By E. W. Henderson

Development work in the state of Utah in 1935 consisted of additional work done on wildcat tests started in previous years and on a number of new wildcat tests started during the year. No effort was made to extend areas or to discover deeper productive horizons in proven fields. Principal areas of development were in Daggett County, northeastern Utah; Grand and Emery counties, east-central Utah; and in Washington County, southwestern Utah. Daggett County Clay Basin.—The Mountain Fuel Supply Co. deepened Murphy No. 2, sec. 21, T.3N., R.24E., from 6030 to 6790 ft. for a test of the Sundance formation. Two sandstone members at 6520 to 6644 ft. and 6737 to 6790 ft. contained water. The hole was plugged back to 5860 ft. and left as a future gas supply for the Salt Lake City-Ogden pipe line. The failure of the Sundance formation to produce in this test, in view of the recent Sundance discoveries in Colorado arid Wyoming, was disappointing Emery County Last Chance.—-Thc wildcat test of the Rainsey Petroleum Corporn-tion, Well No. 1-X, sec. 18, T.26S., R.7E., completed plugging back from total depth of 3168 ft. to 2771 ft. and was shut in as a gas well. A gas sand at 2724 to 2771 ft. produced approximately 21 million cubic fert. A deep test of the structure will be started upon approval of a wit plan of development. Grand County Cisco.—-The wildcat test of the Utah Southern Oil Co., sec. 33, T.22S., R.22E., of which the total depth was 1720 ft. on Dec. 31, 1935, is the most interesting operation ill the state. Location of the test was deter-

Jan 1, 1936

By Arthur C. Spencer

HAVING suggested magmatic waters as the probable agents of vein- and ore-deposition in southeastern Alaska in a paper entitled, The Geology of the Treadwell Ore-Deposits,1 it is with particular interest that I note W. Lindgren's application of the hypothesis of igneous emanations to the gold-quartz veins of Victoria and of California.2 Mr. Lindgren says: "In the above paragraphs I have repeatedly called attention to remarkable similarities in vein-filling and metasomatic action between the Victorian quartz veins and those of Sierra Nevada. Another striking similarity is that in both of these regions the veins were formed just after the intrusions of vast masses of granite or dioritic magma into crumpled and compressed sediments. I am convinced that these similarities are due to closely similar modes of formation. With some confidence, I would formulate the hypothesis that the gold and the quartz in this type of veins have been deposited chiefly by `eruptive after-effects;' in other words, chiefly by hot ascending waters originally contained in the granitic magma and released from it by decreasing pressure, due to its eruption into the upper parts of the lithosphere. It is quite possible that atmospheric waters may have played a certain part by aiding the precipitation and by effecting certain forms of concentration in the deposits." There are many reasons for extending this hypothesis to southeastern Alaska. This region and the Sierra Nevada belt of California are undoubtedly parts of one geologic province, throughout which the main events of geologic time are evidenced by identical or closely similar records in the rocks. Our knowledge of the former region is still fragmentary, to be sure, but the origin-dates of the most prominent features of

Jan 1, 1913

By E. W. Henderson

Development work in the state of Utah in 1935 consisted of additional work done on wildcat tests started in previous years and on a number of new wildcat tests started during the year. No effort was made to extend areas or to discover deeper productive horizons in proven fields. Principal areas of development were in Daggett County, northeastern Utah; Grand and Emery counties, east-central Utah; and in Washington County, southwestern Utah. Daggett County Clay Basin.—The Mountain Fuel Supply Co. deepened Murphy No. 2, sec. 21, T.3N., R.24E., from 6030 to 6790 ft. for a test of the Sundance formation. Two sandstone members at 6520 to 6644 ft. and 6737 to 6790 ft. contained water. The hole was plugged back to 5860 ft. and left as a future gas supply for the Salt Lake City-Ogden pipe line. The failure of the Sundance formation to produce in this test, in view of the recent Sundance discoveries in Colorado arid Wyoming, was disappointing Emery County Last Chance.—-Thc wildcat test of the Rainsey Petroleum Corporn-tion, Well No. 1-X, sec. 18, T.26S., R.7E., completed plugging back from total depth of 3168 ft. to 2771 ft. and was shut in as a gas well. A gas sand at 2724 to 2771 ft. produced approximately 21 million cubic fert. A deep test of the structure will be started upon approval of a wit plan of development. Grand County Cisco.—-The wildcat test of the Utah Southern Oil Co., sec. 33, T.22S., R.22E., of which the total depth was 1720 ft. on Dec. 31, 1935, is the most interesting operation ill the state. Location of the test was deter-

