By P. de Vitry, Willis P. Mould

The wire saw is a tool not less than 60 years old, probably nearer 100 years old. It was developed in Europe and is reputed to have originated in Belgium. Frombold is said to be the original patentee. Wire sawing equipment, as indicated in Fig. I, is very simple. It consists of a three-strand wire cable, usually pis or 1/4 in. in diameter, or a single flat ribbon of medium hard, tough, alloy steel twisted into a helix of those diameters, made to form an endless belt of any length up to several thousand feet. The wire is guided into the cut by sheaves mounted in slides on steel columns situated close to either end of the cut. The feed motion usually is controlled either by gravity or by hand-operated feed screws. The steel columns or "standards" range from 15 to 30 ft. in length. At the top is a swiveled arm supporting a sheave similar to the traveling sheave below. Immediately under the swivel-mounted sheave is a guy plate or collar with shackles attaching four chain or wire-rope guys with suitable tightening devices, or with two guys and two jack legs for supporting the standard vertically or at any desired anale. The usual drive is by a 10-hp. motor through a gear reducer, on which are Insti- two grooved sheaves, One of which is keyed and the other free running On the shaft. Tension is provided by a car running on a track in line with the driving sheave

Jan 1, 1948

By P. de Vitry, Willis P. Mould

The wire saw is a tool not less than 60 years old, probably nearer 100 years old. It was developed in Europe and is reputed to have originated in Belgium. Frombold is said to be the original patentee. Wire sawing equipment, as indicated in Fig. I, is very simple. It consists of a three-strand wire cable, usually pis or 1/4 in. in diameter, or a single flat ribbon of medium hard, tough, alloy steel twisted into a helix of those diameters, made to form an endless belt of any length up to several thousand feet. The wire is guided into the cut by sheaves mounted in slides on steel columns situated close to either end of the cut. The feed motion usually is controlled either by gravity or by hand-operated feed screws. The steel columns or "standards" range from 15 to 30 ft. in length. At the top is a swiveled arm supporting a sheave similar to the traveling sheave below. Immediately under the swivel-mounted sheave is a guy plate or collar with shackles attaching four chain or wire-rope guys with suitable tightening devices, or with two guys and two jack legs for supporting the standard vertically or at any desired anale. The usual drive is by a 10-hp. motor through a gear reducer, on which are Insti- two grooved sheaves, One of which is keyed and the other free running On the shaft. Tension is provided by a car running on a track in line with the driving sheave

Jan 1, 1948

By G. L. Kulcinski, R. D. Leggett

Irradiated uranium containing 635 ppm of carbon, mostly in the form of UC precipitates, was annealed at temperatures from 650" to 900°C under hydrostatic pressures of 0 to 1000 bars. Postirradiation examination revealed that the carbide particles are not stable in the r phase of irradiated material but are stable in unirradiated material annealed under identical conditions. The degree of carbide dissolution appears to be connected with the fission product concentration and independent of annealing pressure. THIS paper describes the change in appearance of carbide particles in irradiated uranium after the uranium has been postirradiation-annealed. It has been proposed by several investigators&apos;-5 that fission gas-induced swelling in irradiated uranium may be reduced by incorporating a fine dispersion of second-phase particles into the metal. Because of the low solubility of carbon in uranium6 and the apparent stability of UC precipitates at high temperatures,6-8 this system has received some attention. The stability of UC particles to low-temperature irradiation has been demonstrated many times, as well as their stability during postirradiation anneals in the high a or B phases.9 Unirradiated uranium containing UC particles has been annealed high in the r phase, and the solubility of carbon was found to be only -115 ppm at 1050ºC.6 Vacuum annealing of irradiated uranium to the same temperature produces a spongelike sample, due to the formation and growth of fission gas bubbles."14 This highly disrupted lattice has made any determination of the stability of UC at these temperatures impossible. Nevertheless, it has always been tacitly assumed that the UC particles were still present. Recently, postirradiation, high pressure-high temperature tests have been performed on irradiated uranium containing a secondary phase of UC. 14 Examination of these samples after 100-hr, 900°C tests revealed that the carbides are not stable, and the results of these tests are presented here. 1) EXPERIMENTAL PROCEDURE The samples, high-pressure equipment, and subsequent analytical techniques are the same as those described elsewhere.14,15 Briefly, cylindrical samples of commercial-purity uranium that had been irradiated at <350°C to 0.37 at. pct B.U. were subjected to 90O°C, 100-hr anneals in NaK at pressures ranging

