, attrition and abrasion have been described earlier. The relative importance of these three main grinding actions and their mutual balance resulting in a continuous uniform operation of the mill depend to a very large extent on the nature of the ore and its physical properties. Homogenous, single mineral ores will behave quite differently from heterogenous ores consisting of different minerals bound together along defined

Jan 1, 1982

By George Sachs, S. M. Clark, George Espey

he tendency of a commercially drawn cartridge case to crack in the mercury test and the relation of cracking tendency to residual stress retained after drawing were studied. The fourth drawpiece (next to the final) of caliber 0.30 cartridge cases produced by Frankford Arsenal were selected as test pieces. These exhibited an exceptionally high cracking tendency, making a detailed study possible. To obtain fast cracking in the mercury test, about 0.0015 to 0.003 in. must be removed from the wall thickness of the drawpiece by pickling, and it must be subjected to the mercury test immediately after washing. Removal of the adhering mercury by annealing and subsequent squeezing of the case in a vise was used to reveal definitely the presence or absence of cracks. Various lots of apparently identically fabricated cases were shown to possess a different cracking tendency. Machining off or boring a hole in the base gradually reduced and eventually eliminated the cracking tendency. On the contrary, shortening of the wall (body) reduced the cracking tendency only if the wall became so short that the cracking zone was directly affected. By boring out the base and pickling from the outside and then splitting the resulting rings, it was possible to determine the approximate stress distribution in the base and in the adjacent part of the wall. Small compression stresses were present in the core and the major part of the base, while the surface of the base and the adjacent wall contained high circumferential tensile stresses. On the contrary, the wall when parted from the base contained only insignificant residual stress. The conception is advanced, that the stress distribution in a drawn cartridge case corresponds fundamentally to that of a tube (wall) shrunk on a disk (base). Such a stress distribution results from the tendency of the base to recover elastically by an increase in diameter from the biaxial compression during drawing while the wall exhibits little tendency to change its diameter after progressing through the die. This is confirmed by measurements which show the base diameter to be slightly larger than the wall diameter.

Jan 1, 1945

By Walter Rosenhain

In selecting solid solutions for the subject of this lecture I have been guided by several considerations. The bodies known under that somewhat paradoxical name play a most important part in all types of alloys; consequently, a deeper knowledge of their constitution must 'be of fundamental importance to both metallurgical science and practice. Further, having been asked to deal with some of the more theoretical aspects of metallurgy, I have been tempted to describe certain considerations, which I believe to be novel, in regard to the nature of solid solutions. These considerations constitute a theory that requires much experimental confirmation, but they have passed the stage of speculations, for experimental evidence has become available and one inference after another, that can be derived from the theory, is found to be in accord with well-known facts. In putting before you these ideas and inferences, it must be understood that detailed quantitative proof of every step cannot be furnished. Our conclusions must therefore be stated with the reservation that their acceptance must depend on the manner in which the discovery of fresh facts may either confirm or confound them. If we wish to understand the structure of solid solutions we nust carefully realize the manner in which these bodies are formed in alloys. The formation of solid solutions is by no means confined to alloys, but it is desirable to confin5 attention, at the outset, to intermetallic solid solutions. It is not easy to formulate a precise definition of the term "solid solution." It may be said that a solid solution is a crystalline body formed from a liquid solution or from an intimate mixture of solids, or of liquid and solid, that retains in the solid state an admixture of the two substances (solvent and solute) as intimate as that which exists in a liquid solution. The term is undoubtedly paradoxical, for one usually associates solution with a liquid, but the difficulty cannot be evaded by using such a term as solidified solution, for this might refer to a solution that has set, or congealed, without undergoing crystallization. The German term mischkry stall avoids the difficulty and appears to