Jan 1, 1936

By R. B. Snow

Inclusions revealed by the ultrasonic inspection of forgings, slabs, and blooms cause costly diversion or rejection of the product. Most of those inclusions are so large that they should have floated out of the liquid steel soon after teeming and been removed when the top discard was taken from the ingot. To investigate the source of the relatively large inclusions found in the body portions of ingots, a large forging ingot was examined from top to bottom along the centerline, and special studies were made of open-hearth and BOP ingots. A study of the inclusion distribution in the as-cast 134-inch-diameter forging ingot revealed only a few inclusions larger than 15 microns in the body of the ingot. Larger inclusions may be formed by entrapment of rising inclusions in large falling dendrites rather than by the precipitation and agglomeration of oxides from the liquid steel-dendrite interface during solidification. The original top crust of the ingot investigated broke away from the hot top and sank to the bottom during the solidification process, as indicated by entrapped inclusions found in a band 12-1/2 inches above the stool. A change in the hot-top insulation practice on subsequent ingots to insure the integrity of the top crust has produced clean ingots. A ZrO2 tracer was added to the hot-topping compound and to the top surface of open-hearth and BOP ingots after teeming. The tracer was found in large inclusions in slabs and blooms from these ingots. Large inclusions in the body of ingots appear to be related to disturbances of the natural freezing and shrinkage processes in the hot- top region of the ingot.

Jan 1, 1972

By Richard F. Miller

Recent studies of creep have made it apparent that plastic deformation may occur in metals under stresses less than the elastic limit as determined from short-time tests. In summarizing conclusions drawn from creep tests by various investigators, Tapselll said: "It is evident that if a material has a true elastic range, the elastic limit must represent the maximum stress for no creep." The presence of a definite elastic limit, represented in single crystals by a critical or threshold shearing stress, is claimed by Schmid2, Elam3 and others who have investigated the plastic deformation of single crystals. However, this "law of critical shearing stress" was determined2 from short-time tests, and the measurement of the deformation was made with apparatus primarily designed to observe large amounts of plastic deformation, not to detect elastic changes. Experimental data recently obtained with highly sensitive instruments by A. W. Hanson4 on zinc and by Podaschewsky5 on rock salt indicate that the elastic range in single crystals is considerably narrower than formerly was supposed. Moreover, a theoretical possibility of permanent deformation, under the influence of even the smallest shear stress in single crystals above a certain temperature (Td), has been developed by G. I. Taylor6. This evidence seemed to warrant an examination of the elastic limit in large single crystals by means of creep tests. The first metal chosen for examination was zinc. AppaRatus The creep-testing apparatus developed for this work is shown in Figs. 1 and 2. The extensometer A is sensitive enough to detect changes in length of 3.3 X 10~6 in. per in., and yet can be used into the plastic range without injury to the apparatus. The specimen,

Jan 1, 1936

By W. J. Uren, Charles R. Kuzell

The industries engaged in winning minerals from the earth, because of their widespread dissemination, are faced with perhaps as wide a variety of labor-management problems as may be found in any other broad sphere of productive activity. Those problems are continually increasing in volume and complexity, and management has become aware of their growing importance. For the past quarter century at least, labor-management problems have largely been union-management problems. During this period tremendous assistance has been given labor unions through legislation and administrative and political action. In the United States, legislation favorable to unions has come about in the form of the now defunct National Industrial Recovery Act; the Wagner Act, most of which has been carried forward in the Taft-Hartley Act; the Norris-La Guardia Act; the Wage and Hour Law; the Walsh-Healey Act; and others. The result has been to transfer from the hands of management to those who direct the affairs of the unions a large share of control over the industry and to hamper in many ways the remaining control left to management. In the United States there are many examples of the power of unions to injure whole industries seriously with- out regard to the interests of management, the employes, or the public. This chapter deals with the various phases of labor-management relations as they affect the principal segments of the mineral industry in North America. To the greatest extent possible available data is presented pertaining to the unions involved, their relative strengths, labor law, compensation and fringe benefits of employes, working conditions, and related matters. As background, the historical development of union-management relations in the respective segments is included where possible. The section dealing with the United States has been divided into separate