Jan 1, 1970

By J. D. Alexander, W. L. Martin, J. N. Dew

This paper presents data obtained using a flood-pot technique to determine the fuel available and the corresponding theoretical air requirements for in situ combustion of crude oils. Since the technique is relatively quick and easy, it is a practical and convenient tool for evaluating reservoirs as fireflood prospects. It is also a research tool which facilitates systematic study of the variables affecting fuel availability and corresponding air requirements. The understanding of these variables is of prime importance to those concerned with the technical and economic development of in situ combustion as an oil-recovery process. The experimental results show conclusively that the fuel available for in situ combustion is not a constant but, rather, varies with crude-oil characteristics, porous-medium type, oil saturation, air flux and time-temperature relationships. Thus, the fuel availability for specified field applications should be determined using actual reservoir crude and core material and the process conditions expected during in situ combustion in the reservoir. INTRODUCTION In situ combustion is a thermal process for recovering crude oil from reservoirs. The thermal energy released during the combustion of a small amount of the oil in place aids in the displacement of the remaining oil. Numerous articles have been published describing the in situ combustion process giving detailed results of laboratory and field experiments.10 In order to engineer an in situ combustion project, a number of important factors must be considered and determined. These factors include: (1) the amount of fuel consumed per unit of reservoir volume swept by the combustion zone, (2) the composition of the fuel consumed, (3) the amount of air required to consume this fuel, (4) the portion of the reservoir swept by the combustion zone, (5) the appropriate air-injection rates and pressures, (6) the amount of oil that will be recovered, (7) the rate of oil production and (8) the operating costs. Nelson and McNiell1 recently have described a procedure which utilizes laboratory combustion-tube data as a basis for the calculation of some of these design factors. Various authors have attempted to describe the in situ combustion process mathematically, and considerable progress has been made. Analytical solutions to the problem of heat transfer from a moving combustion front have been obtained for linear and radial systems."-&apos; All of the published results involve the assumptions that: (1) fuel concentration is constant throughout the reservoir, or that fuel concentration is inversely proportional to the velocity of the front for a given rate of oxygen consumption; and (2) the fuel reacts instantaneously with injected oxygen, while liberating a constant amount of heat per unit weight of fuel at all temperatures. It seems both desirable and reasonable to test the validity of these assumptions experimentally. This paper presents laboratory data which were obtained by means of a "fire flood-pot" method for determining fuel availability and composition, and the corresponding theoretical air requirements for in situ combustion of crude oils under variable conditions. The mechanics of the method are similar to a conventional tube-run experiment.&apos; The important differences involve the size of the reservoir model used and the method for providing the experimental environment. The new method subjects conventionally-sized core samples or unconsolidated sands to a programmed environmental sequence similar to that experienced by a similar volume of rock during the approach and passage of a combustion front in a long tube or in an oil reservoir undergoing in situ combustion. Restored-state samples can also be used. The small samples and relatively simple techniques involved allow an experiment to be set up, run and calculated in about three 8-hour days. This is a considerable improvement over long-combustion-tube techniques which can require several days to run and several more work days to set up and calculate. All the runs presented were run at 40-psig injection pressure. Pressure was not considered as a variable for these experiments, since we previously had found that it had only a small effect on fuel availability up to 600 psig.APPARATUS AND MATERIALS APPARATUS The fire flood-pot apparatus consists of a consolidated

By E. H. Snow, B. E. Deal

Instability effects in semicanductor devices have long been attributed to the motion of charges on or within oxide layers on the surface. These effects are of critical importance in metal-insulator-semiconductor MIS) field-effect devices. For this reason, the capacitance-voltage or the conductance-voltage characteristic of these devices can be used as a sensitive detector to study charge transport and polarization effects in the oxide or insulator. A review is given of the results of such studies of thermally grown SiO2 as well as of other insulating films of importance in silicon technology. Three types of effects are distinguished. The first of these is the drift of mobile cations within the dielectric, examples being thermally grown SiO, which is often contaminated with sodium ions, and a variety of other glasses in which the mobile ions are a part of the glass composition. The second effect is a dipole-type polarization which occurs in phosphosilicate glass films obtained by reacting P2O5 with thermally grown SiO2. The third effect involves the transfer of charges between the dielectric and the silicon electrode. This occurs in silicon nitride and other deposited dielectrics. It is concluded that MIS studies have provided a powerful technique joy the study of charge transport and polarization effects in insulating films. The knowledge gained from these studies has led to an understanding of surface effects on conventional transistors and diodes as well as making possible stable MIS transistors. THE metal-insulator-semiconductor field-effect transistor is conceptually the oldest type of active semiconductor device.&apos; The earliest attempts at making this device were frustrated because of high surface state densities at the interface between the semiconductor and the gate insulation.&apos; However, by using a silicon substrate with thermally produced silicon dioxide as the gate insulation, this problem was solved and metal-silicon dioxide-silicon devices with good characteristics were made as early as 1960. 3 Yet it was still over 5 years before these devices became a commercial reality. This delay was largly due, not to surface states, but to stability problems associated with polarization effects within the insulating layer which caused the threshold voltage of the device to drift under temperature and bias treatments. The solution to these problems has not only made possible stable MIS devices, but it has added immensely to our understanding of failure mechanisms in conventional bipolar transistors and has added to the reliability of ali types of planar devices. In this review, we shall first describe the effects of various types of polarization phenomena on MIS device characteristics. Then, since thermally grown SiO, is by far the most important insulator used in these devices, we shall review historically the type of instabilities which have been observed in thermal oxides, the attempts at understanding and eliminating them, and the present status of the problem. We shall then turn our attention to the various deposited insulators which have been used, including lead glasses, phosphosilicate glass, vapor-deposited silicon oxide, and silicon nitride. Interestingly enough, many of these materials show polarization effects which are quite different from those generally observed in thermally grown SiO2. THE EFFECTS OF POLARIZATION PHENOMENA ON MIS CHARACTERISTICS The simplest MIS device and the one which has been most frequently used in the study of polarization effects is the MIS capacitor. Two modifications of this structure with single- and double-layer dielectrics are illustrated in Figs. l(a) and (b), respectively. The capacitance of this structure as a function of voltage applied to the metal gate electrode is plotted in Fig. 2 for the case of an n-type silicon substrate. When the silicon surface is accumulated (positive bias) the measured capacitance is just that of the insulating layer C. When the surface is inverted (negative bias), the capacitance is that of the insulator and a silicon depletion layer in series CoCs/(Co + Cs). Indicated on the horizontal axis of Fig. 2 is the voltage VT at which the silicon surface becomes strongly inverted. This voltage corresponds to the threshold or turn-on