Jan 1, 1923

By Heihachi Kamura

In this research, the proper temperature for the reduction of iron ores by carbon monoxide was determined. Also, the difference of the rate of reduction on the sizes of ore under four mesh per linear inch was estimated, but no evidence could be found. Rates of reduction on the seven kinds of ore were compared with the results of the experiment, showing a close relation between reducibility and density of ore. Finally, the maximum size of ore that can be reduced in applicable length of time was determined. The author thinks that the process of production of steel may be replaced by low-temperature reduction of iron ores some time in the future. THE reduction of iron oxide, such as Fe203, to iron in the blast furnace is performed principally by carbon monoxide, but partly by solid carbon by the two following reactions: Fe203 + 3CO = 2Fe + 3CO2 2Fe203 + 3C = 4Fe + 3CO2 It is known that reduction by carbon monoxide takes place at a much lower temperature than reduction by carbon and that the reducing action of carbon monoxide progresses to the inside of the ore in lump form by gaseous diffusion. In the reduction by carbon, however, the reducing action takes place only at the contact surface of the ore and carbon, so that the more complete the reduction by carbon monoxide, the more efficient is the operation. However, the reduction does not progress as shown in the foregoing formula, because carbon dioxide acts oxidizingly on the metallic iron to such a degree that when the gaseous composition reaches a certain proportion of carbon dioxide to carbon monoxide, the reduction practically stops, even though the gases are moving slowly through the heated ore. The proportions of carbon monoxide and carbon dioxide in the gas depend on the kind of iron oxide and the temperature of reduction, also the duration of time in the reaction. The longer the time of the reaction, the higher the proportion of carbon dioxide obtained in the gas, but finally it will attain to a condition of equilibrium.

Jan 1, 1925

By William E. Harris

Time and experience have demonstrated that by means of the Waelz process zinc, lead, cadmium, arsenic, antimony, bismuth and tin can be volatilized satisfactorily. In this way difficult gold ores are being treated to allow for the recovery of the precious metal. Iron ore containing zinc is being treated to remove the zinc and recover the iron. In Germany, thallium is being recovered in commercial quantities from the zinc oxide fume; indium, germanium and gallium are also concentrated to a degree warranting recovery, even though these rare metals are only recognizable in the ore by means of the spectroscope. The physical, chemical or mineralogical condition of the raw material affects very little the applicability of the process. The name Waelz is derived from the German word Waelzen, meaning a "trundling motion," which very aptly describes the movement of the charge through the slowly rotating kiln. The recovery of zinc and lead by volatilization in a rotary kiln has its origin in a process patented in 1910 by Edward Dedolph, of British Columbia. The Dedolph patent was taken over by the Metallgesell-schaft of Frankfurt-on-Main, Germany, which in cooperation with the Griesheim-Elektron, now a part of a large industrial combine, introduced certain improvements (Ohlmer, Specketer patents), but without bringing the process to a state suitable for large-scale operations. The war temporarily stopped all work on the process, and it was not until after the war that the Krupp Grusonwerk, of Magdeburg-Buckau, Germany, quite independently of the Metallgesellschaft, instituted research work in this field of metallurgy, which in 1923 led to the Waelz process proper. The Krupp Grusonwerk and the Metallgesellschaft A.G. later on collaborated, and by their joint efforts further developed and perfected the Waelz process, which they are marketing together as "Waelz-Gemeinschaft." The process is capable of treating a varied type of material; for instance, oxidized and sulphide zinc ores, calamine (zinc carbonate ore) waste dumps, jig tailings, jig slimes, table concentrate slimes, brass ashes, zinc-bearing iron ores (where the iron sinter is the real objective and the zinc oxide a by-product), electrolytic-zinc leach residues, zinc muffle residues and works sweepings, lead-furnace slags, tin ores and slags, anti-

Jan 1, 1937

By Carle R. Hayward

This work was first undertaken in the metallurgical laboratory of the Massachusetts Institute of Technology in 1907 by L. A. Dickinson, E. Phelps, and V. S. Rood, under the author's direction. They attempted to determine the diagram for the system Cu2S-MiS, but several inexplicable results were obtained. The following year, P. H. Mayer with Mr. Dickinson carried on some experiments with nickel sulphide and found that the molten material slowly lost sulphur until it reached a composition corresponding to the compound Ni3S2, established by Bornemann.l At this point the composition remained stable. The freezing points of the mixtures gradually fell off with the loss of sulphur. Since the above facts seemed to explain the erratic results obtained in the first experiments, Mr. Mayer with F. Jaeger attempted in 1910 to establish a correct equilibrium diagram for the Cu2S-Ni3S2 series. They prepared pure Cu2S and Ni3S2 and determined the cooling curves for various mixtures. The fusions were made in a platinum resistance furnace and the temperatures were measured with a platinum-iridium thermocouple connected with a Sullivan galvanometer. The curve was established for mixtures containing more than 40 per cent. Cu2S, but they were unable to determine certainly the direction of the curve beyond that point. Nothing further was attempted with this series until the present year, when the work was carried to a successful conclusion with the assistance of A. Butts, Jr., and E. H. Weil. The results of this work are given in the following pages. Preparation of Cu2S.—A piece of cathode' copper from the Buffalo plant of the Calumet & Hecla Co. was cut into shavings by a shaper and converted into sulphide by heating in boiling sulphur. A porcelain casserole was used for the purpose, the heat being furnished by a Bunsen burner. It was found that after boiling in the sulphur for an hour the copper shavings were completely converted into sulphide. The liquid sulphur was then poured off, leaving the solid sulphide in the casserole in