Jan 1, 1959

By Willard Ide Pierce

THE native methods of mining and milling gold-ores in Korea may not present any specially new features, but are chiefly interesting as primitive practices, still followed at the present day. In mining where the rock is hard, wood is piled up near the face of the tunnel or drift and then set on fire. The fire bums for twenty-four hours, after which, three or four days are given for the rocks to cool, before the miners go in and extract the loosened material. The only tools in use are a hammer, a steel gad about five inches long, and a flat spoon-shaped basket. The pay-streak or chute is closely followed, and in places the workings are very small and intricate. Rock not yielding more than $6 per ton is not extracted. The manner of opening a mine is to begin on the outcrop, where the rock pays, sink a shaft or run a tunnel on the vein, and follow the pay-streak and more easily worked ore. When this is exhausted, or the influx of water interferes, the opening is abandoned and operations are begun again at a new spot on the outcrop. The place usually selected is as high up on the mountain as possible, and in no instance is advantage taken of the topography by running a cross-tunnel to tap the vein. The ore is brought in baskets to the surface, and there placed in sacks, holding about 150 1bs. each, and taken to be crushed. The rock is first crushed between two stones, as shown in Fig. 1. The upper stone is oval and rounded on the bottom, so that it can be readily rocked on the under stone. Two pieces of wood, used for handles, are placed, one on each side, in grooves in the upper stone, and held in position by means of straw rope. The lower stone is not smooth on top, but exhibits three elevations running lengthwise, with shallow depressions between them. The middle elevation acts as a fulcrum on which the upper stone may be rocked. From two to ten men, according to the weight and size of the stone used, are employed in rocking. With four men, from 300 to 350 lbs. of rock can be crushed per day, the stone making 50 complete oscillations per minute. The men squat on each side of the stone and move it to and fro by means of the wooden handles. The ore is fed, in pieces up to the size of an egg or even larger, by one of the men. During the crushing one man on each side, as the stone rocks from

Jan 1, 1890

By A. E. Jenkins, A. Jostsons

Isothermal sections of the Ti-0-H phase diagvam at 600°, 700°, and 800°C have been constructed from equilibrium hydrogen pressure measurements over a range of Ti-0-H alloys containing up to 34 at. pct 0. Oxygen reduces the hydrogen solubility at fixed hydrogen pressure but increases the terminal solubility in the a solid solutions at the a/(a + P) phase boundary. Metal-lographic studies of alloys annealed below the eutectoid temperature show that oxygen also increases the ter-ninal solubility of hydrogen in the a solid solution in equilibrium with the hydride phase. The effect of oxygen on hydrogen solubility is discussed in terms of the electronic and geometric structure of interstitial solid solutions. THE isothermal solubility of hydrogen in a Ti-0 alloys at 800°C has been measured by Hepworth and ~chuhmann' who subsequently used ternary Gibbs-Duhem integrations to calculate oxygen activities in binary Ti-0 alloys. The present study aims to extend Hepworth and Schuhmann's measurements to alloys richer in oxygen and to a range of temperatures. This paper presents the results of hydrogen equilibrium pressure/concentration measurements in Ti-0 alloys as well as observations on the effect of oxygen on the terminal solubility of hydrogen in a titanium. The thermodynamic properties of binary Ti-0 alloys, derived from these measurements, will be published separately.' EXPERIMENTAL METHODS Specimen Preparation. Ti-0 alloys were prepared from iodide-refined titanium and titanium dioxide obtained by hydrolysis of redistilled titanium tetrachlo- ride. Specimens containing up to 16 at. pct 0 were prepared by electromagnetic levitation3 whereas a conventional tungsten arc furnace with a water-cooled copper hearth was used to melt oxygen-rich alloys. The specimen homogeneity was indicated by the constancy of lattice parameters of samples from various parts of the ingot as well as by the sharpness of the reflections on X-ray powder patterns. Oxygen-rich specimens in the composition range (20 to 34 at. pct), where ordering has been ~bserved,~ were annealed for 300 hr at 600°C prior to use in hydrogen solubility measurements. Apparatus. The hydrogen pressure/concentration measurements were made with a modified Sieverts apparatus shown diagrammatically in Fig. 1. Specimens were placed in a clear silica tube and impurity pickup by direct reaction with silica was prevented by lining the heated end of the silica tube with thin molybdenum sheet. A double silica tube was required to eliminate loss of hydrogen by diffusion through silica at high temperatures and high hydrogen pressures, the space between the tubes being maintained at a hydrogen pressure equal to that above the specimen. Hydrogen was purified by diffusion through a Ag-Pd tube.= Hydrogen pressures were measured with a mercury McLeod gage in the range 0.001 to 4 Torr