Jan 1, 1969

By A. E. Dwight

Lattice parameters were determined for eighteen equiatornic alloys of the CsCl-type structure, ten of which were previously un-reported. It was found that fomation of the CsCl-type structure in binary alloys of the transition elements is largely dependent on position of the elements in the periodic table. The relative size of the two elements was not found to be a controlling factor. A recent paper by Beck, Darby, and Arora1 corre-lates the occurrence of CsC1-type ordered structures with the position of the constituent elements in the periodic table for the first long period. It was also suggested that a definite increase in relative bond strength between unlike atoms occurred when, in binary alloys of iron-group elements, the other component is changed from a chromium-group element, to a vanadium-group element, to titanium. A later paper by Philip and Beck2 noted that the lattice contraction increased in the order CrFe, VFe, and TiFe. It was also noted by Philip and Beck2 that the lattice contractions of CsC1-type alloys decreased in the order: TiFe, TiCo, and TiNi, which is an apparent reversal of the contractions expected from the position in the periodic table. It was suggested that the increasing lattice contraction is an indication of increased stability, i.e., greater A-Bbond strength. The present investigation was carried out to determine whether the relation of the position in the periodic table to the formation of the CsC1-type structure was also correct for alloys involving the second and third long-period elements. A systematic search was made for CsC1-type structures among equiatomic alloys and for those found, the lattice contraction was determined. EXPERIMENTAL TECHNIQUE The elements Y, Gd, Ti, Zr, Hf, V, and Cb are designated the A group and the elements Mn, Re, Fe, Ru, Os, Co, Rh, Ir, Ni, Pd, Pt, Cu, Ag, and Au are designated the B group. Equiatomic alloys were prepared for 57 AB combinations. The alloys were arc melted in a multicrucible furnace3 in buttons ranging from 5 to 20 g. Chemical analyses were not made, as the charge weights agreed closely with those of the buttons after melting. The alloy buttons were homogenized at 800° to 900°C. Metal log raphic and X-ray specimens were prepared and heat treated at temperatures from 600° to 1200°C. Specimens for X-ray diffraction were usually ground to a powder in an agate mortar; however, needle-shaped solid specimens were used when the alloy was sufficiently ductile to permit their preparation. Diffraction patterns were taken with a Straumanistype Debye-Scherrer camera using filtered Cu or Co radiation. The lattice parameters were obtained in A by plotting the calculated a0 values against the cos29/sin 0 + cos2?/? function and extrapolating linearly to ?= 900. Metallographic control specimens were polished on cloth wheels with diamond paste and etched with various phosphoric and nitric acid reagents. RESULTS The eighteen equiatomic alloys listed in Table I gave evidence of a cubic structure with two atoms in the unit cell, although two of these cubic structures exist only at elevated temperatures and transform to a tetragonal structure on quenching. Nine of these eighteen alloys gave diffraction patterns with super-lattice lines showing that the structure is of the CsC1-type. The lack of superlattice lines in patterns of the other nine alloys may be attributed to the small difference in atomic scattering power of the components. Metallographic study indicates the occurrence of nine narrow single-phase fields at the AB composition. Any or all of these nine may also have a CsC1-type structure. The VFe alloy was found to have a CsCl-type structure by Philip and Beck2 through the use of CrKa radiation (for which the scattering factor of V is anomalously low), whereas the Cu radiation used

Jan 1, 1960

By S. P. Kinney, C. E. Wood, T. L. Joseph

In connection with its investigations of the blast-furnace process, the Bureau of Mines, in cooperation with the Minnesota School of Mines Experiment Station, developed a 6-ton experimental furnace. Such a furnace was needed to determine the feasibility of producing ferroman-ganese from Minnesota manganiferous iron ores, a problem of national importance because of the present need for manganese in the steel industry and our small reserves of ferro-grade ores. Furnace operators are reluctant to use new or untried raw materials or to make decided innovations in practice on account of the financial hazard of experimenting with full-scale equipment. A small furnace which can be operated at a relatively low cost is particularly adapted for testing new raw materials and for determining the feasibility of decided innovations in practice. Laboratory experiments, plus whatever information may be available, are valuable but often do not indicate the net result of changes in an operation involving a large number of interrelated variables. From time to time the cooperation of the Bureau of Mines is solicited in connection with problems involving departures from normal procedure. Under these circumstances some sort of a practical demonstration is a desirable forerunner to full-scale operations which appear feasible after small-scale tests. The Aluminum Co. of America was interested in knowing the practicability of smelting a charge of bauxite, iron ore, and limestone, of proportions that would produce slag of the following composition: A1203, 47 to 48 per cent.; CaO, 41 to 42 per cent.; SiO2,4 to 5 per cent.; TiO2, 2 to 3 per cent.; FeO, 1 percent., and MgO, 1.8 percent. In addition to determining whether it was feasible to operate a blast furnace on slag approaching the composition given above, a quantity of slag was needed for a series of experiments that would show the relative ease and cost of extracting alumina from slag which could be made in the blast furnace, as compared to extracting it from raw bauxite. The value of the slag as a raw material