Jan 1, 1915

By Henry Fay

The erosion of guns is a complex problem which can be solved only by a detailed study of all the factors involved. In the present paper it is proposed to submit the results of observations and experiments which have extended over several years. Certain facts have been established and preliminary reports have been published.' Conclusions have been reached since then which, it is believed, are worth presenting for the purpose of promoting discussion, and with the hope that ultimately the whole truth will be known. The particular phase of the problem which will be presented here is the hardening of the inner surface of the gun tube. It has been known for a long time that after firing a large caliber gun for some time, the surface of the metal becomes hard and brittle, cracks, and wears away.2 The character of this phenomenon may be learned by an examination of some results which are typical, obtained from a detailed study of a 12-in. gun. The gun was trepanned and rings representing various sections of the gun were cut out for examination. The first ring represented the metal at the muzzle end, and the other rings were removed at approximately 120, 240, 325 and 337 in., respectively, toward the breech end. The appearance of the surface of the metal in the different sections is shown in Fig. 1. The greatest amount of wear and maximum amount of hard surface layer was found in section marked E, which is nearest the powder chamber and at the beginning of the rifing; the maximum amount of cracking in D; the maximum amount of copper deposition in C. Section B showed heat cracks on both lands and grooves, and section A showed heat cracks on the driving edge of the lands only. There was much flow of metal in both sections E and D, and there was progressively less effect noticeable toward the muzzle end. The polished cross-section of these same pieces is shown in Fig. 2. The extent of the erosion is greatest nearest the powder chamber, and diminishes toward the muzzle end.

Jan 1, 1917

By Fred H. Poettmann, A. L. Benham

correlation of waters and identification of mixtures of two and three waters is important in secondary recovery evaluation studies and studies involving underground movement of waters. The importance of such studies suggests the need for a method to correlate a great number of water analyses to accurately identify and improve the understanding of mixtures of waters. Geochemical analyses of waters furnish a quantitative measure of each of the ions present in a water. Table L shows a portion of the data on many oilfield water analysis report forms in use today. Under "parts per million" are listed the quantitative amounts of each ion in milligrams per liter. Following the work of Stabler' and Palmer", some laboratories have reported additional data to indicate the reaction capacity, or reacting value of each ion. Table I lists data under two subheads for the "reacting value". Under the first subhead, the reacting value is reported in gram equivalents per million, hereinafter called equivalents per million. This value is determined by multiplying milligrams per liter of the ion by a factor equal to the reciprocal of the equivalent weight of the ion. Under the second subhead (per cent) is listed the percentage of each ion based on the total equivalents per million. Sodium is not usually an analyzed value in routine analyses, but is determined by the difference between total negative equivalent per million values and the sum of all of positive ion values for which analyses were made. This difference is reported as sodium, hereafter labelled "sodium". On this basis, the subtotals of the equivalent per million and per cent reacting values of the positive and negative ions are equal. CORRELATION OF WATER ANALYSES DATA Previously reported methods for correlating oilfield waters have used part of the data in Table 1, and can be classified into two categories. Correlation by Chemical Character Correlation methods using the chemical character of waters, as represented by the per cent reacting values of the ionic constituents, have been used by Palmer2 and Tickell. These methods have the limitation of neglecting the ionic concentration of the waters. This limitation can be serious in areas where waters have the same chemical character, but differ in concentration. Correlation by Concentration of the Ionic Constituents The Reistle' and the Stiff methods use the ionic concentration in parts per million and equivalents per million. These methods are effective in differentiating waters of similar chemical character and varying concentration, as in the highly saline waters of the Mid-Continent area. These methods have the disadvantage that they correlate waters by comparing many graphs of individual water analyses to determine the similarity to, or the variance from "type" waters. PROPOSED METHOD OF CORRELATING WATER ANALYSES DATA Correlation graphs presented in Fig. 1 represent water analyses data as points to facilitate the correlation of waters. The graph on the left of Fig. 1 is a plot of per cent reacting value of magnesium vs calcium. The right