Jan 1, 1968

By Y. Kondo, A. M. Gaudin

A combined method for sizing in the sub-micron range was developed using centrifugation and gamma emission. Its essential features are: 1) Centrifugation of suspended mineral in water carried out at 4°C where water has its maximal density and zero temperature gradient of density 2) Gamma activition of the sample suspension induced by irradiating it in a nuclear reactor prior to centrifugation 3) Measurement of the activity of a beam of suspension as it is sedimenting in the centrifuge, using a scintillation counter provided with a discriminator. Albite, the sodium feldspar, was used as feed to the comminution step, and the induced gamma activity of Na24 was measured. Dissolved sodium ion caused a a non-settling activity in the measurement. Other "noise" is due to scattered gamma radiation from albite particles in the centrifuge outside of the line of sight. These two activities were obtained sep arately and subtracted from the total activity counted. The relative solid concentration in the suspension under the collimating slit is proportional to this net activity. The cumulative weight per cent of undersize particles was calculated and plotted against size on logarithmic scales. The relationship was found to be linear down to about 30 mµ. The specific surfaces calculated from particle size distribution agree with those measured by krypton gas adsorption. The measurement of particle size distribution of comminution products has been of interest in clarifying the mechanism of the process. The Gaudin-Schuhmann equation1,2 relates the cumulative percentage undersize, y, to relative particle size x/k. The particle size, x, and the size modulus, k, together with the distribution modulus, m, characterize the particle size distribution, m is the slope of a plot of log (y) against log (x/k). This equation has been verified for ground particles down to 1 micron in size.3'4 For particle sizes smaller than a few microns, the precision and facility of sedimentation and microscope techniques become questionable. Use of a centrifuge which shortens settling time from weeks to hours is attractive. Many centrifugal methods have been proposed; however, determination of the solid concentration of the suspension at a reference level as a function of time is difficult, and sampling the suspension is likely to introduce errors. Measurement of particle size distribution by X-ray absorption in gravitational5 and in centrifugal6 sedimentation have also been tried. In these methods, the absorption coefficient for the solid is independent of size, since the wave lengths of the X-rays and gamma-rays are orders of magnitude smaller than the particles. Radiometric techniques7 in size distribution measurement have been developed within the last several years. They offer advantages over usual gravimetric and optical methods. PRINCIPLE OF METHOD The combined method of centrifugation and gamma emission for sizing in submicron range described in the present paper has the following essential features. 1) Centrifugation is carried out at 4 ± 0.1°C. Convection currents in the water phase due to density changes caused by temperature variation may disturb completely the settling system. To avoid this difficulty, the unique property of water having zero temperature gradient of density at 4°C is used. 2) Prior to size measurement the sample suspension is irradiated in a nuclear reactor and gamma activity induced. The gamma activity of the particles sedi-mented radially is measured by a scintillation counter provided with a discriminator. By this method, interruption of centrifugation by withdrawing samples is avoided and the counting rate at any time represents the solid concentration in the suspension at the level of the collimating slit of the centrifuge at the particular time at which the measurement is made. 3) By proper selection of the feed material and of the comminution device, gamma activities of foreign