By P. N. Richards, M. K. Ormay

Commercially hot-rolled low-carbon steel strip may have one of two basic types of orientation texture, depending upon the amount of a iron which was present during the finishing passes. The changes in these textures with varying amounts of cold reduction up to 95 pct have been determined for the sheet surface plane and for parallel planes down to the mid-plane. The development of cold reduction textures has been reassessed on the basis of (200), (222). and (110) stereographic pole figures and pole density or inverse pole figure values. In agreement with the literature, it is shown that the textures can be described in terms of partial fiber textures but alternative descriptions are given for one of the fiber textures, in order to more closely correlate with experimental data. One partial fiber texture consists of orientations of the type (hkk)[011] extending from (100)[011] to {322}(011) in agreement with the literature. At moderate amounts of cold reduction, a second partial fiber texture forms with a <331> fiber axis inclined 20 deg to the sheet normal and a range of orientations centered on one close to (1 11)[112] and reaching to (232)[101] or (322)[011]. An alternative description involves a (111) fiber axis parallel to the sheet normal but capable of rotation about the rolling direction with rotation about the fiber axis. ORIENTATIONS developed in low-carbon steel strip after cold reduction are of commercial importance because they control, in part, the final preferred orientations after subsequent annealing. The method of control however is not understood completely. Some preliminary work indicated that the cold-reduced orientations and the subsequent annealing textures of commercial low-carbon steel were dependent on the orientations present in the material before cold reduction, that is, those present in the hot-rolled strip but, to date, the effects of initial orientations have not been extensively investigated. For this reason, much of the information given in the literature on development of preferred orientation is difficult to assess as details of initial texture and processing conditions are often inadequate or are altered by a subsequent heat treatment such as normalizing.&apos; It is known2 that anomalous results for near surface orientations may be obtained if lubrication during cold rolling is not adequate but whether lubricant was used during the experiments has not always been given, nor has the exact depth below the surface at which determinations have been made. A comprehensive review of cold rolling textures has been made recently by Dillamore and Roberts&apos; and more restricted recent reviews are due to stickels4 and Abe.5 Based largely on the experimental work of Bennewitz,1 reviewers have accepted that the preferred orientations produced on cold reducing low-carbon steel can be described in terms of two partial fiber textures as follows: Partial Fiber Texture A which has a (011) direction in the rolling direction and includes orientations within the spread from (211)[011] through (100)[Oll] to (211)[011.]; there is some controversy as to whether it extends as far as the orientation (111)[011]. As Dillamore6 has observed, the extent of this partial fiber texture depends on the intensity levels selected. Partial Fiber -texture B which has a (011) direction located 60 den from the rolling direction in the plane containing the rolling direction and the sheet normal. There are two directions which satisfy these conditions and orientations in this partial fiber texture extend from (21l)[0ll] through (554)[225] to (121)[101]. The orientations {211}(011) are members of both partial fiber textures A and B and it can be noted that a variant of {554)<225> is within 6 deg of a variant of {111}(112). Barrett7 had postulated earlier that, in addition to orientations which would fall into partial fiber texture A, a true fiber texture with a (111) direction in the sheet normal was present after heavy cold reduction. This fiber texture would include orientations such as {111}(011) and {111}(112). Later investigators, notably Bennewitz,&apos; have discounted this, mostly on the ground that the partial fiber textures A and B, as described above, contain all the strong orientations that have been observed. However in other work it has been reported2 that (222) pole density or inverse pole figure values show a continuing increase with increasing reduction by cold rolling and give values considerably greater than for any other low indices plane. Thus it could be inferred that a (111) fiber texture as described by Barrett would be one which becomes more dominant with increasing cold reduction, whereas Bennewitz&apos; concluded that components such as {554)(225) in partial fiber texture B began to decrease in intensity at high reductions. Following Bennewitz, one would expect a decreasing (222) pole density value (parallel to the sheet normal) with increasing cold reduction. Because fiber textures consist of grains with a range of orientations that have one axis in common, it has been inferred that during deformation the crystal orientations rotate about the fiber axis&apos;74 and that the orientations of crystals that at one stage belong to one fiber texture can rotate on further cold reduction into the other fiber texture through an orientation in which the two fiber textures intersect.&apos; For example,

Jan 1, 1970

By J. G. Faller, L. P. Skolnick

The distribution of cobalt and vanadium over non-equivalent crystallographic sites in C14-type Zr(VCo), alloys has been investigated. An anomalous X-ray scattering technique developed by Skolnick, Kondo. and lavine7 by which the separation in the scattering factors of two similar atoms can be enhanced was employed. Six alloys spanning the pseudobinary section ZrV1.6Co0.4-ZrVO.6CO1.4 at 10pct steps showed a nonrandom compositionally dependent distribution. Specifically, at high vanadium content cobalt preferentially occupied sites of type (6h) and vanadium, sites of type (2a; at low vanadium content the reverse was observed. In addition to the distribution fraction the structural parameters x and z were obtained. There was no significant deviation of these parameters from those obtained in the ideal C14 structure. Certain suggestions are made to account for the observed nonrandomness in the distribution of atoms on the two types of sites. INTERMETALLIC compounds of formula AB2 iso-morphous with MgCu2, MgZn2, and MgNi2 are known as Laves phases. Because Laves phases exhibit high symmetry and coordination numbers, the highest possible for an AB2-type compound,1 they are among the most frequently observed compounds in nature. In recent years interest has centered about the purely transition metal Laves phases2-&apos; in efforts to understand the function of atomic size and electronic structure in the formation of these compounds. It has been observed that pseudobinary Laves phase systems often show a variation of structure across the phase diagram. Such a system is the ZrV2-ZrCo2 in which the structure varies from cubic MgCu2 to hexagonal MgZn2 to cubic MgCu2.4 Some understanding about the conditions under which the second modification is stable can perhaps be gained by studying the distribution of cobalt and vanadium atoms on lattice sites in the MgZn2 modification of the system ZrV2-ZrCo2. In both the MgZn2 and MgNi2-types there exist nonequivalent positions open to occupancy by the B element, whereas in the MgCu2 prototype all sites are equivalent. Skolnick, Kondo, and La-vine7 have developed an anomalous scattering technique suitable for this type of investigation. Whereas the influence of size on the formation of a Laves phase is well recognized, no substantial evidence has been put forth in support of the size ratio dependence of a particular prototype. Berry and Raynor8 suggested that RA /RB ratio does indeed affect the type of structure that is chosen, MgZn2 compounds tending to cluster about 1.225 while MgCu2 compounds were found at larger deviations from this ratio. Dwight,3 however, from a study of 164 Laves phases does not believe this generalization to be justified. Electronic effects are certain to play a part in the stability of Laves phases in general and in the choice of a structure type in particular. For example, size along would favor the formation of Laves compounds of Ti, Zr, Hf, Ta, or Nb as the A element with nickel or copper as the B element. The absence of such is attributed to an unfavorable electron : atom ratio by Elliott and rostoker.4 Early experiments of Laves and witte9 with pseudobinary and pseudoternary systems of the three prototypes established the dependence of crystal structure upon electron: atom ratios. They observed that the MgCu2 structure dissolved elements of higher valency until the electron: atom ratio of =1.8 was reached; the MgZn2 likewise dissolved elements of lower valency replacing zinc. witte,6 from calculations of the electron : atom volumes of Brillouin Zones, obtained limits of stability for the prototypes MgCu2 and MgZn2. Elliott and Rostoker4 used these limits with considerable success in the all-transition element Laves phases they investigated. According to witte,6 compounds between the electron :atom ratios of 1.80 and 2.32 were of the MgZn2 type; those above and below exhibited the MgCu2-type structure. On the basis of these limits and an assumed valency of zirconium based upon the near tetra-valence of titanium, Elliott and Rostoker obtained valencies for the first transition series elements. For the Laves phases with which this investigation is concerned, ZrV2 and ZrCo2, the authors calculated electron :atom ratios of 2.54 and 1.56, respectively. These ratios are for the MgCu2-type structure and straddle the stability band of the MgZn2 modification. One could, therefore, predict that a pseudobinary system ZrV2-ZrCo2 should pass through the MgZn2 modification in traversing the composition diagram from one end to the other. Implicit in this assumption is a smooth change of the electron: atom ratio from 2&apos;54 to 1.56. MOSS10 states that his finding the low temperature structure of ZrCr2 to be C15 instead of C14 alters greatly Elliott&apos;s valency of zirconium and hence the assumed valencies of the other metals. Such a quantitative correlation of structure with electron : atom

Jan 1, 1963

By Frank Harris

THE strength of hard drawn copper wire is a question of considerable importance to both manufacturer and consumer. Unlike steel and alloy wires, in which strength is governed by both chemical and physical considerations, the high conductivity required for copper wire in the electrical industry generally precludes the possibility of obtaining tensile strength through the use of alloys. Consequently, this strength is largely a matter of the physical structure, and all factors known to affect this structure, such as rolling temperature, die contours, lubricants, drawing speeds, etc., are matters of prime importance. The experiments described here have been carried out during the past year at the Baltimore plant of the American Smelting & Refining Co., in connection with a general investigation of some of the questions mentioned above, with the object of studying the physical structure of hard drawn copper, wire and the influence of certain factors on that structure. The work has been of an exploratory nature, rather than comprehensive, but it was thought that the results might prove of sufficient general interest to warrant their publication. The bulk of the hard drawn copper wire used in places where strength is an important factor is manufactured to strict specification, based usually in the United States on that of the American Society for Testing Materials (B-1-23). This specification calls for almost as high a value of tensile strength; consistent with elongation, as it is possible practically to obtain, and only physically perfect material can be relied on to meet such a specification. Obvious defects, such as laminations produced through fins in the original rods or brittleness due to overdrawing, are usually recognized and need only passing reference. Laminations can be detected by twisting and untwisting the wire several times; they will show up on the surface in the form of fins. Fig. 1 shows a very bad example of this defect. The wire may be perfectly smooth before twisting but when such laminations are present they will readily show up under this treatment. This trouble is caused by similar defects in the original rod produced by overfills in rolling. Fig. 2 shows the cross-section of the rod from which the wire in Fig.1 was drawn.