Jan 1, 1964

By W. A. Backofen, D. Lee

Tlze condition of superplasticity or neck-resistanl flow that results front high strain-rate sensitivity has been observed in isothermal tension tests on several titanium alloys and one of zirconium hi general, il was associated with reasonably fine-grain micro-structures being stvained in the transformation range at rates below i - 10 -3 sec-&apos;. The metallographic mean-free path, L, was measured at room temperature after rapid cooling from the temperature of test-ing. The flow stress of Ti-GAL-4V at 950°C was proportional to La at different constanl <; the value of a decreased with increasing. E but at E< 1.5 x 10-4 sec-1 it varied only from 0.9 to 1.25. The findings were interpreted to mean that viscous boundary shear is the rate-controlling process of deformation at high levels of strain rate sensitivity in these materials. Elongation of over 1000 pet could be obtained, but a1 temperatures so high and rates so low that any practical application of the full effect would probably be difficult. As the transformation range was narrowed, by turning from Ti-6AL-4V to Ti-5Al-2.5sn to nomznally pure titanium, the allowable temperature varialion was correspondingly reduced. Superplasticily was not found in Armco iron, presumably because the transformation range was too narrow to allow the developtnenl of a reasonably stable microstructure for isolhermal lesting. THE work represented by this paper grew out of a recent study of texture hardening in a(hcp) titanium and zirconium-alloy sheet,&apos; of which part has now been published.2 It was found that, with heating, the tensile plastic-anisotropy index, R,* was decreased from well above 1 towards 1 as the temperature range for the a(hcp) -ß(bcc) phase change was entered. The clearest example of that trend is illustrated with previously unpublished data in Fig. 1. It might have been thought that such a development resulted simply from introduction of the cubic and therefore plastically less anisotropic phase. However, the accompanying change in the index of tensile strain-rate sensitivity, m = a log a/a log E, was rapidly upwards, to a high of 0.85 in some cases (also illustrated in Fig. 1). At the same time, the total tensile elongation rose to a maximum and the flow strength dropped away as R (and m) approached 1. Taken together, the observations cannot be understood as resulting from the presence of cubic phase, per se. It has been concluded instead that they reflect the largely noncrystallographic deformation which characterizes superplasticity. As demonstrated in other recent work? a necessary condition for super-plasticity is strain-rate sensitivity of flow stress sufficiently high that m is above a lower limit of -0.3. The origin of large m has been traced, in turn, to grain size so small that a substantial amount of viscous deformation is introduced by such processes as Nabarro-Herring diffusional flow4 and/or grain boundary shear.5,6 Because of problems in the processing of titanium and zirconium alloys—problems of high strength, limited ductility, and excessive springback, originating largely in slip resistance-it was natural to wonder if something useful might be done with superplasticity in those materials. Therefore experiments were made for more closely identifying and generally bounding the phenomenon with temperature and strain-rate limits, before attempting to decide about its exploitation. The results are being reported here. EXPERIMENTAL Materials. The two of primary interest were the titanium alloys of nominal composition (in wt pct) 5A1-2.5Sn and 6A1-4V. Others were a 4A1-1/4O2 titanium alloy, titanium of commercial purity (RC-70), Zircaloy-4. and Armco iron. All were received as annealed 3/16 in. thick sheet, except RC-70 which was & in. thick, and tested in that condition. Details of transformation temperature and grain size are given in Table I. The results of dilatometry for the measurement of transformation temperatures were unsatisfactory. Data were finally obtained by metallographic examination of each specimen after test, to determine from the amount of transformed 4 where the specimen had been heated in relation to the critical temperatures. Results were in reasonable agreement with information from the supplier. Strip tensile specimens were of full sheet thickness and taken along the rolling direction, except for those

Jan 1, 1968

By R. D. Reiswig

An increasing amount of high-temperature metall~?~gical research is carried out in resistively heated tube furnaces in which a bare specimen is suspended by a fine wire at the midpoint of the tube. It is shown that the assumption of near-blackbody conditions on the surface of the sample may give rise to errors in optical pyrometry of 50°C or more. A number of papers published in the metallurgical literature in recent years have described the use of high-temperature tube furnaces for heat treatments, melting-point determinations, and other work. Typically, the tube is of a refractory metal with open ends, is heated by the passage of an electric current, and has concentric cylindrical radiation shields outside it. In at least one of these,&apos; the specimen is contained within a crucible having a small hole in its lid through which optical-pyrometer measurements are made under essentially blackbody conditions. In another design,* the specimen is inside a muffle which is concentric with the heater tube and which contains a number of washerlike longitudinal radi- ation shields to reduce axial temperature gradients and to give conditions near the specimen closer to those of a black cavity. Yet another design3 employs a wire specimen coaxial with the heater tube. Blackbody conditions are simulated by passing current from a separate supply through the wire until it "disappears" against the background (the inside of the heater tube) as seen through a radial spy hole in the tube. Good agreement with known melting points is achieved when an optical pyrometer is used under such disappearance conditions as the melting point is approached. That this latter method works so well is due, evidently, to considerations such as those mentioned by Dike4 and others.5-8 A more common method than the above, however, has been the suspension of an uncovered specimen by a fine wire in a resistively heated tube with open ends. A radial spy hole about midway between the ends of the tube permits optical-pyrometer observations on the specimen, the inside of the tube, or both. So observed, the specimen typically appears to differ but little in brightness temperature from the inside of the tube. According to De vos9 the radiation from such a spy hole in an empty tube of reasonable 1ength:diameter ratio (e.g., 10 or greater) should be essentially blackbody radiation. For these reasons, apparently, descriptions of work carried out in such furnaces usually include a statement to the effect that conditions surrounding