Jan 1, 1928

By Arthur F. Taggart, A. W. Thomas, T.C. Fitt

It was noticed early by operators that high recoveries and flocculation of the sulphide minerals were closely correlated in agitation-froth flotation. Later, this readily visible flocculation was found almost invariably to be due to the binding together of the oiled sulphides by minute air bubbles, and is now known to be characteristic of pulps in which at least one of the mineral species is coated with an insoluble collecting oil. In 1930 it was reported1 that in differential flotation a correlation exists between Brownian movement of particles in the pulp and their nonfloatability, and that Brownian movement and dispersion are likewise correlated, whence it would appear to follow that dispersion of a mineral particle in a flotation pulp denotes a particle condition unfavorable to flotation. In 1934 it was postulated2 that Brownian movement, dispersion and nonfloatability all flow from the condition of the surface of the dispersed particles. It was also postulated at that time that the surfaces of dispersed particles are ionized, the ionized compound being a product of reaction between a component of the particle and a component of the pulp, of a mass solubility of the general order of a fraction of a milligram to I 5 to 20 mg. per liter. It was then further asserted, and has since been confirmed by Bankoff,3 that sulphides so conditioned with soluble collectors as to be floatable flocculate without the intervention of air bubbles as binding media. The present paper comprises an inquiry into the nature of the bound and counter ions in zinc sulphide dispersed by sodium arsenate. A part of its findings was mentioned in the 1934 paper above cited.= The tests show that: I. When powdered granular zinc sulphide is immersed in aqueous solutions of sodium arsenate, arsenate ion is abstracted from solution and anchored to the solid surface, while sulphate and lower sulphoxy ions are concurrently displaced therefrom in substantially stoichiometric quantities. 2. The ion counterbalancing the anchored arsenate ion is zinc. 3. Dispersion and Brownian movement of zinc sulphide are concurrently maxima at an arsenate-ion concentration lying between 0.01 and 0.001-molar sodium arsenate. 4. Any condition or reaction that tends. to remove the zinc arsenate coating from the zinc sulphide particles decreases dispersion and Brownian movement concurrently. Experimental Three samples of zinc sulphide were used. Lot I was C.P. zinc sulphide, washed well be~ond absence of chloride, as shown by test with silver ion. Lot 2 was prepared by precipitation from hydrochloric acid solution of arsenic-free zinc, and was washed as lot I. Lot 3 was prepared by heating a portion of lot 2 in absence of air at 1200° to r300°C. for one hour."

Jan 1, 1943

By C. W. Haworth, M. G. Hall

THE diffusion of copper in silver has been studied by Sawatzky and Jaumot1 and Cahoon and Youdelis.2 Sawatzky and Jaumot measured tracer diffusion in single crystal specimens but the 12.9 h half-life of CU64 limited the time of the diffusion anneal to about 50 hr, and in consequence the minimum temperature of the investigation was 716°C. Cahoon and Youdelis employed polycrystalline diffusion couples, and measured the interdiffusion coefficient over the range 0 to 2 at. pct Cu. These experiments were performed at temperatures down to 630°C and a discontinuity in the Arrhenius plot was observed at -700°C. The high D-values at lower temperatures were attributed to the effect of grain boundary diffusion. The present experiments were undertaken to investigate this anomaly and study the low temperature region of the diffusion of copper in silver. The method employed single crystal samples and a plated source of copper. Silver single crystals 2½ by 4 in. sq were grown from zone-refined silver bar (>99.99 pct Ag) by the Bridgeman technique, and $ in. thick slices were cut by spark machining. The specimens were electro-polished, and a 2 µm layer of copper was electroplated on to the planar surface at one end of each specimen using a potentiostatic voltage source. The following solution was used for plating: CuSO4 . 5H2O 125 gm H2SO4 (S.G. 1.8) 53 ml H2O 1000 ml The diffusion couples were sealed in capsules, in an argon atmosphere, and were annealed at either 701, 597, or 498°C. The temperature measurements were made to an accuracy of *l°C After the anneal, the penetration of copper into the silver was determined using an electron probe micro-analyzer. 100 sec scaler measurements of the intensity of Cu Ka! X-radiation were performed at 2 to 5 µm intervals along a line normal to the source, with a beam potential of 25 kv. Allowances were made for the background radiation, and the dead-time of the counting system in the normal way, and the intensity ratios were corrected to weight concentration by the method of Duncumb & de-Casa.3 For the analysis of the diffusion profiles, it was first observed that the copper layer did not completely dissolve in the host crystal for the specimens annealed at 498 and 591 whereas for the specimen annealed at 701°C, a single phase solid solution was formed. For the 498" and 597°C specimens, the concentration of copper in the silver at the interface was therefore constant throughout the anneal and the analysis for a

Jan 1, 1970

By Arthur F. Taggart, T. C. Fitt, A. W. Thomas

It was noticed early by operators that high recoveries and flocculation of the sulphide minerals were closely correlated in agitation-froth flotation. Later, this readily visible flocculation was found almost invariably to be due to the binding together of the oiled sulphides by minute air bubbles, and is now known to be characteristic of pulps in which at least one of the mineral species is coated with an insoluble collecting oil. In 1930 it was reported1 that in differential flotation a correlation exists between Brownian movement of particles in the pulp and their nonfloatability, and that Brownian movement and dispersion are likewise correlated, whence it would appear to follow that dispersion of a mineral particle in a flotation pulp denotes a particle condition unfavorable to flotation. In 1934 it was postulated2 that Brownian movement, dispersion and nonfloatability all flow from the condition of the surface of the dispersed particles. It was also postulated at that time that the surfaces of dispersed particles are ionized, the ionized compound being a product of reaction between a component of the particle and a component of the pulp, of a mass solubility of the general order of a fraction of a milligram to I 5 to 20 mg. per liter. It was then further asserted, and has since been confirmed by Bankoff,3 that sulphides so conditioned with soluble collectors as to be floatable flocculate without the intervention of air bubbles as binding media. The present paper comprises an inquiry into the nature of the bound and counter ions in zinc sulphide dispersed by sodium arsenate. A part of its findings was mentioned in the 1934 paper above cited.= The tests show that: I. When powdered granular zinc sulphide is immersed in aqueous solutions of sodium arsenate, arsenate ion is abstracted from solution and anchored to the solid surface, while sulphate and lower sulphoxy ions are concurrently displaced therefrom in substantially stoichiometric quantities. 2. The ion counterbalancing the anchored arsenate ion is zinc. 3. Dispersion and Brownian movement of zinc sulphide are concurrently maxima at an arsenate-ion concentration lying between 0.01 and 0.001-molar sodium arsenate. 4. Any condition or reaction that tends. to remove the zinc arsenate coating from the zinc sulphide particles decreases dispersion and Brownian movement concurrently. Experimental Three samples of zinc sulphide were used. Lot I was C.P. zinc sulphide, washed well be~ond absence of chloride, as shown by test with silver ion. Lot 2 was prepared by precipitation from hydrochloric acid solution of arsenic-free zinc, and was washed as lot I. Lot 3 was prepared by heating a portion of lot 2 in absence of air at 1200° to r300°C. for one hour."