Jan 1, 1964

By N. Van Wingen, Norris Johnston

Laboratory flood pot testing of California sands has progressed to a considerable extent in the past 18 months. Flood evaluations have been carried out on over 200 large core samples. Many of these were heavy oil sands of high permeability and completely unconsolidated in nature. The oil frequently formed a bank, though some of the oil was recovered in the subordinate phase of the flood, by viscous drag. Flood pot recoveries as high as 1400 bbl/acre ft have been recorded. Reservoir analysis suggests a conformance factor of 0.4 to reduce laboratory recovery to probable field practice. Oils with viscosities up to 1800 cp have been successfully handled in flood pot evaluations. The shallow, loose sands are not well adapted to the application of- high pressures to offset the high viscosities. INTRODUCTION Secondary recovery may be said to have started 60 years ago when accidental floods occurred in the Bradford sand in Pennsylvania. About 1921 artificially conducted water drives came into extensive use and since that time the great Bradford field has been almost completely subjected to water flooding. During the last 30 years, most of the known medium and deeper production in California has been discovered and is being exploited by primary recovery methods supplemented in some instances by high pressure gas injection. The California area is just beginning to feel the need for secondary recovery in view of an unprecedented market demand and the rapidly rising cost of new pool discoveries. With the presently recognized desirability of secondary recovery in California, there must also be appreciated a number of serious differences between the water flooding problems here as compared to the territory east of the Rockies. California sands are generally thicker, and are frequently soft and argillaceous. The oils are often heavier and asphaltic. Much of the oil is below 15°API, occurs at shallow depth, is cool and free from appreciable dissolved gas, which results in relatively high reservoir oil viscosity. Secondary recovery is particularly beneficial where primary recovery has been poor and where no natural water drive exists. These conditions apply particularly to the heavy, shallow, clean production from soft, often argillaceous California sands so abundantly found at depths less than 1500 feet. Often, too, there is a totally insufficient supply of water of satisfactory quality to inject at a reasonable cost. Also, the crude oils are priced far below the premium Bradford crude. Although these and a number of minor problems beset the operator desirous of starting secondary recovery, great progress has been made in the past few years in finding how to adapt previous Mid-Continent and Eastern experience to water flooding in California. There are about nine projects for subsurface injection of water which can be said to classify as secondary recovery operations. Subsurface water disposal would so classify when the sand receiving the water is a nearby oil producer, as is often the case. When water is injected subsurface into a barren sand, the operation does not classify as secondary recovery. Several of the most active operators avail themselves extensively of preliminary engineering and laboratory work to guide their decisions, while others enter small scale flooding operations directly in the field. It is the laboratory work pertinent to several of the California secondary recovery projects that this paper discusses. PURPOSES OF LABORATORY FLOODING TESTS Experience in areas where water flood operations have been carried out has indicated that careful engineering planning is an important requisite for subsequent economically successful field operation. Floods that fail are more frequently those where operations were instigated without a prior engineering investigation to determine the effectiveness of the injection fluid as an oil displacing medium. Laboratory data are essential in the evaluation of an oil property for secondary recovery possibilities. Success or failure of secondary operations can under certain special circumstances be determined directly by cores and their subsequent routine analysis. This is particularly the case where flushing of the cores in the course of coring is negligible and where the results of the analysis can be compared with existing secondary recovery operations. Where these conditions cannot be&apos; fulfilled, the application of core analysis is more limited. In such event, the results obtained by water flooding core samples in the laboratory have been found to be of prime importance. Cores may be flooded "raw" as taken from the well or in the event flushing and depletion of the cores in the process of drilling are major factors the fluid content may be artificially restored prior to the flooding. Laboratory studies should also be made to determine the suitability of the water selected for injection. Thus interaction between injected and formation water may cause precipitates to be formed which may plug the sand. Even more important, especially to California operations, is the possibility of the hydration of formation clays by the injection water. The aims of flood pot and associated tests are basically to determine the residual oil saturation after flood, the water-oil throughput ratio and to establish whether an oil bank is formed. Additional information which can be obtained from flood pot tests pertains to the pressure differential required to effect displacement, the relative permeability to oil in the oil bank and the relative permeability to water in the watered out region behind the bank.

Jan 1, 1953

By C. A. Bruch, W. E. McHugh, R. W. Hockenbury

EXPERIMENTAL results of the last decade have shown that both accelerator particles and reactor radiations produce significant changes in the properties of metals. These changes, called radiation damage, are important from both academic and engineering viewpoints. An understanding of the radiation damage produced by reactor radiations is difficult, because many kinds of particles having varying energies are present. Therefore, many fundamental studies are being conducted using accelerators in order to obtain nearly mono-energetic beams of various charged particles. Furthermore, many of these experiments are conducted at low temperatures in order to freeze in the radiation-produced lattice defects, after which the specimens are annealed to study the movement of the defects. It is found that although much of the low temperature radiation damage disappears by annealing at room temperature, a significant amount remains. Because there is no assurance that irradiation followed by annealing at a higher temperature will produce the same effect as irradiation at the higher temperature, and because there is an immediate interest in reactor radiation effects during exposures at and above room temperature, a major program is in progress at this laboratory to investigate some of these effects. This paper, representing a part of the program, compares the radiation damage to a group of metals which were exposed under nearly identical irradiation conditions. The metals, representing the three major crystal systems, include copper, nickel, titanium, zirconium, iron, molybdenum, and type 347 stainless steel. The effects of reactor radiations have been treated from a theoretical viewpoint by Seitz&apos; and Ozeroff.&apos; The problem considered by them has been the atomic displacements produced in an infinite medium by mono-energetic beams of both neutrons and charged particles. For reactor experiments, this treatment is not wide enough in scope, because specimens and reactor components are finite, and there are continuous energy spectra of the various particles. Therefore, the theoretical considerations will be extended in this paper to cover reactor conditions and the findings will be compared with the observed radiation damage. Experimental Materials—The six basic metals for this investigation were of commercial or higher purity, and the type 347 stainless steel was of commercial quality. These materials were supplied in various forms ranging from ingots to finished rods, and were fabricated to rods approximately % in. in diam and annealed for specimen stock. A summary of data pertinent to these materials is shown in Table I. The values for chemical compositions include both actual analytical values and typical values supplied by the manufacturer. More information concerning typical

Jan 1, 1957

By Charles Catlett

THE rapid development of the Portland-cement industry implies that the country is being very carefully searched for material suitable for its manufacture. Such material can be found at a great many places ; but deposits thoroughly satisfactory in chemical composition, and at the same time meeting all the other requirements connected with the economic production and profitable marketing of the product, are exceedingly few, if I may judge from the investigations which I have had to make in a number of States. The raw mixture which by its clinking and grinding forms Portland cement contains approximately 75 per cent. of carbonate of lime. This is found in nature as limestone or marl. The natural rock commonly carries either more than the required percentage of carbonate of lime (in which case it has to be reduced by suitable admixture of clayey ingredients) or less-in which case purer lime carbonate has to be added. The controlling ingredient, therefore, is carbonate of lime, or limestone of the right composition. Among the most serious difficulties is that of finding limestones low enough in magnesia to meet the exacting requirements of certain specifications. All engineers recognize that there is a limit beyond which it is not safe to let the magnesia go; but within that limit there is considerable difference of opinion. Until that difference is finally settled, no one would be willing to invest the large sum of money necessary for a Portland-cement plant, if it were not certain that the usual requirements in this particular could be satisfied. The usual limit in well-established specifications is 5 per cent. of magnesium oxide in the finished cement, but many specifications limit the amount to 3 per cent. These figures

Jan 9, 1907

By Robert E. Delavault, Harry V. Warren

Circumstances determine whether it is better to make analyses in the field or in a permanent laboratory. The rubeanic acid test described in this article has been designed primarily for field use: it is simple and virtually foolproof, and it requires a minimum of field kit.* It is sensitive, easily detecting 4 ppm of readily extractable copper in a soil. This is by no means a quantitative test, but it is accurate enough to provide a valuable indicator of copper anomalous areas for both prospectors and field geologists. The easiest method for detecting metal deposits that do not produce visible float or stains is to make a simple chemical test for the metal in overlying soil, or in the silt of a stream that may have picked up metal farther upstream.

Jan 11, 1958

By B. Ladanyi, B. Hoyaux

A first requirement for assessing the safety of a rock slope, either artificial or natural, particularly if the rock behaves in an elastic-brittle manner, is a propw knowledge of the distribution of stresses within the slope and their development with time and advancement of workings. There are a uumber of different methods that can be used, in principle, for obtaining this information, such as (1) stress measurement in situ, (2) photoelasticity,1 (3) analytical methods, and (4) numerical methods. In cases where the stress distribution cannot be obtained by classical analytical methods, as in the one considered herein, either photoelasticity or numerical methods are norrnally used. However, actually, due to the rapid development of high-speed computers, increasing preference is given to the numerical methods. Among the latter, the most successful ones, to date, for determining the stress distribution in slopes have been (1) the finite difference method,2-4 (2) the lumped parameter method,5 and (3) the finite element rnethod.6 However, for determining gravity stresses in a natural rock slope, only the finite difference method has been used until now.7,8 A solution of the same problem by the finite element method will be shown here in which a particular reference is given to the development of tensile fracture zones within the slope. FINITE ELEMENT METHOD The stress analysis using the finite element method originates from an extension of the matrix analysis of structures.9 It consists in decomposing a continuous medium, assumed herein to be homogeneous and isotropic,