Jan 1, 1943

By J. G. Richardson, K. H. Coats

During the initial growth of a gas bubble in an aquifer storage reservoir the injected gas tends to override the water. The resulting low displacement efficiency and high rate of gas travel down-structure make it difficult to maintain water-free production. This paper illustrates the use of two-dimensional, two-phase calculations to simulate this gas-water displacement. Calculations were performed for a stratified aquifer and for several homogeneous sands differing in permeability, porosity and thickness. Results are discussed and compared with performance predictions obtained from the simpler Buckley-Leuerett and Dietz formulas. This comparison indicates the necessity for the two-dimensional calculations in realistically simulating the gravity override of the water by injected gas. INTRODUCTION In recent years natural gas has been stored near markets in aquifers where insufficient storage capacity is available in depleted fields. Operators of these aquifer storage reservoirs have encountered technical problems relating to the gas-water displacement accompanying initial growth of the gas bubble. Injected gas tends to override the water, with a resultant low displacement efficiency and high rate of gas travel down-structure toward spill points. Low displacement efficiency makes if difficult to sustain water-free gas production. Sometimes the fingering of gas down-structure may be so pronounced that the injection rate must be severely curtailed, which excessively lengthens the time required for bubble growth. This paper is concerned with estimating — for given aquifer characteristics and fluid properties — the displacement efficiency, rate of gas movement down-structure and rate of gravity drainage of water behind the gas front. Several published articles relate to simulative capability necessary to handle this problem. The Dietz formula1 and Buckley-Leverett2 method have some applicability to the problem; Woods and comer3 reported one-dimensional, radial calculations which accounted for the two-phase flow of gas and water. Most recent research directed toward understanding aquifer behavior in relation to gas storage has concentrated on single-phase flow in aquifer.4 Douglas, Peaceman and Rachford5 presented a method for calculating multidimensional two-phase flow in reservoirs; their method has been applied in work reported by Nielsen and Tek,6 Blair and peaceman7 and Goddin.8 Refs. 5 and 7 show comparisons between experimental data and calculations similar to those employed here. One purpose of this paper is to illustrate the use of two-dimensional, two-phase flow calculations in simulating the difficult problem of water displacement by gas in a vertical cross-section. The pronounced fluid density and viscosity differences combine with the disparity in horizontal and vertical dimensions of the cross-section to pose one of the more difficult problems in reservoir simulation. The calculations described account for capillary and gravity forces, relative permeability and reservoir heterogeneity. An example reservoir is described and calculated results are presented for a variety of injection rates and values of permeability, reservoir thickness and dip angle. A second purpose is to compare the two-dimensional calculations with results obtained from the Buckley-Leverett and Dietz formulas. For this reason most calculations were performed for a simplified example reservoir to which the latter techniques might reasonably be applied. However, the computer program employed applies equally well to cases involving arbitrary spatial variations of permeability, porosity, reservoir thickness and dip angle.

By A. Patton

E. T. McCLEARY, Youngstown, Ohio (written discussion).-Perhaps there is no question before the steel manufacturers of America today that causes them more worry than that of maximum production, together with good quality, and Messrs. Patton and Speller have clearly shown in their excellent paper how this may be accomplished. Any operation that tends to uniformity is certainly conducive to good practice, and as the use of roll scale in the converter eliminates to a large extent the variations in temperature due to varying silicon content in the pig iron, it should certainly give a more uniform product. At the plant of The Youngstown Sheet & Tube Co. the use of roll scale was started in the year 1908. A great many tests have been con-

Jan 4, 1917

By Clarence M. Haight

The general practice in drill sharpening shops, of which descriptions have been written, is about as follows: The bit is heated to 1600" to 1900°F. Then when forged to the proper shape and size in the sharpening machine, the steel is allowed to cool; it is then passed to a hardening furnace where only the end is heated to about 1450" F., and then quenched in cold water, brine, or in brine with oil on top.

Jan 1, 1922

By G. R. Speich, S. A. Kulin

R. C. Shnay (Dept. of Mines and Technical Surveys, Ottawa, Ont., Canada)-—The authors are to be congratulated on an interesting and informative paper. However, several questions arise when the isothermal formation of martensite .is considered in relation to the formation of bainite at temperatures near the M, point. The reactions in an alloy and in a plain carbon steel would appear to be comparable; and in the course of a recent investigation of the austenite-bainite transformation in a plain carbon steel,Ia the writer has obtained data at temperatures above and below the M, point. These data are in some respects similar to those of the authors and a comparison would seem justified. The steel used in this investigation had the nominal composition: C, 0.80 pct; Mn, 0.20; and Si, 0.20. The course of the transformation was followed by the use of a magnetic balance. The magnetic moment of the specimen as determined by this instrument is directly proportional to the percentage of the total volume of the specimen which has transformed to bainite. ~lf specimens were austenitized at 1850°F for 4 hr, quenched to the transformation temperature, and quickly transferred to the magnetic balance. Readings were taken at regular intervals until the transformation had stopped. A typical transformation curve is shown in Fig. 9. The preliminary curve preceding the S-shaped curve was found at all temperatures above the M, to around 600°F. Both the extent of this preliminary curve and the time interval between it and the S-shaped curve were found to decrease with increasing temperature as was suggested by Davenport and Bain.14 Therefore,

Jan 1, 1953

By Chase Palmer, Edson S. Bastin

While the reducing action of organic matter, of ferrous sulphate, and of hydrogen sulphide has frequently been invoked to account for the deposition of native gold and silver from ore-forming solutions, the high efficiency in this respect of certain of the metallic minerals which form the ore itself has not been suffciently recognized. If a little finely powdered chalcocite is placed in a test-tube arid 2 or 3 cc. of a dilute solution of gold chloride are poured over it, two or three shakes of the tube suffice to remove all the gold from the solution. The color of the solution changes from yellow to pale green, showing that copper is dissolved simultaneously with the precipitation of metallic gold. If a piece of chalcocite is hung in a dilute aqueous solution of silver sulphate (1/40 normal), a coating of silver begins immediately to form on the mineral, and within a few moments a beautiful silver tree has developed, similar to that formed when metallic zinc is immersed in a similar solution. When similar experiments are conducted with other sulphides and with certain arsenides and sulph-arsenides, especially those known to be commonly associated with native silver in ore deposits, it is found that these minerals differ greatly in their efficiency as precipitants, especially in their effect on silver solutions. The tests made with most of the minerals were qualitatipe only, but the reactions of a silver sulphate solution on chalcocite and niccolite were submitted to quantitative study to determine the nature of the reactions involved. Quantitative studies of the reactions with other minerals are now in progress

Jan 1, 1914

By Charles R. Simcoe

The stress-strain curves in the microyield region for various Fe-C solid solutions shown by Davies and Ku are typical examples of parabolic curves defined by the expression a = kEn 111 These data, when replotted on log-log coordinates, as shown in Fig. 9, exhibit three essentially parallel straight lines. It is apparent that carbon increases the flow stresses, but does not affect the exponent n. In other words, the only factor in Eq. [1] affected by in in carbon content is the constant k. As Eq. [1] is written k is the stress at a strain of 1.0. This is unsatisfactory for examining data in the microyield region. Therefore, the equation can be altered to the form: to permit the use of the authors&apos; microyield stress at a strain of 10-6 as k. Extrapolating the curves in Fig. 9 to a strain of 10-6 gives stress values of 2000, 3200, and 5400 psi for 0.008, 0.014, and 0.02 pct C, respectively. These values do not agree exactly with the authors&apos; measured values, but this will not affect the following discussion. The effect of carbon content on the slopes of the stress-strain curves shown in Fig. 2 of the paper by Davies and Ku can be analyzed by differentiating Eq. [2] with respect to strain. Thus: where n is always less than 1.0. Since n is essen- tially constant as a function of carbon content for the data under discussion, the slopes of the stress-strain curves depend only on k and E. If the slopes are examined at various selected Plastic strains. i.e., 10-6, 10-5, and so forth, it follows from Eq. [3] that the dif-ferent slopes for the different carbon contents depend only on the different values of ke=10-6. Thus, the larger ke=10-6, the steeper the linear stress-strain curve will rise with increasing plastic strain. This

Jan 1, 1969

By A. Ahmadieh, J. E. Dorn, Jack Mitchell

A detailed investigation of the disloccrtion mechanisms controlling prismatic, slip in a solid solutions of magnesium containing up to 15.9 at. pel Li revealed that low-temperature prismatic slip is controlled by the Peicrl&apos;s mechanism for all alloy compositions. At higher temperatures slip in the 7.9 at. pet Li alloy was found to follow the diclates of the cross-slip mechanism from basal to prism planes, while the higlier-lilhium alloys exhibited an athermal dejormation process which might be due COARSE-GRAINED polycrystalline aggregates of distilled magnesium exhibit very limited ductility at low temperatures.&apos; The ductility of polycrystalline magnesium, however, is much improved by solid-solution additions in excess of about 8 at. pct to shot-range ordering. The major effect of lithium additions on the low-temperature Shear] stress. for prismatic slip appears to be due to its efftct in lowering the Peierl&apos;s stress whereas (1 increase in the shear stress with increased lithium conlent at higher temperatures might he due to short-range order strengthening. Additions rip to 7.9 (at. pel Li appear to have only minor effects on the slackiug-jaidt energy. Li.2 Although the relative amounts of basal slip and twinning are not materially altered by such alloying, a substantial change takes place in the relative amounts of prismatic slip. Whereas prismatic slip is negligible and limited to regions of high stress concentrations in the vicinity of the grain boundaries in pure magnesium, extensive prismatic slip over entire grains occurs in the higher lithium content alloys. Furthermore, as the lithium content is increased above 8 at. pct, the flow stress for polycrystalline aggregates decreases. Comparison of the single-crystal data on pure magnesium for basal slip by Sheely and Nash3 and those for prismatic slip by Flynn, Mote, and Dorn4 indicates that the critical resolved shear stress for prismatic slip is much above that for basal slip.

Jan 1, 1965