Jan 1, 1972

By Reger, B. David

FOR many years, the belief that the so-called "Clinton" sand of Ohio might produce. oil and gas, if it could be reached, has been prevalent in West Virginia. To test this theory, many hundreds of thousands of dollars have been spent and several extremely deep wells, including the deepest boring of the world, have been sunk at various points. With the exception of one well now completed through the sand and the possible exception of another still in progress, all of these wells failed to reach the goal, either through failure of funds or through drilling accidents. REVIEW OF DEEP DRILLING The subject of deep-sand oil and gas in West Virginia has already been discussed by the author1 and by White.2 In these papers, it was shown that the Upper and. Middle Devonian shales, lying between the Berea oil sand (basal Mississippian) and the Oriskany sandstone (Lower Devonian), thicken steadily from eastern Ohio across northern West Virginia and Pennsylvania; but it was stated that the same rate of thickening did not occur in that part of West Virginia south of the Great Kanawha River and in the adjoining portion of Kentucky. In spite of this great eastward thickening, the fact that both the Oriskany and "Clinton" sands, the latter of which is equivalent to the White Medina of New York, exist in great thickness all along the Appalachian Mountains farther east, was held as proof of their probable presence in the deep Appalachian basin.

Jan 3, 1925

By John B. Gayle

PRESENT flotation processes depend almost entirely on the buoyant properties of air bubbles to effect separations of mineral and gangue, but there is no convenient method for measuring aeration in flotation cells. Consequently the relation between aeration and cell performance has not been definitely established. In connection with a comparative study of kerosene and froth flotation processes, a modification of the displacement method&apos; was developed in which air escaping from the cell surface is measured with a wet-test meter. The arrangement shown in Fig. 1 is satisfactory for use with a number of cells and is not critical, except that care must be taken to use connections and tubing large enough to avoid excessive back pressures. Attempts to use smaller tubing resulted in back pressures that caused displacement of the liquid level in the receiver, so that some air was lost around the sides, an occurrence readily visible when measurements were taken with only water passing through the cell. With the arrangement shown, the manometer indicated an average reading of about ½ -in. water pressure. No loss of air was evident.

Jan 7, 1958

By Earl W. Palmer, Cyril Stanley Smith

A study of the precipitation-hardening of copper steels1 led the authors to investigate malleable iron containing copper, for the low-carbon ferritic matrix in malleable iron should lend itself admirably to precipitation-hardening. It was soon found that in addition to rendering malleable iron susceptible to improvement by precipitation-hardening treatments, copper has another potentially useful effect as an accelerator of graphitization. Brief mention of these effects was given in a general paper by Lorig and one of the present authors2; the present paper gives further details on the graphitization and precipitation-hardening effects only. After the completion of this work a paper by L. Lykkin3 appeared, confirming the authors&apos; conclusions regarding graphitization. Material Used After some preliminary heats had been made in the laboratory to determine the effect of copper, several castings from commercial air-furnace heats were obtained, and data from these alone are given here. Part of the metal was poured directly and part was treated in the ladle with the desired amount of copper before pouring. Green-sand molds were used, each holding two tensile test pieces of the form adopted by the Malleable Iron Research Institute, or two bars for graphitization studies, 5/8 in, in diameter and 9 in. long, fed through two enlarged sections equidistant from the middle and ends of the bars. Risers of suitable size insured sound castings. Tensile tests were made on the castings after commercial mallealleizing and after special heat treatments to be described. The analyses of the white irons are given in Table 1.

Jan 1, 1935

By Cyril Stanley Smith, Earl W. Palmer

A study of the precipitation-hardening of copper steels1 led the authors to investigate malleable iron containing copper, for the low-carbon ferritic matrix in malleable iron should lend itself admirably to precipitation-hardening. It was soon found that in addition to rendering malleable iron susceptible to improvement by precipitation-hardening treatments, copper has another potentially useful effect as an accelerator of graphitization. Brief mention of these effects was given in a general paper by Lorig and one of the present authors2; the present paper gives further details on the graphitization and precipitation-hardening effects only. After the completion of this work a paper by L. Lykkin3 appeared, confirming the authors&apos; conclusions regarding graphitization. Material Used After some preliminary heats had been made in the laboratory to determine the effect of copper, several castings from commercial air-furnace heats were obtained, and data from these alone are given here. Part of the metal was poured directly and part was treated in the ladle with the desired amount of copper before pouring. Green-sand molds were used, each holding two tensile test pieces of the form adopted by the Malleable Iron Research Institute, or two bars for graphitization studies, 5/8 in, in diameter and 9 in. long, fed through two enlarged sections equidistant from the middle and ends of the bars. Risers of suitable size insured sound castings. Tensile tests were made on the castings after commercial mallealleizing and after special heat treatments to be described. The analyses of the white irons are given in Table 1.

Jan 1, 1935